CN1290948C - 除醛乳胶漆及其制备方法 - Google Patents
除醛乳胶漆及其制备方法 Download PDFInfo
- Publication number
- CN1290948C CN1290948C CN 200410008372 CN200410008372A CN1290948C CN 1290948 C CN1290948 C CN 1290948C CN 200410008372 CN200410008372 CN 200410008372 CN 200410008372 A CN200410008372 A CN 200410008372A CN 1290948 C CN1290948 C CN 1290948C
- Authority
- CN
- China
- Prior art keywords
- percent
- aldehyde
- latex paint
- agent
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
一种除醛乳胶漆，其组分及含量为：丙烯酸共聚乳液20%～30%；聚羧酸盐0.5%～1.0%；芳烃基聚醚0.2%～0.5%；钛白粉10%～25%；填料25%～35%；消泡剂0.2%～0.5%；防腐剂0.2%～0.5%；防霉剂0.2%～0.5%；增稠剂0.2%～0.5%；醇酯1%～2%；pH调节剂0%～0.2%；除醛制剂2%～3%；水为余量；所有百分数为重量百分数。本发明的除醛乳胶漆采用了一种特殊的分散技术，使稀土氧化物、二氧化钛能在水中分散，配制的除醛乳胶漆具有良好的稳定性，除醛效果持久高效，无毒无味，安全环保。
Description
技术领域
本发明涉及一种功能性内墙涂料，尤其涉及一种采用丙烯酸共聚乳液、颜填料、稀土氧化物、二氧化钛、助剂等通过特殊工艺配制而成的除醛乳胶漆。
背景技术
甲醛是一种无色易溶的刺激性气体，现代医学证明，甲醛对神经系统、免疫系统、肝脏等有害。甲醛还有致畸、致癌作用。据流行病学调查，长期接触甲醛的人，可引起鼻腔、口腔、咽喉、皮肤和消化道等的癌症。
净化生态环境，防止有害气体的侵害，是保护人类生存和健康的最基本条件。但是居住环境的恶化，大量有害气体的产生，己严重威胁着人们的身体健康及生活质量。随着人们生活水平的不断提高，“绿色消费”已深入人心。在家居环境方面，人们不再仅注重美观与时尚，更强调健康环保。随着人们对环境保护和自身健康的日益关注，家庭环境健康化已成为当今的发展趋势。
近年来，国内外对室内环境的净化做了深入的研究，开发生产出了一些空气净化产品，如负离子发生器、负离子添加剂、甲醛清除剂等。负离子发生器是通过电力作用产生负离子；负离子添加剂是将其使用时加入乳胶漆成品中或是作为配方加入乳胶漆体系中，这种负离子添加剂是一种压电材料，可释放负离子；甲醛清除剂是一种强氧化还原剂，只能在板材涂装前使用。
发明内容
本发明的目的在于提供一种除醛乳胶漆，其可以持久高效的清除室内空气中的甲醛、苯、氨、氮氧化物等有害气体，而且具有优异的耐水耐碱性能、易洗耐擦、高遮盖力、防霉防藻、安全环保、无毒无味等特点。
本发明的另一目的在于提供一种除醛乳胶漆的制备方法，其可制备一种无毒无味、安全环保的除醛乳胶漆。
为实现上述目的，本发明提供一种除醛乳胶漆，其组分及含量为：
丙烯酸共聚乳液 20％～30％
聚羧酸盐 0.5％～1.0％
芳烃基聚醚 0.2％～0.5％
钛白粉 10％～25％
填料 25％～35％
消泡剂 0.2％～0.5％
防腐剂 0.2％～0.5％
防霉剂 0.2％～0.5％
增稠剂 0.2％～0.5％
醇酯 1％～2％
pH调节剂 0％～0.2％
除醛制剂 2％～3％
水 余量
所有百分数为重量百分数。
所述除醛制剂的组分及含量为：
稀土氧化物 0.1％～0.2％
二氧化钛 10％～15％
助剂 0.2％～1.0％
乙醇 2％～5％
钠盐 2％～5％
消泡剂 0.2％～0.5％
水 余量
所有百分数为重量百分数。
一种除醛乳胶漆的制备方法，其包括：
(1)、将水、助剂、钠盐、消泡剂进行混合，加入稀土氧化物、二氧化钛，高速分散，低速加入乙醇，以制得除醛制剂；
(2)、将水、聚羧酸盐、芳烃基聚醚、钛白粉、填料、消泡剂进行混合，高速分散至50微米以内；加入防腐剂、防霉剂、醇酯，加入除醛制剂，丙烯酸共聚乳液，中速分散；将pH调至8.0-9.0，调节粘度至95-105KU，过滤包装。
本发明的除醛乳胶漆采用了一种特殊的分散技术，使稀土氧化物、二氧化钛能在水中分散，配制的除醛乳胶漆具有良好的稳定性，除醛效果持久高效，无毒无味，安全环保。本发明产品甲醛清除率24小时可达85％以上，氨气、苯、氮氧化物清除率24小时可达80％以上，本发明产品经检验为无毒，真正实现了居室环境的完全环保。它是到目前为止最为科学可行、安全环保、无毒无味的净化室内空气的乳胶漆。填补了国内外的空白。
具体实施方式
为更进一步阐述本发明为实现预定目的所采取的技术手段及功效，请参阅以下有关本发明的详细说明，相信本发明的目的、特征与特点，应当可由此得到深入且具体的了解。
要配制出一种除醛乳胶漆，除要考虑稀土氧化物、二氧化钛在体系中的稳定性以及它们与其它各组分的相容性外，还必须考虑除醛乳胶漆的各项性能指标符合GB 18582-2001和GB/T 9756-2001两个标准。
为减少超细材料的团聚，应选择特殊作用的分散剂和润湿剂，以提高除醛效果，避免产品的团聚。可供选择的涂料助剂很多，除考虑性能之外，一定要注意其和除醛制剂的相容性，除进行理论上论证外，还必须通过大量试验验证。
本发明的除醛乳胶漆配方包括水、丙烯酸共聚乳液、聚羧酸盐、芳烃基聚醚、钛白粉、填料、除醛制剂、消泡剂、防腐剂、防霉剂、醇酯、pH调节剂、增稠剂，其中各组分的含量为：
丙烯酸共聚乳液 20％～30％
聚羧酸盐 0.5％～1.0％
芳烃基聚醚 0.2％～0.5％
钛白粉 10％～25％
填料 25％～35％
消泡剂 0.2％～0.5％
防腐剂 0.2％～0.5％
防霉剂 0.2％～0.5％
增稠剂 0.2％～0.5％
醇酯 1％～2％
pH调节剂 0％～0.2％
除醛制剂 2％～3％
水 余量
所有百分数为重量百分数。
所述除醛制剂的组分及含量为：
稀土氧化物 0.1％～0.2％
二氧化钛 10％～15％
助剂 0.2％～1.0％
乙醇 2％～5％
钠盐 2％～5％
消泡剂 0.2％～0.5％
水 余量
所有百分数为重量百分数。
本发明的除醛乳胶漆选用去离子水，以提高产品的稳定性。
丙烯酸共聚乳液可选用全丙、苯丙、醋丙或醋叔等。它们在中性和弱碱性环境比较稳定，和除醛制剂成分的相容性也较好，也是目前乳胶漆常用的粘接料。
稀土氧化物可选用氧化铈、氧化锆、氧化锶或其组合等。
钠盐可选用丙烯酸钠盐、羧酸钠盐等。
填料可选用碳酸钙、滑石粉、高岭土、硅酸铝或其组合等。
助剂可选用芳烃基聚醚、改性硅酮等。
增稠剂可选用纤维素、丙烯酸类、聚氨酯类。
pH调节剂可选用氨水或醇胺。
一种除醛乳胶漆的制备方法，其包括：
(1)、将水、助剂、钠盐、消泡剂进行混合，加入稀土氧化物、二氧化钛，高速分散，低速加入乙醇，以制得除醛制剂；
(2)、将水、聚羧酸盐、芳烃基聚醚、钛白粉、填料、消泡剂按上述比例混合，高速分散至50微米以内；加入防腐剂、防霉剂、醇酯，加入除醛制剂，丙烯酸共聚乳液，中速分散均匀；将pH调至8.0-9.0，调节粘度至95～105KU，过滤包装。
采用本发明的配方和生产工艺，原料易得，工艺可控，质量稳定，成本较低；产品具有良好的稳定性，除醛效果持久高效，无毒无味，安全环保。
下面通过不同实施例对本发明除醛乳胶漆及其制备方法作具体说明。
实施例1：
取去离子水15.18Kg、丙烯酸钠盐1.0Kg、芳烃基聚醚0.1Kg、改性硅酮0.1Kg、消泡剂0.1Kg进行混合，加入氧化铈0.02Kg、二氧化钛2.5Kg混合后高速分散，低速加入乙醇1.0Kg，制得除醛制剂。
取去离子水249Kg，聚羧酸盐5Kg，芳烃基聚醚2Kg，钛白粉200Kg，碳酸钙150Kg，滑石粉50Kg，高岭土50Kg，消泡剂3Kg，防腐剂2Kg，防霉剂2Kg，醇酯10Kg，纯丙乳液250Kg，将它们混合分散，加入上述配制好的除醛制剂20Kg，pH调节剂适量，加入羟乙基纤维素2Kg，TT-9355Kg，混合分散，过滤包装，即得到1000Kg本发明的除醛乳胶漆。
实施例2：
取去离子水14.18Kg、丙烯酸钠盐1.5Kg、芳烃基聚醚0.1Kg、改性硅酮0.1Kg、消泡剂0.1Kg进行混合，加入氧化锆0.02Kg、二氧化钛3.0Kg混合后高速分散，低速加入乙醇1.0Kg，制得除醛制剂。
取去离子水297Kg，聚羧酸盐5Kg，芳烃基聚醚2Kg，钛白粉150Kg，碳酸钙200Kg，滑石粉50Kg，硅酸铝50Kg，消泡剂3Kg，防腐剂2Kg，防霉剂2Kg，醇酯10Kg，苯-丙乳液200Kg，将它们混合分散，加入上述配制好的除醛制剂20Kg，pH调节剂适量，加入羟乙基纤维素2Kg，ASE-602Kg、TT-9355Kg，混合分散，过滤包装，即得到1000Kg本发明的除醛乳胶漆。
实施例3：
取去离子水15.67Kg、羧酸钠盐1.0Kg、芳烃基聚醚0.1Kg、改性硅酮0.1Kg、消泡剂0.1Kg进行混合，加入氧化锶0.03Kg、二氧化钛2.0Kg混合后高速分散，低速加入乙醇1.0Kg，制得除醛制剂。
取去离子水297Kg，聚羧酸盐5Kg，芳烃基聚醚2Kg，钛白粉160Kg，碳酸钙190Kg，滑石粉50Kg，高岭土50Kg，消泡剂3Kg，防腐剂2Kg，防霉剂2Kg，醇酯10Kg，醋-丙乳液200Kg，将它们混合分散，加入上述配制好的除醛制剂20Kg，pH调节剂适量，加入羟乙基纤维素2Kg，ASE-602Kg、RM-20205Kg，混合分散，过滤包装，即得到1000Kg本发明的除醛乳胶漆。
本发明产品是采用现代纳米技术及高分子技术研制而成，是一种品质卓越的墙面装饰涂料，能恒久有效地降解板材、布匹等物品释放的游离于室内空气中的甲醛、氨气、苯、氮氧化物等有害气体，同时还具备同类高级墙面漆所具备的完美功能。本发明产品中的稀土氧化物具有催化作用，可将空气中的氧催化成一种净化粒子，这种净化兼具有物理和化学作用。它和一般的负离子乳胶漆和负离子添加剂相比，作用机理不一样，清除甲醛等有害气体效果也更好；和一般的甲醛清除剂相比，甲醛清除剂仅是一次性的，而本发明产品是永久性的；和负离子发生器相比，负离子发生器需要通过电力才能起作用，而本发明产品却不需要。因此本发明产品真正做到了安全环保，将除醛功效和内墙装饰保护于一体，免除人们经常除醛的劳累，一劳永逸，可广泛用于室内涂装。
本发明的除醛乳胶漆采用了一种特殊的分散技术，使稀土氧化物、二氧化钛能在水中分散，配制的除醛乳胶漆具有良好的稳定性，除醛效果持久高效，无毒无味，安全环保。本发明产品甲醛清除率24小时可达85％以上，氨气、苯、氮氧化物清除率24小时可达80％以上，而且本发明产品经检验为无毒，真正实现了居室环境的完全环保。它是到目前为止最为科学可行、安全环保、无毒无味的净化室内空气的乳胶漆。填补了国内外的空白。
以上所述，对于本领域的普通技术人员来说，可以根据本发明的技术方案和技术构思作出其他各种相应的改变和变形，而所有这些改变和变形都应属于本发明的权利要求的保护范围。
Claims (8)
1、一种除醛乳胶漆，其组分及重量百分含量为：
丙烯酸共聚乳液 20％～30％； 聚羧酸盐 0.5％～1.0％；
芳烃基聚醚 0.2％～0.5％；钛白粉 10％～25％；
填料 25％～35％； 消泡剂 0.2％～0.5％；
防腐剂 0.2％～0.5％；防霉剂 0.2％～0.5％；
增稠剂 0.2％～0.5％；醇酯 1％～2％；
pH调节剂 0％～0.2％； 除醛制剂 2％～3％；
水 余量；
其中，
所述填料选用碳酸钙、滑石粉、高岭土、硅酸铝或其组合；
所述除醛制剂的组分及重量百分含量为：
氧化铈、氧化锆或氧化锶 0.1％～0.2％；二氧化钛 10％～15％；
芳烃基聚醚或改性硅酮助剂 0.2％～1.0％；乙醇 2％～5％；
钠盐 2％～5％； 消泡剂 0.2％～0.5％；
水 余量。
2、根据权利要求1所述的除醛乳胶漆，其特征在于，所述丙烯酸共聚乳液选用全丙、苯丙、醋丙或醋叔。
3、根据权利要求1所述的除醛乳胶漆，其特征在于，所述增稠剂选用纤维素、丙烯酸类、聚氨酯类。
4、根据权利要求1所述的除醛乳胶漆，其特征在于，所述pH调节剂选用氨水或醇胺。
5、根据权利要求1所述的除醛乳胶漆，其特征在于，所述水为去离子水，以提高产品的稳定性。
6、根据权利要求1所述的除醛乳胶漆，其特征在于，所述钠盐为羧酸钠盐。
7、根据权利要求6所述的除醛乳胶漆，其特征在于，所述羧酸钠盐为丙烯酸钠盐。
8、一种除醛乳胶漆的制备方法，其包括以下步骤：
(1)将水、助剂、钠盐、消泡剂进行混合，加入：氧化铈或氧化锆或氧化锶中的一种、二氧化钛，高速分散，低速加入乙醇，以制得除醛制剂；其中，所述助剂为芳烃基聚醚或改性硅酮；
(2)将水、聚羧酸盐、芳烃基聚醚、钛白粉、填料、消泡剂进行混合，高速分散至50微米以内；加入防腐剂、防霉剂、醇酯，加入除醛制剂，丙烯酸共聚乳液，中速分散均匀；将pH调至8.0-9.0，调节粘度至95-105KU，过滤包装；其中，所述填料选用碳酸钙、滑石粉、高岭土、硅酸铝或其组合。