CN1912037A - 一种环保墙面漆 - Google Patents
一种环保墙面漆 Download PDFInfo
- Publication number
- CN1912037A CN1912037A CN 200610127348 CN200610127348A CN1912037A CN 1912037 A CN1912037 A CN 1912037A CN 200610127348 CN200610127348 CN 200610127348 CN 200610127348 A CN200610127348 A CN 200610127348A CN 1912037 A CN1912037 A CN 1912037A
- Authority
- CN
- China
- Prior art keywords
- auxiliary agent
- environmental protection
- protection wall
- wall surface
- surface paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及涂料产品技术领域，特指一种具有环保效果的墙面漆。该墙面漆的组成成分以及质量百分比为：水：25％～35％；助剂一：0.4％～7.2％；钛白粉：15％～33％；添加料：10％～49％；助剂二：0.1 5％～0.7％；低VOC乳液15％～35％。制作时，首先将水和助剂一进行分散搅拌，然后加入钛白粉以及添加料，再分散搅拌，混合均匀。接着加入助剂二，继续分散搅拌。最后加入低VOC乳液，然后将上述原料充分搅拌均匀即可。本发明通过选择低VOC的乳液来降低乳胶漆有害物质的含量，同时减少或不加一些有害添加剂，以消除或减少产品中甲醛含量，降低对使用者造成的危害。
Description
技术领域：
本发明涉及涂料产品技术领域，特指一种环保墙面漆。
背景技术：
目前市场上常见的乳胶漆中VOC、游离甲醛的含量都很高，其直接影响了人们的身体健康。特别对于有老人和小孩居住的环境，其危害更大。这是因为VOC是挥发性有机化合物，当居室里VOC超过一定浓度时，在短时间内人们会感到头痛，恶心，呕吐，四肢乏力。VOC伤害人的肝脏，大脑和神经系统，甚至会让人患上白血病等其他严重的疾病。而空气中的甲醛可引起流泪、喉部不适及恶心、呕吐、咳嗽胸闷、哮喘甚至肺气肿等健康隐患。同样，由于乳胶漆中所含有的VOC和游离甲醛，其对油漆涂刷人员的健康也造成直接的损害，因为在施工时，伴随着乳胶漆的干燥，会有大量的VOC和游离甲醛释放出来。所以开发具有环保效果的健康型墙面漆是非常迫切的。
发明内容：
本发明所要解决的技术问题旨在克服现有产品之缺点，提供一种环保墙面漆。
为解决上述技术问题，本发明材料所采用的技术方案为：该墙面漆的组成成分以及质量百分比为：
水：25％～35％； 助剂一：0.4％～7.2％；
钛白粉：15％～33％； 添加料：10％～49％；
助剂二：0.15％～0.7％；
低VOC乳液15％～35％。
上述技术方案中的助剂一包含以下一种或多种：增稠剂、消泡剂、有机胺、分散剂、润湿剂、成膜助剂。通常，各组成成分在产品中的质量百分比为增稠剂0.1％～0.6％、消泡剂0.1％～0.4％、有机胺0％～0.3％、分散剂0.1％～0.5％、润湿剂0％～0.4％、成膜助剂1％～5％。
上述技术方案中添加料包括：高岭土、滑石粉、碳酸钙中的一种或多种。通常添加料中各原料的质量百分比为：高岭土10％～20％、滑石粉0％～9％、碳酸钙0％～20％。
所述的助剂二包括消泡剂和防霉剂。其质量百分比为消泡剂0.1％～0.4％和防霉剂0.05％～0.3％。
制作本发明时，首先将水和助剂一进行分散搅拌，使助剂与水充分混合、溶解，然后加入钛白粉以及添加料，再分散搅拌，混合均匀。接着加入助剂二，继续分散搅拌。最后加入低VOC乳液(可适当加入水调节)，然后将上述原料充分搅拌均匀即可。
本发明通过选择低VOC的乳液来降低乳胶漆有害物质的含量，同时减少或不加一些有害添加剂，如：丙二醇、成膜助剂、含有甲醛的杀菌剂等，这样一来就降低、甚至消除了产品中VOC以及甲醛的含量，不会对使用者造成危害。同样，对于居住在使用本产品涂刷居室中的人的健康也不会造成危害，是一款环保、健康型墙面漆。
具体实施方式：
本发明主要由以下原料构成：
水：25％～35％； 助剂一：0.4％～7.2％；
钛白粉：15％～33％； 添加料：10％～49％；
助剂二：0.15％～0.7％；
低VOC乳液15％～35％。
其中，助剂一的组成成分及质量百分比为：
原料 质量百分比
HEC增稠剂 0.1-0.6％
消泡剂 0.1-0.4％
有机胺 0-0.3％
分散剂 0.1-0.5％
润湿剂 0-0.40％
成膜助剂 1-5％
其中，添加料的组成成分及质量百分比为：
原料 质量百分比
高岭土 10-20％
滑石粉 0-9％
碳酸钙 0-20％
其中，助剂二的组成成分及质量百分比为：
原料 质量百分比
杀菌剂 0.05-0.3％
消泡剂 0.1-0.4％
防霉剂 0.05-0.3％
实施例一
本实施例是本发明的较佳实施例。具体制作过程为：
首先，将水和助剂一混合在一起进行分散，分散的转速为1200转/分钟，时间为5分钟。水和助剂一的质量百分比为：
水30％、增稠剂(羟乙基纤维素)0.45％、消泡剂(脂肪族类)0.2％、有机胺0.2％、分散剂丙烯酸氨盐0.4％、润湿剂(非离子型硅氧烷共聚物)0.35％、成膜助剂醇酯十二1.5％。
接着，向上述混合物中加入钛白粉及添加料，继续分散30分钟，分散的转速仍为1200转/分钟。其中钛白粉和添加料的质量百分比为：钛白粉18％、高岭土14％、滑石粉3.5％、碳酸钙5％。
另外，此步骤中，在加入钛白粉和添加料的同时可加入一定量的杀菌剂(甲基异噻唑啉酮)，以对原料进行杀菌、消毒。杀菌剂一般的含量为0.05～0.3％，本实施例中所加入的杀菌剂的比例为：0.2％。
然后，再加入助剂二，继续以1200转/分钟的转速分散5分钟。助剂二的质量百分比为：消泡剂(脂肪类)0.23％、防霉剂(多菌灵、正辛基异噻唑啉酮)0.2％。
上述再分散过程中，温度应控制在50℃。
最后，加入低VOC乳液和适当的水，进行搅拌，将上述混合物搅拌均匀即可。搅拌时以130转/分钟的转速搅拌15分钟即可。低VOC乳液及水的百分比为：低VOC乳液20％、水5.77％。
本实施例使用时的相关参数为：
| 物性 | 参数 |
| 稀释比例 | 漆∶水＝10∶3 |
| 表干时间(分) | ≤30 |
| 刷涂面积 | 13m2/L/遍 |
| 耐碱(24h) | 无异常 |
| 耐洗刷性(GB、次) | ≥5000 |
| 挥发性有机物的含量(VOC)，g/L | 0 |
| 甲醛含量，mg/kg | 0 |
实施例二：
原料 质量百分比
水 25％
增稠剂(羟乙基纤维素) 0.1％
消泡剂(脂肪族类) 0.3％
AMP 95(有机胺) 0.1％
分散剂(丙烯酸氨盐) 0.3％
润湿剂(非离子型硅氧烷共聚物) 0.4％
成膜助剂(醇酯十二) 2％
钛白粉 15％
高岭土 10％
滑石粉 5％
碳酸钙 10％
杀菌剂(甲基异噻唑啉酮) 0.05％
消泡剂(脂肪族类) 0.4％
防霉剂(多菌灵、正辛基异噻唑啉酮) 0.05％
低VOC乳液 25％
水 6.3％
按照实施例一的制作方法将上述原料制成成品油漆即可。
实施例三
原料 质量百分比
水 35％
增稠剂(羟乙基纤维素) 0.6％
消泡剂(脂肪族类) 0.4％
AMP 95(有机胺) 0.2％
分散剂(丙烯酸氨盐) 0.2％
润湿剂(非离子型硅氧烷共聚物) 0.1％
成膜助剂(醇酯十二) 4％
钛白粉 22％
高岭土 12％
滑石粉 4％
碳酸钙 6％
杀菌剂(甲基异噻唑啉酮) 0.1％
消泡剂(脂肪族类) 0.2％
防霉剂(多菌灵、正辛基异噻唑啉酮) 0.2％
低VOC乳液 15％
按照实施例一的制作方法将上述原料制成成品油漆即可。
Claims (10)
1、一种环保墙面漆，其特征在于：该墙面漆的组成成分以及质量百分比为：
水： 25％～35％； 助剂一：0.4％～7.2％；
钛白粉：15％～33％； 添加料：10％～49％；
助剂二：0.15％～0.7％；
低VOC乳液15％～35％。
2、根据权利要求1所述的一种环保墙面漆，其特征在于：所述的助剂一包含以下一种或多种：增稠剂、消泡剂、有机胺、分散剂、润湿剂、成膜助剂。
3、根据权利要求2所述的一种环保墙面漆，其特征在于：所述的助剂一中各原料的质量百分比为：增稠剂0.1％～0.6％、消泡剂0.1％～0.4％、有机胺0％～0.3％、分散剂0.1％～0.5％、润湿剂0％～0.4％、成膜助剂1％～5％。
4、根据权利要求2所述的一种环保墙面漆，其特征在于：所述的助剂一中的增稠剂为羟乙基纤维素；消泡剂为脂肪族类；分散剂为丙烯酸氨盐；润湿剂为非离子型硅氧烷共聚物；成膜助剂为醇酯十二。
5、根据权利要求1所述的一种环保墙面漆，其特征在于：所述的添加料包括：高岭土、滑石粉、碳酸钙中的一种或多种。
6、根据权利要求5所述的一种环保墙面漆，其特征在于：所述的添加料中各原料的质量百分比为：高岭土10％～20％、滑石粉0％～9％、碳酸钙0％～20％。
7、根据权利要求6所述的一种环保墙面漆，其特征在于：所述的添加料中还包含杀菌剂0.05％～0.3％，且该杀菌剂为甲基异噻唑啉酮。
8、根据权利要求1所述的一种环保墙面漆，其特征在于：所述的助剂二包括消泡剂和防霉剂。
9、根据权利要求8所述的一种环保墙面漆，其特征在于：所述的助剂二中原料的质量百分比为：消泡剂0.1％～0.4％和防霉剂0.05％～0.3％。
10、根据权利要求9所述的一种环保墙面漆，其特征在于：所述的助剂二中的消泡剂为脂肪族类；防霉剂为多菌灵、正辛基异噻唑啉酮。