JPH07103277B2 - Polyolefin resin composition and method for producing sheet comprising the composition - Google Patents
Polyolefin resin composition and method for producing sheet comprising the compositionInfo
- Publication number
- JPH07103277B2 JPH07103277B2 JP3224419A JP22441991A JPH07103277B2 JP H07103277 B2 JPH07103277 B2 JP H07103277B2 JP 3224419 A JP3224419 A JP 3224419A JP 22441991 A JP22441991 A JP 22441991A JP H07103277 B2 JPH07103277 B2 JP H07103277B2
- Authority
- JP
- Japan
- Prior art keywords
- ethylene
- polyolefin resin
- resin composition
- weight
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【０００１】[0001]
【産業上の利用分野】本発明はポリオレフィン樹脂組成
物及びその組成物よりなるシート製造方法に関するもの
である。TECHNICAL FIELD The present invention relates to a polyolefin resin composition and a method for producing a sheet comprising the composition.
【０００２】[0002]
【従来の技術及びその問題点】従来此種のポリオレフィ
ン樹脂の加工は、押出し法，インフレーション法により
フィルム状に加工するものが一般的であった。しかし、
これらの押出し法及びインフレーション法によるもので
は生産吐出量が少なく、幅等の調整が困難であり、しか
もこれらの方法によるとフイルムにダイスのキズ跡及び
目ヤニによる擦れ跡が付きやすい欠点を有するものであ
った。2. Description of the Related Art Conventionally, the processing of this kind of polyolefin resin has generally been carried out by processing into a film by an extrusion method or an inflation method. But,
With these extrusion methods and inflation methods, the production discharge rate is small and it is difficult to adjust the width, etc. Moreover, according to these methods, there are the defects that scratches on the film and scratches due to eye blemishes are easily attached to the film. Met.
【０００３】また、このようなポリオレフィン樹脂を、
生産吐出量も多く、幅等の調整も比較的容易なカレンダ
ー加工することによりシート状に成形するには、(1) ロ
ール面との粘着性（滑性），(2) 耐熱変色，(3) カレン
ダー温度に問題があり、このため従来では金属石ケンな
どを添加して加工していたが、加工できる樹脂はポリオ
レフィン樹脂の中でもエチレンビニルアセテートに限ら
れていた。本発明はこの様にカレンダー加工ができない
とされていたポリオレフィン樹脂組成物をカレンダー適
性の優れたものにせんとするものである。Further, such a polyolefin resin is
To produce a sheet by calendering, which produces a large amount of production and has a relatively easy adjustment of width, etc., (1) Adhesiveness (sliding) with the roll surface, (2) Heat discoloration, (3 ) Since there is a problem with the calender temperature, conventionally, metal soap and the like were added for processing, but the processable resin was limited to ethylene vinyl acetate among the polyolefin resins. The present invention provides a polyolefin resin composition, which has been said to be uncalenderable in this manner, with excellent calendering suitability.
【０００４】[0004]
【解決するための手段】本発明は上記の問題点を解決す
るためになされたもので、その手段はエチレンとアクリ
ル酸エステルまたはメタクリル酸エステルとを共重合し
てなるエチレン系コポリマーの１種 100重量部もしくは
これらエチレン系コポリマーの２種以上のブレンド物 1
00重量部に対して、メタクリル酸エステルを主成分とし
た共重合体からなるアクリル系加工助剤 0.005〜10重量
部を添加すること、およびこれをロール温度が100 〜18
0 ℃でカレンダー加工することである。Means for Solving the Problems The present invention has been made to solve the above problems, and the means is one type of ethylene-based copolymer obtained by copolymerizing ethylene with an acrylic ester or a methacrylic ester. Parts by weight or a blend of two or more of these ethylene-based copolymers 1
To 0.00 parts by weight, 0.005 to 10 parts by weight of an acrylic processing aid consisting of a copolymer containing methacrylic acid ester as a main component is added, and a roll temperature of 100 to 18 is added.
Calendering at 0 ° C.
【０００５】[0005]
【実施例】本発明の実施の一例について説明するに、エ
チレン（ＣＨ2 ＝ＣＨ2 ）とＣＨ2 ＝ＣＲ1 ＣＯＯＲ2
＜Ｒ1 はＨ，ＣＨ3 ，Ｒ2 はアルキル基＞とを共重合し
てなるエチレン系コポリマーは、エチレンメチルメタク
リレート，エチレンエチルアクリレート，エチレンメチ
ルアクリレート，エチレンブチルメタクリレート，エチ
レンヘキシルアクリレート，エチレンラウリルメタクリ
レート，エチレンステアリルアクリレートなどのエチレ
ンと各種アクリル酸エステルまたは各種メタクリル酸エ
ステルよりなるものであり、これらの１種もしくはこれ
らの２種以上のブレンド物に、メタクリル酸エステルを
主成分とした共重合体からなるアクリル系加工助剤を添
加するものであり、その添加量は樹脂 100重量部に対し
て0.005 〜10重量部、好ましくは0.01〜３重量部であ
る。EXAMPLES To explain an example of the practice of the present invention, ethylene (CH 2 ═CH 2 ) and CH 2 ═CR 1 COOR 2
The ethylene copolymer obtained by copolymerizing <R 1 is H, CH 3 , and R 2 is an alkyl group> is ethylene methyl methacrylate, ethylene ethyl acrylate, ethylene methyl acrylate, ethylene butyl methacrylate, ethylene hexyl acrylate, ethylene lauryl methacrylate. , Ethylene stearyl acrylate, etc., and various acrylic acid esters or various methacrylic acid esters, and a copolymer containing methacrylic acid ester as a main component is added to one or a blend of two or more of these. The acrylic processing aid is added in an amount of 0.005 to 10 parts by weight, preferably 0.01 to 3 parts by weight, based on 100 parts by weight of the resin.
【０００６】上記エチレン系コポリマーの１種もしくは
これらの２種以上のブレンド物に添加されるアクリル系
加工助剤はアクリル酸，アクリル酸メチル，アクリル酸
エチル，アクリル酸ｎブチル，アクリル酸イソブチル，
アクリル酸−２−エチルヘキシル等のアクリル酸エステ
ル、メタクリル酸エチル，メタクリル酸ｎブチル，メタ
クリル酸−２−エチルヘキシル等のメタクリル酸エステ
ルを主成分とした共重合体からなる一群の重合体で、具
体的には例えば市販品の三菱レイヨン製のメタブレンP-
700 ，メタブレンP-551 ，メタブレンP-530A，メタブレ
ンL-1000，鐘淵化学工業製のカネエースPA-20 ，カネエ
ースPA-100，旭電化工業製のマークLS-3，マークLS-5等
である。Acrylic processing aids added to one or a blend of two or more of the above ethylene copolymers are acrylic acid, methyl acrylate, ethyl acrylate, n-butyl acrylate, isobutyl acrylate,
A group of polymers consisting of acrylic acid esters such as 2-ethylhexyl acrylate and copolymers containing methacrylic acid esters such as ethyl methacrylate, n-butyl methacrylate, and 2-ethylhexyl methacrylate as main components. For example, a commercially available Mitsubishi Rayon Metabrene P-
700, Metabrene P-551, Metabrene P-530A, Metabrene L-1000, Kane Ace PA-20, Kane Ace PA-100, Asahi Denka Kogyo Mark LS-3, Mark LS-5 etc. .
【０００７】上記エチレン系コポリマーの１種もしくは
これらの２種以上のブレンド物に添加される前記のアク
リル系加工助剤は樹脂100 重量部に対して0.005 〜10重
量部を添加せしめるものであるが、この配合物に、他の
添加物として、エチレンと酢酸ビニルの共重合体，エチ
レン，プロピレン，ブテン，ブテンー１，３ーメチルー
ブテンー１，ヘキセンー１，オクテンー１，４ーメチル
ーペンテンー１等の重合体及び共重合体を主成分とする
もので例えば高密度ポリエチレン，中低密度ポリエチレ
ン，超低密度ポリエチレン，結晶性ポリプロピレン，ポ
リブテンなど及びこれらの混合物からなる他のポリオレ
フィンや金属の高級脂肪酸塩、例えばステアリン酸亜
鉛，ラウリン酸亜鉛，オレイン酸亜鉛，ステアリン酸バ
リウム，ステアリン酸カルシウム，ジブチル錫ラウレー
ト，ジブチル錫ステアレート，ジブチル錫ジラウレー
ト，ジブチル錫ジステアレート等である有機酸系金属
塩、及び例えばステアリン酸，オレイン酸，ラウリン
酸，パルミチン酸などの有機脂肪酸ならびにこの種の技
術分野において周知の帯電防止剤，紫外線吸収剤，抗酸
化剤，顔料，ブロッキング防止剤等を添加することも可
能である。The above-mentioned acrylic processing aid to be added to one of the above ethylene-based copolymers or a blend of two or more thereof may be added in an amount of 0.005 to 10 parts by weight based on 100 parts by weight of the resin. Other additives to the blend are ethylene-vinyl acetate copolymer, ethylene, propylene, butene, butene-1,3-methyl-butene-1, hexene-1, octene-1,4-methyl-pentene-1. Polymers and copolymers such as, for example, high density polyethylene, medium and low density polyethylene, ultra low density polyethylene, crystalline polypropylene, polybutene, etc. and other polyolefins composed of a mixture of these and higher fatty acids of metals Salts such as zinc stearate, zinc laurate, zinc oleate, barium stearate, potassium stearate Organic acid metal salts such as sium, dibutyltin laurate, dibutyltin stearate, dibutyltin dilaurate, dibutyltin distearate, and organic fatty acids such as stearic acid, oleic acid, lauric acid, palmitic acid and the like technical field It is also possible to add antistatic agents, ultraviolet absorbers, antioxidants, pigments, antiblocking agents, etc., which are well known in the art.
【０００８】これらの配合物は、そのコポリマーまたは
これらのブレンド物，メタクリル酸エステルを主成分と
した共重合体からなるアクリル系加工助剤の種類および
添加量によるが、カレンダー加工の適性温度範囲は100
〜180 ℃、好ましくは120 〜170 ℃である。100 ℃以下
の場合は溶融不足のためシート化されず、180 ℃以上の
場合は溶融過多のためロールに付着してロールから剥離
しなくなる。[0008] These blends depend on the kind and the amount of addition of the acrylic processing aid consisting of the copolymer or a blend thereof, and a copolymer containing methacrylic acid as a main component, but the suitable temperature range for calendering is 100
˜180 ° C., preferably 120˜170 ° C. When the temperature is 100 ° C or lower, the sheet is not formed due to insufficient melting, and when the temperature is 180 ° C or higher, the sheet is adhered to the roll and is not peeled off from the roll due to excessive melting.
【０００９】次いで具体的実施例および比較例について
説明するに、 実施例１ エチレンメチルメタクリレート共重合体100 重量部に下
記の表１に示す加工助剤を0.5 重量部添加し、この配合
物を140 ±2 ℃のロール温度でカレンダー加工した場合
のロール滑性の評価を示す。Next, concrete examples and comparative examples will be described. Example 1 0.5 parts by weight of a processing aid shown in Table 1 below was added to 100 parts by weight of ethylene methyl methacrylate copolymer, and the mixture was added to 140 parts by weight. The evaluation of roll lubricity when calendered at a roll temperature of ± 2 ° C is shown.
【００１０】[0010]
【表１】 [Table 1]
【００１１】実施例２ エチレンメチルメタクリレート共重合体100 重量部に，
下記の表２に示す加工助剤を，その添加量，ロール温度
でカレンダー加工した場合のロール滑性とシートの平滑
性の評価を示す。Example 2 100 parts by weight of ethylene methyl methacrylate copolymer was added,
Table 2 below shows evaluations of roll lubricity and sheet smoothness when the processing aids shown in Table 2 below were calendered at the addition amount and roll temperature.
【００１２】[0012]
【表２】 [Table 2]
【００１３】[0013]
【発明の効果】本発明はエチレンとアクリル酸エステル
またはメタクリル酸エステルとを共重合してなるエチレ
ン系コポリマーの１種 100重量部もしくはこれらエチレ
ン系コポリマーの２種以上のブレンド物 100重量部に対
して、メタクリル酸エステルを主成分とした共重合体か
らなるアクリル系加工助剤を0.005 〜10重量部を添加し
てなるから、カレンダー適性の優れたポリオレフィン樹
脂組成物が得られると共に、これをロール温度が100 〜
180 ℃でカレンダー加工することにより幅等を自由に調
整しながらエチレンと各種アクリル酸エステルまたは各
種メタクリル酸エステルとの共重合体樹脂シートを生産
することができる。The present invention is based on 100 parts by weight of one type of ethylene-based copolymer obtained by copolymerizing ethylene with acrylic acid ester or methacrylic acid ester or 100 parts by weight of a blend of two or more types of these ethylene-based copolymers. Then, 0.005 to 10 parts by weight of an acrylic processing aid composed of a copolymer containing methacrylic acid ester as a main component is added, so that it is possible to obtain a polyolefin resin composition having excellent calendering suitability and roll it. Temperature is 100 ~
By carrying out calendering at 180 ° C., a copolymer resin sheet of ethylene and various acrylic acid esters or various methacrylic acid esters can be produced while freely adjusting the width and the like.
Claims (4)
タクリル酸エステルとを共重合してなるエチレン系コポ
リマーの１種 100重量部もしくはこれらエチレン系コポ
リマーの２種以上のブレンド物 100重量部に対して、メ
タクリル酸エステルを主成分とした共重合体からなるア
クリル系加工助剤 0.005〜10重量部を添加してなること
を特徴とするポリオレフィン樹脂組成物。1. Methacrylic acid based on 100 parts by weight of one type of ethylene-based copolymer obtained by copolymerizing ethylene with an acrylic acid ester or methacrylic acid ester or 100 parts by weight of a blend of two or more types of these ethylene-based copolymers. A polyolefin resin composition comprising 0.005 to 10 parts by weight of an acrylic processing aid composed of a copolymer containing an acid ester as a main component.
物を、ロール温度が100 〜180 ℃でカレンダー加工する
ことを特徴とするシートの製造方法。2. A method for producing a sheet, which comprises calendering the polyolefin resin composition according to claim 1 at a roll temperature of 100 to 180 ° C.
エチレンメチルメタクリレート，またはエチレンエチル
アクリレート，もしくはエチレンメチルアクリレートで
あるポリオレフィン樹脂組成物。3. A polyolefin resin composition in which the ethylene-based copolymer according to claim 1 is ethylene methyl methacrylate, ethylene ethyl acrylate, or ethylene methyl acrylate.
エチレンメチルメタクリレート，またはエチレンエチル
アクリレート，もしくはエチレンメチルアクリレートで
あるポリオレフィン樹脂組成物を、ロール温度が100 〜
180 ℃でカレンダー加工することを特徴とするシートの
製造方法。4. A polyolefin resin composition in which the ethylene-based copolymer according to claim 1 is ethylene methyl methacrylate, ethylene ethyl acrylate, or ethylene methyl acrylate, and the roll temperature is 100 to 100.
A method for producing a sheet, which comprises calendering at 180 ° C.