JPS5862093A - 記録媒体 - Google Patents

記録媒体

Info

Publication number
JPS5862093A
JPS5862093A JP56161265A JP16126581A JPS5862093A JP S5862093 A JPS5862093 A JP S5862093A JP 56161265 A JP56161265 A JP 56161265A JP 16126581 A JP16126581 A JP 16126581A JP S5862093 A JPS5862093 A JP S5862093A
Authority
JP
Japan
Prior art keywords
metal
layer
recording medium
recording
organic material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP56161265A
Other languages
English (en)
Inventor
Yasuyuki Goto
康之 後藤
Seiya Ogawa
小川　清也
Nagaaki Etsuno
越野　長明
Hironori Goto
後藤　広則
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Fujitsu Ltd
Original Assignee
Fujitsu Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Fujitsu Ltd filed Critical Fujitsu Ltd
Priority to JP56161265A priority Critical patent/JPS5862093A/ja
Publication of JPS5862093A publication Critical patent/JPS5862093A/ja
Pending legal-status Critical Current

Abstract

(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。

Description

【発明の詳細な説明】 本発明は記録媒体に関し、とくに高す光感度を有する光
ディスクに用いられる記録媒体に関する。
光デイスク用記録媒体（以下記録媒体という）は基板面
上に、記録層として、ビスマス（Ｂｉ）やテルル（Ｔｅ
）のような単体の薄膜を蒸着技術等にょシ形成していた
。そしてこの記録層にレーザビームのような光ビームを
照射して情報の記録、再生を行う。
しかし豐これらの記録媒体では、現在の半導体レーザを
用いて、情報の記録を行うには、感度の点から不十分で
あり、高品位の再生ｔＷ報を得ることが困難であった。
本発明はかかる点に鑑みなされたもので、記録時におい
て十分を感度を有する光デイスク用記録媒体を提供する
ことを目的とする。以下図面を参照しながら本発明の好
ましｂ実施例につｈて説明する。
ｇｔ図は本発明の一実施例構成図であって、ｌはプラス
チック基板、２はテルル（Ｔｅ）層（層厚８關）。
３は、銅フタロシアニン層（層厚ｚｏｗｓＬ　４はテル
ル（Ｔｅ）層（層厚２２ｎ）である。
なおＴｅの融点は４５０°Ｃ９銅フタロシアニンの昇華
点は４００〜４２Ｇ″Ｃである。このような薄膜層は蒸
着技術により容易に形成できる。
第２図Ｃａ）（ｂ）はこのようにして形成された記録媒
体を用いていわゆるエアーサンドイッチ構成とした光デ
ィスクである。
第２図（ａ）Ｔｏ３において、５．６は１対の記録円盤
であってスペーサ７．８を介して対向して配置され、記
録層５ａ、６ａは、これら記録円盤５．６の対向面側に
設けられる。
この光ディスクを用いて、半導体レーザで情報の書込み
、読出しを行なった。光ディスクｉ１８００ｒｐｍで回
転させ、情報を記録したがこの時、レーザノくワーの値
はディスク面上で３．３ｔｎＷ　＊また再生信号のシ偶
値は４０ｄＢであり非常に良質の信号を得九。Ｔｅの代
わりにＢｉ、Ｉｎ、Ｓｅ、Ａ＠、ＩｎＧａ、Ｉｎ８ｎの
ような低融点で低熱伝導性のものを用いてもよい。
また有機材料として銅フタロシアニンの代わりにフルオ
レセインなどの低融点、低沸点あるいは昇華性のもので
あってもよい。
このように情報書込みにおける高感度化の理由は。
書込み時における光ビーム照射による熱によって昇華性
を有する有機材料層の有機材の高蒸発性により金属の溶
融除去が助長されるためと考えられる。
また有４Ｎ　寸書のもつ低熱伝導性もその理由の１つと
して考えられる。
積層構造（Ｃおいては基板領から金属、有機物金属の順
に主成分が分布するものが特に高感度であった。これは
金寓によって有機物を、挾むことによって有機物に効率
よく熱が伝わり、高蒸発性、昇華性が十分発現されたた
めと考えられる。
以上の説明から明らかなように１本発明に係る記録媒体
１−ｔ、記録層として、低融点、低沸点、あるいは昇華
性の有機材料含有層の両側に金属含有層を配した構成で
ちるため、光書込み時の感度が高くなり、半導体レーザ
でも情報の書込み読出しが可能であり、光デイスク装置
が小型になる利点がある。
【図面の簡単な説明】
第１図は９本発明の一実施例構成図、第２図は９本発明
に係る光デイスク構成図である。 １；プラスチック基板、２：テルル層、３；鋼フタロシ
アニン１，４；テルル層。 第　１　図 第　Ｚ　閉

Claims (2)

    【特許請求の範囲】
  1. （１）基板と、該基板上に形成された記録層とを有し。 該記録層に光ビームを照射して情報の書込み、読出しを
    行うようにした記録媒体において、前記記録層は金属お
    よび有機材料とを含み、かつ、＃金属は前記基板側およ
    び前記記鋒層表面側で最も多く、＃記録層中心部では少
    なくなる如く分布し、前記有機材料は、前記中心部で最
    も多く、該中心部両側部では少なくなる如く分布せしめ
    たことを特徴とする記録媒体。
  2. （２）前記金属が低融点、低熱伝導性を有するものであ
    り、前記有機材料が低融点、低沸点、又は高昇華性を有
    するものであることを特徴とする特許請求の範囲第（１
    ）項に記載の記録媒体。
JP56161265A 1981-10-09 1981-10-09 記録媒体 Pending JPS5862093A (ja)