WO1987002910A1

WO1987002910A1 - Silica-titania hydrocarbon conversion catalyst

Info

Publication number: WO1987002910A1
Application number: PCT/US1986/002076
Authority: WO
Inventors: Leonard A. Cullo; Francis J. Shiring, Iii
Original assignee: USS Engineers and Consultants Inc
Current assignee: USS Engineers and Consultants Inc
Priority date: 1985-11-08
Filing date: 1986-10-06
Publication date: 1987-05-21
Anticipated expiration: 1988-05-08
Also published as: US4711869A; EP0246272B1; JPS62114656A; CA1279633C; JPH0542299B2; US4814531A; DE3673813D1; EP0246272A1

Abstract

Crystalline silica-titania catalyst compositions, optionally containing magnesium; the titanium is introduced through the use of organo-titanate chelates wherein the titanium has a coordination number of at least 5. The compositions are used in acid-catalyzed reactions such as alkylation reactions.

Description

SILICA-TITANIA HYDROCARBON CONVERSION CATALYST

Technical Field

This invention relates to crystalline silica-titania composite zeolite materials, optionally containing magnesium also in the crystalline structure, and their use as catalysts in hydrocarbon conversion reactions requiring acidic conditions for catalysis. The materials also exhibit shape-selective catalytic behavior as a function of their regular, fine pore structure. In general, molecules with effective kinetic diameters of less than 7-8 angstroms will have ready access to the internal catalytic sites and molecules having greater effective kinetic diameters will be excluded. Our catalyst material may contain up to about 10.0% magnesium as MgO.

Such catalysts represent significant advantages over prior art catalysts for acid catalyzed reactions, particularly those involving substituted or unsubstituted monoaromatic molecules. Reactions such as alkylation, dehydration, isomer ization, dispropor tionation and cracking can be effectively catalyzed. Our new material is also proposed as a support for other catalytic materials having catalytic functions, such as vanadium and noble metals, where the beneficial strong-metal support-interaction properties of titania are realized. Prior to the present invention, the use of titanium in hyrocarbon conversion catalysts has been most commonly proposed only as an adjunct to a pre-formed silicalite or pre-formed silica-alumina catalyst such as those of the ZSM series. See USP 4,358,397 as an example. The distribution of titanium-containing compounds on the structure of a pre-formed crystalline material, such as in USP 4,358,397, typically involves minimal, if any, chemical reaction of the titanium with the crystal lattice of the catalyst, the manufacturing technique usually comprising primarily a physical distribution of discrete moieties of the titanium compound throughout the labyrinthine structure in a more or less uneven manner.

More recently, Taramasso et al, in USP 4,410,501, have disclosed a crystalline material comprising silicon oxide and titanium σxide; it is, however, made using only rapidly hydrolyzable titanium compounds and primarily for this reason has a crystal structure different from ours, as explained further herein. The European patent application No. 84106366.2 filed June 4, 1984 by Norton Company for Saleh employs soluble hydrated titanates, specifically NaTiO₃H, with a silica sol for autoclaving, said to produce a crystalline molecular sieve of silicon, titanium, and oxygen. See also USP 4,396,783, disclosing a "titanium silicalite" prepared with the use of tetraethyltitanate, and suggesting other rapidly hydrolyzable titanium compounds.

Our invention differs from these specifications, inter alia, in that we employ hydrolysis-resistant chelates of titanium-bearing compounds, wherein the titanium has a coordination number of at least 5, giving rise to a unique distribution of titanium in the dried and calcined product.

The reader may also be interested in reviewing USP 4,500,651 suggesting broadly the use of "titanium chelates" to make certain phosphorous and aluminum-containing molecular sieves and employing specifically titanium acetylacetonate.

Disclosure of Invention

We have invented certain new crystalline catalysts containing silicon, titanium, and, optionally, magnesium; methods of making them, and methods of performing certain hydrocarbon conversion r eactions with them.

Expressed in terms of moles of oxides, our new compositions comprise 0.015 to 0.040 TiO₂:1 SiO₂ together with up to 0.17 mole MgO. As has become known in the art, it is extremely difficult to completely exclude alumina and, although we prefer lesser amounts, we can tolerate up to about 1000 or more ppm Al₂O₃ in our composite.

In the method of preparation of our composition, a titanium-containing organo-metallic compound resistant to hydrolysis is added directly to the catalyst synthate, rather than impregnating or depositing a titanium-containing compound on a silica rich substrate as in certain prior art processes such as those described in USP 4,358,397.

Most titanium salts and organic titanium compounds are subject to hydrolysis upon exposure to water or moist air. These compounds are not useful in the preparation of the catalyst of this invention. However, the triethanolamine chelate, acetylacetonate chelate and the ammonium salts of the lactic acid chelates are more resistant to hydrolysis. This enables them to be added to the aqueous synthesis mixture of the catalyst of this invention, and under hydrothermal conditions the mixture will yield a crystalline material with a uniform titanium distribution unobtainable with conventional impregnation methods. The lactic acid chelates of titanium have commonly been used as esterification, polymerization, and crosslinking catalysts, and are commercially available from DuPont among the "Tyzor" series of organic titanates. More generally, we may use any organo-titanate chelate. Thus, we employ lactic acid ammonium salt chelate, trialkanolamine chelates or the β-dicarboxyl chelates, rather than titanium alkoxides, or other more hydrolyzable titanium compounds.

A preferred process for preparation of the catalyst of this invention comprises:

1. Combining one part of an aqueous sodium silicate solution containing about 12% to about 13% SiO₂, at a SiO₂ to Na₂O weight ratio of about

3.22 with 0.94 parts of a second, clear aqueous solution of an organo-titanate chelate containing 0.18 to 0.32% titanium as TiO₂ and wherein the titanium has a coordination number of at least 5, 0.24 to 0.26 gram-equivalents per liter of a tetra-alkyl ammonium halide or hydroxide, up to 0.12 (preferably about 0.06 to about 0.12) gram-equivalents per liter of a magnesium salt, and about 3.3 to about 3.5 gramequivalents per liter of sodium chloride, to form a gel.

2. Crystallizing the gel formed in (1.) under extended hydrothermal treatment, i.e. 150-200°C. for 2-6 days at autogenous pressure. 3. Following hydrothermal treatment, the crystalline product is recovered by filtration and washed prior to drying and calcination at 150°C. and 580°C, respectively.

4. The calcined material is treated with an aqueous solution of ammonium salt to remove residual sodium and recalcined to give the desired catalytic form.

The unique feature of this invention is the introduction of a titanium-containing compound directly into the synthate by the vehicle of a hydrolyis resistant chelate, which gives rise to a unique distribution of titania and the resultant useful catalytic properties of this material.

Following are several examples of the preparation of the catalysts of our invention.

Example I

A solution ( I ) was made of 185. 2 g sodium s il icate ( "N" brand containing 28.7% SiO₂) and 230.2 g deionized water. Another solution (II) was prepared of 311.3 g deionized water, 24.2 g tetrapropyl ammonium bromide, 69.1 g sodium chloride, 9.00 g "Tyzor LA", an ammonia salt of a lactic acid chelate of titanium VI made by DuPont, and 32.36 g MgCl₂.6H₂O. The two solutions were mixed well together by adding them simultaneously to a flask and stirring for 15 minutes. The mixture, including the precipitate formed, was placed in a 600 ml Teflon beaker in an autoclave.

The initial temperature set point was 230°C. and was reset at 226 about 19-1/2 hours later and kept there for another 71 hours. Thermocouple measurements in the flask ranged from 180-182°C. throughout; the pressure ranged from 140-150 psig. The material was dried at 150°C. for three days and calcined at 550°C. for 16 hours. The recovered material had an X-ray diffraction pattern characterized in the following Table I.A.

The washed and calcined catalysts were examined by scanning electron microscopy ( SEM ) . An Etec SEM, with electron beam control by a Tracor Northern computer, was used to analyze particle-byparticle the microtomed magnesium-titanium-silicon distributions. A 20 kV accelerating voltage was used, and with digital electron beam control an energy dispersive X-ray spectrometer gave accurate elemental compositional data for the individual scan points across a given particle. Sample preparation involved the disperson of a 15-30 micron powder on a polycarbonate membrane filter. The data is presented as a table (I.B.) of relative composition versus weight distribution of each particle analyzed. The narrow weight distributions observed are indicative of the uniform nature of the catalyst composition described in the following Table I.B.

Example II

A solution (I) containing 181.56 g sodium silicate ("N" brand) and 223.6 g deionized water was added to a flask simultaneously with a solution of 310.2 g deionized water, 23.03 g tetrapropyl ammonium bromide, 33.6 g MgCl₂.6H₂O, 68.21 sodium chloride and 17.8 g "Tyzor LA", mixed and stirred well to disperse the precipitate, and placed in the autoclave in a 600 ml flask.

Initial temperature set point was 230°C; this was maintained at 230-232°C. for about 63 hours. Measured temperatures ranged from 178°C. to 180°C, and the pressure was 120-125 psig. The material was dried at 150°C. for 16 hours, and calcined at 580°C. for 16 hours.

The calcined ma'terial was subjected to further treatment by a three-step ion exchange procedure with a 5% aqueous ammonium chloride solution at 80-90°C for 90 minutes each, and washing to remove residual chloride and drying before calcination at 580°C for 16 hours.

The X-ray diffraction pattern of this material is shown in Table II.A.

A mass distribution analysis by SEM/EDX (the method described in connection with Example I) again shows an even distribution of titanium throughout.

Example III

A solution of 182.25 g of "N" brand sodium silicate and 235.00 g of deionized water was prepared. A second solution of 23.37 g of tetrapropylammonium bromide, 17.63 g of magnesium chloride hexahydrate, 68.22 g of sodium chloride, 9.49 g Tyzor LA and 308.99 g of deionized water was mixed until clear. Both solutions were added simultaneously to a container, and the resultant slurry was stirred vigorously for 15 minutes. This mixture was placed in an autoclave and allowed to crystallize for 63 hours at 182-184ºC, and autogeneous pressure.

The material was recovered by filtration and washed with deionized water. After drying at 150ºC and calcination for 16 hours at 580°C, the material was subjected to powder X-ray diffraction analysis. This data is presented in Table III.A. Compositional analysis by SEM/EDX is provided in Table III.B.

Further treatment included a three-step ion exchange procedure with a 5% aqueous ammonium chloride solution at 80-90ºC for 90 minutes each, and washing to remove residual chloride and drying before calcination at 580ºC for 16 hours.

The following table recites the ingredients of several similar examples.

Examples

Solution I Solution II Na DI DI MgCl Silicate Water Water TPABr 6H₂O NaCl Ti Ex. (q) (q) (q) (q) (q) (q) cpd (g)

IV 182.76 224.80 311.53 23.75 33.76 68.63 10.89 Tyzor TE

V 180.87 223.50 310.25 23.62 33.98 68.30 35.63 Tyzor LA

VI 183.09 223.10 308.30 23.36 17.49 68.80 22.20 Tyzor TE

VII 181.24 224.40 310.00 22.10 --- 69.10 15.59 Tyzor LA

VIII 181.62 225.40 310.70 22.40 --- 68.19 16.90 Tyzor LA

An X-ray diffraction data for Example IV is presented in Table IV.A.

We have found that chelates of titanium compounds wherein the titanium has a coordination number of at least 5 are superior to those of less than 5.

In Table V is shown data obtained over a nominal 2.2% TiO₂, 10% magnesia-silica catalyst of this invention (made by the process of Example II) for the alkylation of toluene with ethylene. Note that the para-isomer, the more valuable form, is the dominant species and is obtained in concentrations considerably in excess of the equilibrium value. Conditions for the collection of these data were 400°C, atmosphere pressure, vapor phase and WHSV (weight hourly space velocity) =1.0 g feed/g cat/hr.

Significant activity of this catalyst for the alkylation of benzene with isopropanol, alkylation of phenol with methanol and dehydration of isopropanol to propylene has also been observed.

Example IX A catalyst of this invention was prepared according to Example IV. The ammonium chloride washed and calcined version of this catalyst was tested for its ability to catalyze acid catalyzed hydrocarbon conversion reactions, specifically the vapor phase alkylation of toluene with ethylene at 400ºC. and atmospheric pressure. The alkylations were carried out in a microcatalytic activity test reactor which used about 0.5-1.0 gm of powdered catalyst. Reagent grade toluene was vaporized in a stream of nitrogen and mixed with a stream of ethylene, both under mass flow control. This vapor mixture was passed over the catalyst sample in a stainless steel tube, which was submerged in an electrically heated, agitated solder bath. The reactor efflent was condensed in a water cooled coil , and the l iquid product was collected over a 6-16 hour period and analyzed by gas chromatography. Off-gas was measured with a wet test meter. At a toluene to ethylene ratio of 2.3:1.0 nitrogen as a carrier, and a feed rate of 1.0 gm toluene/gm catalyst/hour a typical liquid product analysis was:

toluene 54.5% ortho-ethyltoluene <0.1% meta-ethyltoluene 17.4% para-ethyltoluene 27.1% other aromatics (benzene, xylenes, 0.6% ethylbenzene) heavies and polyalkylates 0.4%

Example X A sample of the catalyst prepared and treated as in Example I of this patent was nixed with acetic acid digested Catapal SB alumina , and pressed into 1/16 " extrudates. After drying at 150°C, and calcining at 550°C. for six hours, the catalyst had about 10% by weight Al₂O₃. The extruded catalyst was placed in a 1" OD stainless steel tube reactor, heated by an electric furnace. A preheat section packed with ceramic saddles was used in the first section of the packed bed. After purging with nitrogen at 300°C. and pressurizing to 150 psig, reagent grade isopropanol was pumped through a vaporizer. This vapor was passed downward over the heated bed. Approximately 43 gms/hour of this feed over 44 gms of catalyst produced a weight hourly space velocity of 0.98 gms feed/gms catalyst/hour. A water cooled condenser was used to recover liquid product over a six to eight hour period, and a wet test meter was used to measure gaseous product rate. After twelve hours of operation, liquid and gaseous samples were analyzed by conventional gas chromatography and are tabulated below. This corresponds to 82.2% conversion of isopropanol, and a 92.2% selectivity to propylene. Catalyst activity remained fairly constant over 3 to 5 days of operation.

Liquid Gas propylene 0.91% 93.0% di-isopropyl ether 5.43% 6.1% isopropanol 73.35% — benzene and other 0.50% 0.9% aromatics water 19.8% —

Example XI A representative catalyst of this invention prepared according to Example III contained 4.1% magnesium at MgO and 2.8% titania as TiO₂ after washing with 5% NH₄Cl at 80ºC, dried and then calcined at 550°C. for 16 hours. Approximately 500 mg of the powdered catalyst was loaded into a 1/4" stainless steel tube reactor and placed in an electrically heated solder bath. After purging with nitrogen the system was allowed to stabilize for one hour at 375ºC. Phenol and methanol were vaporized separately in 2 streams of nitrogen under mass flow control, and introduced into the tube reactor at a weight hourly space velocity of 0.5 gm of liquid feed (methanol plus phenol) per gram of catalyst per hour, at atmospheric pressure. An on-line gas chromatograph was used to verify feed composition; and a condensed liquid product was collected over a sixteen-hour period and analyzed by capillary GC . The product analysis method employed a derivitization technique which formed the trimethyl silyl ethers of the creosols and phenol. This was done to more readily identify specific creosol and xylenol isomers. Average conversion and selectivity was 14.7% and 66% to 2,6 xylenol, respectively. O-creosol and

2,3,6-trimethylphenol were the major by-products.

Claims

1. Method of making a catalyst useful in hydrocarbon conversion reactions comprising

(a) combining about one part of an aqueous sodium silicate solution containing about 12% to about 13% SiO₂, at a SiO₂ to Na₂O weight ratio of about 3.22 with about 0.94 parts of a second, clear aqueous solution of an organo-titanate chelate containing 0.18 to 0.32% titanium as TiO₂ and wherein the titanium has a coordination number of at least 5, 0.24 to 0.26 gram-equivalents per liter of a tetra-alkyl ammonium halide or hydroxide, up to 0.12 (preferably about 0.06 to about 0.12) gram-equivalents per liter of a magnesium salt, and about 3.3 to about 3.5 gram-equivalents per liter of sodium chloride, to form a gel, (b) crystallizing the gel by extended hydrothermal treatment, (c) washing the crystallized gel, (d) calcining the washed crystallized gel, and (e) removing residual alkali metal therefrom.

2. Method of claim 1 wherein the titanium compound solution comprises 0.2 to 0.5% Ti as TiO₂.

3. Method of claim 1 wherein the titanium solution also contains from 0.06 to 0.12 gram-equivalents per liter of a magnesium salt.

4. A calcined crystalline titania-magnesiasilica catalyst having a molar ratio of 0.015 to 0.04 TiO₂:1.0 SiO₂ and an X-ray diffraction pattern characterized by peaks as follows: 2θ d(A) I/Io x100

7 . 75 11.39 49

8 .30 10.64 13

8 .70 10.16 100

13 .70 6.46 13

5. A calcined crystalline titania-magnesiasilica catalyst having molar ratios of 0.015 to 0.04 TiO₂:1.0 SiO₂ and 0.08 to 0.17 MgO, and an X-ray diffraction pattern characterized by peaks as follows:

2θ d(A) I/Io x100

7.90 11.18 31

8.80 10.04 20

20.70 4.29 17

21.90 4.06 100

6. Method of claim 1 wherein the organo-titanate chelate is a lactic acid chelate of titanium VI.

7. Method of claim 1 wherein the organo-titanate chelate is the triethanolamine chelate of titanium.

8. A calcined crystalline titania-magnesiasilica catalyst having the molar ratios 0.015 to 0.04 TiO₂, and 0.08 to 0.17 MgO to 1.0 SiO₂.

9. Method of conducting hydrocarbon alkylation reactions comprising conducting such reactions in the presence of a catalyst of claim 4.

10. Method of converting isopropanol to propylene comprising dehydrating said isopropanol in the presence of a catalyst of claim 4.

11. Method of methylating phenol comprising reacting phenol and methanol in the presence of a catalyst of claim 8.

12. Method of alkylating toluene with ethylene comprising reacting toluene and ethylene in the presence of a catalyst of claim 8.

13. Method of conducting acid catalyzed reactions comprising conducting such reactions in the presence of a calcined crystalline titania-magnesiasilica catalyst having molar ratios of 0.015 to 0.04 TiO₂:1.0 SiO₂ and up to 0.17 MgO, and an X-ray diffraction pattern characterized by peaks as follows:

2θ d(A) I/Io X100

7.75 11.39 49

8.30 10.64 13

8.70 10.16 100

13.70 6.46 13

14. Method of conducting an acid catalyzed reaction comprising conducting such reaction in the presence of a calcined crystalline titania-magnesiasilica catalyst having the molar ratios 0.015 to 0.04 TiO₂ and 0.08 to 0.17 MgO to 1.0 SiO₂.

15. Method of claim 14 wherein the reaction is an alkylation reaction.

16. Method of claim 14 wherein the reaction is a dehydration reaction.

17. Method of claim 14 wherein the reaction is an isomer ization.

18. Method of claim 14 wherein the reaction is a dispropor tionation reaction.

19. A calcined crystalline titania-magnesiasilica catalyst composition having an X-ray diffraction pattern characterized by peaks as follows:

2θ d(A) I/Io x100

8 .0 11.04 25

8 .95 9.87 100

17 .9 4.95 24

23 .15 3.84 42

20. In a method of making a titanium-containing silica-based catalyst composition wherein a silica solution and a titanium-containing solution are combined, dried and calcined, the improvement comprising employing as the titanium-containing component an organo-titanate chelate wherein the titanium has a coordination number of at least 5.

21. Method of ethylating toluene comprising reacting ethylene and toluene under ethylating conditions in the presence of a catalyst made by drying and calcining an aqueous mixture of sodium silicate, magnesium chloride and tetra-alkyl ammonium bromide solutions with a solution of an ammonium salt of a lactic acid chelate of titanium VI, and having the following X-ray peaks:

% Titanium Mass % of Particles

0-2 5.0

2-4 2.7

4-6 19.3

6-8 50.0