WO1991003518A1

WO1991003518A1 - Formulation for extrudable vinylidene chloride copolymers having high barrier properties

Info

Publication number: WO1991003518A1
Application number: PCT/US1990/004851
Authority: WO
Inventors: John A. Naumovitz; Steven R. Jenkins; Mark J. Hall; Stephen R. Betso
Original assignee: Dow Chemical Co
Current assignee: Dow Chemical Co
Priority date: 1989-09-01
Filing date: 1990-08-27
Publication date: 1991-03-21
Anticipated expiration: 1992-03-01
Also published as: EP0441945B1; KR920701328A; CA2024495C; KR0159036B1; JP3179478B2; HK1008430A1; EP0441945A1; JPH04501580A; AU636663B2; AU6402190A; DE69032322D1; EP0441945A4; CA2024495A1; US5002989A; DE69032322T2

Abstract

The present invention is a formulated barrier composition containing tetrasodium pyrophosphate or magnesium hydroxide, high density polyethylene, epoxidized vegetable oil, oxidized polyolefin and a parraffin or polyolefin wax. The composition has a substantially lower oxygen permeability than existing compositions and is at least equally extrudable.

Description

FORMULATION FOR EXTRUDABLE VINYLIDENE CHLORIDE COPOLYMERS HAVING HIGH BARRIER PROPERTIES

The present invention relates to the art of poly(vinylidene chloride) copolymers and formulations for the extrusion thereof.

Copolymers of vinylidene chloride and vinyl chloride or methyl acrylate are known to be useful as barrier polymers. Extruded and coextruded shaped arti¬ cles, such as films, containing a barrier layer of co¬ polymer having from 80 to 98 percent vinylidene chloride provide excellent barrier with respect to transportation of oxygen, water, carbon dioxide and flavoring for food, medical and other high barrier packaging. Vinylidene chloride copolymers and their uses are described in num¬ erous references, such as R. A. Wessling, Polyvinylidene Chloride (Gordon & Breach Sci. Pub. 1977) and 23 Ency. Chem. Tech., Vinylidene Chloride and Poly(Vinylidene Chloride), 76*4 (J. Wiley & Sons 1983).

Vinylidene chloride copolymers are susceptible to thermal degradation during extrusion. That degrada- tion causes specks of carbonaceous material to appear in the extruded product. The level of carbonaceous mate- rial ordinarily increases at higher extrusion rates, which produce higher temperatures in the polymer. Car¬ bonaceous material is unsightly and may cause the cus¬ tomer of the extruded product to reject the product. A variety of additives have been added to vinylidene chlo¬ ride copolymers to help control thermal degradation and permit extrusion at higher rates. See, e.g., R. A. Wessling, Polyvinylidene Chloride at 174-76, and John¬ son, Process for Imparting Stability to Particulate

10 Vinylidene Chloride Polymer Resins, U.S. Patent •4,*418,168 (November 29, 1983). For instance, some commercially available vinylidene chloride copolymer resins contain stabilizing amounts of tetrasodium -.j- pyrophosphate and epoxidized soybean oil. Resins containing those additives have been shown to provide containers having a barrier to oxygen of 0.065 to 0.15 Dow Units, with an average of about 0.10 Dow Units. One Dow Unit (D.U.) equals 0

(1 cm3 of 02 at S.T.P.)(1 mil thickness PVDC) (100 in. area)(1 atm. pressure)(24 hr.) 5

Vinylidene chloride copolymer compositions having higher barrier properties and equal or better extrudability would be more economical than current

30 resins, because equivalent barrier could be obtained in extruded or coextruded products using a lesser amount of barrier resin. What are needed are extrudable and coextrudable vinylidene chloride copolymer compositions which provide improved barrier properties.

35 One aspect of the present invention is a formu¬ lated barrier composition in powder form comprising:

1. a copolymer of vinylidene chloride and a comonomer chosen from the group con¬ sisting of:

(a) 10 to 20 weight percent vinyl chloride;

(b) 4 to 10 weight percent alkyl acrylate; or

(c) a mixture of those comonomers; and

2. a mixture of additives having the following weight concentration per hundred parts of vinylidene chloride copolymer:

(a) an amount of inorganic sta¬ bilizer no greater than about 1.1 parts which is effective to stabilize the formulated barrier composition;

(b) 0.45 to 1.05 parts high density polyethylene;

(c) 0.8 to 1.0 part epoxidized vegetable oil; 5 (d) 0.05 to 0.25 part oxidized polyolefin; and

(e) 0.20 to 0.55 part paraffin or polyethylene Λax.

A second aspect of the present invention is an additive composition comprising, in the following weight ratios:

_c (a) an amount of inorganic stabilizer no greater than about 1.1 parts which is effective to stabilize a formulated barrier composition containing primarily vinylidene chloride-containing copolymer;

(b) 0.45 to 1.05 parts high density polyethylene;

(c) up to 1.0 part epoxidized vegetable oil, chosen such that the total concentra¬ tion when added to a vinylidene chloride copolymer containing one of those compounds will be 0.8 to 1.0 part epoxidized vegetable oil;

(d) 0.05 to 0.25 part oxidized poly¬ olefin; and

(e) 0.2 to 0.55 part paraffin or poly¬ ethylene wax.

A third aspect of the present invention is a multi-layer article containing a barrier layer which comprises the product of a formulated barrier compo¬ sition of the present invention.

Additive compositions of the present invention can be used to make formulated barrier compositions of the present invention. The formulated barrier compo¬ sitions provide an extruded or coextruded article having a barrier superior to the barrier of existing extruded and coextruded vinylidene chloride products.

Formulated barrier compositions of the present invention comprise a vinylidene chloride copolymer, an inorganic stabilizer, high density polyethylene (HDPE) , epoxidized vegetable oil, oxidized polyolefin and paraf- fin or polyethylene wax. The major component is vinyli¬ dene chloride copolymer. The minor components are in an amount suitable to provide a composition which has good extrudability and has high barrier with respect to oxy¬ gen and other permeants.

Vinylidene chloride copolymers suitable for use in the present invention are those vinylidene chloride copolymers formed from a monomer mixture of vinylidene chloride monomer and a comonomer which is vinyl chloride or an alkyl acrylate. The alkyl acrylates are generally selected to have from about 1 to about 8 carbon atoms per alkyl group. Preferably, alkyl acrylates are selected to have from 1 to 4 carbon atoms per alkyl group. The alkyl acrylate is more preferably ethyl or methyl acrylate. The comonomer is most preferably methyl acrylate. Of course, vinylidene chloride copolymers useful in formulated barrier compositions may also contain small amounts (usually less than 1 to 2 percent) of other ethylenically-unsaturated monomers which do not substantially reduce the extrudability or increase the permeability of the copolymer.

The amount of vinyl chloride or alkyl acrylate comonomer in the copolymer is low enough to preserve the semicrystalline character of the copolymer and high enough to provide a commercially extrudable polymer. By "semicrystalline character" it is meant that the copoly¬ mer has between 5 percent and 95 percent crystallinity. Crystallinity values depend upon the measuring technique, and as used herein crystallinity is defined by the commonly used density method. See, for example, the discussion by R. Wessling, in Chapter 6 of Polyvinylidene Chloride, Vol. 5, Gordon and Breach Science Publishers, New York, 1977, the teachings of.

Vinyl chloride comonomer is preferably at least about 10 percent and more preferably at least about 12 percent of the copolymer; it is preferably at most about 20 percent and more preferably at most about 17 percent of the copolymer. Methyl acrylate comonomer is preferably at least about 4 percent and most preferably at least about 6 percent of the resulting copolymer; it is preferably at most about 8 percent and more preferably at most about 6 percent of the resulting copolymer. The vinylidene chloride copolymer is most preferably a 6

10 percent methyl acrylate copolymer.

Vinylidene chloride copolymers are known and are commercially available. Methods to synthesize them,

_._£- such as by an emulsion or suspension polymerization pro¬ cess, are also familiar to persons of ordinary skill in the art. The copolymers and processes to synthesize them are described in U.S. Patents 2,558,728; 3,007,903; 3,642,743; and 3,879,359; in R. A. Wessling, Polyvinyl- 0 idene Chloride, supra, at 21-33 and 44-53; in 23 Ency. Poly Sci, supra, at 783-87; and in Yen et al., Barrier Resins, Report No. 179 of SRI International Process Economics Program 55-106 (February 1986). Typically, the monomeric materials are emulsified or suspended in 5 an aqueous phase. The aqueous phase contains a polymerization initiator and a surface active agent capable of emulsifying or suspending the monomeric materials in the aqueous phase. The polymerization of

30 the monomeric materials is usually carried out with heating and agitation. After polymerization is complete, the resulting suspension or emulsion slurry of vinylidene chloride copolymer has a majority of an aqueous phase. The resultant slurry is vacuum stripped.

35 Thereafter, the slurry is cooled down, unloaded and dewatered, and the resin is collected and further dried. The vinylidene chloride copolymer and the for¬ mulated barrier composition are in powder form prior to extrusion. The vinylidene chloride copolymer preferably has an average particle size no larger than about 300 microns diameter and no smaller than about 100 microns diameter. It preferably contains not more than about 5 percent particles having a particle diameter greater than 425 microns.

The additives used in compositions of the pres¬ ent invention may be individually added and blended with the vinylidene chloride copolymer; or may be blended concurrently with the vinylidene chloride copolymer, such as by physically blending the vinylidene chloride copolymer with an additive composition which has been separately prepared. Such additive compositions make up the second aspect of the present invention. They com¬ prise the same additives as the polymer compositions described herein. The additives will ordinarily be in about the same weight ratios with respect to each other as are found in the formulated barrier composition. However, the inorganic stabilizer and/or the epoxidized vegetable oil may be in a lesser proportion to make up for quantities of those additives already found in the base resin.

Additives should be blended with the vinylidene chloride copolymer to form a formulated barrier composi¬ tion of the present invention before extrusion or melt- -phase processing of the vinylidene chloride copolymer. The additives are blended with the vinylidene chloride copolymer by any method which is effective to achieve substantially homogeneous dispersion of the additives without unduly heating the resin. Blending of the vinylidene chloride copolymer and the formulation pack¬ age can be accomplished by conventional dry blending techniques. It preferably uses high intensity blending. Suitable dry blending equipment includes Hobart mixers, Welex mixers and Henschel High Intensity mixers.

Compositions of the present invention contain an inorganic stabilizer. The inorganic stabilizer is preferably tetrasodium pyrophosphate (TSPP) or magnesium hydroxide (Mg(0H)₂) or an equivalent thereof. Examples of other suitable inorganic stabilizers may include mag¬ nesium oxide, calcium hydroxide, and potassium pyrophos¬ phate, and other inorganic stabilizers disclosed in Johnson, Process for Imparting Stability to Particulate Vinylidene Chloride Polymer Resins, U.S. Patent 4,418,168 (November 29, 1983). Inorganic stabilizers are known compounds which are commercially available. Both TSPP and Mg(0H)₂ can be synthesized by known processes, such as those described in The Merck Index, 10th Edition, (1983). The composition preferably comprises TSPP.

The inorganic stabilizer preferably has an average particle diameter no larger than the average particle diameter of the vinylidene chloride copolymer. Persons skilled in the art will recognize that the effectiveness of the inorganic stabilizer is generally related to the surface area of the stabilizer employed. For purposes of this invention, the TSPP or Mg(0H)2 beneficially has an average particle diameter of from about 1 to about 50 microns. One skilled in the art, without undue experimentation, will be able to determine the optimum particle size for specific additives. The concentration of inorganic stabilizer is no more than about 1.1 parts per hundred (resin), and pref¬ erably no more than about 1.0 part per hundred (resin). (For the purposes of this Application, the term "parts per hundred (resin)" shall mean parts of additive per 100 parts of vinylidene chloride copolymer, by weight.) The specific weight ratios for optimum performance vary with different stabilizers. The concentration of TSPP in the formulated barrier composition is more preferably between 0.7 and 0.9 part per hundred (resin). Its con¬ centration is most preferably about 0.8 part per hundred (resin). The concentration of Mg(0H)₂ is preferably between 0.6 and 0.7 part per hundred (resin), and is most preferably about 0.65 part per hundred (resin).

Formulated barrier compositions of the present invention also comprise high density polyethylene. The high density polyethylene may contain a minor amount of oxygen. These oxygen-containing polyolefins are formed by copolymerization of ethylene with some other comono¬ mer, which may contain oxygen. For the purpose of this invention, a "minor amount" of oxygen means that the polyolefin may contain oxygen below an amount that will significantly change the properties from that of the homopoly er. High density polyethylenes are ordinarily substantially linear and preferably have a weight-aver¬ age molecular weight of at least about 40,000. High density polyethylene, its properties and its synthesis are described in 16 Kirk-Othmer Ency. Chem. Tech. - 3rd Ed. , Linear (High Density) Polyethylene and Olefin Polymers (Ziegler Polyethylene), at 421-51 (J. Wiley & Sons 1980). The concentration of high density polyethylene in the formulated barrier composition is at least about 0.45 part per hundred (resin), preferably at least about 0.5 part per hundred (resin) and more preferably at least about 0.9 part per hundred (resin). It is at most about 1.05 parts per hundred (resin) and preferably at most about 1.0 part per hundred (resin).

The formulated barrier compositions of the

10 present invention also contain epoxidized vegetable oils, such as epoxidized soybean oil and epoxidized lin¬ seed oil. The epoxidized oil should be of a type suit¬ able to act as a plasticizer for the copolymer. The

-.,- epoxidized oil is most preferably epoxidized soybean oil. Epoxidized vegetable oils are known and are com¬ mercially available compounds. They and processes to synthesize them are described in 9 Kirk-Othmer Ency. Chem. Tech. - 3rd Ed., Epoxidation, at 251-63 (J. Wiley 0 & Sons 1980). The concentration of epoxidized vegetable oil in the formulated barrier composition is at least

0.8 parts per hundred (resin) and at most 1.0 part per hundred (resin). It is preferably about 0.9 part per hundred (resin) . 5

The compositions of the present invention also contain oxidized polyolefins, which are low molecular weight polymers which have a number average molecular _Q weight of less than about 5,000, as determined by vapor phase osmometry. Preferably the number average molecu¬ lar weight is 1,000 to 4,000, and most preferably between 1,500 and 2,500. The polyolefins have preferably been oxidized to an acid number of 10 to 35, 5 more preferably 13 to 17. These oxidized polyolefins preferably have a softening point, as determined by ASTM E-28 of 85°C to 145°C, more preferably 95°C to 140°C, and most preferably 98°C to 115°C. Generally, such oxidized polyolefins have a Brookfield viscosity at 140°C of 120 to 300 centipoise (cps), and preferably 170 to 250 cps. Exemplary oxidized polyolefins including oxidized polyethylene, oxidized polypropylene, or mixtures thereof are employed. Oxidized polyethylene is preferred.

10

Oxidized polyethylene and oxidized polypropyl¬ ene are known polymers which are commercially available, for instance under the trademark Allied 629A from Allied-Signal Corp. They can be prepared by reacting an

-.,- ethylene homopolymer or copolymer with oxygen or an or¬ ganic peroxide or hydroperoxide. The processes for syn¬ thesizing them are described in 16 Kirk-Othmer Ency. Chem. Tech. - 3rd Ed. Olefin Polymers (High Pressure Polyethylene), at 412 (J. Wiley & Sons 1980) and 24 0 Kirk-Othmer Ency. Chem. Tech. - 3rd Ed. Waxes, at 477 (J. Wiley & Sons 1980).

The concentration of oxidized polyolefin in the formulated barrier compositions of the present invention

25 is at least about 0.05 part per hundred (resin), prefer¬ ably at least about 0.1 part per hundred (resin), and more preferably at least about 0.2 part per hundred (resin). The concentration is at most about 0.25 part

30 per hundred (resin) and preferably at most about 0.2 part per hundred (resin).

Compositions of the present invention also con¬ tain a paraffin or polyethylene wax. They most prefer- 35 ably comprise a polyethylene wax. Paraffin waxes are defined herein as having a Brookfield viscosity in the range of 50 to 300 cps @ 140°C; a melting point in the range of 40°C to 8θ°C; and a density in the range of 0.85 S/cm3 to 0.95 S/cm3. Exemplary paraffin waxes include waxes commercially available from Hoechst AG, such as Hoechst XL-165FR, Hoechst XL-165SB, Hoechst XL- -165; and the like. Polyethylene waxes are defined herein as having Brookfield viscosity in the range of 130 to 450 cps β 140°C; a melting point in the range of 80°C to 100°C; and a density in the range of 0.85 S/cm3 0 to 0.95 ε/cm3» Exemplary polyethylene waxes include waxes commercially available from Allied Chemical Company such as Allied 617A and 6A.

_C- Paraffin and polyethylene waxes suitable for food contact purposes are known and commercially avail¬ able, as previously described. Their properties and synthesis are described in 24 Kirk-Othmer Ency. Chem. Tech. - 3rd Ed., Waxes, at 473-77 (J. Wiley & Sons 0 1980).

The formulated barrier composition may contain additional additives well-known to those skilled in the art. Exemplary of additives which may be incorporated 5 in the formulation are light stabilizers and antioxi- dants such as hindered phenol derivatives and pigments such as titanium dioxide. Each of these additives is known and several types of each are commercially 0 available.

The formulated barrier composition may be fab¬ ricated into any suitable final product, e.g., a variety of films or other articles. As is well-known in the 5 art, the films and articles are fabricated with conven¬ tional extrusion and coextrusion; for example, feedblock coextrusion, multimanifold die coextrusion, or combina¬ tions of the two; injection molding; extrusion molding; casting; blowing; blow molding; calendering; and lamina¬ tion techniques. Such extrusion typically is carried out using a single or multiple screw extruder, most often a single screw extruder specially constructed for use with thermally sensitive copolymers such as vinylidene chloride copolymer. Such extrusion is familiar to persons of ordinary skill in the art. It is described in a number of patents and other general references, such as R. A. Wessling, Polyvinylidene Chloride, supra, at 176-80; in 23 Ency. Poly Sci, supra, at 788-90; and in Ma et al., Plastic Films, Report No. 159 of SRI International Process Economics Program 179-210 (February 1986).

In using conventional processing equipment for thermally sensitive polymers, three conditions should be met. Two conditions, which are interrelated, are pro¬ cessing time and processing temperature. In melt pro¬ cessing polymers, it is generally recognized that as processing temperatures increase, processing times must decrease in order to avoid undesirable results such as polymer degradation. Melt processing must be accom¬ plished at a temperature below that at which decomposi¬ tion of the vinylidene chloride copolymer becomes sig¬ nificant. A third condition is that sufficient mixing must be generated during melt processing to provide a visually homogeneous blend, that is, no visible solids, within a reasonable mixing time. The most appropriate residence time and temperature conditions vary with different equipment. Persons of ordinary skill in the art can ascertain the optimum conditions for their own equipment without undue experimentation. Articles formed therefrom include blown and cast, mono and multi-layer, films; rigid and flexible containers; rigid and foam sheet; tubes; pipes; rods; fibers; and various profiles. Lamination techniques are particularly suited to produce multi-ply sheets. As is known in the art, specific laminating techniques include fusion; that is, whereby self-sustaining lamina are bonded together by applications of heat and pressure; wet combining, that is, whereby two or more plies are

10 laminated using a tie coat adhesive, which is applied wet, the liquid driven off, and combining by subsequent pressure laminating in one continuous process; or by heat reactivation, that is, combining a precoated film « _- with another film by heating, and reactivating the precoat adhesive so that it becomes receptive to bonding after subsequent pressure laminating.

Exemplary articles include rigid containers 20 used for the preservation of food, drink, medicine and other perishables. Such containers should have good mechanical properties, as well as low gas permeabilities to, for example, oxygen, carbon dioxide, water vapor, odor bodies or flavor bodies, hydrocarbons or agricul¬ 5 tural chemicals. Most organic polymers such as the polyolefins and styrene polymers, by themselves do not possess sufficient resistance to transmission of atmospheric gases and vapors. Consequently, multi-layer 0 sheet structures employed in packaging materials have organic polymer skin layers laminated on each side of a vinylidene chloride copolymer barrier layer, generally with glue layers used to promote adhesion between the barrier layer and dissimilar material layers. 5 The barrier provided by formulated barrier compositions of the present invention varies depending upon the particular ratio of ingredients, the proportion of vinylidene chloride in the vinylidene chloride copol¬ ymer, and the structure (rigid container or flexible film, etc.) into which the formulated barrier product is fabricated. However, for containers using copolymers of vinylidene chloride and about 6 weight percent methyl acrylate, the rate of transmission for oxygen is on average preferably at most about 0.05 D.U., more prefer¬ ably at most about 0.045 D.U., and most preferably at most about 0.04 D.U, both before and after retort, as measured on an Oxtran™ 10/50 oxygen permeability in- - strument produced by Modern Controls Inc. Formulated barrier compositions of the present invention can be extruded under most preferred conditions for up to 24 hours, preferably 48 hours, without noticeable build up of carbonaceous material on the extrusion screw and with 0 very few occurrences of carbonaceous material in the extruded sheet. Furthermore, the formulated barrier compositions have superior interlayer stability in coex¬ truded products.

5 Illustrative Examples

The present invention is illustrated in further detail by the following examples. The examples are for the purposes of illustration only, and are not to be 0 construed as limiting the scope of the present inven¬ tion. All parts and percentages are by weight unless otherwise specifically noted.

_c The compounds shown in Table I are chosen for this Example: TABLE I; POLYMER COMPONENTS

PVDC A vinylidene chloride copolymer is formed through a suspension polymerization process. The vinylidene chloride copolymer is formed from a monomer mixture comprising about 94 weight percent vinylidene chloride and about 6 weight percent methyl acrylate, based on total monomer mixture weight. The copolymer has a average molecular weight of 90,000 and a major melting point 165°C. The copolymer contains a small amount of epoxidized soybean oil (ES0). TSPP A tetrasodium pyrophosphate which is commer¬ cially available from Monsanto and is desig¬ nated as food grade. The TSPP is micronized until it passes through a 200 mesh screen.

HDPE A high density polyethylene commercially available from The Dow Chemical Company under the trade designation HD 65053N. The high density polyethylene resin has a density (ASTM Test D-1505) of 0.953 grams per cubic centime¬ ter and a melt index (ASTM Test D-1238) of 65 grams per 10 minutes. The HDPE is ground to a powder. ES0 An epoxidized soybean oil commercially avail¬ able from Viking Chemical Co. under the trade designation Vikoflex 7177. The epoxidized soybean oil has a viscosity of 3.1-3.8 Stokes § 25°C.

OPE An oxidized polyethylene commercially available under the trade designation as Allied 629A from

Allied Corp. The oxidized polyethylene has a density (ASTM Test D-1505) of 0.93 grams per cubic centimeter § 20°C, a drop point of 104°C, and a Brookfield Viscosity of 200 cps § 140°C.

Wax A polyethylene wax commercially available from Allied Corp. under the trade designation Allied

617A. The polyethylene wax has a density (ASTM Test D-1505) of 0.91 grams per cubic centime¬ ter, a drop point of 102°C, and a Brookfield Viscosity of 180 cps @ 140°C.

The formulated barrier compositions containing the ingredients shown in Table II are formulated by mix- ing those ingredients with the PVDC copolymer in 200-lb batches in a Littleford mixer for a period of 6 to 15 minutes each, until a generally homogeneous mixture is obtained. The ratios shown are final weight concen¬ trations in units of parts per hundred (resin). The amount of ESO actually added is slightly less than that shown, so that the added ESO and that already in the resin total up to the amount shown.

Each formulated resin is coextruded on conventional equipment to form a coextruded sheet con¬ taining 42.5 percent of polypropylene (first layer); 2.5 percent ESC0R™ 5610 tie layer (available from Exxon Corp.) (second layer); 10 percent formulated barrier composition (third layer); 2.5 percent ESC0R™ 5610 tie layer (fourth layer); and 42.5 percent of polypropylene (fifth layer). The sheet is formed into uniform con¬ tainers by melt phase forming. Some containers are sub¬ jected to simulated retort by immersing in boiling water under heightened pressure at 250°F for a period of one hour.

The oxygen permeability of the nonretorted and retorted samples is measured using an Oxtran™ 10/50 oxygen permeability instrument produced by Modern Con¬ trols Inc. with a nitrogen carrier gas at a temperature of about 23°C. Example A has an average oxygen perme¬ ability of 0.038 D.U. for the retorted sample and 0.036 D.U. for the nonretorted sample. Example B has an aver¬ age oxygen permeability of 0.035 D.U. for the retorted sample and 0.050 D.U. for the nonretorted sample. Example C has as an average unretorted oxygen permeability of about 0.048 D.U. Example D has as an average unretorted oxygen permeability of about 0.036 D.U.

The formulated barrier composition from Exam¬ ple A is extruded at a rate of 79-82 lb per hour on an Egan™ 2-1/2 extruder having a 21-1 length-to-diameter ratio and a screw specifically designed for the extru¬ sion of vinylidene chloride copolymers. (The screw design is currently in commercial use among converters of vinylidene chloride resins, and is commercially available from The Dow Chemical Company upon request). Carbonaceous material contamination in the extruded sheet is determined by counting specks of carbonaceous material over a one-minute period every 30 minutes during the 6-hour extrusion trial. The extruded product shows an average of about 3-75 carbonaceous material specks per minute. Inspection of the screw heel after the extrusion is completed shows no accumulation of carbonaceous material.

Claims

Claims ;10

1. A formulated barrier resin composition in powder form, characterized in that the composition contains:

15 (1) a copolymer of vinylidene chloride and either: (a) 10 to 20 weight percent vinyl chloride; or (b) 4 to 10 weight percent alkyl acrylate; or (c) a mixture of those comonomers; and 0

(2) the following additives in the following weight concentration per hundred parts of vinylidene chloride copolymer:

25 (a) an amount of inorganic stabilizer no greater than about 1.1 parts which is effective to stabilize the formulated barrier composition;

(b) 0.45 to 1.05 part high density

30 polyethylene;

(c) 0.8 to 1.0 part epoxidized vegetable oil;

(d) 0.05 to 0.25 part oxidized •_3C- polyolefin; and (e) 0.20 to 0.55 part polyethylene or paraffin wax.

2. The composition of Claim 1 wherein (1) the vinylidene chloride copolymer is a copolymer of vinyl¬ idene chloride and 4 to 8 weight percent methyl acrylate; and (2) the inorganic stabilizer contains tetrasodium pyrophosphate.

3. The composition of Claim 1 wherein (1) the vinylidene chloride copolymer is a copolymer of vinyl¬ idene chloride and 4 to 8 weight percent methyl acrylate; and (2) the inorganic stabilizer contains magnesium hydroxide.

4. The composition of Claim 1 wherein (1) the vinylidene chloride copolymer is a copolymer of vinyl¬ idene chloride and 10 to 20 weight percent vinyl chloride; and (2) the inorganic stabilizer contains tetrasodium pyrophosphate.

5. The composition of Claim 1 wherein (1) the vinylidene chloride copolymer is a copolymer of vinyl¬ idene chloride and 10 to 20 weight percent vinyl chloride; and (2) the inorganic stabilizer contains magnesium hydroxide.

6. The composition of any one of Claims 1, 2, 3, 4, or 5 wherein the inorganic stabilizer consists essentially of 0.7 to 0.9 parts tetrasodium pyrophosphate or 0.6 to 0.7 parts magnesium hydroxide.

7. The composition of any one of Claims 1, 2, 3, 4 or 5 wherein the composition contains about 0.9 part to 1.0 part high density polyethylene.

8. The composition of any one of Claims 1, 2, 3, 4 or 5 wherein the epoxidized vegetable oil is epoxidized soybean oil.

9. The composition of any one of Claims 1, 2, 3, 4 or 5 wherein the oxidized polyolefin is oxidized polyethylene.

10. The composition of any one of Claims 1, 2, 3, 4 or 5 wherein the polyethylene or paraffin wax is a polyethylene wax.

11. The composition of Claim 1 wherein the mixture of additives comprises:

(a) either (i) 0.7 to 0.9 parts tetra¬ sodium pyrophosphate or (ii) 0.6 to 0.7 parts magnesium hydroxide;

(b) 0.5 to 1.0 parts high density polyethylene;

(c) 0.7 to 0.9 parts epoxidized soybean oil;

(d) 0.1 to 0.2 parts oxidized polyethylene; and

(e) 0.23 to 0.5 parts polyethylene wax.

12. A multi-layer article containing at least one organic polymer skin layer and at least one barrier layer, characterized in that the barrier layer contains the extruded product of a formulated barrier composition of any one of Claims 1, 2, 3, 4, 5, 6, 7, 8, 9, 10 or 11.

13. The use in an extrusion or coextrusion process of a powder composition of any one of Claims 1 , 2, 3, 4, 5, 6, 7, 8, 9, 10 or 11.

14. An additive composition comprising, in the following weight ratios:

(a) an amount of inorganic stabilizer no greater than 1.1 parts which is effective to stabilize a formulated barrier com- position containing primarily vinylidene chloride-containing copolymer;

(b) 0.45 to 1.05 parts high density polyethylene;

(c) up to 1.0 part epoxidized vegetable oil, chosen such that the total concen¬ tration when added to a vinylidene chloride copolymer containing one of those compounds will be 0.8 to 1.0 part per hundred (resin) epoxidized vegetable oil;

(d) 0.05 to 0.25 part oxidized polyethylene; and

(e) 0.2 to 0.55 part paraffin or polyethylene wax.