WO1993016010A1 - Production of cement-mortar dry mix - Google Patents

Production of cement-mortar dry mix Download PDF

Info

Publication number
WO1993016010A1
WO1993016010A1 PCT/EP1992/000318 EP9200318W WO9316010A1 WO 1993016010 A1 WO1993016010 A1 WO 1993016010A1 EP 9200318 W EP9200318 W EP 9200318W WO 9316010 A1 WO9316010 A1 WO 9316010A1
Authority
WO
WIPO (PCT)
Prior art keywords
hardener
cement
dry
dry mix
reactive resin
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/EP1992/000318
Other languages
French (fr)
Inventor
Peter Ellenberger
Heinz W. Schmitt
Salvatore Valenti
Qiwei Yang
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Novartis Pharma GmbH Austria
Sandoz AG
Original Assignee
Sandoz Erfindungen Verwaltungs GmbH
Sandoz AG
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Sandoz Erfindungen Verwaltungs GmbH, Sandoz AG filed Critical Sandoz Erfindungen Verwaltungs GmbH
Priority to JP4504145A priority Critical patent/JPH06506433A/en
Priority to AT92904510T priority patent/ATE141904T1/en
Priority to EP92904510A priority patent/EP0580588B1/en
Priority to CA 2105398 priority patent/CA2105398A1/en
Priority to DE69213227T priority patent/DE69213227T2/en
Priority to ES92904510T priority patent/ES2092095T3/en
Priority to AU12292/92A priority patent/AU1229292A/en
Publication of WO1993016010A1 publication Critical patent/WO1993016010A1/en
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

A storable cement-mortar dry mix, which comprises the components cement, aggregate, reaction resin and hardener in a single mixture, wherein the hardener is present as the reaction product of the hardener with an organic acid or a functional derivative thereof.

Description

PRODϋCTICN OF CErøNT-M_KI---R DRY MIX
This invention relates to a process for the production of a storable cement-mortar dry mix containing a reaction resin and hardener therefor.
It is known from German Patent application DE 35 23 479 that, in the production of cement-mortar dry mixes which contain a reactive resin, it is desirable to have available a storable dry mix which contains all the components (except water) and only has to be mixed with water at the place of use. This problem was solved, according to DE 35 23 479, by mixing some of the components to form a prelirninary mix A, and , if necessary, mixing the remaining components to form a preliminary mix B, and mixing these preliminary mixes with water at the place of use. Thus, at least two preliminary mixes have to be mixed with water; there is mentioned the possibility of making a single dry mix containing all the components except water in a storable mixture, but this apparently was not followed through.
It has now been found that it is possible to produce a cement-mortar dry mix comprising a reactive resin and hardener therefor, which contains all the coπponents except water, and which is storable, which remains fluid over a long period of time and which does not harden prematurely. This is achieved by reacting the hardener with an organic acid or a functional derivative thereof, to form an anhydrous product, prior to its addition to the dry mix.
The invention therefore provides a process for the production of a cement-mortar dry mix, which comprises cement, aggregate, reactive resin and hardener in a single mixture, characterized in that the hardener is added in the form of a dry reaction product with an organic acid or a functional derivative thereof. The dry mixes thus produced can be stored for an unlimited period, and only at the place of use need they be mixed with water, after which they harden over time periods typical for equivalent conventional compositions to produce building materials with excellent strength.
The reaction products of the hardener (generally an amino group- containing compound) with an organic acid or a functional derivative thereof, should be dry, that is, they should be powdery or granular solids and not aqueous fluids. They may be dry per se or they may be mixed with amorphous admixed materials such that are absorbed and converted to dry form and they can be added in this dry powder form. These reaction products are generally salts or amides, which hydrolyze in an alkaline medium. Thus, if the dry mix is brought into contact with water, the amine hardener is released and reacts with the reactive resin.
This invention also provides a hardener composition for reactive resins which is the reaction product of a hardener and an organic acid or functional derivative thereof, and which is a dry powder or a granular solid.
It is preferred that, when the hardener is an amino group- containing compound, the relative proportions of hardener and acid or functional derivative thereof are such that at least 30%, more preferably 40% and most preferably from 50-90% of the amino groups are reacted.
It is preferable to use carboxylic acids, polycarboxylic acids or functional derivatives of the acids, e.g. lactones or mixtures of carboxylic acids or polycarboxylic acids, which, after reacting with the hardener, yield a dry powder which readily hydrolyzes in an alkaline medium. Specific examples of such acids are gluconic acid or the lactone thereof, lactic acid, aminosulphonic acid and oxalic acid, oxalic acid being especially preferred. Superplasticizers which contain acidic groups may also be used, e.g. copolymers of styrene and aleic acid. However, if the reaction product is liquid at ambient temperature, for example, as occurs when formic acid is used, it is advantageous firstly to mix it with an amorphous admixed material so that a dry powder is obtained. This can then be easily incorporated into the dry mix according to the invention. 1
The reaction product of the hardener and the organic acid may be prepared by an suitable method known to the art. The choice of method will depend on the natures of the materials involved (as the final product must be a dry powder or granular solid, different techniques will be needed, for example, depending on whether the reaction product is liquid or solid) . The skilled man will readily be able to determine the most approriate method for any given set of circumstances.
During the preparation of the cement-mortar dry mix, the reactive resin should not come into contact with the cement, but initially with an amorphous admixed material, so that during the mixing operation, the reactive resin and hardener are separated not only from each other but also from the cement, and no premature reaction can take place between the resin and hardener, nor can the solidifying properties of the cement be affected. Such admixed materials are non-crystalline materials, usually containing silicon, and which because of their large specific surface have an affinity for the reactive resin, but do not have the same hydraulic effect as cement. Examples of such materials are fly ash, trass, ground blast-furnace slag, silica fume and bentonite. Materials such as lampblack and active silicic acid may also be used, provided that their colour or price is acceptable for the application envisaged. The only proviso is that the grain size of these materials does not exceed 0.05 mm, and that their specific surface is greater than 0.2 m2/g. The smaller the grain size and the greater the specific surface of these admixed materials, the smaller the quantity which will be needed.
Preferred amorphous admixed materials for the process according to the invention are fly ash and silica fume. These may be used alone or mixed.
The mixing procedure according to the invention is preferably carried out such that firstly the aggregate (e.g. sand) is mixed with the reaction resin, and then secondly with the special admixed material and with the cement to give a first preliminary mix. The reaction H product of the hardener, given powder form where necessary by separate mixing with amorphous admixed material, is mixed with any further required admixtures and/or additives to give a second preliminary mix. The two preliminary mixes are finally combined to form a dry mix. Alternatively, the reactive resin may also be initially mixed with amorphous admixed material, and then all the components may be combined in one mixing operation.
The reactive resin suitable for use in this invention may be one of the polymerisable compounds which are known for this purpose and which are crosslinkable by means of an amine hardener. These are available commercially as so-called 2-component resins. Examples of such resins are epoxy resins. The corresponding hardeners are usually (and preferably) compounds containing amino groups.
The cements which are useful in this invention are the known hydraulic binding agents such as Portland cement, iron Portland cement, blast¬ furnace cement and trass cement. The preferred binding agent is Portland cement, and in particular Portland cement which is low in aluminates, such as so-called PCHS (Portland cement with high sulphate resistance) .
The aggregate materials used are either natural stone, e.g. quartz sand, sea gravel, pit gravel, or artificial aggregates, e.g. blast-furnace slag, coal ashes, cinders and granulates, pumice from various base materials, calcined aluminous aggregates or organic aggregate materials. For certain applications, reinforcing materials, such as fibres of steel, glass and plastics, can additionally be used.
There may also be used in the compositions of this invention polymer additives and cement admixtures. These are materials, which, used in small quantities, influence the properties of the finished cement mixes. The additives are usually organic in nature. Examples are defoamers, corrosion inhibitors, degassing agents, adhesion improvers, dispersing agents and pigments. The admixtures alter the workability, the ability to withstand frost or de-icing salt, absorption of water, solidifying times, etc., of the cement mix and are very well known to r and widely used by the art. Examples of such admixtures are plasticizers and superplasticizers, air entraining agents, concrete sealing materials, solidifying retardants, solidifying accelerators, compression aids and stabilizers.
A preferred dry mix contains, in addition to Portland cement, various constituents in the following quantities:
more most referabl referabl referabl
Figure imgf000007_0001
whereby all percentages refer to the weight of the cement, the hardener being present in the form of an anhydrous reaction product with an organic acid or functional derivative thereof.
The dry mixes obtained, which contain reactive resin, may be used in many applications. As mortar (with sand as the aggregate), they may be used in building restoration, especially those attacked to a great extent by frost/salt, or to produce floors and coatings. With the incoproration of coarser aggregates, they may be used as construction material. Such dry mixes are also suitable for spraying.
In the following examples, all parts are understood to be parts by weight. The percentages are by weight and the temperatures are given in degrees Celsius. E x a m p 1
Prepaxation of a dry pov- er hardener
5.263 parts of "Beckopox" (trade mark) EH 623 (amine hardener ex Hoechst) are prepared and heated to 75-80°. 1500 parts of water are added at this teirperature and the mixture is stirred for 60-90 minutes until a homogeneous mixture is obtained. Subsequently, 834 parts of oxalic acid are measured in over the course of 2-3 hours at the same temperature. The reaction mixture is dried over 2 - 2^ hours at 110° in a vacuum drying chamber, and pulverized. The dried powder has a melting point of 123-127°.
E x a m p l e 2
Preparation of a dry powder hardener
40 parts of "Rϋtapox" (trade mark) ECC-4000-B amine hardener (from Bakelite GmbH) are added to a kettle, followed by 54.5 parts of water, and the mixture heated to 75°-80°C and maintained at this teirperature until a homogeneous blend is achieved (this takes no more than one hour) . The blend temporarily becomes milky. To this blend is added 9.5 parts of hydrated oxalic acid (C2H2O4.2H20) , the addition being gradual such that the temperature remains in the range of 80°-85°C.
The product is a 45% (wt) solution of hardener which is converted to a dry powder by spray drying. The temperature at which spray drying is carried out should not exceed 80°C.
E x a m p l e 3
Preparation and testing of a cement-mortar dry mix
The following materials and quantities were used: parts
1. mixed quartz sand 0.1-0.75 mm 53.75
2. "Rutapox" ECC-4000 K.A. epoxy resin 1.143
3. "TiONA" (trade mark) RCL-535 Ti02 pigment 1.00
4. EFA FILLER fly ash 18.00
5. Portland cement 25.00
6. Hardener (from Example 2) 1.107 Materials 1 and 2 are mixed and then materials 3, 4, 5 and 6, are added to this mixture in that order, blending of an added material being completed before the next material is added.
The dry mortar was tested after storing for six months. Fresh mortar is produced according to DIN 18,555 part 1. The mortar is mixed for 3 minutes using 15% mixing water.
Control of the fresh mortar is carried out according to DIN 18,555 part 2.
Prisms of 4/4/16 cm are produced with the fresh mortar according to DIN 18,555. After one day, they are uncovered and stored for 6 days in a climate of 20°/95% relative humidity and for 21 days at normal climate of 20°/50% relative humidity according to DIN 50,014. The tests for flexural-bending strength and compressive strength are similarly carried out according to DIN 1,164. The bonding tensile strength is determined according to ZTV-SIB 87.
In all cases, the values found correspond to the normal values determined with freshly prepared mixtures.

Claims

P a t e n t C l a i m s
1. Process for the production of a storable cement-mortar dry mix, which comprises the components cement, aggregate, reactive resin and hardener in a single mix, characterized in that the hardener is added in the form of a dry reaction product with an organic acid or a functional derivative thereof.
2. Process according to claim 1, characterized in that the reaction product of the hardener with an organic acid or a functional derivative thereof is used as a dry powder or a granular solid.
3. Process according to claim 1 or claim 2, characterized in that the reactive resin is firstly brought into contact with an amorphous admixed material, prior to its being mixed with other materials of the composition.
4. Process according to claim 3, characterized in that fly ash and/or silica fume is used as the amorphous admixed material.
5. Process according to claim 1 or claim 2, characterized in that the aggregate is first mixed with the reactive resin and subsequently with the amorphous admixed material and the cement in succession to give a first preliminary mixture, the reaction product is mixed, optionally separately, with the amorphous admixed material and with possible further admixtures and/or additives to give a second preliminary mixture, and the two preliminary mixtures are combined together to form a dry mix.
6. Process according to claim 5, characterized in that the reactive resin is first of all brought into contact with the amorphous admixed material, and afterwards all the components are combined in a single mixing operation.
7. An amine hardener for reactive resins, obtained by reacting the hardener with an organic acid or a functional derivative thereof, the amine hardener being in the form of a dry powder or a granular solid.
8. An amine hardener according to claim 7, wherein the quantities of hardener and acid reacted are such that at least 30%, preferably at least 40%, more preferably from 50 to 90% of the amine groups are reacted.
9. An amine hardener according to claim 7, characterized in that it is a dry powder or granular solid.
10. An amine hardener according to claim 7, characterized in that the organic acid is oxalic acid.
11. A storable cement-mortar dry mix which comprises cement and the following ingredients in the following proportions expressed by weight of the cement:
- reactive resin 2-25 %
- hardener 2-25 %
- fly ash 10-100 %
- aggregate 50-500 %
- cement admixtures 0-20 %
- additives 0-20 %
the hardener being present in the form of its anhydrous reaction product with an organic acid or functional derivative thereof. /t o
12. A dry mix according to claim 11, wherein the proportions of ingredients are:
- reactive resin 5-20 %
- hardener 5-20 %
- fly ash 10-100 %
- aggregate 100-400 %
- cement admixtures 0.5-10 %
- additives 0-10 %
13. A dry mix according to claim 11, wherein the proportions of fly ash, cement admixtures and additives are from 30-100%, from 0.5-5% and from 0.5-10% respectively.
14. A dry mix according to claim 11, wherein the proportion of fly ash, cement admixtures and additives are from 30-80%, from 1-3% and from 1-6% respectively.
PCT/EP1992/000318 1990-07-12 1992-02-14 Production of cement-mortar dry mix Ceased WO1993016010A1 (en)