WO2000006514A1 - Procede de production de clinker par addition de cendre de charbon - Google Patents

Procede de production de clinker par addition de cendre de charbon Download PDF

Info

Publication number
WO2000006514A1
WO2000006514A1 PCT/CA1998/000718 CA9800718W WO0006514A1 WO 2000006514 A1 WO2000006514 A1 WO 2000006514A1 CA 9800718 W CA9800718 W CA 9800718W WO 0006514 A1 WO0006514 A1 WO 0006514A1
Authority
WO
WIPO (PCT)
Prior art keywords
flyash
clinker
cooler
cement clinker
carbon
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/CA1998/000718
Other languages
English (en)
Inventor
David Bridson Oates
Horace Hershel Compton
Syed Suhail Akhtar
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Lafarge Canada Inc
Original Assignee
Lafarge Canada Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority to US08/833,927 priority Critical patent/US5837052A/en
Priority claimed from US08/833,927 external-priority patent/US5837052A/en
Priority to CA002234523A priority patent/CA2234523C/fr
Application filed by Lafarge Canada Inc filed Critical Lafarge Canada Inc
Priority to AU85254/98A priority patent/AU8525498A/en
Priority to PCT/CA1998/000718 priority patent/WO2000006514A1/fr
Publication of WO2000006514A1 publication Critical patent/WO2000006514A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

Des cendres de charbon contaminées, par exemple des cendres volantes contaminées par du carbone sont introduites dans du clinker chaud dans un refroidisseur (16) situé en aval d'un four (14) à ciment; le carbone est brûlé dans le refroidisseur (16) en vue d'obtenir un clinker à teneur efficace en cendres volantes exemptes de carbone; ce procédé permet d'utiliser des cendres volantes contaminées par du carbone sans devoir mettre en oeuvre des étapes spéciales séparées d'élimination de carbone; des contaminants volatils ou des contaminants comportant un constituant volatil, par exemple de l'ammoniac adsorbé, sont éliminés de manière similaire dans le refroidisseur (16) par volatilisation.
PCT/CA1998/000718 1997-04-10 1998-07-24 Procede de production de clinker par addition de cendre de charbon Ceased WO2000006514A1 (fr)

Priority Applications (4)

Application Number Priority Date Filing Date Title
US08/833,927 US5837052A (en) 1997-04-10 1997-04-10 Process for producing cement clinker containing coal ash
CA002234523A CA2234523C (fr) 1997-04-10 1998-04-09 Methode pour l'obtention d'un clinker de ciment renfermant des cendres volantes
AU85254/98A AU8525498A (en) 1997-04-10 1998-07-24 Process for producing cement clinker by addition of coal ash
PCT/CA1998/000718 WO2000006514A1 (fr) 1997-04-10 1998-07-24 Procede de production de clinker par addition de cendre de charbon

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US08/833,927 US5837052A (en) 1997-04-10 1997-04-10 Process for producing cement clinker containing coal ash
PCT/CA1998/000718 WO2000006514A1 (fr) 1997-04-10 1998-07-24 Procede de production de clinker par addition de cendre de charbon

Publications (1)

Publication Number Publication Date
WO2000006514A1 true WO2000006514A1 (fr) 2000-02-10

Family

ID=25683159

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/CA1998/000718 Ceased WO2000006514A1 (fr) 1997-04-10 1998-07-24 Procede de production de clinker par addition de cendre de charbon

Country Status (2)

Country Link
AU (1) AU8525498A (fr)
WO (1) WO2000006514A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN114409282A (zh) * 2022-02-24 2022-04-29 无锡市金希达新型建材有限公司 一种水泥熟料用超细粉煤灰及其制备方法

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE2624971A1 (de) * 1976-06-03 1977-12-15 Dyckerhoff Zementwerke Ag Verfahren zur verwertung industrieller abfaelle
US5520730A (en) * 1988-08-08 1996-05-28 Barbour; Ronald L. Settable composition for general purpose concrete and method of making same
WO1996026165A1 (fr) * 1995-02-23 1996-08-29 Aalborg Portland A/S Procede de fabrication de brique de ciment portland

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE2624971A1 (de) * 1976-06-03 1977-12-15 Dyckerhoff Zementwerke Ag Verfahren zur verwertung industrieller abfaelle
US5520730A (en) * 1988-08-08 1996-05-28 Barbour; Ronald L. Settable composition for general purpose concrete and method of making same
WO1996026165A1 (fr) * 1995-02-23 1996-08-29 Aalborg Portland A/S Procede de fabrication de brique de ciment portland

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN114409282A (zh) * 2022-02-24 2022-04-29 无锡市金希达新型建材有限公司 一种水泥熟料用超细粉煤灰及其制备方法

Also Published As

Publication number Publication date
AU8525498A (en) 2000-02-21

Similar Documents

Publication Publication Date Title
US5837052A (en) Process for producing cement clinker containing coal ash
AU2002231533B2 (en) Enhancement of cement clinker yield
RU2146660C1 (ru) Способ производства цементного клинкера и устройство для его осуществления
US5976243A (en) Process for producing cement clinker containing blast furnace slag
KR920004853B1 (ko) 회전 킬른(kiln)에서의 분진 재순환 방법 및 그 장치
KR100325282B1 (ko) 순환식 유동층 증기 발생기의 연료 및 흡착제 공급 방법 및 장치
US5370067A (en) Method of incinerating solid combustible materials, especially urban waste
US6755901B1 (en) Ammonia removal from fly ash
AU2002231533A1 (en) Enhancement of cement clinker yield
US5169611A (en) Method of purifying the exhaust gases from plants for the production of cement clinker
JPS61262516A (ja) 汚染された土壌を清浄にする方法
US7048784B2 (en) Method and system for treating exhaust gas from cement manufacturing equipment
JP2005029836A (ja) ロータリーキルンによる廃棄物処理方法
CA2453124C (fr) Methode d'incorporation de cendres de charbon a du clinker de ciment
EP0021558A1 (fr) Procédé et dispositif pour éluer d'anhydrique sulfureux de fumées
US4198201A (en) Method of and apparatus for operating industrial furnace systems
WO2000006514A1 (fr) Procede de production de clinker par addition de cendre de charbon
RU2023016C1 (ru) Устройство для получения губчатого железа, цементного клинкера и электроэнергии
CA2249493C (fr) Procede pour produire du clinker contenant du laitier de haut fourneau
JPH06185705A (ja) 流動床焼成炉
JPS6252152A (ja) コンクリ−ト用骨材製造装置
JPH07139720A (ja) 焼却残灰の処理方法及び装置

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): AL AM AT AU AZ BA BB BG BR BY CA CH CN CU CZ DE DK EE ES FI GB GE GH GM HR HU ID IL IS JP KE KG KP KR KZ LC LK LR LS LT LU LV MD MG MK MN MW MX NO NZ PL PT RO RU SD SE SG SI SK SL TJ TM TR TT UA UG UZ VN YU ZW

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): GH GM KE LS MW SD SZ UG ZW AM AZ BY KG KZ MD RU TJ TM AT BE CH CY DE DK ES FI FR GB GR IE IT LU MC NL PT SE BF BJ CF CG CI CM GA GN GW ML MR NE SN TD TG

DFPE Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101)
121 Ep: the epo has been informed by wipo that ep was designated in this application
REG Reference to national code

Ref country code: DE

Ref legal event code: 8642

122 Ep: pct application non-entry in european phase
NENP Non-entry into the national phase

Ref country code: CA