WO2003016375A1 - Chemically resistant aqueous polyurethane dispersions - Google Patents

Chemically resistant aqueous polyurethane dispersions Download PDF

Info

Publication number
WO2003016375A1
WO2003016375A1 PCT/IB2001/001504 IB0101504W WO03016375A1 WO 2003016375 A1 WO2003016375 A1 WO 2003016375A1 IB 0101504 W IB0101504 W IB 0101504W WO 03016375 A1 WO03016375 A1 WO 03016375A1
Authority
WO
WIPO (PCT)
Prior art keywords
reaction product
diisocyanate
group
aqueous polyurethane
coating
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/IB2001/001504
Other languages
French (fr)
Inventor
Gerard W. Jordens
Henrica A. M. Evenboer
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Henkel AG and Co KGaA
Original Assignee
Henkel AG and Co KGaA
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Henkel AG and Co KGaA filed Critical Henkel AG and Co KGaA
Priority to DE60115965T priority Critical patent/DE60115965D1/en
Priority to EP01956732A priority patent/EP1417246B1/en
Priority to AT01956732T priority patent/ATE312859T1/en
Priority to ES01956732T priority patent/ES2252266T3/en
Priority to PCT/IB2001/001504 priority patent/WO2003016375A1/en
Publication of WO2003016375A1 publication Critical patent/WO2003016375A1/en
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

Silyl-free, aqueous polyurethane dispersions, based on hydroxylated polydiene resins, are provided, as well as the use of such dispersions to apply chemically resistant coatings to various substrates.

Description

CHEMICALLY RESISTANT AQUEOUS POLYURETHANE DISPERSIONS
BACKGROUND OF THE INVENTION
This invention relates to aqueous polyurethane dispersions based on hydroxylated polydiene resins, especially to the use of such dispersions to apply chemically resistant coatings to various surfaces and substrates.
Chemically resistant coatings containing aqueous polyurethane dispersions based upon hydroxylated polydienes can be used in the formulation of temporary protective peelable coatings useful as masking agents for selective chemical and mechanical protection of metal surfaces during chemical treatments such as anodizing, plating, adhesive bonding, or for mechanical protection during forming, machining, drilling, routing, or general part handling of both metallic and non-metallic articles. Chemically resistant peelable coatings when properly formulated have low uniform peel adhesion before and after chemical processing, thermal and oxidative stability, possess the ability to be scribed to produce complex masked patterns, may be machined or drilled without loss of adhesion at the tool surface, and following all processing operations may be removed by hand peeling without the use of solvents or high temperatures.
In the practice of the arts of anodizing or plating of metal surfaces, chemically resistant temporary barriers such as conductive or non-conductive tapes, waxes, solvent-based lacquers, and solvent and water-borne peelable coatings known collectively as "resists" or "stop-offs" are used to protect specific areas of a workpiece from contact with chemical solutions.
Tapes can be applied by hand lay-up to protect the desired areas; waxes can be applied by hot dipping of the entire workpiece followed by hand trimming; solvent-borne lacquers can be applied by brushing, flowing, peelable coatings can be applied selectively by brushing or dipping; and solvent or water-borne peelable coatings can be applied by brushing, flowing, dipping, or spraying followed by hand scribing and peeling to expose areas to be chemically treated, in either acidic or basic environments.
Following chemical treatment(s) tapes can be removed by hand peeling; waxes carrbe removed mechanically, thermally or by the use of cleaning baths; lacquers can be removed by solvents or by thermal destruction; and solvent or water-borne peelable coatings can be removed by hand peeling.
In the construction of aerospace assemblies, it is desirable to protect polished alclad aluminum surfaces from mechanical and chemical treatments. For this purpose, a peelable temporary protective coating known as a bond line maskant is employed. In a typical process, a workpiece is pre-cleaned followed by spray application of the bond line maskant. The coating is cured by combinations of air drying and oven curing. After the maskant is dried and cured, selected areas of the parts to be treated may be removed by mechanical or laser scribing. The scribed sections of the maskant are removed by hand peeling. The exposed areas then receive chemical treatments such as etching and anodizing, and a bonding primer is applied and oven cured. Machining operations such as drilling or routing may also be performed. Different parts may then be assembled by adhesive bonding. Adhesive is applied over the bonding primer and the adhesive joint cured at elevated temperatures and pressures. After all the chemical and mechanical processing is completed, the bond line maskant is removed by hand peeling.
Many of the coatings or maskants used today are rubber elastomers dissolved in organic solvents, such as toluene/xylene, perchloroethylene or methylene chloride. See, for example, U.S. Patent No. 4,301 ,194. With increasing government regulation of volatile organic solvents, it is desirable to find alternative chemistries for such protective coatings. It is also desirable to avoid the expensive incorporation of silyl groups.
BRIEF SUMMARY OFTHE INVENTION
Silyl-free, aqueous polyurethane dispersions containing a urethane prepolymer are provided, which prepolymer comprises the reaction product of one or more hydroxylated polydiene resins (preferably a hydroxy-terminated polybutadiene resin), a diol-containing carboxylic acid salt (preferably a dimethylol propionic acid salt) and an aliphatic diisocyanate, which reaction product has been chain extended with a diamine. Also provided are chemically resistant coatings for substrate surfaces containing such dispersions, methods for applying the dispersion to the surface, the resulting coated surface, and the like. DETAILED DESCRIPTION
It has now been found that chemically resistant coatings for substrates (such as metal), of the type hereinabove described (including tapes, waxes, lacquers, and peelable coatings), can be prepared via the use of aqueous polyurethane dispersions based upon hydroxylated polydiene resins, thus avoiding the need for use of high VOC (volatile organic content) solvents.
These dispersions contain a urethane prepolymer, typically prepared in a light solvent such as methylethylketone or tetrahydrofuran, which prepolymer comprises the reaction product of the polydiene polyol(s), the diol-containing carboxylic acid salt (such as the triethyl ammonium salt of dimethylol propionic acid) and the aliphatic diisocyanate (such as tetramethyl xylene diisocyanate, isophorone diisocyanate, hexamethylene diisocyanate, cyclohexyl diisocyanate, or 4,4-dicyclohexylmethane diisocyanate).
The diene monomer for the polydiene resin can be chosen from the family of butadiene; chloroprene 1 ,3 pentadiene; and cyclopentadiene. The preferred polydiene polyols are the hydroxy-terminated polybutadienes, with a number average molecular weight typically between 2000 and 15000 (preferably between 2000 and 5000). The hydroxy value in milliequivalents per gram (meg/g) is typically between 0.5 and 1.5 (preferably between 0.8 and 0.9). The viscosity is typically between 1000 and 10000 milli-Pascal-seconds (mPas) at 30.8°C. An example of the preferred resin is Poly bd® R-45-HT hydroxy terminated polybutadiene, available commercially from Elf Atochem. The diol-containing carboxylic acid salt preferably is a compound containing one carboxylic acid salt functional group per molecule. Independently, the diol-containing carboxylic acid salt preferably has at least three carbon atom (more preferably, only three carbon atoms) intermediate between the two hydroxyl groups of the salt. Also, independently, it is preferred for a carboxylic acid salt functional group to be substituted on a carbon atom intermediate between the two carbon atoms bearing the two hydroxyl groups. Further, it is preferable for each of the two hydroxyl groups to be primary hydroxyl groups. Preferably, the diol- containing carboxylic acid salt corresponds to the general formula: CH2OH
I
R — C — CO2M
I CH2OH
wherein R is H or a Cι-Cι8alkyl group (preferably, R is methyl) and M is an alkali metal, ammonium or alkyl aryl or aralkyl ammonium (e.g., triethylammonium).
It has unexpectedly been discovered that the choice of reactants and the manner in which such reactants are combined can be critical to the successful preparation of aqueous polyurethane dispersions. When a hydroxylated polydiene resin is used, significant solubility problems are encountered when a free acid of a diol-containing carboxylic acid such as dimethylol propionic acid is used as a co-reactant. The solubility of the salts of such acids, particularly the alkylammonium salts, in the reaction mixture is much greater than that of the free acid, enabling the prepolymer to be more easily prepared.
Another problem which has been encountered using hydroxylated polydiene resins to prepare aqueous polyurethane dispersions is the formation of viscous gels when carboxylic acid groups in the prepolymer are neutralized by the addition of a base. Surprisingly, the use of an already neutralized diol-containing carboxylic acid rather than the free acid has been found to circumvent this problem.
The ratio of reactants used in preparing the prepolymer is normally chosen such that the NCO/OH molar ratio is greater than 1.4 (preferably between 1.5 and 2.5), taking into account that OH groups come from both the polydiene polyol and the diol.
The aqueous polyurethane dispersions are then prepared by dispersion of the prepolymer in water (typically such as to reach a final solids content in the range of 30 to 40 weight %, based on the overall weight of the dispersion); chain extension with a diamine such as hydrazine hydrate or ethylenediamine (typically in an amount such that the molar ratio of NH2 groups to remaining NCO groups in the prepolymer is equal to 1.0), typically at a temperature between room temperature (about 25°C) and 80°C; and distillation (such as under vacuum) to remove solvent and obtain the aqueous dispersion. As noted above, these dispersions are found to be useful for a variety of chemically resistant coating applications, such as for a maskant for chemical milling process. The absence of emulsifiers and/or surfactants in the dispersions as formulated above enables coatings prepared therefrom to show excellent resistances to mineral acids and bases, low temperature flexibility, low Tg, and good adhesion to a variety of substrates, especially metals such as aluminum, titanium, magnesium and steel.
A variety of methods are known in the art for including other additives in the final dispersion to enhance certain properties. For example, acrylics can be added to further enhance adhesion, acrylonitrile butadiene can be added to enhance strength and flexibility of the coatings, pigments and/or fillers (such as clay, talc and/or silicates) can be added to enhance stiffness and strength, thickeners can be added to enhance increase viscosity (maskants typically have a viscosity of about 1-8 Pascal seconds at 25°C), all as are conventionally known in the art.
Application of a maskant coating to a substrate, such as metal, is normally done by one or more coats via dipping, spraying, flowing or brushing. Typical dry film thicknesses are between 100 and 600 microns. Curing of the film can be done at room temperature (about 25°C) or with heat (up to about 120 °C). Drying times typically run from 1 to 20 hours, so as to reduce residual water to below about 3 weight %.

Claims

What is claimed is:
1. A silyl-free, aqueous polyurethane dispersion derived from the reaction product of a hydroxylated polydiene resin, a dimethylol propionic acid salt and an aliphatic diisocyanate, which reaction product has been dispersed in water and chain extended with a diamine.
2. A dispersion as in Claim 1 wherein the hydroxylated polydiene resin is a hydroxy terminated polybutadiene.
3. A chemically resistant coating for article surfaces which coating contains the polyurethane dispersion of Claim 1.
4. A coating as in Claim 3 which is in the form of a tape, a wax, a lacquer or a peelable coating.
5. A method for providing an article surface with a chemically resistant coating which method comprises applying the dispersion of Claim 1 to said article surface by brushing, spraying, dipping, flowing or hand lay-up.
6. An article surface having a chemically resistant coating thereon which coating contains the dispersion of Claim 1.
7. The coated article surface of Claim 6 wherein the article is made of metal.
8. A method of temporarily protecting a metal surface of a workpiece, said method comprising:
(a) applying to said metal surface of a coating of a silyl-free, aqueous polyurethane dispersion derived from the reaction product of a hydroxylated polydiene resin, a diol-containing carboxylic acid salt and an aliphatic diisocyanate, which reaction product has been dispersed in water and chain extended with a diamine;
(b) curing said coating to form a film; (c) carrying out a mechanical or chemical treatment of said workpiece; and
(d) removing the film from said part.
9. The method of claim 8 wherein the diol-containing carboxylic acid salt is a salt of dimethylol propionic acid.
10. The method of claim 8 wherein the hydroxylated polydiene resin is a hydroxy terminated polybutadiene.
11. The method of claim 8 wherein step (a) is accomplished by brushing, spraying, dipping or flowing.
12. The method of claim 8 wherein step (d) is accomplished by peeling.
13 The method of claim 8 wherein step (c) comprises a chemical treatment selected from the group consisting of anodizing, plating, adhesive bonding and etching.
14. The method of claim 8 wherein step (c) comprises a mechanical treatment
. selected from the group consisting of forming, machining, drilling and routing.
15. The method of claim 8 comprising an additional step after step (b) and before step (c) of removing a portion of said film from said part.
16. The method of claim 15 wherein said portion is removed by mechanical or laser scribing.
17. The method of claim 8 wherein said metal surface is a polished alclad aluminum surface.
18. The method of claim 8 wherein said aliphatic diisocyanate is selected from the group consisting of tetramethyl xylene diisocyanate, cyclohexyl diisocyanate and 4, 4-dicyclohexyl methane diisocyanate.
19. The method of claim 8 wherein the hydroxylated polydiene resin has a number average molecular weight between 2000 and 5000.
20. The method of claim 8 wherein the hydroxylated polydiene resin has a hydroxy value between 0.5 and 1.5 milliequivalents per gram.
21. The method of claim 8 wherein the reaction product is prepared using an NCO/OH molar ratio greater than 1.4.
22. The method of claim 8 wherein the diamine is selected from the group consisting of hydrazine hydrate and ethylene diamine.
23. The method of claim 8 wherein said silyl-free, aqueous polyurethane dispersion additionally is comprised of at least one component related from the group consisting of acrylics, acrylonitrile butadiene, pigments, fillers and thickeners.
24. The method of claim 8 wherein said film after step (b) has a thickness of between 100 and 600 microns.
25. The method of claim 8 wherein step (b) is performed at a temperature of from about 25°C to about 120°C.
26. The method of claim 8 wherein said silyl-free, aqueous polyurethane dispersion is free of emulsifiers and surfactants.
27. The method of claim 8 wherein step (d) is accomplished without the use of a solvent.
28. A method of making an aqueous polyurethane dispersion comprising the steps of:
(a) reacting a hydroxylated polydiene resin, a dimethylol propionic acid salt and an aliphatic diisocyanate to form a reaction product; (b) dispersing said reaction product in water; and
(c) chain extending said reaction product with a diamine.
29. The method of claim 28 wherein step (a) is performed in the presence of a solvent selected from the group consisting of methylethylketone and tetrahydrofuran.
30. The method of claim 29 wherein said solvent is removed by distillation after step (c).
31. The method of claim 28 wherein the hydroxylated polydiene resin is a hydroxy terminated polybutadiene.
32. The method of claim 28 wherein said aliphatic diisocyanate is selected from the group consisting of tetramethyl xylene diisocyanate, cyclohexyl diisocyanate, and 4,4-dicyclohexyl methane diisocyanate.
33. The method of claim 28 wherein the hydroxylated polydiene resin has a number average molecular weight between 2000 and 5000.
34. The method of claim 28 wherein the hydroxylated polydiene resin has a hydroxy value between 0.5 and 1.5 milliequivalents per gram.
35. The method of claim 28 wherein the reaction product is prepared using an NCO/OH molar ratio greater than 1.4.
36. The method of claim 28 wherein the diamine is selected from the group consisting of hydrazine hydrate and ethylene diamine.
7. The method of claim 28 wherein step (c) is carried out at a temperature of from about 25°C to 80°C.
PCT/IB2001/001504 2001-08-17 2001-08-17 Chemically resistant aqueous polyurethane dispersions Ceased WO2003016375A1 (en)