WO2004029177A1

WO2004029177A1 - Luminescent material and light emitting diode using the same

Info

Publication number: WO2004029177A1
Application number: PCT/EP2003/010598
Authority: WO
Inventors: Hubertus T. Hintzen; Yuan-Qiang Li
Original assignee: Osram Opto Semiconductors GmbH
Current assignee: Ams Osram International GmbH
Priority date: 2002-09-24
Filing date: 2003-09-23
Publication date: 2004-04-08
Anticipated expiration: 2005-03-24
Also published as: DE60307411D1; JP3906224B2; CN1596292A; JP2005529229A; CN1311055C; TW200422375A; EP1438364B1; DE60307411T2; US20060033081A1; ATE335799T1; EP1413619A1; EP1438364A1; WO2004029177A8; US7485243B2; TWI287566B

Abstract

UV-blue excitable luminescent material consisting of a Eu-doped oxynitride host lattice with general composition MAl2-xSixO4-xNx, wherein M is at least one of an alkaline earth metal chosen from the group Ca, Sr, Ba.

Description

LUMINESCENT MATERIAL AND LIGHT EMITTING DIODE USING THE SAME

Technical Field

This invention relates to a luminescent material which is excitable in the UN- blue part of the spectral region, and more particularly, but not exclusively to a phosphor for light sources, preferably for Light Emitting Diodes (LED). The phosphor belongs to the class of rare-earth activated silicon oxy nitrides.

Background Art

So far white LEDs were realized by combining a blue-emitting diode with a yellow emitting phosphor. Such a combination has a poor color rendition, which, however, can be improved significantly by using a red-green-blue system (RGB). Such a system uses for example a red and blue emitter in combination with a green-emitting aluminate phosphor, like SrAl_0₄:Eu or BaAl₂0 :Eu, with the possible addition of Mn to Eu, whose emission maximum is around 520 nm, see US- A 6 278 135. However, the position of the excitation and emission bands of theses aluminates is not optimum. They have to be excited by short UN in the range of 330 to 400 nm.

New interesting luminescent materials are α-sialon materials doped with Eu²⁺. They have the structure MtSii2-(m+n)Al(m+n)O_nN(i6-n) with M is Ca or Y or rare earth metal. The value t is given as m/val+, wherein val+ is the charge of the valence of the ion M. For example, the val+ value of M=Sr²⁺ is 2. Thus the charge of the whole structure is fully compensated. For further details see for example "Luminescence properties of Tb, Ce, or Eu-Doped α-Sialon Materials" by J. van Krevel et al, J. Sol. St. Chem., April 2002, p. 19-24, and also "Preparation and Luminescence Spectra of Ca and rare Earth co-doped α- SiAlON Ceramics" by R.-J. Xie et al. in J. A. Ceram. Soc. 2002, p. 1229-1234, May 2002, and further on US-Pub 2002/0043926, which references all deal with Ca-Sialon of the α-Sialon type. Other types of sialon were not known at this time.

Disclosure of the Invention

It is an object of the present invention to provide a new luminescent material in accordance with the preamble of claim 1. A further object is to provide a phosphor with a fine-tuned emission which can be efficiently excited by UV/blue radiation. A further object is to provide a phosphor for use in an illumination device with at least one LED as light source, the LED emitting primary radiation in the range from 360 to 470 nm, this radiation being partially or completely converted into longer-wavelength radiation by phos- phors which are exposed to the primary radiation from the LED. A further object is to provide an illumination device which emits white light and in particular has a high color rendering. A further object is to provide a high- efficiency illumination device like a LED device which absorbs well in the range from 360 to 470 nm and is easy to produce.

These objects are achieved by the characterizing features of claim 1 and 10, respectively. Particularly advantageous configurations are given in the dependent claims.

The conversion is achieved at least with the aid of an oxynitride phosphor which originates from the class of the Eu-activated or Eu, Mn-co activated aluminates. In more detail, the disadvantages of the prior art are overcome by incorporation of nitrogen in MAl₂0₄:Eu (M = Ca, Sr, Ba), resulting in an oxynitride phosphor, usually and preferably maintaining the tridymite structure. However other structures are not excluded. More specifically, (A10)⁺ is partially replaced by (SiN)⁺ giving the general composition: MAl_-χSi_x0₄- _xN_x:(Eu or Eu,Mn). The value x is set as x ≥ 0,002 and at most x=l,5. In con- trast to the afore mentioned prior-art α -sialon type structures, which are derived from the nitride Si ₃N 4 , the structure here is more oxide-like, derived from a SiO ₂ modification, and more specifically preferably derived from a tridymite structure.

In contrast, α-sialon materials show a so-called nitridic structure, in other words they are based on Si ₃ N wherein Si-N is partially replaced by Al-O and/ or by Al-N. These different structures result in a different luminescent behavior since possible activator sites in alpha-sialons and tridymites strongly differ in the local interaction with the surrounding ions.

In case of Ca as main component of M a preferred value is 0,01 < x < 0,1. In case of Ba or Sr as main component of M a preferred value is 0,1 ≤ x ≤ 0,7. The incorporation of nitrogen increases the degree of covalent bonding and ligand-field splitting. As a consequence this leads to a shift of excitation and emission bands to longer wavelengths compared to oxide lattices. The obtained phosphors show high chemical and thermal stability. More extended fine tuning of all relevant properties can be obtained by use of a cation M which is achieved by combining several of said M metals (especially Sr and Ba), by further inclusion of Zn as part of cation M (preferably 10-40 mol-%), and/ or at least partial replacement of Si by Ge (preferably 5-25 mol%) and/ or Al by Ga (preferably 5-25 mol%). Preferably, the metal M is mainly Ba and/ or Sr for a green-emitting material, and mainly Ca for a blue- emitting material. The amount of Eu doped to cation M is between 0,1 and 25 %, preferably between 2 and 15% of M. In addition further doping with Mn for fine-tuning of relevant properties is possible with an preferred amount of at most 50% of the Eu doping.

Since these materials can convert UV-blue radiation into blue-green light due to low-energy excitation bands, they can be applied for example in white light sources (e.g. lamps), especially sources based on primarily blue- emitting LEDs (typically GaN or InGaN with emission around 430 to 470 nm) combined with a red-emitting phosphor. A suitable red-emitting phosphor is a Eu-doped silicon nitride material, like M₂Si5N8 (M = Ca, Sr, Ba), see for example WO 01/40403. Also application for colored light sources is possible.

Brief Description of the Drawings

In the text which follows, the invention is explained in more detail with reference to a plurality of exemplary embodiments. In the drawings:

Figure 1 shows a semiconductor component (LED) which serves as light source for white light, with casting resin (Figure la) and without casting resin (Figure lb);

Figure 2 shows an illumination device with phosphors in accordance with the present invention;

Figure 3 shows the emission spectrum and reflection spectrum of a phosphor in accordance with the present invention;

Figures 4 to 8 show the emission spectra and reflection spectra of further phosphors in accordance with the present invention; Figure 9 shows the relationship between the volume of a unit cell and the value of x.

Best Mode for Carrying Out the Invention

By way of example, a structure similar to that used in WO 01/40403 is described for use in a white LED together with an InGaN chip. The structure of such a light source for white light is specifically shown in Figure la. The light source is based on a semiconductor component (chip 1) of type InGaN with a peak emission wavelength of 400 nm, having a first and a second electrical connection 2,3, which is embedded in an opaque base housing 8 in the region of a recess 9. One of the connections 3 is connected to the chip 1 via a bond- ing wire 4. The recess has a wall 7 which serves as reflector for the blue primary radiation of the chip 1. The recess 9 is filled with a potting compound 5 which contains a silicone casting resin (or epoxy casting resin) as its main constituents (pref. more than 80 by weight) and further comprises phosphor pigments 6 (pref. less than 15% by weight). There are also further small amounts of, inter alia, methyl ether and Aerosil. The phosphor pigments are a mixture of three pigments which emit blue, green and red light with the green phosphor being in accordance with the invention.

Fig. lb shows an embodiment of a light source with a semiconductor component 10 in which the conversion into white light is effected by means of phosphor conversion layers 16 which are applied directly to the individual chip. On top of a substrate 11 there are a contact layer 12, a mirror 13, a LED chip 14, a filter 15 and a phosphor layer 16, which is excited by the primary radiation of the LED, and converts it into visible long-wave radiation. This structural unit is surrounded by a plastic lens 17. Only the upper contact 18 of the two ohmic contacts is illustrated. Primary UN radiation of the LED is around 400 nm and secondary radiation is emitted by a first phosphor in ac- cordance with the invention M(_-c)A12_-xSiχθ4-χN_x:Dc with D being Eu or Eu,Mn. Especially preferred is using BaAl_2-χSi_x0₄-χN_x: (10%) Eu²⁺, emitting around 525 nm (or in the language of the a.m. general formula c= 0,1 and D= Eu), and by a second phosphor using a Nitridosilicate emitting orange-red.

Figure 2 shows an illumination device 20. It comprises a common support 21, to which a cubical outer housing 22 is adhesively bonded. Its upper side is provided with a common cover 23. The cubical housing has cutouts in which individual semiconductor components 24 are accommodated. They are blue emitting light-emitting diodes with a peak emission of around 450 to 470 nm. The conversion into white light takes place by means of conversion layers 25 which are arranged on all the surfaces which are accessible to the blue radiation. These include the inner surfaces of the side walls of the housing, of the cover and of the support. The conversion layers 25 consist of phosphors which emit in the red spectral region, and in the green spectral region using a phosphor according to the invention and mixing up together with the non- absorbed part of the primary radiation blue primary into white light.

Eu₂0₃ (with purity 99.99%), BaCOs (with purity > 99.0%), SrCO. (with purity > 99.0%), CaCOs (with purity > 99.0%), A1₂0₃ (with purity 99,9%), Si0₂ and Si₃N₄ were used as commercially available starting materials for the produc- tion of the new inventive phosphors. The raw materials were homogeneously wet-mixed in the appropriate amounts by a planetary ball mill for 4-5 hours in isopropanol. After mixing the mixture was dried in a stove and ground in an agate mortar. Subsequently, the powders were fired in molybdenum crucibles at 1100-1400 °C under a reducing nitrogen/ hydrogen at- mosphere in a horizontal tube furnace. After firing, the materials were characterized by powder X-ray diffraction (copper K-alpha line).

All samples show efficient luminescence under UN-blue excitation with e- mission maxima in the blue (in case of M = Ca), especially 435^" to 445 nm, or green (for M = Sr or Ba), especially in case of Ba 495 to 530 nm and in case of Sr 515 to 575 nm. Two typical examples of emission and excitation spectra can be seen in Fig. 3 and Fig. 4. Figure 3 shows emission spectra and excitation spectra of SrAl₂-χSiχθ4-_xN_x:Eu with varying value of x. Figure 4 shows emission/ excitation spectra of BaAl_2-xSiχ0 -χN_x:Eu with varying value of x.

By varying the amount of nitrogen, the emission can be shifted in the range 495-575 nm. Esp. Sr is sensitive to shifting (Fig. 3), while the top of the excitation band can be shifted from below 400 nm up till 430 to 465 nm, preferably to 440 nm, see M =Ba (Fig. 4). The observed shift to higher wavelengths is the result of a center of gravity of the Eu 5d band at lower energy and a stronger ligand-field splitting of the Eu 5d band.

Additional fine tuning can be achieved by incorporation of Zn as an addition to cation M, preferably not more than 30%, and at least partial replacement of Al by Ga, preferably not more than 25%, and/ or Si by Ge, preferably not more than 25 % .

Table 1

In the following the synthesis procedures for MA12-xSixO4-xNx:(10%) Eu2+ (M = Ca, Sr, Ba) are given. Possible starting materials are shown in table 1.

All the oxynitride phosphors including tridymite are synthesized according to the following reaction equation (gas phases neglected):

(l-y)MCOs + (2-x)/2 A1₂0₃ + x/4 Si₃N₄ + x/4 Si0₂ + y/2 Eu₂0₃ - Mι-yEu_yAl_2-χSiχθ4-χN_x

with M = Ca, Sr, Ba alone or in combination. An example is y =0,1.

For example, the compositions of Ba.₉Euo.ιAl2-χSiχθ4-χN_x are shown in the following table 2.

Table 2 (Unit: gram)

The detailed experimental results showed that the luminescence properties of the phosphors were almost independent of exact Si0₂ content. However, reducing Si0₂ content in an appropriate amount (i.e., it can be reduced up to 1/60 of the calculated amount Siθ2) strongly increases phase purity as well as efficiency.

The powder mixture is fired for several hours in Mo crucibles at 1100-1400 °C in a reducing atmosphere of N₂ with a small amount of H₂ (10%) in the hori- zontal tube furnaces. Further excitation and emission spectra of samples elucidating the role of S-O2 reduction are shown in Figures 5 to 8.

Embodiment according to Fig. 5: Bao.9Euo.1Al2-xSixO4.xNx with x = 0.3 and no Si0₂ reduction. The phosphor was excited with λ_ex = 440 nm for the emis- sion spectrum and monitored at λmon = 530 nm for the excitation spectrum. Its main phase has BaA_2θ4 structure.

Embodiment according to Fig. 6: Bao.9Euo.ιAl2-_xSi_xθ4_-xNχ with x = 0.3, Siθ2 amount reduced to one-fourth of calculated Siθ2 amount (λ_eXc = 440 nm, λ on = 530 nm). Its main phase has BaAhθ4 structure.

Embodiment according to Fig. 7: Bao.9Euo.ιAl₂-χSi_xθ4-χN_x with x = 0.5 and S1O2 amount reduced to 1/16 of calculated S1O2 amount (λ_χ_C = 440 nm, λmon = 530 nm). Its main phase has BaAl2θ₄ structure.

Si₃N₄ was used as the source of (SiN)⁺ according to the following reaction [1]:

MCO3 + (2-x)/2 AI2O3 + x/4 Si₃N₄ + x/4Si0₂ ^ MAl₂-χSiχθ4-χNχ {+ CO21}

(M = Ca, Sr, Ba) .

With the atomic radius decreasing from Ba to Ca it was found that the replacement of (A10)⁺ by (SiN)⁺ by this reaction became more difficult. Lattice parameters results show that the maximum solubility of N in BaA θ4 with tridymite structure was about x ~ 0.6. Fig. 9 shows the relationship between unit cell volume and x values of BaA12-xSix04-xNx with tridymite structure. As expected, from the smaller Si-N distance as compared to the Al-O distance, the unit cell volume decreases with increasing x as shown in Fig. 9. For x values remarkably larger than 0.6, the unit cell volume remains almost constant, and secondary phases are observed. So, good results can be achieved with Ba aluminate and with x up to about 0,6 without the need to adapt the Siθ2 amount.

Also good results are seen with Sr aluminate. Reduction (expressed as amount y) of the Si0₂ content results in an non-stoichiometric aluminate of the type MAl2-χSi_x-_yθ4-x-2yN_x:Eu , preferably with y < 0,25 x. Best performance is achieved with Siθ2 correction, and with x up to 0,5. The same holds true for Ca aluminate, however smaller x values are preferred below 0,05.

The luminescence properties of MAl2-χSi_xθ4-_xN_x:10%Eu²⁺ are now discussed in more detail. Fig. 8 shows the excitation and emission spectra of MAl2-χSi_xθ4_-xN_x:Eu²⁺ (M = Sr, Ca). The Siθ2 content is not reduced. In more detail, Fig. 8a shows excitation and emission spectra of SrAl2-χSi_xθ4-_xN_x:Eu²⁺(10%) and Figure 8b excitation and emission spectra of CaAl2-_xSi_x0₄-_xN_x:Eu²⁺ (10%), each with various x.

Corresponding to the results of the relationship between unit cell volume and x values of MAl2-χSi_xθ4-χN_x, the emission bands shift more or less to the longer wavelength depending on the cation. In case of Ba the shift is typically from 495 to 530 nm, in case of Sr the shift is typically from 515 to 575 nm and in case of Ca the shift is typically from 440 to 445 nm. For BaAl₂-_xSi_xθ4-χNχ: (10%) Eu²⁺, the emission band shifts from about 497 to 527 nm with increasing content x of incorporated nitrogen. The position of the excitation band shifts accordingly from 385 to 425 nm.

For MAl₂-χSi_xθ4-_xN_x: (10%) Eu²⁺, with M is at least one of Sr or Ca, the amount of (SiN)⁺ does not essentially increase the emission and excitation wavelengths because almost no shift in the lattice parameters is observed. The maximum shift of emission bands of Eu is less than 10 nm corresponding to the fact of small nitrogen incorporation in case of M = Ca. Therefore, a small amount of (SiN)⁺ incorporation can only exert weak influence to the local coordination of the Eu²⁺ ion. This discussion is understood with the addition of the normal stoichiometric amount of Siθ2.

However, it turned out very surprisingly that the use of understoichiometric amount of Siθ2 is advantageous in several cases. The effect of an reduced amount of Siθ2 in the reaction (1) to the incorporation of N and to the luminescence properties is most pronounced in the case of SrAl2-χSi_xθ4-_xN_x:Eu²⁺ (10%). The reason is not yet fully understood. When the amount of Siθ2 which should be used in reaction (1) is taken about a factor 60 lower, it is found that an increased amount of (SiN)⁺ is incorporated into SrAl₂0₄ lattice with stuffed tridymite structure. The maximum solubility is x « 0.5 (Table 1). As a result of N incorporation the Eu emission bands shift to longer wavelengths, up to 575 nm (Fig. 3). An evident excitation shoulder at 430 nm appears at the maximum solubility of nitrogen (x = 0,3 ... 0,5), as shown in Fig. 3.

Instead of a structure derived from tridymite, also a structure derived from the structure of SrSiAl2θ₃N₂ is possible. This compound was discovered by Schnick in 1998. It is isotopic with silicate nitrides of the type LnSi₃Ns ( with Ln=La, Ce, Pr, Nd).

Claims

ClaimsWhat is claimed is:

1. Luminescent material, preferably a phosphor for LED-applications, which is excitable in the UN-blue region from 360 to 470 nm, characterized by a Eu- doped host lattice with general composition MAl2-χSi_xθ4-χΝχ, wherein M is at least one of an alkaline earth metal chosen from the group Ca, Sr, Ba, with x ≥ 0,002 and x < 1,5, pref. x below 0,7, and with a proportion of Eu from 0,1 to 25% of M.

2. UV-blue excitable luminescent material according to claim 1, wherein the host lattice is derived from a tridymite structure.

3. UV-blue excitable luminescent material according to claim 1, wherein M is Strontium and/ or Barium in order to achieve green emission.

4. UV-blue excitable luminescent material according to claim 1, wherein M is Calcium in order to achieve blue emission.

5. UV-blue excitable luminescent material according to claim 1, wherein M is a mixture of at least two of these metals.

6. UV-blue excitable luminescent material according to claim 1, wherein M comprises in addition Zn, preferably up to 40 mol-%.

7. UV-blue excitable luminescent material according to claim 1, wherein Al is replaced fully or partially by Ga.

8. UV-blue excitable luminescent material according to claim 1, wherein Si is re- placed fully or partially by Ge, preferably not more than 25% .

9. UV-blue excitable luminescent material according to claim 1, wherein the host material is further doped with Mn, the amount of co-doped Mn being preferably at most up to 50% of the Eu doping.

10. Light source (20) with a UV-blue excitable luminescent material according to one of the preceding claims.

11. Light source according to claim 10, wherein the primary emitted light is blue and the UV-blue excitable luminescent material according to claims 1-9 is combined with other phosphors, esp. a red emitting phosphor, in order to convert part of the primary emitted light into secondary emitted light of longer wave- length resulting in emitting white light..

12. Light source according to claim 10, wherein the primary emitted radiation is UV and the UV-blue excitable luminescent materials according to claims 1-9 are combined with other phosphors, esp. a red and blue emitting phosphor, in order to convert the primary emitted radiation into secondary emitted light of longer wavelength resulting in emitting white light.

13. Light source according to claim 10, wherein the light source is an illuminating device with at least one LED.