WO2004088671A1 - 複合高分子電解質組成物 - Google Patents

複合高分子電解質組成物 Download PDF

Info

Publication number
WO2004088671A1
WO2004088671A1 PCT/JP2004/003447 JP2004003447W WO2004088671A1 WO 2004088671 A1 WO2004088671 A1 WO 2004088671A1 JP 2004003447 W JP2004003447 W JP 2004003447W WO 2004088671 A1 WO2004088671 A1 WO 2004088671A1
Authority
WO
WIPO (PCT)
Prior art keywords
electrolyte composition
polymer electrolyte
cation
monomer
composition according
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2004/003447
Other languages
English (en)
French (fr)
Inventor
Naoya Ogata
Hiroshi Kagawa
Makiko Sada
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Trekion Co Ltd
Original Assignee
Trekion Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Trekion Co Ltd filed Critical Trekion Co Ltd
Priority to JP2005504154A priority Critical patent/JP4674660B2/ja
Priority to CN2004800020565A priority patent/CN1934657B/zh
Priority to US10/551,330 priority patent/US7732099B2/en
Priority to EP04720736.0A priority patent/EP1612809B1/en
Priority to CA2507438A priority patent/CA2507438C/en
Publication of WO2004088671A1 publication Critical patent/WO2004088671A1/ja
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

高いイオン伝導度と向上した力学的性質を有する全固体高分子電解質組成物が提供される。この電解質組成物は重合性官能基を導入した４級アンモニウム塩溶融塩と電荷移動イオン源を含む単量体組成物を高分子補強材料の存在下重合することによって製造される。高分子補強材料は，単量体組成物と補強材料を適当な有機溶媒に溶解し，この溶液を重合することによりポリマーブレンドの形で複合化することができる。代って単量体組成物を補強材料の多孔質シートもしくはフィルムに含浸し，重合することによって複合化することもできる。電荷移動イオン源としてリチウム塩を選ぶことによりリチウムイオン電池用の，プロトン供与体を選ぶことにより燃料電池用の，レドックスイオン対を選ぶことにより色素増感太陽電池用の電解質が得られる。電荷移動イオン源を含まない本発明の高分子電解質組成物は電解キャパシタの電解質としても有用である。

Description

明 糸田 書 複合高分子電解質組成物 〔本発明の分野〕
本発明は， 例えばリチウムイオン電池， 燃料電池， 色素増感太陽 電池， 電解キャパシ夕などの電気化学的デバイスにおいて電極間に 配置される複合高分子電解質組成物に関する。
〔背景技術〕
リチウム二次電池には， リチウム塩を含んでいる非水電解液が一 般に使用されている。 この溶液は， エチレンカーボネート， プロピ レンカーボネート， ジメチルカーポネート， ジェチルカーポネー ト， メチルェチルカーボネートなどのカーボネート類， ァープチ口 ラク トンなどのラク トン， テトラヒ ドロフランなどのエーテルのよ うな非プロ トン性の極性溶媒にリチウム塩を溶かしたものである。 しかしながらこれら有機溶媒は揮発し易く， 引火性であり， 過充 電， 過放電， 及び短絡などの際に安全性の問題がある。 また液体電 解液は電池を液密にシールする際の取扱いが困難である。 ゲル化し た非水電解液を使用しても有機溶媒の揮発および引火危険性の問題 は解消せず， ゲルから相分離した電解液が漏れる問題は依然残って いる。
最近 4級アンモニゥムカチオンを含む常温溶融塩にリチウム塩を 溶かした非水電解質を使ったリチウムニ次電池が提案されている。 例えば特開平 1 0— 9 2 4 6 7， 特開平 1 0— 2 6 5 6 7 4， 特開 平 1 1 — 9 2 4 6 7， 特開 2 0 0 2 — 1 1 2 3 0参照。 常温溶融塩 は常温で液状でありながら， 不揮発性で且つ不燃性であるため安全 であるが， マトリックスポリマーによりゲルとしても液体を含むた め力学的性質が不十分であり， かつ液体が相分離することがあるの で， 取扱上の問題および電池設計上の問題は依然残っている。
イオン伝導性溶融塩を形成するィミダゾリゥム塩にビニル基を導 入し， この単量体を重合して全固体高分子電解質を製造する提案も なされている。 特開平 1 0— 8 3 8 2 1および特開 2 0 0 0 — 1 1 7 5 3参照。 しかしながらこの高分子電解質も充分な力学的強度を 持っていない。
従って高いイオン伝導度と満足な力学的性質を持っている安全な 高分子電解質に対する要望は依然残っている。
〔本発明の開示〕
本発明は， a ) 4級アンモニゥムカチオンとフッ素含有ァニオン からなる 4級アンモニゥム塩構造と重合性官能基を持っている溶融 塩単量体， および電荷移動イオン源を含んでいる単量体組成物を， 電気化学的に不活性な高分子補強材料の存在下で重合することによ り製造された複合高分子電解質組成物を提供することによって上の 要望を満たす。
上記電荷移動イオン源は， 本発明の高分子電解質組成物がリチウ ムイオン電池に使用される場合は， リチウムカチオンとフッ素含有 ァニオンとの塩であり， 燃料電池に使用される場合はプロ トン化し たフッ素含有ァニオンである。 色素増感太陽電池に使用される場合 は I ノ 1 3 ― ペアに代表されるレドックスシステムである。
本発明の原理は， 電解キャパシ夕の電解質にも適用することがで きる。 この場合は電荷移動イオン源を含まない前記単量体組成物 を， 前記高分子補強材料の存在下重合することによって得られる。 ポリフッ化ビニリデンに代表される電気化学的に不活性な高分子 補強材料を溶融塩単量体のポリマーと複合化させるにはいくつかの 方法がある。 第 1の方法はイオン源を含んでいる溶融塩単量体と高 分子補強材料を適当な溶媒に溶解し， この溶液をフィルム状に流延 した後重合する方法である。 第 2の方法は基本的には第 1の方法と 同じであるが， あらかじめ炭素一炭素間二重結合のような架橋点と なる官能基を導入した高分子補強材料を使用する点で第 1の方法と 異なっている。 第 3の方法は高分子補強材料の多孔質シ一トもしく はフィルムを使用する。 このシ一トを溶融塩単量体溶液で含浸し， シートに含まれる単量体を重合して複合化する。 いずれの場合も重 合は熱， 光 （紫外線） または電子線照射によって行う ことができ る。
重合前の溶融塩単量体を含む溶液をガラス， ポリエステルなどの 非接着の基材上にフィルム状に流延し， 重合後剥離して独立膜とし て使用することもできるし， 代って電極の活物質面に塗布し， その 状態で重合して電極と一体化したフィルムとして形成しても良い。
このようにして形成した本発明の高分子電解質フィルムは， 高分 子補強材料の存在によってそれを含まないフィルムに比較して引張 り強度に代表されるその力学的性質が著しく向上する。 もし望むな らば溶融塩単量体に少割合の多官能単量体を共重合し， 力学的性質 をさらに向上させることができる。 補強の結果， 本発明の複合高分 子電解質組成物を使ってコンパク トでエネルギー密度の高い高性能 電池等に組立てることが可能になる。
〔好ましい実施態様〕 4級アンモニゥムカチオンとフッ素原子含有ァニオンとから成る 4級アンモニゥム塩構造及び重合性官能基を含む単量体の塩構造と は， 脂肪族， 脂環族， 芳香族， あるいは複素環の 4級アンモニゥム カチオンとフッ素原子含有のァニオンから成る塩構造である。 ここ でいう 「 4級アンモニゥムカチオン」 とは， 窒素のォニゥムカチォ ンを意味し， イミダゾリウム， ピリジゥムのような複素環ォニゥム イオンを含む。 下記アンモニゥムカチオン群から選ばれた少なく と も 1つのアンモニゥムカチオンと下記ァニオン群から選ばれた少な く とも 1つのァニオンから成る塩構造を挙げることが出来る。
(アンモニゥムカチオン群） ピロリウムカチオン， ピリジニゥム カチオン， イミダゾリウムカチオン， ピラゾリウムカチオン， ベン ズイミダゾリウムカチオン， インドリウムカチオン， カルバゾリウ ムカチオン， キノ リニゥムカチオン， ピロリジニゥムカチオン， ピ ペリジニゥムカチオン， ピペラジニゥムカチオン， アルキルアンモ ニゥムカチオン （但し， 炭素数 1〜 3 0の炭化水素基， ヒ ドロキシ アルキル， アルコキシアルキルで置換されているものを含む） いずれも， Nおよび Z又は環に炭素数 1〜 1 0の炭化水素基， ヒ ド ロキシアルキル基， アルコキシアルキル基が結合しているものを含 む。
(ァニオン群） B F 4 , P F 6 , C n F 2 n + 1 c 02 (但し nは 1〜 4の整数） ， C n F 2 n + i S 03 (但し nは 1〜 4の整数） ，
( F S 02 ) 2 , ( C F 3 S 02 ) 2 , ( C 2 5 S 02 ) 2 ;
( C F 3 S 02 ) 3 c , C F 3 S 02 - N - C〇 C F 3 , R— S O 2 - N - S 02 C F 3 (I ま脂肪族基） ， A r S 02— N _ S 02 C F 3 (A rは芳香族基） 上記のアンモニゥムカチオン及びァニオン種は耐熱性， 耐還元性 又は耐酸化性に優れ， 電気化学窓が広く とれ， 電池やキャパシ夕に 用いるために好ましい。
単量体における重合性官能基としては， ビニル基， アクリル基， メ夕クリル基， ァリル基などの炭素一炭素不飽和基， エポキシ基， ォキセタン基などの環状アルコキシド基ゃイソシァネート基， 水酸 基， 力ルポキシル基などを例示できる。
特に好ましいアンモニゥムカチオン種としては， 1 一ビニル— 3 一アルキルイミダゾリウムカチオン， 4 —ビニル— 1 一アルキルピ リジニゥムカチオン， 1 一アルキル一 3 —ァリルイミダゾリウムカ チオン， 1 一 （4 一ビニルベンジル） 一 3 —アルキルイミダゾリウ ムカチオン， 1 一 （ビニルォキシェチル） — 3 —アルキルイミダゾ リウムカチオン， 1 —ビニルイミダゾリウムカチオン， 1 —ァリル イミダゾリウムカチオン， N—ァリルべンズイミダゾリウムカチォ ン， ジァリル—ジアルキルアンモニゥムカチオンなどを挙げること が出来る。 伹し， アルキルは炭素数 1〜 1 0のアルキル基である。 特に好ましいァニオン種としてはビス { (トリフルォロメチル） スルフォニル }ァミ ド ァニオン， 2， 2， 2 — トリフルオロー N 一 （トリフルォロメチルスルフォニル） ァセ 卜アミ ド ァニオン， ビス { (ペンタフルォロェチル） スルフォニル } アミ ド ァニオン, ビス { (フルォロ） スルフォニル }ァミ ド ァニオン， テトラフルォ ロボレート ァニオン， トリ フルォロメタンスルフォネート ァニ オン， などを挙げることが出来る。
特に好ましい単量体としては， 1 ービニルー 3 —アルキルイミダ ゾリゥム ビス { (ト リ フルォロメチル） スルフォニル }ァミ ド （伹 し， アルキルは C 1〜 C 1 0 ) ， 1〜ビニルー 3—アルキルイミダ ゾリゥム テ トラフルォロポレート （伹し， アルキルは C 1〜（： 1 0 ) , 4ービニルー 1 一アルキルピリジニゥム ビス { (ト リ フル ォロメチル） スルフォニル }アミ ド （但し， アルキルは C 1〜C 1 0 ) ， 4 _ビニル— 1 一アルキルピリジニゥム テトラフルォロポ レート （伹し， アルキルは C 1〜C 1 0 ) ， 1— (4一ビニルベン ジル） — 3—アルキルイミダゾリウム ビス { (トリフルォロメチ ル） スルフォニル }アミ ド （但し， アルキルは C 1〜 C 1 0 ) , 1 一 （ 4—ビニルベンジル） — 3—アルキルイミダゾリウム テトラ フルォロポレート （但し， アルキルは C 1〜（： 1 0 ) ， 1ーグリシ ジルー 3—アルキル一イミダゾリウム ビス { (トリフルォロメチ ル） スルフォニル }アミ ド （但し， アルキルは C 1〜 C 1 0 ) , 1 ーグリシジルー 3—アルキル—イミダゾリウム テトラフルォロボ レート （但し， アルキルは C 1〜 C 1 0 ) , N—ビニルカルバゾリ ゥム テトラフルォロポレートなどを例示出来る。
リチウムイオン電池の電荷移動イオン源はリチウム塩であるが， 本発明では， 好ましくは下記のリチウムカチオンとフッ素原子含有 ァニオンとからなるリチウム塩を使用することが出来る。
L i B F 4， L i P F 6 , C n F 2 n + 1 C〇 2 L i (但し nは 1〜 4の整数） ，
C n F 2 n+ i S 03 L i (但し nは 1〜 4の整数） ， （F S〇 2)
2 N L i ,
( C F 3 S O 2 ) 2 N L i , ( C 2 F 5 S O 2 ) 2 N L i ,
( C F 3 S O 2 ) 3 C L i ， L i (C F 3 S〇 2— N— C O C F
3 ) ， L i (R— S〇 2 _N— S〇 2 C F 3) (Rは脂肪族基） ，
L i ( A r S〇 2 — N— S O 2 C F 3 ) (A rは芳香族基）
又， 燃料電池の電荷移動イオン源 （プロ トン源） は， 上の溶融塩単 量体の 4級アンモニゥム塩構造のァニオン種に相当するプロ トン供 与体である。
色素増感太陽電池の電荷移動イオン源は典型的には I— / 13 一 レドックペアであるが， 他にも B r— ZB r 3 — ペア， キノン Zハ ィ ドロキノンペアなどがある。
高分子補強材料は， 耐酸化性， 耐還元性， 耐溶剤性， 低吸水性， 難燃性などの電気化学的ゾ化学的安定性や耐熱性， 耐寒性などの温 度特性， 更に力学的特性 （強伸度， 柔軟性） に優れ， 且つ加工性に 優れたポリマーである。 例えば， ポリテトラフルォロエチレン， ポ リフッ化ビニリデンなどのフッ素系ポリマー， ポリエチレン， ポリ プロピレンなどのポリオレフイ ン， ポリアクリ ロニトリル， ポリス チレンなどのビニル系ポリマ一, ポリスルフォン, ポリエーテルス ルフォンなどのポリスルフォン系ポリマー， ポリエーテルケトン， ポリエーテルエーテルケトンなどのポリエーテルケトン系ポリマー, ポリエーテルイミ ド， ポリアミ ドイミ ド， ポリイミ ドなどのポリイ ミ ド系ポリマー （いずれも共重合ポリマーを含む） を挙げることが 出来る。
好ましい高分子補強材料はフッ素系ポリマーであり， 特に好まし いのはポリフッ化ビニリデン及びその共重合ポリマー， その変性ポ リマーである。 その分子量は数平均分子量として 2 0 0 0〜 2 0 0 0 0 0 0 , 好ましくは 3 0 0 0〜 1 0 0 0 0 0 , 特に好ましくは， 5 0 0 0〜 5 0 0 0 0である。 以下にリチウムニ次電池に使用される電解質組成物を例にとって その調製方法を説明する。 この方法はリチウム塩を他の電荷移動ィ オン源に変更することにより燃料電池または色素増感太陽電池用の 電解質組成物にも適用できることは当業者には自明であろう。
高分子補強材料を複合化する方法には， 既に該材料の多孔質シー トもしくはフィルムにリチウム塩を含む溶融塩単量体で含浸し， そ の状態で重合反応に服せしめる方法や， リチウム塩を含んでいる溶 融塩単量体に高分子補強材料の繊維を分散し， 重合反応に服させる 方法が含まれる。
この場合， 高分子補強材料は， 具体的には織物ゃ不織布， 多孔質 フィルムやシート類であり， 厚さは 5〜 1 0 0 m, 好ましくは 1 0〜 5 0 mである。 不織布の透気度 （ J I S— 1 0 9 6による） は 5〜4 0 <:で 71112 ' 3 6 ( ， 多孔質フィルムの孔径は 0. 0 5 m〜 l ^m， 好ましくは 0. 0 5 m〜 0. 5 ΠΙ， 気孔率は 2 0 %〜 8 0 %, 好ましくは 3 5 %〜 6 0 %である。 これらの補強材 料は既存の製法， 設備で製造でき， 又市販品を利用出来る。
さらに， 溶融塩単量体， リチウム塩， および高分子補強材料をジ メチルァセタミ ドのような適切な溶媒に溶かし， この溶液をガラス やポリエステルフィルムのような基材に流延またはコ一ティ ング し， 重合後剥離して複合化した高分子電解質組成物の薄膜を得るこ ともできる。 補強材料の高分子の種類によっては溶剤を使用するこ となく溶融によって単量体と複合化することもできるであろう。 溶融塩単量体のポリマーと補強材料のポリマ一ブレンドを形成し ている電解質組成物の場合， 高分子補強材料の割合は， 力学的性質 とイオン伝導度との最適なバランスが得られるように決定される。 溶融塩単量体に対する補強材料の重量比は， 一般的には 0. 1〜 0. 8 , 特に好ましくは 0. 3 5〜 0. 6 5の間にある。 特定の溶 融塩単量体と特定の高分子補強材料の組合わせについては， 力学的 性質とイオン伝導度の最適なバランスは実験的に定めることができ る。
補強材料の多孔質シートもしくはフィルムを溶融塩単量体で含浸 する場合には， リチウム塩を含んだ高分子電解質が連続相を形成す るので， 力学的性質とイオン伝導度のバランスを最適化する必要は ない。
同様にブレンドタイプの電解質組成物の場合， リチウム塩と力学 的性質の最適のバランスは溶融塩単量体に対するリチウム塩の比に 依存する。 この比は重量で一般に 0. 0 5〜 0 . 8， 好ましくは 0. 1〜 0. 7， 特に好ましくは 0. 1 5〜 0. 5の範囲である。 特定の溶融塩単量体と特定のリチウム塩の組合わせの最適比は実験 的に容易に決めることができる。 多孔質シートもしくはフィルムを 使用する場合は， 上に記載した理由により， 溶融塩単量体に対する リチウム塩の比はイオン伝導度を最大にするのに充分な量でよい。 溶融塩単量体は単独重合， またはこれ共重合し得る単量体と共重 合させることができる。
好ましい態様の 1つは， 溶融塩単量体と反応する官能基を有する 高分子補強材料を用いたグラフ ト架橋重合体の形成である。 共重合 する単量体は 2種類以上の溶融塩単量体を用いてもよいし， 塩構造 を含まない単量体や更には複数の重合性官能基を有する多官能単量 体であってもよい。
本重合反応は， 単量体熱重合開始剤や硬化剤を加え， 通常 4 0 T: 〜 2 0 0 °Cに加熱して行なう。 重合性官能基が炭素一炭素不飽和基 である場合， 熱重合開始剤としては， ベンゾィルパーオキサイ ド， ジクミルパーォキサイ ド， ジー t 一ブチルパーォキサイ ド， 1 , 1 一ビス （ t 一ブチルパーォキシ） シクロへキサン， キュメン八イ ド 口パーオキサイ ドなどのパーオキサイ ド類， 2 , 2 ' —ァゾビスィ ソブチロニトリル， 2， 2 ' —ァゾビス （ 2 , 4 —ジメチルバレロ 二トリル） などのァゾビス化合物， 過硫酸アンモニゥムなどの無機 系開始剤などを挙げることが出来る。
重合開始剤の使用量は， 通常重合性単量体の総重量に対して 0 . 1〜 1 0 %， 好ましくは， ：！〜 5 %である。
重合性官能基がエポキシ基である場合， 硬化剤としてアミン類ゃ酸 無水物， カルボン酸， 反応触媒としてアルキルイミダゾール誘導体 を用いることが出来る。
重合させるために紫外線 （光重合開始剤を使用） や電子線などの 放射線を照射することも出来る。 電子線重合は， 高分子補強材料自 体の架橋反応や単量体の補強材料へのグラフ ト反応も期待でき， 好 ましい態様である。 照射量は 0 . 1〜 5 0 M r a d， 好ましくは 1 〜 2 0 M r a dである。
溶融塩と共重合可能な重合性官能基を 2個以上含む多官能単量体 の例は， ジビエルベンゼン， ジァリルフタレート， エチレングリコ ールジ （メタ） ァクリ レート， ジエチレングリコールジ （メタ） ァ クリ レート， トリエチレングリコールジ （メタ） ァクリ レート， ト リメチロールプロパントリ （メタ） ァクリレート， ペン夕エリスリ トール テトラ （メタ） ァクリ レート， トリアリルイソシァヌ レ一 ト， トリァリルシアヌ レー ト， ジァリル一ジメチルアンモニゥム ビス一 { (トリフルォロメチル） スルフォニル }ァミ ド， ジァリル一 ジメチルアンモニゥムテトラフルォロポレート， 2 , 2—ビス （グ リシジルォキシ） フエニルプロパンなどがある。 これらの多官能モ ノマ一は溶融塩単量体の 0 . 5〜 1 0モル％の量で使用し得る。 本発明の複合高分子電解質組成物は， ポリマーブレンドの場合， 電荷移動ィオン源を含んでいる溶融塩単量体と補強材料ポリマーと がミク口に相分離し， それぞれのイオン伝導性に力学的性質を付与 する機能を果たしているものと考えられる。 補強材料の多孔質シー トもしくはフィルムを含む場合は， 電荷移動イオン源を含む溶融塩 単量体の連続相がイオン伝導性を担っている。
本発明の複合高分子電解質組成物は， 例えばリチウムイオン電 池， 燃料電池， 色素増感太陽電池， 電解キャパシ夕などの電気化学 デバイスの対向する電極間にサンドイッチされる。 それぞれのデバ イスに使用される電極はこれらの技術分野において良く知られてい る。
例えば， リチウムイオン電池には， 典型的には黒鉛であるリチウ ムイオンを吸蔵放出する炭素材料よりなる活物質層を備えた負極 と， L i C o〇2 ， L i F e O， L i N i n C ο ι - η , L i M n 2 〇4 などに代表されるリチウムイオンを吸蔵放出するリチウムを含 む複合金属酸化物よりなる活性物質層を有する正極が使用される。 負極洁物質として金属リチウムもしくはその合金が使用される場合 は， 正極活物質は二酸化マンガン， T i S 2 , M o S 2 , N b S 2 , Μ ο Ο 3 および V 2〇5のような L i を含まない金属酸化物もし くは硫化物を使用することができる。
燃料電池では， 一般に P t に代表される触媒を付与した多孔質電 W
極が使用される。 色素増感太陽電池の作用極として導電性表面を有 する基板上に形成した T i 〇2 ， Z n Oなどの酸化物半導体膜に色 素を吸着させた半導体電極が用いられる。 対極は白金蒸着ガラス基 板に代表される導電性電極である。 キャパシタの電極対は従来の液 型電解キャパシ夕に用いられている電極対と同じものを使用し得 る。
〔実施例〕
以下に限定を意図しない実施例によって本発明を例証する。 これ ら実施例はリチウムイオン電池の電解質を意図したものであるが， 当業者は電荷移動イオン源を上に述べたように変更することによつ て他の電気化学デバイスに適用するためこれら実施例を容易に修飾 することができる。
実施例中すベての部および％は特記しない限り重量基準による。 実施例中の測定は下記の方法によつて行った。
イオン伝導度 ： 電極面積 0. 9 5 c m 2の白金電極間に試料を挟 み， 室温， 6 5 % RHで， 交流インピーダンス法 （ 0. I V， 周波 数 1 Η ζ〜 1 0 ΜΗ ζ ) により膜抵抗を測定し， イオン伝導率を算 出した。
引張り強度 ： A&D社製， 引張り試験機テンシロン R T 1 3 5 0を 用い， 2 3 °C， 5 c m/m i n . で測定した。
また実施例中で合成した化合物は I Rスぺク トル， NMRスぺク ト ルで同定した。
〔実施例 1〕 1 ーメチルー 3— （ 4一ビニルベンジル） イミダゾリ ゥム ビス { ( ト リ フルォロ メチル） スルフ ォニル } アミ ド _CMVBI · TFSIと略—す〕—の合成 1 一メチルイミダゾ一ル 3 7. 0 g ( 0. 4 5 m o 1 ) を 2 0 0 m l の 1， 1 , 1 一 トリクロロェタンに溶解し， 室温で攪拌しなが ら， p—クロルメチルスチレン 6 8. 7 g ( 0. 4 5 m o 1 ) を
1 0 0 m l の 1， 1， 1 — トリクロロェタンに溶解した溶液を 1時 間かけて滴下後， 更に 1 0時間， 65°Cで撹拌を続けて反応を行った, 生成物を分離し， 各 1 0 0 m l の 1 , 1 , 1 一 トリクロロェタンで 2回洗浄後， 6 5 °C， 0. 1 mmで 2時間， 乾燥し， 淡黄色の固体 1 —メチルー 3 — ( 4—ビニルベンジル） イミダゾリウム クロラ イ ド 〔MVBI · Cl〕 5 2. 8 g ( 5 0 %) を得た。
次にカリウム ビス { (トリフルォロメチル） スルフォニル }アミ ド
(KTFSI) 3 1. 9 g ( 0. l m o l ) を 1 0 0 m l の水に 7 0 °C で溶解し， 5 0 °Cで攪拌しながら， 上で得た MVBI · C1 2 3. 4 g
( 0. l m o l ) を 5 0 m l の水に溶解した溶液を 1 5分で滴下 · 混合した。 5 0 °Cで激しく攪拌しながら更に 2時間， 複分解反応を 行った後， 生成した油層を分離した。 生成物を各 5 0 m 1 の水で 2 回洗浄した後， 6 0 °C， 0. 1 mmH gで 2時間乾燥し， 1 ーメチ ル— 3 — （ 4一ビニルベンジル） イミダゾリウム ビス { (トリフ ルォロメチル） スルフォニル } アミ ド 〔MVBI · TFSIと略す〕 4 0. 8 g (収率 8 5 % ) を得た。
〔実施例 2〕 炭素一炭素間二重結合を含有するポリフッ化ビニリデ ン変性ポリマー 〔DBFと略す〕 の合成
ァ トフイナ 〔 （株） 製ポリフッ化ビニリデン （Kynar 4 6 1 ) 1 5 gと N—メチルピロリ ドン一 2 〔NMP〕 8 5 gを撹拌機付きの 3 0 0 m l三口フラスコに入れ， 9 0 °Cで溶解した。 同温度で撹拌し ながら トリェチルァミン 2. 3 7 gを約 1 0分で滴下 ' 添加した。 更に同温度で撹拌しながら 3 0分間反応させた。 冷却後， 3 0 0 m 1 の水に撹拌下で添加し， 再沈殿させた。 沈殿したポリマーを各 5 0 0 m l の水で 2回浸漬洗浄 · 濾過し， 6 0 °Cで 1 0時間， 真空乾 燥した。
回収したポリマーは NMRスぺク トル分析より， 約 8モル％の二重 結合が導入されていることが分かった。
〔実施例 3〕 実施例 1で得られた， 1 ーメチルー 3 — （ 4一ビニル ベンジル） イミダゾリウム ビス { (トリフルォロメチル） スルフ ォニル } アミ ド 〔MVBI · TFSIと略す〕 8. 4 g , 実施例 2で得られ たポリフッ化ビニリデン変性ポリマー 〔 D B F〕 1 0. 0 g， ベン ゾィルパ一ォキサイ ド 0. 1 7 gをジメチルァセトァマイ ド 8 0 g に溶解した溶液を調整した。 この溶液にリチウム ビス { (トリ フ ルォロメチル） スルフォニル }アミ ド 〔L i T F S I と略す〕 4. 0 gを溶解させ， 電解質プリカーサ一液を調整した。 本溶液を 1 0 のポリエステルフィルム （東レ製 Tタイプ） 上にコーティ ングし， 熱風乾燥機で 1 3 0 °C， 3 0分間加熱し， 乾燥と同時に重 合反応を行った。 塗工膜をポリエステルフィルムから剥がし， 膜厚 2 5 mの透明なフィルムを得た。 このフィルムのイオン伝導度は 2 0 °Cで 2. 1 X 1 0— 3 S Z c m， 引張り強度は l l M P aであ つに。
〔実施例 4〕 実施例 1 と同様に， トリェチルァミンと p—クロルメ チルスチレンから， トリェチルー （ 4一ビニルベンジル） アンモニ ゥム クロライ ドを合成し， 更にこれを KT F S I と反応させ， ト リエチルー （ 4一ビニルベンジル） アンモニゥム ' ビス { (トリフ ルォロメチル） スルフォニル } アミ ド 〔TEVBA · TFSIと略す〕 を合 成した。
次いで， 上記で得た TEVBA · TFSI 7. 0 g , ポリフッ化ビニリデ ン樹脂 （ァ トフイナ社製 Kynar 461) 1 3. O g， ベンゾィルパ 一オキサイ ド 0. 1 4 g， L i T F S I 7. O gをジメチルァセ トアマイ ド 8 0 gに溶解した電解質プリカーサ一液を調整した。 本溶液を 3 mmのガラス板上に塗布し， ガラス板と共に 1 3 0 °Cで 3 0分間加熱し， 乾燥と重合反応を行った。 塗膜をガラス板から剥 がし， 膜厚 3 0 mのフィルムを得た。 本フィルムのイオン伝導度 は 3. 0 X 1 0 ~ 4 S / c m, 引張り強度は 6 M P aであった。
〔実施例 5〕 多孔質ポリフッ化ビニリデンフィルム
呉羽化学社製 ポリフッ化ビニリデン樹脂 （#1700) 5 0 g及びポ リエチレングリコール （分子量 1 0 0 0 ) 5 0 gをジメチルァセト アマイ ド 4 5 0 gに溶解した溶液を作り， 本溶液を厚さ 3 mmの ガラス板上にコーティ ングした。 ガラス板と共に熱風乾燥機に入れ, 1 5 0 °Cで 1 0分間加熱 · 乾燥後， 室温まで冷やし， 次いで室温で 大量の水の中に 3 0分間浸漬し， ポリエチレングリコールを抽出除 去した。 新鮮な水に換え， 更に 3 0分間浸漬 · ， 水洗後， 1 0 0 °C で 3 0分間乾燥し， ポリフッ化ビニリデンの孔空きフィルムを得た 本フィルムは， 厚さ 2 5 ^m, 空孔率 5 9 %, 平均孔径 5 ΠΙ
(走査型電子顕微鏡写真で評価） であった。
〔実施例 6〕 実施例 1 と同様にして， 1 一ビニルイミダゾールとェ チルブ口マイ ドより 1 ービニルー 3 —ェチルイミダゾリゥム ブロ マイ ド 〔E V I · B r と略す〕 を合成した。 E V I ' B r と力リウ ム ビス { (トリフルォロメチル） スルフォニル }アミ ド 〔KTFSIと 略す〕 とから 1 一ビニルー 3 —ェチルイミダゾリゥム ビス { (ト リフルォロメチル） スルフォニル }ァミ ド 〔EVI · TFSIと略す〕 を合 成した。
次いで， 本 E V I · T F S I 4 2 gに L i T F S I 1 5 g , ベ ンゾィルパーオキサイ ド 0. 8 gを溶解した溶液を， 上記で作製 した孔空きフィルムに真空含浸した。 含浸率は 5 7 %であった。 但 し， 含浸率％ = { (含浸後の重量一含浸前の孔空きフィルムの重 量） Z含浸後の重量 } X I 0 0 より求めた。 なお気孔率と含浸液 の比重から計算した理論含浸率は 5 5 %であった。
本含浸フィルムを 1 3 0 °Cで 3 0分間加熱 · 重合させ， 複合フィル ムを作製した。
本複合フィルムのイオン伝導度は 6. 5 X 1 0— 4 S Z c m， 引張 り強度は 1 2 MP aであった。
〔実施例 7〕 リチウムイオン電池
高分子複合電解質プリカーサ一液の調製 ： 実施例 1と同様にしてァ リルブロマイ ドと 1 ーメチルイミダゾールょり， 1 ーァリル一 3 — メチルイミダゾリゥム ブロマイ ドを合成し， これをカリウム ビ ス { (トリフルォロメチル） スルフォニル } アミ ド 〔KT F S I と 略す〕 と反応させ， 1 ーァリル一 3—メチルイミダゾリゥム ビス
{ (トリフルォロメチル） スルフォニル } アミ ド 〔AM I · T F S I と略す〕 を合成した。 同様にジァリル一ジメチルアンモニゥム クロライ ドと KT F S I よりジァリル一ジメチルアンモニゥム ビ ス { (トリフルォロメチル） スルフォニル } アミ ド 〔D AA * T F S I〕 を合成した。
上記 AM I ' T F S I 2. 4 g , D AA - T F S I 2. 4 g , L i T F S I 2. 0 g , ベンゾィルパーオキサイ ド 0. 2 4 g， ポリフッ化ビニリデン樹脂 （ァ トフイナ社製カイナー # 4 6 1 ) 5 0 gを N—メチルピロリ ドン一 2 9 5 gに溶解した。
正極の作製 ：
正極活物質である L i C o〇 2と導電剤であるアセチレンブラック を上記高分子複合電解質プリカーサ一溶液に混合した正極合剤液を 作製し， 集電体であるアルミニウム箔に塗布し， 1 3 0 °Cで 1 0分 間加熱し， 乾燥させた後， 正極合剤厚みが 9 0 mになる様にプレ スした。
負極の作成 ：
負極活物質である天然グラフアイ 卜と導電剤であるケッチェンブラ ックとを， 上記高分子複合電解質プリカーサ一溶液に混合した負極 合剤液を集電体である銅箔に塗布し， 1 3 0 °Cで 1 0分間加熱し， 乾燥させた後， 負極合剤厚みが 9 0 mになる様にプレスした。
電極間電解質膜 ：
上記高分子複合電解質プリカーサ一液を 1 0 0 mのポリエステル フィルム （東レ製 Tタイプ） にコ一ティ ングし， 1 3 0で 3 0分 間加熱し乾燥と同時に重合させ， 膜厚 3 0 の高分子複合電解質 膜をポリエステルフィルム上に形成した。
前記の正極の塗工面に， 上記複合電解質膜面を重ね， 1 3 0 °Cの口 ール間で積層後， ポリエステルフィルムを剥離し正極/電解質膜積 層シートを作製した。 この積層シートの電解質膜面に前記の負極の 塗工面を重ね， 同様に 1 3 0 °Cのロール間で積層し， 正極 Z電解質 膜 負極積層体を作製した。 この積層体を 1 5 0 °C X 1 0 k g Z c m 2で 3 0分間， 加熱圧着しながら重合させた。
本積層体を直径 1 5 m mに打ち抜き， アルミニウム製の容器に入れ, 同素材のパネと蓋を重ねプレスしてコイン型のセルを作製した。 次いで本コインセルを用い， 2 0 °Cで充放電サイクル試験を行った 充放電サイクル試験条件 ： 充電は電流 1 mA, 終止電圧 4. 0 Vで 定電流充電とした。 放電は電流 l mA， 終止電圧 2. 5 Vで定電流 放電とした。
電池設計容量との比率を放電容量 （％) とし， 充放電初期の放電容 量は 9 5 %, 2 0サイクル目においても 8 5 %の放電容量が保持さ れた。

Claims

言青 求 の 範 囲
1 . a ) 4級アンモニゥムカチオンとフッ素含有ァニオンからな る 4級アンモニゥム塩構造と， 重合性官能基を持っている溶融塩単 量体を含んでいる単量体組成物を， 電気化学的に不活性な高分子補 強材料の存在下で重合することにより製造された複合高分子電解質 組成物。
2 . 前記単量体組成物は， 前記溶融塩単量体と共重合し得る多官 能単量体を含んでいる請求項 1の複合高分子電解質組成物。
3 . 前記溶融塩単量体は， 1 ービニルー 3 —アルキルイミダリゥ ムカチオン， 4ービニルー 1 一アルキルピリジニゥムカチオン， 1 一アルキル— 3 —ァリルイミダゾリウムカチオン， 1 一 （4ービニ ルペンジル） 一 3 —アルキルイミダゾリウムカチオン， 1 一 （ビニ ルォキシェチル) 一 3 —アルキルイミダゾリウムカチオン， 1 ービ 二ルイミダゾリウムカチオン， 1 ーァリルイミダリゥムカチオン， N—ァリルべンズイミダゾリウムカチオン， および 4級ジァリルジ アルキルアンモニゥムからなる群から選ばれた 4級アンモニゥムカ チオンと， ビス 〔 （トリフルォロメチル） スルフォニルアミ ドア二 オン， 2 , 2， 2— トリフルオロー N— (トリフロォロメチルスル フォニル） ァセ トアミ ドア二オン， ビス 〔 （ペンタフルォロェチ ル） スルフォニル〕 アミ ドア二オン， ビス 〔 （フルォロ） スルホ二 ル〕 アミ ドア二オン， テトラフルォロポレートァニオン， およびト リフルォロメタンスルフォネートァニオンからなる群から選ばれた ァニオンとの塩である請求項 1の複合高分子電解質組成物。
4 . 前記高分子補強材料は， ポリテトラフルォロエチレン， ポリ フッ化ビニリデン， ポリエチレン， ポリプロピレン， ポリアクリロ 二トリル， ポリスチレン， ポリスルフォン， ポリエーテルスルフォ ン， ポリエーテルケトン， ポリエーテルエーテルケトン， ポリエ一 テルイミ ド， ポリアミ ドイミ ド， およびポリイミ ドからなる群から 選ばれる請求項 1の複合高分子電解質組成物。
5. 前記高分子補強材料は， ポリフッ化ビニリデンまたは炭素一 炭素間不飽和二重結合を含んでいるポリフッ化ビニリデンである請 求項 4の複合高分子電解質組成物。
6. 前記高分子補強材料は， 前記溶融塩単量体の重合体とポリマ 一ブレンドを形成している請求項 1の複合高分子電解質組成物。
7. 前記高分子補強材料は， 連続ポアを含んでいる多孔質フィル ムもしくはシートであり， 前記溶融塩単量体の重合体は該多孔質フ イルムもしくはシート中で連続相を形成している請求項 1の複合高 分子電解質組成物。
8. 前記単量体組成物は熱によって重合される請求項 1の複合高 分子電解質組成物。
9. 前記単量体組成物は紫外線照射によって重合される請求項 1 の複合電解質組成物。
1 0. 前記単量体組成物は電子線照射によつて重合される請求項 1の複合電解質組成物。
1 1. 前記単量体組成物は電荷移動イオン源を含んでいる請求項 1の複合電解質組成物。
1 2. 前記イオン源は， L i B F ， 1 Γ B 6 , C n t 2n+lC 〇 2 L i (但し nは 1〜 4の整数） C n F 2n+ 1 S O 3 L i (伹し nは 1〜4の整数） ， （F S〇2 ) 2 N L i， ( C F 3 S O 2 ) N L i , ( C 2 F 5 S 02 ) 2 N L i , ( C F 3 S O 2 ) 3 C L i , ( C F 3 - S O 2 - N - C O C F 3 ) L i , および （R— S O 2 - N - S O 2 C F 3 ) L i ( Rはアルキル基またはァリール基） からなる群から選ばれたリチウム塩である請求項 1 1の複合高分子 電解質組成物。
1 3. 対向する負極と正極の間に配置されている請求項 1 2の複 合高分子電解質組成物を備えているリチウムイオン電池。
1 4. 前記イオン源は， H B F4 , H P F 6 , C n F 2n+1 C O 2 H (但し nは；！〜 4の整数） ， C n F 2n+1 S〇 3 Η (但し ηは 1〜 4の整数） ， （F S〇 2 ) NH， ( C F 3 S O 2 ) NH, ( C 2 F 5 S O 2 ) N H, (C Fs S O2 ) 3 C H, ( C F 3 - S O 2 - N H - C O C F 3 ) , および （R— S〇 2 - N H - S O 2 C F 3 )
( Rはアルキル基またはァリ一ル基） からなる群から選ばれたプロ トン供与体である請求項 1 1の複合高分子電解質組成物。
1 5. 対向する負極と正極の間に配置された請求項 1 4の複合高 分子電解質組成物を備えている燃料電池。
1 6. 前記イオン源は 13 — / 1— または B r 3 — ZB r レド ックスイオン対である請求項 1 1の複合高分子電解質組成物。
1 7. 色素を吸着させた酸化物半導体膜を有する作用極と， 導電 性対極の間に配置された請求項 1 6の複合高分子電解質組成物を備 えている色素増感太陽電池。
1 8. 対向する導電性電極間に配置された電荷移動イオン源を含 まない請求項 1の複合高分子電解質組成物を備えているキャパシ 夕。
PCT/JP2004/003447 2003-03-31 2004-03-15 複合高分子電解質組成物 Ceased WO2004088671A1 (ja)