WO2004102234A1 - 対象物の識別媒体及び識別方法 - Google Patents

対象物の識別媒体及び識別方法 Download PDF

Info

Publication number
WO2004102234A1
WO2004102234A1 PCT/JP2004/006545 JP2004006545W WO2004102234A1 WO 2004102234 A1 WO2004102234 A1 WO 2004102234A1 JP 2004006545 W JP2004006545 W JP 2004006545W WO 2004102234 A1 WO2004102234 A1 WO 2004102234A1
Authority
WO
WIPO (PCT)
Prior art keywords
layer
liquid crystal
cholesteric liquid
circularly polarizing
identification medium
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2004/006545
Other languages
English (en)
French (fr)
Inventor
Hidekazu Hoshino
Itsuo Takeuchi
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
NHK Spring Co Ltd
Original Assignee
NHK Spring Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by NHK Spring Co Ltd filed Critical NHK Spring Co Ltd
Priority to DE602004026860T priority Critical patent/DE602004026860D1/de
Priority to EP04733095A priority patent/EP1628147B1/en
Priority to KR1020057021771A priority patent/KR101055015B1/ko
Priority to US10/557,001 priority patent/US7391546B2/en
Publication of WO2004102234A1 publication Critical patent/WO2004102234A1/ja
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

　識別媒体１０ａは、特定の右円偏光性の光を反射する右円偏光性高分子コレステリック液晶層１１と、特定の左円偏光性の光を反射する左円偏光性高分子コレステリック液晶層１２とを互いに積層した第１の２層体１０１を備えている。識別媒体１０ａを、対象物３０に貼り付けて、右円偏光の光だけを通すフィルタ２１と左円偏光の光だけ通すフィルタ２２を備えた簡易判定器２０を通して目視すると、右円偏光フィルタ２１側に右円偏光性高分子コレステリック液晶層１１の色、左円偏光フィルタ２２側に左円偏光性高分子コレステリック液晶層１２の色が見える。このように通常では再現できない識別媒体１０ａによる特異な現象を確認することにより簡単に対象物３０の真正性を確実に識別することができる。

Description

明 細 書
対象物の識別媒体及び識別方法
技術分野
[0001] 本発明は、商品を梱包したパッケージ、パスポート、カード、紙幣、金券、証券、証 書、商品券、絵画、切符、公共競技投票券、ブランドロゴ'マークを表すタグ、シール 、ラベル等の平面的な対象物または各種立体的な対象物の真正性を識別するため の識別媒体に関し、特に、偽造することの難度が高いことと、その真偽の判定を容易 に行えることを両立させた、対象物の真正性を識別するための識別媒体と識別方法 に関する。
背景技術
[0002] 従来、例えばカード、証書類の偽造防止方法としては、その対象物の表面にホログ ラムを貼付したり特殊なインクを塗布する技術、あるいは、紙の中に磁性粉、磁性繊 維、金属粉、金属繊維等の被検知物質をランダムに混入させる技術が知られている 。ホログラムでは、立体的に見えたり見る角度で色が変わることを目視で確認して識 別を行っていた。また、特殊なインクとしては、蛍光インクや磁気インクなどがあり、 目 視では通常のインクと変わりがないが、紫外線を照射したり磁気センサで検出するこ とにより、隠れた情報によって対象物を識別することができる。また、ランダムに被検 知物質を混入させたものは、その固有の分布のパターンを記録しておき、使用した際 に再度分布を測定して、記録してぉレ、たパターンと比較して真偽を判定する。
[0003] 特許文献 1には、ホログラムにコレステリック液晶を組みあわせた偽造防止技術が 開示されている。これは、ホログラムの視角に依存して変化する潜像とコレステリック 液晶の同じく視角に依存して色が変化する性質を組み合わせたものと、コレステリッ ク液晶の円偏光の反射特性、つまり、右ないし左の円偏光の光だけを選択的に反射 させ、しかも、反射した光も元と同じ方向の偏光特性を有する性質を組み合わせたも のがある。さらに、特許文献 2には、コレステリック液晶の特定の円偏光のみを反射す る性質と視角に依存して反射波長を変える性質を利用したものが開示されている。
[0004] し力しながら、ホログラム製造技術が普及するに伴い、その偽造技術も向上し、真 正品と見分けがつかない偽造品が容易に製造できるようになってきている。また、蛍 光インクや磁気インク、あるいは磁性粉、磁性繊維、金属粉、金属繊維等の被検知 物質をランダムに分散させたものは、偽造困難性という点では優れている力 識別の ための装置が大力 Sかりで場所をとり、電源を必要とするため、簡易に持ち運ぶ用途に は適してレヽなレ、とレ、う欠点がある。
ホログラムにコレステリック液晶を組みあわせた偽造防止技術においても、ホロダラ ムの製造技術の普及に伴レ、、より複雑な構成が求められている。偽造防止に求めら れているのは、偽造することの難度の高い困難さと、真偽の識別の容易さの両立であ る。
[0005] 特許文献 1には、ホログラムとコレステリック液晶を組み合わせ、その反射光を左右 の円偏光フィルタを通して観察し、たとえば、右円偏光フィルタで見えるときは、左円 偏光フィルタでは見えないという現象を用いて真偽を識別する技術が開示されている 。し力 ながら、片方が黒くなりそこの画像が見えなくなるだけでは、円偏光フィルタを 細工する等の偽造品が出現する可能性がある。
[0006] 特許文献 2には、コレステリック液晶を 2枚重ねた識別媒体を、同じ性質を有する液 晶フィルタを通して目視し、それぞれの対応する液晶フィルタに応じて色が変化する ことにより、真偽の識別をする技術が開示されている。し力しながら、用いられている コレステリック液晶と同じ液晶を用いた簡易判定器は汎用性が低ぐ常に個別の検査 器を準備しなければならないという問題があった。
[0007] 特許文献 1 :特願平 9一 319566号公報
特許文献 2：特開平 11 - 42875号公報
発明の開示
発明が解決しょうとする課題
[0008] したがって、本発明は、容易に偽造することができないとともに、真偽の識別が容易 力つ確実である対象物の識別媒体および識別方法を提供することを目的としている
課題を解決するための手段
[0009] 本発明の対象物の識別媒体は、対象物に識別表示を光学的に認識可能に設けて 対象物の真正性を識別するための対象物の識別媒体であって、前記識別媒体中に 、特定の右円偏光性の光を反射する右円偏光性高分子コレステリック液晶層と、特 定の左円偏光性の光を反射する左円偏光性高分子コレステリック液晶層とを互いに 積層した第 1の 2層体を備え、その第 1の 2層体の前記対象物とは反対側の外側に、 円偏光性高分子コレステリック液晶層を保護するための保護フィルム層を備えたこと を特徴としている。
[0010] さらに、本発明の対象物の識別方法は、対象物に識別表示を光学的に認識可能 に設けて対象物の真正性を識別するための対象物の識別媒体を識別する識別方法 であって、前記識別媒体は、特定の右円偏光性の光を反射する右円偏光性高分子 コレステリック液晶層と、特定の左円偏光性の光を反射する左円偏光性高分子コレス テリック液晶層とを互レ、に積層した第 1の 2層体を備え、その第 1の 2層体の前記対象 物とは反対側の外側に、円偏光性高分子コレステリック液晶層を保護するための保 護フィルム層を備え、前記対象物の識別媒体を右円偏光の光だけを通すフィルタと 左円偏光の光だけ通すフィルタを備えた簡易判定器を通して目視し、右円偏光フィ ルタ側に右円偏光性高分子コレステリック液晶層の色、左円偏光フィルタ側に左円 偏光性高分子コレステリック液晶層の色が見えることにより対象物の真贋を識別する ことを特徴としている。
[0011] まず、本発明の基本的な原理について説明する。図 1はコレステリック液晶の構造 を示す図である。コレステリック液晶は層状構造をなしており、各層での分子長軸方 向が互いに平行であり、かつ層面に平行である。また、各層は少しずつ回転して重な つており、立体的にスパイラル構造をとる。この方向因子が 360度回転して元へ戻る までの距離、すなわちピッチ Pと、各層内の平均屈折率 nとから、 s =n' Pで表され る中心波長; I sの特定の円偏光に対して選択的に反射する特徴を有する（円偏光選 択性)。したがって、各層のコレステリック液晶の方向が入射光に対して右回りならば 、中心波長 sの成分の右円偏光がそのまま右円偏光として反射され、左円偏光は コレステリック液晶を透過する。通常の媒体の反射においては右円偏光の反射光は 左円偏光になるのと対照的である。また、その他の波長の光は全てコレステリック液 晶を透過する。例えば、可視光を吸収する黒紙のような材料の上に、赤色の中心波 長 λ sを反射する右回りのコレステリック液晶を配置し、太陽光などのランダム光を当 てると透過光は全て黒紙に吸収され、中心波長え sの右円偏光のみがコレステリック 液晶によって反射されるので、コレステリック液晶は鮮やかな赤色に見える。
[0012] また、コレステリック液晶は見る角度によって色が変わるという特徴を有する。これは 、入射光が斜めの場合には、ピッチ Pが見かけ上減少することから、中心波長 sが 短波長側へ移行するためである。たとえば、垂直入射光を観察して赤色に呈色する コレステリック液晶の反射色は、視野角を大きくするに従いオレンジ色、黄色、緑色、 青緑色、青色と順次変化するように観察される（ブルーシフト）。
[0013] したがって、本発明の対象物の識別媒体に自然光を当てると、保護フィルム層を透 過した光のうち、 1番目の（例えば左）円偏光性高分子コレステリック液晶層の回転方 向とピッチ P (例えば赤）に対応した (左で赤）円偏光だけが同じ回転方向の（左で赤） 円偏光として反射され、再び保護フィルム層を透過して表面に出射する。その他の光 は 1番目の円偏光性高分子コレステリック液晶層を透過して、 2番目の（この場合は右 )円偏光性高分子コレステリック液晶層に到達する。 1番目と 2番目の円偏光性高分 子コレステリック液晶層の回転方向は逆なので、透過してきた光の中の 2番目の円偏 光性高分子コレステリック液晶層の回転方向とピッチ P (例えば緑）に対応した (右で 緑）円偏光だけ力 同じ回転方向の（右で緑）円偏光として反射され、再び 1番目の（ 左）円偏光性高分子コレステリック液晶層と保護フィルム層を透過して表面に出射す る。その他の光は 2番目の円偏光性高分子コレステリック液晶層をも透過し、 （例えば 青の）対象物に到達する。到達したその他の光は対象物の表面で反射され、 2番目 の円偏光性高分子コレステリック液晶層、 1番目の円偏光性高分子コレステリック液 晶層、保護フィルム層と順次透過して出射する。これを目視すると、赤と緑と青の光が 合成された白色に近い色として認識される。さらにこの出射光を左円偏光だけを透過 する左円偏光フィルタを通して目視すると、赤に見え、右円偏光フィルタを通して目 視すると緑に見える。しかも、それらの色は、 目視する視角を傾斜させるにつれて、そ れぞれブルーシフト現象を呈示し色の変化を観察することができる。また、この識別 媒体に左または右円偏光フィルタを近接させて観察した場合は、入射光も、左または 右の円偏光に選別されるので、より鮮明に円偏光性高分子コレステリック液晶層のピ ツチに対応する色を確認することができる。この通常の識別媒体とは著しく異なる特 徴により対象物の真贋を容易に、し力も、確実に識別することができる。
[0014] 次に、本発明の第 2の対象物の識別媒体は、対象物に識別表示を光学的に認識 可能に設けて対象物の真正性を識別するための対象物の識別媒体であって、前記 識別媒体は、特定の右あるいは左円偏光性の光を反射する 2つの同方向偏光性の 円偏光性高分子コレステリック液晶層を互いに積層した第 2の 2層体と、その第 2の 2 層体の間に設けられて透過光の円偏光の方向を右から左、あるいは、左から右に変 える機能を有する 1/2波長板層を備え、前記第 2の 2層体の前記対象物とは反対の 外側に、円偏光性高分子コレステリック液晶層を保護するための保護フィルム層とを 備えたことを特徴としている。
[0015] さらに、本発明の第 2の対象物の識別方法は、対象物に識別表示を光学的に認識 可能に設けて対象物の真贋を識別するための対象物の識別媒体を識別する識別方 法であって、前記識別媒体は、特定の右あるいは左円偏光性の光を反射する 2つの 同方向偏光性高分子コレステリック液晶層を互いに積層した第 2の 2層体と、その第 2 の 2層体の間に設けられて透過光の円偏光の方向を右から左、あるいは、左から右 に変える機能を有する 1/2波長板層を備え、前記第 2の 2層体の前記対象物とは反 対の外側に、円偏光性高分子コレステリック液晶層を保護するための保護フィルム層 とを備え、前記対象物の識別媒体を右円偏光の光だけを通すフィルタと左円偏光の 光だけ通すフィルタを備えた簡易判定器を通して目視し、右円偏光フィルタ側と左円 偏光フィルタ側に、前記第 2の 2層体のうち前記保護フィルムに近い側と、前記対象 物に近い側の円偏光性高分子コレステリック液晶層の色が、それぞれ別々に見える ことにより対象物の真贋を識別することを特徴としている。
[0016] ここで、本発明の第 2の特徴で用いられる、波長板について説明する。透明なフィ ルムの屈折率の分布が、フィルムの面内における垂直方向と水平方向で異なってい ると、そのフィルムを透過する光の垂直方向と水平方向の位相にずれが生じる。こうし たフィルムを光学的に異方性を有するという。逆に、位相にずれを生じないものを光 学的に等方性のフィルムという。その位相のずれは、屈折率の違いの程度とフィルム の厚さに依存する。たとえば、直線光が 1/4位相のずれるフィルムを透過すると、円 偏光になり、円偏光が 1/2位相のずれるフィルムを透過すると、逆の回転の円偏光 になる。また、この 1/4波長板と偏光フィルタを組み合わせることにより、特定の方向 の円偏光だけを透過させる円偏光フィルタを作ることができる。
[0017] 本発明の第 2の特徴によれば、対象物の識別媒体に自然光を当てると、保護フィノレ ム層を透過した光のうち、 1番目の（例えば左）円偏光性高分子コレステリック液晶層 の回転方向とピッチ P (例えば赤）に対応した (左で赤）円偏光だけが同じ回転方向の (左で赤）円偏光として反射され、再び保護フィルム層を透過して表面に出射する。そ の他の光は 1番目の円偏光性高分子コレステリック液晶層を透過し、さらに、 1Z2波 長板層を透過するが、このとき円偏光の回転方向は逆回転になりながら、 2番目の（ この場合は左）円偏光性高分子コレステリック液晶層に到達する。透過してきた光の 中の 2番目の円偏光性高分子コレステリック液晶層の回転方向とピッチ P (例えば緑） に対応した (左で緑）円偏光だけが、同じ回転方向の（左で緑）円偏光として反射され 、 1/2波長板層を透過する際に回転方向が逆 (右）になり、再び 1番目の（左）円偏 光性高分子コレステリック液晶層と保護フィルム層を透過して表面に出射する。その 他の光は 2番目の円偏光性高分子コレステリック液晶層をも透過し、（例えば青の）対 象物に到達する。到達したその他の光は対象物の表面で反射され、 2番目の円偏光 性高分子コレステリック液晶層、 1番目の円偏光性高分子コレステリック液晶層、保護 フィルム層と順次透過して出射する。これを目視すると、赤と緑と青の光が合成された 白色に近い色として認識される。さらにこの出射光を、簡易判定器の左円偏光だけを 透過する左円偏光フィルタを通して目視すると、赤に見え、右円偏光フィルタを通し て目視すると緑に見える。しかも、それらの色は、 目視する視角を傾斜させるにつれ て、それぞれブルーシフト現象を呈示し色の変化を観察することができる。また、この 識別媒体に左または右円偏光フィルタを近接させて観察した場合は、入射光も左ま たは右の円偏光に選別されるので、より鮮明に円偏光性高分子コレステリック液晶層 のピッチに対応した色を確認することができる。この通常の識別媒体とは著しく異なる 特徴により対象物の真贋を容易に、し力も、確実に識別することができる。
[0018] 本発明では、前記識別媒体に含まれる 2層の円偏光性高分子コレステリック液晶層 のうち、 1層または 2層に、凹凸からなるホログラム形成層を備えると好適である。この 態様によれば、対象物の真贋の判別を、色の変化によるだけでなぐあわせて、絵柄 、デザイン、模様等の変化によっても、さらに確実に識別することができる。
[0019] また、本発明では、前記保護フィルム層および前記対象物の少なくとも一方の円偏 光性高分子コレステリック液晶層側に凹凸からなるホログラム形成層を備え、このホロ グラム形成層に、円偏光性高分子コレステリック液晶が前記の凹凸に倣うように、ほ ぼ均一な膜厚で積層されていると好適である。この態様によれば、ホログラム形成層 が円偏光性高分子コレステリック液晶層よりも、 目に近い位置にあるため、より鮮明に ホログラム形成層の絵柄を目視することができ、より確実に対象物の真贋を識別する ことができるようになる。
[0020] さらに、本発明の第 3の対象物の識別方法は、対象物に識別表示を光学的に認識 可能に設けて対象物の真正性を識別するための対象物の識別媒体を識別する識別 方法であって、前記識別媒体は、特定の右円偏光性の光を反射する右円偏光性高 分子コレステリック液晶層と、特定の左円偏光性の光を反射する左円偏光性高分子 コレステリック液晶層とを互いに積層した第 1の 2層体を備え、その第 1の 2層体の前 記対象物とは反対側の外側に、円偏光性高分子コレステリック液晶層を保護するた めの保護フィルム層を備え、前記識別媒体に含まれる 2層の円偏光性高分子コレス テリック液晶層のうち、 1層または 2層に、凹凸からなるホログラム形成層を備え、前記 対象物の識別媒体を右円偏光の光だけを通すフィルタと左円偏光の光だけ通すフィ ルタを備えた簡易判定器を通して目視し、右円偏光フィルタ側に右円偏光性高分子 コレステリック液晶層の色と、ホログラム形成層を有するときはそこに描かれた絵柄と が見え、左円偏光フィルタ側に左円偏光性高分子コレステリック液晶層の色と、ホロ グラム形成層を有するときはそこに描かれた絵柄とが見えることにより対象物の真贋 を識別することを特徴としている。
[0021] 本発明の第 3の特徴によれば、第 1の発明の特徴と同様に、識別媒体に自然光を 当てると、保護フィルム層を透過した光のうち、 1番目の（例えば左）円偏光性高分子 コレステリック液晶層の回転方向とピッチ P (例えば赤）とに対応した光が反射し、さら に、そこにホログラム形成層を有するときは、その絵柄を伴って、（左で赤で絵柄付） 円偏光として反射され、再び保護フィルム層を透過して表面に出射する。その他の光 は 1番目の円偏光性高分子コレステリック液晶層を透過して、 2番目の（この場合は右 )円偏光性高分子コレステリック液晶層に到達する。 1番目と 2番目の円偏光性高分 子コレステリック液晶層の回転方向は逆なので、透過してきた光の中の 2番目の円偏 光性高分子コレステリック液晶層の回転方向とピッチ P (例えば緑）に対応した光が反 射し、さらに、そこにホログラム形成層を有するときは、その絵柄を伴って、（右で緑で 絵柄付）円偏光として反射され、再び 1番目の (左）円偏光性高分子コレステリック液 晶層と保護フィルム層を透過して表面に出射する。その他の光は 2番目の円偏光性 高分子コレステリック液晶層をも透過し、対象物に到達する。対象物に絵柄が描かれ ていれば、到達したその他の光は対象物の表面で絵柄を伴って反射され、 2番目の 円偏光性高分子コレステリック液晶層、 1番目の円偏光性高分子コレステリック液晶 層、保護フィルム層と順次透過して出射する。これを目視すると、赤と緑の光が合成さ れた黄色に近い色と、全て絵柄を伴った場合は、 3重の絵柄として認識される。さらに この出射光を左円偏光だけを透過する左円偏光フィルタを通して目視すると、赤色と 、さらにホログラム形成層を有するときは、その絵柄が見え、右円偏光フィルタを通し て目視すると緑色と、さらにホログラム形成層を有するときは、その絵柄が見える。し 力も、それらの色は、 目視する視角を傾斜させるにつれて、それぞれブルーシフト現 象を呈示し色の変化を観察することができる。また、この識別媒体に左または右円偏 光フィルタを近接させて観察した場合は、入射光も左または右の円偏光に選別され るので、より鮮明に色と絵柄を確認することができる。この通常の識別媒体とは著しく 異なる特徴により対象物の真贋を容易に、しかも、確実に識別することができる。 さらに、本発明の第 4の対象物の識別方法の特徴は、対象物に識別表示を光学的 に認識可能に設けて対象物の真正性を識別するための対象物の識別媒体を識別す る識別方法であって、前記識別媒体中に、特定の右あるいは左円偏光性の光を反 射する 2つの同方向偏光性高分子コレステリック液晶層を互いに積層した第 2の 2層 体と、その第 2の 2層体の間に設けられて透過光の円偏光の方向を右から左、あるい は、左から右に変える機能を有する 1Z2波長板層を備え、前記第 2の 2層体の前記 対象物とは反対の外側に、円偏光性高分子コレステリック液晶層を保護するための 保護フィルム層とを備え、前記識別媒体に含まれる第 2の 2層体の円偏光性高分子コ レステリック液晶層のうち、 1層または 2層に、凹凸からなるホログラム形成層を備え、 前記対象物の識別媒体を右円偏光の光だけを通すフィルタと左円偏光の光だけ通 すフィルタを備えた簡易判定器を通して目視し、 2つのフィルタの片側に、前記第 2の 2層体のうち、前記保護フィルム層側の円偏光性高分子コレステリック液晶層の色と、 ホログラム形成層を有するときはそこに描かれた絵柄とが見え、他方側に、前記対象 物側の円偏光性高分子コレステリック液晶層の色と、ホログラム形成層を有するとき はそこに描かれた絵柄とが見えることにより対象物の真贋を識別することを特徴とす る。
[0023] 本発明の第 4の特徴によれば、第 2の発明の特徴として述べたように、対象物の識 別媒体に自然光を当てたときと、左右の各円偏光フィルタを通して目視したときの色 の違いによる識別だけでなぐ自然光を当てたときは、対象物の表面の色および絵柄 と、第 1と第 2の円偏光性高分子コレステリック液晶層の色と、そこにホログラム形成層 を有するときは、そこに描かれた絵柄とが渾然一体となって目視され、簡易判定器の 左右の各円偏光フィルタを通して目視したときは、それぞれの円偏光フィルタを通過 する側の光を反射する、円偏光性高分子コレステリック液晶層の色と、そこにホロダラ ム形成層を有するときは、そのホログラム形成層の絵柄が見える。また、この識別媒 体に左または右円偏光フィルタを近接させて観察した場合は、入射光も左または右 の円偏光に選別されるので、より鮮明に色と絵柄を確認することができる。このような 、通常の識別媒体とは著しく異なる特徴により対象物の真贋を容易に、しかも、確実 に識另 IJすることができる。
[0024] 本発明では、前記識別媒体に含まれる第 1あるいは第 2の 2層体の円偏光性高分 子コレステリック液晶層のスパイラル構造のピッチがそれぞれ異なると好適である。こ の態様によれば、対象物の真贋の判別を、自然光のもとで目視したときと、簡易判定 器の円偏光フィルタを通したときの色の変化によるだけでなぐ右と左の円偏光フィル タどうしの色も異なるので、対象物の真正さを容易に、しかも、確実に識別することが できる。
[0025] さらに、本発明では、前記識別媒体に含まれる前記 2層体のホログロラム形成層の 描く絵柄が、それぞれ異なるとさらに好適である。この態様によれば、対象物の真贋 の判別を、 自然光のもとで目視したときと、簡易判定器の円偏光フィルタを通したとき の色と絵柄の変化によるだけでなぐ右と左の円偏光フィルタ同士の色と絵柄も異な るので、対象物の真正さをさらに容易に、しかも、確実に識別することができる。
[0026] さらにまた、本発明では、前記識別媒体の前記対象物側の外側に粘着層を備えて レ、ると好適である。この態様によれば、前記識別媒体を、容易に対象物に貼り付ける こと力 Sできる。
[0027] また、本発明では、前記粘着層に暗色の顔料が含まれているとさらに好適である。
この態様によれば、自然光のもとで対象物を目視したときは、対象物の表面状態は 観察されず、第 1と第 2の円偏光性高分子コレステリック液晶層の色が金属光沢をお びて発色する。簡易判定器の右と左の各円偏光フィルタを通して目視したときには、 それぞれの対応する円偏光性高分子コレステリック液晶層の色だけが鮮明に、金属 光沢をおびて観察される。さらに、円偏光性高分子コレステリック液晶層にホログラム 形成層がある場合は、 自然光のもとで対象物を目視したときは、 2種類の絵柄が、鮮 明にし力も金属光沢を帯びて、 2重に重なり合って観察され、簡易判定器の左右の 円偏光フィルタを通して目視したときは、右円偏光フィルタ側に右円偏光性高分子コ レステリック液晶層の色とホログラム形成層に描かれた絵柄、左円偏光フィルタ側に 左円偏光性高分子コレステリック液晶層の色とホログラム形成層に描かれた絵柄が 金属光沢をおびて鮮明に観察されるので、対象物の真正さを容易に、しかも、確実 に識另 IJすることができる。
発明の効果
[0028] 本発明によれば、 2種類のコレステリック液晶を積層した 2層体と、 2種類のホロダラ ムの絵柄を積層して組み合わせているので、 自然光のもとで見たときと、右、左円偏 光フィルタを通して見たときに、それぞれ別々の色と絵柄が観察されるので、容易に 偽造することができないとともに、真偽の識別が容易かつ確実である等の優れた効果 を奏する。
発明を実施するための最良の形態
[0029] 以下に本発明の実施の形態について説明する。
高分子コレステリック液晶は、特開昭 63—51 193号公報、特開昭 57—165480号 公報、特開昭 58— 17119号公報等に開示された公知の方法により製造することがで きる。たとえば、低分子コレステリック液晶を重合性モノマー中に溶解して保持するこ とでコレステリック液晶を成長させた後、光反応または熱反応などで低分子液晶を架 橋して分子配向を固定するとともに高分子化する。あるいは、側鎖型または主鎖型の サーモト口ピック高分子液晶をその液晶転移点以上に加熱してコレステリック液晶構 造を成長させた後、液晶転移点以下の温度に冷却して分子配向を固定しても良い。 さらに、側鎖型または主鎖型のリオトロピック高分子液晶を溶媒中でコレステリック配 向させた後、溶媒を徐々に揮発させて分子配向を固定しても良い。
[0030] 具体的には、側鎖に液晶形成基を有するポリアタリレート、ポリメタタリレート、ポリシ ロキサン、ポリマロネートなどの側鎖型ポリマーや、主鎖に液晶形成基を有するポリエ ステル、ポリエステノレアミド、ポリカーボネート、ポリアミド、ポリイミドなどの主鎖型ポリ マーを挙げることができる。
[0031] 上記のような高分子コレステリック液晶は、保護フィルム、等方性フィルム、 1/2波 長板層あるいは剥離層を有する薄いプラスチックフィルムでできたベースフィルム（例 えば、 PETフィルムなど）の片面に原料液を塗工し、コレステリック配向および分子配 向の固定等を行うことで製造することができる。この場合の高分子コレステリック液晶 は、分子の積層方向に沿った（例えば)左回転の捻れのピッチ Pがー様で 0. 1— 5. 0 / m程度の膜の厚さを有するものとする。通常は保護フィルム、等方性フィルム等に よって保護されている力 ホットメルトするとベースフィルム、さらに場合によっては、剥 離層もベースフィルムと共に剥がれて、高分子コレステリック液晶層が表面に露出す ることもある。また、高分子コレステリック液晶層に文字などを印刷してもよい。
[0032] ホログラムは、対象物に形成した回折格子の格子間隔、回折方向を画素サイズの 微少領域で変化させることで所望のパターン、像、文字などを結像させるものである。 ホログラムはその構造力 体積型と平面型の 2種類に分類され、また、光の変調方式 力 振幅型と位相型に分類されるが、工業的には 1つのマスター型からマイクロレプリ 力法で大量複製が可能な位相変調平面型ホログラム（エンボス 'ホログラム）が広く普 及している。
[0033] ホログラム形成層は、円偏光性高分子コレステリック液晶層あるいは、保護フィルム 、等方性フィルム、 1/2波長板層の片側にマスター型から転写することにより形成さ れる。これをエンボス加工と呼ぶ。転写の方法は、プレス機、圧延機、カレンダーロー ノレ、ラミネーター、スタンパーなどで加熱加圧する方法があげられる。エンボス加工に より表面に凹凸が形成されるが、その凹凸の影響は、円偏光性高分子コレステリック 液晶層あるいは各種フィルムの表面だけに留まらず、内側にも伝わる。表面の凹凸と 影響を受けた内側を含めて、ホログラム形成層と呼ぶ。
[0034] 保護フィルムは、円偏光性高分子コレステリック液晶層を保護する層である。材質と しては、アクリル系樹脂、ウレタン系樹脂、エポキシ系樹脂、シリコン系樹脂、 EVA系 樹脂、ポリアミド系樹脂、ポリエステル系樹脂、ポリスチレン系樹脂、セルロース系樹 脂、およびこれらの混合物などを好適に用いることができるが、これに限定するもので はない。用途によって要求される、平滑性、ハードコート性、耐摩耗性などに応じて適 宜選択するとよいが、円偏光性高分子コレステリック液晶層の性質によっては、必ず しも必要不可欠なものではない。
[0035] 1/2波長板として用いる異方性フィルム、あるいは、光をそのまま透過させる等方 性フィルムは、プラスチック製が好ましぐポリカーボネート、ポリビニルアルコール、ポ リスルホン、ポリエチレン、ポリプロピレン、ポリスチレン、ポリアリレート、ポリエチレンテ レフタレート、トリァセチルセルロース、ジァセチルセルロース、ポリエチレンーェチノレ ビュルアルコールを例示できる力 S、これに限定するものではない。異方性フィルムとし て用いるときは、一方向への延伸等の加工を適宜加えて調節する。
[0036] 粘着層に用いる一般的な粘着剤には、主成分で大別すると、アクリル系、ゴム系、 シリコーン系があり、これらのうちから適宜、基材と被着体との相性のよいものを適宜 選定する。一般的には、アクリル系が混合物としての調整範囲が広いため、シールや ラベル類では最も適応性が高ぐ使いやすい。また、粘着層の中でも、ホットメルト用 の粘着層には、主成分で大別すると、ポリエステル系、ポリウレタン系、ナイロン系が あり、これらのうちから適宜、基材と被着体との相性のよいものを選定する。さらに、こ れらの粘着層に暗色の顔料あるいは染料、例えばカーボンの粉末を混入することに より、暗色の粘着層とすることができる。対象物の色、絵柄等を目視されたくないとき は、酸化チタン、クロムイェロー等の有色の顔料を混入してもよい。また、これらの粘 着層の粘着力をコレステリック液晶層の層間結合力よりも強くすることにより、一度対 象物に貼り付けると、コレステリック液晶層の層間破壊なしには剥がすことができなく なり再利用ができないため、より好適に真正性を保持することができる。
実施例
[0037] 以下に実際の製造方法の例を述べながらさらに詳細に本発明を説明する。
(実施例 1)
実施例 1の識別媒体 10aの断面を図 2に示す。以下の説明全てに共通するが、製 造時は上下逆にして積層していくので、上下の表現が図と逆になる。
まず、保護フィルム層 14の上に、反射光の中心波長が 0· 70 μ ΐη (赤）となるスパイ ラル構造のピッチを有する右円偏光性高分子コレステリック液晶層 11を塗布し、さら にその上に、反射光の中心波長が 0· 55 μ ΐη (緑）となるスパイラル構造のピッチを有 する左円偏光性高分子コレステリック液晶層 12を塗布して第 1の 2層体 101を構成し 、その上に、アクリル系の粘着層 15aを塗布する。こうして製造した識別媒体 10aを、 工程の延長上で、ただちに対象物 30に貼り付ける場合は、離型紙は不要である。こ れに対して、一旦、保存、運搬等をした後に対象物 30に貼り付ける場合は、図 3に断 面を示すように、離型紙 18を粘着層 15の上に積層した後にロール状に卷き取る。
[0038] 図 4は、こうして製造した識別媒体 10aを表面が青色の対象物 30に貼り付け、それ を簡易判定器 20で観察している断面の模式図である。図 4に示す円偏光の回転方 向の表記方法を図 5に示す。図 4には簡易判定器が示されている。簡易判定器は、 図 6に示すように、右円偏光性の光だけを透過させる右円偏光フィルタ 21と、左円偏 光の光だけを透過させる左円偏光フィルタ 22を備え、例えばボール紙等の台紙でで きたカード状の手軽に持ち運びできる真正性の識別手段である。
[0039] 図 4に示すように、対象物 30に向力 自然光のうち、右円偏光性の光だけが右円偏 光フィルタ 21を透過し、保護フィルム層 14を経て、右円偏光性コレステリック液晶層 1 1で赤色の波長の右円偏光の光だけが右円偏光のまま反射し、再び、保護フィルム 層 14と右円偏光フィルタ 21を透過して赤色として視認することができる。その他の赤 色以外の波長の右円偏光の光は、右円偏光性コレステリック液晶層 11と左円偏光性 高分子コレステリック液晶層 12を透過し、対象物 30の表面で反射するが、このとき左 円偏光になる。このため、左円偏光性高分子コレステリック液晶層 12と右円偏光性高 分子コレステリック液晶層 11は、透過できる力 右円偏光フィルタ 21は透過できない 。また、左円偏光性の光は左円偏光フィルタ 22を透過し、保護フィルム層 14と右円 偏光性コレステリック液晶層 11を透過し、左円偏光性コレステリック液晶層 12で、左 円偏光性の緑色の光として反射し、右円偏光性コレステリック液晶層、保護フィルム 層、左円偏光フィルタと順次透過して、緑色として視認することができる。その他の緑 以外の波長の左円偏光の光は左円偏光性高分子コレステリック液晶層 12を透過し、 対象物 30で反射するが、このとき右円偏光になる。このため、左円偏光フィルタ 22を 透過することができない。また、円偏光フィルタを置かない場合は、対象物 30からの 反射光も、再び全ての層を透過して青色として視認される。つまり、この対象物 30に 貝占り付けた識別媒体 10aは、自然光の元では赤と緑と青の混合された白色に近い色 として視認され、右円偏光フィルタを通すと赤ぐ左円偏光フィルタを通すと緑になる という、通常では再現できない特異な現象を確認することにより簡単に真正性を確実 に識別することができる。なお、厳密に言うと、対象物の色が青である場合、 Y (イエロ 一）を吸収した C (シアン）と M (マゼンダ）の合成で青く見えるため、上記フィルタを用 レ、て目視したときに見える赤や緑にも対象物の青が少し入ってくるので、粘着層 15を 黒色にするのが好ましい。この場合、対象部の色が粘着層 15に吸収されて反射され るのが防止されるので、上記コレステリック液晶層の赤と緑とをより鮮明に見ることがで きる。
(実施例 2)
第 2の実施例の識別媒体 10bの断面を図 7に示す。まず、保護フィルム層 14の上 に、反射光の中心波長が 0. 70 z m (赤）となるスパイラル構造のピッチを有する右円 偏光性高分子コレステリック液晶層 11aを塗布し、その上に、 1/2波長板層 13を図 示しない粘着層を介して貼り付ける。 1Z2波長板層 13は、ポリエチレンテレフタレー ト (PET)からなり、光学的に異方性で 1Z2波長位相をずらすように調節されている。 さらにその上に、反射光の中心波長が 0. 55 x m (緑）となるスパイラル構造のピッチ を有する右円偏光性高分子コレステリック液晶層 l ibを塗布して第 2の 2層体 102を 構成し、その上に、アクリル系の粘着層 15を塗布し、離型紙 18を積層した後にロー ル状に巻き取る。
こうして製造した識別媒体 10bを表面が青色の対象物 30に貼り付け、それを簡易 判定器 20で観察している断面の模式図を図 8に示す。対象物 30に当たる自然光の うち、右円偏光性の光だけが、右円偏光フィルタ 21を透過し、保護フィルム層 14を透 過し、 1番目の右円偏光性コレステリック液晶層 11aで赤色の波長の右円偏光の光だ けが右円偏光のまま反射し、再び、保護フィルム層 14と右円偏光フィルタ 21を透過 して赤色として視認することができる。その他の波長の右円偏光の光は、右円偏光性 コレステリック液晶層 11aと 1Z2波長板層 13を透過して左円偏光となり、 2番目の右 円偏光性高分子コレステリック液晶層 l ibを透過し、対象物 30の表面で反射するが 、このとき右円偏光になる。このため、右円偏光性高分子コレステリック液晶層 l la、 1 lbは透過できるが、 1/2波長板層 13を透過するときに左円偏光になるため右円偏 光フィルタは透過できなレ、。また、左円偏光性の光は左円偏光フィルタ 22を透過し、 保護フィルム層 14と 1番目の右円偏光性コレステリック液晶層 11aと 1/2波長板層 1 3を透過する。 1/2波長板層を透過するときに右円偏光になった光は、 2番目の右 円偏光性コレステリック液晶層 l ibで右円偏光性の緑色の光として反射し、 1/2波 長板層 13、 1番目の右円偏光性コレステリック液晶層、保護フィルム層を透過し、 1/ 2波長板層を透過するときに左円偏光になり、左円偏光フィルタを透過して、緑色とし て視認すること力できる。その他の波長の右円偏光の光は 2番目の右円偏光性高分 子コレステリック液晶層 l ibを透過し、対象物 30で反射するが、このとき左円偏光に なる。このため、 1/2波長板層 13を透過するときに右円偏光に変わり、左円偏光フィ ルタ 22を透過することができない。また、円偏光フィルタを通さない場合は、円偏光 性高分子コレステリック液晶層で反射されなかった光が対象物 30まで到達し、反射し て再び、全ての層を透過して青色として視認される。つまり、この対象物 30に貼り付 けた識別媒体 10bは、 自然光の元では赤と緑と青の混合された白色に近い色として 視認され、右円偏光フィルタを通すと赤ぐ左円偏光フィルタを通すと緑になるという、 通常では再現できない特異な現象を確認することにより、簡単に真正性を識別するこ とができる。なお、厳密に言うと、対象物の色が青である場合、 Y (イェロー）を吸収し た C (シアン）と M (マゼンダ）の合成で青く見えるため、上記フィルタを用いて目視し たときに見える赤や緑にも対象物の青が少し入ってくるので、粘着層を黒色にするの が好ましい。この場合、対象部の色が粘着層 15に吸収されて反射されるのが防止さ れるので、上記コレステリック液晶層の赤と緑とをより鮮明に見ることができる。
[0042] (実施例 3)
PET製の 1Z2波長板層 13の上に、右円偏光性高分子コレステリック液晶層 1 1aを 塗布し、絵柄 Aのホログラム形成層 19aをエンボス加工し、その上に粘着材 15aを塗 布し、その上に離型紙 18を貼り付けて、図 9にその断面を示すようなロール A41を作 成する。
次に、等方性のトリァセチルセルロース (TAC)力 なる保護フィルム層 14の上に、 右円偏光性高分子コレステリック液晶層 1 lbを塗布し、絵柄 Bのホログラム形成層 19 bをエンボス加工し、その上にホットメルト用の粘着材 15bを塗布し、図 10にその断面 を示すようなロール B42を作成する。
さらに、ローノレ A41の上に、熱と圧力をかけながらロール B42を貼り合わせ、図 11 に示すような識別媒体 10cを作成する。この識別媒体 10cは 1番目と 2番目の右円偏 光性高分子コレステリック液晶層 l la， l ibの間に、 1/2波長板層 13が狭持された 第 2の 2層体 102を含んでいる。
こうして作成した識別媒体 10cを、例えば型を用いて一定形状のシールに打ち抜き し、図 12に示すように、対象物 30に貼り付けることができる。
[0043] このシールに対する光線の透過、反射の様子を模式的に断面図で表したのが図 1 3である。このシールを自然光の中で眺めると、対象物 30の色と絵柄、 1番目の右円 偏光性高分子コレステリック液晶層の色とホログラム形成層の絵柄 B、 2番目の右円 偏光性高分子コレステリック液晶層の色とホログラム形成層の絵柄 Aとが、渾然一体 となって観察され、簡易判定器 20を通して眺めると、右円偏光フィルタ 21側に 1番目 の右円偏光性高分子コレステリック液晶層の色とホログラム形成層の絵柄 Bが、左円 偏光フィルタ側に 2番目の右円偏光性高分子コレステリック液晶層の色とホログラム 形成層の絵柄 Aが観察されるとレ、う、通常では再現できなレ、特異な現象を確認する ことにより、簡単に真正性を識別することができる。光の透過の仕組みの説明は、図 8 に示す実施例 2の場合と同じであるので省略する。また、粘着材 15aを黒色にするの が好ましい。この場合、対象部の色が粘着材 15aに吸収されて反射されるのが防止 されるので、上記コレステリック液晶層の色とホログラム形成層の絵柄とをより鮮明に 見ること力 Sできる。
[0044] (実施例 4)
光学的に等方性の TACでできた等方性フィルム層 16に、左円偏光性高分子コレ ステリック液晶層 12を塗布し、絵柄 Aのホログラム形成層 19aをエンボス加工し、その 上にホットメルト用の粘着材 15aを塗布し、図 14に断面構造を示すようなロール D44 を作成する。
次に、ベースフィルム 17に保護フィルム 14を密着させ、その上に右円偏光性高分 子コレステリック液晶層 11を塗布し、絵柄 Bのホログラム形成層 19bをエンボス加工し 、その上に粘着材 15aよりも低温で熱融着できるホットメルト用の粘着材 15bを塗布し 、図 15に断面構造を示すようなロール C43を作成する。
さらに、ロール D44の上に、熱と圧力をかけながら、ロール C43を貼り合わせて、図 16に示すような識別媒体 10dを作成する。この識別媒体 10dは、右円偏光性高分子 コレステリック液晶層 11と左円偏光性高分子コレステリック液晶層 12とが積層された 第 1の 2層体 101を含んでいる。
[0045] こうして作成した識別媒体 10dは、例えば、図 17に示すように、ホットプレス 50で対 象物 30に貼り付けることができる。ホットプレス 50と対象物 30との間には、識別媒体 10dがベースフィルム 17を駆動体として図示されない卷き取り機によって移動してい る。加熱されたホットプレス 50は、対象物 30に対して上下動を繰り返し、下がった状 態のときに、識別媒体 10dを加熱しつつ対象物 30に圧着する。識別媒体 10dは、圧 着された部分だけが対象物 30に密着して残り、他はホットプレス 50が上昇したときに 、対象物 30から離れる。
[0046] こうして対象物 30に貼り付けた識別媒体 10dを自然光の中で眺めると、対象物 30 の色と絵柄、右円偏光性高分子コレステリック液晶層 11の色とホログラム形成層 19b の絵柄 B、左円偏光性高分子コレステリック液晶層 12の色とホログラム形成層 19aの 絵柄 Aとが、渾然一体となって観察され、簡易判定器 20を通して眺めると、図 18に 模式的に断面を示すように、右円偏光フィルタ 21側に右円偏光性高分子コレステリ ック液晶層 11の色とホログラム形成層 19bの絵柄 B力 左円偏光フィルタ側に左円偏 光性高分子コレステリック液晶層 12の色とホログラム形成層 19aの絵柄 Aが観察され るという、通常では再現できない特異な現象を確認することにより、簡単に真正性を 識別すること力 Sできる。光の透過の仕組みの説明は、図 4に示す実施例 1の場合と同 じであるので省略する。また、粘着材 15aを黒色にするのが好ましい。この場合、対 象部の色が粘着材 15aに吸収されて反射されるのが防止されるので、上記コレステリ ック液晶層の色とホログラム形成層の絵柄とをより鮮明に見ることができる。
[0047] 実施例 3、 4において、ロール A, B, C, Dは、いずれも円偏光性高分子コレステリッ ク液晶層 11、 12にホログラム形成層 19をエンボス加工して付与した力 図 19に 1例 を示すように、保護フィルム層 14、あるいは、 1Z2波長板層 13、等方性フィルム層 1 6にホログラム形成層 19をエンボス加工し、その上に、円偏光性高分子コレステリック 液晶層 11または 12を塗布し、その上に粘着層 15を塗布してロール E45を作成し、口 ール A, B, C, Dに代えて用いることもできる。
[0048] (実施例 5)
実施例 3、 4において使用したロール A、 Dに塗布した粘着層 15aに、黒色のカーボ ン製の顔料を混ぜて黒色のホットメルト材 (熱融着接着剤）を作成する。こうして得た 黒色の粘着層付きの識別媒体 10を、マイクロスリツター等で例えば 1一 5mmの幅に スリットしてフィルム状とする。そして、図 20に示すように、例えば上層、中層および下 層を積層して商品券等を製造する際に、その中間にフィルム状の識別媒体 10を挟 み込み、上層に窓 Wを開けておくことにより、図 21に示すようなスレッド状に識別媒体 10を縫い込んだ対象物 30を作ることができる。このスレッド部を自然光のもとで眺め ると、 2種類の絵柄が重なり合って、かつ、金属光沢を帯びた色が一体となって観察 され、簡易判定器 20を用いて眺めると、それぞれのフィルタを通して、金属光沢を帯 びた別々の絵柄と色が観察される。
[0049] なお、本発明は上記実施例に限定されるものではなぐ種々の変形が可能である。
たとえば、上記実施例では、高分子コレステリック液晶層のそれぞれを中心波長が 0 . 70 z m (赤）、 0. (緑）である光を反射するようにした力、これに限定されるも のではなぐ高分子コレステリック液晶層のスパイラル構造のピッチや屈折率を適宜 設計することにより同じ色の光を反射するようにしてもよい。また、上記実施例では、 対象物の識別媒体に自然光をあてるようにした力 これに限定されるものではなぐた とえば赤外光をあてるようにしてもょレ、。
図面の簡単な説明
[図 1]本発明の原理を説明するための高分子コレステリック液晶を示す斜視図である
[図 2]第 1の発明の識別媒体を示す断面図である。
[図 3]識別媒体に離型紙を付けた様子を示す断面図である。
[図 4]対象物に貼り付けた第 1の発明の識別媒体への光線の透過、反射を模式的に 示す断面図である。
[図 5]円偏光の回転方向の表記方法を定義する模式図である。
[図 6]簡易判定器の一例を示す平面図である。
[図 7]第 2の発明の積層構造を示す断面図である。
[図 8]対象物に貼り付けた第 2の発明の識別媒体への光線の透過、反射を模式的に 示す断面図である。
[図 9]第 3の発明の識別媒体の中間部材であるロール Aの断面図である。
[図 10]第 3の発明の識別媒体の中間部材であるロール Bの断面図である。
[図 11]第 3の発明の識別媒体の断面図である。
[図 12]対象物にシール状の識別媒体を貼り付けた例を示す斜視図である。
[図 13]対象物に貼り付けた第 3の発明の識別媒体への光線の透過、反射を模式的に 示す断面図である。
[図 14]第 4の発明の識別媒体の中間部材であるロール Dの断面図である。
[図 15]第 4の発明の識別媒体の中間部材であるロール Cの断面図である。
[図 16]第 4の発明の識別媒体の断面図である。
[図 17] (A)および (B)は、対象物に識別媒体をホットプレスで貼り付ける様子を模式 的に示す正面図である。
[図 18]対象物に貼り付けた第 4の発明の識別媒体への光線の透過、反射を模式的に 示す断面図である。 [図 19]第 3、第 4の発明の中間部材であるロールの別の例の断面図である。
[図 20]対象物に識別媒体をスレッド状に挟み込む様子を概念的に示す斜視図である
[図 21]識別媒体をスレッド状に縫い込んだ対象物の例を示す平面図である。
符号の説明
10 識別媒体
11、 l la、 l ib 右円偏光性高分子コレステリック液晶層
12 左円偏光性高分子コレステリック液晶層
13 1/2波長板層
14 保護フィルム層
15、 15a、 15b 粘着層
16 等方性フィルム層
17 ベースフィルム
18 離型紙
19、 19a, 19b ホログラム形成層
20 簡易判定器
21 右円偏光フィルタ
22 左円偏光フィルタ
30 対象物
41、 42、 43、 44、 45 卩ール
50 ホットプレス
60 入射光
61 出射光
101 第 1の 2層体
102 第 2の 2層体

Claims

請求の範囲
[1] 対象物に識別表示を光学的に認識可能に設けて対象物の真正性を識別するため の対象物の識別媒体であって、前記識別媒体中に、特定の右円偏光性の光を反射 する右円偏光性高分子コレステリック液晶層と、特定の左円偏光性の光を反射する 左円偏光性高分子コレステリック液晶層とを互いに積層した第 1の 2層体を備え、そ の第 1の 2層体の前記対象物とは反対側の外側に、円偏光性高分子コレステリック液 晶層を保護するための保護フィルム層を備えたことを特徴とする対象物の識別媒体。
[2] 対象物に識別表示を光学的に認識可能に設けて対象物の真正性を識別するため の対象物の識別媒体であって、前記識別媒体中に、特定の右あるいは左円偏光性 の光を反射する 2つの同方向円偏光性高分子コレステリック液晶層を互いに積層し た第 2の 2層体と、その第 2の 2層体の間に設けられて透過光の円偏光の方向を右か ら左、あるいは、左から右に変える機能を有する 1/2波長板層を備え、前記第 2の 2 層体の前記対象物とは反対の外側に、円偏光性高分子コレステリック液晶層を保護 するための保護フィルム層とを備えたことを特徴とする対象物の識別媒体。
[3] 前記識別媒体に含まれる 2層の円偏光性高分子コレステリック液晶層のうち、 1層ま たは 2層に、凹凸からなるホログラム形成層を備えたことを特徴とする請求項 1または 2に記載の対象物の識別媒体。
[4] 前記保護フィルム層および前記対象物の少なくとも一方の円偏光性高分子コレス テリック液晶層側に凹凸からなるホログラム形成層を備え、このホログラム形成層に、 前記円偏光性高分子コレステリック液晶が前記の凹凸に倣うように、ほぼ均一な膜厚 で積層されていることを特徴とする請求項 1または 2に記載の対象物の識別媒体。
[5] 前記第 1または第 2の 2層体の円偏光性高分子コレステリック液晶層のスパイラル構 造のピッチがそれぞれ異なることを特徴とする請求項 1一 4のいずれかに記載の対象 物の識別媒体。
[6] 前記第 1または第 2の 2層体のホログロラム形成層は、互いに異なる絵柄を有するこ とを特徴とする請求項 3— 5のいずれかに記載の対象物の識別媒体。
[7] 前記識別媒体の前記対象物側の外側に粘着層を備えていることを特徴とする請求 項 1一 6のいずれかに記載の対象物の識別媒体。
[8] 前記粘着層に暗色の顔料が含まれていることを特徴とする請求項 1一 7のいずれか に記載の対象物の識別媒体。
[9] 対象物に識別表示を光学的に認識可能に設けて対象物の真正性を識別するため の識別媒体を識別する識別方法であって、前記識別媒体は、特定の右円偏光性の 光を反射する右円偏光性高分子コレステリック液晶層と、特定の左円偏光性の光を 反射する左円偏光性高分子コレステリック液晶層とを互いに積層した第 1の 2層体を 備え、その第 1の 2層体の前記対象物とは反対側の外側に、円偏光性高分子コレス テリック液晶層を保護するための保護フィルム層を備え、前記対象物の識別媒体を 右円偏光の光だけを通すフィルタと左円偏光の光だけ通すフィルタを備えた簡易判 定器を通して目視し、右円偏光フィルタ側に右円偏光性高分子コレステリック液晶層 の色、左円偏光フィルタ側に左円偏光性高分子コレステリック液晶層の色が見えるこ とにより対象物の真贋を識別することを特徴とする対象物の識別方法。
[10] 対象物に識別表示を光学的に認識可能に設けて対象物の真正性を識別するため の識別媒体を識別する識別方法であって、前記識別媒体は、特定の右あるいは左 円偏光性の光を反射する 2つの同方向偏光性高分子コレステリック液晶層を互いに 積層した第 2の 2層体と、その第 2の 2層体の間に設けられて透過光の円偏光の方向 を右から左、あるいは、左から右に変える機能を有する 1/2波長板層を備え、前記 第 2の 2層体の前記対象物とは反対の外側に、円偏光性高分子コレステリック液晶層 を保護するための保護フィルム層とを備え、前記対象物の識別媒体を右円偏光の光 だけを通すフィルタと左円偏光の光だけ通すフィルタを備えた簡易判定器を通して 目視し、右円偏光フィルタ側と左円偏光フィルタ側に、前記第 2の 2層体のうち前記 保護フィルムに近い側と、前記対象物に近い側の円偏光性高分子コレステリック液晶 層の色が、それぞれ別々に見えることにより対象物の真贋を識別することを特徴とす る対象物の識別方法。
[11] 前記識別媒体に含まれる第 1の 2層体の円偏光性高分子コレステリック液晶層のう ち、 1層または 2層に、凹凸からなるホログラム形成層を備え、前記対象物の識別媒 体を右円偏光の光だけを通すフィルタと左円偏光の光だけ通すフィルタを備えた簡 易判定器を通して目視し、右円偏光フィルタ側に右円偏光性高分子コレステリック液 晶層の色と、ホログラム形成層を有するときはそこに描かれた絵柄とが見え、左円偏 光フィルタ側に左円偏光性高分子コレステリック液晶層の色と、ホログラム形成層を 有するときはそこに描かれた絵柄とが見えることにより対象物の真贋を識別することを 特徴とする請求項 9に記載の対象物の識別方法。
[12] 前記識別媒体に含まれる第 2の 2層体の円偏光性高分子コレステリック液晶層のう ち、 1層または 2層に、凹凸からなるホログラム形成層を備え、前記対象物の識別媒 体を右円偏光の光だけを通すフィルタと左円偏光の光だけ通すフィルタを備えた簡 易判定器を通して目視し、 2つのフィルタの片側に、前記第 2の 2層体のうち、前記保 護フィルム層側の円偏光性高分子コレステリック液晶層の色と、ホログラム形成層を 有するときはそこに描かれた絵柄とが見え、他方側に、前記対象物側の円偏光性高 分子コレステリック液晶層の色と、ホログラム形成層を有するときはそこに描かれた絵 柄とが見えることにより対象物の真贋を識別することを特徴とする請求項 10に記載の 対象物の識別方法。
PCT/JP2004/006545 2003-05-16 2004-05-14 対象物の識別媒体及び識別方法 Ceased WO2004102234A1 (ja)