WO2005080628A2 - Method for producing silicon nitride films and silicon oxynitride films by chemical vapor deposition - Google Patents

Method for producing silicon nitride films and silicon oxynitride films by chemical vapor deposition Download PDF

Info

Publication number
WO2005080628A2
WO2005080628A2 PCT/IB2005/000170 IB2005000170W WO2005080628A2 WO 2005080628 A2 WO2005080628 A2 WO 2005080628A2 IB 2005000170 W IB2005000170 W IB 2005000170W WO 2005080628 A2 WO2005080628 A2 WO 2005080628A2
Authority
WO
WIPO (PCT)
Prior art keywords
silicon nitride
vapor deposition
chemical vapor
reaction chamber
substrate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/IB2005/000170
Other languages
French (fr)
Other versions
WO2005080628A3 (en
Inventor
Eri Tsukuda
Christian Dussarrat
Jean-Marc Girard
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Air Liquide SA
LAir Liquide SA pour lEtude et lExploitation des Procedes Georges Claude
Original Assignee
Air Liquide SA
LAir Liquide SA a Directoire et Conseil de Surveillance pour lEtude et lExploitation des Procedes Georges Claude
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Air Liquide SA, LAir Liquide SA a Directoire et Conseil de Surveillance pour lEtude et lExploitation des Procedes Georges Claude filed Critical Air Liquide SA
Priority to US10/587,427 priority Critical patent/US20070160774A1/en
Priority to EP05702330A priority patent/EP1713953A2/en
Publication of WO2005080628A2 publication Critical patent/WO2005080628A2/en
Publication of WO2005080628A3 publication Critical patent/WO2005080628A3/en
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

To provide a CVD-based method for the relatively low temperature production of silicon nitride films and silicon oxynitride films that exhibit excellent film properties wherein said method is not accompanied by the production of ammonium chloride. Gaseous aminosilane such as tris(isopropylamino)silane and a gaseous hydrazine compound such as dimethylhydrazine are fed into a chemical vapor deposition reaction chamber that holds at least one substrate and silicon nitride film is formed on the substrate by reacting the two gases in said chemical vapor deposition reaction chamber.

Description

Method for producing silicon nitride films and silicon oxynitride films by chemical vapor deposition This invention relates to a method for producing silicon nitride films and silicon oxynitride films. More particularly, this invention relates to a method for producing silicon nitride films and silicon oxynitride films by chemical vapor deposition (CVD). Silicon nitride films have excellent barrier properties and exhibit an excellent oxidation resistance and for these reasons are "used in the fabrication of microelectronic devices as, for example, an etch stop layer, barrier layer, gate dielectric layer, ONO stack, and so forth. Plasma-enhanced CVD (PECVD) and low-pressure CVD (LPCVD) are the main methods in use at the present time to form silicon nitride films. PECVD is typically carried out by introducing a silicon source (typically silane) and a nitrogen source (typically ammonia and most recently nitrogen) between a pair of parallel plate electrodes and generating a plasma from the silicon source and nitrogen source at low temperature (about 300°C) and low pressure (0.1 torr to 5 torr) by applying high-frequency energy between the electrodes. A silicon nitride film is produced by reaction of the active nitrogen species in the plasma with the active silicon species. The silicon nitride films produced by PECVD in this manner typically do not have a stoichiometric composition and are also hydrogen rich. As a consequence, these silicon nitride films exhibit a low film density and an inadequate thermal stability; they also exhibit poor step coverage. LPCVD uses low pressures (0.1 to 5 torr) and high temperatures (800-900°C). The silicon nitride films afforded by LPCVD have better properties than those of the silicon nitride films produced by PECVD. At the present time, silicon nitride is typically produced by LPCVD by the reaction of dichlorosilane and ammonia gas. However, ammonium chloride is a by-product of the reaction of dichlorosilane and ammonia gas in LPCVD: this ammonium chloride deposits in and clogs the exhaust lines of the reaction device and also deposits on the wafer. LPCVD also has a high thermal budget. The production of silicon nitride by the reaction of hexachlorodisilane and ammonia has recently been introduced in order to reduce the thermal budget (Nonpatent Reference 1). However, due to the large number of chlorine atoms in each molecule of hexachlorodisilane, the use of hexachlorodisilane in fact worsens the problem of ammonium chloride deposition. Moreover, the use of hexachlorodisilane results in the production of silicon-containing particles, which causes a substantial shortening of the life of the pumping system. Another method that has been introduced in order to reduce the thermal budget involves the reaction of ammonia with an organosilicon source (silazane, aminosilane) (Nonpatent Reference 2). This method, however, still uses a high reaction temperature and has a relatively high reaction activation energy.
[Nonpatent Reference 1] M. Tanaka et al., Journal of the Electrochemical Society, Volume 147, p. 2284 (2000). [Nonpatent Reference 2] R. K. Laxman et al., Proceedings of the VMIC Conference, p. 568 (1998).
The object .of this invention, therefore, is to provide a CVD-based method for the relatively low temperature production of silicon nitride films and silicon oxynitride films that exhibit excellent film properties wherein said method is not accompanied by the production of ammonium chloride. According to a first aspect of the present invention, there is provided a method for producing silicon nitride film by chemical vapor deposition, said method being characterized by feeding gaseous aminosilane with formula (I) (H)n - Si - (N(R)2)4_n (I) (each R is independently selected from the hydrogen atom, C-,-4 alkyl, and the trimethylsilyl group and n is an integer with a value of 0-3, wherein the groups R are not all simultaneously a hydrogen atom) and gaseous hydrazine compound with formula (II) N2(H)4.X(R1)X ' (II) (each R1 is independently selected from methyl, ethyl, and phenyl and x is an integer with a value of 0-4) into a chemical vapor deposition reaction chamber that holds at least one substrate, and forming silicon nitride film on said at least one substrate by reacting the two gases in the chemical vapor deposition reaction chamber. According to a second aspect of the present invention, there is provided a method for producing silicon oxynitride film by chemical vapor deposition, said method being characterized by feeding gaseous aminosilane with formula (I) (H)n - Si - (N(R)2)4_n (I) (each R is independently selected from the hydrogen atom, C-,- alkyl, and the trimethylsilyl group and n is an integer with a value of 0-3, wherein the groups R are not all simultaneously a hydrogen atom), . gaseous hydrazine compound with formula (II) N2(H)4.X(R1)X (II) (each R1 is independently selected from methyl, ethyl, and phenyl and x is an integer with a value of 0-4), and oxygenated gas into a chemical vapor deposition reaction chamber that holds at least one substrate, and forming silicon oxynitride film on said at least one substrate by reacting these gases in the chemical vapor deposition reaction chamber. This invention provides a CVD-based method for the relatively low temperature production of silicon nitride films and silicon oxynitride films that exhibit excellent film properties wherein said method is not accompanied by the production of ammonium chloride. This invention is described in additional detail hereinbelow. This invention relates to a method for forming a silicon nitride film or silicon oxynitride film (in some instances collectively referred to hereinbelow as silicon (oxy)nitride film) on a substrate by CVD. The inventive method encompasses the use of gaseous aminosilane with formula (I) as precursor for the silicon (oxy)nitride film
Figure imgf000005_0001
and the reaction therewith of gaseous hydrazine compound with formula (II). N2(H)4.X(R1)X (II)
Each R in formula (I) is independently selected from the hydrogen atom, C1-4 alkyl, and the trimethylsilyl group (-Si(CH3)3), while the subscript n is an integer with a value of 0 to 3. However, the groups R may not all simultaneously be a hydrogen atom. Each R1 in formula (II) is independently selected from methyl, ethyl, and phenyl, while the subscript x is an integer with a value of 0 to 4. Specific examples of the aminosilane (I) are bis(tert-butylamino)silane (BTBAS), tris(isopropylamino)silane (TIPAS), and tetrakis(ethylamino)silane (TEAS). The hydrazine compound (II) can be specifically exemplified by dimethylhydrazines such as 1 ,1- dimethylhydrazine (UDMH). The production of silicon nitride films will be described first. In this case, the gaseous aminosilane and gaseous hydrazine compound, along with inert diluent gas as necessary or desired, are fed into a chemical vapor deposition reaction chamber (referred to below as the
CVD reaction chamber) that holds at least one semiconductor substrate and the gaseous aminosilane and gaseous hydrazine compound are therein reacted to produce a silicon nitride film on the substrate.
The interior of the CVD reaction chamber can be maintained under a pressure from 0.1 torr to 1000 torr during this reaction between the gaseous aminosilane and gaseous hydrazine compound. This reaction (formation of silicon nitride film) can generally be run at the relatively low temperatures of 300°C to 650°C. An appropriate gaseous aminosilane : gaseous hydrazine compound molar ratio is from 1 : 1 to 1 : 100. As may be understood from formulas (l) and (II), these compounds do not produce ammonium chloride upon their reaction, and the inventive method therefore does not suffer from the prior-art problem of ammonium chloride deposition. The inert diluent gas that may be introduced into the CVD reaction chamber on an optional basis can be an inert gas such as nitrogen or a rare gas such as argon. In order in accordance with the present invention to form a silicon oxynitride film on the substrate, at least one oxygen source gas is fed into the CVD reaction chamber along with the gaseous aminosilane, gaseous hydrazine compound, and (optional) diluent gas already described above with reference to the production of silicon nitride film. This oxygen source gas can be an oxygen-containing gas selected from the group consisting of oxygen (O2), ozone (O3), waϊer vapor (H2O), hydrogen peroxide (H2O2), nitric oxide (NO), nitrogen dioxide (NO2), and nitrous oxide (N2O). The silicon oxynitride film can be formed on the substrate by reacting the gaseous aminosilane, gaseous hydrazine compound, and oxygen source gas using the same temperature and pressure conditions and gaseous aminosilane : gaseous hydrazine compound molar ratio already described above with reference to the production of silicon nitride film. The oxygen source gas can be introduced into the CVD reaction chamber at a molar ratio with respect to the gaseous aminosilane of 1 : 1 to 1 : 100.
Examples This invention is described hereinbelow through examples, but this invention is not limited by these examples.
Example 1 BTBAS gas, UDMH gas, and nitrogen (carrier gas) were introduced under the conditions given below into a reaction chamber holding a silicon substrate and a silicon nitride film was formed on the silicon substrate at temperatures of 525°C to 620°C. BTBAS gas flow rate: 3.5 seem UDMH gas flow rate: 25 seem nitrogen flow rate: 35 seem pressure in the reaction chamber: 1.0 torr The silicon nitride deposition (growth) rate was measured at 525°C, 550°C, 575°C, and 620°C and its logarithmic value was plotted against the reciprocal of the reaction temperature (T in kelvin) times 1000. The results are reported in Figure 1. In addition, the Si/N atomic ratio of the silicon nitride grown at 620°C was determined by Auger electron spectroscopy; the results are reported in Table 1. Table 1 also reports the silicon nitride growth rate at 620°C and the reaction activation energy.
Example 2 TIPAS gas, UDMH gas, and nitrogen (carrier gas) were introduced under the conditions given below into a reaction chamber holding a silicon substrate and a silicon nitride film was formed on the silicon substrate at temperatures of 550°C to 620°C. TIPAS gas flow rate: 3.0 seem UDMH gas flow rate: 25 seem nitrogen flow rate: 30 seem pressure in the reaction chamber: 1.0 torr The silicon nitride deposition (growth) rate was measured at 550°C, 575°C, 600°C, and 620°C and its logarithmic value was plotted against the reciprocal of the reaction temperature (T in kelvin) times 1000. The results are reported in Figure 2. In addition, the Si/N atomic ratio of the silicon nitride grown at 620°C was determined by Auger electron spectroscopy; the results are reported in Table 1. Table 1 also reports the silicon nitride growth rate at 620°C and the reaction activation energy.
Example 3 TEAS gas, UDMH gas, and nitrogen (carrier gas) were introduced under the conditions given below into a reaction chamber holding a silicon substrate and a silicon nitride film was formed on the silicon substrate at temperatures of 525°C to 620°C. TEAS gas flow rate: 3.5 seem UDMH gas flow rate: 25 seem . nitrogen flow rate: 35 seem pressure in the reaction chamber: 1.0 torr The Si/N atomic ratio of the silicon nitride grown at 620°C was determined by Auger electron spectroscopy; the results are reported in Table 1. Table 1 also reports the silicon nitride growth rate at 620°C and the reaction activation energy. Comparative Example 1 Silicon nitride was grown on a silicon substrate as described in Example 1 , but in this case using ammonia in place of the UDMH gas. The Si/N atomic ratio of the silicon nitride grown at 620°C was determined by Auger electron spectroscopy; the results are reported in
Table 1. Table 1 also reports the silicon nitride growth rate at 620°C and the reaction activation energy.
Comparative Example 2 Silicon nitride was grown on a silicon substrate as described in Example 2, but in this case using ammonia in place of the UDMH gas. The Si/N atomic ratio of the silicon nitride grown at 620°C was determined by Auger electron spectroscopy; the results are reported in Table 1. Table 1 also reports the silicon nitride growth rate at 620°C and the reaction activation energy.
Comparative Example 3 Silicon nitride was grown on a silicon substrate as described in Example 3, but in this case using ammonia in place of the UDMH gas. The Si/N atomic ratio of the silicon nitride grown at 620°C was determined by Auger electron spectroscopy; the results are reported in Table 1. Table 1 also reports the silicon nitride growth rate at 620°C and the reaction activation energy. Table 1
Figure imgf000010_0001
As the preceding examples make clear, this invention enables the relatively low temperature growth of high-quality silicon nitride at a relatively low activation energy.
Brief Description of the Drawings - Figure 1 contains a graph that shows the relationship between the CVD reaction temperature and silicon nitride growth rate in Example 1; - Figure 2 contains a graph that shows the relationship between the CVD reaction temperature and silicon nitride growth rate in Example 2.

Claims

Claims
1. Method for producing silicon nitride film by chemical vapor deposition, characterized by feeding gaseous aminosilane with formula (I) (H)n - Si - (N(R)2)4_n (I) (each R is independently selected from the hydrogen atom, C-|.4 alkyl, and the trimethylsilyl group and n is an integer with a value of 0-3, wherein the groups R are not all simultaneously a hydrogen atom) and gaseous hydrazine compound with formula (II) N2(H)4.X(R1)X (II) (each R is independently selected from methyl, ethyl, and phenyl and x is an integer with a value of 0-4) into a chemical vapor deposition reaction chamber that holds at least one substrate, and forming silicon nitride film on said at least one substrate by reacting the two gases in the chemical vapor deposition reaction chamber.
2. The method described in Claim 1 , characterized in that the reaction is run at temperatures of 300°C to 650°C.
3. The method described in Claim 1 or 2, characterized in that the pressure in the reaction chamber is established at 0.1-1000 torr.
4. Method as described in any of Claims 1-3, characterized in that the aminosilane : hydrazine compound molar ratio is 1 : 1 to 1 : 100.
5. Method for producing silicon oxynitride film by chemical vapor deposition, characterized by feeding gaseous aminosilane with formula (I) (H)n - Si - (N(R)2)4_n (I) (each R is independently selected from the hydrogen atom, C^ alkyl, and the trimethylsilyl group and n is an integer with a value of 0-3, wherein the groups R are not all simultaneously a hydrogen atom), gaseous hydrazine compound with formula (II) N2(H)4.X(R1)X (II) (each R1 is independently selected from methyl, ethyl, and phenyl and x is an integer with a value of 0-4), and oxygenated gas into a chemical vapor deposition reaction chamber that holds at least one substrate, and forming silicon oxynitride film on said at least one substrate by reacting these gases in the chemical vapor deposition reaction chamber.
6. The method described in Claim 5 for producing silicon oxynitride film, characterized in that the oxygenated gas is at least one selection from the group consisting of O2, O3, H2O, H2O2, NO, NO2, and N2O.
7. The method described in Claim 5 or 6, characterized in that the reaction is run at temperatures of 300°C to 650°C.
8. Method as described in any of Claims 5-7, characterized in that the pressure in the reaction chamber is established at 0.1-1000 torr.
9. Method as described in any of Claims 5-8, characterized in that the aminosilane : hydrazine compound molar ratio is 1 : 1 to 1 : 100.
10. Method as described in any of Claims 5-9, characterized in that the aminosilane oxygenated gas molar ratio is 1 : to 1 : 00.
PCT/IB2005/000170 2004-02-02 2005-01-19 Method for producing silicon nitride films and silicon oxynitride films by chemical vapor deposition Ceased WO2005080628A2 (en)