WO2005087897A1 - Process and plant for conversion of waste material to liquid fuel - Google Patents

Abstract

A process and plant for the thermocatalytic conversion of waste materials into reusable fuels and a fuel produced by the process, involving the steps of delivering melted waste material (11) to one or more pyrolysis chambers (26) via heated and valved manifolds (22) and effecting pyrolysis of the waste material into a gascous state in an oxygen purged and pressure controlled environnent. Pyrolytic gases are, then transferred to a catalytic converter (29) where the molecular structure of the gaseous material is altered in structure and form, with gases then transferred to one or more condensers (30a) to distil and cool gases in to their respective fractions. After post pyrolysis treatment, fuel fractions thon form a useable fuel. Includes the melting of waste (plastic) material (11) before delivery into any of the pyrolysis chambers (26), making the movement of material into the catalytic tower (29) a semi-continuous operation, directing melted waste material into one or more, but preferably four, pyrolysis ehambers (26a, b, c, d), making each chamber capable of independent operation, optionally mechanically removing waste char fram the pyrolysis chamber (107) by use of an internat auger (112) or other suitable means.

Description

PROCESS AND PLANT FOR CONVERSION OF WASTE MATERIAL TO LIQUID FUEL

FIELD OF INVENTION The present invention relates to the field of processing plastic and preferably waste plastic material into new products, which have valuable and useful properties. In one aspect, the present invention relates to a process for converting plastics to liquid hydrocarbons, particularly diesel fuel. It will be convenient to hereinafter describe the invention in relation to the conversion of plastics to diesel fuel, however it should be appreciated that the present invention is not limited to that use only. BACKGROUND ART Numerous unsuccessful attempts have been made in the past to efficiently reprocess a feedstock of waste plastics back into a liquid hydrocarbon product that has valuable and useful properties. A considerable tonnage of waste commodity plastics, or polymers, are improperly disposed of each year. In previous years, there has ^"been considerable improvement in the collection and recycling of common waste polymers. However, the recycling and reuse of waste polymers, as now practiced without subsidies have proven to be uneconomic, forcing the abandonment of many recycling efforts. The recycling of waste polymers as fuel has also not proven practical because of the inability to collect sufficient quantities to sustain operation of the recycling machinery. Thermolysis refers to the dissociation or decomposition of chemical compounds by heat and, in particular, is a process that has been described whereby plastic waste material is converted to liquid fuel by thermal degradation (cracking) in the absence of oxygen. Plastic waste is typically first made molten within a stainless steel chamber under an inert purging gas, such as nitrogen. This chamber then heats the molten material to a gaseous state that is drawn into a catalytic converter and cracked to form carbon chain lengths of a certain desirable range. ^• Hot pyrolytic gases of the desired carbon length range are then condensed in one or more condensers to yield a hydrocarbon distillate comprising straight and branched chain aliphatics, cyclic aliphatics and aromatic hydrocarbons. The resulting mixture is roughly equivalent to regular diesel fuel after the placement of additives and the implementation of other minor downstream processing actions. Diesel fuel is a blend of hydrocarbon compounds known as distillates that are heavier than gasoline but lighter than lubricating oil. Diesel is a mixture of straight-chain and branched alkanes, cyclic saturated hydrocarbons and aromatics. Diesel fuel is designed to operate in a diesel engine only, where it is injected into the diesel engine combustion chamber with compressed, high-temperature air and ignites spontaneously. Conversely, gasoline in a petrol engine is ignited by spark plugs. Diesel fuel produced by pyrolysis and other methods must meet a range of composition requirements before being certified for sale in a number of countries. Existing thermolysis system based plants are. in operation but display a series of significant shortfalls and disadvantages, which ultimately result in inefficient production and throughput of liquid hydrocarbons from waste plastic materials. A. primary- disadvantage is the process of loading plastic waste manually, and also the system being unable to receive variable sizes of plastic waste feedstocks. Existing systems that receive manually loaded blocks or rolls of plastics leave a great deal of excess air space in the pyrolysis chamber, which must be sealed to allow purging f atmospheric gas and melting of the material. Once sealed, no fbrther waste can be added to the chamber which otherwise has space for more material once it is melted. The inability to fill the pyrolysis chamber to its maximum reduces the speed of the entire process and ultimately the throughput of these known thermolysis systems. Typically, the known thermolysis plants have two pyrolysis chambers, known as twin-chamber systems, which work together at- n approximately equal rate. Of particular issue with the set up of existing pyrolysis chambers is that fuel may nly be produced in a batch type basis. Once both chambers complete the pyrolysis of waste material in unison, it is necessary to wait for each to 'cool before unwanted carbonaceous char can be removed from the internal base of each chamber. It is therefore presently necessary to •wait for each chamber to cool and be hand cleaned of char before the chambers can be used again for second and subsequent batches. Whilst it may be necessary in a batch process according to one aspect of the present invention to manually vacuum out char by access through the manhole (inspection port) in the chamber lid, in a preferred continuous process according to another aspect of the invention this issue is addressed below. In addition to this set-up limitation associated with batch processes, the physical size of the existing chambers greatly limits the batched throughput capacity of waste materials. Of further issue with existing thermolysis systems are higher frequency clean out times of chambers, poor heat transfer within the waste feedstock itself, increased process time per chamber load and also the expense and fouling of consumable catalysts. The final issue is the quality of the final fuel product including a measure of diesel fuel's ability to reduce wear on contacting solid surfaces found in some fuel pumps and injectors. Of further issue with existing thermolysis systems is that fuel produced is often of a variable standard and cannot be used in engines and other machinery that lacks a tolerance to such fuel inconsistency. Of particular concern is the property of the fuels produced by these existing processes, which have a flash point generally varying between 25°C and 45°C, which are too low due to the high presence of light fuel fractions. Such fuels are therefore unsuitable for the expected use in all regions of the world, and applications other than stationary engines. Other prior art processes produce heavier oils which, are also unsuitable for diesel engine operation. The above discussion and any other discussion of pre-existing documents, devices, acts or knowledge in this specification is included to explain the context of the invention- It should not be taken as an admission that any of the material forms a part of the prior art base or the common general knowledge in the relevant art in Australia or elsewhere on or before the priority date of the disclosure and claims herein. In light of the foregoing discussion, an object of the present invention is to provide a thermolysis process that has an increased throughput of liquid hydrocarbons that are of consistent quality, using waste plastic stockfeed, A further object of the present invention is to at least alleviate or overcome at least one disadvantage associated with the prior art.

SUMMARY OF INVENTION The present invention provides a process for the thermocatalytic conversion of waste materials into reusable fuels, comprising the steps of: delivering waste material to a melting means; directing melted waste material from one or more manifolds into one or more pyrolysis chambers; heating waste material to effect pyrolysis of material, into gaseous state in a substantially oxygen purged and. pressure controlled env onment; transferring resulting gases to a catalytic converter means wherein the molecular structure of the gaseous material is altered in structure and form; transferring gases to one or more condenser means to distil and cool gases in to their respective fractions; and wherein the fractions form at least one type of useable fuel. In another aspect, the present invention provides a process for the conversion of waste organic plastic materials into diesel fuels, including the steps of: b) delivering the comminuted waste material to a melting means; c) transferring the melted waste material to one or more pyrolysis chambers; d) heating waste material to effect pyrolysis of material into a gaseous state in a substantially oxygen purged and pressure controlled environment; e) transferring the gaseous material to a catalytic converter means wherein the molecular structure of the gaseous material is altered; and f) transferring gases to condenser means to cool and separate the gaseous material into fractions to form at least one type of useable fuel The raw waste plastic material may initially be fed into the melting means! However- preferably the waste material is subject to preliminary processing whereby the inventive process includes the preliminary step of: a) comminuting the waste material. Step a) may comprises mechanically working bodies of waste material, such as sheets, clumps, blocks, lumps and other forms, to break the material into smaller pieces or particuiate material such as flakes having a high surface to volume ratio. The advantages of comminuting the waste plastic material include: i) the feeding of the waste material in the next step in the process is made easier as the material may be conveyed by a variety of means including blowing, gravity feed, etc., through an delivery means or opening of optionally limited width or size; and ϋ) the duration or energy required for the melting means is reduced as .the individual particles are easier to melt and the heat transfer between particles in enhanced. In another aspect, the invention provides a plant for the conversion of waste plastic materials into diesel fuels, the plant including: a) comminuting means for breaking the waste material into particuiate matter; b) melting means for receiving and melting the particuiate waste material ; c) pyrolysis chamber for receiving waste material, the pyrolysis chamber operative to: i) seal the chamber from the environment and to purge air-borne oxidants from the pyrolysis chamber by the introduction of a non-oxidising gas; and ii) heat the waste material to effect pyrolysis of the waste material into a gaseous state in a substantially air-borne oxidant-free and pressure-controlled environment; d) catalytic converter means operative to receive and crack the gaseous waste material whereby the molecular structure of the gaseous material is altered; and e) condenser means operative to receive, cool and separate the cracked gaseous material into fractions to form at least one type of useable fuel. The pyrolysis chamber may include an auger to remove accumulating char from the base of the pyrolysis chamber and allow continuous feed of molten waste material into the pyrolysis chamber and continuous production and delivery to the catalytic converter means of the of the gaseous waste material. The heat source required for the melting means may involve a furnace or electrical heating means having an independent heating source not associating with another part of the process. Alternatively, heat energy from another part of the process may be reclaimed and/or recycled and used for the melting means. In a preferred form, the heat energy from heating means of one or more of the pyrolysis chambers is directed to the melting means. For example, where the pyrolysis chamber is heated by a furnace, the hot exhaust gases may be reclaimed and used to heat the melting means. The hot exhaust gases may be fed directly coils surrounding a melting means chamber or may transfer heat energy to the melting means via a heat exchanger. The heat exchanger may utilise a suitable heat exchange fluid such as steam or, more preferably, oil. The condenser means may include a selective low-teanperature condenser operative to remove light fractions from the cracked gaseous material. The condenser means may differentially condense different fractions of the gaseous product from the catalytic converter means to select one or more fractions suitable for use as a fuel. For example, the condenser means may include two more condensers capable of condensing fractions at different temperatures or ranges thereof. In a preferred aspect, the condenser means includes a condenser for obtaining fractions suitable for diesel fuel and light fractions to be utilised or disposed of. In a preferred aspect, the invention provides for a process for the thermocatalytic . conversion of waste materials into reusable fuels, wherein melted waste material is directed into one or more pyrolysis chambers that are capable of independent operation. In a further preferred aspect, the invention provides for a process for the theimocatalytic conversion of waste materials into reusable fuels, wherein a plurality of pyrolysis chambers operate independently to allow cyclic transferral of gaseous material from one or more pyrolysis chambers to a catalytic converter means. In a further preferred aspect, the invention provides for a process for the thermocatalytic conversion of waste materials into reusable fuels, wherein a plurality of pyrolysis chambers are used alternately at least one at a time so that one pyrolysis

' chamber is able to cool while another pyrolysis chamber is able to transfer gaseous material to a catalytic converter means. In a further preferred aspect, the invention provides for a process for the thermocatalytic conversion of waste materials into reusable fuels, wherein one or more pyrolysis chambers are actively cooled after completing transferral of gaseous waste material to a catalytic converter means. In a further preferred aspect, the invention provides for a process for the thermocatalytic conversion of waste materials into reusable fuels, wherein char is mechanically removed from one or more pyrolysis chambers by use of one or more augers. This automated method of removing char from the chamber allows the chamber to perform a semi-continuous operation because the need to remove char manually from the chamber after a particular batch is eliminated. Although char may continue to accumulate in the chamber over time, the rate of accumulation is slower due to the continual removal of a large proportion of the char produced. Much less frequent manual removal of the char from the chamber may therefore be required. Accordingly, in a further preferred aspect, the invention provides for a process for the thermocatalytic conversion of waste materials into reusable fuels, wherein the process is at least semi-continuous in operation. The continuous process thermolysis system may operate, in principle, similar to a batch system. It may have, however, several distinct refinements that differ from the batch system. Principally, the continuous process may include a continuous feed system to the pyrolysis chambers and/or distillation columns in lieu of one or a series of condensers. The thermolysis continuous process plant may use the thermocatalytic conversion of waste plastic into useable clean fuel (for example, diesel fuel, also known as middle distillate). This system can use contaminated plastics in the process. The level of contamination will, however, affect yield rates, as less plastic per volume is processed. The process thermally degrades (cracks) plastic waste in an oxygen free environment inside a pyrolysis chamber, pyrolysing (cracking) it into a gaseous state. The hot pyrolysis gases may pass through a catalytic converter. The catalytic converter may include a number of catalytic surfaces. Preferably, the catalytic surfaces comprise alloy plates and, more preferably, these catalytic surfaces characterised by not being able to be poisoned or ^• consumed. Two reactions occur in the process. A first reaction involving cracking occurs while the plastic is heated and a second reaction occurs when the hot pyrolysis gases contact the alloy plates. The gases are then cracked and reformed to form carbon chain lengths of a certain desirable range. Hot pyrolytic gases of the desired carbon length range may then be condensed in one or more condensers or, more preferably, in one or more distillation towers, to yield a hydrocarbon distillate comprising straight and branched chain aliphatics, cyclic aliphatics and aromatic hydrocarbons. The resulting mixture is preferably roughly equivalent to regular diesel fuel after the placement of additives and the implementation of other minor downstream processing actions, such as the removal of particularly light fractions. Thus the inventive process may produce fuel that is substantially equivalent to the diesel fuel standard in Australia, specified as AS 3570-1 98. In a further preferred aspect, the invention provides for a process for the thermocatalytic conversion of waste materials into reusable fuels, wherein the process uses at least four pyrolysis chambers which receive melted waste material by selective operation of a manifold system having a corresponding number of inlet pathways. The manifold system is preferably pre-heateςL optionally using hot exhaust gases from, for example, the pyrolysis furnace. The four-way manifold is preferably adapted to automatically feed each of four pyrolysis chambers in torn. In a further preferred aspect, the invention provides for a process wherein the waste material includes or consists of polyolefins and/or other material considered waste material for the purposes of the invention. The waste materials are preferably selected from the group consisting of addition polymers, condensation polymers, and combinations thereof. The waste organic materials are preferably selected from the group consisting of waste plastic, used oils and lubricants, and combinations thereof. In a fhrther preferred aspect, the invention provides for a process wherein the waste organic materials are selected from the group consisting of aliphatic species, aromatic species, species containing both aliphatic and aromatic substituents, and combinations thereof. In a further preferred aspect, the invention provides for a process wherein the melting means is a hot-melt in-feed system. The melting means may be located prior to the pyrolysis chamber. In a further preferred aspect, the invention provides for a process wherein the catalytic converter consists of a series of high-surface area, internal metal plates that are the catalyst. The plate catalyst preferably is selected from the group including ceramics, zeolites, the silicates of iron Fe3+, cobalt Co2+, nickel Ni2+, Raney nickel, manganese

Mn\2+, chromium Cr3+₃ copper Cu2+ and or their mixtures or the catalyst MCM-41 , In a further preferred aspect, the invention provides for a substantially carbon based fuel product produced by the process of the invention, the fuel including carbon chains in the range of length C6 to C25. The substantially carbon based fuel product preferably includes carbon chains in a range peaking at length CI6. Preferably, the substantially carbon based fuel product that is substantially equivalent to the diesel fuel standard in Australia, specified as AS 3570-199S. Reusable hydrocarbons and reusable fuels include liquid hydrocarbons. The fuel product may be stored in a storage vessel. The storage vessel is preferably a storage tank. In the inventive process, the following are further preferred options. Drawing off may be by a screw drive system. A pipe means may be a heated lag pipe. A manifold may be a heated 4-way manifold. The manifold may direct melted waste to one of four pyrolysis chambers. The oxidative atmosphere in the pyrolysis chamber must be neutralised, for example, by purging oxygen and other air-bom oxidaπts from the chamber by the introduction of a gas. The purge gas is preferably selected from the group consisting of nitrogen, helium, or other inert gases or combinations thereof. In a further preferred aspect, the invention provides for a process wherein the pyrolysis chamber heating range is 390 °C - 410 °C. The pyrolysis chamber heating range may, however, have a wider range, of 350 °C - 425 °C. The pyrolysis chambers is preferably pressurised to a pressure of 1.08 bar- In a further preferred aspect, the invention provides for a process wherein the catalytic converter uses no consumable catalyst. The gaseous material is preferably pyxolised to form hydrocarbon molecules. Excess non-condensable (very light) gases may be transferred through a caustic wash to remove acids, then to an off-gas chamber where they can be destroyed. The catalytic converter is preferably adapted to modify carbon chains longer than C25 and to reform carbon chains shorter than C6. The catalytic converter is preferably heated to 220 °C or greater. The metal catalyst will preferably 'crack' parafϊnic chains longer than C25. The catalyst preferably ensures that the final fuel has a carbon chain distribution in ^"the range CS-C25 and peaking at CI 6 (cetane). The catalytic converter is preferably heated by exhaust gases from the furnace of one or more of the pyrolytic chambers. Similarly, the hot melt chamber may be heated by exhaust gases from the furnace of one or more of the pyrolytic chambers. The non-condensable gases may be directed to the furnace for burning. In a further preferred aspect, the invention provides for a process wherein the condensing temperature is not consistent across all elements of the condensing system. The upper condensing coil is preferably run at a lower temperature than the lower condensing coil, for example, to separate the light fractions from the remaining fractions best suited for a middle distillate composition. The separation of the light fraction may be carried out during the thermolysis process. Other aspects and preferred aspects are disclosed in the specification and/ or defined in the appended claims, forming a part of the description of the invention. Advantageously, the invention provides a new process that has the capacity, compared to the prior art, to greatly increase the throughput of waste plastic stockfeed to produce liquid hydrocarbon fuel that is of a consistent quality. This throughput is primarily achieved by the method by which waste stockfeed is prepared and delivered into a pyrolysis chamber system. Advances made by the invention process include melting waste (plastic) material before delivery into any of the main pyrolysis chambers, for example, by use of a hot-melt in-feed system to affect a greater fill and therefore the efBciency of each pyrolysis chamber. Further advances are made by making the movement of material into the catalytic tower a semi-continuous operation. This semi- continuous operation is in part achieved by: • Directing melted waste material into a minimum of one pyrolysis chamber, but preferably two or more, and most preferably four pyrolysis chambers, each chamber preferably being capable of independent operation. • The optional use of a pre-heated four-way manifold system having a corresponding number of inlet pathways that may be adjusted to direct melted waste material into ne or more of the pyrolysis chambers. • Where more than one pyrolysis chamber is employed, cooling one pyrolysis chamber while another pyrolysis chamber is able to maintain operation to continue to transfer gaseous material to a catalytic converter means. • Mechanically removing waste char from one or more pyrolysis chambers by use of one or more internal augers or other suitable means. Further aspects of invention relate to various performance improvements to the overall process as disclosed herein. The process and associated apparatus of the present invention have been found to result in one or more of the following advantages: • reduction or elimination of manual handling of the plastic feedstock; • shortening the time taken to get the prime pyrolysis chamber to full operating temperature; • achieving 100% molten plastic feedstock capacity prior to prime chamber operation commencesment - this maximises the volume of material in each chamber before treatment commences; # improved uniformity of temperature, heat transfer to materials and pyrolysis; • improved fuel consistency; and • reduction in the effort and time required for the removal of charring and in system cleaning. The above advantages result in the expansion of the throughput and production capacity (compared to the prior art systems) to 9,500 litres per day from 10 tonnes of waste plastics. Active cooling increases each chamber cycle time per day from one current cycle per day to approximately 2.5 cycles per 48 hour period (per chamber) increasing the capacity of the system to process up to 12.5 tonnes per 24 hour period, yielding approximately 11,750 litres of fuel oil and approximately 750 litres of lights per 24 hour period, ("lights" being a type of white spirit (light hydrocarbon)).

BRIEF DESCRIPTION OF THE DRAWINGS Further scope of applicability of the present invention will become apparent from the detailed description given hereinafter. However, it should be understood that the detailed description and Specific examples,^' hile indicating preferred embodiments of the invention, are given by way of illustration only, since various changes and modifications within the spirit and scope of the invention will become apparent to those skilled in the art from this detailed description. Further disclosure, objects, advantages and aspects of the present application may be better understood by those skilled in the relevant art by reference to the following drawings of preferred embodiments which are given by way of illustration only, and thus are not limitative of the present invention, and in which: FIG 1 illustrates a diagrammatic overview of a thermolysis system with major features according to a first preferred embodiment of the present invention; PIG 2 illustrates a plan view of a plant layout of a thermolysis system according to the first preferred embodiment of the present invention; FIG 3 illustrates an elevation or side view of the plant layout shown in FIG 2; FIG 4 illustrates a gas chromatography chromatogram chart indicating the relative proportion of carbon chain lengths within normal diesel fuel. The Y axis of this chart indicates the quantity; PIG 5 illustrates a gas chromatography chromatogram chart indicating the relative proportion of carbon chain lengths within diesel fuel produced by the thermolysis system of the first preferred embodiment of the present invention. The Y axis of this chart indicates the quantity; FIG 6 illustrates a diagrammatic overview of a thermolysis system with major features according to a second preferred embodiment of the present invention; and FIG. 7 illustrates a diagrammatic overview of a desulphurising system. DETAILED DESCRIPTION Unless defined otherwise in this specification, all technical terms are used herein according to their conventional definitions as they are commonly used and understood by those of ordinary skill in the art. Referring to the figures wherein like reference numerals designate like or corresponding parts throughout the several views, and referring particularly to Figs, 1, 2 and 3, an overview process 6 and plant set up for converting waste plastic to diesel fuel using a batch process according to the invention is shown.

Early process operation Waste plastics in their original form of plastic sheets, drums, rolls, blocks and flat pieces are placed in a stockpile 11 and moved via an underfloor variable speed pan conveyor 13, through to a granulator 12 to reduce the size of the large items of waste plastic. An over-band magnet 15 and metals container (14) is situated above the conveyor 13 to remove any metals prior to entry into the granulator 12. From the granulator 12, the reduced plastics are delivered (for example, by conveyor, auger or blower) through to a fluidised holding silo 17. Although a variety of mechanisms could be used to transfer the plastic from one place to another, delivery in this preferred method is achieved via a blower 16. A dust collector I S associated with the holding silo 17 collects excess dust, created by the action of the blower 16. All operations just described are r^liminary preparations and may or may not be completed outside the normal operating times of the general thermolysis system discussed below.

BATCH THERMOLYSIS PROCESS To ^"begin the thermolysis process, granulated waste plastics are drawn from the holding silo 17 via a second blower 19 and force feeder 20, into a hot-melt feed system 21 including an extruder, which melts the waste plastics to a suitable temperature for adequate liquefied flow into a heated melt distribution manifold 22 via heated pipes which maintain adequate flow rates. The distribution manifold 22 is a valve operated system allowing distribution of liquid waste through four separate outlet pipes which each lead to a separate pyrolysis chamber 26a, 26b, 26c or 26d. Although the description is made with reference to four chambers, it is to be understood that the present invention is applicable to any number of chambers, designated at feature 26 herein. The chamber receiving liquid waste is preferably filled to 80% capacity with liquid waste and then sealed and annospheric ambient gases are substantially purged through the introduction of a preferably nitrogen gas blanket. Nitrogen is sourced from the nitrogen generator 25, through a nitrogen storage vessel 24, according to a nitrogen monitoring device 23. The gas used to purge the atmospheric gas may otherwise be selected from the group consisting of helium, or other inert gases or combinations thereof. Each pyrolysis chamber is situated inside a heating unit, such as a furnace 28 with a natural gas burner 27. Furnace heat is applied to bring the internal temperature of the main^' pyrolysis chamber up to a temperature between 375°C and 420°C. Standard internal rotating agitators 42 ensure even heat transfer and a homogenous plastic mixture. Non feedstock materials or contaminants then fall to the bottom of the chamber 26 to create a carbonaceous char material which must be regularly removed before it builds-up on the pyrolysis chamber walls, wherein it acts as a thermal insulator and lowers the heat transfer to the plastic waste material. Char is therefore removed by suitable means, such as being continually scrapped off by rotating blades so that liberated char accumulates as a friable fine black powder at the bottom of the pyrolysis chamber, wherein it is vacuumed out by hand after each batch. However, as will be explained below with reference to an alternative continuous process, an auger positioned at the base of the chamber can be used to periodically remove accumulated char. To effect faster input and output of waste material, active cooling is achieved by cooling the inside of each chamber with Na from the Nz line, and external cooling of the chamber by the burner fan blowing air around the chamber inside the fomace, which is used on each of the main chambers 26 to reduce the cooling time from the standard (prior art) 12 hours- to a maximum (for the plant and process of the invention) of 7 hours, allowing faster turnaround between one process cycle and the next. Cooling may be implemented by fan or by other suitable cooling means known in the art. With a system of at least four pyrolysis chambers available for operation, one or two chambers may be set to operate and deliver pyrolytic gases to the catalytic converter . 29, While one or two chambers deliver these gases as required, the remaining chambers may be prepared for a subsequent batch of molten plastic input from the hot melt system, thus allowing a semi-continuous operation and fuel output as a result of staggering the operation of the chambers. The valved heat distribution manifold 22 may be used to direct molten plastic material into any of the chambers as necessary to allow for system operation in a semi-continuous manner. The next chamber in sequence of operation is pre-heated to between 170°C-220^ΛC while the liquefied feedstock fills the chamber to 80% capacity. Upon completion of filling, the selected main chamber temperature is raised to between 375°C and 420°C and the liquid waste plastic in the sealed chamber is made gaseous by pyrolysis at this temperature causing at least partial breaking of carbon chain lengths randomly into various lengths. The pyrolised gases are then drawn through into a catalytic converter reaction tower 29 where the gas components are theπnolytically cracked. The catalytic reaction tower 29 contains a system of plates made from a special catalytic metal alloy. The metal plates are positioned so that the hot pyrolytic gases must take a torturous path to maximize contact area and time with the metal plates. The catalyst chamber 29 is heated to 220 Deg.C or greater -using the exhaust gases from the furnace of the selected pyrolysis chamber 26. The metal catalyst cracks carbon paraf ic chains longer than C25 and reforms chains shorter than C6. There is conversion of alpha-olefln chains (1-alkenes) to saturated alkanes. The catalyst ensures that the final fuel has a carbon chain distribution in the range C8-C25 and peaking at C16 (cetane). The metaϊ catalyzers are made of metals including Ni and Cu, or ceramics or zeolites in shape of punched plate and wire mesh type. The other catalysts include CM-41 and the silicates of iron Pe3+, cobalt Co2+, nickel NΪ2-K, Raney nickel, manganese

chromium Cr3+, copper Cu2+ and/or their mixtures. The catalytic plates may be made from any one of these metals, or a combination thereof. T-he catalyst is preferably not consumed or poisoned. The catalytic tower 29 uses technology known in the petrochemical industry and all detail concerning the processes of the reaction tower are publicly available in JP 3344952. Thermalytically cracked gases are then drawn from the reaction tower 29 into one or more condensers 30 and/or 30a, where gases are distilled into separate fractions. Condenser 30 cools an distils the gases, drawing off liquids condensed by contact with a 60°C inlet temperature condensing coll.. Condenser 30a cools and distils gases using two 20*C inlet temperature coils and a top condensing coil having an inlet temperature of 8°C for light fractions.. There are three cooling coils in the second condenser 30a and these are cooled with cooling tower water or water chiller units 31 . Water flows through preferably three coils run co-current with the direction of pyrolysis gas flow. At each coil position there is a catchment tray and a bubble cap so the hot pyrolysis vapours must flow through the condensing coils.. This allows efficient condensation of the pyrolysis condensates. Cooling tower or chiller water also flows to some of the seals throughout the line to keep them cool. In particular, seals that are most advantageously cooled include the agitator seal on the agitator shaft 42 and the seal on the chamber 26 inspection port (man hole) in the chamber lid. The remaining non-condensable gases (NCG) not condensed by the 8"C condensing coil are piped through to a gas scrubber 34 which supplies mildly basic water to scrub out the acid, neutralize the remaining NCGs and render the gases suitable for incineration by the off-gas burner 40. Alternatively, the gas may be recycled to a burner m the furnace as necessary. A caustic water tank 36 supplies alkaline water which is regularly dosed with caustic from a caustic make up tank (35) via a dosing pump to maintaining the correct pH value in the caustic water tank 36. From the condensers, the bulk of fractionated fuel that is not the light component is piped into an oil recovery tank 33. or other operating tanks designed for the storage of liquid fuels, in this embodiment intermediate tanks 32. The fractionated fuels is then piped to a centrifuge 38, noting that more than one centrifuge may be necessary depending on the production volumes. The centrifuge removes carbon particles, water, ammonium hydroxide and other contaminates that may be present in the fuel. The fuel is then pumped to quality assurance tanks (QA) 39, from which it is sent to mass storage tank 41.

Carbon chain length distribution The resultant liquid fuel is not a 'pure' compound but a mixture of straight-chain and branched alkanes, cyclic saturated hydrocarbons and aromatics consistent with a premium diesel fuel composition. The finished cleaned fuels are piped to a storage tank 41, for later distribution, by various means consistent with diesel fuel handling requirements. With particular reference to Figs 4 and 5, thermolysis diesel made by the batch process as described above and regular (conventional) diesel fuel have been analyzed by gas chromatography (GC). The resiultant cbromatograms give a 'finge rint^* of the diesel with respect to the proportion of hydrocarbon chains of various carbon chain lengths. To perfor as diesel fbel, tihe inventors have found that the fuel must be substantially rich in chains with a carbon chain length peaking around C16 (i.e. cetane). With reference to Figs 4 and 5, the carbon chain length distribution curve for regular diesel and thermolysis diesel produced in accordance with the present invention respectively are shown. It is important to note that a higher proportion of light fraction (especially C8, C9, Cl 1 and C13) is demonstrably present in the thermolysis produced fuel shown in Fig. 5 compared to regular diesel shown in Fig. 4.

Flash point modification To meet the relevant standards for transportation diesel fuel (e.g. AS3570-1998), it is necessary to increase the flash point of the thermolysis diesel to above 45 °C - 53°C, preferably up to at least 61.5°C or a relevant minimum specification of standard. This can be achieved by removing a proportion of the light fraction in the fuel (approx. 5-7% by weight). It is accordingly necessary to strip the lights fraction from the thermolysis diesel. This is achievable by removing the tight fraction with boiling points less than 160 Deg.C, which accounts for about 5-7% of the thermolysis fuel (see table below). The light fractions condensed in the top 8°C condensing coil of the second condenser 30a are treated separately from the heavier fractions- The light liquids stream is piped to a lights tank 37 where it is stored- The lights are separated from the heavⁱer fractions to ensure that the heavier fractions (diesel fuel) remain at specified flash points, not less than 61.5 °C. Table 1. discloses the full distillation range data [in accordance with American Society for Testing and Materials standard ASTM D86] for diesel made according to batch process described above (and regular diesel fuel in parenthesis): Initial boiling point 141.5 deg.C (190 deg.C) 5% recovery 154.5 deg.C (210 eg.C) 10% recovery 172.5 deg.C (240 deg.C) 20% recovery 209.5 deg.C (250 deg.C) 30% recovery 245.5 deg.C (265 deg.C) 40% recovery 270.5 deg.C (270 deg.C) 50% recovery 282.5 deg.C (285 deg.C) 60% recovery 290.5 deg.C (295 deg.C) 70% recovery 297.5 deg.C (310 deg.C) 80% recovery 307.5 deg.C (330 deg.C) 90% recovery 321.5 deg.C (345 deg.C) 95% recovery 332.5 deg.C (360 deg.C) Final boiling point 348.5 deg.C (380 deg.C)

Recovery 98% (98.5%) Loss ^" 1% (0.5%) Barometric reading 102.5. kPa

In order to shift the boiling point range to a higher temperature and concomitantly increase the flash point of the fuel, any one or more of a number of inline strategies can be employed as part ofthe thermolysis process of the invention: (i) Operate the condenser coils (not shown) at a higher operating temperature thus preventing condensation of the lighter fractions and allowing these them to carry on in the gas stream to the acid scrubber 34 and subsequently to the off gas burner 40. (ii) Heating the fuel in the primary oil recovery tank 33 by running heating fluid through the heat exchanger coils. In this way the light fraction can be taken off while the process is running. The heating coils use hot water to prevent waxing in the bottom ofthe tanks but hot thermal fluid (heat transfer oil) may be used to keep the tanks around 80-100 deg. C. Under these conditions the light vapours gently flash off Because the ventmg of flammable hydrocarbons to the atmosphere is not permitted in many countries, it is preferable and mandatory in some countries to send these light gases to the off gas burner 40 or to otherwise capture them for disposal , recycling or use as light fuel . (iii) Although it is not permitted to process flammable liquids in centrifuges for health and safety reasons in many countries, it is technically possible to do so provided suitabl e health and safety practices are folio wed. Each o the above techniques for removing the unwanted light fraction can be used individually or in any combination thereof.

Thermolysis process mass balance As an example of the use of the present invention, the following details are provided by way of example only and the invention is not to be construed as being limited by the following: MASS BALANCE FOR THERMOLYSIS PLANT - PER 1000kg of processed clean feed stock made by the batch process according to one aspect ofthe invention 1. MATERIAL INPUT 10,000kg of post industrial waste, composed of 55% polyethylene (PE) 28% polypropylene (PP) and 17% polystyrene (PS) * • Natural gas for furnace burner = 5 Gj or 2100 m³ • Nitrogen gas = 1,7 m³ x 4 = 6.8 m* 2. OUTPUTS • 10-15% Non condensable gases J by weight kg %% • 3-5% (Wt) char residue • Waste fraction from centrifuge = 10 kg (carbon, tar and water) • Remaining, approximately 8,250 kg liquid fuel / 0.81 SG produces yield of 10,185 litres • Removal of 6% of light fractions in process produces on "spec" diesel fuel of nett.9,574 litres. • Ammoniated water from centrifuge = 88 L x 0.9 (density) = 79.5 kg • Scrubber waste stream = < 3.3 kg (neutralized by NaOH) Notes: * The above mass balance is for clean PE/PP PS feedstock. If the feedstock is post-consumer PE containing contaminates, the solid residue portion ofthe feedstock would be expected to be at least 5% by weight of feedstock. Also the waste portion from centrifuge would also be expected to increase as the contaminates are expected to contain water which would be processed within the chamber. $ Off-gas composition is mainly saturated short-chain hydrocarbons including methane, ethylcne, ethane, propylene, propane, n-butane and iso -butane^, t Flue gas composition from off-gas incinerator is: Nox 198 ppm SOx < 5 ppm Temp. 438 deg.C H20 content- 13% dust density 0.06 g rα3

SEMI-CONTINUOUS THERMOLYSIS PROCESS A second embodiment of the invention will now be described with reference to

Fig. 6. The thermolysis chamber and down stream train are purged by an inert gas, like nitrogen, through pipe line 109, Nitrogen ca*ι be supplied from a nitrogen generator or from gas bottles. The nitrogen is managed by a monitoring device in the main control cabinet PLC and computer system and discrete controllers. Plastic flake (<15mm²) is delivered by any means into the xluidized silo 101. The plastic flake is then taken by a conveyor or auger 102 or blown, to the crammer 103. The plastic is then compressed by the crammer and delivered into a pre-heated extruder barrel 104 (heated steel barrel with screw). The barrel 104 is j cketed 132 and heated via heating medium which is transfeixed from the heating medium vessel 130. The heating medium vessel 130 contains a medium, like oil, that is delivered to the heating jacket 132 ofthe barrel via the heating medium piping 131. The heating medium vessel 130 is heated from the hot flue gases being exhausted from the furnace 110 via exhaust flue 115. The plastic is melted inside the barrel between 120-280°C. The melted plastic is forced along by the rotation ofthe screw inside the barrel directing the melted plastic through the hot melt line 105. The line is pre-heated by electric or other means in case of cold starting through a two way valve 106 (this valve will not exist in a single chamber system) which directs the hot melted plastic into the pyrolysis chambers or single chamber 107. The pyrolysis chamber is situated within the pyrolysis chamber furnace 110. The pyrolysis chamber, usually manufactured from stainless steel, is pre-heated to 2OO-270°C by the burner 111. When the melted plastic begins to flow into the chamber, the agitator 108 is activated. The agitator 108 rotates inside the pyrolysis chamber 107, the blades ofthe agitator 108 having a close tolerance clearance between the walls 107a ofthe chamber 107 and the edge ofthe blades 108a. The blades 108a substantially span the inside diameter ofthe chamber and extend up the walls 107a ofthe chamber 107 slightly protruding beyond the liquid level ofthe melted in the chamber 107. The operation ofthe agitator 108 assists to evenly distribute the heat throughout the molten plastic. When an initial charge of approximately 1000kg-2000kg or approximately 50% capacity of melted plastic is received in the chamber 107, the furnace 110 temperature is caused to rise to 500-650°C, thereby transferring additional heat inside the pyrolysis chamber 107, raising it to between 370-425°C At this temperature, the plastic becomes gaseous. The reaction of the plastic at this temperature causes the plastic carbon chain lengths to randomly break into various lengths. A subsequent reaction occurs in the catalytic converter 118, the short carbon chain lengths reform and further breaking of longer chains lengths occur, such that the distribution is in the range of C8 to C25 and peaking at C 16 (cetane). The pressure inside the chamber 107 rises marginally above atrnospheri c to 1.08 bar. The pyrolysis gas is subsequently forced to exit the chamber 107 through the path of least resistance being the pyrolysis gas pipe 128 into the catalyst tower 118. The catalyst is not consumed or poisoned. The catalyst tower 118 contains a series of plates 118a selected from the group including ceramics, zeolites, the silicates of iron Fe³⁺, cobalt Co²⁺, nickel Ni²⁺, Raney nickel, manganese n\2+, chromium Cr ⁺, copper Cu^2"'^" _> Rhenium Nickel, and/or their, mixtures or the catalyst MCM-41. MCM- 1 (Mobile Crystalline Material) is a silicate obtained by a templatϊng mechanism^1,2'³. It is ordered to some degree, so that there are arrays of non intersecting hexagonal channels, identifiable by TEM, XRD, and vapor adsorption. By changing the length ofthe template molecule, the width of he channels can be controlled to be within 2 to 10 ran. The walls ofthe^' channels are amorphous SiO₂. This feature, together with its exceptional porosity (up to 80%), makes MCM-41 is the least mechanically stable compared to, e.g._τ other porous silicas, silica gels or zeolites⁴. Attempts to synthesize crystalline MCM- 1 are underway. The catalyst tower 118 is housed in a jacket ! 17, (usually manufactured from stainless steel), through which exhaust gases from the furnace 11 are diverted through a pipe 116 to heat the catalyst plates 118a to 220°C or greater. The metal plates 118a are positioned so that the hot pyrolytic gases must take a torturous path to maximise.contact area and time with the metal plates 118a. The hot pyrolysis gases react with the catalytic plates 118a. The metal catalyst of the plates 118a cracks carbon parafinic chains longer than C25 and reforms chains shorter than C6. There is conversion of alpha-olefin chains (1-alkenes) to saturated alkanes. The catalyst ofthe plates 118a ensures that the final fuel has a carbon chain distribution in the range C8-C25 and peaking at Cl 6 (cetane). The reformed pyrolysis gases proceed from the catalytic converter 118 to the distillation tower 119, where the gases are condensed in their various fractions. The distillation tower 119 operates in its known form. The various fractions of liquid exit the distillation tower 11 via process lines 120 and enter oil reco ery tanks 121, The fuel oil liquid is further pumped to one or more operating intermediate tanks 1 9. The intermediate tanks 129 can store one day's production. A centrifuge 125, specified for diesel oil operation, is located downstream ofthe intermediate tanks 129, The centrifuge 125 processes the oil and removes any or virtually all solids and water contained in the oil. However, as will be described below, desulphurisation, a desirable process to remove sulphur contamination f the fuel, requires a chemical process rather than the aforedescribed physical treatment. The centrifuge 125 delivers this oil to a Quality Assurance tank 126 where any additives can be added as necessary, and samples taken for testing. The fuel oil can be sent to mass storage or distributed as necessary. Other products exiting the distillation tower(s) or condenser(s), are non condensable gases and lights, commonly referred to as white spirits, being the lightest fraction ofthe carbon chains, typical having chain lengths of less than C6. This product is delivered to the lights tank 124 via process piping 120 where it is stored for distribution. The non condensable gases continue in the process train and are directed to the gas scrubber 122 where the gases are scrubbed with water. The gas scrubber 122 water is periodically, as necessary, automatically dosed with a caustic agent to neutralise the acids which are added during the scrubbing process. Gases that are not condensed during the scrubbing process are recycled into the furnace 110 to be used for heating. Char resi ue remains suspended in the molten plastic during the pyrolysis process. The semi-continuous system is designed to hold approximately 400-600kg of char per chamber. When this limit is reached, it is indicated by a level indicator 114 which signals to the hot melt feeder to stop feeding melted plastic into the chamber 107. The pyrolysis process continues to operate until all of he existing plastic is pyrolised and the chamber 107 is empty of plastic. The control system turns on the auger system 112 which is built into the pyrolysis chamber 107. The auger 112 extracts the char from the chamber 107 and empties it into a char vessel 113 for removal afterwards. The agitator 108 continues to operate to ensure that all of the char is evacuated from the chamber 1 7. When this is complete, the serai-continuous process commences again from the beginning. It is noted that the operation ofthe condenser 11 is substantially the same as for the condenser 30 included in the batch system as described with reference to Figs 1 to 3.

Thermalysis mass balance The values of yield are dependent on plastic types as different plastics have inherent molecular structures that effect yield rates. For example, 1000 kg of mixed plastic(printed film, waste packaging, etc). Yields the following output: • 50kg of char • 125 of off gas - • 825kg of liquid fuel / specific gravity 0.82 = 1006 litres of liquid fuel, o 60 litres of lights o 946 litres of diesel oil fuel Energy • 250 kW/hr of power • 30Gj of natural gas for heating.

DIESEL DESULPHURISATION PROCESS

Summary Referring to Fig.7, a desulphurisation process removes inorganic sulphur by water wash and cyclone separation, and organic sulphur by oxidation and adsorption.

Detail Diesel from the Storage Tank (200) is mixed with water, and pumped into a

Hydrocyclone Separator (201). The pump is a high-shear type in order to provide a high degree of mixing of water and diesel. Inorganic compounds in the diesel are present in micro-droplets of water, and thus pass into the bulk water phase. The Hydrocyclone removes substantially all ofthe water, and hence the inorganic sulphur. Removal of organic sulphur compounds is achieved by oxidising them to polar compounds, which are then susceptible to adsorption onto zeolite beads. Two optional gaseous oxidising agents are proposed - ozone and oxygen. In the ozone option, the gas is supplied by a conventional Ozone Generator and mixed into the diesel stream. In the oxygen option, oxygen is mixed into the diesel stream, after which free oxygen radicals are generated in the stream by means of ultrasonic sound waves, La both options, sufficient length of pipe is provided downstream (202) to allow the oxidisation reactions to proceed to completion. The stream then passes through a ilica gel Guard Bed (203) which serves to prolong the life ofthe more expensive zeolite beds. Two zeolite absorption vessels are provided (204 A/B), each consisting of a bed of zeolite beads. Diesel passes through one vessel whilst the other vessel is being regenerated using ethanol. Polar organic sulphur compounds are adsorbed onto the zeolite beads, and hence removed from the diesel stream, which goes to storage. Lean ethanol from tank 207 is pumped through the regenerating bed, desorbing the polar sulphur compounds from the bed before collection in the Rich Ethanol Tank (205). Sulphur-rich compounds are removed from the ethanol stream by distillation in an Ethanol Still (206). A sulphur-rich hydrocarbon stream is produced from the bottom ofthe stream, and may be re-used in the process as fuel.

Equipment legend for Fig.7: 200. Diesel storage tank 201. Hydrocyclone separator 202. Ultrasonic chamber 203. Reaction pipe 204. Silica gel guard bed 205. A/B Zeolite absorption vessel 206. Rich ethanol tank 207. Ethanol Still 208. Lean ethanol tank As the present invention may be embodied in several forms without departing from the spirit ofthe essential characteristics ofthe invention, it should be understood that the above described embodiments are not to limit the present invention unless otherwise specified, but rather should be construed broadly wimin the spirit and scope of the invention as defined in the appended claims. Various modifications and equivalent arrangements are intended to be included wilhin the spirit and scope of the invention and appended claims. Therefore, the specific embodiments are to be understood to be illustrative of the many ways in which the principles of the present invention may be practiced. In the following claims, means-plus-function clauses are intended to cover structures as performing the defined function and not only structural equivalents, but also equivalent structures. For example, although a nail and a screw may not be structural equivalents in that a nail employs a cylindrical surface to secure wooden parts together, whereas a screw employs a helical surface to secure wooden parts together, in the environment of fastening wooden parts, a nail and a screw are equiYaleπtt structures. "Comprises/comprising" when used in this specification is taken to specify the presence of stated features, integers, steps or components but does not preclude the presence or addition of one or more other features, integers, steps, components or groups thereof." Item lisr for 10TPD batch plant described with reference to Figs. 1 to 3. 11 Plastic stock pile 12 Conveyor 13 Granulator 14 Metals container 15 Magnet 16 Blower 17 Fluidised Silo 18 Dust collector 19 Blower 20 Force feeder 21 Hot melt feed 22 Hot melt manifold 23 Nitrogen monitoring device 24 Nitrogen storage vessel 25 Nitrogen generator 26 a,b,c,d, Pyrolysis chamber 27 Burner 28 Furnace 29 Catalytic converter, (catalytic reactor) 30 a, Condenser 31 Chiller unit (water tower) 32 Intermediate tank (operating tanks) 33 Oil recovery tank 34 Gas scrubber 35 Caustic make up tank 36 Caustic water tank 37 Lights tank 38 Centrifuge 39 Quality assurance (QA) tank 40 Off gas burner 41 Storage tank 42 Agitator

Item list for Fig. 6- 101 Fluidised hopper 102 Flake delivery system 103 Crammer 104 Hot melt extruder

105 Hot melt line

106 Two way valve

107 Pyrolysis chamber ^'

107a Chamber wall

108 Agitator

108a Agitator blades

109 nitrogen line

110 Furnace

111 Gas burner

112 Char removal auger

113 vessel for containing char

114 Height, detector

115 Furnace exhaust flue

116 Exhaust flue? to catalytic tower

117 Heating jaclcet

118 Catalytic tower

118a Catalyst plates

119 Distillation column

120 Process piping

121 Oil recovery tanks

122 Gas scrubber

123 Non condensable gas line to furnace

124 Lights tank

125 Centrifuge

126 QA tank

127 Mass storage

128 Pyrolysis gas pipe

129 Intermediate tank

130 Heating medium vessel

131 Heating medium piping

132 Heating jacket

Claims

Claims 1. A process for the thermocatalytic conversion of waste organic materials into reusable fuels, comprising the steps of: a) delivering waste material to a melting means to form a molten materi al; b) heating said molten waste material in a pyrolysis chamber to effect pyrolysis of said material into a gaseous state in a substantially oxygen purged and pressure controlled environment; c) transferring resulting gases to a catalytic converter . means wherein the molecular structure ofthe gaseous material is altered; d) transferring gases to one or more condenser means to distil and cool gases into fractions to form at least one useable fuel.

2. A process according to claim 1, wherein said pyrolysis chamber does not include said melting means and step a) is carried out in a separate melting apparatus to the pyrolysis chamber of step b).

3. A process as claimed in claim 1 or 2, including the step of receiving said melted- waste material in the or each pyrolysis chamber by the selective operation of a manifold system having a corresponding one or more inlet pathways to the or each pyrolysis chamber.

4. A process according to claim 1 or 2, wherein said pyrolysis chamber is one of a plurality of pyrolysis chambers and said process includes the alternate use of each said pyrolysis chamber at least one at a time so that one of said pyrolysis chambers is cooled while another of said pyrolysis chambers transfers gaseous material to said catalytic converter means.

5. A process according to claim 4, including the step of operating each said pyrolysis chamber independently to allow cyclic transferral of gaseous material from one or more of said pyrolysis chambers to the catalytic converter means.

6. A process according to any one ofthe preceding claims, including the step of actively cooling the or each pyrolysis chamber after completing transferral of gaseous waste material therefrom to said catalytic converter means.

7. A process according to any one ofthe preceding claims, including the step of mechanically removing char from the or each pyrolysis chamber during the pyrolysis process.

8, A process according to claim 7, wherein the step of mechanically removing char from the or each pyrolysis chamber during the pyrolysis process is carried out by use of an auger.

9. A process according to any one ofthe preceding claims, including the step of mechanically dislodging char from the internal wall o the or each pyrolysis chamber during the pyrolysis process by use of an agitator.

10. A process according to claim 9. wherein the or each said agitator" has one or more blades adapted to continuously remove char from the or each pyrolysis chamber wall surface during the pyx-olysis process.

11. A process for the conversion of plastic materials into diesel fuels including the steps of: b) delivering the plastic material to a melting means; c) transferring the melted plastic material to one or more pyrolysis chambers; d) heating waste material to effect pyrolysis of said material into a gaseous state in a substantially oxygen purged and pressure controlled environment; e) transferring the gaseous material to a catalytic converter means wherein the molecular structure ofthe gaseous material is altered; and f) transferring gases to condenser means to cool and separate the gaseous material into fractions to form at least one type of useable fuel.

12. A process aLccording to any one of the preceding claims, further Including the preUminary step of comminuting or granulating the plastic material into psirticulate matter,

13. A plant for the conversion of plastic materials into diesel fuels, said plant including: a) COrnminuting means for breaking said plastic material into particuiate nxatter; b) melting means for receiving and melting said particuiate plastic material ; c) pyrolysis chamher for receiving molten plastic material from said melting means, said pyrolysis chamber operative to: i) seal the chamber from the environment and to purge air-borne oxidants from said pyrolysis chamber by the introduction of a non-oxidising gas; arid ii) heat said molten plastic material to effect pyrolysis of said plastic material into a gaseous state in a substantially air-borne oxidant-free and pressure- controlled environjoαent; d) catalytic converter means operative to receive and crack said gaseovxs plastic material whereby the molecular structure of said gaseous material is altered; and e) condenser means operative to receive, cool and separate said cracked gaseous material into fractions to form at least one type of useable fuel.

14. A plant according to claim 13, wherein said plastic tna.teri.al is waste material and said pyrolysis chamber includes an auger to remove accumulating char from the base of said pyrolysis chamber and allow continuous feed of molten plastic material into said pyrolysis chamber and continuous production and delivery to said catalytic converter means of said gaseous plastic material.

15. A plant according to claim 13 or 14, wherein said condenser means includes a selective low-temperature condenser operative to remove fight fractions from said cracked gaseous material.

16. A plant according to any one of claims 13 to 15, wherein said melting means is a hot-melt in-feed system.

17. A plant according to any one of claims 13 to 16, wherein said catalytic converter comprises a series of high-surface area internal metal plate catalysts.

18. A plant according to claim 17, wherein said plate catalyst is selected from the group including ceramics, zeolites, the silicates of iron Fe3+, cobalt Co2+, nickel Ni2+, Raney nickel, manganese Mh\2+, chromium Cr3+, copper Cu2+ and/or their mixtures or the catalyst MCM-41. 1 . A substantially carbon based fuel product produced by the process or plant of any one ofthe preceding claims that is suitable for use as a diesel fuel. 20. A fuel according to claim 19 wherein said fuel is substantially equivalent to the diesel fuel standard specified as Australian Standard AS 3570-1998.