WO2006095943A1

WO2006095943A1 - Red phosphorescene compounds and organic electroluminescence devices using the same

Info

Publication number: WO2006095943A1
Application number: PCT/KR2005/001414
Authority: WO
Inventors: Jung Keun Kim; Chun Gun Park; Jeong Dae Seo; Hyun Cheol Jeong; Kyung Hoon Lee; Jae Man Lee
Original assignee: LG Electronics Inc
Current assignee: LG Electronics Inc
Priority date: 2005-03-08
Filing date: 2005-05-13
Publication date: 2006-09-14
Anticipated expiration: 2007-09-08
Also published as: KR100803125B1; JP2008532997A; JP4913122B2; KR20060098860A; US7378162B2; US20060202194A1; CN101160370A; EP1856227A1; CN101160370B; US7470928B2; EP1856227B1; US20070004918A1

Abstract

Red phosphorescene compounds and organic electro-luminescence device using the same are disclosed. In an organic electroluminescence device including an anode, a hole injecting layer, a hole transport layer, a light emitting layer, an electron transport layer, an electron injecting layer, and a cathode serially deposited on one another, the organic electroluminescence device may use a compound as a dopant of the light emitting layer. Formula 1 wherein N represents.

Description

[DESCRIPTION]

RED PHOSPHORESCENE COMPOUNDS AND ORGANIC ELECTROLUMINESCENCE DEVICES USING THE SAME

Technical Field

The present invention relates to an organic electroluminescence device, and

more particularly, to red phosphorescene compounds and organic electroluminescence device using the same. Most particularly, the present invention relates to red

phosphorescence being used as a dopant of a light emitting layer of an organic electroluminescence device, which is formed by serially depositing an anode, a hole injecting layer, a hole transport layer, a light emitting layer, an electron transport layer, an electron injecting layer, and a cathode. Background Art

Recently, as the size of display devices is becoming larger, the request for flat

display devices that occupy lesser space is becoming more in demand. Such flat

display devices include organic electroluminescence devices, which are also referred to as an organic light emitting diode (OLED). Technology of such organic electroluminescence devices is being developed at a vast rate and various prototypes have already been disclosed.

The organic electroluminescence device emits light when electric charge is

injected into an organic layer, which is formed between an electron injecting electrode (cathode) and a hole injecting electrode (anode). More specifically, light is emitted when

an electron and a hole form a pair and the newly created electron-hole pair decays. The organic electroluminescence device can be formed on a flexible transparent substrate

such as plastic. The organic electro-luminescence device can also be driven under a voltage lower than the voltage required in a plasma display panel or an inorganic electroluminescence (EL) display (i.e., a voltage lower than or equal to 10V). The

organic electroluminescence device is advantageous in that it consumes less energy as

compared to other display devices and that it provides excellent color representation. Moreover, since the organic EL device can reproduce pictures by using three colors (i.e., green, blue, and red), the organic EL device is widely acknowledged as a next generation

color display device that can reproduce vivid images.

The process of fabricating such organic electroluminescence (EL) device will be

described as follows: (1) An anode material is coated over a transparent substrate. Generally, indium tin

oxide (ITO) is used as the anode material.

(2) A hole injecting layer (HIL) is deposited on the anode material. The hole

injecting layer is formed of a copper phthalocyanine (CuPc) layer having a thickness of

10 nanometers (nm) to 30 nanometers (run). (3) A hole transport layer (HTL) is then deposited. The hole transport layer is mostly formed of 4,4'-bis[N-(l-naphtyl)-N-phenylamino]-biρhenyl (NPB), which is

treated with vacuum evaporation and then coated to have a thickness of 30 nanometers

(nm) to 60 nanometers (nm).

(4) Thereafter, an organic light emitting layer is formed. At this point, a dopant may be added if required. In case of green emission, the organic light emitting layer is

generally formed of tris(8-hydroxy-quinolate)aluminum (AIq₃) which is vacuum

evaporated to have a thickness of 30 nanometers (nm) to 60 nanometers (nm). And,

MQD(N-Methylquinacridone) is used as the dopant (or impurity).

(5) Either an electron transport layer (ETL) and an electron injecting layer (EIL) are sequentially formed on the organic emitting layer, or an electron injecting/transport layer is formed on the organic light emitting layer. Ih case of green emission, the AIq₃ of step (4) has excellent electron transport ability. Therefore, the electron injecting and

transport layers are not necessarily required.

(6) Finally, a layer cathode is coated, and a protective layer is coated over the

entire structure.

A light emitting device emitting (or representing) the colors of blue, green, and red, respectively, is decided in accordance with the method of forming the light emitting

layer in the above-described structure. As the light emitting material, an exciton is

formed by a recombination of an electron and a hole, which are injected from each of the electrodes. A singlet exciton emits fluorescent light, and a triplet exciton emits

phosphorescene light. The singlet exciton emitting fluorescent light has a 25%

probability of formation, whereas the triplet exciton emitting phosphorescene light has a

75% probability of formation. Therefore, the triplet exciton provides greater light

emitting efficiency as compared to the singlet exciton. Among such phosphorescene materials, red phosphorescence material may have greater light emitting efficiency than fluorescent materials. And so, the red phosphorescene material is being researched and

studied as an important factor for enhancing the efficiency of the organic

electroluminescence device. When using such phosphorescene materials, high light emitting efficiency, high color purity, and extended durability are required. Most particularly, when using red

phosphorescene materials, the visibility decreases as the color purity increases (i.e., the X

value of the CIE chromacity coordinates becomes larger), thereby causing difficulty in

providing high light emitting efficiency. Accordingly, red phosphorescence material that can provide characteristics of excellent chromacity coordinates (CEE color purity of

X=O.65 or more), enhanced light emitting efficiency, and extended durability needs to be

developed.

Disclosure of Invention An object of the present invention devised to solve the problem lies on providing

red phosphorescence compounds and an organic electro-luminescence device using the

same that substantially obviate one or more problems due to limitations and

disadvantages of the related art.

Another object of the present invention devised to solve the problem lies on providing an organic electroluminescence device having high color purity, high

brightness, and long durability by combining the compound shown in Formula 1, which

is used as a dopant in a light emitting layer of the organic EL device.

The object of the present invention can be achieved by providing a red phosphorescence compound that is indicated as Formula 1 below:

Formula 1

wherein

^v ^

represents

Herein each of Rl, R2, R3, and R4 may be one of substituted or non-substituted

Cl to C6 alkyl groups with disregard of one another. And, each of the Cl to c6 alkyl

groups may be selected from a group consisting of methyl, ethyl, n-propyl, i-propyl, n-

butyl, i-butyl, and t-butyl.

Additionally,

may include 2,4-pentanedione ( ),

2,2,6,6,-tetra-methylheptane-3,5-dione (

), 1,3-propanedione

), 1,3-butanedione ( ), 3,5-heptanedione ( ),

l,l,l-trifiuoro-2,4-pentanedione (

), l,l,l,5,5,5-hexafluoro-2,4-

pentanedione ( ), and 2,2~dimethyl-3,5-hexanedione

Moveover, ^■N may be any one of the following chemical formulas:

Furthermore, the Formula 1 may be any one of the following chemical formulas:

B-IO B-I l

In another aspect of the present invention, provided herein is an organic

electroluminescence device including an anode, a hole injecting layer, a hole transport

layer, a light emitting layer, an electron transport layer, an electron injecting layer, and a

cathode serially deposited on one another, wherein the organic electroluminescence device may use any one of the above-described formulas as a dopant of the light emitting layer. Herein, any one of Al and Zn metallic complexes and a carbazole derivative may be used as a host of the light emitting layer, and usage of the dopant may be within the range of 0.1 wt.% to 50 wt.%. The efficiency of the present invention may be provided

when the amount of dopant used is within the above-described range. Furthermore, a ligand of each of the Al and Zn metallic complexes may include quinolyl, biphenyl,

isoquinolyl, phenyl, methylquinolyl, dimethyl-quinolyl, dimethyl-isoquinolyl, and wherein the carbazole derivative may include CBP.

Brief Description of Drawings

The accompanying drawings, which are included to provide a further

understanding of the invention, illustrate embodiments of the invention and together with the description serve to explain the principle of the invention.

In the drawings:

FIG. 1 illustrates a graph showing a decrease in visibility as color purity of an

organic EL device increases (i.e., as the X value of chromacity coordinates becomes

greater).

FIG. 2 illustrates structural formula of NPB, copper (II) phthalocyanine (CuPc),

(bpt)₂Ir(acac), AIq₃, BAIq, and CBP, which are compounds used in embodiments of the

present invention.

Best Mode for Carrying Out the Invention Reference will now be made in detail to the preferred embodiments of the present invention, examples of which are illustrated in the accompanying drawings.

A method of combining the red phosphorescence compound according to the

present invention will now be described. An iridium (lll)(2-(3-methylphenyl)-7-methyl- quinolinato-N, C²)(2,4-pentanedionate-0,0) compound, which is shown as A-2 among the red phosphorescene compounds used in the organic EL device according to the present

invention.

Combination example 1. Combination of 2-(3 -methylphenyl)-7-methyl-quinoline

3-methyl-phenyl-boric acid (1.3 mmol), 2-chloro-7- methyl-quinoline (1 mmol), tetralds (triphenyl phosphine) palladium(O) (0.05 mmol), and potassium carbonate (3 mmol) are dissolved in a two-neck round bottom flask containing THF (30 ml) and H₂O

(10 ml). The mixture is then stirred for 24 hours in a bath of 100 degrees Celsius (^°C).

Subsequently, when reaction no longer occurs, the THF and toluene are discarded. The mixture is extracted by using dichloromethane and water, which is then treated with vacuum distillation. Then, after filtering the mixture with a silica gel column, a solvent is

treated with vacuum distillation. Thereafter, by using dichloromethane and petroleum

ether, the mixture is re-crystallized and filtered, thereby yielding solid 2-(3-

methylphenyl)-7-methyl-quinoline.

2. Formation of chloro-cross-linked dimer complex

Iridium chloride (1 mmol) and 2-(3-methylphenyl)-7-methyl-qumolme (2.5

mmol) are mixed in a 3:1 liquid mixture (30 ml) of 2-ethoxyethanol and distilled water.

Then, the mixture is refluxed for 24 hours. Thereafter, water is added so as to filter the

solid form that is produced. Subsequently, the solid form is washed by using methanol and petroleum ether, thereby yielding the chloro-cross-linked dimer complex.

3. Formation of iridium (Ul)(2-(3-methylphenyl)-7-methyl-quinolinato-N, C²)(2,4- pentanedionate-0,0)

A chloro-cross-linked dimer complex (1 mmol), 2,4-pentane dione (3 mmol),

and Na₂CO₃ (6 mmol) are mixed into 2-ethoxyethanol (30 ml) and refluxed for 24 hours.

The refluxed mixture is then cooled at room temperature. Thereafter, distilled water is added to the cooled mixture, which is filtered so as to yield a solid form. Subsequently, the solid form is dissolved in dichloromethane, which is then filtered by using silica gel. Afterwards, the dichloromethane is treated with vacuum suction, and the solid form is washed by using methanol and petroleum ether, so as to obtain the chemical compound.

Hereinafter, examples of preferred embodiments will be given to describe the

present invention. It will be apparent that the present invention is not limited only to the proposed embodiments.

Embodiments

1. First embodiment

An ITO glass substrate is patterned to have a light emitting area of 3 mm * 3 mm. Then, the patterned ITO glass substrate is washed. Subsequently, the substrate is mounted on a vacuum chamber. The standard pressure is set to IxIO^"6 torn Thereafter,

layers of organic matter are formed on the ITO substrate in the order of CuPC (200 A),

NPB (400 A), CBP + (btp)₂h-(acac)(7%) (200 A), a hole support layer (100 A), AIq₃ (300

A), LiF (5 A), and Al (1000 A).

When forming a hole support layer using BAIq, the brightness is equal to 689 cd/m² (8.1 V) at 0.9 niA. At this point, CIE x = 0.651, y = 0.329. Furthermore, the

durability (half of the initial brightness) lasts for 1600 hours at 2000 cd/m².

2. Second embodiment

An ITO glass substrate is patterned to have a light emitting .area of 3 mm x 3 mm. Then, the patterned ITO glass substrate is washed. Subsequently, the substrate is

mounted on a vacuum chamber. The standard pressure is set to IxIO^"6 torr. Thereafter, layers of organic matter are formed on the ITO substrate in the order of CuPC (200 A),

NPB (400 A), BAIq + A-2(7%) (200 A)₅ AIq₃ (300 A), LiF (5 A), and Al (1000 A).

At 0.9 mA, the brightness is equal to 1448 cd/m² (6.2 V). At this point, CIE x = 0.644, y = 0.353. Furthermore, the durability (half of the initial brightness) lasts for 8000 hours at 2000 cd/m².

3. Third embodiment

An ITO glass substrate is patterned to have a light emitting area of 3 mm x 3 mm. Then, the patterned ITO glass substrate is washed. Subsequently, the substrate is mounted on a vacuum chamber. The standard pressure is set to IxIO^"6 torr. Thereafter,

NPB (400 A), BAIq + A-5(7%) (200 A), AIq₃ (300 A), LiF (5 A), and Al (1000 A).

At 0.9 mA, the brightness is equal to 1378 cd/m² (6.0 V). At this point, CIE x = 0.659, y = 0.351. Furthermore, the durability (half of the initial brightness) lasts for 7000 hours at 2000 cd/m².

Comparison example

An ITO glass substrate is patterned to have a light emitting area of 3 mm x 3 mm. Then, the patterned ITO glass substrate is washed. Subsequently, the substrate is

mounted on a vacuum chamber. The standard pressure is set to IxIO^'6 torr. Thereafter,

NPB (400 A), BAIq + (btp)₂Ir(acac)(7%) (200 A), AIq₃ (300 A), LiF (5 A), and Al (1000 A). At 0.9 mA, the brightness is equal to 780 cd/m² (7.5 V). At this point, CIE x = 0.659, y = 0.329. Furthermore, the durability (half of the initial brightness) lasts for 2500 hours at 2000 cd/m².

In accordance with the above-described embodiments and comparison example, the characteristics of efficiency, chromacity coordinates, brightness, and durability are shown in Table 1 below.

Table 1

As shown in Table 1, the device is operated with high efficiency at a low voltage

even when the color purity is high. Furthermore, the current efficiency of the second

embodiment has increased by 100% or more as compared to the comparison example.

Additionally, the durability of the second embodiment has increased to three times that of the comparison example.

Table 2 below shows the characteristics of efficiency, chromacity coordinates,

and brightness in accordance with the increase in voltage and electric current in the organic electroluminescence device according to the second embodiment of the present

invention.

Table 2

As shown in Table 2, the second embodiment provides excellent efficiency, and

the chromacity coordinates according to the driving voltage also maintains high color purity.

It will be apparent to those skilled in the art that various modifications and

variations can be made in the present invention without departing from the spirit or scope

of the invention. Thus, it is intended that the present invention cover the modifications

and variations of this invention provided they come within the scope of the appended claims and their equivalents. Industrial Applicability

By using the compound shown in Formula 1 as the light emitting layer of the organic electroluminescence device, the present invention provides an organic electro-

luminescence device having excellent color purity and brightness, and an extended durability.

Claims

[CLAIMS]

1. A red phosphorescence compound being indicated as Formula 1 below: Formula 1

wherein ^■N represents

2. The red phosphorescence compound of claim 1, wherein each of Rl, R2, R3, and R4 is one of substituted or non-substituted Cl to C6 alkyl groups with disregard of

one another.

3. The red phosphorescence compound of claim 2, wherein each of the Cl to c6 alkyl groups is selected from a group consisting of methyl, ethyl, n-propyl, i-propyl, n-

butyl, i-butyl, and t-butyl. 4. The red phosphorescence compound of claim 1, wherein

comprises 2,4-pentanedione, 2,2,6,6,-tetra-methylheptane-3,5-dione, 1,3-propanedione,

1,3-butanedione, 3,5-heptanedione, l,l,l-trifluoro-2,4-pentanedione, 1,1,1,5,5,5- hexafluoro-2,

4-pentanedione, and 2,2-dimethyl-3,5-hexanedione.

5. The red phosphorescence compound of claim 1, wherein N is any

one of the following chemical formulas:

6. The red phosphorescence compound of claim 1, wherein the Formula 1 is any one of the following chemical formulas:

7. In an organic electroluminescence device comprising an anode, a hole

injecting layer, a hole transport layer, a light emitting layer, an electron transport layer, an electron injecting layer, and a cathode serially deposited on one another, the organic electroluminescence device using a compound of any one of claim 1 to claim 6 as a dopant of the light emitting layer.

8. The organic electroluminescence device of claim 1, wherein any one of Al and

Zn metallic complexes and carbazole derivatives is used as a host of the light emitting

layer.

9. The organic electroluminescence device of claim 7, wherein any one of Al and

Zn metallic complexes and a carbazole derivative is used as a host of the light emitting

layer, and wherein usage of the dopant within the range of 0.1 wt.% to 50 wt.%.

10. The organic electroluminescence device of claim 8, wherein a ligand of each

of the Al and Zn metallic complexes comprises quinolyl, biphenyl, isoquinolyl, phenyl, methylquinolyl, dimethylquinolyl, dimethyl-isoquinolyl, and wherein the carbazole derivative comprises CBP.