WO2007116793A1 - 離型フィルム、離型性クッション材およびプリント基板の製造方法 - Google Patents

離型フィルム、離型性クッション材およびプリント基板の製造方法 Download PDF

Info

Publication number
WO2007116793A1
WO2007116793A1 PCT/JP2007/056734 JP2007056734W WO2007116793A1 WO 2007116793 A1 WO2007116793 A1 WO 2007116793A1 JP 2007056734 W JP2007056734 W JP 2007056734W WO 2007116793 A1 WO2007116793 A1 WO 2007116793A1
Authority
WO
WIPO (PCT)
Prior art keywords
release film
cushion material
layer
film
printed circuit
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2007/056734
Other languages
English (en)
French (fr)
Inventor
Tamao Okuya
Hiroshi Aruga
Masaru Yamauchi
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
AGC Inc
Original Assignee
Asahi Glass Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Asahi Glass Co Ltd filed Critical Asahi Glass Co Ltd
Priority to EP20070740172 priority Critical patent/EP2002973B1/en
Priority to JP2008509803A priority patent/JPWO2007116793A1/ja
Publication of WO2007116793A1 publication Critical patent/WO2007116793A1/ja
Priority to US12/245,139 priority patent/US7754326B2/en
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

　熱プレスの際に頻繁に取り替える必要がなく、かつ取り替えが容易な離型フィルム；クッション材本体の取り替え頻度を抑えることができる離型性クッション材；及び生産性よく低コストでプリント基板を製造できるプリント基板の製造方法を提供する。 　シリコーンゴムからなるクッション材の表面に設けられる離型フィルム１０であり、フッ素樹脂からなる基材１２の片面にＳｉを含む層１４を有する離型フィルム１０；離型フィルムが、シリコーンゴムからなるクッション材の表面に、Ｓｉを含む層がクッション材側となるように設けられた離型性クッション材；プリント基板本体とカバーレイフィルムとの積重物をプレス板で挟んで熱プレスする際に、離型フィルムが、クッション材のカバーレイフィルム側の表面に、Ｓｉを含む層がクッション材側となるように配置されているプリント基板の製造方法。

Description

明 細 書
離型フィルム、離型性クッション材およびプリント基板の製造方法 技術分野
[0001] 本発明は、シリコーンゴムからなる熱プレス用のクッション材の表面に設けられる離 型フィルム、該離型フィルムが表面に設けられた熱プレス用の離型性クッション材、該 離型フィルムを用いたプリント基板の製造方法に関する。 背景技術
[0002] フレキシブルプリント基板は、たとえば、ポリイミド基材上に銅箔力もなる回路が形成 されたフレキシブルプリント基板本体を、片面に接着剤が塗布されたカバーレイフィ ルムで挟んで積重物とし、該積重物をプレス板で挟んで熱プレスしてフレキシブルプ リント基板本体にカバーレイフイルムを圧着することにより製造される。
[0003] 熱プレスの際には、フレキシブルプリント基板本体の回路および補強基材の凹凸を 吸収し、フレキシブルプリント基板本体とカバーレイフイルムとを隙間なく積層するた めに、積重物とプレス板との間にシリコーンゴム力もなるクッション材を介在させる。 また、カバーレイフイルムの接着剤がクッション材に付着することを防止するために、 クッション材とカバーレイフイルムとの間に離型フィルムが配置される。
[0004] し力し、該離型フィルムは、クッション材に接着しな 、ため、熱プレスのたびに再セッ ティングするまたは取り替える必要がある。そのため、フレキシブルプリント基板の生 産性が不充分で、コストも高くなる。一方、離型フィルムをクッション材に接着剤等で 接着させると、フレキシブルプリント基板本体の凹凸が転写された離型フィルムを取り 替える際、繰り返し行われる熱プレスによって離型フィルムがクッション材に強固に接 着するため、離型フィルムをクッション材力 容易に剥がせな!/、。
[0005] そこで、クッション材の表面に離型性を付与した離型性クッション材が提案されてい る (特許文献 1、 2)。
しかし、該離型性クッション材は、熱プレスを繰り返すことによって、フレキシブルプリ ント基板本体の凹凸が離型性クッション材に転写されるため、離型性クッション材自 体を頻繁に取り替える必要がある。そのため、フレキシブルプリント基板の生産性が 不充分で、コストも高くなる。
特許文献 1 :特開 2000— 052369号公報
特許文献 2 :特開 2002— 144484号公報
発明の開示
発明が解決しょうとする課題
[0006] 本発明の目的は、熱プレスのたびに再セッティングするまたは取り替える必要がなく 、かつ取り替えが容易な離型フィルム;クッション材本体の取り替え頻度を抑えること ができる離型性クッション材;生産性よく低コストでプリント基板を製造できるプリント基 板の製造方法を提供することにある。
課題を解決するための手段
[0007] 本発明の離型フィルムは、シリコーンゴムからなるクッション材の表面に設けられる 離型フィルムであり、フッ素榭脂からなる基材の片面に Siを含む層を有することを特 徴とする。
上記 Siを含む層は、スパッタリング法によって形成された Siと Snとの酸ィ匕物の層、 または真空蒸着法によって形成された SiO 層（ただし、 Xは 1〜2である。）であること が好ましい。
[0008] 本発明の離型性クッション材は、本発明の離型フィルムが、シリコーンゴムカゝらなる クッション材の表面に、 Siを含む層がクッション材側となるように設けられたものである ことを特徴とする。
[0009] 本発明のプリント基板の製造方法は、プリント基板本体とカバーレイフイルムとの積 重物をプレス板で挟んで熱プレスする際に、積重物とプレス板との間にシリコーンゴ ムカもなるクッション材を介在させるプリント基板の製造方法において、少なくとも一方 のクッション材のカバーレイフイルム側の表面に、本発明の離型フィルム力 Siを含む 層がクッション材側となるように配置されて 、ることを特徴とする。
発明の効果
[0010] 本発明の離型フィルムは、熱プレスのたびに再セッティングするまたは取り替える必 要がなぐかつ取り替えが容易である。
O
本発明の離型性クッション材によれば、クッション材本体の取り替え頻度を抑えるこ とが1—
〇でさる。
本発明のプリント基板の製造方法によれば、生産性よく低コストでプリント基板を製 造できる。
図面の簡単な説明
011] [図 1]本発明の離型フィルムの一例を示す概略断面図である。
[図 2]本発明の離型性クッション材の一例を示す概略断面図である。
[図 3]本発明のプリント基板の製造方法の一例を示す概略断面図である。
[図 4]本発明のプリント基板の製造方法の他の例を示す概略断面図である。
[図 5]本発明のプリント基板の製造方法の他の例を示す概略断面図である。
符号の説明
離型フィルム
12 基材
14 Siを含む層
20 離型性クッション材
22 アルミニウム板
24 クッション材
30 フレキシブルプリント基板本体（プリント基板本体)
32 ポリイミド基材
34 回路
40 カノ一レイフイノレム
42 接着剤層
50 プレス機
52 プレス板
56 ガラス繊維強化 PTFEフィルム
発明を実施するための最良の形態
<離型フィルム >
本発明の離型フィルムは、シリコーンゴムからなる熱プレス用のクッション材の表面 に設けられる離型フィルムである。
図 1は、本発明の離型フィルムの一例を示す概略断面図である。離型フィルム 10は 、フッ素榭脂からなる基材 12の片面に Siを含む層 14を有するフィルムである。
[0014] 基材 12は、フッ素榭脂からなるフィルムであり、プリント基板のカバーレイフイルムの 接着剤に対して離型性を発揮するフィルムである。
上記フッ素榭脂とは、榭脂の分子構造式中にフッ素を含む熱可塑性榭脂である。 上記フッ素榭脂としては、たとえば、テトラフルォロエチレン系榭脂、クロロトリフノレオ口 エチレン系榭脂、フッ化ビ -リデン系榭脂、フッ化ビュル系榭脂、これら榭脂の複合 物等が挙げられ、離型性の点から、テトラフルォロエチレン系榭脂が好ましい。
[0015] テトラフルォロエチレン系榭脂としては、たとえば、ポリテトラフルォロエチレン（PTF E)、テトラフルォロエチレン パーフルォロ（アルキルビュルエーテル）共重合体（P FA)、テトラフルォロエチレン一へキサフルォロプロピレン パーフルォロ（アルキル ビュルエーテル）共重合体（EPE)、テトラフルォロエチレン一へキサフルォロプロピ レン共重合体 (FEP)、テトラフルォロエチレン エチレン共重合体 (ETFE)等が挙 げられ、成形性の点から、 PFA、 ETFE, FEP、 EPEが好ましぐ機械的強度に優れ る点で、 ETFEが好ましい。
に応じ、少量のコモノマーを共重合させたものであってもよ 、。
コモノマー成分としては、以下の化合物が挙げられる。
CF =CFC1、 CF =CH等の含フッ素エチレン類、
2 2 2
CF =CFCF 、 CF =CHCF等の含フッ素プロピレン類、
2 3 2 3
CH =CHC F 、 CH =CHC F 、 CH =CFC F 、 CH =CF (CF ) H等のフル
2 2 5 2 4 9 2 4 9 2 2 3 ォロアルキル基の炭素数が 2〜10の含フッ素アルキルエチレン類、
CF =CFO (CF CFXO) Rf (ただし、 Rfは炭素数 1〜6のパーフルォロアルキル基
2 2 m
、 Xはフッ素原子またはトリフルォロメチル基、 mは 1〜5の整数を示す。
)等のパーフルォロ（アルキルビュルエーテル）類、
CF =CFOCF CF CF COOCH 、 CF =CFOCF CF (CF ) OCF CF SO F等
2 2 2 2 3 2 2 3 2 2 2 の、容易にカルボン酸基またはスルホン酸基に変換可能な基を有するビニルエーテ ル類。
[0017] ETFEにおけるエチレンに基づく繰り返し単位 Zテトラフルォロエチレンに基づく繰 り返し単位のモノ kttiま、 40/60〜70/30力 S好ましく、 40/60〜60/40力 S特に好 ましい。また、 ETFEがコモノマーに基づく繰り返し単位を含有する場合には、その含 有量は、全モノマーに基づく繰り返し単位（100モル0 /0)に対して、 0. 3〜10モル％ が好ましぐ 0. 3〜5モル％が特に好ましい。
[0018] クロ口トリフルォロエチレン系榭脂としては、たとえば、ポリクロ口トリフルォロエチレン
(PCTFE)、エチレン クロ口トリフルォロエチレン共重合体（ECTFE)等が挙げられ る。
[0019] 基材 12には、離型性を損なわない範囲で、必要に応じ、フッ素榭脂を除く熱可塑 性榭脂、公知の添加剤等が含まれていてもよい。
基材 12の厚さは、 5〜300 111カ 子ましく、 25〜： LOO /z m力特に好ましい。
[0020] Siを含む層 14は、シリコーンゴム力もなるクッション材に対して高い親和性を有する 層である。 Siを含む層 14としては、たとえば、 Siを含む金属の酸化物の層が挙げられ る。
酸化物としては、 SiO (ただし、 Xは 1〜2である。 )、 Siと Snとの酸ィ匕物、 Siと Zrとの 酸化物、 Siと Tiとの酸化物、 Siと Taとの酸化物、 Siと Nbとの酸化物、 Siと Znとの酸ィ匕 物、 Siと Snと Tiとの酸ィ匕物等が挙げられる。
[0021] 酸化物の層としては、クッション材との接着性の点で、 SiO (ただし、 Xは 1〜2である 。）を主成分とする層（以下、 SiO層と記す。）又は Siと Snとの酸ィ匕物を主成分とする 層（以下、 STO層と記す。）が好ましい。 STO層を形成する Siと Snとの酸化物として は、 SiOと SnOの混合物が好ましい。また、 STO層には、 Zr、 Ti、 Ta、 Nb、 Znなど
2 2
の金属酸化物を含有することも好ま ヽ。
SiO層における Siの含有割合は、クッション材との接着性の点で、含有される全元 素（100原子％)に対して、 33. 3〜50原子％が好ましぐ 33. 3〜40原子％が特に 好ましい。
[0022] STO層における Siの含有割合は、クッション材との接着性の点で、含有される全元 素（100原子％)に対して、 3. 3原子％以上が好ましぐ 10原子％以上が特に好まし ぐ成膜性の点で、 30原子％以下が好ましぐ 23. 3原子％以下が特に好ましい。ま た、 STO層における Siと Snの存在割合は、原子比で Si: Snが 1 : 9〜9 : 1が好ましく 、より好ましくは、 3 : 7〜7 : 3である。
Siを含む層 14の厚さは、クッション材との接着性の点で、 lnm以上が好ましぐ 3n m以上が特に好ましぐ成膜性の点で、 lOOnm以下が好ましぐ 60nm以下が特に 好ましい。
[0023] Siを含む層 14の形成方法としては、乾式法が好ましい。
乾式法としては、真空蒸着法、スパッタリング法、 CVD法、イオンプレーティング法 等が挙げられ、真空蒸着法、スパッタリング法などが好ましぐスパッタリング法が特に 好ましい。スパッタリング法は、生産性に優れ、工業的に幅広く使われているとともに 、該方法により非常に緻密で、かつ基材 12との密着性が高い Siを含む層 14が均一 な膜厚で得られる。スパッタリング法としては、直流スパッタリング法、高周波スパッタ リング法等が挙げられ、大面積の基材に大きな成膜速度で、効率よく成膜できる点で 、直流スパッタリング法が好ましい。
[0024] SiO層の形成方法としては、（i)蒸発材料として SiZSiO 2を用いた真空蒸着法、 (ii
) Siターゲットを用いた、酸素含有雰囲気中での高周波スパッタリング法 (反応性スパ ッタリング法）、（m) sioターゲットを用いた、無酸素雰囲気中での高周波スパッタリン グ法等が挙げられ、成膜性の点で、 ω真空蒸着法が好ましい。
[0025] STO層の形成方法としては、 Siと Snとの混合物ターゲットを用いた、酸素含有雰囲 気中での反応性スパッタリング法が挙げられる。
Siと Snとの混合物ターゲットを用いた場合では、 Siターゲットとは異なり、ターゲット の導電性の向上等の理由力 直流スパッタリング法が可能となり、成膜速度を大きく することができる。
[0026] Siと Snとの混合物ターゲットは、混合物の状態のものであってもよぐ合金の状態で あってもよい。 Siと Snとの混合物ターゲットは、 Siと Snとの混合物を CIP法 (冷間等方 プレス法）、または温間プレス法 (Snの融点直下の温度で金型成形プレスする方法） で成形して得ることができる。
[0027] 以上説明した離型フィルム 10にあっては、フッ素榭脂からなる基材 12の片面に、シ リコーンゴム力もなるクッション材に対して親和性の高い Siを含む層 14を有するため 、最初の熱プレスによって、 Siを含む層 14を介して離型フィルム 10がクッション材に 接着する。その結果、熱プレスのたびに離型フィルム 10を再セッティングするまたは 取り替える必要がなくなる。
[0028] また、離型フィルム 10の Siを含む層 14は、接着剤等によってクッション材に接着さ れるわけではないため、離型フィルム 10をクッション材カも容易に剥離できる。その結 果、フレキシブルプリント基板本体の凹凸が離型フィルム 10に転写され、離型フィル ム 10を取り替える必要が生じた際、離型フィルム 10を容易に取り替えできる。
[0029] <離型性クッション材>
本発明の離型性クッション材は、本発明の離型フィルムが、シリコーンゴムカゝらなる クッション材の表面に、 Siを含む層が好ましくはクッション材側となるように設けられた 熱プレス用のクッション材である。
[0030] 図 2は、本発明の離型性クッション材の一例を示す概略断面図である。離型性タツ シヨン材 20は、アルミニウム板 22が裏打ちされたクッション材 24の表面に、離型フィ ルム 10力 Siを含む層 14がクッション材 24側となるように設けられたものである。
[0031] シリコーンゴムとしては、好ましくはポリジメチルシロキサン、その誘導体等が挙げら れる。
クッション材 24には、クッション材 24の機能を損なわない範囲で、必要に応じて公 知の添加剤等が含まれて 、てもよ 、。
[0032] 離型フィルム 10とクッション材 24との接着は、離型フィルム 10がシリコーンゴムから なるクッション材 24に対して親和性の高い Siを含む層 14を有するため、接着剤等を 用いずに、離型フィルム 10とクッション材 24とを単に貼り合わせるだけでよい。
離型フィルム 10とクッション材 24との接着は、熱プレスの前にあらかじめ行ってもよく 、最初の熱プレス時に行ってもよい。
[0033] 以上説明した離型性クッション材 20にあっては、離型フィルム 10をクッション材 24 力も容易に剥離できるため、フレキシブルプリント基板本体の凹凸が離型フィルム 10 に転写された際には、離型フィルム 10のみを取り替えればよい。結果、クッション材 2 4の取り替え頻度を抑えることができる。 [0034] <プリント基板の製造方法 >
本発明のプリント基板の製造方法は、プリント基板本体とカバーレイフイルムとの積 重物をプレス板で挟んで熱プレスする際に、積重物とプレス板との間にシリコーンゴ ムカもなるクッション材を介在させるプリント基板の製造方法において、少なくとも一方 のクッション材のカバーレイフイルム側の表面に、本発明の離型フィルム力 Siを含む 層がクッション材側となるように配置されて 、る方法である。
[0035] プリント基板としては、フレキシブルプリント基板、多層プリント基板、プリント配線板 等が挙げられる。
以下、本発明のプリント基板の製造方法の一例を、図を参照しながら説明する。
[0036] 図 3は、両面に回路が形成されたフレキシブルプリント基板本体の両面を力バーレ ィフィルムで被覆したフレキシブルプリント基板の製造方法の例を示す概略断面図で ある。
まず、ポリイミド基材 32の両面に銅箔力もなる回路 34が形成されたフレキシブルプ リント基板本体 30を、片面に接着剤層 42が形成されたカバーレイフイルム 40で挟ん で積重物とする。
[0037] ついで、離型フィルム 10を、アルミニウム板 22が裏打ちされたクッション材 24、 24 がプレス板 52、 52の間に設けられたプレス機 50の、クッション材 24、 24の間に配置 する。このとき、離型フィルム 10の Siを含む層 14がクッション材 24側となるようにそれ ぞれ配置する。
ついで、積重物がない状態でこのまま熱プレスし、離型フィルム 10とクッション材 24 との接着を行う。
ついで、前記積重物を、クッション材 24、 24に接着された離型フィルム 10、 10の間 に配置し、熱プレスしてフレキシブルプリント基板本体 30にカバーレイフイルム 40を 圧着し、フレキシブルプリント基板を得る。
[0038] 図 4は、両面に回路が形成されたフレキシブルプリント基板本体の両面を力バーレ ィフィルムで被覆したフレキシブルプリント基板の製造方法であり、離型フィルムをフ レキシブルプリント基板の片面のみに用いた例を示す概略断面図である。
まず、ポリイミド基材 32の両面に銅箔力もなる回路 34が形成されたフレキシブルプ リント基板本体 30を、片面に接着剤層 42が形成されたカバーレイフイルム 40で挟ん で積重物とする。
[0039] ついで、該積重物を、アルミニウム板 22が裏打ちされたクッション材 24、 24がプレ ス板 52、 52の間に設けられたプレス機 50の、クッション材 24、 24の間に配置し、熱 プレスしてフレキシブルプリント基板本体 30にカバーレイフイルム 40を圧着し、フレキ シブルプリント基板を得る。
熱プレスの際、上側のクッション材 24と積重物のカバーレイフイルム 40との間に、離 型フィルム 10を、 Siを含む層 14がクッション材 24側となるように配置する。また、下側 のクッション材 24と積重物のカバーレイフイルム 40との間に、ガラス繊維強化 PTFE フィルム 56を配置する。
[0040] 図 5は、片面に回路が形成されたフレキシブルプリント基板本体の片面を力バーレ ィフィルムで被覆したフレキシブルプリント基板の製造方法の例を示す概略断面図で ある。
まず、ポリイミド基材 32の両面に銅箔力もなる回路 34が形成されたフレキシブルプ リント基板本体 30に、接着剤層 42が形成されたカバーレイフイルム 40を、回路 34を 覆うように被せて積重物とする。
[0041] ついで、該積重物を、アルミニウム板 22が裏打ちされたクッション材 24、 24がプレ ス板 52、 52の間に設けられたプレス機 50の、クッション材 24、 24の間に配置し、熱 プレスしてフレキシブルプリント基板本体 30にカバーレイフイルム 40を圧着し、フレキ シブルプリント基板を得る。
熱プレスの際、上側のクッション材 24と積重物のカバーレイフイルム 40との間に、離 型フィルム 10を、 Siを含む層 14がクッション材 24側となるように配置する。また、下側 のクッション材 24と積重物との間に、ガラス繊維強化 PTFEフィルム 56を配置する。
[0042] カバーレイフイルム 40としては、ポリイミドフィルム、ポリエステルフィルム等が挙げら れる。
接着剤層 42としては、エポキシ榭脂が挙げられる。
[0043] 以上説明した本発明のプリント基板の製造方法にあっては、本発明の離型フィルム 10を、シリコーンゴムからなるクッション材 24のカバーレイフイルム 40側の表面に、 Si を含む層 14がクッション材 24側となるように配置して 、るため、最初の熱プレスによつ て、 Siを含む層 14を介して離型フィルム 10がクッション材 24に接着する。結果、熱プ レスのたびに離型フィルム 10を再セッティングするまたは取り替える必要がなくなり、 フレキシブルプリント基板本体 30を生産性よく低コストで製造できる。
[0044] また、離型フィルム 10の Siを含む層 14は、接着剤等によってクッション材 24に接着 されて!/、るわけではな!/、ため、離型フィルム 10をクッション材 24力も容易に剥離でき る。結果、フレキシブルプリント基板本体 30の凹凸が離型フィルム 10に転写され、離 型フィルム 10を取り替える必要が生じた際、離型フィルム 10を容易に取り替えでき、 フレキシブルプリント基板本体 30を生産性よく低コストで製造できる。
実施例
[0045] 以下に、実施例を挙げて本発明を具体的に説明する力 本発明はこれらの例によ つて限定されない。
例 1、 2は実施例であり、例 3は比較例である。
[0046] 〔例 1〕
厚さ 100 μ mの ETFEフィルム（旭硝子社製、商品名フルオン ETFE)の片面を 40 W · minZm2の放電量でコロナ放電処理した。
蒸発材料である Siと SiOとの混合物を電子ビームを用いて加熱することにより、 ET
2
FEフィルムのコロナ放電処理面に、真空蒸着法による 40nmの SiO膜を成膜し、離
2
型フィルム（1)を得た。
[0047] ポリイミド基材の両面に銅箔力もなる回路が形成されたフレキシブルプリント基板本 体を、片面に 15 μ mの感熱エポキシ接着剤が塗布された 12. 5 μ mのポリイミド基材 であるカバーレイフイルムで挟んで積重物とした。
ついで、該積重物の両面に、 Siを含む層がクッション材側となるように離型フィルム (1)を配置した状態で、図 3に示すプレス機 50を用い、プレス温度 180°C、プレス圧 4MPa、プレス時間 3分の条件で熱プレスを行った。
該熱プレスを繰り返し行 、、熱プレスを 160回行つた後および 180回行つた後にお ける、離型フィルム（1)とクッション材との接着性、離型フィルム（1)の凹凸の状態を目 視にて評価した。また、熱プレスを 160回行った後および 180回行った後における、 クッション材カゝらの離型フィルム（1)の剥離性を評価した。結果を表 1に示す。
接着性は、全面で接着することが好ましい。また、剥離性は、手で剥離可能である ことが好ましい。
[0048] 〔例 2〕
厚さ 100 μ mの ETFEフィルム（旭硝子社製、商品名フルオン ETFE)の片面に例 1 と同じ条件にてコロナ放電処理を施した。
ETFEフィルムのコロナ放電処理面に、 DCマグネトロン方式ロールコーターを用い た直流スパッタリング法により 5nmの STO膜を成膜し、離型フィルム（2)を得た。 成膜は、アルゴンガス 75体積0 /0と酸素ガス 25体積0 /0との混合ガス雰囲気下、ターゲ ットとして Si— Sn合金ターゲット（組成： Si50原子％、 Sn50原子％)を用い、 4kw/ mの電力密度の条件で行った。
[0049] 離型フィルム（1)の代わりに離型フィルム（2)を用いた以外は、例 1と同様にして熱 プレスを行い、評価を行った。結果を表 1に示す。
[0050] 〔例 3〕
厚さ 100 μ mの ETFEフィルム（旭硝子社製、商品名フルオン ETFE)の片面に例 1 と同じ条件にてコロナ放電処理を施した。
離型フィルム（1)の代わりに該 ETFEフィルムを用い、コロナ放電処理面がクッショ ン材側となるように積重物の両面に ETFEフィルムを配置した以外は、例 1と同様にし て熱プレスを行った。 ETFEフィルムはクッション材に接着せず、最初の熱プレスの直 後に、 ETFEフィルムはクッション材力 全面剥離した。
[0051] [表 1]
Figure imgf000013_0001
産業上の利用可能性 本発明の離型フィルムは、プリント基板本体にカバーレイフイルムを圧着してプリント 基板を製造する際に用いられる離型フィルムとして有用である。 なお、 2006年 4月 5日に出願された日本特許出願 2006— 104018号の明細書、 特許請求の範囲、図面及び要約書の全内容をここに引用し、本発明の明細書の開 示として、取り入れるものである。

Claims

請求の範囲
[1] シリコーンゴムからなるクッション材の表面に設けられる離型フィルムであり、フッ素 榭脂からなる基材の片面に Siを含む層を有することを特徴とする離型フィルム。
[2] Siを含む層が、スパッタリング法によって形成された Siと Snとの酸ィ匕物の層である、 請求項 1に記載の離型フィルム。
[3] Siを含む層が、真空蒸着法によって形成された SiO層（ただし、 Xは 1〜2である。 ) である、請求項 1に記載の離型フィルム。
[4] Siと Snとの酸ィ匕物の層に含有される全元素（100原子0 /0)に対して、 Siの含有割合 が 3. 3〜30原子％である、請求項 2に記載の離型フィルム。
[5] SiO層に含有される全元素（100原子％)に対して、 Siの含有割合が 33. 3〜50 原子％である、請求項 3に記載の離型フィルム。
[6] Siを含む層の厚さ力 1〜： LOOnmである、請求項 1〜5のいずれかに記載の離型フ イノレム。
[7] フッ素榭脂が、テトラフルォロエチレン系榭脂である、請求項 1〜6のいずれかに記 載の離型フィルム。
[8] フッ素榭脂が、テトラフルォロエチレン—エチレン共重合体である、請求項 1〜6の
V、ずれかに記載の離型フィルム。
[9] 請求項 1〜8のいずれかに記載の離型フィルム力 シリコーンゴムからなるクッション 材の表面に、 Siを含む層がクッション材側となるように設けられた、離型性クッション 材。
[10] プリント基板本体とカバーレイフイルムとの積重物をプレス板で挟んで熱プレスする 際に、積重物と該 2枚のプレス板との間にシリコーンゴム力もなるクッション材を介在さ せるプリント基板の製造方法において、
少なくとも一方のクッション材のカバーレイフイルム側の表面に、請求項 1〜8のいず れかに記載の離型フィルム力 Siを含む層がクッション材側となるように配置されて ヽ ることを特徴とする、プリント基板の製造方法。
PCT/JP2007/056734 2006-04-05 2007-03-28 離型フィルム、離型性クッション材およびプリント基板の製造方法 Ceased WO2007116793A1 (ja)