WO2009102258A1

WO2009102258A1 - Separation of biomolecules

Info

Publication number: WO2009102258A1
Application number: PCT/SE2009/000083
Authority: WO
Inventors: Anders Larsson; Ulrika Meyer; Nils Norrman; Johan ÖHMAN
Original assignee: GE Healthcare Bio Sciences Corp
Current assignee: Global Life Sciences Solutions USA LLC
Priority date: 2008-02-15
Filing date: 2009-02-12
Publication date: 2009-08-20
Anticipated expiration: 2010-08-15
Also published as: US20100294977A1; US8632883B2; EP2240271A1; EP2240271A4

Abstract

The present invention relates to separation of biomolecules. More closely, the invention relates to a method for production of a separation medium comprising hybrid particles of inorganic and organic material as well as the hybrid particles produced by this method. Finally, the invention relates to use of said hybrid particles for separation of biomolecules, preferably phosphoproteins. The method comprises the following steps: addition of inorganic metal oxide particles to an organic solution to form a mixture; and emulsification of said mixture to form porous hybrid particles, wherein the density of said porous hybrid particles is between 1.0 and 1.5 g/ml, and wherein said inorganic particles have a shape and size that maximizes their active surface area enabling said inorganic particles to interact with biomolecules.

Description

Title: Separation of biomolecules

Field of the invention

The present invention relates to separation of biomolecules. More closely, the invention relates to a method for production of a separation medium comprising hybrid particles of inorganic and organic material as well as the hybrid particles produced by this method. Finally, the invention relates to use of said hybrid particles for separation of biomolecules, preferably phosphoproteins.

Background of the invention There are various known interactions between biomolecules and inorganic material, for example electrostatic interactions, used e.g. in ion exchange chromatography, hydrophobic interactions, used e.g. in hydrophobic interaction chromatography and reversed phase chromatography, pi electron interactions. Also, in affinity chromatography, highly specific and geometrically defined combinations of several interactions are used to obtain very high specificities.

Phosphorylation is a reversible post-translational modification in eukaryotes. Phosphorylation occurs either by addition or by removal of a phosphate group in a protein. Kinases are responsible for the addition of phosphate to a protein while phosphatases are responsible for the removal of phosphate from a protein. The function of these post-translational modifications is to alter the substrate's activity, subcellular localization, binding properties or association with other proteins. Many enzymes and receptors acts like an on-off switch when phosphorylated. This means that enzymes and receptors are activated or deactivated by phosphorylation. An important feature of kinases and phosphatases is that a single molecule is able to activate many substrate molecules, thus allowing for amplification of the initial signal. Both kinases and phosphates are interesting because all signal transduction pathways are regulated, on some level, by phosphorylation, making phosphorylation relevant to most, if not a\\, areas of cell signalling and neuroscience research. Furthermore, phosphorylation plays an important role in cancer diseases, inflammatory diseases, metabolic disorders and neurological diseases.

To enrich phosphopeptides for example IMAC (Immobilized metal ion affinity chromatography) or MOAC (metal oxide/hydroxide affinity chromatography) may be used.

Recently, titanium dioxide was reported useful for isolation of phosphopeptides (Martin R. Larsenφ, Tine E. Thingholm, Ole N. Jensen, Peter Roepstorff, and Thomas J. D. Jørgensen. Highly Selective Enrichment of Phosphorylated Peptides from Peptide Mixtures Using Titanium Dioxide Microcolumns. Molecular & Cellular Proteomics 4.7 p.873-886). For enrichment of phosphopeptides zirconium dioxide has also reported useful (Kweon.H.K. and Hάkansson.K. Selective Zirconium Dioxide-Based Enrichment of Phosphorylαted peptides for Mass Spectrometric Analysis Anal Chem 2006, 78, 1743-1749)

Another common post-translational modification of proteins is glycosylation Glycosylation is an enzyme directed site-specific process of attaching saccharides to proteins The donor molecule is a nucleotide sugar The glycosylation is of importance for the protein folding, for the cell-cell adhesion as well as for the immune system For many diseases like cancer the protein glycosylation pattern is affected Therefore the glycosylated proteins are being studied as biomarkers used for diagnosis and follow-up of certain unhealthy conditions The sialiome, sialic acid-containing glycopeptides, was characterized using titanium dioxide as an enrichment step in a report from Martin R Larsen, Søren S Jensen, Leene A Jakobsen, and Niels H H Heegard Exploring the Sialiome Using Titanium Dioxide Chromatography and Mass Spectrometry Molecular & Cellular Proteomics 6 1O p 1778- 1787

EP1477800 describes a method and apparatus for analyzing phosphoproteins using a reversed phase HPLC column having a titanium dioxide pre-treatment column

EP1780537 describes the purification of phosphorylated proteins on an immobilized metal or titania carrier wherein a solution containing acetonitrile is used

EP 1165201 relates to particulate material for fluidised bed purification of bio-macromolecules The particles are essentially construed of a polymeric base matrix, e g a polysaccharide such as agarose, and a non-porous core material, e g steel and titanium The purpose of the core material is to give the particulate material a density above 2 5 g/ml

Summary of the invention

The present invention relates to a novel separation medium comprising porous hybrid particles capable of interacting with specific biomolecules

In a first aspect the invention relates to a method for production of separation media for separation of biomolecules from a sample, comprising the following steps addition of inorganic metal oxide particles to an organic solution to form a mixture, and emulsification of said mixture to form porous hybrid particles, wherein the density of said porous hybrid particles is between 1 0 and 1 5 g/ml, and wherein said inorganic particles have a shape and size that maximizes their active surface area enabling said inorganic particles to efficiently interact with biomolecules In this way the inorganic metal oxide particles are accessible for binding of proteinaceous and peptide material The inorganic particles should have a shape and size that maximizes their active surface area. For example, the inorganic particles may be porous and/or small. Preferably the inorganic particles are small, namely less than 1000 nm, preferably less than 300 nm, in size. These small particles can either be individually dispersed or can be used in the form of aggregates made up from small primary particles.

The inorganic particles may be selected from Group 4, 12, 13 and/or 14 and are preferably titania, zirconia, hafnia, alumina, zinc oxide, germania and/or tin dioxide, preferably titania, zirconia and/or alumina, most preferably titania.

The organic particles solution comprises polysaccharides, for example agarose or dextran. Alternatively, the organic solution comprises synthetic material, for example; polystyrene/dvb and porogens or methacrylates and porogens.

In a preferred embodiment of the method according to the present invention inorganic particles are added to the disperse phase in suspension gelation/polymerisation of porous beads. During emulsification the inorganic particles will be incorporated in the organic porous phase. In a further embodiment the hybrid particles might be synthesised in a fashion that adds superparamagnetic properties to the hybrid particles. For example magnetite may be added together with the inorganic particles in the dispersed solution made for emulsification. The magnetic format is advantageous since it is very easy to handle in the small scale sample preparation mode.

In a second aspect, the invention relates to porous hybrid particles comprising inorganic metal oxide particles selected from Group 4, 12, 13 and/or 14 which are incorporated in organic solution to form porous hybrid particles, wherein the density of the hybrid particles is between 1.0 and 1.5 g/ml, preferably between 1.0 and 1.3 g/ml, and wherein said inorganic particles have a shape/size that maximizes their active surface area and said inorganic particles are capable of interacting with biomolecules. The incorporation is made in such a way that the inorganic particles are active and available for protein and peptide binding. The hybrid particles are preferably in the form of porous beads.

The inorganic particles have a (volume-weighted, sphere volume-equivalent) average diameter of 10 to 1000 nm, preferably 10-300 nm. If aggregated particles are used, the primary particles in the aggregates have an average diameter of 10 to 1000 nm, preferably 10-300 nm. For a description of methods to determine average particle diameters, see e.g. M Rhodes: Introduction to particle technology, Wiley 1998, pp 55-72. For a discussion about determination of primary particle sizes in aggregated particles, see Degussa technical bulletin pigments no 60, Significance and existence of primary particles in highly dispersed materials 2^nd Ed. 1986. This reference (p 7) also describes the inverse proportionality between particle size and specific surface area. Preferably the inorganic particles are selected from titania, zirconia, hafnia, alumina, zinc oxide, germania and/or tin dioxide, preferably titania, zirconia and/or alumina, most preferably titania. Preferably the organic porous material is selected from polysaccharides or synthetic polymers.

In a preferred embodiment the inorganic particles comprise titania and the organic particles comprise agarose, wherein the titania particles are dispersed into the agarose.

Preferably, the size of the hybrid particles is 5-500 μm, preferably 25-100 μm.

In a further embodiment the porous hybrid particles comprise a lid covering the hybrid particles, wherein said lid comprises up to 20% agarose. It is possible to vary the amount of agarose in the porous beads to exclude different sizes of biomolecules from interaction with the active part, i.e. the inorganic material, of the porous beads. For example, large phosphoproteins may be excluded from interaction and elute in the flow through if the separation medium of the invention is used in a chromatographic mode. The medium of the invention is not restricted to chromatography but may also used in other formats, preferably small scale formats, for example high throughput plates, magnetic centrifugation and spin trap columns.

In a third aspect, the invention relates to use of the porous hybrid particles in the purpose of separation, purification or enrichment of biomolecules, such as phosphoproteins or -peptides or glycoproteins or -peptides.

Brief description of the drawing

Fig. 1 A. Inorganic metal oxide particles (illustrated by filled squares) dispersed in organic polymer/monomer solution. B. Emulsification droplets containing the dispersed inorganic particles followed by gelation or polymerisation. C. The resulting porous organic/inorganic hybrid particles

Detailed description of the invention

The invention relates to porous hybrid particles comprising inorganic and organic material. Preferentially the inorganic material is particles having a large active surface area, meaning that they should either be small (below 1000 nm primary particle diameter, preferably below 300 nm) or that they should be porous. It is preferred that they are small and nonporous due to mass transport, availability and ease of manufacture reasons. For example, pigment-grade titanium dioxide particles are readily available in the desired particle size range and can be used, provided that the particles show a pure titanium dioxide surface (many TiO₂ pigments are surface treated with other oxides or with organic material). Porous hybrid particles made from polysaccharide may be used directly without hydrophilisation for the intended application while porous hybrid particles based on for example; polystyrene/dvb or methacrylates need hydrophilisation before use for separation of biomolecules. Hydrophilisation might be done using for example radical grafting using DEGVE, sorbitol coupling or dextran modification.

The amount of inorganic particles should be high enough to give a large available surface but not so high that the density of the hybrid beads is increased above 1.5 g/ml, preferably not above 1.2. causing difficulties in handling and in column packing.

Preferably the organic particles are made of agarose. Agarose has an ability to assemble itself in complex bundles to form gels in aqueous solution when cooling. Agarose dissolved in warm water can be emulsified in for example toluene, thus forming small droplets in the toluene-phase. Upon cooling below the gelling temperature the small droplets of water dissolved agarose forms a spherical, porous gel built from agarose bundles. The size of these particles can be altered using different stirring rates.

In a preferred embodiment of the present invention, small titanium dioxide particles were mixed with the hot agarose water phase. The agarose/titanium slurry was emulsified into toluene.The inorganic particles are physically caught in the bundles or in the porosity of the particle. Epichlorohydrin was used to fixate the agarose structure by means of crosslinking.

EXPERIMENTAL PART

The experiments below are only intended for illustrative purposes and are not to be construed as limiting for the invention.

Experiment 1: Screening of commercial inorganic particles on distribution in agarose gel

A screening experiment was carried out to identify the inorganic particles having the best distribution in agarose gel. The distribution of inorganic particles in agarose gel was evaluated in a thin film format. The commercial inorganic particles listed in Table 1 were included in this experiment.

Table 1 The properties of seven different commercial inorganic particles.

A 4 w% agarose solution was prepared taking into consideration that the agarose raw material contains 8.3 % water and 0.44 % ash. The amount pure agarose was calculated with Formula 1 (assuming the density of water 1.0 g/ml) and the quantity of agarose raw material was calculated using Formula 2.

^X — _^ = 0.04 →X = 1,053

(X + 25 ) Formula 1

X = Weight{g) pure agarose

Y = 1,053 + 0,083Y + 0,0044Y →Y = 1,1538

Formula 2

Y — Weight(g) crude agarose

Agarose, water and inorganic particles were mixed in round bottom flasks. The flasks were placed in an oil bath and during stirring heated to approximately 95⁰C for 4 hours. Thereafter the temperature of the oil bath was decreased to 55°C. 5-10 ml agarose /titanium dioxide mixture was placed on a warm preheated glass plate and then cast using an adjustable film applicator with a unit gap of 1 mm. The resulting agarose films were studied by optical light microscope to evaluate the distribution of inorganic particles and aggregate formation in the agarose gel matrix.

FINNTI X- 141 showed an even distribution in agarose with no aggregates formed. VP TiO2 PV90, Kemira AFDC and VP Zirkonoxid 3-YSZ showed some small aggregate formation. UV-Titan Mill and VP Zirkonoxid PH had formed large aggregates. The Titanium oxide T815 gave discoloration and the agarose mixture did not gel upon cooling. The VP TiO2 PV90, Kemira AFDC, UV-Titan Mill and FINNTI X- 141 were chosen for further experiments.

Experiment 2: Synthesis of porous agarose/inorganic hybrid particles using different amounts of inorganic particles

This experiment was performed with different amounts of inorganic particles of FINNTI X- 141. 4 w% agarose in water was mixed with inorganic particles (Table 2) and placed in a round bottom flask equipped with mechanical stirring. The slurry was heated in an oil bath tempered at 100⁰C for 4 hours.

In parallel, a solution of 3 g ethyl cellulose in 50 ml toluene was prepared in a jacketed reactor. A circulation bath was connected to the reactor and set to a temperature of 60 ⁰C. A glass stirrer was used to mix and solve the ethyl cellulose with the toluene.

When the temperature reached 60⁰C, 5-10 ml agarose/inorganic solution was added to the toluene phase in the reactor. The stirring rate was stepwise increased during emulsification and the emulsion was allowed to equilibrate for at least 10 min at each stirring rate. After each step a sample was withdrawn and the size of the agarose/inorganic particles was estimated using an optical light microscope. When the mean particle diameter was estimated to less then 100 μm the emulsification process was stopped by cooling the reactor to 5⁰C by adding ice to the circulation bath.

The obtained agarose/inorganic particles were slurried in ethanol to remove ethylcellulose and thereafter allowed to sediment. The supernatant was removed. This washing procedure was repeated 3-4 times. Thereafter the agarose/inorganic particles were washed in plenty of water to remove the ethanol.

Table 2 Parameters used in Experiment 2

The above experiment was performed with different amounts of inorganic particles of FIIMNTI X-141 resulting in calculated densities from I₁O to 1,8 g/ml Particles having a density of 1,4 g/ml or below, were selected for further experiments because they had suitable properties in respect of viscosity

Experiment 3: Synthesis of porous agarose/inorganic hybrid particles using different types of inorganic particles

Experiment 3 was performed using different types of inorganic particles 4 w% agarose in water was mixed with inorganic particles (Table 3) and placed in a round bottom flask equipped with mechanical stirring The slurry was heated in an oil bath tempered at 100⁰C for 4 hours

In parallel, a solution of 3 g ethyl cellulose in 50 ml toluene was prepared in a jacketed reactor A circulation bath was connected to the reactor and set to a temperature of 60 ⁰C. A glass stirrer was used to mix and solve the ethyl cellulose with the toluene

When the temperature reached 6O⁰C, 5-10 ml agarose/inorganic solution was added to the toluene phase in the reactor The stirring rate was stepwise increased during emulsification and the emulsion was allowed to equilibrate for at least 10 mm at each stirring rate After each step a sample was withdrawn and the size of the agarose/inorganic particles was estimated using an optical light microscope. When the mean particle diameter was estimated to less then 100 μm the emulsification process was stopped by cooling the reactor to 5⁰C by adding ice to the circulation bath

The obtained agarose/inorganic particles were slurried in ethanol to remove ethylcellulose and thereafter allowed to sediment. The supernatant was removed. This washing procedure was repeated 3-4 times. Thereafter the agarose/inorganic particles were washed in plenty of water to remove the ethanol

Table 3 Parameters used in Experiment 3

Experiment 4: Synthesis of porous agarose/inorganic hybrid particles

A mixture of 3,7 g agarose and 40 g titanium dioxide Kemira AFDC solved in 80 ml water was placed in a round bottle flask and heated in an oil bath [100⁰C) for one hour (approximately 95⁰C in the flask)

In parallel, a solution of 14 g ethyl cellulose in 200 ml toluene was prepared in a jacketed reactor A circulation bath was connected to the reactor and set to a temperature of 60 ⁰C An inpeller was used to mix and solve the ethyl cellulose with the toluene

When the temperature reached 60 ⁰C, the ml agarose/ inorganic solution was added to the toluene phase in the reactor The stirring rate was stepwise increased during emulsification and the emulsion was allowed to equilibrate for at least 5 mm at each stirring rate After each step a sample was withdrawn and the size of the agarose/ inorganic particles was estimated using an optical light microscope When the mean particle diameter was estimated to less then 100 μm the emulsification process was stopped by cooling the reactor to 15⁰C by adding ice to the circulation bath

The obtained agarose/ inorganic particles were slurried in ethanol to remove ethylcellulose and thereafter allowed to sediment The supernatant was removed This washing procedure was repeated 5 times To see if the supernatant was removed after 5 washes, some of the supernatant was added to water If there was a precipitation the ethylcellulose was still present and the agarose/ inorganic particles was further washed with ethanol Thereafter the agarose/inorganic particles were washed with water to remove the ethanol

The calculated density of the hybrid particles obtained in experiment 4 is 1 3 g/ml

Experiment 5: Synthesis of magnetic porous agarose/inorganic particles hybrid particles

A mixture of 3 7 g agarose, 30 g Kemira AFDC and 7 g magnetite disperged in 80 ml water was placed in a round bottom flask and heated in an oil bath (100⁰C) for one hour (approximately 95⁰C in the flask) In parallel, a solution of 14 g ethyl cellulose in 200 ml toluene was prepared in a jacketed reactor. A circulation bath was connected to the reactor and set to a temperature of 60⁰C. An impeller was used to mix and solve the ethyl cellulose with the toluene.

When the temperature reached 60 ⁰C, the agarose/magnetite/inorganic slurry was added to the toluene phase in the reactor. The stirring rate was stepwise increased during emulsification and the emulsion was allowed to equilibrate for at least 5 min at each stirring rate. After each step a sample was withdrawn and the size of the agarose/magnetite/inorganic particles was estimated using an optical light microscope. When the mean particle diameter was estimated to less than 100 μm the emulsification process was stopped by cooling the reactor to 15 ⁰C by adding ice to the circulation bath.

The obtained agarose/magnetite/inorganic particles were disperged in ethanol to remove ethyl cellulose and thereafter allowed to sediment. The supernatant was removed. This washing procedure was repeated 5 times. To see if the supernatant was removed after 5 washes, some of the supernatant was added to water. If there was a precipitation the ethyl cellulose was still present and the agarose/magnetite/inorganic hybrid particles were further washed with ethanol. Thereafter the agarose/inorganic particles were washed with distilled water to remove the ethanol.

The calculated density of the magnetic hybrid particles obtained in experiment 5 is 1.3 g/ml.

Experiment 6 A-C

A mixture of 18 g agarose, 100 g titanium dioxide (see Table 4) and 40 g magnetite dispersed in 400 ml water was placed in a round bottom flask and heated in an oil bath (100⁰C) for one hour (approximately 95⁰C in the flask).

Table 4 Properties of titanium dioxide used for Experiment 6. In parallel, a solution of 68-90 g ethyl cellulose in 1500 ml toluene was prepared in a jacketed reactor. A circulation bath was connected to the reactor and set to a temperature of 60 ⁰C. lntermig stirrers were used to mix and solve the ethyl cellulose with the toluene.

When the temperature reached 60⁰C, the agarose/magnetite/inorganic slurry was added to the toluene phase in the reactor. The stirring rate was stepwise increased during emulsification and the emulsion was allowed to equilibrate for at least 10 min at each stirring rate. After each step a sample was withdrawn and the size of the agarose/magnetite/inorganic particles was measured (using Low Angle Laser Light Scattering?). When the mean particle diameter was 62+5 μm the emulsification process was stopped by cooling the reactor to 15 ⁰C by adding ice to the circulation bath.

The obtained agarose/magnetite/inorganic particles were dispersed in ethanol to remove ethyl cellulose and thereafter allowed to sediment The supernatant was removed. This washing procedure was repeated 5 times. To see if the supernatant was removed after 5 washes, some of the supernatant was added to water. If there was a precipitation the ethyl cellulose was still present and the agarose/magnetite/inorganic hybrid particles were further washed with ethanol. Thereafter the agarose/inorganic particles were washed with distilled water to remove the ethanol.

The calculated density of the magnetic hybrid particles obtained in experiment 6 is 1.2 g/ml.

Experiment 7: Cross-linking of porous agarose/inorganic hybrid particles

A total volume of 0.12 1 of the in Experiment 2 and Experiment 3 synthesized hybrid particles and distilled water was added to a three-necked round bottom flask. 14.9 g sodium sulphate, 0.10 g sodium borohydride and 1.05 ml sodium hydroxide (50%) were also added. The round bottom flask was placed in a preheated oil bath (47⁰C). Epichlorohydrin was added with a dose speed of 0.034 ml/min using a Doεimat pump to a total volume of 12.4 ml. Sodium hydroxide (50%) was added with a dose speed of 0.024 ml/min using a Dosimat pump to a total volume of 85 ml. The reaction was left to proceed over night.

The next day the reaction mixture was neutralized by adding acetic acid, approximately 2.86 ml, until pH was 7. The cross-linked particles were washed on glass filter with plenty of distilled water Finally, the hybrid particles were sieved through a 315 μm sieving cloth. Experiment 8: Functional tests of hybrid particles prepared in Experiment 3-5

A model sample was used containing a tryptic digest of bovine serum albumin, BSA, spiked with a pure mono phosphopeptide (0.9 mass%) from β-casein with known molecular weight (2062 g/mol).

A functional test was performed to see if the inorganic particles were able to enrich β-casein. MALDI- TOF was used for qualitative evaluation of the sample after enrichment on the hybrid particles. The model sample was prepared with such low initial concentration of the phosphopeptide β-casein in the sample so that no signal at m/z 2062 was obtained from β-casein in the MALDI-TOF spectra before the enrichment step. Meaning that, if a peak with m/z 2062 was detected in the MALDI- spectrum enrichment was achieved. The enrichment was performed on a small scale using SpinTrap columns. The hybrid particles were loaded in the columns and thereafter the sample was applied. The following protocol was used in the functional test:

Protocol for Functional test

1) Add 80μl 50% media slurry to SpinTrap column (use large pipette tip or cut the pipette tip). This gives 40μ! particles. Centrifuge 1 min 200xg.

2) Add 500 μl wash/equilibration buffer ( DHB (20mg/ml) in 80% ACN, 0,1% TFA). Vortex SpinTrap column briefly. Centrifuge 1 min 200xg.

3) Mix 20 μl mono phosphate peptides dissolved in equilibration buffer (5OmM Glycin-HCL, 50% ACN) with 220 μl trypsinated BSA (2mg/ml) 4) Add 240 μl wash/equilibration buffer ( DHB (20mg/ml) in 80% ACN, 0,1% TFA) to the sample mixture.

5) Add the diluted sample mixture to the SpinTrap column. Rotate end-over-end 90 min. Centrifuge 1 min 200xg. Save flow through.

6) Add 500 μl wash/equilibration buffer ( DHB (20mg/ml) in 80% ACN, 0,1% TFA). Vortex SpinTrap column briefly. Centrifuge 1 min 200xg. Save wash 1.

7) Add 500 μl wash/equilibration buffer ( DHB (20mg/ml) in 80% ACN, 0,1% TFA). Vortex SpinTrap column briefly. Centrifuge 1 min 200xg. Save wash 2.

8) Add 500 μl wash buffer 5OmM Glycin-HCL, 50% ACN. Vortex SpinTrap column briefly. Centrifuge 1 min 200xg. Save wash 3. 9) Add 500 μl wash buffer 5OmM Glycin-HCL, 50% ACN. Vortex SpinTrap column briefly.

Centrifuge 1 min 200xg. Save wash 4.

10) Elute sample by adding 500 μl elution buffer (1% Phosphoric acid, 50% ACN). Incubate 5 min with end-over-end rotation. Centrifuge 1 min lOOOxg. Save eluate.

11) Store flow through, wash 1, wash 2, wash 3, wash 4 and eluate at -2O⁰C. Results of functional test

Results from the first try to enrich phosphopeptides, which was only washed with 80% ACN and 0 1% TFA, shows in a MALDI-spectrum that an enrichment of phosphopeptides was achieved In a MALDI-spectrum of a spiked sample (ι e a sample before enrichment), the peak that indicates the mono phosphopeptide at 2062 m/z could not be detected

The agarose/inorganic particles were evaluated according to the above protocol in experiment 5 Table 5 describes how many peaks and the peak intensity for the mono phosphopeptide

Table 5 Results from screening of agarose/inorganic particles

Screening of the agarose/inorganic particles showed excellent results (Table 5) For experiment 3B (Kemira AFDC) only two peaks were detected, the mono phosphopeptide with a peak intensity at 100 % and a peak at 1992 m/z This titanium dioxide was selected for the further evaluation in Experiments 4 and 5, and the same excellent result was obtained

Experiment 9: Functional test with more complex sample

The hybrid particles from Experiment 7 were further evaluated using a more complex sample containing tryptic peptides from a mixture of EoIiI cell extract spiked with bovine β -casein (10%), chicken egg ovalbumin (5%) and creatin kinase from rabbit muscle (2 5%) According to annotations in the swissprot database and MS/MS analysis of pure proteins there should be 2 phosphorylated tryptic peptides from beta-casein, 2 from ovalbumin and 1 from creatin kinase

The peptide mix was purified using the porous hybrid particles and the eluates were evaporated to remove residual acetonitπle The peptides remaining after purification with the hybrid particles produced according to the present invention were analyzed with LC-MS/MS (pepmap C-18 RPC column connected to an ion trap MS instrument via nanospray interface) After enrichment and analysis with LC-MS/MS both beta-casein and ovalbumin were recovered, by detection of one phosphorylated peptide from each protein. The expected tryptic peptide from creatin kinase was not found by MS/MS. Some phosphorylated peptides give a prominent loss of phosphoric acid in MS/MS as a neutral loss without extensive fragmentation of the peptide backbone giving very poor MS/MS spectra that are not suitable for database searches. Several different MS methods need to be used to get a complete analysis of phosphorylated peptides.

Experiment 10 Functional test of hybrid particles from Experiment 6A and 6B

Sample mixture

The sample mixture consisted of three phosphopeptides:

• 100 ng (59pmol) Kinase Domain of Insulin Receptor-3, m/z 1702.7472

• 100 ng (48 pmol) Bovine β-Casein monophosphopeptide, m/z 2061.8284

• 1000 ng (460 pmol) PKA Regulatory Subunit Il Substrate Calcineurin (PP2B) Substrate, m/z 2192.0859

spiked in 100 μg trypsin digested Bovine Serum Albumin (BSA). The sample was then diluted with equilibration/binding buffer to a total volume of 112 μl before applied on the hybrid particles.

Buffer System The buffer systems used in testing hybrid particles from experiment 6A and 6B are listed in Table 6.

Table 6: Buffer system used in functional test of hybrid particles from experiment 6A and 6B

Protocol for Functional testing 1.5 ml micro centrifuge tubes were used together with a magnetic rack. The magnet was removed before buffer and sample application.

1. Add 20μl 50% media slurry into a micro tube. Gives 10 μl media.

2. Add 500 μl binding/equilibration buffer, mix a few times and throw away buffer. 3. Add the diluted sample mixture. Rotate end-over-end 30 min. Throw away flow trough.

4. Add 500 μl wash buffer I₁ mix a few times and throw away buffer. 5. Add 500 μl wash buffer 2, mix a few times and throw away buffer.

6. Add 500 μl wash buffer 3, mix a few times and throw away buffer.

7. Elute sample by adding 20 μl elution buffer. Incubate 5 min with end-over-end. Repeat once. Save eluates.

Start material and eluates were analyzed with MALDI-ToF.

Results

The results from the functional testing of hybrid particles from experiment 6A and 6B showed enrichment of phosphopeptides (Table 7).

Table 7 Results from functional testing of hybrid particles from experiment 6A and 6B

Experiment 11 Functional test of hybrid particles from Experiment 6C Sample mixture

The sample mixture consisted of three phosphopeptides:

• 1000 ng (590pmol) Kinase Domain of Insulin Receptor-3, m/z 1702.7472

• 1000 ng (480 pmol) Bovine β-Casein monophosphopeptide, m/z 2061.8284

spiked in 100 μg trypsin digested Bovine Serum Albumin [BSA). The sample was then diluted with equilibration/binding buffer to a total volume of 145 μl before applied on the hybrid particles.

Buffer System

The buffer systems used in testing hybrid particles from experiment 6C are listed in Table i

Table 8: Buffer system used in functional test of hybrid particles from experiment 6C Protocol for Functional testing

1.5 ml micro centrifuge tubes were used together with a magnetic rack. The magnet was removed before buffer and sample application.

1) Add 20μl 50% media slurry into a micro tube. Gives 10 μl media.

2) Add 500 μl binding/equilibration buffer.

3) Add the diluted sample mixture, 145 μl. Rotate end-over-end 30 mm. Throw away flow through.

4) Add 500 μl wash buffer 1, mix a few times and throw away buffer. 5) Add 500 μl wash buffer 2, mix a few times and throw away buffer.

6) Elute sample by adding 50 μl elution buffer. Incubate 5 mm with end-over-end rotation. Repeat once. Save eluates.

Start material and eluates were analyzed using MALDI-ToF.

Results

Starting material showed 27 detected peaks. All 3 phospho peptides were detected after enrichment. Total number of peaks in 1^st eluate was 12. Total number of peaks in 2^nd eluate was 9

Claims

1. A method for production of separation media for separation of biomolecules from a sample, comprising the following steps: addition of inorganic metal oxide particles to an organic solution to form a mixture; and emulsification of said mixture to form porous hybrid particles, wherein the density of said porous hybrid particles is between 1.0 and 15 g/ml, preferably 1.0-1.3, and wherein said inorganic particles have a shape and size that maximizes their active surface area enabling said inorganic particles to interact with biomolecules.

2. Method according to claim I₁ wherein the inorganic metal oxide particles are porous

3. Method according to claim 1 or 2, wherein the inorganic metal oxide particles are less than 1000 nm, preferably less than 300 nm, in size.

4. Method according to one or more of the above claims, wherein the inorganic metal oxide particles are selected from Group 4, 12, 13 and/or 14.

5. Method according to claim 4, wherein the inorganic metal oxide particles are selected from titania, zirconia, hafnia, alumina, zinkoxide, germania and/or tin dioxide, preferably titania, zirconia and/or alumina, most preferably titania.

6. Method according to one or more of the above claims, wherein the organic solution comprises polysaccharides, for example agarose or dextran.

7. Method according to one or more of the above claims 1-6, wherein the organic solution comprise synthetic material, for example; polystyrene/dvb and porogens or methacrylates and porogens.

8. Method according to claim 6, wherein the organic solution comprise agarose and said inorganic metal oxide particles comprise titania.

9. Method according to one or more of the above claims, wherein magnetic particles are incorporated into said organic solution.

10. Porous hybrid particles comprising inorganic metal oxide particles selected from Group 4,

12, 13 and/or 14 which are incorporated in organic solution to form porous hybrid particles, wherein the density of the hybrid particles is between 1.0 and 1.5 g/ml, preferably between

1.0-1.3 g/ml, and wherein said inorganic particles have a shape and size that maximizes their active surface area enabling said inorganic particles to interact with biomolecules.

11. Porous hybrid particles according to claim 10, wherein the inorganic particles have a (volume-weighted, sphere volume-equivalent) average diameter less than 1000 nm, preferably less than 300 nm.

12. Porous hybrid particles/Porous beads according to claim 10 or 11, wherein the inorganic particles are selected from titania, zirconia, hafnia, alumina, zinc oxide, germania and/or tin dioxide, preferably titania, zirconia and/or alumina, most preferably titania.

13. Porous hybrid particles/Porous beads according to claim 10, 11 or 12, wherein the organic solution is selected from polysaccharides or synthetic polymers.

14. Porous hybrid particles according to one or more of claims 10-13, wherein said inorganic particles comprise titania and the organic solution comprise agarose.

15. Porous hybrid particles according to one or more of claims 10-14 comprising a lid covering the hybrid particles, wherein said lid comprising up to 20% agarose.

16. Porous hybrid particles according to one or more of claims 10-15 comprising magnetic particles incorporated into said organic solution.

17. Porous hybrid particles according to one or more of claims 10-16, wherein the size of the particles is 5-500 μm, preferably 25-100 μm.

18. Use of the porous hybrid particles according to one or more of the claims 10-17 for separation/purification/enrichment of biomolecules.

19. Use of the porous hybrid particles according claim 18, wherein the biomolecules are phosphoproteins or -peptides.

20. Use of the porous hybrid particles according claim 18, wherein the biomolecules are glycoproteins or -peptides.