WO2011004300A1 - Process for producing microfibrillated cellulose - Google Patents

Process for producing microfibrillated cellulose Download PDF

Info

Publication number
WO2011004300A1
WO2011004300A1 PCT/IB2010/053043 IB2010053043W WO2011004300A1 WO 2011004300 A1 WO2011004300 A1 WO 2011004300A1 IB 2010053043 W IB2010053043 W IB 2010053043W WO 2011004300 A1 WO2011004300 A1 WO 2011004300A1
Authority
WO
WIPO (PCT)
Prior art keywords
fibres
process according
treatment
alkali metal
metal hydroxide
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/IB2010/053043
Other languages
French (fr)
Inventor
Marianna Vehviläinen
Taina Kamppuri
Maarit Peltola
Ali Harlin
Pertti Nousiainen
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Stora Enso Oyj
Original Assignee
Stora Enso Oyj
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority to CA2767290A priority Critical patent/CA2767290C/en
Priority to JP2012519095A priority patent/JP2012532952A/en
Priority to RU2012103990/04A priority patent/RU2530022C2/en
Priority to CN201080030882.6A priority patent/CN102472013B/en
Priority to BR112012000142-6A priority patent/BR112012000142B1/en
Priority to EP10796796.0A priority patent/EP2452013B1/en
Application filed by Stora Enso Oyj filed Critical Stora Enso Oyj
Priority to US13/382,573 priority patent/US8778134B2/en
Priority to AU2010269912A priority patent/AU2010269912B2/en
Priority to KR1020127002536A priority patent/KR101715428B1/en
Publication of WO2011004300A1 publication Critical patent/WO2011004300A1/en
Anticipated expiration legal-status Critical
Priority to ZA2012/00327A priority patent/ZA201200327B/en
Ceased legal-status Critical Current

Abstract

The invention relates to a process for treating cellulosic fibres which process comprises mechanically pre-treating the fibres followed by treating the fibres with an enzyme and thereafter mixing the fibres with a solution comprising an alkali metal hydroxide followed by mechanically treating the fibres to form microfibrillated cellulose. In this way it is possible to produce MFC in an improved and energy efficient way.

Description

Process for producing microfibrillated cellulose
Field of the invention
The present invention relates to a process for producing microfibrillated cellulose by treating cellulosic fibres.
Background
Cellulosic fibres are multi-component structures made from cellulose polymers, i.e. cellulose chains. Lignin, pentosans and other components known in art may also be present. The cellulose chains in the fibres are attached to each other to form elementary fibrils. Several elementary fibrils are bound to each other to form microfibrils and several microfibrils form aggregates. The links between the cellulose chains, elementary- and microfibrils are hydrogen bonds. Microfibrillated cellulose (MFC) (also known as nanocellulose) is a material made from wood cellulose fibres, where the individual microfibrils have been detached from each other. MFC is normally very thin (~20 nm) and the length is often between 100 nm to 1 μm. MFC can be produced in a number of different ways. It is possible to mechanically treat cellulosic fibres so that microfibrils are formed. However, it is very energy consuming method to for example shred or refine the fibres and it is therefore not often used. The production of nanocellulose or microfibrillated cellulose with bacteria is another option. In contrast to the above, this is a bio-synthetic process starting from another raw material than wood fibres. However, it is a very expensive process and time consuming. It is also possible to produce microfibrils from cellulose by the aid of different chemicals which will break or dissolve the fibres. However, it is difficult to control the length of the formed fibrils and the fibrils are often too short. One example of production of MFC is described in WO2007091942. In the method described in WO20070912942, the MFC is produced by the aid of refining in combination with addition of an enzyme. However, there is still a need for an improved process for the production of microfibrillated cellulose.
Summary of the invention
It is an object of the present invention to provide a process for production of microfibrillated cellulose in an improved and energy efficient way.
These objects and other advantages are achieved by the process according to claim 1. By mechanically pre-treating cellulosic fibres, followed by enzymatic treatment and addition of a solution comprising an alkali metal hydroxide and finally an additional mechanical treatment, it is possible to produce microfibrillated cellulose (MFC) in a very energy efficient way. This is achieved by the independent claim and preferred embodiments of the process are defined in the dependent claims.
The invention relates to a process for treating cellulosic fibres which process comprises mechanically pre-treating the fibres followed by treating the fibres with an enzyme and thereafter mixing the fibres with a solution comprising an alkali metal hydroxide in order to make the fibres expand. The expanded fibres are thereafter mechanically treated to form microfibrillated cellulose. In this way it is possible to produce MFC in an improved and energy efficient way.
The concentration of the alkali metal hydroxide can be between 4-18% of weight, preferably between 5-9% by weight. The concentration of the alkali metal hydroxide regulates the expansion of the fibres before the final mechanical treatment. The alkali metal hydroxide is preferably sodium hydroxide. The solution comprising alkali metal hydroxide may also comprises a zinc salt. The combination of alkali metal hydroxide and zinc salt has been shown to improve expansion of the fibres. The zinc salt is preferably zinc oxide. The concentration of the zinc salt can be between 0,1-2% by weight preferably between 0,5-1 ,3% by weight.
The pre-treatment is preferably done by shredding or refining of the fibres. The pre-treatment opens the fibre structure before the treatment with the enzyme and the solution comprising alkali metal hydroxide. In this way the enzymatic treatment as well as the treatment with the solution comprising alkali metal hydroxide and zinc salt will be more effective and the expansion of the fibres will improve and thus also the production of MFC.
The consistency of the fibres during refining is preferably between 2,5- 30% by weight.
It is also possible to add an enzyme before or during the pre-treatment in order to decompose the fibre structure. An enzyme which affects or breaks down hemicellulose is preferably used, for example xylanase but cellulase for example endogulcanase can also be used.
The temperature during the treatment with the solution may be between 0-15°C. Lower temperatures have been shown to increase the expansion of the fibres.
The enzyme used in the process is preferably cellulase which will decompose the cellulosic fibres and increase the accessibility and activity of the fibres and thus also the production of microfibrillated cellulose.
The cellulosic fibres are preferably fibres of kraft pulp.
Detailed description
The invention relates to a process for producing microfibrillated cellulose in an improved and energy efficient way.
It has been shown that the combination of mechanical pre-treatment followed by enzymatic treatment and addition of a solution comprising alkali metal hydroxide makes it possible to expand the fibres in a gentle and controlled way. Moreover, it has been shown that further mechanical treatment of the expanded fibres can be done in order to produce microfibrillated cellulose. By this process it has been shown that it is possible to produce MFC in a very controlled and cost efficient way.
The enzymatic treatment followed by addition of the solution
comprising alkali metal hydroxide expands the fibres and it is by this treatment possible to control the expansion of the fibres. By using enzyme and the mentioned chemical/s it is possible to make small adjustments in, for example the concentrations, and in that way be able to control and regulate the extent of expansion of the fibres in a very precise way. The fibres expand due to that the hydrogen bonds between the cellulose chains are weakened. Even though the hydrogen bonds are weakened by the treatment, the fibres are otherwise quite unaffected. Thus, the strength of the fibres is thus not as decreased as after a purely mechanical treatment used in order to receive the same fibre length.
The enzyme will decompose the primary layer of the fibres and thus increase the accessibility of the fibres and is then able to penetrate the fibre structure and get in between the fibrils. The solution comprising alkali metal hydroxide will then be able to affect the fibre structure in a much more efficient way since the primary layer of the fibres is weakened. Some of the fibres will dissolve during the treatment with the solution comprising alkali metal hydroxide. When the alkali metal hydroxide content thereafter is decreased, the dissolved fibrils will go back to solid state. When the fibrils go back to solid state they will work as a glue and thus increase the bonding between the fibres and fibrils. Consequently, the produced MFC will have very good film forming properties.
The cellulosic fibres are pre-treated before the treatment with the enzyme and the solution comprising alkali metal hydroxide. The fibres are preferably shredded or refined in order to increase the specific surface area of the fibres before the enzymatic treatment and in this way facilitate and improve the effect of the enzymatic treatment. The shredding or refining may be done at a consistency between 2-40% by total weight. However, high consistency, preferably between 15-40% by total weight is often preferred. Low consistency, for example 2-6% by total weight or medium consistency, for example 10-20% of total weight can also be used. It is also possible to add enzymes during the pre-treatment. It is then preferred to use enzymes which break down hemicellulose, such as xylanase but other enzymes such as cellulase for example endoglucanase can also be used. Enzymes may be added in order to further improve the pre-treatment and be able to decrease the extension of the mechanical treatment and thus save both the fibre strength and energy needed.
Other mechanical pre-treatments besides refining and shredding, such as beating, steam explosion, defibration, homogenization, ultrasonic treatment, dry cutting or other known mechanical fibre treatments in order to soften the fibres and make them more active and reactive before the following treatments can also be used.
After the pre-treatment, enzyme is added to the fibres which are in the form of a slurry which has a concentration of approximately 4-5%. The enzyme is added during stirring either in the beginning of the treatment or during the entire reaction time. The purpose with the enzymatic treatment is to break the hydrogen bonds between the microfibrils present in the slurry and thus enable expansion of the fibres. The enzyme increases the
accessibility and the activity of the fibres and improves the following treatment with the solution.
The enzyme used can be any wood degrading enzymes which decompose cellulosic fibres. Cellulase is preferably used but other examples of usable enzymes are xylanase and mannanase. The enzyme is often an enzymatic preparation which can contain small parts of other enzymatic activities than the main enzyme of the preparation. The temperature used for the treatment with the enzyme may be between 30-85°C. However, it depends on the enzyme used and the optimal working temperature for that specific enzyme as well as other parameters of the treatment, such as time and pH. If cellulase is used, the temperature during the treatment may be approximately 500C.
The enzymatic treatment may last for 30 minutes-5 hours. The time needed depends on the cellulosic fibres which are treated and on the activity of the enzyme as well as the temperature and the pH of the treatment. The activity of the enzyme may be 10-1000 nkat/g. The enzymatic treatment can be terminated by either rising the temperature or the pH in order to denaturate the enzymes. As an alternative, if the solution comprising alkali metal hydroxide is added directly to the treated fibres, it is not necessary to denaturate the enzymes separately since the pH of the alkali metal hydroxide solution is high enough to terminate the enzymatic treatment. The pH during the treatment with the enzyme is preferably between 4-6. The solution comprising alkali metal hydroxide is thereafter added to the enzyme-treated fibres to form a slurry. The slurry preferably has a concentration between 1-7% by total weight. The concentration of the alkali metal hydroxide may be between 4-18% by total weight, preferably between 5-9% by total weight. By total weight means the total weight of the slurry, i.e. the total weight of the solution and the pulp.
The solution may also contain a zinc salt. The combination of an alkali metal hydroxide and a zinc salt has been shown to be very efficient when expanding the fibres. The concentration of the zinc salt may be between 0,1- 2% by total weight preferably between 0,5-1 ,3% by total weight.
If the solution comprises both alkali metal hydroxide and a zinc salt, the alkali metal hydroxide concentration and the zinc salt concentration are dependent of each other. For example, when there is a high alkali metal hydroxide concentration, less zinc salt is required. The amount of the alkali metal hydroxide and the zinc salt should be adjusted in a stepless manner inside their above determined ranges so optimum results can be reached. The alkali metal hydroxide concentration and the zinc salt concentration are thus dependent on each other in respect of the efficiency of expansion of the cellulosic fibres.
The temperature during the treatment with the solution may be between 0-150C. Lower temperatures have been shown to increase the expansion of the fibres. However, it is important not to decrease the temperature too much since the dissolution of the fibres increases with decreased temperature. It is not desirable to dissolve the fibres so the temperature, as well as other parameters, must be controlled in order to only expand the fibres and not to dissolve them.
The alkali metal hydroxide is preferably sodium hydroxide but other alkali metal hydroxides, such as potassium hydroxide or a mixture of sodium hydroxide and potassium hydroxide or other alkali metal hydroxides can be used. The zinc salt is preferably zinc oxide, but other zinc salts such as zinc chloride or mixtures between different zinc salts can be used. The pH during the treatment with the solution comprising alkali metal hydroxide or alkali metal hydroxide and zinc salt is preferably above 13.The treatment of the fibres with the solution comprising alkali metal hydroxide may last between 5 minutes to 2 hours depending on if the slurry is mixed during the treatment or not.
When the treatment with the solution is completed, the solution can be washed away with water or an acid. Before the addition of water or acid, low concentration sodium hydroxide, or another alkali metal hydroxide, can be added in order to remove the part with dissolved cellulose (if any) to be able to further use that part.
When the alkali metal hydroxide content decreases dissolved fibrils or particles will go back to solid state (as previously described). This
regeneration of dissolved fibrils or particles occurs when the alkali metal hydroxide content is decreased. The decrease can either be accomplished by addition of water or acid or the produced slurry comprising the produced MFC can be mixed with another pulp slurry, for example in the wet end of a paper or board machine. Dissolved cellulose is a clear or slightly turbid solution containing both dissolved cellulosic material and nanoparticles. The solid particles in the solution which we call dissolved should however be of the size that they can not be visible under a light microscope. Thus, the dissolved part also contains nano sized fibres and it should therefore also be recovered and used.
The solid part received by the process according to the invention and the dissolved part can be further treated either together or separately. A drawback with the addition of water or acid is that the fibres tend to partially shrink, and it is advantageous to prevent such shrinkage. It can for example be prevented by defibrillating the fibres before addition of water or acid or by mechanical means making nano-cellulose before addition of water or acid. It is also possible to add chemicals that will prevent shrinkage. The choice of chemical is related to the end use of the expanded fibres. For example, surface active components, mechanical prevention by addition of bentonite or TiO2, by addition of CMC or starch or surfactants in order to "freeze" the fibre structure before addition of water or acid.
The fibres are thereafter mechanically treated in order to form microfibrillated cellulose. The time and temperature during such treatment varies depending on the fibres treated as well as on the previous treatments and are controlled in order to receive fibres with the desired fibre length. The mechanical treatment may be done by a refiner, defibrator, beater, friction grinder, high shear fibrilator (such as cavitron rotor/stator system), disperger, homogenizator (such as micro fluidizer) or other known mechanical fibre treatment apparatus.
The cellulosic fibres used in the process according to the invention are preferably fibres of kraft pulp, i.e. they have been treated according to the kraft process. It has been shown that the primary wall of the fibres in kraft pulp often prevents the fibres from expanding. Thus, it is necessary to remove the primary wall before the expanding treatment. The primary wall of the fibres can be removed by enhancing the pre-treatment of the fibres. Thus, increased refining, preferably high consistency refining has been shown to be very effective. Also, enzymes affecting hemicellulose can be used, either alone or in combination with refining, preferably high consistency refining. It is also possible to treat the fibres with enzymes before the refining of the fibres. However, other chemical pulps, mechanical pulps or chemi-mechanical pulps can also be used, one example is sulphite pulp. The fibres can also be bleached or unbleached, even though the bleached is preferred since the lignin content is decreased and the fibres expand more easily.
The cellulosic fibres may be hardwood and/or softwood fibres. It has been shown that sulphite pulps and pine kraft pulp disintegrate into smaller fractions when treated according to the invention compared to eucalyptus and birch kraft pulps. Thus, it is preferred to treat softwood fibres with the process according to the invention. The cellulosic material produced according to the invention may be used for the production of films. MFC produced from softwood kraft pulps according to the process as described herein has been shown to achieve very good film forming properties. Micro fibrillated cellulose (MFC) is often also referred to as
nanocellulose. Fibres that has been fibrillated and which have microfibrille on the surface and microfibrils that are separated and located in a water phase of a slurry are included in the definition MFC. Example
Birch kraft pulp was treated accordingly:
- mechanical shredding for 5 hours at pulp consistency 20%
- enzymatic treatment with cellulase, 250nkat/g, pH 5, 500C, 3 hours.
The pulp was thereafter subjected to 9wt% NaOH at 1O0C without intermediate drying to study its expanding ability. The wet pulp (cons. 20%) was added into NaOH at 100C, the final content of the mixture was 5wt% pulp and 9wt% NaOH. The mixture was stirred for 15 minutes at 1000 rpm and thereafter left stable for 1 h45min at the same temperature. The sample was then studied under light microscope and the portion of soluble cellulose measured.
The expanded sample was purified by adding 4% NaOH, centrifuging the mixture and separating the clear/slightly turbid supernatant. The supernatant was treated with 10% H2SO4 to precipitate the dissolved cellulose. Thereafter, both the purified undissolved part and the precipitated dissolved part were further washed with water in dialysis. It was concluded that 42% of the fibres were dissolved.
Both the undissolved part and the precipitated dissolved part were thereafter subjected to high shear mixing at a consistency of about 1 ,5% for 10 minutes in order to produce MFC. The total energy consumption when producing MFC as described in this example was about 0,3MWh/t.
Prior art studies has shown that production of MFC by the aid of mechanical treatment is about 2-3 MWh/t according to prior art studies.
Consequently, the energy consumption has strongly decreased.

Claims

Claims
1. A process for treating cellulosic fibres which process comprises: -mechanically pre-treating the fibres,
-treating the fibres with an enzyme,
-mixing the fibres with a solution comprising an alkali metal hydroxide in order to make the fibres expand and
-mechanically treat the expanded fibres to form microfibrillated cellulose.
2. The process according to claim 1 characterized in that the
concentration of the alkali metal hydroxide is between 4-18% by total weight, preferably between 5-9% by total weight.
3. The process according to claim 1 characterized in that the solution comprises a zinc salt.
4. The process according to claim 3 characterized in that the
concentration of zinc salt is between 0, 1 - 2% by total weight preferably between 0,5-1 ,3% by weight.
5. The process according to any of the preceding claims characterized in that the fibres are pre-treated by shredding or refining.
6. The process according to claim 5 characterized in that the fibres are treated at a consistency of between 2,5-40% by total weight during the shredding or refining.
7. The process according to any of the preceding claims characterized in that the temperature during the treatment with the solution is between 0-
150C.
8. The process according to any of the preceding claims characterized in that the alkali metal hydroxide is sodium hydroxide.
9. The process according to claims 3-8 characterized in that the zinc salt is zinc oxide.
10. The process according to any of the preceding claims
characterized in that the enzyme is cellulase.
11. The process according to any of the preceding claims
characterized in that enzyme affecting hemicellulose, such as xylanase or an enzyme affecting cellulose such as cellulase is added before or during the mechanically pre-treatment of the fibres.
12. The process according to any of the preceding claims
characterized in that the fibres are fibres of kraft pulp.
PCT/IB2010/053043 2009-07-07 2010-07-02 Process for producing microfibrillated cellulose Ceased WO2011004300A1 (en)