WO2011045433A1

WO2011045433A1 - Aqueous stoving binder

Info

Publication number: WO2011045433A1
Application number: PCT/EP2010/065576
Authority: WO
Inventors: Roland Feola; Willi Paar; Johann Gmoser; Norbert Cvetko; Rudolf Schipfer
Original assignee: Cytec Austria GmbH
Current assignee: Allnex Austria GmbH
Priority date: 2009-10-16
Filing date: 2010-10-16
Publication date: 2011-04-21
Anticipated expiration: 2012-04-16
Also published as: EP2488565A1; CN102639587A; HRP20141106T1; SI2488565T1; JP2013507512A; EP2488565B1; EP2319877A1; CN102639587B; KR101731254B1; JP6128850B2; KR20120100994A; ES2524339T3

Abstract

The invention relates to an aqueous stoving binder comprising a mixture AB of an amide-modified epoxy amine adduct A and a capped isocyanate B that has an allophanate as a structural element, and a process of making thereof.

Description

Aqueous Stoving Binder

Field of the Invention

The invention relates to an aqueous stoving binder. It also relates to a process for its preparation, and a method of use thereof.

Background of the Invention

Aqueous binders based on epoxy resins are usually cured with polyfunctional curing agents such as polyamines, polyfunctional acids or anhydrides thereof, polyamidoamines , aminoplast resins and phenoplast resins. These curing agents react with functional groups present in the epoxy resin, such as epoxide groups, and hydroxyl groups which stem from the usual chain-extension reactions whereby secondary hydroxyl groups are formed in the growing chain, due to ring opening of an epoxide group.

Coatings based on epoxy resins are used for a plethora of purposes, i. a. for corrosion protection of base metals. Coating compositions used therefor usually comprise also pigments and fillers, particu- larly such pigments or fillers that enhance the corrosion protec^¬ tion, such as zinc based pigments.

Summary of the Invention

It is an object of the present invention to further improve the epoxy resin-based coating compositions that are presently used, particularly with regard to pigment wetting, compatibility with substrates such as steel, aluminium, and zinc-coated steel and iron, and lowering the amount of volatile by-products such as blocking agents, also referred to as capping agents, that are libe^¬ rated upon curing.

It has been found in the investigations that have led to the present invention that a combination of an amide-modified epoxy amine adduct and a capped isocyanate that comprises an allophanate structure forms a water-reducible coating binder that has the desired properties as outlined supra. The present invention is therefore directed to an aqueous stoving binder comprising a mixture AB of an amide-modified epoxy amine adduct A and a capped isocyanate B that has an allophanate as a structural element. Detailed Description of the Preferred Embodiments

The amide-modified epoxy amine adduct A is a reaction product of an epoxide functional compound Al, of an amidoamine A3 prepared from a fatty acid A31 and an amine A32 having at least one primary or secondary amino group, and of compounds A2 which are reactive towards epoxide groups which compounds A2 are selected from amines A21 having at least one primary or secondary amino group, from phenolic compounds A22 having at least two phenolic hydroxy groups, and from organic acids A23, with the proviso that at least one amine A21 and at least one phenolic compound A22 are used in the reaction to prepare the adduct A.

The capped isocyanate B has at least two capped isocyanate structures -NH-CO-OR and at least one allophanate structure,

-NH-CO-NR-CO-OR- wherein

R is the residue of a hydroxy functional capping agent B21, also commonly referred to as blocking agent, R-OH, selected from the group consisting of linear aliphatic monohydroxy compounds B211 having from 1 to 20 carbon atoms, branched aliphatic monohydroxy compounds B212 having from 4 to 20 carbon atoms, and cyclic ali^¬ phatic monohydroxy compounds B213 having from 4 to 20 carbon atoms, wherein in any of B211, B212, and B213, one or more methylene groups may be replaced by an ether group, -0-, in a way that two ether groups are separated by at least two consecutive methylene groups which may optionally be substituted, aromatic monohydroxy compounds B214 such as phenol, alkyl phenols which may be the known cresol and xylenol isomers, 1- and 2-hydroxynaphthalene, or homo- logues thereof, such as methyl, dimethyl, or ethyl substituted hydroxynaphthalenes , and dialkyl or arylalkyl ketoximes B215 such as butanonoxime and diethylketoxime and phenylmethylketoxime,

R¹ is the residue of a polyfunctional isocyanate Bll having n isocyanate groups,

0=C=N-R¹- (N=C=0)„__!,

R² is the residue of a polyfunctional isocyanate B12 having m isocyanate groups,

0=C=N-R²- (N=C=0)_m__x, where Bll and B12 may be identical or may be different from each other, and are independently selected from the group consisting of aromatic polyfunctional isocyanates, from heteroaromatic poly- functional isocyanates, from aliphatic polyf nctional isocyanates, and from mixed aromatic-aliphatic polyfunctional isocyanates such as meta-xylylene diisocyanate, and where n and m each can assume integer values of 2 or more, independently from the other in each case, preferably from 2 to 10, and where it is possible that one or more of the isocyanate groups in R¹ and/or in R² may have been consumed by reaction with a hydroxy functional compound under formation of a urethane group, or by reaction with an amino functional compound under formation of a urea group, and R³ can be the same as R, or can be different from R, and is the residue of a hydroxy functional compound B22 of formula R³-OH, selected from the group consisting of linear aliphatic monohydroxy compounds B221 having from 1 to 20 carbon atoms such as methanol, n- and sec . -butanol , 1-hexanol, decyl alcohol, tridecylalcohol , and stearylalcohol , branched aliphatic monohydroxy compounds B222 having from 4 to 20 carbon atoms, such as iso- and tert . -butanol , amyl alcohol, 2-ethyl-l-hexanol, and cyclic aliphatic monohydroxy compounds B223 having from 4 to 20 carbon atoms, such as hydroxy- cyclohexane, borneol and isoborneol, wherein in any of B221, B222, and B223, one or more methylene groups may be replaced by an ether group in a way that two ether groups -0- are separated by at least two consecutive methylene groups, which may optionally be substi^¬ tuted, aromatic monohydroxy compounds B224 such as phenol, alkyl phenols which may be the known cresol and xylenol isomers, 1- and 2-hydroxynaphthalene, and dialkyl or arylalkyl ketoximes B225 such as butanonoxime and diethylketoxime and phenylmethylketoxime .

Suitable aromatic polyfunctional isocyanates are 1 , 4-diisocyanato- benzene, 2,4- or 2 , 6-diisocyanatotoluene and mixtures of these iso- mers, 4 , 4 ' - or 2 , 4 ' -diisocyanatodiphenylmethane, 4 , 4 ' -diisocyanato- diphenylpropane- (2 , 2 ) , 1,2-, 1,4-, 2,3-, and 1 , 8-diisocyanato- naphthalene . Suitable heteroaromatic polyfunctional isocyanates are derivatives of melamine or guanamines having at least two isocyanate groups per molecule . Suitable mixed aromatic-aliphatic polyfunctional isocyanates are preferably alpha, alpha, alpha ' , alpha ' -tetramethyl- m- or -p-xylylene diisocyanate, and mixtures comprising two or more of these compounds . Suitable aliphatic polyfunctional isocyanates are 1,4-tetra- methylene diisocyanate, 1 , 6-hexamethylene diisocyanate, 1,5-diiso- cyanato-2-methyl-pentane, 1 , 8-octamethylene diisocyanate, 2,2,4- or 2,4, 4-trimethylhexamethylene-l , 12-diisocyanate, 1, 12-dodecamethy- lene diisocyanate, 1 , 4-diisocyanatocyclohexane, 3-isocyanatomethyl- 3 , 5 , 5-trimethylcyclohexyl isocyanate (isophorone diisocyanate, IPDI ) , 4,4' -diisocyanatodicyclohexylmethane, 4,4' -diisocyanatodi- cyclohexylpropane- (2 , 2 ) , 1 , 4-diisocyanatobenzene, 2,4- or 2,6-di- isocyanatotoluene and mixtures of these isomers, 4,4'- or 2,4'-di- isocyanatodiphenylmethane, 4,4' -diisocyanatodiphenylpropane- (2,2) , p-xylylene diisocyanate, alpha, alpha, alpha', alpha ' -tetramethyl- m- or -p-xylylene diisocyanate, and mixtures comprising these compounds .

It is preferred to use an aliphatic isocyanate in combination with ketoxime capping agents B215 and B225, or with phenolic capping agents B214 or B224, while aromatic isocyanates are best combined with aliphatic capping agents according to B211, B212, B213, B221, B222, and B223. The epoxides Al can be monoepoxides All or diepoxides A12. It is also possible to use higher functional epoxides A13 having three or more epoxide groups per molecule, in a mass fraction of up to 10 %, based on the sum of the masses of epoxide compounds. A higher amount of tri-or polyfunctional epoxides may lead to embrittlement of the coating prepared with the binder of the present invention. Suitable monoepoxides All are ethers of glycidol (2,3-epoxy- propanol) with monofunctional aliphatic alcohols having from 4 to 40 carbon atoms, and glycidyl esters of aliphatic monocarboxylic acids having from 5 to 20 carbon atoms, where preferably the alcohols or the acids have at least one tertiary or quaternary carbon atom, and also epoxyalkanes having from 4 to 40 carbon atoms. The epoxide functional compound A12 has two epoxide groups per molecule. Among the difunctional epoxide compounds, preferred are diepoxyalkanes , ethers of glycidol (2, 3-epoxypropanol) with dihydroxy compounds selected from dihydroxyalkanes having from 2 to 20 carbon atoms, which may also be branched or cyclic provided that the lower limit of the number of carbon atoms is 3 for branched and cyclic dihydroxyalkanes, from oligomeric and polymeric dihydroxy alkylene ethers

HO- [- (CH₂)_n-0-]_m- (CH₂)_n-OH with n = 2 to 4 and m = 1 to 1000, particularly polyoxyethylene glycol and polyoxypropylene glycol and also mixed ethers of these, and polyoxybutylene glycol, and from dihydroxyaromatic compounds having at least one aromatic ring, which aromatic compounds are preferably selected from the group consisting of resorcinol, hydro- quinone, the isomeric dihydroxynaphthalenes , bisphenol A, bisphenol F, alkylated bisphenol A such as tetramethyl bisphenol A, halo- genated bisphenol A, dihydroxy diphenyl, dihydroxybenzophenone, dihydroxy diphenyl sulphone, and dihydroxy diphenyl ether, esters of glycidol with organic alkylene diacids having from 1 to 40 carbon atoms in the alkylene residue which may be linear, branched or cyclic, particularly preferably dicarboxylic acids such as succinic acid, adipic acid, and dimeric fatty acids, and esters of aromatic diacids such as isophthalic or terephthalic acids. Especially preferred are the diglycidyl ethers of bisphenol A and bisphenol F and the so-called advancement products thereof which are made by reacting bisphenol A or bisphenol F with the diglycidyl ether of bisphenol A or bisphenol F.

Preferably, the amine A21 having at least one primary or secondary amino group has the amino group (s) bound to an aliphatic carbon atom, and has from 2 to 40 carbon atoms. The amine A21 may be an araliphatic amine such as m-xylylene diamine, a hydroxyamine A211 having at least one primary or secondary amino group and at least one hydroxyl group, such as ethanolamine, diethanolamine, dipropa- nolamine, 4-hydroxybutylamine, N-methyl ethanolamine, N-ethyl ethanolamine, an amine A212 having at least one primary and at least one tertiary amino group such as N, -dimethylaminopropyl- amine, N,N-diethylaminopropylamine, N- (2-aminoethyl) piperidine, N- (2-aminoethyl) pyrrolidine, and N- (2-aminoethyl) piperazine, or particularly preferred an amine A213 having at least two primary and at least one secondary amino group, such as diethylene triamine, triethylene tetramine, tetraethylene pentamine and pentaethylene hexamine, oligomeric or polymeric diaminopolyethylene imine having a degree of polymerisation of from 6 to 100, dipropylene triamine, and tripropylene tetramine, and N,N-bis-(4- aminobutyl ) -amine, N, ' -bis- ( 4-aminobutyl ) -1 , 4-diaminobutane, as well as N, -bis- ( 6-aminohexyl) -amine, and N, N ' -bis- ( 6-aminohexyl ) - 1 , 6-diaminohexane . It is also preferred to use mixtures of at least two of the amines as mentioned.

The phenolic compound A22 can be a mono- or di-hydroxy aromatic compound. Preferred are phenol itself, the isomeric cresols, parti^¬ cularly o- and p-cresol, and xylenols, particularly 2,6-xylenol, and among the dihydroxyaromatic compounds, resorcinol, hydro- quinone, dihydroxydiphenyl , dihydroxydiphenyl ether, dihydroxydi- phenylsulphone, dihydroxybenzophenone, 2, 2-bis- (4-hydroxyphenyl) propane (= bisphenol A), 2, 2-bis- (4-hydroxyphenyl) methane (= bis- phenol F) , and 2, 2-bis- (4-hydroxy-3, 5-dimethylphenyl) propane (= tetramethyl bisphenol A) , as well as other alkylated or halogenated derivatives of the compounds mentioned, and mixtures of at last two of these.

The organic acid A23 can be preferably an aliphatic monocarboxylic acid having from 2 to 40 carbon atoms, which can be linear, branched (with a minimum of 4 carbon atoms) or cyclic (with a minimum of 5 carbon atoms) , and may further preferably have at least one olefinic unsaturation . Particularly preferred are unsaturated fatty acids such as oleic acid, linolic acid, linolenic acid, palmitoleic acid, erucic acid, and ricinoleic acid, as well as mix^¬ tures of fatty acids made from naturally occurring sources, which mixtures preferably comprise a mass fraction of at least 20 %, par^¬ ticularly preferred of at least 30 %, of unsaturated fatty acids. Among the fatty acid mixtures obtained from natural oils, linseed oil fatty acid and tall oil fatty acid are especially preferred.

The amidoamine A3 has at least one primary or secondary amino group and at least one amide group, and is derived from fatty acids A31 having one carboxyl functional group and from 6 to 40 carbon atoms, preferably from 8 to 36 carbon atoms, and may also comprise ole^¬ finic double bonds in their molecules which are preferentially non- conjugated if there is more than one per molecule, and from amines A32 having at least two amino groups, at least one thereof being a primary amino group, which may be selected from amines A321 having at least one primary and at least one secondary amino group, such as N-methylethylene diamine, N- (2-aminoethyl) pyrrolidine, and N- (2-aminoethyl) piperazine, and from amines A322 having at least two primary amino groups, such as ethylene diamine, diethylene triamine, triethylene tetramine, tetraethylene pentamine and penta- ethylene hexamine, oligomeric or polymeric diaminopolyethylene imine having a degree of polymerisation of from 6 to 100, dipropy- lene triamine, and tripropylene tetramine, and N, -bis- (4-amino- butyl) -amine, N, ' -bis- (4-aminobutyl) -1, 4-diaminobutane, as well as N, -bis- ( 6-aminohexyl) -amine, and N, ' -bis- ( 6-aminohexyl ) -1 , 6- diaminohexane . Preferred fatty acids A31 are the saturated monocarboxylic acids caproic acid, enanthic acid, caprylic acid, pelargonic acid, capric acid, undecanoic acid, lauric acid, tridecanoic acid, myristic acid, pentadecanoic acid, palmitic acid, margaric acid, stearic acid, nonadecanoic acid, arachidic acid, behenic acid, lignoceric acid, cerotic acid, montanic acid, and melissic acid, the unsaturated acids myristoleic acid, palmitoleic alic, petroselinic acid, petroselaidic acid, oleic acid, elaidic acid, linoleic acid, linolelaidic acid, linolenic acid, linolenelaidic acid, gadoleic acid, arachidonic acid, erucic acid, brassidic acid, and clupanodonic acid. Mixtures of these acids, particularly those that are naturally occurring and commercially available in purified form or in broad cuts from naturally occurring vegetable oil fatty acid mixtures, such as tall oil, soy bean oil, cottonseed oil, castor oil, linseed oil, palm kernel oil, corn oil, peanut oil, rapeseed oil, sunflower oil, and cocoanut oil fatty acids, are also preferred .

The aqueous self-cross-linking binder is preferably made by the following process:

In the first step, a fatty acid amidoamine A3 is prepared from a fatty acid A31 and an amine A32 as defined supra. The amounts of the reactants A31 and A32 are chosen such that the fatty acid amidoamine A3 has at least one remaining primary or secondary amino group . These amino-functional fatty acid amidoamines A3 are then mixed in the second step with at least two different compounds of the class A2, and a first portion of the epoxide Al is added, which is in this second step preferably predominantly (i. e. with a mass fraction of more than 50 % of the epoxide compounds used in this step) a monoepoxide All, or a mixture of two or more monoepoxides , and the mixture thus obtained is heated to a temperature of preferably from 60 ^'C to 100 ^'C and reacted until no more epoxide groups can be detected. In the third step, in an optional preferred embodiment, a further quantity of at least one of the compounds according to A2 is then added, and then mandatorily, a second portion of the epoxide compound Al is added, which in this third step is preferably a diepoxide A12, optionally with admixture of an epoxide A13 having a functionality of more than two, and the reaction mass is treated at the same temperature as above until all epoxide groups have been consumed .

In a separate step, a curing agent is prepared from an at least difunctional isocyanate Bl and a capping agent B2 by first charging the capping agent B2 and admixing a catalyst, the mixture is heated and the isocyanate Bl is added in portions keeping the temperature constant, and reacting until the isocyanate groups are completely consumed .

In the fourth step, the curing agent formed in the separate step is added to the reaction mixture of step 3, homogenised well, and the resulting homogeneous mixture is cooled and dispersed in water to which a neutralisation agent has been added prior to the addition of the homogenised mixture.

In a further optional step, further diepoxide A12 is added and reacted again until all epoxide groups have been consumed.

A preferred reaction sequence provides that in the second step, only a portion of the amine A21 is added, while the remaining amine A21 is added before the third step.

It has been found in the experiments leading to the present invention that a ratio of the amounts of substance of monoepoxides All to diepoxides A12 of from 1:1.5 to 1:5 leads to the best corrosion protection. Preferred ratios are 1:2 to 1:4.5, and particularly preferred, 1:2.5 to 1:4.

Good corrosion protection can also be provided if the ratio of the amounts of substance for the two portions of diepoxide A12 in the third step and the optional step after step 4 are within the limits of from 10:1 to 4:1, preferably between from 9.5:1 to 5:1, and particularly preferred, between from 9:1 to 6:1. Preferably, there is no residual amount of amine hydrogen atoms in the binders left as these have all been converted to tertiary amino groups by reaction with the epoxides. Therefore, the amount of epoxides has to be chosen to at least convert all of the amino groups to tertiary amino groups.

The amount of monoepoxide All in the second step is preferably chosen such that from 4 % to 30 %, especially preferred from 6 % to 20 %, of all aminic NH groups are converted to beta-hydroxyamine structures by addition of monoepoxide All.

The hydroxyl number of the binders is preferably in the range of from 20 mg/g to 150 mg/g, particularly preferably from 30 mg/g to 120 mg/g.

Coatings prepared with the binders of this invention provide good corrosion protection to base metals, be it steel, aluminium, or zinc, to name only a few, and they exhibit good pigmnet wetting both with inorganic pigments such as ultramarine pigments, titanium dioxide, and iron oxide pigments, and also organic pigments, such as quinacridone and phthalocyanine pigments. A particularly important property is the low amount of organic compounds split off during curing. In combination with non- allophanate curing agents, a higher amount of blocked isocyanate has to be used to achieve the same degree of crosslinking; this leads both to an increase in the amount of volatile products evolved during the crosslinking reaction, and to a loss in stability of the dispersion in combination with the amide-modified epoxy amine adduct A of the present invention.

The invention is further illustrated by the following examples which are not intended to be limiting.

Examples

Example 1 Preparation of fatty acid amidoamines

A fatty acid amide containing amino groups was synthesised according to the following procedure:

215 g (1 mol) of bis-hexamethylene triamine (BHMTA) were heated to 40 ^°C. 560 g (2 mol) of tall oil fatty acid (TOFA) were added under stirring during fifteen minutes; thereafter the mixture was heated, profiting of the slight exotherm, to 150 ^'C within one hour. The water formed in the reaction was separated, and the mixture was held at 150 ^'C for a further three hours, and then heated to 180 ^'C over a period of two further hours. The reaction mixture was held at that temperature until an amine value (determined according to DIN 53 176, as the ratio of that mass m(KOH) of potassium hydroxide that consumes the same amount of acid for neutralisation as the sample under consideration, and the mass m(B) of that sample, or the mass of solid matter in the sample in the case of solutions or dispersions) of approximately 76 mg/g was reached, which corresponds to an amount of substance of 1 mol in this experiment. A waxy brown solid was obtained having an amine value of 75.3 mg/g and an acid value of 8.1 mg/g.

The acid value was determined according to DIN EN ISO 3682 (DIN 53 402), as the ratio of that mass jn(KOH) of potassium hydroxide which is needed to neutralise the sample under examination, and the mass 271(B) of this sample, or the mass of the solids in the sample in the case of a solution or dispersion; its customary unit is "mg/g".

Further fatty acid amides 1.2 to 1.5 were synthesised according to the same procedure, with kind and mass of educts (starting materials) as indicated in table 1. The following abbreviations are used in the row "kind" for amines ¹ and fatty acids ² :

BHMTA bis-hexamethylene triamine

DETA diethylene triamine

TETA triethylene tetramine

POFA peanut oil fatty acid, <M> = 280 g/mol

INA isononanoic acid, M = 158 g/mol TOFA tall oil fatty acid, <M> = 280 g/mol,

M denoting the molar mass, and <M> the number average molar mass the compounds supra.

Table 1 Fatty Acid Amidoamines

A comparative compound V (a hydroxy amine) was also synthesised by reaction of 1 mol of hexamethylene diamine and 2 mol of the glycidyl ester (available as ©Cardura E10P from Hexion Specialty Chemicals) of a mixture of branched decanoic acids (also referred to as "Neodecanoic Acid") . Example 2 Amide-modified epoxy resins

Binder Bl was synthesised according to the following procedure: 739 g (1 mol) of the amine-functional fatty acid amide 1.2 from Example 1 were mixed with 280 g (1 mol) of tall oil fatty acid and 215 g of bis-hexamethylene triamine (1 mol) and 1093 g of methoxy- propanol as solvent at 90 ^'C and stirred until a clear melt had formed. Within one hour, 774 g (3.1 mol) of the glycidyl ester of neodecanoic acid were added while holding the temperature between 85 ^'C and 90 ^'C by cooling. After one further hour of stirring at 85 ^° C at 85 ^'C, the following products were added in sequence: 968 g (4.24 mol) of bisphenol A (BA) , 206 g (1.96 mol) of di- ethanolamine (DOLA) , and 184 g (1.8 mol) of dimethylamino propylamine (DMAPA) . When a clear melt was obtained at 80 ^"C, a first portion of 3230 g (8.5 mol) of a liquid epoxide resin based on bisphenol A and having a molar mass of 380 g/mol were added, the temperature rising due to the heat of reaction to about 150 ^'C. The reaction mixture was held at 150 ^'C for about one hour until no unreacted epoxide groups were detectable. A dilution vessel was prepared by charging a mixture of 8800 g of deionised water and 450 g of an aqueous solution of acetic acid (having a concentration of 60 g/100 g, 3 mol), the resin solution was then added within thirty minutes under stirring. Temperature was then set to 70 ^°C, and stirring was continued for one further hour until a homogeneous dispersion was obtained. Water was added in portions to a final mass fraction of solids of 45 %. The dispersion thus obtained was heated to 80 ^°C, and a second portion of 400 g (1.05 mol) of the epoxy resin mentioned supra was added and the resulting mixture held under stirring at a temperature of from 70 ^'C to 80 ^" C until no free epoxide groups were detectable any more. The resulting product had a Staudinger index of 60 cmVg. Further binders were made according to table 2 :

The following abbreviations were used:

CE : ©Cardura E10 P (glycidyl ester of neodecanoic acid)

EP: bisphenol A diglycidyl ether (M = 380 g/mol)

m/g: mass of the component in g

n/mol: amount of substance of the component in mol Table 2: Amide-Modified Epoxy Resins

Exam Fatty Acid Components reactive towards Epoxy Resins pie Amidoamine epoxide groups

m/g n/mol Kind m/g n/mol Kind m/g n/mol Kind

2.1 739 1 1.2 280 1 TOFA 750 3 CE

215 1 BHMTA 3420 9 EP

935 4.1 BA

210 2 DOLA

184 1.8 DMAPA

2.2 739 1 1.1 560 2 TOFA 3230 8.5 EP

935 4.1 BA

210 2 DOLA

184 1.8 DMAPA

2.3 1340 2 1.4 912 4 BA 500 2 CE

210 2 DOLA 3230 8.5 EP

184 1.8 DMAPA

2.4 852 2 1.5 912 4 BA 500 2 CE

210 2 DOLA 3230 8.5 EP

184 1.8 DMAPA

2.5 766 2 1.3 560 2 TOFA 250 1 CE

935 4.1 BA 3230 8.5 EP

210 2 DOLA

184 1.8 DMAPA

2.6 739 1 1.1 560 2 TOFA 250 1 CE

935 4.1 BA 3230 8.5 EP

210 2 DOLA

184 1.8 DMAPA

2.7 616 1 V 560 2 TOFA 250 1 CE

935 4.1 BA 3230 8.5 EP

210 2 DOLA

184 1.8 DMAPA

2.8 739 1 1.1 560 2 TOFA 250 1 CE

935 4.1 BA 3230 8.5 EP

210 2 DOLA

184 1.8 DMAPA

2.9 739 1 1.1 560 2 TOFA 250 1 CE

935 4.1 BA 3230 8.5 EP

210 2 DOLA

184 1.8 DMAPA 1.1 to 1.5: Fatty acid amidoamines from Example 1

V is an adduct made of 1 mol of HDA and 2 mol of ©Cardura E10 P, see supra,

The resins prepared were neutralised and had the physico-chemical properties as shown in table 3:

Table 3 Neutralisation and Physico-chemical Properties of the

Resins

Binder Neutralisation agent Solid Mass Fraction of Viscosity at

(Acetic Acid) Re sin Solids 23 ^"C m/g Ji/mol m/g w/% n/mPa-s

2 .1 156 2.6 9841 38.2 620

2 .2 162 2.7 8600 38.1 430

2 .3 180 3 9366 37.8 380

2 .4 180 3 8668 40.4 522

2 .5 162 2.7 8996 36.3 627

2 .6 162 2.7 8957 39.7 583

2 .7 156 2.6 8773 39.5 433

2 .8 162 2.7 8957 39.7 583

2 .9 162 2.7 12256 40.1 338 η IS the usual symbol for the dynamic viscosity which is measured at a shear rate of 100 s ¹.

Example 3 Preparation of allophanate-containing isocyanate- functional crosslinking agents

1430 g (11 mol) of 2-ethyl hexanol and 3.1 g of sodium phenolate were charged in a glass vessel and heated to 80 ^"C. 1740 g (10 mol) of 2 , 4-toluylene diisocyanate were added in portions under cooling to keep the temperature in the range of from 80 ^°C to 85 ^'C. When the whole amount of diisocyanate had been added, the reaction mass was kept at from 80 ^'C to 90 ^°C until complete consumption of the isocyanate groups. An allophanate-containing oligomeric isocyanate having an average molar mass of 3170 g/mol and a specific content of crosslinking isocyanate groups of 6.33 mol/kg was obtained. Example 4 Comparative Crosslinking Agent

A comparative crosslinking agent was synthesised by reacting 134 g (1 mol) of trimethylolpropane with 851 g (2.8 mol) of a toluylene diisocyanate which was semi-blocked with 2-ethyl hexanol. This crosslinking agent was free of allophanate groups. It specific content of crosslinking isocyanate groups was 2.84 mol/kg.

Example 5 Coating Compositions

Mixtures were prepared from the binders 2.1 through 2.9, and crosslinking agents of Example 3 (according to the invention) and the comparative crosslinking agent of example 4. Binders 2.1 to 2.6, 2.8 and 2.9 are according to the invention, while binder 2.7 was made without the amide component. These mixtures are detailed in Table 4.

Table 4 Coating Compositions

Paint Binder Crosslinker Amount of Ratio of Sto-

Substance masses of ving of Isocya- solids of loss nate crosslingroups ker XL and

binder B

kind m(B) kind flj(XL) n (NCO) flj(XL) /m(B) w_ST

in g in g in mol in % in %

1 2.1 9841 Ex . 3 2952 18.7 30 13.5

2 2.2 8600 Ex . 3 2580 16.3 30 13.5

3 2.3 9366 Ex . 3 2810 17.8 30 13.5

4 2.4 8668 Ex . 3 2600 16.4 30 13.5

5 2.5 8996 Ex . 3 2699 17.1 30 13.5

6 2.6 8957 Ex . 3 2687 17.0 30 13.5

7 2.7 8773 Ex . 3 2632 16.6 30 13.5

8 2.8 8957 Ex . 4 2687 7.6 30 11.1

9 2.9 12256 Ex . 4 5986 17.0 49 18.1 flj(B) is the mass of solids in the binder

flj(XL) is the mass of solids in the crosslinking agent

w_ST :Stoving Loss, ratio of masses of volatiles split off during stoving and mass of coating composition solids in %

Example 6 Coating Test Results

For the coating compositions (paints) of example 5, the composition of which is given in table 4, the following tests were made: a) Sieve Test: 1 kg of the coating compositions were passed through a sieve having a mesh width of 28 ym, the amount of sediment was weighed and stated as ratio of mass of sediment to mass of paint, in mg/kg b) Appearance of coated substrate, using three different kinds of substrate, aluminium panels (bl), ©Gardobond test panels S26/6800 OC (steel, zinc coated and phosphatised) (b2), and (DGardobond test panels S26/6800 OC ( steel , electrolytically zinc coated) (b3) ; the substates were used as obtained, and rinsed with deionised water prior to coating

The ratings for appearance are:

"0" glossy, smooth

"1" silky gloss

"2" glossy, single pinholes

"3" matte

"4" matte, single pinholes

"5" matte, grainy c) Cross Hatch Test of coated substrate, using three different kinds of substrate, aluminium panels (bl), ©Gardobond test panels

S26/6800 OC (steel, zinc coated and phosphatised) (b2), and ©Gardobond test panels S26/6800 OC ( steel , electrolytically zinc coated) (b3) ; the substates were used as obtained, and rinsed with deionised water prior to coating. Rating is according to the norm, Method B of ASTM D3359. d) reverse impact test according to ISO 6272, using steel sheets, zinc coated and phosphatised, results are given in the commonly used non-SI units, and converted to SI units (1 in-lb = 0.113 J) e) salt spray test, where a steel sheet coated with zinc and phosphatised is subjected to salt spray according to DIN EN ISO 7253, degree of rust formation el classified as

"0" no rust staining

"1" single rust stains

"2" about 20 % of the surface are covered with rust stains

"3" more than 50 % of the surface are covered with rust stains "4" rust covers the whole surface, and e2 states the distance of the corrosion creep front from a scratch in the paint film.

Dry film thickness was 22 ym in all cases. The following test results were obtained with the paints (coating compositions) binders 1 to 9: Table 5 Coating tests

Paint 1 2 3 4 5 6 7 8 9

Sieve Test a 7 8 10 3 4 8 30 5 >100 in mg/kg

Appearance of bl 0 0 0 0 0 0 4 2 5

Coated b2 1 1 1 1 1 1 3 0 5

Surface

b3 1 1 1 1 1 1 3 0 5

Cross Hatch cl 0 0 0 0 0 2..3 0 3 2

Test c2 0 0 0 0 0 1 1..2 0..1 c3 0 0 0 0 0..1 2..2 2

Reverse d in J 9.0 9.0 9.0 9.0 9.0 9.0 9.0 1.1 5.7

Impact (in-lb)

Salt Spray el 1 1 1 1 1 1 1 2 2..3

Test e2 in mm 1 1 1..2 1..2 1..2 2 2 2 2..3

It can be seen that the surface appearance is improved by the use of amide-containing epoxy amine adducts as binders (paints 7, without amide; vs. paints 1 to 6, with amide) . The same is true for the results of the cross-hatch test.

Numbers in the table in the format "2 .. 3" mean that the value is between 2 and 3, etc.

Using a comparative crosslinking agent which does not comprise allophanate groups (Paint 8) in the same amount as the allophanate containing crosslinker (Paints 1 to 6) together with a binder comprising an amide component in the epoxy amine adduct gives much lower impact values, and marked reduced protection against corrosion, as evidenced by the salt spray test results. There is also worse performance in the cross-hatch test. If the amount of comparative crosslinker is increased according to the stoichiometry (Paint 9) , the impact is improved over that with paint 8, and so are the results of the cross-hatch test, but still not as good as in paints 1 to 6. It can also be noted that the surface appearance is gravely impaired, as well as the corrosion test results.

Claims

1. An aqueous stoving binder comprising a mixture AB of an amide- modified epoxy amine adduct A and a capped isocyanate B that has an allophanate as a structural element.

2. The aqueous stoving binder of claim 1 wherein the amide- modified epoxy amine adduct A is a reaction product of an epoxide functional compound Al, of an amidoamine A3 prepared from a fatty acid A31 and an amine A32 having at least two amino groups, at least one being a primary amino group, and of compounds A2 which are reactive towards epoxide groups which compounds A2 are selected from amines A21 having at least two amino groups, where at least one is a primary amino group, from phenolic compounds A22 having at least two phenolic hydroxy groups, and from organic acids A23, with the proviso that at least one amine A21 and at least one phenolic compound A22 are used in the reaction to prepare the adduct A.

3. The aqueous stoving binder of claim 1 wherein the capped isocyanate B has at least two capped isocyanate structures -NH-CO- OR and at least one allophanate structure, R^NH-CO-NR^CO-OR³, wherein

R is the residue of a hydroxy functional capping agent B21, also commonly referred to as blocking agent, R-OH, selected from the group consisting of linear aliphatic monohydroxy compounds B211 having from 1 to 20 carbon atoms, branched aliphatic monohydroxy compounds B212 having from 4 to 20 carbon atoms, and cyclic aliphatic monohydroxy compounds B213 having from 4 to 20 carbon atoms, wherein in any of B211, B212, and B213, one or more methylene groups may be replaced by an ether group, -0-, in a way that two ether groups are separated by at least two consecutive methylene groups which may optionally be substituted, aromatic monohydroxy compounds B214, and dialkyl or arylalkyl ketoximes B215, R¹ is the residue of a polyfunctional isocyanate Bll having n isocyanate groups,

0=C=N-R¹- (N=C=0) n-i, R² is the residue of a polyfunctional isocyanate B12 having m isocyanate groups,

0=C=N-R²- (N=C=0)_m__x, where Bll and B12 may be identical or may be different from each other, and are independently selected from the group consisting of aromatic polyfunctional isocyanates, from heteroaromatic poly- functional isocyanates, from aliphatic polyfunctional isocyanates, and from mixed aromatic-aliphatic polyfunctional isocyanates such as meta-xylylene diisocyanate, and where n and m each can assume integer values of 2 or more, independently from the other in each case, preferably from 2 to 10, and where it is possible that one or more of the isocyanate groups in R¹ and/or in R² may have been consumed by reaction with a hydroxy functional compound under formation of a urethane group, or by reaction with an amino functional compound under formation of a urea group, and R³ can be the same as R, or can be different from R, and is the residue of a hydroxy functional compound B22 of formula R³-OH, selected from the group consisting of linear aliphatic monohydroxy compounds B221 having from 1 to 20 carbon atoms, branched aliphatic monohydroxy compounds B222 having from 4 to 20 carbon atoms, and cyclic aliphatic monohydroxy compounds B223 having from 4 to 20 carbon atoms, wherein in any of B221, B222, and B223, one or more methylene groups may be replaced by an ether group in a way that two ether groups -0- are separated by at least two consecutive methylene groups, which may optionally be substituted, aromatic monohydroxy compounds B224, and dialkyl or arylalkyl ketoximes B225.

4. The aqueous stoving binder of claim 3 wherein the aromatic polyfunctional isocyanates are selected from the group consisting of 1 , 4-diisocyanatobenzene, 2,4- and 2 , 6-diisocyanatotoluene, mixtures of these isomers, 4,4'- and 2 , 4 ' -diisocyanatodiphenyl- methane, 4 , 4 ' -diisocyanatodiphenylpropane- (2 , 2 ) , 1,2-, 1,4-, 2,3-, and 1 , 8-diisocyanatonaphthalene .

5. The aqueous stoving binder of claim 3 wherein the heteroaromatic polyfunctional isocyanates are derivatives of melamine or guanamines having at least two isocyanate groups per molecule .

6. The aqueous stoving binder of claim 3 wherein the mixed aromatic-aliphatic polyfunctional isocyanates are selected from the group consisting of alpha, alpha, alpha ', alpha ' -tetramethyl- m- and -p-xylylene diisocyanate, and mixtures comprising at least two of these compounds.

7. The aqueous stoving binder of claim 3 wherein the aliphatic polyfunctional isocyanates are selected from the group consisting of 1 , 4-tetramethylene diisocyanate, 1 , 6-hexamethylene diisocyanate, 1, 5-diisocyanato-2-methyl-pentane, 1, 8-octamethylene diisocyanate, 2,2,4- and 2 , 4 , 4-trimethylhexamethylene-l , 12-diisocyanate, 1,12- dodecamethylene diisocyanate, 1 , 4-diisocyanatocyclohexane, 3- isocyanatomethyl-3 , 5, 5-trimethylcyclohexyl isocyanate (isophorone diisocyanate, IPDI), 4 , 4 ' -diisocyanatodicyclohexylmethane, 4,4'-di- isocyanatodicyclohexylpropane- (2,2), 1, 4-diisocyanatobenzene, 2, 4- or 2 , 6-diisocyanatotoluene and mixtures of these isomers, 4,4'- or 2,4' -diisocyanatodiphenylmethane, 4,4' -diisocyanatodiphenylpropane- (2,2), p-xylylene diisocyanate, alpha, alpha, alpha', alpha '- tetramethyl-m- or -p-xylylene diisocyanate, and mixtures comprising these compounds.

8. The aqueous stoving binder of claim 3 wherein an aliphatic isocyanate is used in combination with ketoxime capping agents B215 and B225, or with phenolic capping agents B214 or B224.

9. The aqueous stoving binder of claim 3 wherein an aromatic isocyanates is used combined with one or more aliphatic capping agents selected from the group consisting of B211, B212, B213, B221, B222, and B223 as detailed in claim 3.

10. The aqueous stoving binder of claim 2 wherein the epoxides Al are selected from the group consisting of monoepoxides All and diepoxides A12, wherein the monoepoxides All are selected from the group consisting of monoepoxyalkanes , ethers of glycidol with monofunctional aliphatic alcohols having from 4 to 40 carbon atoms, and glycidyl esters of aliphatic monocarboxylic acids having from 5 to 20 carbon atoms, and wherein the diepoxide A12 has two epoxide groups per molecule and is selected from the group consisting of diepoxyalkanes , ethers of glycidol with dihydroxy compounds selected from dihydroxyalkanes having from 2 to 20 carbon atoms, from oligomeric and polymeric dihydroxy alkylene ethers

HO- [- (CH₂)_n-0-]_m- (CH₂)_n-OH

with n = 2 to 4 and m = 1 to 1000, and from dihydroxyaromatic compounds having at least one aromatic ring, esters of glycidol with organic arylene diacids and alkylene diacids having each from 1 to 40 carbon atoms in the arylene or alkylene residue which latter may be linear, branched or cyclic.

11. The aqueous stoving binder of claim 2 wherein the amine A21 has at least one primary or secondary amino group which are bound to an aliphatic carbon atom, and has from 2 to 40 carbon atoms.

12. The aqueous stoving binder of claim 2 wherein the phenolic compound A22 is a mono- or di-hydroxy aromatic compound.

13. The aqueous stoving binder of claim 2 wherein the organic acid A23 is a saturated or an unsaturated aliphatic monocarboxylic acid having from 2 to 40 carbon atoms.

14. The aqueous stoving binder of claim 2 wherein the amidoamine A3 has at least one primary or secondary amino group and at least one amide group, and is derived from saturated or unsaturated fatty acids A31 having from 6 to 40 carbon atoms, and from amines A32 having at least two amino groups, and at least one being a primary amino group, selected from amines A321 having at least one primary and at least one secondary amino group, and from amines A322 having at least two primary amino groups.

15. A process to make an aqueous stoving binder comprising the steps of

in the first step, a fatty acid amidoamine A3 is prepared from a fatty acid A31 and an amine A32 having at least two amino groups, at least one being a primary amino group, wherein the amounts of the reactants A31 and A32 are chosen such that the amide A3 has at least one remaining primary or secondary amino group,

mixing these amino-functional fatty acid amides A3 in the second step with at least two different compounds of the class A2 selected from amines A21 having at least two amino groups, where at least one is a primary amino group, from phenolic compounds A22 having at least two phenolic hydroxy groups, and from organic acids A23, with the proviso that at least one amine A21 and at least one phenolic compound A22 is used, and a first portion of a monofunctional epoxide Al is added, and the mixture thus obtained is reacted until no more epoxide groups can be detected,

in an optional step, a further quantity of one of the compounds according to A2 is then added, and then,

in a third step, a second portion of the epoxide compound Al is added, and the reaction mass is reacted as above until all epoxide groups have been consumed,

in a separate step, a curing agent is prepared from an at least difunctional isocyanate Bl and a capping agent B2 by first charging the capping agent B2 and admixing a catalyst, the mixture is heated and the isocyanate Bl is added in portions keeping the temperature constant, and reacting until the isocyanate groups are completely consumed,

in the fourth step, the curing agent formed in the separate step is added to the reaction mixture, homogenised well, and the resulting homogeneous mixture is cooled and dispersed in water to which a neutralisation agent has been added prior to the addition of the homogenised mixture, and in a further optional step, diepoxide A12 is added to the aqueous dispersion formed in the fourth step and reacted again until all epoxide groups have been consumed.