WO2013033153A1 - Preparation of inorganic samples by fusion - Google Patents
Preparation of inorganic samples by fusion Download PDFInfo
- Publication number
- WO2013033153A1 WO2013033153A1 PCT/US2012/052783 US2012052783W WO2013033153A1 WO 2013033153 A1 WO2013033153 A1 WO 2013033153A1 US 2012052783 W US2012052783 W US 2012052783W WO 2013033153 A1 WO2013033153 A1 WO 2013033153A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- mold
- sample
- mix
- crucible
- inert gas
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Ceased
Abstract
Description
Claims