WO2014135999A1 - PROCÉDÉ DE RÉALISATION D'UNE TÔLE À REVÊTEMENT ZnAl AVEC UN ESSORAGE OPTIMISÉ, TÔLE, PIÈCE ET VÉHICULE CORRESPONDANTS - Google Patents

PROCÉDÉ DE RÉALISATION D'UNE TÔLE À REVÊTEMENT ZnAl AVEC UN ESSORAGE OPTIMISÉ, TÔLE, PIÈCE ET VÉHICULE CORRESPONDANTS Download PDF

Info

Publication number
WO2014135999A1
WO2014135999A1 PCT/IB2014/058879 IB2014058879W WO2014135999A1 WO 2014135999 A1 WO2014135999 A1 WO 2014135999A1 IB 2014058879 W IB2014058879 W IB 2014058879W WO 2014135999 A1 WO2014135999 A1 WO 2014135999A1
Authority
WO
WIPO (PCT)
Prior art keywords
metal coating
sheet
less
equal
μηι
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/IB2014/058879
Other languages
English (en)
Inventor
Jean-Michel Mataigne
Didier Dauchelle
Florence Bertrand
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ArcelorMittal Investigacion y Desarrollo SL
Original Assignee
ArcelorMittal Investigacion y Desarrollo SL
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Family has litigation
First worldwide family litigation filed litigation Critical https://patents.darts-ip.com/?family=48095906&utm_source=google_patent&utm_medium=platform_link&utm_campaign=public_patent_search&patent=WO2014135999(A1) "Global patent litigation dataset” by Darts-ip is licensed under a Creative Commons Attribution 4.0 International License.
Priority to UAA201504705A priority Critical patent/UA114936C2/uk
Priority to EP14706122.0A priority patent/EP2906734B1/fr
Priority to ES14706122T priority patent/ES2922948T3/es
Priority to KR1020157035274A priority patent/KR20160003293A/ko
Priority to MA38092A priority patent/MA38092B1/fr
Priority to US14/442,955 priority patent/US10041162B2/en
Priority to DE14706122.0T priority patent/DE14706122T1/de
Priority to EP23210177.4A priority patent/EP4299782A3/fr
Priority to PL14706122.0T priority patent/PL2906734T3/pl
Priority to BR112015011189-0A priority patent/BR112015011189B1/pt
Priority to MX2015006180A priority patent/MX386534B/es
Priority to RU2015118412A priority patent/RU2631220C2/ru
Priority to GB1422248.3A priority patent/GB2517622B/en
Application filed by ArcelorMittal Investigacion y Desarrollo SL filed Critical ArcelorMittal Investigacion y Desarrollo SL
Priority to CN201480003066.4A priority patent/CN104812923B/zh
Priority to JP2015552195A priority patent/JP6009100B2/ja
Priority to KR1020157012780A priority patent/KR101598326B1/ko
Priority to DE112014000102.3T priority patent/DE112014000102T5/de
Priority to KR1020167025914A priority patent/KR20160114732A/ko
Priority to CA2892007A priority patent/CA2892007C/fr
Priority to IN4084DEN2015 priority patent/IN2015DN04084A/en
Publication of WO2014135999A1 publication Critical patent/WO2014135999A1/fr
Priority to ZA2015/03173A priority patent/ZA201503173B/en
Anticipated expiration legal-status Critical
Priority to US15/825,994 priority patent/US10119187B2/en
Priority to US15/826,037 priority patent/US10745790B2/en
Priority to US16/874,608 priority patent/US11572613B2/en
Priority to US18/068,904 priority patent/US12606898B2/en
Priority to US19/344,496 priority patent/US20260022444A1/en
Ceased legal-status Critical Current

Abstract

Dans ce procédé, l'une au moins des équations (A, B) suivantes est satisfaite : où : Z est la distance entre la tôle (1) et la buse (17) le long de la direction principale d'éjection (E), Z étant exprimée en mm, d est la hauteur moyenne de la sortie (25) de la buse (17) le long du sens (S) de défilement de la tôle (1) devant la buse (17), d étant exprimée en mm, V est la vitesse de défilement de la tôle (1) devant la buse (17), V étant exprimée en m. s-1, P est la pression du gaz d'essorage dans la buse (17), P étant exprimée en N.m-2, et fO2 est la fraction volumique d'oxygène dans le gaz d'essorage.

Description

Procédé de réalisation d'une tôle à revêtement ZnAI avec un essorage optimisé, tôle, pièce et véhicule correspondants
La présente invention concerne un procédé de réalisation d'une tôle comprenant un substrat en acier dont au moins une face est revêtue par un revêtement métallique comprenant de l'Ai, le reste du revêtement métallique étant du Zn, des impuretés inévitables et éventuellement un ou plusieurs éléments additionnels choisis parmi Si, Sb, Pb, Ti, Ca, Mn, Sn, La, Ce, Cr, Zr, ou Bi, la teneur en poids de chaque élément additionnel dans le revêtement métallique étant inférieure à 0,3%, le revêtement métallique ayant une teneur en poids d'aluminium comprise entre 0,2 et 0,7%, le procédé comprenant au moins des étapes de :
- fourniture du substrat,
- dépôt d'un revêtement métallique sur au moins une face par trempe du substrat dans un bain pour obtenir la tôle,
- essorage du revêtement métallique par au moins une buse projetant par au moins une sortie un gaz d'essorage sur le revêtement métallique, la tôle défilant devant la buse et le gaz étant éjecté de la buse selon une direction principale d'éjection, et
- solidification du revêtement métallique.
Une telle tôle est plus particulièrement destinée à la fabrication de pièces de carrosserie pour un véhicule terrestre à moteur tel qu'un véhicule automobile.
La tôle est alors découpée et déformée pour réaliser des pièces qui sont assemblées pour former la carrosserie ou caisse.
Cette caisse est ensuite revêtue par un film de peinture (ou système peinture), lequel assure un bon aspect de surface et participe, avec le revêtement métallique à base de zinc, à la protection contre la corrosion.
Les revêtements à base de zinc des tôles présentent ce qu'on appelle une ondulation de leurs surfaces extérieures, qui ne peut actuellement être compensée que par des épaisseurs importantes de peinture, sous peine d'avoir un aspect dit de « peau d'orange » inacceptable pour des pièces de carrosserie.
L'ondulation W (waviness en anglais) de la surface extérieure d'un revêtement est une irrégularité géométrique douce, pseudopériodique, d'assez grande longueur d'onde (0,8 à 10 mm) que l'on distingue de la rugosité R qui correspond aux irrégularités géométriques de faibles longueurs d'ondes.
Dans la présente invention, la moyenne arithmétique Wa du profil d'ondulation, exprimée en μηι, a été retenue pour caractériser l'ondulation de la surface extérieure d'un revêtement de tôle, et les mesures d'ondulation ont été réalisées avec un seuil de coupure de 0,8 mm et désignées par Wa0,8.
Une diminution de l'ondulation Wa0,8 peut permettre de réduire l'épaisseur du film de peinture utilisé pour atteindre une qualité donnée d'aspect peint ou, à épaisseur constante de film de peinture, d'améliorer la qualité de l'aspect peint.
Le but de l'invention est donc de fournir un procédé de réalisation d'une tôle, comprenant un substrat dont au moins une face a été revêtue au trempé par un revêtement métallique à base de zinc et comprenant entre 0,2 et 0,7% en poids d'AI, la surface extérieure du revêtement métallique ayant une ondulation Wa0,8 réduite.
A cet effet, l'invention a pour objet un procédé selon la revendication 1 .
Le procédé peut également comprendre les caractéristiques des revendications 2 à 7, prises isolément ou en combinaison.
L'invention a également pour objet une tôle selon la revendication 9.
La tôle peut également comprendre les caractéristiques des revendications 10 et 1 1 , prises isolément ou en combinaison.
L'invention a également pour objet une pièce selon la revendication 12.
La pièce peut également comprendre les caractéristiques des revendications 13 à 17, prises isolément ou en combinaison.
L'invention a également pour objet un véhicule selon la revendication 18.
L'invention va être illustrée par des exemples donnés à titre indicatif, et non limitatif, et en référence aux figures annexées sur lesquelles :
- la figure 1 est une vue schématique en coupe illustrant la structure d'une tôle selon l'invention,
- la figure 2 est une vue schématique de côté illustrant un creuset et des buses d'essorage pour réaliser la tôle de la figure 1 ,
- la figure 3 est une vue partielle, schématique et agrandie de la partie cerclée III de la figure 2, et
- la figure 4 est une vue schématique prise selon la flèche IV de la figure 3, et illustrant la forme de la sortie de la buse de la figure 3.
La tôle 1 de la figure 1 comprend un substrat 3 en acier recouvert sur chacune de ses deux faces 5 par un revêtement métallique 7.
On observera que les épaisseurs relatives du substrat 3 et des différentes couches le recouvrant n'ont pas été respectées sur la figure 1 afin de faciliter la représentation.
Les revêtements 7 présents sur les deux faces 5 sont analogues et un seul sera décrit en détail par la suite. En variante (non-représentée), seule une des faces 5 présente un revêtement 7. Le revêtement 7 a généralement une épaisseur inférieure ou égale à 25 μηι et vise à protéger le substrat 3 contre la corrosion.
Le revêtement 7 comprend du zinc et de l'aluminium. La teneur en poids d'aluminium du revêtement métallique 7 est comprise entre 0,2 et 0,7%, de préférence entre 0,2 et 0,6%, et de préférence encore entre 0,2 et 0,5%. Comme indiqué ci-dessous, les bornes de ces plages de teneur d'aluminium sont supérieures à celles du bain utilisé pour réaliser le revêtement 7. Ceci s'explique par la formation d'intermétalliques à la jonction entre le substrat 3 et le revêtement 7 qui conduit à une augmentation de la teneur en aluminium dans le revêtement 7.
Pour réaliser la tôle 1 , on peut par exemple procéder comme suit.
On utilise un substrat 3 sous forme d'une bande obtenue par exemple par laminage à chaud puis à froid.
De préférence, pour le laminage à froid, on commence par laminer à froid le substrat 3 avec un taux de réduction généralement compris entre 60 et 85%, de manière à obtenir un substrat 3 d'épaisseur comprise par exemple entre 0,2 et 2 mm.
Dans un mode de réalisation préféré, on veille à ce qu'au moins la dernière passe du laminage à froid soit réalisée avec des cylindres de travail dits « lisses », c'est à dire des cylindres rectifiés et non gravés, dont les surfaces de travail présentent une rugosité Ra2,5, c'est-à-dire mesurée avec un seuil de coupure à 2,5 mm, inférieure à 0,5 μηι.
On rappelle que les cylindres de travail sont les cylindres du laminoir directement en contact du substrat 3 pour assurer sa déformation. On désigne par le terme surface de travail leurs surfaces en contact du substrat 3.
Les cylindres de travail lisses seront présents au moins dans la ou les dernière(s) cage(s) du laminoir lorsque l'on considère le sens de défilement du substrat 3 dans le laminoir.
L'utilisation de cylindres de travail lisses au moins pour la dernière passe permet de mieux contrôler l'ondulation Wa0,8 d'une part de la tôle 1 obtenue ultérieurement par revêtement du substrat 3 et d'autre part des pièces que l'on peut produire en déformant la tôle 1 .
En particulier, un tel laminage à froid permet de réduire l'ondulation Wa0,8 par rapport à un laminage ne faisant appel qu'à des cylindres à plus forte rugosité, gravés soit par gravillonnage, soit par décharge électrique (cylindres dits EDT, Electron Discharge Texture en anglais), soit encore par faisceau d'électrons (cylindres dits EBT, Electron Beam Texture en anglais). Le substrat 3 laminé à froid peut ensuite subir un recuit réalisé de manière conventionnelle dans un four de recuit sous atmosphère réductrice, en vue de le recristalliser après l'écrouissage qu'il a subi lors de l'opération de laminage à froid.
Le recuit de recristallisation permet en outre d'activer les faces 5 du substrat 3 afin de favoriser les réactions chimiques nécessaires à l'opération ultérieure de trempé.
Selon la nuance de l'acier, le recuit de recristallisation est effectué à une température comprise entre 650 et 900Ό pendant un temps nécessaire à la recristallisation de l'acier et à l'activation des faces 5.
Le substrat 3 est ensuite refroidi à une température voisine de celle d'un bain 13 contenu dans un creuset 15.
La composition du bain 13 est à base de zinc et contient entre 0,1 et 0,5% en poids d'aluminium, de préférence entre 0,1 et 0,4%, et de préférence encore entre 0,1 et 0,3%.
La composition du bain 13 peut également contenir jusqu'à 0,3% en poids d'éléments optionnels d'addition tels que Si, Sb, Pb, Ti, Ca, Mn, Sn, La, Ce, Cr, Ni, Zr ou Bi.
Ces différents éléments peuvent permettre, entre autres, d'améliorer la résistance à la corrosion du revêtement ou bien sa fragilité ou son adhésion, par exemple.
L'homme du métier qui connaît leurs effets sur les caractéristiques du revêtement saura les employer en fonction du but complémentaire recherché. On a également vérifié que ces éléments n'interféraient pas avec la maîtrise de l'ondulation obtenue par le procédé selon l'invention.
Enfin, le bain 13 peut contenir des impuretés inévitables provenant des lingots d'alimentation du creuset ou bien encore du passage du substrat 3 dans le bain 13. On pourra ainsi citer notamment, le fer.
Après passage dans le bain 13, le substrat 3 est revêtu sur ses deux faces 5 par les revêtements 7 pour obtenir la tôle 1 .
Comme illustré par la figure 2, la tôle 1 est ensuite soumise à un essorage au moyen de buses 17 placées de part et d'autre de la tôle 1 et qui projettent un gaz d'essorage, par exemple de l'air ou un gaz inerte, vers les surfaces extérieures 21 des revêtements 7. Le gaz d'essorage est éjecté de chaque buse 17 le long d'une direction principale d'éjection E. Les directions principales d'éjection E de chaque buse 17 sont matérialisées en pointillés sur les figures 2 et 3.
Dans l'exemple représenté, les directions E sont horizontales et orthogonales à la tôle 1 . Dans d'autres modes de réalisation, les directions E peuvent avoir d'autres inclinaisons par rapport à la tôle 1 . La vitesse V de défilement du substrat 3 sur la ligne de production utilisée et donc devant les buses 17 est en général comprise entre 80m/min et 300 m/min, et elle est de préférence supérieure à 120 m/min, voire 150m/min.
Afin de limiter l'oxydation des revêtements 7, on peut prévoir un caisson de confinement 23 pour confiner l'atmosphère autour de la tôle 1 en aval des buses 17. Le terme aval s'entend ici par rapport au sens de défilement S de la tôle 1 en regard des buses 17.
Le caisson de confinement 23 peut en variante se prolonger vers l'amont jusqu'à la surface du bain 13 ou jusqu'à une position intermédiaire entre les buses 17 et la surface du bain 13.
Dans certaines variantes, l'installation peut ne pas comprendre de caisson de confinement.
Dans l'exemple décrit ci-dessus, les buses 17 ont des structures, des positionnements par rapport à la tôle 1 qui sont analogues et elles fonctionnent avec des réglages analogues. Ainsi, seule la buse 17 droite de la figure 2 sera décrite ci-dessous, par référence à la figure 3.
En variante, les buses 17 peuvent avoir des structures différentes, des positions différentes et/ou fonctionner avec des réglages différents. On peut également ne prévoir une buse que d'un côté de la tôle 1 .
La buse 17 présente une sortie 25 par laquelle le gaz d'essorage est éjecté vers la surface extérieure 21 du revêtement 7 placé en regard. Différentes formes extérieures sont envisageables pour la buse 17.
La sortie 25 de la buse 17 est disposée à une distance de Z de la tôle 1 le long de la direction principale d'éjection E. Comme illustré par la figure 4, la sortie 25 se présente généralement sous forme d'une fente qui s'étend, perpendiculairement au sens de défilement S et au plan de la figure 3, sur une largeur L au moins égale à la largeur de la tôle 1 .
Généralement, la hauteur de la sortie 25, c'est-à-dire sa dimension parallèlement au sens S de défilement de la tôle 1 devant la buse 17, est constante comme illustré par la figure 4. Cela étant, dans certaines variantes, cette hauteur peut varier sur la largeur de la sortie 25. Ainsi, la sortie 25 peut avoir par exemple une forme légèrement évasée vers ses extrémités (forme de nœud papillon).
Afin de tenir compte de ces éventuelles variations de hauteur et des différents modes de réalisation possibles, on considérera par la suite la hauteur moyenne d de la sortie 25 sur sa largeur L. La pression du gaz d'essorage dans la buse 17 est notée P et la fraction volumique d'oxygène dans le gaz d'essorage est notée f02.
Selon l'invention, l'une au moins des équations suivantes est respectée :
— + 181nf— | < 81nf— 1 - 27,52 (A) d J y
Figure imgf000008_0001
ou :
Z est exprimée en mm
d est exprimée en mm
V est exprimée en m. s"1
P est exprimée en N.m"2
En d'autres termes, si l'équation (A) n'est pas respectée, il faut que l'équation (B) le soit et vice versa. Les équations (A) et (B) peuvent également être simultanément respectées.
Généralement, les paramètres V et d sont imposés par la ligne de production utilisée. Il ne reste donc plus que Z et P, voire f02, à ajuster pour satisfaire aux exigences ci-dessus.
Des paramètres ainsi fixés permettent d'atteindre, après solidification des revêtements 7 et avant éventuel skin-pass, une ondulation Wa0,8 inférieure ou égale à 0,55 μηι comme illustré par l'exemple 1 ci-dessous.
De manière encore plus avantageuse, l'une au moins des équations suivantes est respectée :
+ 181n[¾ < 81nW -36,32 (C)
Figure imgf000008_0002
ou :
Z est exprimée en mm
d est exprimée en mm
V est exprimée en m.s"
P est exprimée en N.m En d'autres termes, si l'équation (C) n'est pas respectée, il faut que l'équation (D) le soit et vice versa. Les équations (C) et (D) peuvent également être simultanément respectées.
Si les paramètres Z, d, V, P et f02 satisfont à l'équation (C) et/ou à l'équation (D) alors on atteint, après solidification des revêtements 7 et avant éventuel skin-pass, une ondulation Wa0,8 inférieure ou égale à 0,35 μηι .
On laisse refroidir ensuite les revêtements 7 de façon contrôlée pour qu'ils se solidifient.
Comme indiqué précédemment, à l'issue de ces refroidissements 7 les surfaces extérieures 21 des revêtements 7 ont des ondulations Wa0,8 inférieure à 0,55 μηι, voire inférieure à 0,35 μηι .
En variante, un brossage peut être effectué pour enlever le revêtement 7 déposé sur une face 5 de sorte qu'une seule des faces 5 du substrat 3 sera en définitive revêtue par un revêtement 7.
Lorsque les revêtements 7 sont complètement refroidis, la tôle 1 peut subir une opération de skin-pass pour conférer aux surfaces extérieures 21 des revêtements 7 une texture facilitant la mise en forme ultérieure de la tôle 1 .
En effet, l'opération de skin-pass permet de transférer aux surfaces extérieures 21 des revêtements 7 de la tôle 1 une rugosité suffisante pour que sa mise en forme s'effectue dans de bonnes conditions, en favorisant une bonne rétention de l'huile appliquée sur la tôle 1 avant sa mise en forme. Le taux d'allongement de la tôle 1 lors de l'opération de skin-pass est généralement compris entre 0,5 et 2%.
De préférence, l'opération de skin-pass permettra de conserver aux surfaces extérieures 21 des revêtements 7 une ondulation Wa0,8 inférieure à 0,55 μηι, et de préférence inférieure à 0,35 μηι .
Dans une première variante, l'opération de skin-pass sera réalisée avec des cylindres de travail EDT dont les surfaces de travail présentent une rugosité Ra2,5 comprise entre 2,05 et 2,95 μηι. Si le taux d'allongement lors de l'opération de skin-pass est inférieur ou égal à 1 ,1 %, la rugosité Ra2,5 des surfaces de travail des cylindres de travail EDT sera de préférence comprise entre 2,50 et 2,95 μηι. Si le taux d'allongement lors de l'opération de skin-pass est supérieur ou égal à 1 ,1 %, la rugosité Ra2,5 des surfaces de travail des cylindres de travail EDT sera de préférence comprise entre 2,05 et 2,50 μηι.
Dans une autre variante, l'opération de skin-pass sera réalisée avec des cylindres de travail EBT dont les surfaces de travail présentent une rugosité Ra2,5 comprise entre 2,90 et 4,10 μηι. Si le taux d'allongement lors de l'opération de skin-pass est inférieur ou égal à 1 ,1 %, la rugosité Ra2,5 des surfaces de travail des cylindres de travail EBT sera de préférence comprise entre 3,50 et 4,10 μηι. Si le taux d'allongement lors de l'opération de skin-pass est supérieur ou égal à 1 ,1 %, la rugosité Ra2,5 des surfaces de travail des cylindres de travail EBT sera de préférence comprise entre 2,90 et 3,50 μηι.
L'opération de skin-pass est généralement réalisée pour une tôle 1 destinée à la fabrication de pièces de carrosserie pour véhicules automobiles.
Lorsque la tôle 1 est destinée à la fabrication d'appareils électroménagers, par exemple, on ne procède pas à cette opération supplémentaire.
La tôle 1 skin-passée ou non peut ensuite être découpée puis mise en forme, par exemple par emboutissage, pliage ou profilage, pour former une pièce que l'on peut ensuite mettre en peinture pour former, sur chaque revêtement 7, un film de peinture (ou système peinture).
Dans le cas des pièces pour les appareils électroménagers, on peut aussi soumettre éventuellement les films de peinture à un recuit par des moyens physiques et/ou chimiques, connus en eux-mêmes.
A cet effet, on peut faire passer la pièce peinte au travers d'un four à air chaud ou à induction, ou encore sous des lampes UV ou sous un dispositif diffusant des faisceaux d'électrons.
Après déformation, les surfaces extérieures des revêtements 7 de la pièce ont une ondulation Wa0,8 inférieure ou égale à Ο,ΘΟμηι, voire inférieure ou égale à 0,45μηι, voire inférieure ou égale à 0,43μηι, voire 0,41 μηι voire encore 0,37μηι.
Cette ondulation pourra par exemple être mesurée après déformation equi-biaxiale de 3,5%.
La maîtrise de l'ondulation Wa0,8 avant éventuel skin-pass et après éventuel skin- pass à des valeurs inférieures ou égales à 0,55μηι, respectivement 0,35μηι, comme décrit ci-dessus permet de maîtriser l'ondulation Wa0,8 après déformation à des valeurs inférieures ou égales à Ο,ΘΟμηι, respectivement 0,45μηι, 0,43μηι, 0,41 μηι voire 0,37μηι.
Pour les applications automobiles, après phosphatation, on trempe chaque pièce dans un bain de cataphorèse, et on applique successivement, une couche de peinture d'apprêt, une couche de peinture de base, et éventuellement une couche de vernis de finition.
Avant d'appliquer la couche de cataphorèse sur la pièce, celle-ci est préalablement dégraissée puis phosphatée de manière à assurer l'adhérence de la cataphorèse.
La couche de cataphorèse assure à la pièce une protection complémentaire contre la corrosion. La couche de peinture d'apprêt, généralement appliquée au pistolet, prépare l'apparence finale de la pièce et la protège contre le gravillonnage et contre les UV. La couche de peinture de base confère à la pièce sa couleur et son apparence finale. La couche de vernis confère à la surface de la pièce une bonne résistance mécanique, une résistance contre les agents chimiques agressifs et un bon aspect de surface.
Généralement, le poids de la couche de phosphatation est compris entre 1 ,5 et 5 g/m2.
Les films de peinture mis en œuvre pour protéger et garantir un aspect de surface optimal aux pièces, comprennent par exemple une couche de cataphorèse de 15 à 25 μηι d'épaisseur, une couche de peinture d'apprêt de 35 à 45 μηι d'épaisseur, et une couche de peinture de base de 40 à 50 μηι d'épaisseur.
Dans les cas, où les films de peinture comprennent en outre une couche de vernis, les épaisseurs des différentes couches de peinture sont généralement les suivantes : couche de cataphorèse : entre 15 et 25μηι, de préférence inférieure à 20μηι, couche de peinture d'apprêt : inférieure à 45μηι,
couche de peinture de base : inférieure à 20μηι, et
couche-de vernis : inférieure à 55 μηι.
Les films de peinture pourront également ne pas comprendre de couche de cataphorèse, et ne comprendre qu'une couche de peinture d'apprêt et une couche de peinture de base et éventuellement une couche de vernis.
De préférence, l'épaisseur totale des films de peinture sera inférieure à 120 μηι voire 100 μηι.
L'invention va à présent être illustrée par des essais donnés à titre indicatif et non limitatif.
Exemple 1 - influence de la fraction volumique fO?
Les essais réalisés dans cet exemple visent à montrer l'influence positive du respect des équations (A) et/ou (B), voire (C) et/ou (D).
Le tableau I ci-dessous détaille les conditions d'une série d'essais menés avec des valeurs différentes de Z, d, V, P et f02 et rapporte les ondulations Wa0,8 mesurées avant skin-pass, NSKP signifiant non skin-passé.
La procédure de mesure de l'ondulation Wa0,8 consiste à acquérir par palpage mécanique (sans patin) un profil de tôle d'une longueur de 50 mm, à 45°de la direction de laminage. On retranche au signal obtenu par palpage l'approximation de sa forme générale par un polynôme de degré au moins 5. On sépare ensuite l'ondulation Wa et la rugosité moyenne arithmétique Ra par un filtre gaussien en appliquant un cutt-off de 0,8 mm.
Les colonnes de droite précisent, pour chaque essai, si les paramètres satisfaisaient aux équations (A), (B), (C) et (D). Essais Wa0,8 Eq (A) Eq (B) Eq (C) Eq (D)
Z d V P NSKP
(mm) (mm) (m/min) (N/m2) f02 (Mm)
1 9 1 ,2 150 38800 0,21 0,36 oui oui non non
2 1 1 1 ,2 150 48200 0,21 0,47 oui oui non non
3 7 1 ,2 150 26300 1 .10 0,27 oui oui oui oui
4 9 1 ,2 150 38800 1 .10 0,31 oui oui non oui
5 13 1 ,2 150 59000 1 .10 0,44 non oui non non
6 8 1 120 33100 0,21 0,43 oui oui non non
7 10 1 120 40700 0,21 0,50 oui oui non non
8 14 1 120 60900 0,21 0,84 non non non non
9 6,5 1 120 32600 1 .10 0,31 oui oui oui oui
10 10 1 120 52000 1 .10 0,41 oui oui non non
1 1 14 1 120 64900 1 .10 0,66 non non non non
12 8 1 ,5 100 22400 1 .10 0,31 oui oui oui oui
13 15 1 ,5 100 40800 1 .10 0,37 oui oui non non
Ainsi, l'utilisation de paramètres satisfaisant l'équation (A) et/ou (B) permet d'atteindre des ondulations avant skin-pass Wa0,8 inférieure à 0,55 μηι.
L'utilisation de paramètres satisfaisant l'équation (C) et/ou (D) permet d'atteindre des ondulations avant skin-pass Wa0,8 encore plus faibles et inférieures ou égales à 0,35 μηι.
Des ondulations avant skin-pass Wa0,8 inférieures ou égales à 0,35 μηι peuvent dans certains cas être atteintes sans respecter les équations (C) et/ou (D), notamment en respectant les équations (A) et/ou (B) et en utilisant des cylindres de travail lisses pour le laminage à froid et/ou de rugosité particulière pour le skin-pass, comme exposé ci- dessous.
Exemple 2 - influence du laminage à froid avec des cylindres de travail lisses
Les essais réalisés dans cet exemple visent à montrer l'influence positive d'un laminage à froid effectué avec des cylindres de travail lisses, par rapport à un laminage réalisé avec des cylindres de travail EDT dont les surfaces de travail présentent une rugosité plus importante.
A cet effet, des substrats en acier sont soumis à un laminage à froid pour atteindre une épaisseur de 0,8 mm, en utilisant soit des cylindres de travail dits lisses dont les surfaces de travail présentent une rugosité Ra2,5 de 0,5 μηι, soit des cylindres de travail EDT dont les surfaces de travail présentent une rugosité Ra2,5 de 3 μηι. Les substrats 3 sont ensuite revêtus par un revêtement de zinc par trempé à chaud dans un bain de zinc comprenant 0,18 % en poids d'aluminium, dont la température est de 460 Ό, et sont essorés avec de l'azote pour former des revêtements de zinc présentant une épaisseur de 6,5 μηι.
Après refroidissement complet des tôles 1 ainsi obtenues, celles-ci sont soumises à une opération de skin-pass réalisée avec des cylindres de travail gravés EBT, dont les surfaces de travail présentent une rugosité Ra2,5 de 5 μηι, avant d'être découpées et mises en forme par emboutissage.
Les valeurs d'ondulation Wa0,8 des surfaces extérieures 21 des revêtements 7 sont relevées à l'issue de chacune des étapes du procédé, à savoir après le laminage à froid (LAF), après l'opération de skin-pass (SKP) et après la mise en forme (DEF). Cette dernière est réalisée par déformation équi-biaxiale de 3,5% avec un outil de Marciniak.
Les résultats des mesures de Wa0,8 sont regroupés dans le tableau II.
Comme on peut le constater, l'utilisation du laminage lisse permet de réduire l'ondulation Wa0,8 que ce soit à l'issue du laminage à froid, du skin-pass ou de l'étape de mise en forme.
Tableau II
Figure imgf000013_0001
Exemple 3 - influence du skin-pass
Les essais réalisés dans cet exemple visent à montrer l'influence positive d'un skin-pass réalisé en utilisant des cylindres de travail dont les surfaces de travail présentent une certaine rugosité Ra2,5.
A cet effet, des substrats 3 en acier sont soumis à un laminage à froid pour former des substrats laminés à froid dont l'épaisseur est de 0,7 mm.
Les substrats 3 sont ensuite revêtus par un revêtement de zinc par trempé à chaud dans un bain de zinc comprenant 0,18 % en poids d'aluminium, dont la température est de 460 et sont essorés avec de l'azote pour former des revêtements de zinc présentant une épaisseur de 6,5 μηι.
Les tôles 1 ainsi obtenues sont divisées en deux lots. Avant d'être mises en forme par déformation équi-biaxiale de 3,5% avec un outil de Marciniak, les tôles 1 issues du premier lot sont soumises à un skin-pass réalisé avec cylindres de travail EDT et avec un taux d'allongement de 1 ,4%. La rugosité Ra2,5 des surfaces de travail est de 2,20 μηι.
Les tôles 1 issues du deuxième lot sont soumises à une opération de skin-pass avec le même taux d'allongement mais avec des cylindres de travail gravés EDT, dont les surfaces de travail présentent une rugosité Ra2,5 de 2,60μηι.
Les résultats des essais sont regroupés dans le tableau III.
Tableau III
Ra2,5^m)
Wa0,8 Wa0,8
Wa0,8
cylindres (μηι) (μηι) Eq (A) Eq (B) Eq (C) Eq (D)
Essais (μηι)
de travail après après après
LAF
du SKP SKP DEF
16 2,20 0,42 0,28 0,37 oui oui non non
17 2,60 0,42 0,41 0,47 oui oui non non

Claims

REVENDICATIONS
1 . Procédé de réalisation d'une tôle (1 ) comprenant un substrat (3) en acier dont au moins une face (5) est revêtue par un revêtement métallique (7) comprenant de l'Ai, le reste du revêtement métallique (7) étant du Zn, des impuretés inévitables et éventuellement un ou plusieurs éléments additionnels choisis parmi Si, Sb, Pb, Ti, Ca, Mn, Sn, La, Ce, Cr, Zr ou Bi, la teneur en poids de chaque élément additionnel dans le revêtement métallique (7) étant inférieure à 0,3%, le revêtement métallique (7) ayant une teneur en poids d'aluminium comprise entre 0,2 et 0,7%, le procédé comprenant au moins des étapes de :
- fourniture du substrat (3),
- dépôt d'un revêtement métallique (7) sur au moins une face (5) par trempe du substrat (3) dans un bain pour obtenir la tôle (1 ),
- essorage du revêtement métallique (7) par au moins une buse (17) projetant par au moins une sortie (25) un gaz d'essorage sur le revêtement métallique (7), la tôle (1 ) défilant devant la buse, le gaz d'essorage étant éjecté de la buse (17) le long d'une direction principale d'éjection (E),
- solidification du revêtement métallique (7),
- la surface extérieure (21 ) du revêtement métallique (7) présentant, après solidification et avant éventuelle opération de skin-pass, une ondulation Wa0,8 inférieure ou égale à 0,55μηι,
procédé dans lequel l'une au moins des équations suivantes est satisfaite:
Figure imgf000015_0001
Figure imgf000015_0002
où :
Z est la distance entre la tôle (1 ) et la buse (17) le long de la direction principale d'éjection (E), Z étant exprimée en mm,
d est la hauteur moyenne de la sortie (25) de la buse (17) le long du sens (S) de défilement de la tôle (1 ) devant la buse (17), d étant exprimée en mm,
V est la vitesse de défilement de la tôle (1 ) devant la buse (17), V étant exprimée en m. s"1 , P est la pression du gaz d'essorage dans la buse (17), P étant exprimée en N.m"2 ,et ι2 est la fraction volumique d'oxygène dans le gaz d'essorage.
Procédé selon la revendication 1 , dans lequel l'ondulation Wa0,8 de la surface extérieure du revêtement métallique (7) après solidification et avant éventuelle opération de skin-pass est inférieure ou égale à 0,35 μηι.
Procédé selon la revendication 1 ou 2, dans lequel le procédé comprend, avant l'étape de dépôt, une étape de laminage à froid de la tôle (1 ) dont au moins la dernière passe est réalisée avec des cylindres de travail rectifiés et non gravés dont les surfaces de travail présentent une rugosité Ra2,5 inférieure ou égale à 0,5 μηι.
Procédé selon l'une des revendications précédentes, le procédé comprenant une étape de skin-pass de la tôle (1 ) avec des cylindres de travail EDT dont les surfaces de travail présentent une rugosité Ra2,5 comprise entre 2,05 et 2,95 μηι.
Procédé selon l'une des revendications 1 à 3, le procédé comprenant une étape de skin-pass de la tôle (1 ) avec des cylindres de travail EBT dont les surfaces de travail présentent une rugosité Ra2,5 comprise entre 2,90 et 4,10 μηι.
Procédé selon l'une des revendications précédentes, dans lequel l'une au moins des équations suivantes est satisfaite :
Figure imgf000016_0001
Figure imgf000016_0002
7. Procédé selon l'une des revendications précédentes, dans lequel le revêtement métallique (7) a une teneur en poids d'aluminium inférieure ou égale à 0,6%.
8. Procédé selon la revendication 7, dans lequel le revêtement métallique (7) a une teneur en poids d'aluminium inférieure ou égale à 0,5%.
9. Tôle (1 ) susceptible d'être obtenue selon le procédé d'une des revendications précédentes, la tôle (1 ) comprenant un substrat (3) en acier dont au moins une face (5) est revêtue par un revêtement métallique (7) comprenant de l'Ai, le reste du revêtement métallique (7) étant du Zn, des impuretés inévitables et éventuellement un ou plusieurs éléments additionnels choisis parmi Si, Sb, Pb, Ti, Ca, Mn, Sn, La, Ce, Cr, Zr ou Bi, la teneur en poids de chaque élément additionnel dans le revêtement métallique (7) étant inférieure à 0,3%, le revêtement métallique (7) ayant une teneur en poids d'aluminium comprise entre 0,2 et 0,7%, la surface extérieure du revêtement métallique (7) présentant une ondulation Wa0,8, avant éventuelle opération de skin- pass, inférieure ou égale à 0,35μηι.
10. Tôle selon la revendication 9, dans laquelle le revêtement métallique (7) a une teneur en poids d'aluminium inférieure ou égale à 0,6%.
1 1 . Tôle selon la revendication 10, dans laquelle le revêtement métallique (7) a une teneur en poids d'aluminium inférieure ou égale à 0,5%.
12. Pièce obtenue par déformation d'une tôle selon l'une des revendications 9 à 1 1 , dans laquelle la surface extérieure du revêtement métallique présente une ondulation Wa0,8 inférieure ou égale à 0,43μηι.
13. Pièce selon la revendication 12, dans laquelle la surface extérieure du revêtement métallique présente une ondulation Wa0,8 inférieure ou égale à 0,41 μηι.
14. Pièce selon la revendication 13, dans laquelle la surface extérieure du revêtement métallique présente une ondulation Wa0,8 inférieure ou égale à 0,37μηι.
15. Pièce selon l'une des revendications 12 à 14, la pièce comprenant en outre un film de peinture sur le revêtement métallique (7).
16. Pièce selon la revendication 15, dans laquelle l'épaisseur du film de peinture est inférieure ou égale à 120 μηι.
17. Pièce selon la revendication 16, dans laquelle l'épaisseur du film de peinture est en inférieure ou égale à 100 μηι.
18. Véhicule terrestre à moteur comprenant une carrosserie, la carrosserie comprenant une pièce selon l'une des revendications 12 à 17.
PCT/IB2014/058879 2013-03-06 2014-02-10 PROCÉDÉ DE RÉALISATION D'UNE TÔLE À REVÊTEMENT ZnAl AVEC UN ESSORAGE OPTIMISÉ, TÔLE, PIÈCE ET VÉHICULE CORRESPONDANTS Ceased WO2014135999A1 (fr)