WO2014152798A1

WO2014152798A1 - Ceramic support structure

Info

Publication number: WO2014152798A1
Application number: PCT/US2014/027775
Authority: WO
Inventors: Benjamin A. DEMUTH; Adam R. Pawloski
Original assignee: INTERFACIAL SOLUTIONS IP LLC
Current assignee: INTERFACIAL SOLUTIONS IP LLC
Priority date: 2013-03-14
Filing date: 2014-03-14
Publication date: 2014-09-25
Anticipated expiration: 2015-09-14
Also published as: US10022889B2; EP2969487A4; CN105408091B; US20180339426A1; EP2969487B1; US20180243941A1; EP2969487A1; US20160023373A1; US10059031B1; US10272592B2; CN105408091A

Abstract

A pre-ceramic support structure for additive manufacturing, that upon thermal processing, is soluble in various solvents.

Description

TECHNICAL FIELD

10 1} The disclosure is related to the use of a melt processable pre-ceramic materials for applications as a support structure in additive manufacturing,

BACKGROUND fO002j Additive manufacturing technology, also recognized as three dimensional printing technology, builds three-dimensional objects through layer~by-fayer deposition of thermoplastic materials. A plastic filament is utilized to deliver materials to an extrusion nozzle. The nozzle is heated to melt the material and can he moved in both horizontal and vertical directions by computer control. Tire three dimensional object is produced by extruding small beads of thermoplastic material to form layers. The layers of thermoplastic material harden after extrusion. Support materials are often employed to assist in building certain three dimensional objects. The support structures are thermoplastic materials that can be removed from contact with other extruded materials by physical or chemical means. Certain support materials are selectively soluble in certain liquids. The composition, of a thermoplastic support materials and the liquid can be selected so that the liquid dissolves the support material, but not the intended material of construction for the desired object.

SUMMARY

(0003] One embodiment Involving additive manufacturing of ceramics is a process where thermoplastic filaments of pre-eeramic powders are extruded to form a three dimensional article. In certain applications of additive manufacturing,, a sacrificial "support^" layer is utilized to assis in forming "build" layers that create the intended three-dimensional product. The support layer will be subsequently removed to create a final object. During the additive manufacturing of ceramics in accordance with this disclosure, thermoplastic polymers carry the pre-ceramic powders to form three-dimensional green ceramic parts that contain the thermoplastic binder. For purposes of this disclosure, the thermoplastic polymers with the pre-ceramic can be intended as either the support layer as well as the build layer. The pails are then subjected to a binder removal, and sintering cycle during firing of the object, resulting in certain embodiments in ceramifi cation. Due to the elevated temperatures for sintering, conventional thermoplastic support layers are not sui table simply because the temperatures are far above the degradation temperatures of the polymer. The degradation of the support structure in turn may adversely affect the build layer and. the intended article. This has limited the types of three-dimensional ceramic objects produced, utilizing conventional additive manufacturing practices.

|1O04] This disclosure is directed to the use of a pre-sintered support, layer or structure for additive manufacturing, that upon firing or sintering, is soluble in various solvents, The compositions are additive manufacturing feedstocks, having a polymeric matrix and a pre- ceramic compound, wherein the post-sintered support layer is soluble or removable in a solvent. In general, the feedstocks are produced using melt processing techniques to form filaments that are suitable in applications with additive manufacturing processes and equipment.

[0005] For purposes of this disclosure, ceramic means a material that has been subject to a thermal process, or firing, to form an anhydrous or substantially anhydrous materia!. A green ceramic is a materia! that has not been subjected to a thermal process. Green ceramifiable articles can be produced with additive manufacturing wherein a pre-sintered build layer is supported by a pre-sintered support layer. Upon firin of the green article, the polymeric binders from both the build and support, layers are removed by thermal degradation, and in doing so, the build layer is transformed into a ceramic composition by additional thermal processing or sintering. The support layer maintains shape and structural support of the build layer during this process. With the removal of polymeric binder, the remaining material of the support layer is soluble or removable in a solvent. The entire object of the now ceramic support structure can be subject to a solvent where ii is removed, thereby lea ving the finished ceramic article formed by the build layer. DETAILED DESCRIPTION

|00G6| A pre-sintered support structure for additive manufacturing can be used io assist in the formation of three-dimensional ceramic articles. The feedstocks for the pre-sintered support structure are produced using melt processing techniques to form, in certain embodiments, filaments that are suitable in applications with additive manufacturing processes and equipment. The support structure filaments are employed with build structure filaments to create three-dimensional objects by additive manufacturing.

[8007] In certain embodiments, green ceraraifiabie articles may be produced with additive manufacturing techniques. The green ceraraifiabie article is supported by a support composition of a polymeric matrix and a pre-ceramic compound. Upon firing of the green article at elevated temperatures, the entire object including the post sintered support structure can be subject to a solvent bath where the ceramic support structure is removed, thereby leaving the finished ceramic article.

[0008] The support layer feedstock intended as the support structure is primarily a pre- ceramic powder or powder blend in a polymeric matrix. The polymer serves as a binder for the pre-ceramic powder or powder blend. The polymeric matrix imparts the necessary strength for the creation of a molded, or printed support structure. Additionally, it imparts the desired physical properties required to make the feedstock for the additive manufacturing process. The polymeric matrix may be any thermoplastic polymer capable of melt processing and functioning as a feedstock for additive manufacturing. They include both hydrocarbo and non-hydrocarbon polymers. In certain embodiments, the polymeric matrix may be a polyethylene, an ethylene-octene copolymer, or combinations thereof. Other non-limiting examples of polymeric matrices include other polyolef!ns, po!ylactic acid polymers, and acrylonitrile butadiene styrene polymers or combinations thereof. The polymeric matrix may be included in the pre-ceramic feedstock in amounts ranging from about 0.1% to about 25% by weight, in certain embodiments, the polymeric matrix may be included at about 0.5% to about 5% by weight. In some embodiments, the feedstock is generally in the form of an extruded filament. [0009] The pre-ceramic materials suitable for additive manufacturing are powders or micron sized compounds that are soluble in either a pre-ceramic or sintered state in various solvents. In some embodiments, the pre-ceramic is an acid labile mineral capable of forming a semi - solid under high heat. The intended application suggests that in certain embodiments the support structure, upon formation, must not soften below 700 °C. Additionally, the support structure must not melt below .1200 °C. Non-limiting examples of pre-ceramic materials include calcium carbonate, sodium carbonate, sodium a!uminaie or calcium carbide. Those of ordinary skill in the art with knowledge of this disclosure are capable of selecting a specific material to match the intended additive manufacturing article. For example, in applications where sintering does not exceed 850 °C sodium carbonate may also be used. In applications exceeding the 950 °C limits of calcium carbonate, sodium aluminate ma be used up to 1500 °C. In applications requiring extreme heat, calcium carbide may be employed, up to 2000 °C. The amount of pre- ceramic material in the feedstock may be at least 50%. In certain embodiments the pre- eeramic material is greater than 75% and even greater than 95%.

(^"0810] In some embodiments, a flux is used to reduce the overall melting point of the pre- ceramic material and thereby enhance the efficiency of the sintering process. The .flux may be any glass or ceramic material, which flows below the softening point of the pre-ceramic material Non-limiting examples of flux materials include glass frits comprised of boron trloxide, silicon oxide, zirconium dioxide, lithium oxide, fluorine, titanium dioxide, and combinations thereof. The flux may be included in the feedstock composition in amounts up to 20%. In one embodiment, a suitable flux is Ferro Frits 90 740 F from the Ferro Corporation, Frankfurt, D.E. In another embodiment, the flux may include silicates with melting points from 600 °C to 1000 °C, The flu may be added to the feedstock during melt processing.

[0011] In alternative embodiment, various processing additives may be utilized in the formation of the feedstock. Non-limiting examples of processing aids include waxes, moisture scavengers, lubricants and debinders. The processing additives are included in the melt processable composition In an amount of about 0.5 wt% to about 5 wt%.

[0012] The components comprising the feedstock are blended and subjected to melt processing. The feedstock can be palletized and then subsequently formed into a filament suitable for additive manufacturing. In some embodiments, the filament has a modulus of approximately 300 MPa to 1600 MPa,

[0013] The melt processing of the feedstock is generally performed in a twin-screw extruder. In certain embodiments, the processing is performed in co-rotating, segmented twin-screw extruder. In such instances, the length:diameter ratio of the twin screw extruder is at least 32:1. In another embodiment, the length: diameter ratio of the twin screw extruder is at least 40: 1. Typical temperature profiles may range ^'from 120- 220 °C with typical screw speeds potentially in the range of about 200-300 RPM. Die pressures can be minimized to ensure incorporation of all pre-ceramic materials into the thermoplastic binder. Those who are skilled in the art will recognize preferred screw designs and temperature profiles to achieve optimal blending of the melt processable composi tions of this invention.

[0014] The feedstock containing pre-ceramic materials is used in additive manufacturing as a support structure for ceramic articles. The support structure or layers are utilized with build layers to form a three-dimensional article or object The materials are capable of withstanding the elevated temperatures necessary to place a green ceramic article into its desired ceramic form. Those of ordinary skill in the art are capable of selecting an appropriate feedstock to match a particular ceramic, Additionally, additive manufacturing equipment and techniques ma be selected depending upon the desired finished article. One example of an additive manufacturing device is a Makerbot Replicator 2X additive manufacturing printer, available from Stratasys Ltd, Minneapolis, MN. 0Θ15] An article created with a pre-sintered build structure, along with the pre-sintered support structure or layer, is fired at elevated temperatures. During the firing of the green ceramic article the support structure or layers withstand the elevated temperatures and do not deform and thereby do not adversely affect the intended ceramic article. The support structure or layers may then be removed in suitable solvents. The removal of the support structure or layers results in the finished ceramic article. Suitable solvents vsill depend upon the pre-ceramic material used in the feedstock, Non-limiting examples include; water, carbonated solutions, and acidic solutions. Those of ordinary skill in the art are capable of selecting a specific solvent based on the pre-ceramic material selected in the feedstock.

10161

EXAMPLES

[0017| Compoundin Procedure for Exampl Ϊ

For Example 1, ethylene -octene copolymer resin PEI, and Calcium Carbonate powder were dry blended and then fed using a gravimetric feeder into a 27 mm co-rotating twin screw extruder (32:1 , L:D) fitted with a strand die (commercially available from Leistritz Corporation, Allendale, NJ). Samples were processed with a screw rotational speed of 250 Tpm using the following temperature profile; Zone 1-10 - 180 °C, Die ~ 160 °C. The resulting strands of extrudate were subsequently continuously processed onto a belt, cooled to room temperature by fans, and peUetized into 0.64 cm pellets. The resulting pellets were used to press 6 mm square plaques, 6 mm in depth.

|Θ018] Press g Froeed&re for CE1 &nd Exam le 2

Plaques in Example 2 were made using a heated platen hydraulic press (commercially available from Dake Corporation, Grand Haven, Mi). Approximately 1 ! Og of pellets from example. 1 were spread in an aluminum frame equating to the dimensions previously listed, and covered with aluminum foil. The top and bottom platens, heated to 175 °C, were made to contact the pellets of example 1 in the aluminum frame for 3 min, under minimal pressure. After 3 min, 15 tons of pressure was applied to the material for 5 min, after which time, the material was removed and allowed to coo! to room temperature at an unspecified rate. This procedure was repeated using, previously demonstrated, cerami liable polymer to produce 10 x 10 x 0.6 cm plaques of CE1. Three aluminum frames were stacked vertically. A. plaque of CE1 was placed in the bottom. The plaque of example 1 was cut into a cross of equal legs, 5 cm wide with an outer diameter of 4 inches, fitting into the aluminum frame previously used. Pellets of a ceramifiabie material used to make CE1 were placed in the cavities of the second frame. A third plaque of CE1 was placed on top and the sample pressing procedure was followed to mak example 2. Example 2 having final dimensions of 10 x 10 x 0.6 cm, made of CE1 and having a cross of example I centered internally.

P¾Ji 9] Ceramificatioit &®ά Dissolution of Example 2 into Example 3

Example 2 was heated in a muffle furnace (commercially available from ThemioPisher Scientific Corporation, Weldham, MA) to 950 °C for 20 ruin at an unspecified rate. This material was removed from the furnace and allowed to cool to room temperature at an unspecified rate. This conversion yielded a wholly ceramified, intact article of similar initial dimensions of example 2. Upon immersion in a water bath, the CaC⁽¾ material from example 1 was entirely dissolved leaving example 3 of dimensions equal to the CE 1 material only, in example 2,

[00201 Example 4

A filament containing a pre-ceramic material suitable as a support layer, is extruded in a manner similar to that of Example 1, and wound onto a spool. A. second filament containing a pre-ceramic material suitable as a build layer is also produced in a manner similar to Example I and wound onto a spool. The spools are loaded into a MakerBot Replicator 2X additive manufacturing printer, available from Stratasys Ltd, Minneapolis, MN. The filament from each spool is fed into the MakerBot 2X extruder nozzles in accordance with the printers loading procedures.

A CAD file of a three-dimensional article requiring a support layer and a build layer with 90° overhangs of the build layer is selected and loaded into the MakerBot 2X.

The loaded filaments are printed at temperature of about 160 to 200 °C and at printing speeds ranging between 20 and 100 .mm/sec with acceleration enabled. The materials are printed onto a standard apton tape heated to about 100 °C. Filament are printed with an infill between 5 and 95%. Layer heights are between 0.10 and 0.35 mm.

The printed article having a build and support layer constructed from pre-ceramic filaments is subjected to a thermal treatment. The printed article is placed in a muffle furnace and heated to about 450 °C, under an inert, oxidizing, or reducing gas, to thermally remove any thermoplastic material and water. The printed article is then further heated to in excess of 750 °C, under an inert, oxidizing, or reducing gas, to enable sintering and thereby create a ceramic, or substantially ceramic, article.

The article is cooled at an appropriate rate so as not to produce thermal cracking or warping. The article does not exhibit any warping of either the support layer or the build layer. ^'The structure of the build layer is supported by the support layer material that remains post-thermal treatment. The article is then submersed in an appropriate solvent to dissolve or disperse the support layer. The article comprising the remaining build material is removed from solvent and dried.

|Θ021] Table 1 gives the formulations for example I [0022] Table I. Formulation for Example 1

FEl CaC0₃

CE1 25 75 1

Claims

What is claimed is:

1. A composition comprising an additive manufacturing feedstock having a polymeric matrix and a pre-ceramic material, wherein the pre-ceramic material is removable in a solvent,

2. A composition according to claim 1, wherein the polymeric matrix Is one or more of polyolefins, polyiactic acid polymers, and acryionstrile butadiene styrene polymers or combinations (hereof.

3. A composition according to claim L wherein the pre-ceramic material is calcium carbonate, sodium carbonate, sodium aluminate or combinations thereo

4. A composition according to claim 1 , farther comprising one o more of a fluxing material, a polymer processing additive or combinations thereof

5. A composition according to claim 4, wherein the fluxing material includes glass frits having boron trioxide, silicon oxide, zirconium dioxide, lithium oxide, fluorine, titanium dioxide, and combinations thereof.

6. A composition according to claim 1, wherein the solvent includes water, carbonated solutions, and acidic solutions.

7. A composition according to claim 1 , wherein the additive manufacturing feedstock is suitable as a support structure.

8. A composition comprising a feedstock for additive manufacturing, wherein the feedstock is a polymeric matrix and a pre-ceramic material, the pre-ceramic material upon thermal processing is removable in a solvent.

9. A. method comprising producing an article by additive manufacturing using a feedstock of a polymeric matrix and a pre-ceramic material, wherein the pre-ceramic material post- sintering is removable in a solvent.

10. A method comprising creating a green article with additive manufacturing wherein the green article has a build layer supported by a support layer derived from a polymeric matrix and a pre-ceramic material, wherein the pre-ceramic materia! is removable in a solvent,

1 1. A method according to claim 10, further comprising firing the green article.

12. A method according to claim. 1 1 , further comprising removing the support layer by a solvent.

13. A method according to claim 11 , wherein the solvent includes water, carbonated s lutions, and acidic so Unions.

14. An article comprising a filament for additive manufacturing wherein the filament is a polymeric matrix and a pre-ceramic material, wherein the pre-ceramic material is removable in a solvent.

1.5, An article comprising a green ceramic article wherein the green ceramic article is supported by a support composition of a polymeric matrix, and a pre-ceramic material, wherein the pre-ceramic material is removable in a solvent.