Publication number: WO2016137738A1
Application number: PCT/US2016/017055
Authority: WO
Inventors: Ruud VAN ROSSUM; Cornelis Johannes Gerardus Maria HERMANS; Daniel Henry Bolton
Original assignee: Eastman Chemical Co
Current assignee: Eastman Chemical Co
Priority date: 2015-02-26
Filing date: 2016-02-09
Publication date: 2016-09-01
Anticipated expiration: 2017-08-26
Also published as: CN107257834B; EP3262231B1; EP3262231A1; CN107257834A; US20160251798A1

Abstract

A bonding composition for adhering PVC to fabric is disclosed. The bonding composition contains isocyanurate and organophosphate at an organophosphate to isocyanurate weight ratio of 4:1 to 10:1.

Description

BONDING AGENTS FOR PLASTISOLS CONTAINING

DOTP OR DINCH

FIELD OF THE INVENTION

[0001] The invention generally relates to compositions for bonding flexible PVC to synthetic fabric and to their use.

BACKGROUND OF THE INVENTION

[0002] There are many applications for polyvinyl chloride (PVC) coated fabrics. These include tarpaulins, conveyor belts, geomembranes, marquees, roofing and cladding materials, protective clothing, floor coverings, and many others. Historically, natural fabrics were used in these applications, but the natural fabrics have now been substituted, in many instances, with synthetic fibers. Compared to natural fibers, synthetic fibers have been found to offer improved strength, toughness, lightness, moisture resistance, resistance to microorganisms, and flexibility.

[0003] Synthetic fibers, however, generally have smooth monofilaments. PVC coatings tend to have poor mechanical adhesion to smooth surfaces. To improve adhesion, a specific bonding agent can be added to the PVC coating solution (often a plastisol) just prior to application. The bonding agent chemically bonds with the reactive groups of the fabric and allows the PVC coating to adhere to the fabric.

[0004] Most bonding agents incorporate isocyanates. A class of

isocyanates is called isocyanurate.

[0005] It is common to incorporate into the bonding composition an ortho- phthalate carrier, for instance, dibutyl phthalate, dioctyl phthalate, or diisononyl phthalate (DINP). However, even though using ortho-phthalate carriers is common, such use is often undesirable due to public opinion on the adverse health effect of phthalates.

[0006] Recently, there has been a movement away from using ortho- phthalate plasticizers. [0007] Alternatives to ortho-phthalate plasticizers include dioctyl

terephthalate (DOTP) (also known as diethylhexyl terephthalate (DEHT)), 1 ,2- cyclohexane dicarboxylic acid diisononyl ester (DINCH), hydrogenated dioctyl phthalate (DHEH), hydrogenated DOTP (DOCH), citrates, Mesamoll®

(alkylsulfonic acid ester with phenol), butyloctyl terephthalate (BOTP), and isononyl benzoate (INB).

[0008] However, commercially available bonding agents can show poor compatibility with ortho-phthalate free plastisols. Poor compatibility can result in a very short pot life due to rapidly increasing plastisol viscosity and gelation of the plastisol shortly after adding the bonding agent.

[0009] Thus, there is a need for a bonding agent that shows good

compatibility with ortho-phthalate free PVC plastisols. There is also a need for a bonding agent that, in addition to showing good compatibility with ortho- phthalate free PVC plastisols, can improve the adherence of the PVC to fabric, especially synthetic fabric.

[0010] The present invention addresses these needs as well as others, which will become apparent from the following description and the appended claims.

SUMMARY OF THE INVENTION

[0011] The invention is as set forth in the appended claims.

[0012] Briefly, in one aspect, the present invention provides a bonding composition for adhering polyvinyl chloride to fabric. The composition comprises (a) isocyanurate and (b) organophosphate at an organophosphate to isocyanurate weight ratio of 4:1 to 10:1 .

[0013] In another aspect, the present invention provides a coating composition. The coating composition comprises:

(a) a plastisol comprising polyvinyl chloride powder dispersed in a plasticizer comprising dioctyl terephthalate or 1 ,2-cyclohexane dicarboxylic acid diisononyl ester; and

(b) the bonding composition according to the invention. [0014] In yet another aspect, the present invention provides a process for coating a fabric. The process comprises:

(a) combining the bonding composition according to the invention with a plastisol comprising polyvinyl chloride powder dispersed in a plasticizer comprising dioctyl terephthalate or 1 ,2-cyclohexane dicarboxylic acid diisononyl ester; and

(b) coating at least one side of a fabric with the mixture from step

(a).

[0015] The present invention also provides for articles of manufacture comprising a fabric coated with the coating composition according to the invention.

BRIEF DESCRIPTION OF THE DRAWINGS

[0016] Figure 1 is a bar graph of the peel strength of various PVC

formulations based on DINP plasticizer from Example 3.

[0017] Figure 2 is a bar graph of the peel strength of various PVC

formulations based on DOTP plasticizer from Example 4.

DETAILED DESCRIPTION OF THE INVENTION

[0018] It has been found, surprisingly, that organophosphates can improve the compatibility of bonding agents containing isocyanurates with plastisols containing non-ortho-phthalate plasticizers.

[0019] Thus, in one aspect, the present invention provides a bonding composition for adhering polyvinyl chloride to fabric. The composition comprises:

(a) isocyanurate; and

(b) organophosphate,

wherein the weight ratio of organophosphate to isocyanurate ranges from 4:1 to 10:1 .

[0020] The isocyanurate preferably comprises aromatic diisocyanate groups, such as 2,4-diisocyanatotoluene, 2,6-diisocyanatotoluene, or mixtures thereof. In one embodiment, the isocyanurate comprises 2,4-toluene diisocyanate trimer (CAS # 26603-7).

[0021] Bonding agents containing isocyanurate are commercially available. Alternatively, the isocyanurate may be prepared by methods using catalysts known in the art. For example, isocyanurates can be produced by

oligomerization, in particular trimerization, from diisocyanates. The

diisocyanates normally used for this purpose include the isomeric

diisocyanatotoluenes (TDI), composed mainly of 2,4-diisocyanatotoluene (2,4- TDI) and 2,6-diisocyanatotoluene (2,6-TDI). These can easily be converted almost completely to isocyanurates. The isocyanurate may also be produced exclusively from 2,4-TDI.

[0022] The isocyanurate may be prepared by treating the toluene

diisocyanate, either alone or in a suitable solvent, with a basic catalyst such as an aliphatic tertiary amine, a basic metallic compound such as an alkali or alkaline earth metal oxide, hydroxide carbonate, alcoholate or phenate, an alkali metal salt of an enolizable compound or a metallic salt of a weak organic carboxylic acid. Co-catalysts may be used, such as, for example, mono-N-substituted carbamic esters in conjunction with basic metallic compounds. Catalysts containing metallic salts of weak organic carboxylic acids, optionally in the presence of a mono-N-substituted carbamic ester, can considerably reduce polymerization times.

[0023] Suitable solvents for preparing the isocyanurate include solvents that are inert towards isocyanates, and include, for example, esters such as ethyl acetate, butyl acetate, amyl acetate, diethyl phthalate, the acetate of the monoethyl ether of ethylene glycol, dimethyl phthalate, and butyl benzoate; ketones such as methyl isobutyl ketone; chloroform; benzene; toluene;

xylene; sulfur dioxide; butyrolactone; monochlorobenzene; o-dichlorobenzene; ethers; or mixtures of such solvents.

[0024] The preparation of isocyanurate may conveniently be carried out by polymerizing the toluene diisocyanate with a suitable catalyst until the desired polymer has been obtained; further polymerization may then be prevented, for example, by mechanical removal of insoluble catalysts by filtration or by the inactivation of soluble catalysts by treatment with the calculated amount, or a slight excess thereof, of a strong acid, such as anhydrous hydrogen chloride or phosphoric acid. Alternatively, the toluene diisocyanate may be

polymerized to a degree such that the required polymer formation has taken place and then after removal or inactivation of catalyst, residual free toluene diisocyanate may be removed by such processes as extraction, distillation, or precipitation of the polymer with a solvent in which the monomeric toluene diisocyanate is soluble.

[0025] In addition to diisocyanates, other polyisocyanates may be used to prepare the isocyanurate polymer, for example, p-phenylene diisocyanate, m- phenylene diisocyanate, 1 -methoxyphenylene-2,4-diisocyanate, 3,3-dimethyl- 4,4'-diisocyanatodiphenylmethane, diphenylene-4,4'-diisocyanate, 4,4'- diisocyanatodiphenyl ether, naphthylene-1 ,5-diisocyanate, hexamethylene diisocyanate, diisocyanatodicyclohexylmethane, p-xylylene diisocyanate, m- xylylene diisocyanate, isocyanatobenzyl isocyanates, 1 ,2,3,4,5,6- hexahydrodiphenylene-4,4'-diisocyanate, 4,4'-diisocyanato-1 ,2,3,4,5,6- hexahydrodiphenylmethane, 1 ,2,3,4-tetrahydronaphthylene-1 ,5-diisocyanate, toluene-2,4,6-triisocyanate, 3-methyl-4,6,4'-triisocyanato diphenylmethane, 2,4,4'-triisocyanatodiphenyl, 2,4,4'-triisocyanato-diphenyl ether, 4,4'- diisocyanatodiphenyl methane, 1 -chlorophenylene-2,4-diisocyanate, and p- isocyanato benzyl isocyanate.

[0026] The amount of isocyanurate in the bonding composition may range from 0.5 to 30% by weight, based on the total weight of the bonding

composition. Other amounts of the isocyanurate are possible, such as from 5 to 30% by weight, 8 to 30% by weight, 10 to 30% by weight, 0.5 to 25% by weight, 5 to 25% by weight, 8 to 25% by weight, 10 to 25% by weight, 0.5 to 20% by weight, 5 to 20% by weight, 8 to 20% by weight, 10 to 20% by weight, 0.5 to 15% by weight, 5 to 15% by weight, 8 to 15% by weight, or 10 to 15% by weight. [0027] Any organophosphate that can improve the compatibility of isocyanurate with PVC plastisols containing non-ortho-phthalate plasticizers can be used in the bonding composition according to the invention. Such organophosphates include those containing alkyl or aryl groups having 7 to 10 carbon atoms. Specific examples of suitable organophosphates include tri- ethylhexyl phosphate, tricresyl phosphate, isodecyl diphenyl phosphate, 2- ethylhexyl diphenyl phosphate, or mixtures thereof. In one embodiment, the organophosphate comprises tri-ethylhexyl phosphate.

[0028] The amount of organophosphate in the bonding composition may range from 50 to 99.5% by weight, based on the total weight of the bonding composition. Other amounts of the organophosphate are possible, such as from 75 to 99.5% by weight, 80 to 99.5% by weight, 85 to 99.5% by weight, 50 to 95% by weight, 75 to 95% by weight, 80 to 95% by weight, 85 to 95% by weight, 50 to 92% by weight, 75 to 92% by weight, 80 to 92% by weight, 85 to 92% by weight, 50 to 90% by weight, 75 to 90% by weight, 80 to 90% by weight, or 85 to 90% by weight.

[0029] The weight ratio of organophosphate to isocyanurate in the bonding composition ranges from 4:1 to 10:1 . In one embodiment, the weight ratio of organophosphate to isocyanurate ranges from 4.5:1 to 10:1 . In yet other embodiments, the weight ratio of organophosphate to isocyanurate ranges from 5:1 to 10:1 , 6:1 to 10:1 , 7:1 to 10:1 , 4:1 to 9:1 , 5:1 to 9:1 , 6:1 to 9:1 , or 7:1 to 9:1 .

[0030] The bonding composition may also include typical amounts of traditional additives such as flame retardants, stabilizers, chlorinated hydrocarbons, secondary plasticizers, viscosity depressants, antioxidants, or mixtures thereof.

[0031] The components of the bonding composition according to the invention may be combined in any known manner, including simultaneously or sequentially. Heating may facilitate dissolution of one or more of the components along with vigorous mixing. [0032] The bonding composition of the invention is particularly suitable as adhesion promoters for plasticized PVC and in particular for PVC plastisols.

[0033] Thus, in another aspect, the invention provides a coating

composition. The coating composition comprises:

(a) a plastisol comprising polyvinyl chloride (PVC) powder dispersed in a plasticizer comprising dioctyl terephthalate or 1 ,2-cyclohexane dicarboxylic acid diisononyl ester; and

(b) the bonding composition according to the invention.

[0034] The plastisol typically contains from 20 to 150 parts by weight of plasticizer per 100 parts of PVC powder. In one embodiment, the plastisol contains from 40 to 120 parts by weight of plasticizer per 100 parts of PVC powder.

[0035] In one embodiment, the plasticizer is dioctyl terephthalate.

[0036] In addition to PVC, the plastisol may include vinyl copolymers such as vinyl acetate or vinyl acrylate.

[0037] The amount of the bonding composition employed in the coating composition can vary, depending on the desired degree of adhesion and the isocyanurate content of the bonding composition. For example, for a bonding composition containing 25 wt% of isocyanurate, the coating composition typically contains from 1 to 8 wt% of the bonding composition. As another example, for a bonding composition containing 8 to 20 wt% of isocyanurate, the coating composition may contain from 1 to 20% by weight of the bonding composition. In one embodiment, the coating composition contains from 4 to 20% by weight of the bonding composition. In another embodiment, the coating composition contains from 4 to 15% by weight of the bonding composition. The amount by weight of the bonding composition is based on the total weight of the coating composition.

[0038] The coating composition according to the invention may further comprise a variety of additives, such as flame retardants (e.g., antimony trioxide or aluminum trihydroxide), stabilizers (including epoxy stabilizers), fillers (e.g., calcium carbonate or dolomite), pigments (e.g., titanium dioxide, carbon black, or ultramarine blue), chlorinated hydrocarbons, plasticizers, viscosity depressants (e.g., white spirit or tallates), antioxidants (e.g., 2,6-di-t- butyl-4-methylphenol, 3,5-bis(1 ,1 -dimethylethyl)-4-hydroxybenzenepropanoic acid octadecyl ester, butylated hydroxytoluene, or octadecyl 3,5-di-t-butyl-4- hydroxyhydrocinnamate), UV absorbers (e.g., 2-hydroxyphenylbenzotriazole or 2-hydroxybenzophenones), biocides (e.g., 2-n-octyl-4-isothiazolin-3-one, 4,5,-dichloro-2-n-octyl-4- isothiazolin-3-one or 10,10'-oxybisphenoxarsine), or mixtures thereof.

[0039] The bonding agent is typically added to the plastisol, mixed at slightly elevated temperature (e.g., 20-30^QC), and de-aerated shortly before use. The mixed composition is particularly suitable for coating fabric, particularly fabric made from synthetic fiber.

[0040] Thus, in another aspect, the invention provides a process for coating a fabric. The process comprises:

(b) coating at least one side of a fabric with the mixture from step

(a).

[0041] The fabric to be coated preferably comprises polyester or polyamide fibers. The fabric may be coated on one or both sides using techniques known in the art, such as by spreading, dipping, or calendering on

conventional equipment.

[0042] In one embodiment, the coating process further comprises (c) exposing the coated fabric to elevated temperature to fuse the coating. The fusing step may be carried out, for example, at a temperature of 1 10 to 210^QC for 30 to 90 seconds, until fusion is sufficiently completed.

[0043] Additional coats of the coating composition of the invention, or of another PVC composition may subsequently be applied and heated in a similar fashion. [0044] The present invention also provides for articles of manufacture comprising a fabric coated with the coating composition according to the invention. Such articles of manufacture include tarpaulins, billboards, air- supported structures and other textile structures, flexible containers, polygonal roofs, geomembranes, pool-liners, awnings, protective apparel, conveyor belts, flock carpets, and foamed synthetic leather.

[0045] The present invention includes any and all combinations of embodiments, features, parameters, and/or ranges disclosed herein. That is, the invention may be defined by any combination of embodiments, features, parameters, and/or ranges described herein.

[0046] As used herein, the indefinite articles "a" and "an" mean one or more, unless the context clearly suggests otherwise. Similarly, the singular form of nouns includes their plural form, and vice versa, unless the context clearly suggests otherwise.

[0047] While attempts have been made to be precise, the numerical values and ranges described herein should be considered to be approximations (even when not qualified by the term "about"). These values and ranges may vary from their stated numbers depending upon the desired properties sought to be obtained by the present invention as well as the variations resulting from the standard deviation found in the measuring techniques. Moreover, the ranges described herein are intended and specifically contemplated to include all sub-ranges and values within the stated ranges. For example, a range of 50 to 100 is intended to describe and include all values within the range including sub-ranges such as 60 to 90 and 70 to 80.

[0048] The content of all documents cited herein, including patents as well as non-patent literature, is hereby incorporated by reference in their entirety. To the extent that any incorporated subject matter contradicts with any disclosure herein, the disclosure herein shall take precedence over the incorporated content.

[0049] This invention can be further illustrated by the following examples of preferred embodiments thereof, although it will be understood that these examples are included merely for purposes of illustration and are not intended to limit the scope of the invention.

EXAMPLES

[0050] Table 1 shows the commercial bonding agents that were tested in the examples below, where DINP is diisononyl phthalate, INB is isononyl benzoate, and TEHP is triethylhexyl phosphate.

Table 1

[0051] Table 2 shows the plasticizers that were tested.

Table 2

Example 1

[0052] To quickly determine the compatibility of the plasticizers with the commercial bonding agents and to detect visual changes, the commercial bonding agents were mixed directly with the plasticizers, instead of using PVC plastisols.

[0053] The mixtures were prepared by adding the plasticizer to the bonding agent in a vial at a 5:1 weight ratio of plasticizer to bonding agent, shaking the vial firmly by hand, and then observing the mixture after 24 hours.

[0054] The appearance of the mixtures was rated for cloudiness, gelation, color change, and viscosity according to scale set forth in Table 3.

Table 3

[0055] The appearance rating of the mixtures is reported in Table 4.

Table 4

n/t = not tested [0056] As seen from Table 4, the results show that DINP and DPHP, both ortho-phthalates, are more compatible with most of the tested bonding agents than the other plasticizers tested. DOTP, in particular, showed low

compatibility with most of the tested bonding agents.

Example 2

[0057] The procedure of Example 1 was repeated with mixtures containing 2 parts by weight of bonding agent, 6 parts by weight of DOTP as the plasticizer, and 1 part by weight of triethylhexyl phosphate (TEHP) as a compatibilizer.

[0058] The appearance of the mixtures was rated using the scale in Table 3 immediately after mixing as well as after 3 days. The results are reported in Table 5.

Table 5

[0059] As seen from Table 5, adding TEHP significantly improved the compatibility of DOTP with the bonding agents.

Example 3

[0060] A plastisol was prepared by mixing the ingredients shown in Table 6 at the listed proportions. Table 6

[0061] Adhesive compositions were prepared by adding 2, 3, or 4 wt% of the bonding agent Vulcabond TP to the prepared plastisol at 30^QC. The compositions were properly mixed and de-aerated. Vulcabond TP is a 25 wt% isocyanurate solution mainly in a mixture of DBT (50 wt%) and TEHP (15 wt%).

[0062] A second bonding agent was prepared using a mixture of Vulcabond TP and TEHP in a 1 :1 weight ratio. The dosing level of this bonding agent was twice the amount of the neat Vulcabond TP, since the isocyanate content was diluted to 12.5 wt% with the TEHP. Adhesive compositions were prepared by adding 4, 6, and 8 wt% of the second bonding agent to the prepared plastisol at 30^QC. The compositions were properly mixed and de- aerated.

[0063] The adhesive compositions were then coated onto 12 fiber threads/cm x 12 fiber threads/cm sheets of polyester fiber (DEWHURST, 550 dtex) at a layer thickness of 100 g/m² and placed in a Werner Mathis oven within 1 hour of adding the bonding agent. Additional coated samples were prepared with adhesive compositions that were allowed to sit for 24 hours at 30^QC. [0064] The adhesive compositions on the coated fabric were fused in the oven at 190^QC for 1 minute.

[0065] The coated fabric samples were then subjected to a 90^Q peel test. Peel Test Procedure

[0066] Two test pieces of coated fabric size 3 x 20 cm were HF welded together with the coated sides facing each other, for an area of 2 x 15 cm.

[0067] Each loose end of the test sample was clamped in a material test machine and peeled under an angle of 90 degrees at a speed of 100 mm/min. The average peel force was measured on 8 cm of the welded area,

disregarding the start and ending of the test.

[0068] The force was extrapolated to N/5 cm bond width.

[0069] The peel test results are shown in Figure 1 along with a coated sample that was made with just the prepared plastisol and no bonding agent.

[0070] As seen from Figure 1 , the results show a good increase in peel strength with increasing amount of bonding agent. The Vulcabond TP/TEHP 50/50 mixture results were comparable with the neat Vulcabond TP results. The results of adhesive compositions that were allowed to sit for 24 hours at 30^QC showed little increase in peel strength, which is expected due to the limited pot life of the adhesive composition.

Example 4

[0071] Example 3 was repeated except that DINP in the prepared plastisol was replaced with DOTP.

[0072] The 90^Q peel test results are shown in Figure 2 along with a coated sample that was made with just the prepared plastisol and no bonding agent.

[0073] As seen from Figure 2, the results for DOTP adhesive compositions showed good peel strength increase with increasing amount of bonding agent. The Vulcabond TP/TEHP 50/50 mixture results were in line or even better compared to the neat Vulcabond TP results. Also, there was no positive adhesion effect after storage of the adhesive composition for 24 hours at 30^QC, as expected due to the limited pot life.

[0074] Comparing the results of Figures 1 and 2, even though the DOTP- based plastisols seemed to have lower initial peel strength at 2 and 3 wt% loadings of neat Vulcabond TP compared to the corresponding DINP-based samples; at 8 wt% of the Vulcabond TP/TEHP 50/50 mixture, the initial peel strength surpassed that of the corresponding DINP-based plastisol.

Example 5

[0075] Besides adhesion, it is also desirable to have a more or less constant viscosity during the pot life. Increasing viscosity could have a negative effect on the penetration of the adhesive composition into the fiber structure of the fabric and reduce the final peel strength. Therefore, the viscosity of the adhesive compositions from Examples 3 and 4 were monitored in the first 5 hours after addition of the bonding agent and after 24 hours.

[0076] A Brookfield viscosity measurement was conducted on the plastisols at 30^QC using spindle 5, at a rotation speed of 10 rpm.

[0077] The viscosity results for adhesive compositions from Examples 3 and 4 are shown in Tables 7 and 8, respectively, where TP refers to Vulcabond TP and the percentages of TP are by weight.

Table 7

Viscosity Stability at 30⁹C for DINP-Based Plastisol Samples

Table 8

Viscosity Stability at 30⁹C for DOTP-Based Plastisol Samples

[0078] As seen from Tables 7 and 8, the results show a stable viscosity for both the DINP- and DOTP-based plastisols without bonding agent. The adhesive compositions with Vulcabond TP showed higher initial viscosity compared to the samples with TP/TEHP. Overall, the Vulcabond TP samples showed more viscosity increase within the first 5 hours than the samples with TP/TEHP. TEHP provided a lower initial viscosity and better viscosity stability.

Example 6

[0079] A bonding agent was prepared by vacuum distilling Desmodur RC (an aromatic isocyanurate trimer product from Bayer with 35 wt% of isocyanate in ethyl acetate) to remove the majority of the ethyl acetate. The ethyl acetate was replaced with TEHP. This solution was further diluted with TEHP to obtain a bonding agent containing 12.5 wt% of isocyanate.

[0080] The invention has been described in detail with particular reference to preferred embodiments thereof, but it will be understood that variations and modifications can be effected within the spirit and scope of the invention.

Claims

CLAIMS We claim:

1 . A bonding composition for adhering polyvinyl chloride to fabric, comprising:

(a) isocyanurate; and

(b) organophosphate,

2. The bonding composition according to claim 1 , wherein the isocyanurate comprises aromatic diisocyanate groups.

3. The bonding composition according to claim 1 or 2, wherein the isocyanurate comprises 2,4-toluene diisocyanate trimer.

4. The bonding composition according to claim 1 , 2, or 3 which comprises 8 to 20% by weight of the isocyanurate, based on the total weight of the bonding composition.

5. The bonding composition according to any one of claims 1 to 4, wherein the organophosphate comprises alkyl or aryl groups having 7 to 10 carbon atoms.

6. The bonding composition according to any one of claims 1 to 5, wherein the organophosphate comprises tri-ethylhexyl phosphate, tricresyl phosphate, isodecyl diphenyl phosphate, 2-ethylhexyl diphenyl phosphate, or mixtures thereof.

7. The bonding composition according to any one of claims 1 to 6, wherein the organophosphate comprises tri-ethylhexyl phosphate.

8. The bonding composition according to any one of claims 1 to 7, which comprises 85 to 90% by weight of organophosphate, based on the total weight of the bonding composition.

9. The bonding composition according to any one of claims 1 to 8, wherein the weight ratio of organophosphate to isocyanurate ranges from 7:1 to 9:1 .

10. A coating composition comprising:

(b) the bonding composition according to claim 1 .

1 1 . The coating composition according to claim 10, wherein the plastisol further comprises vinyl copolymers.

12. The coating composition according to claim 10 or 1 1 , which comprises 4 to 15% by weight of the bonding composition, based on the total weight of the coating composition.

13. The coating composition according to claim 10, 1 1 , or 12, which comprises from 40 to 120 parts by weight of plasticizer per 100 parts of PVC particles.

14. The coating composition according to any one of claims 10 to

13, wherein the organophosphate comprises tri-ethylhexyl phosphate.

15. The coating composition according to any one of claims 10 to

14, which further comprises flame retardants, stabilizers, fillers, pigments, chlorinated hydrocarbons, secondary plasticizers, viscosity depressants, antioxidants, UV absorbers, biocides, or mixtures thereof.

16. A process for coating a fabric, comprising:

(a) combining the bonding composition according to claim 1 with a plastisol comprising polyvinyl chloride powder dispersed in a plasticizer comprising dioctyl terephthalate or 1 ,2-cyclohexane dicarboxylic acid diisononyl ester; and

(b) coating at least one side of a fabric with the mixture from step

(a).

17. The process according to claim 16, wherein the plastisol further comprises vinyl copolymers.

18. The process according to claim 16 or 17, wherein the fabric comprises polyester or polyamide.

19. The process according to claim 16, 17, or 18, which further comprises (c) exposing the coated fabric to elevated temperature to fuse the coating.

20. An article of manufacture comprising a fabric coated with the coating composition according to claim 10.