WO2018207958A1 - 자외선 차단 기능을 가진 화장료 조성물이 함침된 화장품 - Google Patents

자외선 차단 기능을 가진 화장료 조성물이 함침된 화장품 Download PDF

Info

Publication number
WO2018207958A1
WO2018207958A1 PCT/KR2017/004876 KR2017004876W WO2018207958A1 WO 2018207958 A1 WO2018207958 A1 WO 2018207958A1 KR 2017004876 W KR2017004876 W KR 2017004876W WO 2018207958 A1 WO2018207958 A1 WO 2018207958A1
Authority
WO
WIPO (PCT)
Prior art keywords
sunscreen
cosmetic composition
rubber sponge
cosmetic
foam rubber
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/KR2017/004876
Other languages
English (en)
French (fr)
Inventor
박성미
박명삼
김희용
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Cosmax Inc
Original Assignee
Cosmax Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Cosmax Inc filed Critical Cosmax Inc
Priority to US16/611,619 priority Critical patent/US20200154850A1/en
Priority to PCT/KR2017/004876 priority patent/WO2018207958A1/ko
Priority to EP17909176.4A priority patent/EP3622944A4/en
Priority to CN201780090555.1A priority patent/CN110612091A/zh
Publication of WO2018207958A1 publication Critical patent/WO2018207958A1/ko
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

본 발명은 발포 고무 스펀지와 발포 고무 스펀지에 함침되는 화장료 조성물을 포함하는 화장품에 있어서, 상기 화장료 조성물은 자외선 차단제로서 무기 자외선 차단제만을 포함하는 것을 특징으로 하는 자외선 차단 화장품에 관한 것이다. 본 발명에 따르면, 발포 고무 스펀지와 발포 고무 스펀지에 함침되는 화장료 조성물을 포함하는 화장품에 있어서, 상기 화장료 조성물에 자외선 차단제로서 무기 자외선 차단제만을 포함하도록 한 자외선 차단 화장품의 경우, 발포 고무 스펀지에 함침되는 자외선 차단제 조성물 중, 무기 자외선 차단제 성분은 발포 고무 스펀지에 흡착되지 않아 흡착에 의한 손실 없이 모두 배출할 수 있기 때문에 함침 후에도 내용물에 부가한 자외선 차단 효과를 온전히 발휘할 수 있다. 또한, 본원발명의 발포 고무 스펀지는 발포시 포어 사이즈를 조절함으로써 함침된 내용물 용량 대비 소비자가 사용할 수 있는 양의 비율을 개선하여 사용량의 효율을 높였다.

Description

자외선 차단 기능을 가진 화장료 조성물이 함침된 화장품
본 발명은 자외선 차단 기능을 가진 화장료 조성물이 함침된 화장품에 관한 것으로, 더욱 구체적으로 발포 고무 스펀지와 발포 고무 스펀지에 함침되는 화장료 조성물을 포함하는 화장품에 있어서, 상기 화장료 조성물은 자외선 차단제로서 무기 자외선 차단제만을 포함하는 것을 특징으로 하는 자외선 차단 화장품에 관한 것이다.
최근 환경오염으로 인한 오존층의 파괴로 자외선의 지표도달 양이 증가 되어 자외선이 인체에 미치는 영향에 대해 많은 연구가 행해지고 있는 가운데 가장 대표적인 것이 자외선에 대한 지속적인 노출로써 발생 되는 피부노화에 관한 것이다. 상기와 같은 피부노화 현상을 지연시키기 위한 방법으로, 일차적으로는 자외선 차단제를 이용하여 자외선의 피부 투과를 감소시키는 방법이 있다. 이와 관련하여 현재 자외선(특히, UV-A, B)으로부터 피부를 보호하기 위한 자외선 차단 화장료 조성물에 대한 연구가 많이 진행되고 있다.
현재 화장품 업계에서 사용되는 자외선 차단제는 크게 무기 자외선 차단제와 유기 자외선 차단제로 나뉠 수 있다. 무기 자외선 차단제는 피부에 흡수되지 않고 표면에서만 작용하는 것으로 자외선을 반사하고 분산시키는 물리적 성질을 가진 물질로서, 예컨대 티타늄디옥사이드, 징크옥사이드 등을 포함한다. 무기 자외선 차단제는 굴절률이 높아 자외선을 산란시키는 효과 및 피부 자극이 적다는 장점이 있으나 백탁현상을 유발하는 단점이 있다. 유기 자외선 차단제는 태양광선 에너지를 분자 내 잡아둠으로써 자외선을 흡수하여 차단효과를 나타내는 물질로서, 예컨대 에틸헥실메톡시신나메이트, 옥틸메톡시신나메이트, 에칠헥실살리실레이트 등을 포함한다. 유기 자외선 차단제는 무기 자외선 차단제와는 달리 백탁현상이 없으나 피부 자극을 유발한다는 단점이 있다.
자외선 차단용 화장품에 사용되고 있는 제형으로는 액상, 크림상, 스프레이형, 스틱형이 있다. 그러나 액상 및 크림상 자외선 차단 화장품은 손에 덜어 펴서 발라야 하는 사용상의 불편함이 있고 스프레이형이나 스틱형의 경우에는 안면에 적용이 어려워 용도가 제한적이라는 단점이 있다. 상기와 같은 문제점을 해결하기 위하여 최근 다공성 스펀지나 다공성 폼에 화장료 조성물을 함침시켜 사용하는 제형이 개발되었다.
한국등록특허 제1542917호는 상기와 같이 스펀지에 화장료 조성물을 함침시킨 화장품에 관한 것으로, 상기 화장료 조성물은 자외선 차단제로서 유기 자외선 차단제만을, 또는 유기 자외선 차단제 및 무기 자외선 차단제를 함유하고 있는 것이 특징이다. 그러나, 유기 자외선 차단제 성분의 경우에는 스펀지에 흡착되는 성질을 가지고 있어 스펀지에 함침된 화장료 조성물을 소비자가 실질적으로 사용하고자 하였을 때, 함침 전 화장료 조성물의 자외선 차단 효과 대비 배출되는 화장료 조성물의 자외선 차단 효과가 낮아질 수 밖에 없다. 또한, 기존 포어사이즈가 작은 고무제 스폰지의 경우는 화장료 조성물을 충전량 대비 사용량의 효율이 낮은 문제점이 있다.
이에, 본 발명자들은 상기 종래기술들의 문제점들을 극복하기 위하여 예의 연구노력한 결과, 포어사이즈를 제어한 발포 고무 스펀지와 발포 고무 스펀지에 함침되는 화장료 조성물을 포함하는 화장품에 있어서, 상기 화장료 조성물에 자외선 차단제로서 무기 자외선 차단제만을 포함하도록 한 자외선 차단 화장품의 경우, 무기 자외선 차단제 성분이 발포 고무 스펀지에 흡착되지 않아 흡착에 의한 손실 없이 모두 배출할 수 있기 때문에 함침 후에도 내용물에 부가한 자외선 차단 효과를 온전히 발휘할 수 있다. 또한, 본원발명의 발포 고무 스펀지는 발포시 포어 사이즈를 조절함으로써 함침된 내용물 용량 대비 소비자가 사용할 수 있는 양의 비율을 개선하여 사용량의 효율을 높여 본 발명을 완성하게 되었다.
따라서, 본 발명의 주된 목적은 스펀지에 함침되기 전의 내용물이 함침 후에도 실제 부가된 자외선 차단 기능을 온전히 발휘될 수 있는 화장료 조성물 및 화장품을 제공하는 데 있다.
본 발명의 또 다른 목적은 고무제 스펀지의 발포 사이즈를 제어함으로써, 충전량 대비 사용량의 효율을 증가시키는 데 있다.
본 발명의 한 양태에 따르면, 본 발명은 발포 고무 스펀지와 발포 고무 스펀지에 함침되는 화장료 조성물을 포함하는 화장품에 있어서, 상기 화장료 조성물은 자외선 차단제로서 무기 자외선 차단제만을 포함하는 것을 특징으로 하는 자외선 차단 화장품을 제공한다.
종래에 스펀지에 자외선 차단 기능을 갖는 화장료 조성물을 함침시키는 화장품의 경우, 일반적으로 유기 자외선 차단제 성분 또는 유기 자외선 차단제 및 무기 자외선 차단제 성분을 함유하고 있는데, 유기 자외선 차단제 성분의 경우에는 스펀지에 흡착되는 성질을 갖고 있어 스펀지에 함침되는 양 대비 배출되는 유기 자외선 차단제의 양이 적어 자외선 차단의 효율성이 낮다는 단점이 있다. 이에, 본 발명자들은 상기 문제점을 해결하기 위하여 발포 고무 스펀지에 함침되는 화장료 조성물에 유기 자외선 차단제는 제외하고 무기 자외선 차단제 성분만을 포함하도록 한 자외선 차단 화장품을 발명하게 되었다.
본 발명의 실험예에 따르면, 동일한 포어, 밀도 및 경도를 갖는 발포 고무 스펀지에 무기 자외선 차단제만을 함유하는 화장료 조성물을 함침시킨 자외선 차단 화장품(실시예 1)과 유기 자외선 차단제 및 무기 자외선 차단제를 함유하는 화장료 조성물을 함침시킨 자외선 차단 화장품의 화장료 조성물(비교예 1)의 함침 대비 배출 정도를 확인한 결과, 화장료 조성물 함침 대비 배출되는 양은 실시예 1이 비교예 1보다 더 높았고 이러한 결과를 토대로 사용효율(소진량/충전량(%))을 계산한 결과, 실시예 1의 사용 효율이 더 높은 것을 확인할 수 있었다. 이러한 결과로 볼 때, 본 발명의 자외선 차단 화장품은 화장료 조성물의 우수한 배출로서 더욱 효과적인 자외선 차단 효과를 나타낼 수 있음을 알 수 있다.
또한, 본 발명의 실험예에 따르면, 무기 자외선 차단제만을 함유하는 화장료 조성물을 함침시킨 자외선 차단 화장품(실시예 1)과 유기 자외선 차단제 및 무기 자외선 차단제를 함유하는 화장료 조성물을 함침시킨 자외선 차단 화장품의 화장료 조성물(비교예 1-3)의 제형 안정성을 확인한 결과, 발포 고무 스펀지의 포어 사이즈 및 밀도가 동일(비고예 1)하거나 작은(비교예 2) 경우에는 본원발명과 같이 내용물이 분리되지 않고 안정한 결과를 나타내었으나, 본원발명보다 포어 사이즈가 큰 비교예 3의 경우에는 내용물이 분리되는 현상이 나타났다. 이러한 결과로 볼 때, 본원발명의 발포 고무 스펀지는 내용물을 안정하게 함침시켜 내용물이 분리되지 않도록 함으로써 제형 안정성을 유지시켜 줄 수 있음을 의미한다.
본 발명에 있어서, 상기 자외선 차단 화장품은 유기 자외선 차단제를 포함하지 않는 것을 특징으로 한다.
유기 자외선 차단제는 스펀지에 흡착되는 성질을 가지고 있어 자외선을 더욱 효율적으로 차단 하기에는 한계가 있기 때문에 본 발명은 유기 자외선 차단제를 함유하지 않는다.
본 발명의 실험예에 따르면, 유기 자외선 차단제를 함유하는 비교예(1-3)의 경우, 함침된 유기 자외선 차단제 양 대비 배출되는 유기 자외선 차단제 양의 비 율이 낮은 것을 확인할 수 있었다. 이에 반해, 무기 자외선 차단제의 경우에는 함침된 무기 자외선 차단제 양 대비 배출되는 무기 자외선 차단제 양의 비율이 100%인 것을 확인할 수 있었다. 이러한 결과로 볼 때, 무기 자외선 차단제만을 함침하는 본원발명의 자외선 차단 화장품은 무기 자외선 차단제가 스펀지에 흡착되지 않고 제품을 이용 시 온전히 모두 배출됨으로써, 더욱 우수한 자외선 차단 효과를 나타낼 수 있음을 알 수 있다.
본 발명에 있어서, 상기 발포 고무 스펀지는 포어 사이즈가 0.1 내지 1.0㎜, 밀도가 150 내지 250g/L, 및 애스커 경도기 F 기준으로 경도가 22±5 인 것을 특징으로 한다. 포어 사이즈가 상기 범위 미만이면 함침이 어려울 뿐만 아니라 충전량 대비 사용량 효율이 적다는 문제점이 있고, 포어 사이즈가 상기 범위를 초과하면 충전량 대비 사용량 효율은 좋으나 포어 사이즈가 너무 커 내용물의 안정도가 좋지 않으며 내용물을 포집하고 있는 힘이 작아서 작은 충격에도 내용물이 배출된다는 문제점이 있다. 상기 발포 고무 스펀지의 밀도가 상기 범위 미만이면 화장료 조성물이 너무 많이 묻어나 사용성이 떨어지며, 밀도가 상기 범위를 초과하면 내용물을 함침할 수 있는 포어(pore)가 부족하여 효과적으로 함침하기 어려운 문제가 있다.
본 발명에 있어서, 상기 발포 고무 스펀지는 무기 자외선 차단제를 포함하는 화장료 조성물을 함침 시킬 수 있는 것이라면 어떠한 것도 사용될 수 있으며, 바람직하게는 SBR(styrene-butadiene rubber), BR(butadiene rubber), NR(acrylonitrile rubber) 또는 NBR(acrylonitrile-butadiene rubber)일 수 있으며, 더욱 바람직하게는 NBR(acrylonitrile-butadiene rubber)인 것을 특징으로 한다.
본 발명에 있어서, 상기 발포 고무 스펀지에 함침되는 화장료 조성물은 점도가 4,000 내지 15,000cps 인 것을 특징으로 한다. 화장료 조성물의 점도가 4,000cps 미만일 경우에는 함침 전의 벌크상태 내용물의 분리가 빨리 일어나 부적합하며, 15,000cps 초과의 내용물은 점도가 너무 높아 함침이 어렵고, 쿠션의 장점인 얇고 가벼운 사용감이 줄어든다는 문제점이 있다.
본 발명에 있어서, 상기 화장료 조성물은 메이크업 베이스(make-up base), 비비(Blemish Balm)크림, 파운데이션(foundation), 프라이머(primer) 또는 선스크린(sunscreen)인 것을 특징으로 한다.
본 발명에 따른 화장료 조성물의 제조는 성분의 종류, 함량 및 제형 등을 고려하여, 당업계에 공지된 통상의 방법에 따를 수 있다. 또한, 제조된 화장료 조성물을 발포 고무 스펀지에 함침하는 공정 역시 당업계에 공지된 통상의 방법에 따를 수 있다.
이상 설명한 바와 같이, 본원발명의 자외선 차단 기능을 갖는 화장료 조성물이 함침된 화장품은 화장료 조성물의 자외선 차단제로서 무기 자외선 차단제만을 포함하도록 함으로써, 화장품 사용시 발포 고무 스펀지에 함침된 화장료 조성물 양 대비 배출되는 양의 비율이 더 높고 무기 자외선 차단제가 발포 고무 스펀지에 흡착되지 않기 않으므로, 자외선 차단 효과가 매우 우수할 뿐만 아니라 제형 안정성 또한 우수하다.
이하, 실시예를 통하여 본 발명을 더욱 상세히 설명하기로 한다. 이들 실시예는 단지 본 발명을 예시하기 위한 것이므로, 본 발명의 범위가 이들 실시예에 의해 제한되는 것으로 해석되지는 않는다.
본 발명에 따른 W/O 유화 메이크업 화장료 조성물을 하기 표 1에 기재된 성분 및 함량으로 실시예1, 비교예 1 내지 3의 파운데이션을 제조하였다.
실시예 1: 무기 자외선 차단제만을 함유하는 화장료 조성물 제조
실시예 1은 무기 자외선 차단제만을 함유하는 유중수형 화장료 조성물을 포어 사이즈가 0.1 내지 1.0mm 이고, 밀도가 150 내지 250g/L인 고무스펀지에 담지시킨 예로서, 유중수형 파운데이션은 표 1의 조성 및 함량으로 다음과 같이 제조하였다.
유상조에 유상성분과 점증제를 넣고 70℃로 열을 가하여 균일하게 한 후, 피그먼트를 넣고 분산 시켰다. 수상조에는 수상 성분을 넣고, 70℃로 교반하면서 열을 가하여 완전히 용해시킨 후, 피그먼트가 분산되어 있는 유상조에 천천히 투입시키고 호모믹서로 유화하여 유중수형의 저점도 자외선 차단 유화물을 제조하였다.
비교예 1: 무기 및 유기 자외선 차단제를 함유하는 화장료 조성물 제조
비교예 1은 무기 및 유기 자외선 차단제를 함유하는 유중수형 화장료 조성물을 포어사이즈가 0.1 내지 1.0mm 이고, 밀도가 150 내지 250g/L인 고무스펀지에 담지 시킨 예로서, 유중수형 파운데이션의 제조는 표 1의 조성 및 함량으로 상기 실시예 1과 동일한 방법으로 제조하였다.
비교예 2: 무기 및 유기 자외선 차단제를 함유하는 화장료 조성물 제조
비교예 2는 무기 및 유기 자외선 차단제를 함유하는 유중수형 화장료 조성물을 포어사이즈가 평균 0.15mm이고, 밀도가 330g/L인 고무스펀지에 담지 시킨 예로서, 유중수형 파운데이션의 제조는 표 1의 조성 및 함량으로 상기 실시예 1과 동일한 방법으로 제조하였다.
비교예 3: 무기 및 유기 자외선 차단제를 함유하는 화장료 조성물 제조
비교예 3은 무기 및 유기 자외선 차단제를 함유하는 유중수형 화장료 조성물을 포어사이즈가 평균 1.2mm이고, 밀도가 90g/L인 고무스펀지에 담지 시킨 예로서, 유중수형 파운데이션의 제조는 상기 실시예 1과 동일한 방법으로 제조하였다.
구분 원료명 함량(중량%)
실시예1 비교예1 비교예2 비교예3
유상성분 사이클로펜타실록산 25.0 14.5 14.5 14.5
에칠헥실메톡시신나메이트 - 7.5 7.5 7.5
에칠헥실살리실레이트 - 4.0 4.0 4.0
카프릴릭/카프릭트리글리세라이드 5.0 5.0 5.0 5.0
피이지-10디메치콘 3.0 3.0 3.0 3.0
디페닐실록시페닐트리메치콘 2.0 2.0 2.0 2.0
디메치콘 2.0 2.0 2.0 2.0
소르비탄이소스테아레이트 1.0 1.0 1.0 1.0
점증제 디스테아디모늄헥토라이트 적량 적량 적량 적량
피그먼트 이산화티탄 4.0 4.0 4.0 4.0
이산화티탄알루미늄하이드록사이드스테아릭애씨드 9.0 9.0 9.0 9.0
황색산화철 0.8 0.8 0.8 0.8
적색산화철 0.2 0.2 0.2 0.2
흑색산화철 0.1 0.1 0.1 0.1
마이카 4.0 4.0 4.0 4.0
수상성분 정제수 to 100 to 100 to 100 to 100
글리세린 5.0 5.0 5.0 5.0
소금 1.0 1.0 1.0 1.0
　
적용 스펀지 NBR 포어사이즈 0.5mm밀도 200g/L NBR 포어사이즈 0.5mm밀도 200g/L NBR 포어사이즈 0.15mm밀도 330g/L NBR 포어사이즈 1.2mm밀도 90g/L
실험예 1: 화장료 조성물의 함침 대비 배출 정도 효과 실험
실험예 1은 상기 실시예와 비교예1, 2, 3 제품을 내용물 14.5g 함침시켜, 25℃ 항온조에서 하루이상 보관하였다.
아래와 같은 방법으로 각 단계별 사용량을 측정한 값을 하기 표 2 내지 4에 나타내었다.
<측정방법>
(1단계) 루비셀 퍼프를 이용하여 흰색 종이에 칠하여 내용물이 거의 묻어 나오지 않을 때까지 취한량
(2단계) 함침용 스폰지의 뒷면을 앞으로 뒤짚은 후 루비셀 퍼프를 이용하여 흰색 종이에 칠하여 내용물이 거의 묻어 나오지 않을 때까지 취한량
(3단계) 함침용 스폰지를 꺼내어 직접 흰색 종이에 칠하여 내용물이 거의 묻어 나오지 않을 때까지 취한량
실시예1 Applicator 충진량(g) 1 단계 소진량(g) 2단계 소진량(g) 3단계 소진량(g) 총 소진량(g) 소진량/충전량(%)
Sample No.1 퍼프 14.5 9.18 3.22 0.84 13.24 91.31
Sample No.2 퍼프 14.5 9.4 2.41 1.2 13.01 89.72
Sample No.3 퍼프 14.5 9.52 3.01 0.91 13.44 92.69
Average 91.24
비교예1 Applicator 충진량(g) 1단계 소진량(g) 2단계소진량 (g) 3단계 소진량 (g) 총 소진량(g) 소진량/충전량(%)
Sample No.1 퍼프 14.5 8.95 1.79 1.31 12.05 83.10
Sample No.2 퍼프 14.5 8.69 1.95 1.95 12.59 86.83
Sample No.3 퍼프 14.5 9.26 2.06 0.65 11.97 82.55
Average 84.16
비교예2 Applicator 충진량 (g) 1단계소진량 (g) 2단계소진량 (g) 3단계소진량 (g) 총소진량(g) 소진량/충전량(%)
Sample No.1 퍼프 14.5 5.2 2.04 2.85 10.09 69.59
Sample No.2 퍼프 14.5 3.39 2.1 4.25 9.74 67.17
Sample No.3 퍼프 14.5 5.8 2.55 2.8 11.15 76.90
Average 71.22
비교예3 Applicator 충진량 (g) 1단계소진량 (g) 2단계소진량 (g) 3단계소진량 (g) 총소진량(g) 소진량/충전량(%)
Sample No.1 퍼프 14.5 9.01 2.72 0.94 12.67 87.38
Sample No.2 퍼프 14.5 9.19 2.54 0.7 12.43 85.72
Sample No.3 퍼프 14.5 9.21 2.51 0.85 12.57 86.69
Average 86.60
그 결과 상기 표 2 내지 5에서 나타나는 바와 같이, 무기 및 유기 자외선 차단제 모두를 포함하는 유화물을 포어 사이즈 0.15mm, 밀도 330g/L의 고무 스펀지에 함침한 비교예 2의 사용 효율이 약 71%로 가장 낮았고, 무기 차단제 단독 포함하는 유화물을 포어 사이즈 0.5mm, 밀도 200g/L의 고무 스펀지에 함침한 실시예 1의 효율이 약 91%로 가장 좋았으며, 사용량의 차이는 대략 20%라는 것을 확인할 수 있었다.
실험예 2: 자외선 차단제 처방 함량 대비 분석 함량 실험
실시예 1과 비교예 1 내지 3의 파운데이션을 14.5g씩 함침한 후 25℃ 항온조에 하루 이상 보관하였다.
먼저, 상기 4가지 샘플의 파운데이션이 함침된 스폰지를 각각 손으로 압박하여 짜내어 파운데이션을 채득하였다.
식품의약품 안전처 고시 제2013-28호 기능성 화장품 기준 및 시험방법(KFCC)에 따라, 스펀지에 함침하기 이전의 파운데이션과 스펀지로부터 채득한 파운데이션을 각각 용매에 녹여 액체크로마토그래프법에 따라 자외부흡광광도계로 시험하여 에칠헥실메톡시신나메이트(EHMC)와 에칠헥실살리실레이트(EHS)의 피크면적 AT 및 표준품의 피크면적 AS를 구하여 함침 이전과 함침 이후의 변화된 값을 분석하였다.
그리고 이산화티탄(TiO2)는 스폰지에 함침하기 이전의 파운데이션과 스폰지로부터 채득한 파운데이션을 산에 넣어 전처리하여 유도결합플라즈마 분광광도기로 시험하여 함침 이전과 함침 이후의 변화된 값을 하기 식 1 내지 3에 따라 계산 및 분석하였다. 그 결과를 표 6에 나타내었다.
[식 1]
에칠헥실메톡시신나메이트의 양 (mg) = AT/ AS X 에칠헥실메톡시신나메이트 표준품의 양(mg) X 1/10
[식 2]
에칠헥실살리실레이트의 양 (mg) = AT/ AS X 에칠헥실살리실레이트 표준품의 양(mg) X 1/10
[식 3]
티타늄디옥사이드 양 함량 (%) = (Ti 측정농도(ppm) X 검액용량(mL) X 1.668494) / (검체 채취량(g) X 10000)
구분　 분석성분 함량 (처방함량 대비 비율)
EHMC EHS 이산화티탄
실시예1 ─ ─ 11.63 (101.3%)
비교예1 4.36 (58.1%) 2.77 (69.3%) 11.71 (102%)
비교예2 4.25 (56.6%) 2.65 (66.2%) 11.83 (103%)
비교예3 4.79 (63.8%) 2.95 (73.7%) 11.75 (102%)
고무 스펀지에서 유기 자외선 차단제의 처방대비 배출 함량을 분석하였을 때, 에칠헥실메톡시신나메이트는 평균 59.5%, 에칠헥실살리실레이트는 평균 69.7% 만이 분석되는 결과로, 고무제 스펀지에 흡착되어 배출되는 양이 크게 감소함을 알 수 있었다. 이에 반해 무기 자외선 차단제인 이산화티탄의 경우, 처방대비 100% 분석됨으로써, 고무 스펀지에 흡착되지 않고, 제품 이용시 처방 대비 온전히 다 배출됨을 확인 할 수 있었다.
실험예 3: 제형 안정도 실험
상기 표 1의 4가지 파운데이션 제품에 대하여 하기 표 7의 조건으로 제형의 안정도 테스트를 진행하였고, 그 결과는 하기 표 7에 나타내었다.
　 45℃ 15일 관찰 싸이클 (-10℃ → 15℃ → 40℃ 각 8시간 씩) 5일 관찰
실시예1 안정 안정
비교예1 안정 안정
비교예2 안정 안정
비교예3 내용물 분리 현상 보임 내용물 분리 현상 보임
그 결과 상기 표 7에서 나타나는 바와 같이, 본 발명에 따른 W/O 유화메이크업 화장료 조성물을 포어 사이즈와 밀도가 다른 고무 스펀지에 함침시켜 안정도를 비교한 결과 포어 사이즈가 평균 1.2mm인 비교예 3은 각 항온조에서 제형이 분리되어 불안정하였다.

Claims (5)

  1. 발포 고무 스펀지와 발포 고무 스펀지에 함침되는 화장료 조성물을 포함하는 화장품에 있어서, 상기 화장료 조성물은 자외선 차단제로서 무기 자외선 차단제만을 포함하고 유기 자외선 차단제를 포함하지 않는 것을 특징으로 하는 자외선 차단 화장품.
  2. 제 1항에 있어서, 상기 발포 고무 스펀지는 포어 사이즈가 0.1 내지 1.0㎜, 밀도가 150 내지 250g/L, 및 애스커 경도기 F 기준으로 경도가 22±5 인 것을 특징으로 하는 자외선 차단 화장품.
  3. 제 1항에 있어서, 상기 발포 고무 스펀지는 상기 발포 고무 스펀지는 SBR(styrene-butadiene rubber), BR(butadiene rubber), NR(acrylonitrile rubber) 또는 NBR(acrylonitrile-butadiene rubber)인 것을 특징으로 하는 자외선 차단 화장품.
  4. 제 1항에 있어서, 상기 발포 고무 스펀지에 함침되는 화장료 조성물은 점도가 4,000 내지 15,000cps 인 것을 특징으로 하는 자외선 차단 화장품.
  5. 제 1항에 있어서, 상기 화장료 조성물은 메이크업 베이스(make-up base), 비비(Blemish Balm)크림, 파운데이션(foundation), 프라이머(primer) 또는 선스크린(sunscreen)인 것을 특징으로 하는 자외선 차단 화장품.
PCT/KR2017/004876 2017-05-11 2017-05-11 자외선 차단 기능을 가진 화장료 조성물이 함침된 화장품 Ceased WO2018207958A1 (ko)