WO2020069619A1 - Additives for electrolytes in li-ion batteries - Google Patents

Additives for electrolytes in li-ion batteries

Info

Publication number
WO2020069619A1
WO2020069619A1 PCT/CA2019/051415 CA2019051415W WO2020069619A1 WO 2020069619 A1 WO2020069619 A1 WO 2020069619A1 CA 2019051415 W CA2019051415 W CA 2019051415W WO 2020069619 A1 WO2020069619 A1 WO 2020069619A1
Authority
WO
WIPO (PCT)
Prior art keywords
battery
compound
alkyl
cyano
electrolyte
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/CA2019/051415
Other languages
French (fr)
Inventor
Charlotte MALLET
Sylviane ROCHON
Karim Zaghib
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hydro Quebec
Murata Manufacturing Co Ltd
Original Assignee
Hydro Quebec
Murata Manufacturing Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority to KR1020257005078A priority Critical patent/KR20250026888A/en
Priority to KR1020257041542A priority patent/KR20260006044A/en
Priority to KR1020217008795A priority patent/KR102925738B1/en
Priority to CN201980062375.1A priority patent/CN112771022B/en
Priority to JP2021516923A priority patent/JP7460612B2/en
Priority to CN202410234917.1A priority patent/CN118099524A/en
Priority to CN202410234961.2A priority patent/CN118117168A/en
Priority to US17/281,120 priority patent/US12100807B2/en
Priority to EP19868859.0A priority patent/EP3860974A4/en
Application filed by Hydro Quebec, Murata Manufacturing Co Ltd filed Critical Hydro Quebec
Priority to CN202410235009.4A priority patent/CN118099525A/en
Priority to CA3112350A priority patent/CA3112350C/en
Priority to KR1020257005075A priority patent/KR20250026887A/en
Publication of WO2020069619A1 publication Critical patent/WO2020069619A1/en
Anticipated expiration legal-status Critical
Priority to JP2023200825A priority patent/JP2024026195A/en
Priority to US18/893,679 priority patent/US12614756B2/en
Priority to JP2025101544A priority patent/JP2025131854A/en
Ceased legal-status Critical Current

Abstract

Method of improving the performance and safety of a Li-ion battery. The method comprises using a nitrile-based small organic compound of general formula I, V or IX outlined below in association with the electrolyte of the battery.

Description

TITLE OF THE INVENTION
ADDITIVES FOR ELECTROLYTES IN Li-ION BATTERIES
FIELD OF THE INVENTION
[0001] The present invention relates generally to additives for Li-ion batteries. More specifically, the present invention relates to nitrile-based additives for use in association with the electrolyte in Li-ion batteries.
BACKGROUND OF THE INVENTION
[0002] Li-ion batteries are widely used as energy source, and the demand is increasing. Typically, such battery comprises a negative electrode or anode, a positive electrode or cathode, and an electrolyte provided between the two spaced-apart electrodes. The electrolyte may comprise organic molecules or polymers and generally also comprises a lithium salt such as LiPF6, LiTFSI or LiFSI. Moreover, the electrolyte may comprise linear carbonates such as dimethyl carbonate (DMC), diethyl carbonate (DEC), ethylmethyl carbonate (EMC) or cyclic carbonates such as ethylene carbonate (EC), propylene carbonate (PC) and butylene carbonate (BC).
[0003] Various studies related to the nature and composition of electrolytes and aimed at improving the performance and safety of Li-ion batteries, are reported in the art. For example, the use of additives comprising one or more nitrile groups is reported [1-3] Indeed, it is known in the art that organic compounds comprising nitrile groups present good electrochemical properties and stability at high voltage and temperature.
[0004] There is still a need for methods of improving the performance and safety of Li-ion batteries. In particular, there is a need for nitrile-based organic compounds for use as additives in electrolytes.
SUMMARY OF THE INVENTION
[0005] The inventors have designed and prepared an additive for use in association with the electrolyte in a Li-ion battery. The additive of the invention is an organic compound as described herein below and which comprises at least one nitrile group. The organic compound is compatible with the electrolyte as well as other components of the battery. [0006] The invention thus provides the following in accordance with aspects thereof:
(1) A method of improving the performance and safety of a Li-ion battery, comprising using a nitrile-based organic compound in association with the electrolyte of the battery, wherein the compound has a general formula I outlined below
Figure imgf000004_0001
wherein:
Q is a 5 to 12-member ring or bicycle ring, optionally the ring comprises one or more heteroatom which are the same or different and selected from the group consisting of N, O and S; preferably Q is a 5-10-, or a 5-, or a 6-member ring or bicycle ring;
L is present or absent and is a linker comprising one or more of alkyl, alkene and alkyne groups; and
m in an integer from 1 to 10, or 1 to 6, or 1 to 5, or 1 to 4, or 1 to 3.
(2) A method of improving the performance and safety of a Li-ion battery, comprising using a nitrile-based organic compound in association with the electrolyte of the battery, wherein the compound has a general formula II outlined below
Figure imgf000004_0002
wherein:
X is C or N;
L is present or absent and is a linker comprising one or more of alkyl, alkene and alkyne groups;
Ri each independently selected from the group consisting of H, alkyl, cycloalkyl, alkene, alkyne, aryl and alkylaryl, alkoxy, thioalkoxy, OH, SH, NH2, a halogen atom, a halogeno alkyl, a halogeno alkoxy, a halogeno thioalkoxy, a cyano alkyl, a cyano alkene, a cyano alkyne, CN, NO2, SO2, COOH and acyloxycarbonyl; preferably selected from the group consisting of H, alkyloxy, halogen, halogeno alkyl, nitro, and cyano; more preferably selected from the group consisting of H, halogen, nitro and cyano;
m is an integer from 1 to 5, or 1 to 4, or 1 to 3; and
m’ is an integer from 0 to 5, or 0 to 4, or 0 to 3, or 1 to 5, or 1 to 4, or 1 to 3.
(3) A method of improving the performance and safety of a Li-ion battery, comprising using a nitrile-based organic compound in association with the electrolyte of the battery, wherein the compound has a general formula III outlined below
Figure imgf000005_0001
wherein:
X is C or N;
Ri are each independently selected from the group consisting of H, alkyl, cycloalkyl, alkene, alkyne, aryl and alkylaryl, alkoxy, thioalkoxy, OH, SH, NH2, a halogen atom, a halogeno alkyl, a halogeno alkoxy, a halogeno thioalkoxy, a cyano alkyl, a cyano alkene, a cyano alkyne, CN, NO2, SO2, COOH and acyloxycarbonyl; preferably Ri are each independently selected from the group consisting of H, alkyloxy, halogen, halogeno alkyl, nitro, and cyano; more preferably selected from the group consisting of H, halogen, nitro and cyano; and
m’ is an integer from 0 to 5, or 0 to 4, or 0 to 3, or 1 to 5, or 1 to 4, or 1 to 3.
(4) A method of improving the performance and safety of a Li-ion battery, comprising using a nitrile-based organic compound in association with the electrolyte of the battery, wherein the compound has a general formula IV outlined below
Figure imgf000006_0001
wherein:
X is C or N;
Ri are each independently selected from the group consisting of H, alkyl, cycloalkyl, alkene, alkyne, aryl and alkylaryl, alkoxy, thioalkoxy, OH, SH, NH2, a halogen atom, a halogeno alkyl, a halogeno alkoxy, a halogeno thioalkoxy, a cyano alkyl, a cyano alkene, a cyano alkyne, CN, NO2, SO2, COOH and acyloxycarbonyl; preferably selected from the group consisting of H, alkyloxy, halogen, halogeno alkyl, nitro and cyano; more preferably selected from the group consisting of H, halogen, nitro and cyano; and
m’ is an integer from 0 to 5, or 0 to 4, or 0 to 3, or 1 to 5, or 1 to 4, or 1 to 3.
(5) A method of improving the performance and safety of a Li-ion battery, comprising using a nitrile-based organic compound in association with the electrolyte of the battery, wherein the compound has a general formula A outlined below
Figure imgf000006_0002
wherein: R1 to R5 are each independently selected from the group consisting of H, alkyl, cycloalkyl, alkene, alkyne, aryl and alkylaryl, alkoxy, thioalkoxy, OH, SH, NH2, a halogen atom, a halogeno alkyl, a halogeno alkoxy, a halogeno thioalkoxy, a cyano alkyl, a cyano alkene, a cyano alkyne, CN, NO2, SO2, COOH and acyloxycarbonyl; preferably R1 to R5 are each independently selected from the group consisting of H, alkyloxy, halogen, halogeno alkyl, nitro and cyano; more preferably selected from the group consisting of H, halogen, nitro and cyano.
(6) A method of improving the performance and safety of a Li-ion battery, comprising using a nitrile-based organic compound in association with the electrolyte of the battery, wherein the compound has a general formula B outlined below
B
Figure imgf000007_0001
wherein:
X is C and R3 is H; or X is N; and
R1 to R5 are each independently selected from the group consisting of H, alkyl, cycloalkyl, alkene, alkyne, aryl and alkylaryl, alkoxy, thioalkoxy, OH, SH, NH2, a halogen atom, a halogeno alkyl, a halogeno alkoxy, a halogeno thioalkoxy, a cyano alkyl, a cyano alkene, a cyano alkyne, CN, NO2, SO2, COOH and acyloxycarbonyl; preferably R1 to R5 are each independently selected from the group consisting of H, alkyloxy, halogen, halogeno alkyl, nitro and cyano; more preferably selected from the group consisting of H, halogen, nitro and cyano.
(7) A method of improving the performance and safety of a Li-ion battery, comprising using a nitrile-based organic compound in association with the electrolyte of the battery, wherein the compound is A1 , A2, A3 or A4 outlined below
Figure imgf000008_0001
(8) A method of improving the performance and safety of a Li-ion battery, comprising using a nitrile-based organic compound in association with the electrolyte of the battery, wherein the compound is B1 , B2, B3, B4, B5, B6, B7 or B8 outlined below
Figure imgf000008_0002
B1 B2 B3
Figure imgf000009_0001
(9) A method of improving the performance and safety of a Li-ion battery, comprising using a nitrile-based organic compound in association with the electrolyte of the battery, wherein the compound has a general formula V outlined below
Figure imgf000009_0002
wherein: L is present or absent and is a linker comprising one of more of alkyl, alkene and alkyne groups; and
Ri to R3 are each independently alkyl groups; preferably C1 to C6 or C1 to C3 alkyl groups; more preferably at least one of R1 to R3 is CH3, or each of R1 to R3 is CH3.
(10) A method of improving the performance and safety of a Li-ion battery, comprising using a nitrile-based organic compound in association with the electrolyte of the battery, wherein the compound has a general formula VI outlined below
Figure imgf000010_0001
wherein:
n is an integer from 0 to 6, or 0 to 5, or 0 to 4, or 0 to 3, or 0 to 2; preferably n is an integer from 0 to 3; more preferably n is 0 or 1 ; and
R1 to R3 are each independently alkyl groups; preferably C1 to C6 or C1 to C3 alkyl groups; more preferably at least one of R1 to R3 is CH3, or each of R1 to R3 is CH3.
(11) A method of improving the performance and safety of a Li-ion battery, comprising using a nitrile-based organic compound in association with the electrolyte of the battery, wherein the compound has a general formula C outlined below
Figure imgf000010_0002
wherein n is an integer from 0 to 6, or 0 to 5, or 0 to 4, or 0 to 3, or 0 to 2; preferably n is an integer from 0 to 3; more preferably n is 0 or 1.
(12) A method of improving the performance and safety of a Li-ion battery, comprising using a nitrile-based organic compound in association with the electrolyte of the battery, wherein the compound is C1 or C2 outlined below
Figure imgf000011_0001
Cl C2
or
(13) A method of improving the performance and safety of a Li-ion battery, comprising using a nitrile-based organic compound in association with the electrolyte of the battery, wherein the compound has a general formula IX outlined below
IX
Figure imgf000011_0002
wherein:
Ri is CN or CH3;
Li and L2 are each independently present or absent and are each independently a linker comprising alkyl, alkene and/or alkyne groups; and
Y is Na, K or Li; preferably Y is Na.
(14) A method of improving the performance and safety of a Li-ion battery, comprising using a nitrile-based organic compound in association with the electrolyte of the battery, wherein the compound has a general formula X outlined below
X
Figure imgf000011_0003
wherein:
Li and L2 are each independently present or absent and are each independently a linker comprising one or more of alkyl, alkene and alkyne groups; and
Y is Na, K or Li; preferably Y is Na. (15) A method of improving the performance and safety of a Li-ion battery, comprising using a nitrile-based organic compound in association with the electrolyte of the battery, wherein the compound has a general formula XI outlined below
XI
Figure imgf000012_0001
wherein:
n1 and n2 are each independently an integer from 0 to 10, or 0 to 6, or O to 3; preferably at least one of n1 and n2 is 0, or both n1 and n2 are 0; and
Y is Na, K or Li; preferably Y is Na.
(16) A method of improving the performance and safety of a Li-ion battery, comprising using a nitrile-based organic compound in association with the electrolyte of the battery, wherein the compound has a general formula D outlined below
D
Figure imgf000012_0002
wherein Y is Na, K or Li; preferably Y is Na.
(17) A method of improving the performance and safety of a Li-ion battery, comprising using a nitrile-based organic compound in association with the electrolyte of the battery, wherein the compound has a general formula D1 outlined below
Na+
Figure imgf000012_0003
D1
(18) A compound having a general formula VII outlined below
VII
Figure imgf000013_0001
wherein Ri and R2 are each independently selected from the group consisting of H, alkyl, cycloalkyl, alkene, alkyne, aryl and alkylaryl, alkoxy, thioalkoxy, OH, SH, NH2, a halogen atom, a halogeno alkyl, a halogeno alkoxy, a halogeno thioalkoxy, a cyano alkyl, a cyano alkene, a cyano alkyne, CN, N02, S02, COOH and acyloxycarbonyl; preferably selected from the group consisting of H, alkyloxy, halogen, halogeno alkyl, nitro and cyano; more preferably selected from the group consisting of H, halogen, nitro and cyano.
(19) A compound having a general formula VIII outlined below
VIII
Figure imgf000013_0002
wherein X is a halogen atom; preferably X is F.
(20) A compound of formula B4 outlined below B4
Figure imgf000014_0001
(21) A method of improving the performance and safety of a Li-ion battery, comprising using a nitrile-based organic compound in association with the electrolyte of the battery, wherein the compound as defined in any one of (18) to (20) above.
(22) The method according to any one of (1) to (17) and (21) above, wherein the nitrile-based organic compound is added to the electrolyte; optionally an amount of the additive (nitrile- based organic compound) is between about 0.01 to about 5.0%wt, or about 0.01 to about 3.0%wt, or about 0.01 to about 1.0%wt, or about 0.05 to about 1.0%wt, or about 0.1 to about 1.0%wt, about 0.1 to about 0.8%wt, or about 0.1 to about 0.5%wt, or about 0.1 to about 0.3%wt, is 0.1 %wt, or is 0.5%wt.
(23) An electrolyte comprising a compound which is selected from the group consisting of: I,
I, IV, A, B, A1 , A2, A3, A4, B1 , B2, B3, B4, B5, B6, B7, B8, V, VI, C, C1 , C2, IX, X, XI,
D, and D1 as defined in any one of the methods of (1) to (17) above.
(24) An electrolyte comprising the compound as defined in any one of (18) to (20) above.
(25) A battery comprising the electrolyte as defined in (23) or (24) above.
(26) An additive for an electrolyte for use in a Li-ion battery, comprising a compound which is selected from the group consisting of: I, II, III, IV, A, B, A1 , A2, A3, A4, B1 , B2, B3, B4, B5, B6, B7, B8, V, VI, C, C1 , C2, IX, X, XI, D, and D1 as defined in any one of the methods of (1) to (17) above.
(27) An additive for an electrolyte for use in a Li-ion battery, comprising a compound as defined in any one of (18) to (20) above.
(28) The method, electrolyte, battery or additive according to any one of (1) to (27) above, wherein the Li-ion battery is a battery wherein the cathode comprises a lithium-containing material;
(29) The method, electrolyte, battery or additive according to any one of (1) to (27) above, wherein the Li-ion battery is a battery wherein the cathode comprises lithium cobalt oxide (LCO), lithium manganese oxide (LMO), lithium nickel oxide (LNO) and the like including olivines, lithium oxides, nickel manganese cobalt oxide (NMC).
(30) The method, electrolyte, battery or additive according to (28) or (30) above, wherein the performance (capacity, reversibility) of the battery is improved.
[0007] Other objects, advantages and features of the present invention will become more apparent upon reading of the following non-restrictive description of specific embodiments thereof, given by way of example only with reference to the accompanying drawings.
BRIEF DESCRIPTION OF THE DRAWINGS
[0008] The patent or application file contains at least one drawing executed in color. Copies of this patent or patent application publication with color drawing(s) will be provided by the Office upon request and payment of the necessary fee.
[0009] In the appended drawings:
[0010] Figure 1 : Cycling data of LMFP-LTO battery (PC/EMC/DMC (4/3/3) + 1 M LiPF6 + 0.1 wt% additive according to the invention (a compounds of Serie A)) versus Reference after 300 cycles at 45°C. [0011] Figure 2: Static capacity (0.05C) of LMFP-LTO battery (PC/EMC/DMC (4/3/3) + 1 M LiPF6 + 0.1wt% additive according to the invention (a compound of Serie A)) versus Reference at 45°C.
[0012] Figure 3: Nyquist plots of LMFP-LTO battery (PC/EMC/DMC (4/3/3) + 1 M LiPF6 + 0.1 wt% additive according to the invention (a compound of Serie A)) versus Reference, at 0 and 100 cycles.
[0013] Figure 4: Cycling data of LMFP-LTO battery (PC/EMC/DMC (4/3/3) + 1 M LiPF6 + 0.5wt% additive according to the invention (a compounds of Serie B)) versus Reference after 300 cycles at 45°C.
[0014] Figure 5: Static capacity (0.05C) of LMFP-LTO battery (PC/EMC/DMC (4/3/3) + 1 M LiPF6 + 0.5wt% additive according to the invention (a compound of Serie B)) versus Reference at 45°C.
[0015] Figure 6: Nyquist plots of LMFP-LTO battery (PC/EMC/DMC (4/3/3) + 1 M LiPF6 + 0.5wt% additive according to the invention (a compound of Serie B)) versus Reference, at 0 and 200 cycles.
[0016] Figure 7: Cycling data of LMFP-LTO battery (PC/EMC/DMC (4/3/3) + 1 M LiPF6 + 0.5wt% additive according to the invention (a compounds of Serie C)) versus Reference after 300 cycles at 45°C.
[0017] Figure 8: Static capacity (0.05C) of LMFP-LTO battery (PC/EMC/DMC (4/3/3) + 1 M LiPF6 + 0.5wt% additive according to the invention (a compound of Serie C)) versus Reference at 45°C.
[0018] Figure 9: Nyquist plots of LMFP-LTO battery (PC/EMC/DMC (4/3/3) + 1 M LiPF6 + 0.5wt% additive according to the invention (a compound of Serie C)) versus Reference, at 0 and 100 cycles.
[0019] Figure 10: Cycling data of LMFP-LTO battery (PC/EMC/DMC (4/3/3) + 1 M LiPF6 + 0.5wt% additive according to the invention (a compounds of Serie D)) versus Reference after 100 cycles at 45°C. [0020] Figure 11 : Static capacity (0.05C) of LMFP-LTO battery (PC/EMC/DMC (4/3/3) + 1 M LiPF6 + 0.5wt% additive according to the invention (a compound of Serie D)) versus Reference at 45°C.
DESCRIPTION OF ILLUSTRATIVE EMBODIMENTS
[0021] Before the present invention is further described, it is to be understood that the invention is not limited to the particular embodiments described below, as variations of these embodiments may be made and still fall within the scope of the appended claims. It is also to be understood that the terminology employed is for the purpose of describing particular embodiments, and is not intended to be limiting. Instead, the scope of the present invention will be established by the appended claims.
[0022] In order to provide a clear and consistent understanding of the terms used in the present specification, a number of definitions are provided below. Moreover, unless defined otherwise, all technical and scientific terms as used herein have the same meaning as commonly understood to one of ordinary skill in the art to which this disclosure pertains.
[0023] The use of the word“a” or“an” when used in conjunction with the term“comprising” in the claims and/or the specification may mean“one”, but it is also consistent with the meaning of “one or more”,“at least one”, and“one or more than one”. Similarly, the word“another” may mean at least a second or more.
[0024] As used in this specification and claim(s), the words“comprising” (and any form of comprising, such as“comprise” and“comprises”),“having” (and any form of having, such as “have” and“has”),“including” (and any form of including, such as“include” and“includes”) or “containing” (and any form of containing, such as“contain” and“contains”), are inclusive or open-ended and do not exclude additional, unrecited elements or process steps.
[0025] As used herein when referring to numerical values or percentages, the term“about” includes variations due to the methods used to determine the values or percentages, statistical variance and human error. Moreover, each numerical parameter in this application should at least be construed in light of the number of reported significant digits and by applying ordinary rounding techniques. [0026] Term“alkyl” or“alk” as used herein, represents a monovalent group derived from a straight or branched chain saturated hydrocarbon comprising, unless otherwise specified, from 1 to 15 carbon atoms and is exemplified by methyl, ethyl, n- and /so-propyl, n-, sec-, iso- and tert- butyl, neopentyl and the like and may be optionally substituted with one, two, three or, in the case of alkyl groups comprising two carbons or more, four substituents.
[0027] The term“alkoxy” or“alkyloxy” as used interchangeably herein, represents an alkyl group attached to the parent molecular group through an oxygen atom.
[0028] The term“alkylthio” or“thioalkoxy” as used interchangeably herein, represents an alkyl group attached to the parent molecular group through a sulfur atom.
[0029] The term “alkylene” as used herein, represents a saturated divalent hydrocarbon group derived from a straight or branched chain saturated hydrocarbon by the removal of two hydrogen atoms, and is exemplified by methylene, ethylene, isopropylene and the like.
[0030] The term“alkenyl” as used herein, represents monovalent straight or branched chain groups of, unless otherwise specified, from 2 to 15 carbons, such as, for example, 2 to 6 carbon atoms or 2 to 4 carbon atoms, containing one or more carbon-carbon double bonds and is exemplified by ethenyl, 1-propenyl, 2-propenyl, 2-methyl-1-propenyl, 1-butenyl, 2- butenyl and the like and may be optionally substituted with one, two, three or four substituents.
[0031] The term“alkynyl” as used herein, represents monovalent straight or branched chain groups of from two to six carbon atoms comprising a carbon-carbon triple bond and is exemplified by ethynyl, 1-propynyl, and the like and may be optionally substituted with one, two, three or four substituents.
[0032] The term “cycloalkyl” as used herein, represents a monovalent saturated or unsaturated non-aromatic cyclic hydrocarbon group of three to eight carbon atoms, unless otherwise specified, and is exemplified by cyclopropyl, cyclobutyl, cyclopentyl, cyclohexyl, cycloheptyl, bicyclo[2.2.1]heptyl and the like.
[0033] The term“halogen” or“halo” as used interchangeably herein, represents F, Cl, Br and [0034] The term “heteroatom”, as used herein, is understood as being oxygen, sulfur or nitrogen.
[0035] The inventors have designed and prepared an additive for use in association with the electrolyte in a Li-ion battery. The additive of the invention is an organic compound as described herein below and which comprises at least one nitrile group. Also, the organic compound is compatible with the electrolyte as well as other components of the battery.
[0036] More specifically, the additive of the invention for use in association with the electrolyte is a nitrile-based organic compound as described herein and having general formulae l-XI, A, B, C and D depicted below.
Figure imgf000019_0001
Figure imgf000020_0001
Figure imgf000021_0001
Figure imgf000022_0001
Y+
N; D
NC CN
[0037] Such organic compounds are exemplified by compounds defined in Table 1 below, namely, Compounds A1-A4, B1-B8, C1-C2 and D1.
[0038] Table 1. Organic compounds according to the invention (Series A, B, C and D)
Figure imgf000022_0002
Figure imgf000023_0002
Figure imgf000023_0001
[0039] The present invention is illustrated in further details by the following non-limiting examples.
Nitrile-based organic compounds for use as additive in association with Li-ion electrolytes
[0040] Example 1 - General procedure for the preparation of the compounds. To a solution of aldehyde (1 eq.) in 15 mL of chloroform are added, molonodinitrile (1.5 eq.) and few drops of triethylamine. The mixture is refluxed one night under nitrogen. After return to room temperature, dichloromethane is added, and the solution is washed twice with water and dried over MgS04. After solvent removal, the residue is chromatographed (silica gel / dichloromethane) to give a solid. [0041] Example 2 - Compound B1
Figure imgf000024_0001
[0042] Bright yellow solid (70%). NMR 1H (400 MHz, CDC ) d: 7.69 (d, 1H, J = 4Hz); 7.64 (s, 1H); 7.38 (dd, 1H, J = 4Hz, J = 12Hz); 6.95 (d, 1H, J = 12Hz); 3.99 (s, 3H); 3.93 (s, 3H).
[0043] Example 3 - Compound B2
Figure imgf000024_0002
[0044] Yellow solid (40%). NMR 1H (400 MHz, CDC ) d: 7.77 (s, 1H). NMR 19F (400 MHz, CDC ) d: -132.55 (s, 2H); -143.68 (s, 1H); -158.50 (s, 1H).
[0045] Example 4 - Compound B3
Figure imgf000024_0003
[0046] White solid. NMR 1H (400 MHz, CDC ) d: 8.60 (d, 1H, J = 4Hz); 8.25 (dd, 1H, J = 4Hz, J = 12Hz); 8.18 (s, 1H); 8.15 (d, 1H, J = 12Hz).
[0047] Example 5 - Compound B4
Figure imgf000025_0001
[0048] Bright yellow solid. NMR 1H (400 MHz, CDC ) d: 8.12 (d, 1 H, J = 4Hz); 8.03 (s, 1 H); 7.67 (dd, 1 H, J = 4Hz, J = 12Hz). NMR 19F (400 MHz, CDC ) d: -63.65 (s, 3F).
[0049] Example 6 - Compound B5
Figure imgf000025_0002
[0050] White solid. NMR 1H (400 MHz, CDCI3) d: 8.02 (d, 2H, J = 12Hz); 7.83 (d, 2H, J = 8Hz); 7.80 (s, 1 H). NMR 19F (400 MHz, CDCI3) d: -63.48 (s, 3F).
[0051] Example 7 - Compound B6
Figure imgf000025_0003
[0052] White solid. NMR 1H (400 MHz, CDCI3) d: 7.99 (d, 2H, J = 8Hz); 7.83 (d, 2H, J = 8Hz); 7.74 (s, 1 H).
[0053] Example 8 - Compound B7
Figure imgf000026_0001
[0054] Pale orange solid. NMR 1H (400 MHz, CDC ) d: 8.39 (d, 2H, J = 12Hz); 8.07 (d, 2H, J = 8Hz); 7.88 (s, 1 H).
[0055] Example 9 - Compound B8
Figure imgf000026_0002
[0056] Pink solid. NMR 1 H (400 MHz, CDC ) d: 8.89 (d, 2H, J = 12Hz); 7.81 (s, 2H); 7.68 (d, 2H, J = 8Hz).
[0057] Compounds of the Series A and C and Compound D1 are commercially available and were used as received.
[0058] Referring to the figures, Figures 1 -3 outline results obtained using compounds of the Serie A; Figures 4-6 outline results obtained using compounds of the Serie B; Figures 7-9 outline results obtained using compounds of the Serie C; and Figures 10-11 outline results obtained using compounds of the Serie D. It should be noted that Reference batteries as well as batteries according to the invention, do not contain vinylene carbonate (VC), which explains the poor stability after 300 cycles. Nonetheless as can be seen, batteries comprising the additive according to the invention present a far better stability.
[0059] As can be seen in Figure 2, use of 0.1 wt% of compound A1 or A4 allows for improvement of the battery capacity as well as a better reversibility. Moreover, a global decrease of the battery resistance is noted (Figure 3). [0060] Figure 5 shows results obtained for compounds B1 and B4. Use of 0.5wt% of the additive allows for an improvement of the battery capacity. A global decrease of the battery resistance is noted (Figure 6).
[0061] Figure 7 shows results obtained for compounds C1 and C2. Use of 0.5wt% of the additive yields a good stability after 300 cycles at 45°C. As can be seen in Figure 8, better results are obtained for compound C1 (shorter carbon chain).
[0062] Figure 10 shows results obtained for compound D1. As can be seen in Figure 11 , use of 0.5wt% of compound D1 allows for improvement of the battery capacity as well as a better reversibility.
[0063] As will be understood by a skilled person, the additive for use in association with the electrolyte are adapted to be compatible with the components of the battery including the electrolyte and the cathode active material.
[0064] The invention is described in relation to lithium manganese iron phosphate (LMFP) - lithium titanium oxide (LTO) batteries. As will be understood by a skilled person, other lithium- ion batterie types may also be used. In other words, any battery wherein the cathode active material comprises a lithium-containing material may be used. Such lithium-containing material may be lithium cobalt oxide (LCO), lithium manganese oxide (LMO), lithium nickel oxide (LNO) and the like including olivines, lithium oxides, nickel manganese cobalt oxide (NMC).
[0065] Also, as will be understood by a skilled person, the anode material may be of any suitable type, such as for example lithium alloys, Si, SiOx, graphite and carbon mixtures, titanates, lithium titanates.
[0066] The scope of the claims should not be limited by the preferred embodiments set forth in the examples but should be given the broadest interpretation consistent with the description as a whole.
[0067] The present description refers to a number of documents, the content of which is herein incorporated by reference in their entirety. REFERENCES
1. Rohan R. et al. J. Phys. Chem. C (2016), 120 (12), 6450-6458.
2. Kim Y.-S. et al. ACS Appl. Mater. Interfaces (2014), 6 (11), 8913-8920.
3. Pohl B. et al. J. Electrochem. Soc. (2015), 162 (3), A460-A464.

Claims

1. A method of improving the performance and safety of a Li-ion battery, comprising using a nitrile-based organic compound in association with the electrolyte of the battery, wherein the compound has a general formula I outlined below
Figure imgf000029_0001
wherein:
Q is a 5 to 12-member ring or bicycle ring, optionally the ring comprises one or more heteroatom which are the same or different and selected from the group consisting of N, O and S; preferably Q is a 5-10-, or a 5-, or a 6-member ring or bicycle ring;
L is present or absent and is a linker comprising one or more of alkyl, alkene and alkyne groups; and
m in an integer from 1 to 10, or 1 to 6, or 1 to 5, or 1 to 4, or 1 to 3.
2. A method of improving the performance and safety of a Li-ion battery, comprising using a nitrile-based organic compound in association with the electrolyte of the battery, wherein the compound has a general formula II outlined below
Figure imgf000029_0002
wherein:
X is C or N;
L is present or absent and is a linker comprising one or more of alkyl, alkene and alkyne groups;
Ri each independently selected from the group consisting of H, alkyl, cycloalkyl, alkene, alkyne, aryl and alkylaryl, alkoxy, thioalkoxy, OH, SH, NH2, a halogen atom, a halogeno alkyl, a halogeno alkoxy, a halogeno thioalkoxy, a cyano alkyl, a cyano alkene, a cyano alkyne, CN, NO2, SO2, COOH and acyloxycarbonyl; preferably selected from the group consisting of H, alkyloxy, halogen, halogeno alkyl, nitro, and cyano; more preferably selected from the group consisting of H, halogen, nitro and cyano;
m is an integer from 1 to 5, or 1 to 4, or 1 to 3; and
m’ is an integer from 0 to 5, or 0 to 4, or 0 to 3, or 1 to 5, or 1 to 4, or 1 to 3.
3. A method of improving the performance and safety of a Li-ion battery, comprising using a nitrile-based organic compound in association with the electrolyte of the battery, wherein the compound has a general formula III outlined below
Figure imgf000030_0001
wherein:
X is C or N;
Ri are each independently selected from the group consisting of H, alkyl, cycloalkyl, alkene, alkyne, aryl and alkylaryl, alkoxy, thioalkoxy, OH, SH, NH2, a halogen atom, a halogeno alkyl, a halogeno alkoxy, a halogeno thioalkoxy, a cyano alkyl, a cyano alkene, a cyano alkyne, CN, NO2, SO2, COOH and acyloxycarbonyl; preferably Ri are each independently selected from the group consisting of H, alkyloxy, halogen, halogeno alkyl, nitro, and cyano; more preferably selected from the group consisting of H, halogen, nitro and cyano; and
m’ is an integer from 0 to 5, or 0 to 4, or 0 to 3, or 1 to 5, or 1 to 4, or 1 to 3.
4. A method of improving the performance and safety of a Li-ion battery, comprising using a nitrile-based organic compound in association with the electrolyte of the battery, wherein the compound has a general formula IV outlined below
Figure imgf000031_0001
wherein:
X is C or N;
Ri are each independently selected from the group consisting of H, alkyl, cycloalkyl, alkene, alkyne, aryl and alkylaryl, alkoxy, thioalkoxy, OH, SH, NH2, a halogen atom, a halogeno alkyl, a halogeno alkoxy, a halogeno thioalkoxy, a cyano alkyl, a cyano alkene, a cyano alkyne, CN, NO2, SO2, COOH and acyloxycarbonyl; preferably selected from the group consisting of H, alkyloxy, halogen, halogeno alkyl, nitro and cyano; more preferably selected from the group consisting of H, halogen, nitro and cyano; and
m’ is an integer from 0 to 5, or 0 to 4, or 0 to 3, or 1 to 5, or 1 to 4, or 1 to 3.
5. A method of improving the performance and safety of a Li-ion battery, comprising using a nitrile-based organic compound in association with the electrolyte of the battery, wherein the compound has a general formula A outlined below
Figure imgf000031_0002
wherein: R1 to R5 are each independently selected from the group consisting of H, alkyl, cycloalkyl, alkene, alkyne, aryl and alkylaryl, alkoxy, thioalkoxy, OH, SH, NH2, a halogen atom, a halogeno alkyl, a halogeno alkoxy, a halogeno thioalkoxy, a cyano alkyl, a cyano alkene, a cyano alkyne, CN, NO2, SO2, COOH and acyloxycarbonyl; preferably R1 to R5 are each independently selected from the group consisting of H, alkyloxy, halogen, halogeno alkyl, nitro and cyano; more preferably selected from the group consisting of H, halogen, nitro and cyano.
6. A method of improving the performance and safety of a Li-ion battery, comprising using a nitrile-based organic compound in association with the electrolyte of the battery, wherein the compound has a general formula B outlined below
B
Figure imgf000032_0001
wherein:
X is C and R3 is H; or X is N; and
R1 to R5 are each independently selected from the group consisting of H, alkyl, cycloalkyl, alkene, alkyne, aryl and alkylaryl, alkoxy, thioalkoxy, OH, SH, NH2, a halogen atom, a halogeno alkyl, a halogeno alkoxy, a halogeno thioalkoxy, a cyano alkyl, a cyano alkene, a cyano alkyne, CN, NO2, SO2, COOH and acyloxycarbonyl; preferably R1 to R5 are each independently selected from the group consisting of H, alkyloxy, halogen, halogeno alkyl, nitro and cyano; more preferably selected from the group consisting of H, halogen, nitro and cyano.
7. A method of improving the performance and safety of a Li-ion battery, comprising using a nitrile-based organic compound in association with the electrolyte of the battery, wherein the compound is A1 , A2, A3 or A4 outlined below
Figure imgf000033_0001
8. A method of improving the performance and safety of a Li-ion battery, comprising using a nitrile-based organic compound in association with the electrolyte of the battery, wherein the compound is B1 , B2, B3, B4, B5, B6, B7 or B8 outlined below
Figure imgf000033_0002
B1 B2 B3
Figure imgf000034_0001
9. A method of improving the performance and safety of a Li-ion battery, comprising using a nitrile-based organic compound in association with the electrolyte of the battery, wherein the compound has a general formula V outlined below
Figure imgf000034_0002
wherein: L is present or absent and is a linker comprising one of more of alkyl, alkene and alkyne groups; and
Ri to R3 are each independently alkyl groups; preferably C1 to C6 or C1 to C3 alkyl groups; more preferably at least one of R1 to R3 is CH3, or each of R1 to R3 is CH3.
10. A method of improving the performance and safety of a Li-ion battery, comprising using a nitrile-based organic compound in association with the electrolyte of the battery, wherein the compound has a general formula VI outlined below
Figure imgf000035_0001
wherein:
n is an integer from 0 to 6, or 0 to 5, or 0 to 4, or 0 to 3, or 0 to 2; preferably n is an integer from 0 to 3; more preferably n is 0 or 1 ; and
R1 to R3 are each independently alkyl groups; preferably C1 to C6 or C1 to C3 alkyl groups; more preferably at least one of R1 to R3 is CH3, or each of R1 to R3 is CH3.
11. A method of improving the performance and safety of a Li-ion battery, comprising using a nitrile-based organic compound in association with the electrolyte of the battery, wherein the compound has a general formula C outlined below
Figure imgf000035_0002
wherein n is an integer from 0 to 6, or 0 to 5, or 0 to 4, or 0 to 3, or 0 to 2; preferably n is an integer from 0 to 3; more preferably n is 0 or 1.
12. A method of improving the performance and safety of a Li-ion battery, comprising using a nitrile-based organic compound in association with the electrolyte of the battery, wherein the compound is C1 or C2 outlined below
Figure imgf000036_0001
Cl C2
or
13. A method of improving the performance and safety of a Li-ion battery, comprising using a nitrile-based organic compound in association with the electrolyte of the battery, wherein the compound has a general formula IX outlined below
IX
Figure imgf000036_0002
wherein:
Ri is CN or CH3;
Li and L2 are each independently present or absent and are each independently a linker comprising alkyl, alkene and/or alkyne groups; and
Y is Na, K or Li; preferably Y is Na.
14. A method of improving the performance and safety of a Li-ion battery, comprising using a nitrile-based organic compound in association with the electrolyte of the battery, wherein the compound has a general formula X outlined below
X
Figure imgf000036_0003
wherein:
Li and L2 are each independently present or absent and are each independently a linker comprising one or more of alkyl, alkene and alkyne groups; and
Y is Na, K or Li; preferably Y is Na.
15. A method of improving the performance and safety of a Li-ion battery, comprising using a nitrile-based organic compound in association with the electrolyte of the battery, wherein the compound has a general formula XI outlined below
XI
Figure imgf000037_0001
wherein:
n1 and n2 are each independently an integer from 0 to 10, or 0 to 6, or O to 3; preferably at least one of n1 and n2 is 0, or both n1 and n2 are 0; and
Y is Na, K or Li; preferably Y is Na.
16. A method of improving the performance and safety of a Li-ion battery, comprising using a nitrile-based organic compound in association with the electrolyte of the battery, wherein the compound has a general formula D outlined below
D
Figure imgf000037_0002
wherein Y is Na, K or Li; preferably Y is Na.
17. A method of improving the performance and safety of a Li-ion battery, comprising using a nitrile-based organic compound in association with the electrolyte of the battery, wherein the compound has a general formula D1 outlined below
Na+
Figure imgf000037_0003
D1
18. A compound having a general formula VII outlined below
VII
Figure imgf000038_0001
wherein Ri and R2 are each independently selected from the group consisting of H, alkyl, cycloalkyl, alkene, alkyne, aryl and alkylaryl, alkoxy, thioalkoxy, OH, SH, NH2, a halogen atom, a halogeno alkyl, a halogeno alkoxy, a halogeno thioalkoxy, a cyano alkyl, a cyano alkene, a cyano alkyne, CN, N02, S02, COOH and acyloxycarbonyl; preferably selected from the group consisting of H, alkyloxy, halogen, halogeno alkyl, nitro and cyano; more preferably selected from the group consisting of H, halogen, nitro and cyano.
19. A compound having a general formula VIII outlined below
VIII
Figure imgf000038_0002
wherein X is a halogen atom; preferably X is F.
20. A compound of formula B4 outlined below B4
Figure imgf000039_0001
21. A method of improving the performance and safety of a Li-ion battery, comprising using a nitrile-based organic compound in association with the electrolyte of the battery, wherein the compound as defined in any one of claims 18 to 20.
22. The method according to any one of claims 1 to 17 and 21 , wherein the nitrile-based organic compound is added to the electrolyte; optionally an amount of the additive (nitrile- based organic compound) is between about 0.01 to about 5.0%wt, or about 0.01 to about 3.0%wt, or about 0.01 to about 1.0%wt, or about 0.05 to about 1.0%wt, or about 0.1 to about 1.0%wt, about 0.1 to about 0.8%wt, or about 0.1 to about 0.5%wt, or about 0.1 to about 0.3%wt, is 0.1 %wt, or is 0.5%wt.
23. An electrolyte comprising a compound which is selected from the group consisting of: I,
I, IV, A, B, A1 , A2, A3, A4, B1 , B2, B3, B4, B5, B6, B7, B8, V, VI, C, C1 , C2, IX, X, XI,
D, and D1 as defined in any one of method claims 1 to 17.
24. An electrolyte comprising the compound as defined in any one of claims 18 to 20.
25. A battery comprising the electrolyte as defined in claim 23 or 24.
26. An additive for an electrolyte for use in a Li-ion battery, comprising a compound which is selected from the group consisting of: I, II, III, IV, A, B, A1 , A2, A3, A4, B1 , B2, B3, B4, B5, B6, B7, B8, V, VI, C, C1 , C2, IX, X, XI, D, and D1 as defined in any one of method claims 1 to 17.
27. An additive for an electrolyte for use in a Li-ion battery, comprising a compound as defined in any one of claims 18 to 20.
28. The method, electrolyte, battery or additive according to any one of claims 1 to 27, wherein the Li-ion battery is a battery wherein the cathode comprises a lithium-containing material;
29. The method, electrolyte, battery or additive according to any one of claims 1 to 27, wherein the Li-ion battery is a battery wherein the cathode comprises lithium cobalt oxide (LCO), lithium manganese oxide (LMO), lithium nickel oxide (LNO) and the like including olivines, lithium oxides, nickel manganese cobalt oxide (NMC).
30. The method, electrolyte, battery or additive according to claim 28 or 30, wherein the performance (capacity, reversibility) of the battery is improved.
PCT/CA2019/051415 2018-10-04 2019-10-03 Additives for electrolytes in li-ion batteries Ceased WO2020069619A1 (en)