WO2020167638A1 - Elastomeric compositions and methods of use - Google Patents
Elastomeric compositions and methods of use Download PDFInfo
- Publication number
- WO2020167638A1 WO2020167638A1 PCT/US2020/017455 US2020017455W WO2020167638A1 WO 2020167638 A1 WO2020167638 A1 WO 2020167638A1 US 2020017455 W US2020017455 W US 2020017455W WO 2020167638 A1 WO2020167638 A1 WO 2020167638A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- prepolymer
- elastomeric
- elastomeric prepolymer
- coreactive composition
- coreactive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Ceased
Abstract
Description
Claims