WO2023074513A1 - 水性インクジェットインク用バインダー、水性インクジェットインク、及び印刷層 - Google Patents

水性インクジェットインク用バインダー、水性インクジェットインク、及び印刷層 Download PDF

Info

Publication number
WO2023074513A1
WO2023074513A1 PCT/JP2022/039034 JP2022039034W WO2023074513A1 WO 2023074513 A1 WO2023074513 A1 WO 2023074513A1 JP 2022039034 W JP2022039034 W JP 2022039034W WO 2023074513 A1 WO2023074513 A1 WO 2023074513A1
Authority
WO
WIPO (PCT)
Prior art keywords
acid
mass
binder
meth
glycol
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2022/039034
Other languages
English (en)
French (fr)
Inventor
和香奈 内藤
辰弥 山本
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
DIC Corp
Original Assignee
DIC Corp
Dainippon Ink and Chemicals Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by DIC Corp, Dainippon Ink and Chemicals Co Ltd filed Critical DIC Corp
Priority to US18/699,442 priority Critical patent/US20240409761A1/en
Priority to JP2023556367A priority patent/JP7517618B2/ja
Priority to EP22886841.0A priority patent/EP4394004A4/en
Priority to CN202280063412.2A priority patent/CN117999323B/zh
Publication of WO2023074513A1 publication Critical patent/WO2023074513A1/ja
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

本発明は、複合樹脂（Ａ）及び水性媒体（Ｂ）を含有する水性インクジェットインク用バインダーであって、前記複合樹脂（Ａ）が、酸基を有するポリウレタン（ａ１）を含むシェル部と、脂肪族共役ジエンを必須原料とする重合体（ａ２）を含むコア部とを有するコアシェル型粒子を形成していることを特徴とする水性インクジェットインク用バインダー、前記水性インクジェットインク用バインダーを含む水性インクジェットインク及び印刷層を提供するものである。この水性インクジェットインク用バインダーは、普通紙やコート紙、フィルム等の印刷物の耐擦過性及び布帛の耐洗濯性に優れることから、各種記録媒体への印刷に好適に用いることができる。

Description

水性インクジェットインク用バインダー、水性インクジェットインク、及び印刷層
　本発明は、水性インクジェットインク用バインダー、水性インクジェットインク、及び印刷層に関する。
　インクジェット（ＩＪ）記録装置はインク組成物の小液滴を飛翔させ、紙などの記録媒体に付着させて印刷を行う印刷方式である。オンデマンド印刷需要の高まりを背景に、ＩＪプリンターは近年、産業用ワイドフォーマット用途、テキスタイル用途、軟包装用途などで急速に利用が拡大している。
前記インクジェット記録装置に用いられるインクジェット用インクとしては、例えば、破断伸度が３００％以上のポリカーボネート系ウレタン樹脂を含むものが提案されている（特許文献１参照）。しかしながら、このインクは、近年、より高度に要求される印刷物の耐擦過性や耐洗濯性が不十分であるという問題があった。
特許第６１１９９１９号公報
　本発明が解決しようとする課題は、耐擦過性及び耐洗濯性に優れた印刷物が得られる水性インクジェットインク用バインダーを提供することである。
　本発明者等は、上記の課題を解決するため鋭意研究した結果、特定の複合樹脂及び水性媒体を含有する水性インクジェットインク用バインダーが、上記課題を解決し得ることを見出し、発明を完成させた。
　すなわち、本発明は、複合樹脂（Ａ）及び水性媒体（Ｂ）を含有する水性インクジェットインク用バインダーであって、前記複合樹脂（Ａ）が、酸基を有するポリウレタン（ａ１）を含むシェル部と、脂肪族共役ジエンを必須原料とする重合体（ａ２）を含むコア部とを有するコアシェル型粒子を形成していることを特徴とする水性インクジェットインク用バインダーに関する。
　本発明の水性インクジェットインク用バインダーは、普通紙やコート紙、フィルム等の印刷物の耐擦過性及び布帛の耐洗濯性に優れることから、各種記録媒体への印刷に好適に用いることができる。
　本発明の水性インクジェットインク用バインダーは、複合樹脂（Ａ）及び水性媒体（Ｂ）を含有する水性インクジェットインク用バインダーであって、前記複合樹脂（Ａ）が、酸基を有するポリウレタン（ａ１）を含むシェル部と、脂肪族共役ジエンを必須原料とする重合体（ａ２）を含むコア部とを有するコアシェル型粒子を形成しているものである。
　前記複合樹脂（Ａ）のコアシェル型粒子は、前記ポリウレタン（ａ１）が前記重合体（ａ２）の一部又は全部を内部に取り込み被覆する形態を有するものであり、前記水性媒体（Ｂ）中に分散していることが好ましい。
　前記複合樹脂（Ａ）のシェル部を構成する前記ポリウレタン（ａ１）は、ポリオールとポリイソシアネートとの反応により得られるが、前記ポリウレタン（ａ１）の有する酸基は、前記ポリオールを構成する一成分として、酸基を有するポリオールを使用することによって、前記ポリウレタン（ａ１）中に容易に導入することができる。
　前記酸基を有するポリオールとしては、カルボキシル基又はスルホン酸基を有するジオールが挙げられ、カルボキシル基を有するジオールを含むことが好ましい。前記カルボキシル基を有するジオールとしては、例えば、２，２－ジメチロールプロピオン酸、２，２－ジメチロールブタン酸、２，２－ジメチロール酪酸、２，２－ジメチロール吉草酸等が挙げられる。これらの中でも２，２－ジメチロールプロピオン酸が好ましい。また、前記カルボキシル基を有するポリオールと各種ポリカルボン酸とを反応させて得られるカルボキシル基を有するポリエステルポリオールも使用することもできる。前記ポリカルボン酸としては、コハク酸、アジピン酸、セバシン酸、ドデカンジカルボン酸等の脂肪族ポリカルボン酸；１，４－シクロヘキサンジカルボン酸、シクロヘキサントリカルボン酸等の脂環式ポリカルボン酸；テレフタル酸、イソフタル酸、フタル酸、ナフタレンジカルボン酸等の芳香族ポリカルボン酸；これらの酸無水物等が挙げられる。なお、これらのポリオールは、単独で用いることも２種以上併用することもできる。
　前記スルホン酸基を有するポリオールとしては、例えば、５－スルホイソフタル酸、スルホテレフタル酸、４－スルホフタル酸、５［４－スルホフェノキシ］イソフタル酸等のジカルボン酸またそれらの塩と、前記芳香族構造を有するポリエステルポリオールの製造に使用可能なものとして例示した低分子量ポリオールとを反応させて得られるポリエスルポリオールが挙げられる。なお、これらのポリオールは、単独で用いることも２種以上併用することもできる。
　前記酸基を有するポリオールと組み合わせ使用可能なその他のポリオールとしては、例えば、ポリエーテルポリオール、ポリエステルポリオール、ポリカーボネートポリオール等が挙げられる。
　前記ポリエーテルポリオールとしては、例えば、活性水素原子を２個以上有する化合物の１種または２種以上を開始剤として、アルキレンオキサイドを付加重合させたもの等が挙げられる。
　前記開始剤としては、例えば、エチレングリコール、ジエチレングリコール、トリエチレングリコール、トリメチレングリコール、１，２－プロパンジオ－ル、１，３－プロパンジオ－ル、１，３－ブタンジオール、１，４－ブタンジオール、１，６－ヘキサンジオール、ネオペンチルグリコール、グリセリン、トリメチロールエタン、トリメチロールプロパン、ソルビトール、蔗糖、アコニット糖、トリメリット酸、ヘミメリット酸、リン酸、エチレンジアミン、ジエチレントリアミン、トリイソプロパノールアミン、ピロガロール、ジヒドロキシ安息香酸、ヒドロキシフタル酸、１，２，３－プロパントリチオール等が挙げられる。
　前記アルキレンオキシドとしては、エチレンオキサイド、プロピレンオキサイド、ブチレンオキサイド、スチレンオキサイド、エピクロロヒドリン、テトラヒドロフラン等が挙げられる。
　また、前記ポリエステルポリオールとしては、例えば、低分子量のポリオールとポリカルボン酸とをエステル化反応して得られる脂肪族ポリエステルポリオールや芳香族ポリエステルポリオール、ε－カプロラクトン等の環状エステル化合物を開環重合反応して得られるポリエステルや、これらの共重合ポリエステル等が挙げられる。
　前記ポリエステルポリオールの製造に用いられる低分子量のポリオールとしては、例えば、エチレングリコール、ジエチレングリコール、トリエチレングリコール、テトラエチレングリコール、１，２－プロパンジオール、１　，３－プロパンジオール、ジプロピレングリコール、トリプロピレングリコール、１，２－ブタンジオール、１，３－ブタンジオール、１，４－ブタンジオール、２，３－ブタンジオール、１，５－ペンタンジオール、ネオペンチルグリコール、１，５－ヘキサンジオール、１，６－ヘキサンジオール、２，５－ヘキサンジオール、１，７－ヘプタンジオール、１，８－オクタンジオール、１，９－ノナンジオール、１，１０－デカンジオール、１，１１－ウンデカンジオール、１，１２－ドデカンジオール、２－メチル－１，３－プロパンジオール、ネオペンチルグリコール、２－ブチル－２－エチル－１，３－プロパンジオール、３－メチル－１，５－ペンタンジオール、２－エチル－１，３－ヘキサンジオール、２－メチル－１，８－オクタンジオール、グリセリン、トリメチロ－ルプロパン、ジトリメチロールプロパン、トリメチロールプロパン、ペンタエリスリトール等の分子量が５０～３００である脂肪族ポリオール；シクロヘキサンジメタノール、水添ビスフェノールＡ等の脂環式構造を有するポリオール；ビスフェノールＡ及びビスフェノールＦ等の芳香族構造を有するポリオールなどが挙げられる。
　また、前記ポリカルボン酸としては、例えば、コハク酸、アジピン酸、セバシン酸、ドデカンジカルボン酸等の脂肪族ポリカルボン酸；１，４－シクロヘキサンジカルボン酸、シクロヘキサントリカルボン酸等の脂環式ポリカルボン酸；テレフタル酸、イソフタル酸、フタル酸、ナフタレンジカルボン酸等の芳香族ポリカルボン酸；それらの無水物またはエステル化物などが挙げられる。
　前記ポリカーボネートポリオールとしては、例えば、炭酸エステルとポリオールとを反応させて得られるものや、ホスゲンとビスフェノールＡ等とを反応させて得られるものを使用することができる。
　前記炭酸エステルとしては、メチルカーボネートや、ジメチルカーボネート、エチルカーボネート、ジエチルカーボネート、シクロカーボネート、ジフェニルカーボネ－ト等を使用することできる。
　前記炭酸エステルと反応しうるポリオールとしては、例えば、エチレングリコール、ジエチレングリコール、トリエチレングリコール、１，２－プロピレングリコール、１，３－プロピレングリコール、ジプロピレングリコール、１，４－ブタンジオール、１，３－ブタンジオール、１，２－ブタンジオール、２，３－ブタンジオール、１，５－ペンタンジオール、１，５－ヘキサンジオール、２，５－ヘキサンジオール、１，６－ヘキサンジオール、１，７－ヘプタンジオール、１，８－オクタンジオール、１，９－ノナンジオール、１，１０－デカンジオール、１，１１－ウンデカンジオール、１，１２－ドデカンジオール、３－メチル－１，５－ペンタンジオール、２－エチル－１，３－ヘキサンジオール、２－メチル－１，３－プロパンジオール、２－メチル－１，８－オクタンジオール、２－ブチル－２－エチルプロパンジオール、２－メチル－１，８－オクタンジオール、ネオペンチルグリコール、１，４－シクロヘキサンジオール、１，４－シクロヘキサンジメタノール、ハイドロキノン、レゾルシン、ビスフェノール－Ａ、ビスフェノール－Ｆ、４，４’－ビフェノール等の比較的低分子量のジヒドロキシ化合物や、ポリエチレングリコール、ポリプロピレングリコール、ポリテトラメチレングリコール等のポリエーテルポリオールや、ポリヘキサメチレンアジペート、ポリヘキサメチレンサクシネート、ポリカプロラクトン等のポリエステルポリオールなどを使用することができる。
　前記酸基を有するポリオールの使用量は、前記ポリウレタン（ａ１）の製造に使用するポリオールの全量に対して、３～５０質量％が好ましい。
　前記ポリイソシアネートとしては、例えば、フェニレンジイソシアネート、トリレンジイソシアネート、ジフェニルメタンジイソシアネート、ナフタレンジイソシアネート等の芳香族ジイソシアネート；ヘキサメチレンジイソシアネート、リジンジイソシアネート、シクロヘキサンジイソシアネート、イソホロンジイソシアネート、ジシクロヘキシルメタンジイソシアネート、キシリレンジイソシアネート、テトラメチルキシリレンジイソシアネート等の脂肪族または脂肪族環式構造を有するジイソシアネートなどが挙げられるが、耐擦過性及び耐洗濯性がより向上することから、脂肪族環式構造を有するジイソシアネートが好ましい。なお、これらのポリイソシアネートは、単独で用いることも２種以上併用することもできる。
　前記ポリイソシアネートに含まれるイソシアネート基（ＮＣＯ）と、前記ポリオールに含まれる水酸基（ＯＨ）とのモル比（ＮＣＯ／ＯＨ）は、０．９～２が好ましい。
　また、前記ポリウレタン（ａ１）としては、ポリアミン等の鎖伸長剤を使用し高分子量化したものを使用してもよい。
　前記ポリアミンとしては、例えば、エチレンジアミン、１，２－プロパンジアミン、１，６－ヘキサメチレンジアミン、ピペラジン、２，５－ジメチルピペラジン、イソホロンジアミン、４，４’－ジシクロヘキシルメタンジアミン、３，３’－ジメチル－４，４’－ジシクロヘキシルメタンジアミン、１，４－シクロヘキサンジアミン等のジアミン；Ｎ－ヒドロキシメチルアミノエチルアミン、Ｎ－ヒドロキシエチルアミノエチルアミン、Ｎ－ヒドロキシプロピルアミノプロピルアミン、Ｎ－エチルアミノエチルアミン、Ｎ－メチルアミノプロピルアミン等の１個の１級アミノ基と１個の２級アミノ基を有するジアミン；ジエチレントリアミン、ジプロピレントリアミン、トリエチレンテトラミン等のポリアミン；ヒドラジン、Ｎ，Ｎ’－ジメチルヒドラジン、１，６－ヘキサメチレンビスヒドラジン等のヒドラジン化合物；コハク酸ジヒドラジッド、アジピン酸ジヒドラジド、グルタル酸ジヒドラジド、セバシン酸ジヒドラジド、イソフタル酸ジヒドラジド等のジヒドラジド化合物；β－セミカルバジドプロピオン酸ヒドラジド、３－セミカルバジド－プロピル－カルバジン酸エステル、セミカルバジッド－３－セミカルバジドメチル－３，５，５－トリメチルシクロヘキサン等のセミカルバジド化合物を使用することができる。なお、これらのポリアミンは、単独で用いることも２種以上併用することもできる。
　前記ポリアミンは、ポリアミンが有するアミノ基と、ウレタンプレポリマーの有するイソシアネート基との当量比が、０．８～１で使用することが好ましい。
　前記鎖伸長反応は、ポリウレタンの水分散体を製造した後、前記水分散体と前記ポリアミン等の鎖伸長剤とを混合することによって行うことが好ましい。
　前記ポリウレタン（ａ１）の酸価は、水分散性、耐擦過性、及び耐洗濯性のバランスがより向上することから、１０～７０ｍｇＫＯＨ／ｇが好ましく、１５～６５ｍｇＫＯＨ／ｇがより好ましい。
　本発明におけるポリウレタン（ａ１）の酸価は、原料組成から計算により得られる値である。
　前記ポリウレタン（ａ１）の重量平均分子量は、水分散性、耐擦過性、及び耐洗濯性のバランスがより向上することから、１０，０００～５００，０００が好ましく、１０，０００～３００，０００がより好ましい。
　本発明において、重量平均分子量及び数平均分子量は、特記ない限り、ポリスチレンを標準試料としてゲル・パーミエーション・クロマトグラフィ法（ＧＰＣ）により測定した値である。
　前記ポリウレタン（ａ１）の酸基は、前記複合樹脂（Ａ）の水分散性がより向上することから、塩基性化合物で中和されていることが好ましい。
　前記塩基性化合物としては、例えば、モノメチルアミン、ジメチルアミン、トリメチルアミン、モノエチルアミン、ジエチルアミン、トリエチルアミン、モノプロピルアミン、ジプロピルアミン、トリプロピルアミン等のアルキルアミン；モノエタノールアミン、ジエタノールアミン、モノイソプロパノールアミン、ジイソプロパノールアミン、Ｎ－メチルエタノールアミン、Ｎ，Ｎ－ジメチルエタノールアミン、Ｎ，Ｎ－ジエチルエタノールアミン、２－アミノ－２－メチルプロパノール、２－（ジメチルアミノ）－２－メチルプロパノール、Ｎ－メチルジエタノールアミン等のアルカノールアミン；エチレンジアミン、ジエチレントリアミン、トリエチレンテトラミン、テトラエチレンペンタミン等の多価アミンなどの有機アミン、アンモニア（水）、水酸化ナトリウム、水酸化カリウム、水酸化リチウム等の金属水酸化物などが挙げられるが、耐擦過性及び耐洗濯性がより向上することから、金属水酸化物が好ましく、水酸化カリウムがより好ましい。なお、これらの塩基性化合物は、単独で用いることも２種以上併用することもできる。
　前記複合樹脂（Ａ）のコア部を構成する重合体（ａ２）は、脂肪族共役ジエン、必要に応じてその他の不飽和単量体の重合反応により得られる。
　前記脂肪族共役ジエンとしては、例えば、１，３－ブタジエン、イソプレン、２，３－ジメチル－１，３－ブタジエン、１，３－ペンタジエン、１，３－ヘキサジエン、１，３－ヘプタジエン、２，３－ジメチルブタジエン、３－メチル－１，３－ペンタジエン、２－クロル－１，３－ブタジエン等が挙げられるが、耐擦過性、及び耐洗濯性がより向上することから、１，３－ブタジエン、イソプレンが好ましい。これらの脂肪族共役ジエンは、単独で用いることも２種以上併用することもできる。
　前記その他の不飽和単量体としては、例えば、メチル（メタ）アクリレート、エチル（メタ）アクリレート、プロピル（メタ）アクリレート、ブチル（メタ）アクリレート、イソブチル（メタ）アクリレート、ｔｅｒｔ－ブチル（メタ）アクリレート、ペンチル（メタ）アクリレート、３－メチルブチル（メタ）アクリレート、ネオペンチル（メタ）アクリレート、イソアミル（メタ）アクリレート、ヘキシル（メタ）アクリレート、ヘプチル（メタ）アクリレート、オクチル（メタ）アクリレート、２－エチルヘキシル（メタ）アクリレート、イソオクチル（メタ）アクリレート、ノニル（メタ）アクリレート、ドデシル（メタ）アクリレート、トリデシル（メタ）アクリレート、ステアリル（メタ）アクリレート、イソステアリル（メタ）アクリレート、ヘキサデシル（メタ）アクリレート、等の炭素原子数４～２２のアルキル（メタ）アクリレート；
　シクロペンチル（メタ）アクリレート、シクロヘキシル（メタ）アクリレート、イソボルニル（メタ）アクリレート等の炭素原子数６～２０のシクロアルキル（メタ）アクリレート；
　フェニル（メタ）アクリレート等のアリル（メタ）アクリレート；
　ベンジル（メタ）アクリレート、フェネチル（メタ）アクリレート等の炭素原子数１０～２０のアラルキル（メタ）アクリレート；
　フェノキシエチル（メタ）アクリレート等のアリルオキシアルキル（メタ）アクリレート；
　クロトン酸メチル、クロトン酸エチル等のクロトン酸アルキルエステル；
　ジメチルマレート、ジブチルマレート、ジメチルフマレート、ジブチルフマレート、ジメチルイタコネート、ジブチルイタコネート等の不飽和ジカルボン酸アルキルエステル；
　スチレン、ｐ－ｔｅｒｔ－ブチルスチレン、α－メチルスチレン、ビニルトルエン、ビニルピリジン、クロロスチレン、クロロメチルスチレン等の芳香族ビニルモノマー；
　（メタ）アクリロニトリル、クロトノニトリル、（メタ）アクリルアミド、Ｎ－メチル（メタ）アクリルアミド、Ｎ－イソプロピル（メタ）アクリルアミド、Ｎ－ヒドロキシエチル（メタ）アクリルアミド、Ｎ－メチロール（メタ）アクリルアミド、Ｎ－メトキシエチル（メタ）アクリルアミド、Ｎ，Ｎ－ジメチル（メタ）アクリルアミド、Ｎ，Ｎ－ジエチル（メタ）アクリルアミド、Ｎ，Ｎ－ジメチルアミノエチル（メタ）アクリレート、Ｎ，Ｎ－ジメチルアミノプロピル（メタ）アクリルアミド、Ｎ，Ｎ－ジエチルアミノエチル（メタ）アクリレート、Ｎ，Ｎ－ジエチルアミノプロピル（メタ）アクリレート、Ｎ－（メタ）アクリロイルモルホリン、Ｎ－（メタ）アクリロイルピロリジン、Ｎ－ビニルホルムアミド、Ｎ－ビニルピロリドン、Ｎ－ビニルイミダゾール、Ｎ－ビニルカルバゾール、Ｎ－ビニルキノリン、Ｎ－ビニルピペリジン等の窒素原子含有モノマー（好ましくは１置換又は２置換の（メタ）アクリルアミド（置換基が結合して環を形成しているものも含む））及び該窒素原子含有モノマーの塩化メチル塩；
　フッ化ビニル、フッ化ビニリデン、テトラフルオロエチレン、クロロトリフルオロエチエレン、ヘキサフルオロプロピレン、塩化ビニル、塩化ビニリデン等のハロゲン化オレフィン；エチレン、プロピレン、イソブチレン、１－ブテン等のα－オレフィン；
　酢酸ビニル、プロピオン酸ビニル、ピバリン酸ビニル、バーサティック酸ビニル、安息香酸ビニル、ネオデカン酸ビニル等のカルボン酸ビニルエステル；
　メチルビニルエーテル、エチルビニルエーテル、ｎ－ブチルビニルエーテル、イソブチルビニルエーテル等のアルキルビニルエーテル；シクロヘキシルビニルエーテル等のシクロアルキルビニルエーテル；
　アクロレイン、メチルビニルケトン等のカルボニル基含有モノマー；
　ポリエチレングリコール（メタ）アクリレート、メトキシポリエチレングリコール（メタ）アクリレート、ポリエチレングリコールポリプロピレングリコール共重合（メタ）アクリレート、メトキシポリエチレングリコールポリプロピレングリコール共重合（メタ）アクリレート、ポリエチレングリコールポリテトラメチレングリコール共重合（メタ）アクリレート、メトキシポリエチレングリコールポリテトラメチレングリコール共重合（メタ）アクリレート等のポリオキシエチレン基含有（メタ）アクリルモノマー；
　パーフルオロシクロヘキシル（メタ）アクリレート、ジ－パーフルオロシクロヘキシルフマレート、Ｎ－イソプロピルフルオロオクタンスルフォン酸アミドエチル（メタ）アクリレート等のフルオロアルキル基含有モノマー；
　無水マレイン酸、無水シトラコン酸、無水メサコン酸、無水イタコン酸、テトラヒドロ無水フタル酸等の不飽和ジカルボン酸類無水物；
　グリシジル（メタ）アクリレート、アリルグリシジルエーテル、テトラヒドロフルフリル（メタ）アクリレート等の環状エーテル含有モノマー；
ビニリトリクロロシラン、ビニルトリエトキシシラン、ビニルトリス（β－メトキシエトキシ）シラン、γ－（メタ）アクリロキシプロピルトリメトキシシラン等のシリル基含有モノマー；
　２－ヒドロキシエチル（メタ）アクリレート、２－ヒドロキシプロピル（メタ）アクリレート、２－ヒドロキシブチル（メタ）アクリレート、４－ヒドロキシブチル（メタ）アクリレート、２－ヒドロキシエチルビニルエーテル、４－ヒドロキシブチルビニルエーテル、２－ヒドロキシエチルアリルエーテル等のヒドロキシ基含有モノマー；
　ビニルスルホン酸、３－アクリロキシプロパン－１－スルホン酸、３－アクリロキシオクチルオキシベンゼンスルホン酸、３－アクリロキシベンゼンジアゾスルホン酸、３－アクリロキシアゾベンゼン－４’－スルホン酸、２－アクリロイルアミノ－２－メチルプロパン－１－スルホン酸、２－アクリロイルアミド－２－メチルプロパンスルホン酸、アクリロニトリル－ｔｅｒｔ－ブチルスルホン酸等のビニル基含有スルホン酸化合物並びにそれらの塩；
などが挙げられる。なお、これらの単量体は単独で用いることも２種以上併用することもできる。
　なお、本発明において、「（メタ）アクリレート」とは、メタクリレートとアクリレートの一方又は両方をいう。
　前記重合体（ａ２）の単量体原料中の前記脂肪族共役ジエンは、耐擦過性及び耐洗濯性がより向上することから、５０質量％以上が好ましく、７０質量％以上がより好ましく、９０質量％以上がさらに好ましい。
　前記重合体を重合する際は、重合開始剤を共存させることが好ましい。前記重合開始剤としては、２，２’－アゾビス（イソブチロニトリル）、２，２’－アゾビス（２－メチルブチロニトリル）、２，２’－アゾビス（２－メチルプロピオンアミジン）二塩酸塩、４，４’－アゾビス（４－シアノ）吉草酸、２，２’－アゾビス（２－アミジノプロパン）ジヒドロクロライド等のアゾ化合物；ベンゾイルパーオキサイド、ｔｅｒｔ－ブチルハイドロパーオキサイド、ｔｅｒｔ－ブチルパーオキシピバレート、ｔｅｒｔ－ブチルパーオキシベンゾエート、ｔｅｒｔ－ブチルパーオキシ－２－エチルヘキサノエート、ジ－ｔｅｒｔ－ブチルパーオキサイド、ジ－ｔｅｒｔ－ブチルハイドロパーオキサイド、クメンハイドロパーオキサイド、ベンゾイルパーオキサイド、ラウロイルパーオキサイド、デカノイルパーオキサイド、ｔｅｒｔ－ブチルクミルパーオキサイド、ジクミルパーオキサイド、ｔｅｒｔ－ブチルパーオキシラウレート、ｔｅｒｔ－ブチルパーオキシベンゾエート、クメンハイドロパーオキサイド、パラメンタンハイドロパーオキサイド、等の有機過酸化物；過酸化水素、過硫酸アンモニウム、過硫酸カリウム、過硫酸ナトリウム等の無機過酸化物などを使用することができる。
　前記重合開始剤は、前記重合体（ａ２）の単量体原料の合計１００質量部に対して、０．００５～５質量部が好ましく、０．０１～１質量部がより好ましく、０．０２～０．２質量部がさらに好ましい。
　前記ポリウレタン（ａ１）と前記重合体（ａ２）との質量比（ａ１／ａ２）は、耐擦過性及び耐洗濯性がより向上することから、９５／５～５０／５０が好ましく、９０／１０～６５／３５がより好ましい。
　前記水性媒体（Ｂ）としては、水、水と混和する有機溶剤及びこれらの混合物が挙げられる。水と混和する有機溶剤としては、例えば、メタノール、エタノール、ｎ－プロパノール、イソプロピルアルコール、１，２－プロピレングリコール、１，３－ブチレングリコール等のアルコール溶剤；アセトン、メチルエチルケトン等のケトン溶剤；エチレングリコール－ｎ－ブチルエーテル、ジエチレングリコール－ｎ－ブチルエーテル、ジエチレングリコールモノエチルエーテルアセテート、ジエチレングリコールジメチルエーテル、プロピレングリコールメチルエーテル、ジプロピレングリコールメチルエーテル、ジプロピレングリコールジメチルエーテル、ジプロピレングリコール－ｎ－ブチルエーテル、トリプロピレングリコールメチルエーテル等のグリコールエーテル溶剤；Ｎ－メチル－２－ピロリドン、Ｎ－エチル－２－ピロリドン等のラクタム溶剤；Ｎ，Ｎ－ジメチルホルムアミド等のアミド溶剤などが挙げられ、ケトン溶剤が好ましい。
　前記水性媒体（Ｂ）は、安全性や環境に対する負荷低減を考慮すると、水のみ、又は、水及び水と混和する有機溶剤との混合物が好ましく、水のみがより好ましい。水の含有率は、前記水性媒体（Ｂ）中、５０質量％以上が好ましく、７０質量％以上がより好ましい。
　前記水性媒体（Ｂ）の含有率は、水性インクジェットインク用バインダー中、３０～８０質量％が好ましく、５０～７０質量％がより好ましい。
　本発明の水性インクジェットインク用バインダーは、さらに、添加剤（Ｃ）として、架橋剤、可塑剤、帯電防止剤、ワックス、界面活性剤、光安定剤、流動調整剤、染料、レベリング剤、レオロジーコントロール剤、紫外線吸収剤、酸化防止剤、光触媒性化合物、防腐剤、粘度調整剤、ｐＨ調整剤、キレート剤等を含んでいてもよい。
　前記添加剤（Ｃ）の含有量は、前記複合樹脂（Ａ）１００質量部に対して、２０質量部以下が好ましく、１０質量部以下がより好ましい。
　前記複合樹脂（Ａ）は、前記ポリウレタン（ａ１）の存在下で、前記重合体（ａ２）の単量体原料を重合することにより得られる。
　本発明の水性インクジェットインク用バインダーは、例えば、前記ポリウレタン（ａ１）の有する酸基の一部又は全部を、塩基性化合物を用いて中和し、得られた中和物を水性媒体（Ｂ）中に分散させることによって、前記ポリウレタン（ａ１）の水分散体を製造する工程（Ｉ）、次いで、得られた前記ポリウレタン（ａ１）の水分散体中に、脂肪族共役ジエン及び必要に応じてその他の不飽和単量体を供給し、ラジカル重合を行う工程（ＩＩ）により得ることができる。この際、疎水性である脂肪族共役ジエンは、前記ポリウレタン（ａ１）の粒子内に取り込まれるため、前記ポリウレタン（ａ１）を含むシェル部と、前記アクリル重合体（ａ２）を含むコア部とを有するコアシェル型粒子が形成される。また、前記ラジカル重合の際は、必要に応じて、前記添加剤（Ｃ）を共存させてもよく、重合反応後に前記添加剤（Ｃ）を添加してもよい。
　本発明の水性インクジェットインクは、前記水性インクジェットインク用バインダー及び着色剤を含有するものであるが、さらに、有機溶剤、表面調整剤、顔料分散剤、乾燥抑止剤、浸透剤、界面活性剤等を含んでいてもよい。
　前記着色剤としては、染料及び顔料が挙げられ、顔料を含むことが好ましい。
　前記顔料としては、例えば、カラーインデックス（Ｔｈｅ　Ｓｏｃｉｅｔｙ　ｏｆ　Ｄｙｅｒｓ　ａｎｄ　Ｃｏｌｏｕｒｉｓｔｓ出版）でピグメントに分類されている化合物を用いることができ、無機顔料や有機顔料が挙げられる。
　前記無機顔料としては、酸化鉄；カーボンブラック（コンタクト法、ファーネス法、サーマル法等により製造されたカーボンブラック）；酸化チタン等が挙げられる。
　前記カーボンブラックとしては、例えば、＃２３００、＃２２００Ｂ、＃９９０、＃９００、＃９６０、＃９８０、＃３３、＃４０、＃４５、＃４５Ｌ、＃５２、ＨＣＦ８８、ＭＡ７、ＭＡ８、ＭＡ１００等（以上、三菱ケミカル株式会社製）；Ｒａｖｅｎシリーズ（５７５０、５２５０、５０００、３５００、１２５５、７００等）（以上、コロンビア社製）；Ｒｅｇａｌシリーズ（４００Ｒ、３３０Ｒ、６６０Ｒ等）、Ｍｏｇｕｌシリーズ（Ｌ、７００等）、Ｍｏｎａｒｃｈシリーズ（８００、８８０、９００、１０００、１０、１３００、１４００等）（以上、キャボット社製）；Ｃｏｌｏｒ　Ｂｌａｃｋシリーズ（ＦＷ１、ＦＷ２、ＦＷ２Ｖ、ＦＷ１８、ＦＷ２００、Ｓ１５０、Ｓ１６０、Ｓ１）、Ｐｒｉｎｔｅｘシリーズ（３５、Ｕ、Ｖ、１４００Ｕ等）、Ｓｐｅｃｉａｌ　Ｂｌｃｋシリーズ（６、５、４、４Ａ等）、ＮＩＰＥＸシリーズ（１５０、１６０、１７０、１８０、９５、９０、８５、８０、７５等）（以上、オリオン・エンジニアドカーボンズ株式会社製）などが挙げられる。
　前記有機顔料としては、１種又は２種以上を用いることができ、化学構造によれば、アゾレーキ顔料、不溶性アゾ顔料、縮合アゾ顔料、キレートアゾ顔料等のアゾ顔料；フタロシアニン顔料、ペリレン顔料、ペリノン顔料、アントラキノン顔料、キナクリドン顔料、ジオキサジン顔料、チオインジゴ顔料、イソインドリン顔料、キノフタロン顔料等の多環式顔料；塩基性染料型キレート、酸性染料型キレート等の染料キレート；ニトロ顔料；ニトロソ顔料；アニリンブラック等が挙げられる。
　前記有機顔料としては、具体的には、
　Ｃ．Ｉ．ピグメントイエロー１、２、１２、１３、１４、１６、１７、７３、７４、７５、８３、９３、９５、９７、９８、１０９、１１０、１１４、１２０、１２８、１２９、１３８、１５０、１５１、１５４、１５５、１７４、１８０、１８５等のイエロー顔料；
　Ｃ．Ｉ．ピグメントレッド５、７、１２、４８（Ｃａ）、４８（Ｍｎ）、５７（Ｃａ）、５７：１、１１２、１２２、１２３、１４６、１５０、１６８、１７６、１８４、１８５、２０２、２０９、２１３、２６９、２８２等のマゼンダ顔料；
　Ｃ．Ｉ．ピグメントブルー１、２、３、１５、１５：１、１５：２、１５：３、１５：４、１５：６、１６、２２、６０、６３、６６等のシアン顔料；
Ｃ．Ｉ．ピグメントオレンジ５、１３、１６、１７、３４、３６、４３、５１、６４、７１等のオレンジ顔料；
　Ｃ．Ｉ．ピグメントバイオレット１、３、５：１、１６、１９、２３、３８等のバイオレット顔料；
Ｃ．Ｉ．ピグメントグリーン１、４、７、８、１０、１７、１８、３６等のグリーン顔料；
　Ｃ．Ｉ．ピグメントレッド１、２、３、５、１７、２２、２３、３１、３８、４８：２、４８：３、４８：４、４９：１、５２：２、５３：１、５７：１、６０：１、６３：１、６３：２、６４：１、８１、８３、８８、１０１、１０４、１０５、１０６、１０８、１１２、１１４、１２２、１２３、１４６、１４９、１５０、１６６、１６８、１７０、１７２、１７７、１７８、１７９、１８４、１８５、１９０、１９３、２０２、２０７、２０８、２０９、２１３、２１９、２２４、２５４、２６４等のレッド顔料などが挙げられる。
　前記顔料の一次粒子径は、分散性の観点から、好ましくは２５μｍ以下、より好ましくは１０μｍ以下、さらに好ましくは１μｍ以下であり、安定性の観点から、例えば１０ｍ以上、３０ｎｍ以上であってもよい。前記一次粒子径は、透過型電子顕微鏡（ＴＥＭ）により測定できる。
　前記顔料の体積平均粒子径は、分散性の観点から、好ましくは１μｍ以下、より好ましくは２５０ｎｍ以下、さらに好ましくは２００ｎｍ以下であり、安定性の観点から、例えば１０ｎｍ以上、５０ｎｍ以上であってもよい。前記顔料の体積平均粒子径は、レーザー回折法により測定できる。
　前記顔料の含有率は、前記着色剤中、好ましくは８０質量％以上、より好ましくは９質量％以上、さらに好ましくは９５質量％以上であり、上限は１００質量％である。
　前記着色剤の含有率は、前記インクジェットインク組成物の固形分中、好ましくは１質量％以上、より好ましくは５質量％以上、さらに好ましくは１０質量％以上であり、好ましくは９０質量％以下、より好ましくは８０質量％以下、さらに好ましくは７０質量％以下である。
　前記顔料分散剤は、親水部と疎水部とを有する化合物であり、水性媒体中における顔料の分散性を向上する作用を有する。該顔料分散剤としては、スチレン－（メタ）アクリル酸共重合体、スチレン－（メタ）アクリル酸エステル－（メタ）アクリル酸共重合体、（メタ）アクリル酸エステル－（メタ）アクリル酸共重合体等のスチレン－アクリル酸共重合体等が挙げられる。前記スチレン－アクリル酸共重合体を用いる場合、前記水性顔料分散体には、水酸化カリウム等の塩基性化合物が共存していてもよい。
　前記顔料分散剤の含有量は、前記着色剤１００質量部に対して、好ましくは５質量部以上、より好ましくは１０質量部以上、さらに好ましくは２０質量部以上であり、好ましくは１００質量部以下、より好ましくは７０質量部以下、さらに好ましくは５０質量部以下である。
　前記有機溶剤としては、親水性有機溶剤（２５℃において水と混和しうる有機溶剤）が好ましく、具体的には、アセトン、メチルエチルケトン、メチルブチルケトン、メチルイソブチルケトン等のケトン溶剤；メタノール、エタノール、１－プロパノール、２－プロパノール、２－メチル－１－プロパノール、１－ブタノール、２－ブタノール、ペンチルアルコール、２－メトキシエタノール等のアルコール溶剤；テトラヒドロフラン、１，４－ジオキサン、１，２－ジメトキシエタン等のエーテル溶剤；ジメチルホルムアミド、Ｎ－メチルピロリドン等のアミド溶剤；エチレングリコール、ジエチレングリコール、トリエチレングリコール、テトラエチレングリコール、プロピレングリコール、ジプロピレングリコール、ポリエチレングリコール、ポリプロピレングリコール等のグリコール溶剤；ブタンジオール、ペンタンジオール、ヘキサンジオール、およびこれらと同族のジオール等のジオール溶剤；ラウリン酸プロピレングリコール等のグリコールエステル溶剤；ジエチレングリコールモノエチルエーテル、ジエチレングリコールモノブチルエーテル、ジエチレングリコールモノヘキシルエーテル、プロピレングリコールモノエチルエーテル、プロピレングリコールモノメチルエーテル、ジプロピレングリコールモノエチルエーテル、トリエチレングリコールモノエチルエーテル等のグリコールエーテル溶剤；スルホラン；γ－ブチロラクトン等のラクトン溶剤；Ｎ－メチルピロリドン、Ｎ－（２－ヒドロキシエチル）ピロリドン、２－ピロリドン等のラクタム溶剤；アセトニトリル等のニトリル溶剤；グリセリン；ポリオキシアルキレンを付加したグリセリン等のグリセリン誘導体等；これらの１種又は２種以上の混合溶剤などが挙げられる。
　前記有機溶剤は、分散性及び保存安定性の観点から、前記顔料１００質量部に対して、好ましくは１～３００質量部、より好ましくは４～２００質量部である。
　前記水性インクジェットインクは、予め、前記着色剤、前記顔料分散剤、前記有機溶剤、前記水性媒体及び必要に応じて用いる塩基性化合物を混合分散させることで、着色剤分散体を調製し、さらに、前記樹脂組成物、乾燥抑止剤、浸透剤、界面活性剤等の添加剤を混合することによって、製造することができる。前記着色剤分散体を調製する際、混合分散法としては、湿式分散法、混練分散法等が挙げられ、湿式分散法が好ましい。
　乾燥抑止剤としては、水性媒体との混和性があり、インクジェットプリンターのヘッドの目詰まり防止効果が得られるものを使用することが好ましく、例えば、グリセリン、エチレングリコール、ジエチレングリコール、トリエチレングリコール、トリエチレングリコールモノ－ｎ－ブチルエーテル、分子量２０００以下のポリエチレングリコール、プロピレングリコール、ジプロピレングリコール、トリプロピレングリコール、１，３－プロピレングリコール、イソプロピレングリコール、イソブチレングリコール、１，４－ブタンジオール、１，３－ブタンジオール、１，５－ペンタンジオール、１，６－ヘキサンジオール、メソエリスリトール、ペンタエリスリトール、等が挙げられる。なかでも、前記乾燥抑止剤としては、グリセリン、トリエチレングリコールを使用することが、安全性が高く、インクの乾燥性、吐出性能に優れた効果を付与できるため好ましい。前記乾燥抑剤の含有率は、前記水性インクジェットインク中、３～５０質量％であることが好ましい。
　前記浸透剤としては、例えばエタノール、イソプロピルアルコール等の低級アルコール；エチレングリコールヘキシルエーテル、ジエチレングリコールブチルエーテル、プロピレングリコールプロピルエーテル等のアルキルアルコールのグリコールモノエーテルが挙げられる。前記浸透剤の含有率は、記録媒体へのインクの浸透性の改良や、記録媒体上でのインクのドット径を調整する観点から、前記水性インクジェットインク中、０．０１～１０質量％であることが好ましい。
　前記界面活性剤としては、例えば、アニオン性界面活性剤、ノニオン性界面活性剤、カチオン性界面活性剤、両性界面活性剤等が挙げられ、表面張力等のインク特性を調整する観点から、アニオン性界面活性剤、ノニオン性界面活性剤が好ましい。
　アニオン性界面活性剤としては、例えば、アルキルベンゼンスルホン酸塩、アルキルフェニルスルホン酸塩、アルキルナフタレンスルホン酸塩、高級脂肪酸塩、高級脂肪酸エステルの硫酸エステル塩、高級脂肪酸エステルのスルホン酸塩、高級アルコールエーテルの硫酸エステル塩及びスルホン酸塩、高級アルキルスルホコハク酸塩、ポリオキシエチレンアルキルエーテルカルボン酸塩、ポリオキシエチレンアルキルエーテル硫酸塩、アルキルリン酸塩、ポリオキシエチレンアルキルエーテルリン酸塩等が挙げられ、これらの具体例として、ドデシルベンゼンスルホン酸塩、イソプロピルナフタレンスルホン酸塩、モノブチルフェニルフェノールモノスルホン酸塩、モノブチルビフェニルスルホン酸塩、ジブチルフェニルフェノールジスルホン酸塩等が好ましい。
　ノニオン性界面活性剤としては、例えば、ポリオキシエチレンアルキルエーテル、ポリオキシエチレンアルキルフェニルエーテル、ポリオキシエチレン脂肪酸エステル、ソルビタン脂肪酸エステル、ポリオキシエチレンソルビタン脂肪酸エステル、ポリオキシエチレンソルビトール脂肪酸エステル、グリセリン脂肪酸エステル、ポリオキシエチレングリセリン脂肪酸エステル、ポリグリセリン脂肪酸エステル、ショ糖脂肪酸エステル、ポリオキシエチレンアルキルアミン、ポリオキシエチレン脂肪酸アミド、脂肪酸アルキロールアミド、アルキルアルカノールアミド、アセチレングリコール、アセチレングリコールのオキシエチレン付加物、ポリエチレングリコールポリプロピレングリコールブロックコポリマー等を挙げることができ、これらの中では、ポリオキシエチレンノニルフェニルエーテル、ポリオキシエチレンオクチルフェニルエーテル、ポリオキシエチレンドデシルフェニルエーテル、ポリオキシエチレンアルキルエーテル、ポリオキシエチレン脂肪酸エステル、ソルビタン脂肪酸エステル、ポリオキシエチレンソルビタン脂肪酸エステル、脂肪酸アルキロールアミド、アセチレングリコール、アセチレングリコールのオキシエチレン付加物、ポリエチレングリコールポリプロピレングリコールブロックコポリマーが好ましい。
　その他の界面活性剤として、ポリシロキサンオキシエチレン付加物のようなシリコーン系界面活性剤；パーフルオロアルキルカルボン酸塩、パーフルオロアルキルスルホン酸塩、オキシエチレンパーフルオロアルキルエーテルのようなフッ素系界面活性剤；スピクリスポール酸、ラムノリピド、リゾレシチンのようなバイオサーファクタント等を使用してもよい。
　前記界面活性剤の含有率は、印刷画像等のにじみ等を効果的に防止する観点から、前記水性インクジェットインク中、好ましくは０．００１～２質量％であり、より好ましくは０．００１～１．５質量％であり、さらに好ましくは０．０１～１質量％である。
　インクジェット記録用水性インクは、各種記録媒体への印刷に使用することができる。前記記録媒体としては、複写機で一般的に使用されているコピー用紙（ＰＰＣ紙）等の吸収性の記録媒体、インクの吸収層を有する記録媒体、インクの吸収性を有しない非吸水性の記録媒体、インクの吸水性の低い難吸収性の記録媒体、布帛、フィルム等がありうる。
　本発明の水性インクジェットインク用バインダーは、保存安定性及び吐出性、並びに、印刷物の耐擦過性及び耐洗濯性に優れることから、各種記録媒体への印刷に有用である。
　以下に本発明を具体的な実施例を挙げてより詳細に説明する。なお、重量平均分子量及び平均粒子径は、下記の測定条件で測定したものである。
［ＧＰＣ測定条件］
測定装置：高速ＧＰＣ装置（東ソー株式会社製「ＨＬＣ－８２２０ＧＰＣ」）
カラム：東ソー株式会社製の下記のカラムを直列に接続して使用した。
　「ＴＳＫｇｅｌ　Ｇ５０００」（７．８ｍｍＩ．Ｄ．×３０ｃｍ）×１本
　「ＴＳＫｇｅｌ　Ｇ４０００」（７．８ｍｍＩ．Ｄ．×３０ｃｍ）×１本
　「ＴＳＫｇｅｌ　Ｇ３０００」（７．８ｍｍＩ．Ｄ．×３０ｃｍ）×１本
　「ＴＳＫｇｅｌ　Ｇ２０００」（７．８ｍｍＩ．Ｄ．×３０ｃｍ）×１本
検出器：ＲＩ（示差屈折計）
カラム温度：４０℃
溶離液：テトラヒドロフラン（ＴＨＦ）
流速：１．０ｍＬ／分
注入量：１００μＬ（試料濃度４ｍｇ／ｍＬのテトラヒドロフラン溶液）
標準試料：下記の単分散ポリスチレンを用いて検量線を作成した。
（単分散ポリスチレン）
　東ソー株式会社製「ＴＳＫｇｅｌ　標準ポリスチレン　Ａ－５００」
　東ソー株式会社製「ＴＳＫｇｅｌ　標準ポリスチレン　Ａ－１０００」
　東ソー株式会社製「ＴＳＫｇｅｌ　標準ポリスチレン　Ａ－２５００」
　東ソー株式会社製「ＴＳＫｇｅｌ　標準ポリスチレン　Ａ－５０００」
　東ソー株式会社製「ＴＳＫｇｅｌ　標準ポリスチレン　Ｆ－１」
　東ソー株式会社製「ＴＳＫｇｅｌ　標準ポリスチレン　Ｆ－２」
　東ソー株式会社製「ＴＳＫｇｅｌ　標準ポリスチレン　Ｆ－４」
　東ソー株式会社製「ＴＳＫｇｅｌ　標準ポリスチレン　Ｆ－１０」
　東ソー株式会社製「ＴＳＫｇｅｌ　標準ポリスチレン　Ｆ－２０」
　東ソー株式会社製「ＴＳＫｇｅｌ　標準ポリスチレン　Ｆ－４０」
　東ソー株式会社製「ＴＳＫｇｅｌ　標準ポリスチレン　Ｆ－８０」
　東ソー株式会社製「ＴＳＫｇｅｌ　標準ポリスチレン　Ｆ－１２８」
　東ソー株式会社製「ＴＳＫｇｅｌ　標準ポリスチレン　Ｆ－２８８」
　東ソー株式会社製「ＴＳＫｇｅｌ　標準ポリスチレン　Ｆ－５５０」
［粒子径測定条件］
　水性インクジェットインク用バインダーを水で希釈し、濃度０．１質量％の希釈分散体とした後、この希釈分散体を用い、粒子径測定装置（マイクロトラック・ベル株式会社製「ナノトラックＷａｖｅＩＩ」：動的光散乱法により算出）にて測定し、５０％メジアン径を平均粒子径とした。
（合成例１：アクリルマクロマー（１）の合成）
　温度計、攪拌装置、還流冷却管及び窒素導入管を備えた４ッ口フラスコに、メチルエチルケトン ７００質量部を仕込み、次いで前記反応容器中にメチルメタクリレート　２９１質量部と３－メルカプト－１，２－プロパンジオール ８．７質量部と２，２’－アゾビス（２－メチルプロピオニトリル)　０．１５質量部を供給し、反応させることによって、数平均分子量３０００の片末端に２個の水酸基を有するビニル重合体として、アクリルマクロマー（１）を得た。
（製造例１：酸基を有するポリウレタン（ａ１－１）の製造）
　温度計、攪拌装置、還流冷却管及び窒素導入管を備えた４つ口フラスコに、ＰＴＭＧ１ｋ（三菱ケミカル製「ＰＴＭＧ１０００」；数平均分子量１０００のポリテトラメチレンエーテルグリコール）５０．９質量部、及び２，２－ジメチロールプロピオン酸（ＤＭＰＡ）１２．６質量部を入れ、十分に撹拌させた。次いで、イソホロンジイソシアネート（ＩＰＤＩ）３１．５質量部、触媒としてジブチルスズジラウリレート０．０１質量部を加え、７５℃で４時間反応させた。反応後、メチルエチルケトン（ＭＥＫ）で固形分濃度が６０質量％になるようＭＥＫを入れ、３０分撹拌させるとともに、４０℃以下まで冷却し、ウレタンプレポリマー溶液を得た。得られたウレタンプレポリマー溶液に水酸化カリウム５．０質量部を加え、酸基を中和させた。次いで強攪拌下で固形分濃度が１８％になるようイオン交換水を添加し、ポリウレタンを乳化させた。反応完結後、減圧蒸留によりＭＥＫを留去し、酸基を有するポリウレタン（ａ１－１）の水分散体を得た。この水分散体の不揮発分は３０質量％であった。
（製造例２：酸基を有するポリウレタン（ａ１－２）の製造）
　原料配合を表１に変更した以外は、製造例１と同様にして、酸基を有するポリウレタン（ａ１－２）の水分散体を得た。この水分散体の不揮発分は３０質量％であった。
（製造例３：酸基を有するポリウレタン（ａ１－３）の製造）
　原料配合を表１に変更した以外は、製造例１と同様にして、酸基を有するウレタンプレポリマー溶液を得た。得られたウレタンプレポリマー溶液に水酸化カリウム１．９質量部を加え、酸基を中和させた。次いで強攪拌下で固形分濃度が１８％になるようイオン交換水を添加し、エチレンジアミンを２．７質量部滴下し、伸長反応を行った。反応完結後、減圧蒸留によりＭＥＫを留去し、酸基を有するポリウレタン（ａ１－３）の水分散体を得た。この水分散体の不揮発分は３０質量％であった。
（製造例４：酸基を有するポリウレタン（ａ１－４）の製造）
　原料配合を表１に変更した以外は、製造例３と同様にして、酸基を有するポリウレタン（ａ１－４）の水分散体を得た。この水分散体の不揮発分は３０質量％であった。
（製造例５：酸基を有するポリウレタン（ａ１－５）の製造）
　原料配合を表１に変更した以外は、製造例１と同様にして、酸基を有するポリウレタン（ａ１－５）の水分散体を得た。この水分散体の不揮発分は３０質量％であった。
（製造例６：酸基を有するポリウレタン（ａ１－６）の製造）
　原料配合を表１に変更した以外は、製造例１と同様にして、酸基を有するポリウレタン（ａ１－６）の水分散体を得た。この水分散体の不揮発分は３０質量％であった。
　上記で得た酸基を有するポリウレタン（ａ１－１）～（ａ１－６）の配合を表１に示す。
Figure JPOXMLDOC01-appb-T000001
　表１中の略号は下記の通りである。
　ＰＴＭＧ１ｋ：三菱ケミカル製「ＰＴＭＧ１０００」；数平均分子量１０００のポリテトラメチレンエーテルグリコール
　Ｅｘｃｅｎｏｌ　２０２０：ＡＧＣ製「Ｅｘｃｅｎｏｌ　２０２０」；数平均分子量２０００のポリプロピレングリコール
　ＵＨ－１００：宇部興産製「ＥＴＥＲＮＡＣＯＬＬ　ＵＨ－１００」；数平均分子量１０００の結晶性ポリカーボネートジオール　
　ＵＨ－２００：宇部興産製「ＥＴＥＲＮＡＣＯＬＬ　ＵＨ－２００」；数平均分子量２０００の結晶性ポリカーボネートジオール
　Ｇ３４５０Ｊ：旭化成製「ＤＵＲＡＮＯＬ　Ｇ３４５０Ｊ」；数平均分子量８００の非晶性ポリカーボネートジオール
（実施例１：水性インクジェットインク用バインダー（１）の製造）
　製造例１で得た酸基を有するポリウレタン（ａ１－１）の水分散体２３３．４０質量部にイオン交換水２３６．５９質量部を加え、イソプレン２９．９９質量部、及びスチレン０．０１質量部を過硫酸アンモニウム（ＡＰＳ）０．０１質量部でモノマー一括乳化重合（反応温度８０℃）の条件下で反応させて、次に未反応モノマー除去の濃縮を行い、水分量を２０質量％に調整し水性インクジェットインク用バインダー（１）を得た。質量比（ａ１／ａ２）は、７０／３０であった。また、複合樹脂の粒度分布は単一のピークを示し、コアシェル粒子を形成していることが確認され、平均粒子径は４０ｎｍであった。
（実施例２～６：水性インクジェットインク用バインダー（２）～（６）の製造）
　実施例１で使用した酸基を有するポリウレタン（ａ１－１）の水分散体を、酸基を有するポリウレタン（ａ１－２）～（ａ１－６）の水分散体に変更した以外は、実施例１と同様にして、水性インクジェットインク用バインダー（２）～（６）を得た。質量比（ａ１／ａ２）は、全て７０／３０であった。また、複合樹脂の粒度分布は単一のピークを示し、コアシェル粒子を形成していることが確認され、平均粒子径は水性インクジェットインク用バインダー（２）が１１１ｎｍ、水性インクジェットインク用バインダー（３）が９５ｎｍ、水性インクジェットインク用バインダー（４）が４２ｎｍ、水性インクジェットインク用バインダー（５）が３３ｎｍ、水性インクジェットインク用バインダー（６）が３８ｎｍであった。
（比較例１：水性インクジェットインク用バインダー（Ｒ１））
　製造例１で得た酸基を有するポリウレタン（ａ１－１）の水分散体を、水性インクジェットインク用バインダー（Ｒ１）とした。
［顔料分散体の製造］
ミニプラネタリーミキサー（株式会社愛工舎ｍｉｎｉ-ＰＬＭ）の０．５Ｌジャケット付タンクに、５０質量部のＣ．Ｉ．ピグメントレッド１２２（ＤＩＣ株式会社製「ＦＡＳＴＯＧＥＮ　Ｓｕｐｅｒ　Ｍａｇｅｎｔａ　ＲＹ」）Ｃ．Ｉ．ピグメントブルー１５：３（ＤＩＣ株式会社製、ＳＢＧ－ＳＤ）、１０質量部のスチレン－アクリル酸共重合体（重量平均分子量１１，０００、酸価１８０　ｍｇＫＯＨ／ｇ）を順番に投入し、ジャケット付タンクの温度を８０℃に加温した状態で、自転回転数８０ｒｐｍ、公転回転数２５ｒｐｍで１０分間撹拌した。
　次に、ジャケット付タンクの温度を８０℃に保温した状態で、５．３質量部の３４質量％水酸化カリウム水溶液、３０質量部のトリエチレングリコールを前記組成物に加え、自転回転数８０ｒｐｍ、公転回転数２５ｒｐｍで６０分間混練を行うことによって、固形状の混練物を得た。
　前記混練物に、イオン交換水１００質量部とトリエチレングリコール１０質量部を加え、ジューサーミキサーで１０分間攪拌混合した。イオン交換水とＰｒｏｘｅｌ－ＧＸＬ（ロンザジャパン株式会社）を混合することによって、顔料濃度が１５．０質量％、トリエチレングリコール濃度が１２．０質量％、Ｐｒｏｘｅｌ－ＧＸＬ濃度が０．１質量％、不揮発分が１８．２質量％の水性顔料分散体を得た。
［水性インクジェットインクの製造］
上記で得た顔料分散体２０．０質量部、前記水性インクジェット用バインダー３．３質量部、２－ピロリジノン（ＢＡＳＦ社製）８.０質量部、トリエチレングリコールモノ－ｎ－ブチルエーテル（東京化成工業株式会社製）８.０質量部、グリセリン（花王株式会社製）３.０質量部、サーフィノール４４０（非イオン系界面活性剤、エボニックジャパン株式会社製）０．５質量部、イオン交換水５７．３質量部を１時間撹拌した。
次に、５質量％水酸化カリウム水溶液を用いｐＨを９～９．８の範囲内に調整したものを、孔径５～１０μｍのフィルターでろ過することによって、水性インクジェットインク（顔料濃度３．０％、ウレタン固形分濃度１．０％）を得た。
［耐擦過性の評価］
　上記で得た水性インクジェットインクを市販のインクジェットプリンターＥＮＶＹ４５００（ＨＰ社製）ブランクインクカートリッジに充填し、写真印刷用紙（ＨＰアドバンスフォトペーパー　ＨＰ社製）の印刷面に印字濃度設定１００％のベタ印刷を行った。印刷物を常温下で１分間乾燥した後、学振式摩擦試験機を用いて荷重２００ｇの条件にて印刷士紙と同じ紙で印刷面を３往復摩擦させた。
次に、前記印刷物の印刷面をスキャン処理して画像データ化し、下記の式に基づきピクセル残存率（％）を算出し、下記の基準により、耐擦過性を評価した。
ピクセル残存率（％）＝（擦過試験後の着色部のピクセル数）／（擦過試験前の着色部のピクセル数）×１００
〇：４０％以上
△：２０％以上４０％未満
×：２０％未満
［耐洗濯性の評価］
　綿ブロード全面を染色後、１５０℃で５分間乾燥させた。その後ＪＩＳＬ０８４４：２０１１に基づいて調製した洗濯液を５０℃に加温し、前記綿ブロードを浸漬（３０分間）させた。次いでフードミキサー中で１分間攪拌させ、取り出した試験用サンプルを水で洗った後乾燥した。積分球分光測色計Ｘ－Ｒｉｔｅでミキサー攪拌後の綿ブロードの光学濃度（ＯＤ）を測定した。下記の式に基づきＯＤ保持率（％）を算出し、下記の基準により、耐洗濯性を評価した。
　ＯＤ保持率（％）＝（攪拌後の綿ブロードのＯＤ）／（洗濯液浸漬前の綿ブロードのＯＤ）×１００
〇：５０％以上
△：４５％以上５０％未満
×：４５％未満
　上記で得た水性インクジェットインク用バインダー（１）～（５）及び（Ｒ１）の配合及び評価結果を表２に示す。
Figure JPOXMLDOC01-appb-T000002
　本発明の水性インクジェットインク用バインダーである実施例１～６から得られる印刷物は、耐擦過性及び耐洗濯性に優れることが確認された。
　一方、比較例１は、本発明の必須成分であるラテックス（ａ２）を含まないウレタン樹脂を用いた例であるが、得られる印刷物は耐擦過性及び耐洗濯性に劣ることが確認された。

Claims (5)

  1. 　複合樹脂（Ａ）及び水性媒体（Ｂ）を含有する水性インクジェットインク用バインダーであって、前記複合樹脂（Ａ）が、酸基を有するポリウレタン（ａ１）を含むシェル部と、脂肪族共役ジエンを必須原料とする重合体（ａ２）を含むコア部とを有するコアシェル型粒子を形成していることを特徴とする水性インクジェットインク用バインダー。
  2. 前記ポリウレタン（ａ１）の酸価が１０～７０ｍｇＫＯＨ／ｇである請求項１記載の水性インクジェットインク用バインダー。
  3. 　前記ポリウレタン（ａ１）と前記重合体（ａ２）との質量比（ａ１／ａ２）が、９５／５～５０／５０である請求項１又は２記載の水性インクジェットインク用バインダー。
  4. 　請求項１～３いずれか１項記載の水性インクジェットインク用バインダーを含む水性インクジェットインク。
  5. 　請求項４記載の水性インクジェットインクから形成される印刷層。
PCT/JP2022/039034 2021-10-28 2022-10-20 水性インクジェットインク用バインダー、水性インクジェットインク、及び印刷層 Ceased WO2023074513A1 (ja)