WO2023164931A1 - 正极极片、二次电池、电池模块、电池包和用电装置 - Google Patents

正极极片、二次电池、电池模块、电池包和用电装置 Download PDF

Info

Publication number
WO2023164931A1
WO2023164931A1 PCT/CN2022/079295 CN2022079295W WO2023164931A1 WO 2023164931 A1 WO2023164931 A1 WO 2023164931A1 CN 2022079295 W CN2022079295 W CN 2022079295W WO 2023164931 A1 WO2023164931 A1 WO 2023164931A1
Authority
WO
WIPO (PCT)
Prior art keywords
positive electrode
active material
electrode active
range
preparation example
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/CN2022/079295
Other languages
English (en)
French (fr)
Inventor
周翔
蒋耀
刘江
李白清
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Contemporary Amperex Technology Co Ltd
Original Assignee
Contemporary Amperex Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Contemporary Amperex Technology Co Ltd filed Critical Contemporary Amperex Technology Co Ltd
Priority to PCT/CN2022/079295 priority Critical patent/WO2023164931A1/zh
Priority to EP22902499.7A priority patent/EP4280301A4/en
Priority to CN202280017128.1A priority patent/CN116941063A/zh
Priority to US18/363,989 priority patent/US20230378462A1/en
Publication of WO2023164931A1 publication Critical patent/WO2023164931A1/zh
Priority to US18/669,469 priority patent/US12548772B2/en
Priority to US18/669,462 priority patent/US12633539B2/en
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

本申请提供了一种正极极片、二次电池、电池模块、电池包和用电装置；其中，正极极片包括正极集流体和设置在其至少一个表面上的具有单层或多层结构的正极膜层；当正极膜层为单层结构时，至少一个正极膜层同时包含化学式为Li aA xMn 1-yR yP 1-zC zO 4-nD n的第一正极活性材料和第二正极活性材料；和/或，当正极膜层为多层结构时，至少一个正极膜层的至少一层中同时包含第一正极活性材料和第二正极活性材料。本申请正极极片所制二次电池的能量密度高，电芯倍率性能高，动力学性能和低温性能好，循环性能好，安全性高。

Description

正极极片、二次电池、电池模块、电池包和用电装置 技术领域
本申请涉及二次电池技术领域，尤其涉及一种正极极片、二次电池、电池模块、电池包和用电装置。
背景技术
近年来，随着二次电池的应用范围越来越广，二次电池广泛应用于水力、火力、风力和太阳能电站等储能电源系统，以及电动工具、电动自行车、电动摩托车、电动汽车、军事装备、航空航天等多个领域。由于二次电池取得了极大的发展，因此对其能量密度、循环性能和安全性能等也提出了更高的要求。以现有的磷酸锰铁锂作为主材，与三元材料镍钴锰酸锂、镍钴铝酸锂或钴酸锂等混掺后制作二次电池，这种技术虽然结合了磷酸锰铁锂与三元材料的各自优势，但磷酸锰铁锂使得电池的动力学性能较差、电芯倍率性能较低，不能满足动力电池需求。
发明内容
本申请是鉴于上述课题而进行的，其目的在于，提供一种正极极片、二次电池、电池模块、电池包和用电装置，以解决采用现有正极活性材料所制二次电池的能量密度低、电芯倍率性能低、动力学性能差、低温性能差、循环寿命短、安全性低的问题。
为了达到上述目的，本申请的第一方面提供了一种正极极片，包括正极集流体和设置在正极集流体的至少一个表面上的正极膜层；正极膜层为单层结构或多层结构；当正极膜层为单层结构时，至少一个正极膜层同时包含化学式为Li aA xMn 1-yR yP 1-zC zO 4-nD n的第一正极活性材料和第二正极活性材料；和/或，当正极膜层为多层结构时，至少一个正极膜层的至少一层中同时包含化学式为 Li aA xMn 1-yR yP 1-zC zO 4-nD n的第一正极活性材料和第二正极活性材料；其中，A包括选自Zn、Al、Na、K、Mg、Nb、Mo和W中的一种或多种元素；R包括选自Ti、V、Zr、Fe、Ni、Mg、Co、Ga、Sn、Sb、Nb和Ge中的一种或多种元素；C包括选自B、S、Si和N中的一种或多种元素；D包括选自S、F、Cl和Br中的一种或多种元素；a选自0.9至1.1的范围，x选自0.001至0.1的范围，y选自0.001至0.5的范围，z选自0.001至0.1的范围，n选自0.001至0.1的范围；第二正极活性材料选自LiNi bCo cMn (1-b-c)O 2、LiNi bCo cAl (1-b-c)O 2和LiCoO 2中的一种或多种；其中，b独立地选自0.3-0.9(可选为0.33-0.8)，b与c之和独立地选自0.3-0.9(可选为0.66-0.9)。
由此，本申请人意外地发现：通过在化合物LiMnPO 4的Li位、Mn位、P位和O位同时以特定量掺杂特定的元素获得第一正极活性材料，能获得明显改善的倍率性能，同时显著减少Mn与Mn位掺杂元素的溶出，获得显著改善的循环性能和/或高温稳定性，并且材料的克容量和压实密度也得到提高，界面副反应减少。本申请通过将第一正极活性材料和第二正极活性材料混合使用，两种材料的优势互补，提升了二次电池的能量密度，同时使电池兼具优良的倍率性能、动力学性能、循环性能、低温性能和安全性。第一正极活性材料的颗粒均匀包覆在第二正极活性材料表面，使第二正极活性材料的晶格相对独立、骨架稳定，在二次电池充放电过程中不易坍塌，进一步提高了二次电池的循环寿命；并且，第一正极活性材料形成的包覆层为外力撞击或剪切提供了弹性应变力，有效解决了第二正极活性材料的安全性问题。
本申请的第二方面还提供一种正极极片，包括正极集流体和设置在正极集流体的至少一个表面上的正极膜层；至少一个正极膜层为多层结构，任一具有多层结构的正极膜层在不同层中分别包含化学式为Li aA xMn 1-yR yP 1-zC zO 4-nD n的第一正极活性材料和第二正极活性材料；其中，A包括选自Zn、Al、Na、K、Mg、Nb、Mo和W中的一种或多种元素；R包括选自Ti、V、Zr、Fe、Ni、Mg、Co、Ga、Sn、Sb、Nb和Ge中的一种或多种元素；C包括选自B、S、Si和N中的一种 或多种元素；D包括选自S、F、Cl和Br中的一种或多种元素；a选自0.9至1.1的范围，x选自0.001至0.1的范围，y选自0.001至0.5的范围，z选自0.001至0.1的范围，n选自0.001至0.1的范围；第二正极活性材料选自LiNi bCo cMn (1-b-c)O 2、LiNi bCo cAl (1-b-c)O 2和LiCoO 2中的一种或多种；其中，b独立地选自0.3-0.9(可选为0.33-0.8)，b与c之和独立地选自0.3-0.9(可选为0.66-0.9)；可选地，任一具有多层结构的正极膜层在相邻层中分别包含第一正极活性材料和第二正极活性材料。
由此，第一正极活性材料具有明显改善的倍率性能，同时显著减少Mn与Mn位掺杂元素的溶出，获得显著改善的循环性能和/或高温稳定性，并且材料的克容量和压实密度也得到提高，界面副反应减少。本申请将第一正极活性材料和第二正极活性材料组合使用，两种材料的优势互补，提升了二次电池的能量密度，同时使二次电池兼具优良的倍率性能、动力学性能、循环性能和低温性能，并且，第一正极活性材料为外力撞击或剪切提供了弹性应变力，有效解决了第二正极活性材料的安全性问题。
本申请的第三方面提供一种正极极片，包括正极集流体和分别设置在正极集流体的两个表面上的正极膜层A和正极膜层B；正极膜层A和正极膜层B独立地为单层结构或多层结构；正极膜层A的至少一层中包含化学式为Li aA xMn 1-yR yP 1-zC zO 4-nD n的第一正极活性材料，同时，正极膜层B的至少一层中包含第二正极活性材料；其中，A包括选自Zn、Al、Na、K、Mg、Nb、Mo和W中的一种或多种元素；R包括选自Ti、V、Zr、Fe、Ni、Mg、Co、Ga、Sn、Sb、Nb和Ge中的一种或多种元素；C包括选自B、S、Si和N中的一种或多种元素；D包括选自S、F、Cl和Br中的一种或多种元素；a选自0.9至1.1的范围，x选自0.001至0.1的范围，y选自0.001至0.5的范围，z选自0.001至0.1的范围，n选自0.001至0.1的范围；第二正极活性材料选自LiNi bCo cMn (1-b-c)O 2、LiNi bCo cAl (1-b-c)O 2和LiCoO 2中的一种或多种；其中，b独立地选自0.3-0.9(可选为0.33-0.8)，b与c之和独立地选自0.3-0.9(可选为0.66-0.9)。
由此，第一正极活性材料具有明显改善的倍率性能，同时显著减少Mn与Mn位掺杂元素的溶出，获得显著改善的循环性能和/或高温稳定性，并且材料的克容量和压实密度也得到提高，界面副反应减少。本申请将第一正极活性材料和第二正极活性材料组合使用，两种材料的优势互补，提升了二次电池的能量密度，同时使二次电池兼具优良的倍率性能、动力学性能、循环性能和低温性能，并且，第一正极活性材料为外力撞击或剪切提供了弹性应变力，有效解决了第二正极活性材料的安全性问题。
除非另有说明，否则化学式Li aA xMn 1-yR yP 1-zC zO 4-nD n中，当A为两种以上元素时，上述对于x数值范围的限定不仅是对每种作为A的元素的化学计量数的限定，也是对各个作为A的元素的化学计量数之和的限定。例如当A为两种以上元素A1、A2……An时，A1、A2……An各自的化学计量数x1、x2……xn各自均需落入本申请对x限定的数值范围内，且x1、x2……xn之和也需落入该数值范围内。类似地，对于B、C和D为两种以上元素的情况，本申请中对R、C和D化学计量数的数值范围的限定也具有上述含义。
在第一方面至第三方面的任意实施方式中，第一活性材料与第二活性材料的质量比为1:7-7:1，可选为1:4-4:1，进一步可选为1:3-3:1，例如1:7、1:5、1:3、1:2、3:5、1:1、5:3、2:1、3:1、5:1、7:1。以保证二次电池兼具优良的倍率性能和循环性能，具有较高的能量密度、优良的动力学性能和低温性能，减少界面副反应，提高二次电池的安全性。
在第一方面至第三方面的任意实施方式中，第一正极活性材料中，R选自Ti、V、Zr、Fe、Ni、Mg、Co、Ga、Sn、Sb、Nb和Ge中的至少两种元素。由此，可更准确地控制第一正极活性材料的组成。
在第一方面至第三方面的任意实施方式中，第一正极活性材料中，A为选自Mg和Nb中的任一种元素；和/或，R为选自Fe、Ti、V、Co和Mg中的至少两种元素，可选地为Fe与选自Ti、V、Co和Mg中的一种以上元素；和/或，C为S；和/或，D为F。通过在上述范围内对掺杂元素进行选择，能进一步地改善二次电池的倍率性能、提高 电子电导率，从而提升二次电池的倍率性能、克容量和高温性能，减轻界面的副反应。
在第一方面至第三方面的任意实施方式中，第一正极活性材料中，x选自0.001-0.005的范围。通过在该范围内对x值进行选择，能进一步提升第一正极活性材料的动力学性能。
在第一方面至第三方面的任意实施方式中，第一正极活性材料中，y选自0.01至0.5的范围，可选地选自0.25至0.5的范围。通过在该范围内对y值进行选择，能进一步提升第一正极活性材料的克容量和倍率性能。
在第一方面至第三方面的任意实施方式中，第一正极活性材料中，z选自0.001至0.005的范围。通过在该范围内对z值进行选择，能进一步提升二次电池的倍率性能。
在第一方面至第三方面的任意实施方式中，第一正极活性材料中，n选自0.001至0.005的范围。通过在该范围内对n值进行选择，能进一步提升二次电池的高温性能。
在第一方面至第三方面的任意实施方式中，第一正极活性材料中，(1-y)与y的比值选自1-4，可选为选自1.5-3。这样可以使二次电池的能量密度和循环性能进一步提升。
在第一方面至第三方面的任意实施方式中，第一正极活性材料中，a与x的比值选自9-1100，可选为选自190-998。在满足这一条件时，使二次电池的能量密度和循环性能进一步提升。
在第一方面至第三方面的任意实施方式中，第一正极活性材料的晶格变化率为8％以下，可选地为4％以下。通过降低晶格变化率，有利于改善二次电池的倍率性能。晶格变化率可通过本领域中已知的方法，例如X射线衍射图谱(XRD)测得。
在第一方面至第三方面的任意实施方式中，第一正极活性材料的Li/Mn反位缺陷浓度为2％以下，可选地为0.5％以下。所谓Li/Mn反位缺陷，指的是LiMnPO 4晶格中，Li +与Mn 2+的位置发生互换。Li/Mn反位缺陷浓度指的是正极活性材料中与Mn 2+发生互换的Li +占Li +总量的百分比。通过降低Li/Mn反位缺陷浓度，有利于提高第一正极活 性材料的克容量和倍率性能。Li/Mn反位缺陷浓度可通过本领域中已知的方法，例如XRD测得。
在第一方面至第三方面的任意实施方式中，第一正极活性材料的表面氧价态为-1.82以下，可选地为-1.89～-1.98。通过降低表面氧价态，能够减轻第一正极活性材料与电解液的界面副反应，从而改善二次电池的循环性能和高温稳定性。表面氧价态可通过本领域中已知的方法测量，例如通过电子能量损失谱(EELS)测量。
在第一方面至第三方面的任意实施方式中，第一正极活性材料在3T下的压实密度为2.0g/cm 3以上，可选地为2.2g/cm 3以上。压实密度越高，单位体积的第一正极活性材料的重量越大，因此提高压实密度有利于提高电芯的体积能量密度。压实密度可依据GB/T24533-2009测量。
在第一方面至第三方面的任意实施方式中，第一正极活性材料的表面还包覆有碳。由此，可以改善第一正极活性材料的导电性。
在第一方面至第三方面的任意实施方式中，LiNi bCo cMn (1-b-c)O 2中的b、(1-b-c)和c的比值为5:2:3或3:1:1或8:1:1；和/或，LiNi bCo cAl (1-b-c)O 2中的b、c和(1-b-c)的比值为5:2:3或3:1:1或8:1:1。由此能进一步提升二次电池的能量密度。
在第一方面至第三方面的任意实施方式中，第一正极活性材料和第二正极活性材料的质量之和占正极极片的质量的88％-98.7％。进一步保证二次电池具有优良的倍率性能、动力学性能、循环性能和低温性能，且具有较高的能量密度。
本申请的第四方面提供一种二次电池，包括本申请第一方面至第三方面中任一的正极极片。
本申请的第五方面提供一种电池模块，包括本申请的第四方面的二次电池。
本申请的第六方面提供一种电池包，包括本申请的第五方面的电池模块。
本申请的第七方面提供一种用电装置，包括选自本申请的第四方面的二次电池、本申请的第五方面的电池模块和本申请的第六方面的 电池包中的至少一种。
附图说明
图1是本申请一实施方式的二次电池的示意图。
图2是图1所示的本申请一实施方式的二次电池的分解图。
图3是本申请一实施方式的电池模块的示意图。
图4是本申请一实施方式的电池包的示意图。
图5是图4所示的本申请一实施方式的电池包的分解图。
图6是本申请一实施方式的二次电池用作电源的用电装置的示意图。
图7是本申请正极极片P1所制电池结构的示意图。
图8是本申请正极极片P2所制电池结构的示意图。
图9是本申请正极极片P3所制电池结构的示意图。
图10是本申请正极极片P8所制电池结构的示意图。
图11是本申请正极极片P10所制电池结构的示意图。
图12是本申请正极极片P11所制电池结构的示意图。
图13是本申请正极极片P12所制电池结构的示意图。
图14是本申请正极极片P17所制电池结构的示意图。
图15是本申请正极极片P18所制电池结构的示意图。
图16是本申请正极极片P23所制电池结构的示意图。
图17是本申请正极极片P24所制电池结构的示意图。
图18是本申请正极极片P26所制电池结构的示意图。
图19是本申请正极极片P27所制电池结构的示意图。
附图标记说明：
1电池包；2上箱体；3下箱体；4电池模块；5二次电池；51壳体；52电极组件；53顶盖组件。
具体实施方式
以下，适当地参照附图详细说明具体公开了本申请的正极极片、二次电池、电池模块、电池包和用电装置的实施方式。但是会有省略 不必要的详细说明的情况。例如，有省略对已众所周知的事项的详细说明、实际相同结构的重复说明的情况。这是为了避免以下的说明不必要地变得冗长，便于本领域技术人员的理解。此外，附图及以下说明是为了本领域技术人员充分理解本申请而提供的，并不旨在限定权利要求书所记载的主题。
本申请所公开的“范围”以下限和上限的形式来限定，给定范围是通过选定一个下限和一个上限进行限定的，选定的下限和上限限定了特别范围的边界。这种方式进行限定的范围可以是包括端值或不包括端值的，并且可以进行任意地组合，即任何下限可以与任何上限组合形成一个范围。例如，如果针对特定参数列出了60-120和80-110的范围，理解为60-110和80-120的范围也是预料到的。此外，如果列出的最小范围值1和2，和如果列出了最大范围值3，4和5，则下面的范围可全部预料到：1-3、1-4、1-5、2-3、2-4和2-5。在本申请中，除非有其他说明，数值范围“a-b”表示a到b之间的任意实数组合的缩略表示，其中a和b都是实数。例如数值范围“0-5”表示本文中已经全部列出了“0-5”之间的全部实数，“0-5”只是这些数值组合的缩略表示。另外，当表述某个参数为≥2的整数，则相当于公开了该参数为例如整数2、3、4、5、6、7、8、9、10、11、12等。
如果没有特别的说明，本申请的所有实施方式以及可选实施方式可以相互组合形成新的技术方案。
如果没有特别的说明，本申请的所有技术特征以及可选技术特征可以相互组合形成新的技术方案。
如果没有特别的说明，本申请的所有步骤可以顺序进行，也可以随机进行，优选是顺序进行的。例如，方法包括步骤(a)和(b)，表示方法可包括顺序进行的步骤(a)和(b)，也可以包括顺序进行的步骤(b)和(a)。例如，提到方法还可包括步骤(c)，表示步骤(c)可以任意顺序加入到方法，例如，方法可以包括步骤(a)、(b)和(c)，也可包括步骤(a)、(c)和(b)，也可以包括步骤(c)、(a)和(b)等。
如果没有特别的说明，本申请所提到的“包括”和“包含”表示开放式，也可以是封闭式。例如，“包括”和“包含”表示还可以包括或包含 没有列出的其他组分，也可以仅包括或包含列出的组分。
如果没有特别的说明，在本申请中，术语“或”是包括性的。举例来说，短语“A或B”表示“A，B，或A和B两者”。更具体地，以下任一条件均满足条件“A或B”：A为真(或存在)并且B为假(或不存在)；A为假(或不存在)而B为真(或存在)；或A和B都为真(或存在)。
[二次电池]
二次电池又称为充电电池或蓄电池，是指在电池放电后可通过充电的方式使活性材料激活而继续使用的电池。
通常情况下，二次电池包括正极极片、负极极片、隔离膜及电解液。在电池充放电过程中，活性离子(例如锂离子)在正极极片和负极极片之间往返嵌入和脱出。隔离膜设置在正极极片和负极极片之间，主要起到防止正负极短路的作用，同时可以使活性离子通过。电解液在正极极片和负极极片之间，主要起到传导活性离子的作用。
[正极极片]
本申请第一个方面的实施方式提供一种正极极片，包括正极集流体和设置在正极集流体的至少一个表面上的正极膜层；正极膜层为单层结构或多层结构；当正极膜层为单层结构时，至少一个正极膜层同时包含化学式为Li aA xMn 1-yR yP 1-zC zO 4-nD n的第一正极活性材料和第二正极活性材料；和/或，当正极膜层为多层结构时，至少一个正极膜层的至少一层中同时包含化学式为Li aA xMn 1-yR yP 1-zC zO 4-nD n的第一正极活性材料和第二正极活性材料；其中，A包括选自Zn、Al、Na、K、Mg、Nb、Mo和W中的一种或多种元素；R包括选自Ti、V、Zr、Fe、Ni、Mg、Co、Ga、Sn、Sb、Nb和Ge中的一种或多种元素；C包括选自B、S、Si和N中的一种或多种元素；D包括选自S、F、Cl和Br中的一种或多种元素；a选自0.9至1.1的范围，x选自0.001至0.1的范围，y选自0.001至0.5的范围，z选自0.001至0.1的范围，n选自0.001至0.1的范围；第二正极活性材料选自 LiNi bCo cMn (1-b-c)O 2、LiNi bCo cAl (1-b-c)O 2和LiCoO 2中的一种或多种；其中，b独立地选自0.3-0.9(可选为0.33-0.8，例如0.5)，b与c之和独立地选自0.3-0.9(可选为0.66-0.9，例如0.7)。
需要说明的是：当正极极片包括两个正极膜层时，“正极膜层为单层结构或多层结构”指两个正极膜层各自独立地为单层结构或多层结构；“当正极膜层为单层结构时”指一个或两个正极膜层为单层结构时；“当正极膜层为多层结构时”指一个或两个正极膜层为多层结构时。
本申请的第一正极活性材料通过在化合物LiMnPO 4中进行元素掺杂而获得，其中，A、B、C和D分别为在化合物LiMnPO 4的Li位、Mn位、P位和O位掺杂的元素。不希望囿于理论，本申请发明人发现磷酸锰锂的性能提升与减小脱嵌锂过程中磷酸锰锂的晶格变化率和降低表面活性有关。减小晶格变化率可减小晶界处两相间的晶格常数差异，减小界面应力，增强Li +在界面处的传输能力，从而提升正极活性材料的倍率性能。而表面活性高容易导致界面副反应严重，加剧产气、电解液消耗和破坏界面，从而影响二次电池的循环等性能。本申请中，通过Li和Mn位掺杂减小了晶格变化率。Mn位掺杂还有效降低表面活性，从而抑制Mn溶出和正极活性材料与电解液的界面副反应。P位掺杂使Mn-O键长的变化速率更快，降低材料的小极化子迁移势垒，从而有利于电子电导率。O位掺杂对减小界面副反应有良好的作用。P位和O位的掺杂还对反位缺陷的Mn溶出及动力学性能产生影响。因此，掺杂减小了材料中反位缺陷浓度，提高材料的动力学性能和克容量，还可以改变颗粒的形貌，从而提升压实密度。本申请人意外地发现：通过在化合物LiMnPO 4的Li位、Mn位、P位和O位同时以特定量掺杂特定的元素，能够获得明显改善的倍率性能，同时显著减少了Mn与Mn位掺杂元素的溶出，获得了显著改善的循环性能和/或高温稳定性，并且材料的克容量和压实密度也可以得到提高；另外，本申请通过将第一正极活性材料和第二正极活性材料混合使用，两种材料的优势互补，提升了二次电池的能量密度，同时使二次电池兼具优良的倍率性能、动力学性能、循环性能、低温性能和安全性。第一正极活性材料的颗粒均匀包覆在第二正极活性材料表面， 使第二正极活性材料的晶格相对独立、骨架稳定，在二次电池充放电过程中不易坍塌，进一步提高了二次电池的循环性能；并且，第一正极活性材料形成的包覆层为外力撞击或剪切提供了弹性应变力，有效解决了第二正极活性材料的安全性问题。
在第一个方面的一些实施方式中，在正极集流体的两个表面上分别设置有正极膜层C和正极膜层D，正极膜层C为多层结构，正极膜层D为单层结构，正极膜层C中的至少一层同时包含第一正极活性材料和第二正极活性材料；可选地，正极膜层D包含第一正极活性材料和第二正极活性材料中的一种或两种；可选地，正极膜层C中的其余层包含第一正极活性材料或第二正极活性材料。
在第一个方面的一些实施方式中，在正极集流体的两个表面上分别设置有正极膜层C和正极膜层D，正极膜层C为多层结构，正极膜层D为单层结构，正极膜层D同时包含第一正极活性材料和第二正极活性材料；可选地，正极膜层C中的任一层包含第一正极活性材料或第二正极活性材料。
在第一个方面的一些实施方式中，在正极集流体的两个表面上分别设置有一个正极膜层，每个正极膜层都为多层结构，每个正极膜层中的至少一层同时包含第一正极活性材料和第二正极活性材料；可选地，正极膜层中的其余层包含第一正极活性材料或第二正极活性材料。
本申请第二个方面的实施方式提供一种正极极片，包括正极集流体和设置在正极集流体的至少一个表面上的正极膜层；至少一个正极膜层为多层结构，任一具有多层结构的正极膜层在不同层中分别包含化学式为Li aA xMn 1-yR yP 1-zC zO 4-nD n的第一正极活性材料和第二正极活性材料；其中，A包括选自Zn、Al、Na、K、Mg、Nb、Mo和W中的一种或多种元素；R包括选自Ti、V、Zr、Fe、Ni、Mg、Co、Ga、Sn、Sb、Nb和Ge中的一种或多种元素；C包括选自B、S、Si和N中的一种或多种元素；D包括选自S、F、Cl和Br中的一种或多种元素；a选自0.9至1.1的范围，x选自0.001至0.1的范围，y选自0.001至0.5的范围，z选自0.001至0.1的范围，n选自0.001至0.1的范围；第二正极活性材料选自LiNi bCo cMn (1-b-c)O 2、LiNi bCo cAl (1-b-c)O 2和 LiCoO 2中的一种或多种；其中，b独立地选自0.3-0.9(可选为0.33-0.8，例如0.5)，b与c之和独立地选自0.3-0.9(可选为0.66-0.9，例如0.7)；可选地，任一具有多层结构的正极膜层在相邻层中分别包含第一正极活性材料和第二正极活性材料。
在第二个方面的一些实施方式中，在正极集流体的两个表面上分别设置有一个正极膜层，每个正极膜层都为多层结构，每个正极膜层中的相邻两层分别包含第一正极活性材料和第二正极活性材料。
在第二个方面的一些实施方式中，在正极集流体的两个表面上分别设置有正极膜层E和正极膜层F，正极膜层E为多层结构，正极膜层F为单层结构，正极膜层E中的相邻两层分别包含第一正极活性材料和第二正极活性材料；可选地，正极膜层E中的其余层和正极膜层F包含第一正极活性材料或第二正极活性材料。
本申请第三个方面的实施方式提供一种正极极片，包括正极集流体和分别设置在正极集流体的两个表面上的正极膜层A和正极膜层B；正极膜层A和正极膜层B独立地为单层结构或多层结构；正极膜层A的至少一层中包含化学式为Li aA xMn 1-yR yP 1-zC zO 4-nD n的第一正极活性材料，同时，正极膜层B的至少一层中包含第二正极活性材料；其中，A包括选自Zn、Al、Na、K、Mg、Nb、Mo和W中的一种或多种元素；R包括选自Ti、V、Zr、Fe、Ni、Mg、Co、Ga、Sn、Sb、Nb和Ge中的一种或多种元素；C包括选自B、S、Si和N中的一种或多种元素；D包括选自S、F、Cl和Br中的一种或多种元素；a选自0.9至1.1的范围，x选自0.001至0.1的范围，y选自0.001至0.5的范围，z选自0.001至0.1的范围，n选自0.001至0.1的范围；第二正极活性材料选自LiNi bCo cMn (1-b-c)O 2、LiNi bCo cAl (1-b-c)O 2和LiCoO 2中的一种或多种；其中，b独立地选自0.3-0.9(可选为0.33-0.8，例如0.5)，b与c之和独立地选自0.3-0.9(可选为0.66-0.9，例如0.7)。
本申请第二个或第三个方面的实施方式中，第一正极活性材料具有明显改善的倍率性能，同时显著减少Mn与Mn位掺杂元素的溶出，获得显著改善的循环性能和/或高温稳定性，并且材料的克容量和压实密度也得到提高，界面副反应减少，具体原理同本申请第一个实施 方式中。虽然机理并不十分清楚，但是本申请通过将第一正极活性材料和第二正极活性材料组合使用，两种材料的优势互补，提升了二次电池的能量密度，同时使二次电池兼具优良的倍率性能、动力学性能、循环性能、低温性能和安全性。具体来说，可能是由于第一正极活性材料为外力撞击或剪切提供了弹性应变力，有效解决了第二正极活性材料的安全性问题。
除非另有说明，否则化学式Li aA xMn 1-yR yP 1-zC zO 4-nD n中，当A为两种以上元素时，上述对于x数值范围的限定不仅是对每种作为A的元素的化学计量数的限定，也是对各个作为A的元素的化学计量数之和的限定。例如当A为两种以上元素A1、A2……An时，A1、A2……An各自的化学计量数x1、x2……xn各自均需落入本申请对x限定的数值范围内，且x1、x2……xn之和也需落入该数值范围内。类似地，对于R、C和D为两种以上元素的情况，本申请中对R、C和D化学计量数的数值范围的限定也具有上述含义。
在第一个至第三个方面的一些实施方式中，第一正极活性材料Li aA xMn 1-yR yP 1-zC zO 4-nD n整个保持电中性。
在第一个至第三个方面的一些实施方式中，第一活性材料与第二活性材料的质量比为1:7-7:1，可选为1:4-4:1。以保证二次电池兼具优良的倍率性能、优良的循环性能和高温稳定性、较高的能量密度、优良的动力学性能和低温性能，减少界面副反应，提高二次电池的安全性。
在第一个至第三个方面的一些实施方式中，第一正极活性材料中，R选自Ti、V、Zr、Fe、Ni、Mg、Co、Ga、Sn、Sb、Nb和Ge中的至少两种元素。由此，能够更容易且准确地控制第一正极活性材料的组成。
在第一个至第三个方面的一些实施方式中，第一正极活性材料中，A为选自Mg和Nb中的任一种元素；和/或，R为选自Fe、Ti、V、Co和Mg中的至少两种元素，可选地为Fe与选自Ti、V、Co和Mg中的一种以上元素；和/或，C为S；和/或，D为F。通过在上述范围内对Li位掺杂元素进行选择，能够进一步减小脱锂过程中的晶格变 化率，从而进一步改善二次电池的倍率性能。通过在上述范围内对Mn位掺杂元素进行选择，能够进一步提高电子电导率并进一步减小晶格变化率，从而提升二次电池的倍率性能和克容量。通过在上述范围内对P位掺杂元素进行选择，能够进一步改善二次电池的倍率性能。通过在上述范围内对O位掺杂元素进行选择，能够进一步减轻界面的副反应，提升二次电池的高温性能。
在第一个至第三个方面的一些实施方式中，第一正极活性材料中，x选自0.001-0.005的范围。通过在该范围内对x值进行选择，能进一步提升第一正极活性材料的动力学性能。
在第一个至第三个方面的一些实施方式中，第一正极活性材料中，y选自0.01至0.5的范围，可选地选自0.25至0.5的范围。通过在该范围内对y值进行选择，能进一步提升第一正极活性材料的克容量和倍率性能。
在第一个至第三个方面的一些实施方式中，第一正极活性材料中，z选自0.001至0.005的范围。通过在该范围内对z值进行选择，能进一步提升二次电池的倍率性能。
在第一个至第三个方面的一些实施方式中，第一正极活性材料中，n选自0.001至0.005的范围。通过在该范围内对n值进行选择，能进一步提升二次电池的高温性能。
在第一个至第三个方面的一些实施方式中，第一正极活性材料中，(1-y)与y的比值选自1-4，可选为选自1.5-3，且a与x的比值选自9-1100，可选为选自190-998。在满足这一条件时，使二次电池的能量密度和循环性能进一步提升。
在第一个至第三个方面的一些实施方式中，第一正极活性材料的晶格变化率为8％以下，可选地为4％以下。通过降低晶格变化率，能够使得Li离子传输更容易，即Li离子在材料中的迁移能力更强，有利于改善二次电池的倍率性能。晶格变化率可通过本领域中已知的方法，例如X射线衍射图谱(XRD)测得。
在第一个至第三个方面的一些实施方式中，第一正极活性材料的Li/Mn反位缺陷浓度为2％以下，可选地为0.5％以下。所谓Li/Mn反 位缺陷，指的是LiMnPO 4晶格中，Li +与Mn 2+的位置发生互换。Li/Mn反位缺陷浓度指的是正极活性材料中与Mn 2+发生互换的Li +占Li +总量的百分比。通过降低Li/Mn反位缺陷浓度，有利于提高第一正极活性材料的克容量和倍率性能。Li/Mn反位缺陷浓度可通过本领域中已知的方法，例如XRD测得。
在第一个至第三个方面的一些实施方式中，第一正极活性材料的表面氧价态为-1.82以下，可选地为-1.89～-1.98。通过降低表面氧价态，能够减轻第一正极活性材料与电解液的界面副反应，从而改善二次电池的循环性能和高温稳定性。表面氧价态可通过本领域中已知的方法测量，例如通过电子能量损失谱(EELS)测量。
在第一个至第三个方面的一些实施方式中，第一正极活性材料在3T下的压实密度为2.0g/cm 3以上，可选地为2.2g/cm 3以上。压实密度越高，单位体积的第一正极活性材料的重量越大，因此提高压实密度有利于提高电芯的体积能量密度。压实密度可依据GB/T24533-2009测量。
在第一个至第三个方面的一些实施方式中，第一正极活性材料的表面还包覆有碳。由此，可以改善第一正极活性材料的导电性。
在第一个至第三个方面的一些实施方式中，LiNi bCo cMn (1-b-c)O 2中的b、(1-b-c)和c的比值为5:2:3或3:1:1或8:1:1；和/或，LiNi bCo cMn (1-b-c)O 2中的b、c和(1-b-c)的比值为5:2:3或3:1:1或8:1:1。由此能进一步提升二次电池的能量密度。
在第一个至第三个方面的一些实施方式中，第一正极活性材料和第二正极活性材料的质量之和占正极极片的质量的88％-98.7％。进一步保证二次电池具有优良的倍率性能、动力学性能、循环性能和低温性能，具有较高的能量密度。
在第一个至第三个方面的一些实施方式中，正极集流体具有在其自身厚度方向相对的两个表面，正极膜层设置在正极集流体相对的两个表面的其中任意一者或两者上。
在第一个至第三个方面的一些实施方式中，正极集流体可采用金属箔片或复合集流体。例如，作为金属箔片，可采用铝箔。复合集流 体可包括高分子材料基层和形成于高分子材料基层至少一个表面上的金属层。复合集流体可通过将金属材料(铝、铝合金、镍、镍合金、钛、钛合金、银及银合金等)形成在高分子材料基材(如聚丙烯(PP)、聚对苯二甲酸乙二醇酯(PET)、聚对苯二甲酸丁二醇酯(PBT)、聚苯乙烯(PS)、聚乙烯(PE)等的基材)上而形成。
在第一个至第三个方面的一些实施方式中，正极膜层还可包含本领域公知的用于二次电池的其它正极活性材料。作为示例，正极活性材料可包括以下材料中的至少一种：橄榄石结构的含锂磷酸盐、锂过渡金属氧化物及其各自的改性化合物。但本申请并不限定于这些材料，还可以使用其他可被用作二次电池正极活性材料的传统材料。这些正极活性材料可以仅单独使用一种，也可以将两种以上组合使用。其中，锂过渡金属氧化物的示例可包括但不限于锂镍氧化物(如LiNiO 2)、锂锰氧化物(如LiMnO 2、LiMn 2O 4)、锂镍钴氧化物、锂锰钴氧化物、锂镍锰氧化物及其改性化合物等中的至少一种。橄榄石结构的含锂磷酸盐的示例可包括但不限于磷酸铁锂(如LiFePO 4(也可以简称为LFP))、磷酸铁锂与碳的复合材料、磷酸锰锂(如LiMnPO 4)、磷酸锰锂与碳的复合材料、磷酸锰铁锂、磷酸锰铁锂与碳的复合材料中的至少一种。
在第一个至第三个方面的一些实施方式中，正极膜层还可选地包括粘结剂。作为示例，粘结剂可以包括聚偏氟乙烯(PVDF)、聚四氟乙烯(PTFE)、偏氟乙烯-四氟乙烯-丙烯三元共聚物、偏氟乙烯-六氟丙烯-四氟乙烯三元共聚物、四氟乙烯-六氟丙烯共聚物及含氟丙烯酸酯树脂中的至少一种。
在第一个至第三个方面的一些实施方式中，正极膜层还可选地包括导电剂。作为示例，导电剂可以包括超导碳、乙炔黑、炭黑、科琴黑、碳点、碳纳米管、石墨烯及碳纳米纤维中的至少一种。
[负极极片]
负极极片包括负极集流体以及设置在负极集流体至少一个表面上的负极膜层，负极膜层包括负极活性材料。
作为示例，负极集流体具有在其自身厚度方向相对的两个表面，负极膜层设置在负极集流体相对的两个表面中的任意一者或两者上。
在一些实施方式中，负极集流体可采用金属箔片或复合集流体。例如，作为金属箔片，可以采用铜箔。复合集流体可包括高分子材料基层和形成于高分子材料基材至少一个表面上的金属层。复合集流体可通过将金属材料(铜、铜合金、镍、镍合金、钛、钛合金、银及银合金等)形成在高分子材料基材(如聚丙烯(PP)、聚对苯二甲酸乙二醇酯(PET)、聚对苯二甲酸丁二醇酯(PBT)、聚苯乙烯(PS)、聚乙烯(PE)等的基材)上而形成。
在一些实施方式中，负极活性材料可采用本领域公知的用于二次电池的负极活性材料。作为示例，负极活性材料可包括以下材料中的至少一种：人造石墨、天然石墨、软炭、硬炭、硅基材料、锡基材料和钛酸锂等。硅基材料可选自单质硅、硅氧化合物、硅碳复合物、硅氮复合物以及硅合金中的至少一种。锡基材料可选自单质锡、锡氧化合物以及锡合金中的至少一种。但本申请并不限定于这些材料，还可以使用其他可被用作电池负极活性材料的传统材料。这些负极活性材料可以仅单独使用一种，也可以将两种以上组合使用。
在一些实施方式中，负极膜层还可选地包括粘结剂。作为示例，粘结剂可选自丁苯橡胶(SBR)、聚丙烯酸(PAA)、聚丙烯酸钠(PAAS)、聚丙烯酰胺(PAM)、聚乙烯醇(PVA)、海藻酸钠(SA)、聚甲基丙烯酸(PMAA)及羧甲基壳聚糖(CMCS)中的至少一种。
在一些实施方式中，负极膜层还可选地包括导电剂。作为示例，导电剂可选自超导碳、乙炔黑、炭黑、科琴黑、碳点、碳纳米管、石墨烯及碳纳米纤维中的至少一种。
在一些实施方式中，负极膜层还可选地包括其他助剂，例如增稠剂(如羧甲基纤维素钠(CMC-Na))等。
在一些实施方式中，可以通过以下方式制备负极极片：将上述用于制备负极极片的组分，例如负极活性材料、导电剂、粘结剂和任意其他组分分散于溶剂(例如去离子水)中，形成负极浆料；将负极浆料涂覆在负极集流体上，经烘干、冷压等工序后，即可得到负极极片。
[电解质]
电解质在正极极片和负极极片之间起到传导离子的作用。本申请对电解质的种类没有具体的限制，可根据需求进行选择。例如，电解质可以是液态的、凝胶态的或全固态的。
在一些实施方式中，电解质为液态的，且包括电解质盐和溶剂。
在一些实施方式中，电解质盐可选自六氟磷酸锂、四氟硼酸锂、高氯酸锂、六氟砷酸锂、双氟磺酰亚胺锂、双三氟甲磺酰亚胺锂、三氟甲磺酸锂、二氟磷酸锂、二氟草酸硼酸锂、二草酸硼酸锂、二氟二草酸磷酸锂及四氟草酸磷酸锂中的至少一种。
在一些实施方式中，溶剂可选自碳酸亚乙酯、碳酸亚丙酯、碳酸甲乙酯、碳酸二乙酯、碳酸二甲酯、碳酸二丙酯、碳酸甲丙酯、碳酸乙丙酯、碳酸亚丁酯、氟代碳酸亚乙酯、甲酸甲酯、乙酸甲酯、乙酸乙酯、乙酸丙酯、丙酸甲酯、丙酸乙酯、丙酸丙酯、丁酸甲酯、丁酸乙酯、1,4-丁内酯、环丁砜、二甲砜、甲乙砜及二乙砜中的至少一种。
在一些实施方式中，电解液还可选地包括添加剂。作为示例，添加剂可以包括负极成膜添加剂、正极成膜添加剂，还可以包括能够改善电池某些性能的添加剂，例如改善电池过充性能的添加剂、改善电池高温或低温性能的添加剂等。
[隔离膜]
在一些实施方式中，二次电池中还包括隔离膜。本申请对隔离膜的种类没有特别的限制，可以选用任意公知的具有良好的化学稳定性和机械稳定性的多孔结构隔离膜。
在一些实施方式中，隔离膜的材质可选自玻璃纤维、无纺布、聚乙烯、聚丙烯及聚偏二氟乙烯中的至少一种。隔离膜可以是单层薄膜，也可以是多层复合薄膜，没有特别限制。在隔离膜为多层复合薄膜时，各层的材料可以相同或不同，没有特别限制。
在一些实施方式中，上述的正极极片、负极极片和隔离膜可通过卷绕工艺或叠片工艺制成电极组件。
在一些实施方式中，二次电池可包括外包装。该外包装可用于封装上述电极组件及电解质。
在一些实施方式中，二次电池的外包装可以是硬壳，例如硬塑料壳、铝壳、钢壳等。二次电池的外包装也可以是软包，例如袋式软包。软包的材质可以是塑料，作为塑料，可列举出聚丙烯、聚对苯二甲酸丁二醇酯以及聚丁二酸丁二醇酯等。
本申请对二次电池的形状没有特别的限制，其可以是圆柱形、方形或其他任意的形状。例如，图1是作为一个示例的方形结构的二次电池5。
在一些实施方式中，参照图2，外包装可包括壳体51和盖板53。其中，壳体51可包括底板和连接于底板上的侧板，底板和侧板围合形成容纳腔。壳体51具有与容纳腔连通的开口，盖板53能够盖设于开口，以封闭容纳腔。正极极片、负极极片和隔离膜可经卷绕工艺或叠片工艺形成电极组件52。电极组件52封装于容纳腔内。电解液浸润于电极组件52中。二次电池5所含电极组件52的数量可以为一个或多个，本领域技术人员可根据具体实际需求进行选择。
在一些实施方式中，二次电池可以组装成电池模块，电池模块所含二次电池的数量可以为一个或多个，具体数量本领域技术人员可根据电池模块的应用和容量进行选择。
图3是作为一个示例的电池模块4。参照图3，在电池模块4中，多个二次电池5可以是沿电池模块4的长度方向依次排列设置。当然，也可以按照其他任意的方式进行排布。进一步可以通过紧固件将该多个二次电池5进行固定。
可选地，电池模块4还可以包括具有容纳空间的外壳，多个二次电池5容纳于该容纳空间。
在一些实施方式中，上述电池模块还可以组装成电池包，电池包所含电池模块的数量可以为一个或多个，具体数量本领域技术人员可根据电池包的应用和容量进行选择。
图4和图5是作为一个示例的电池包1。参照图4和图5，在电池包1中可以包括电池箱和设置于电池箱中的多个电池模块4。电池 箱包括上箱体2和下箱体3，上箱体2能够盖设于下箱体3，并形成用于容纳电池模块4的封闭空间。多个电池模块4可以按照任意的方式排布于电池箱中。
另外，本申请还提供一种用电装置，用电装置包括本申请提供的二次电池、电池模块、或电池包中的至少一种。二次电池、电池模块、或电池包可以用作用电装置的电源，也可以用作用电装置的能量存储单元。用电装置可以包括移动设备(例如手机、笔记本电脑等)、电动车辆(例如纯电动车、混合动力电动车、插电式混合动力电动车、电动自行车、电动踏板车、电动高尔夫球车、电动卡车等)、电气列车、船舶及卫星、储能系统等，但不限于此。
作为用电装置，可以根据其使用需求来选择二次电池、电池模块或电池包。
图6是作为一个示例的用电装置。该用电装置为纯电动车、混合动力电动车、或插电式混合动力电动车等。为了满足该用电装置对二次电池的高功率和高能量密度的需求，可以采用电池包或电池模块。
[实施例]
以下，说明本申请的实施例。下面描述的实施例是示例性的，仅用于解释本申请，而不能理解为对本申请的限制。实施例中未注明具体技术或条件的，按照本领域内的文献所描述的技术或条件或者按照产品说明书进行。所用试剂或仪器未注明生产厂商者，均为可以通过市购获得的常规产品。
正极活性材料及其浆料的制备
制备例1
制备掺杂的草酸锰：将1.3mol MnSO 4·H 2O与0.7mol FeSO 4·H 2O在混料机中充分混合6小时；将混合物转移至反应釜中，加入10L去离子水和2mol二水合草酸，加热至80℃，之后以600rpm转速搅拌6小时，反应终止(无气泡产生)，得到Fe掺杂的草酸锰的悬浮液；过滤悬浮液，滤饼在120℃下烘干，研磨，得到粒径Dv 50为100nm 左右的Fe掺杂的草酸锰颗粒；
制备掺杂的磷酸锰锂：取1mol Fe掺杂的草酸锰颗粒、0.497mol碳酸锂、0.001mol的Mo(SO 4) 3、含有0.999mol磷酸的浓度85％的磷酸水溶液、0.001mol的H 4SiO 4、0.0005mol的NH 4HF 2和0.005mol蔗糖加入到20L去离子水中，将混合物转入砂磨机中充分研磨搅拌10小时，得到浆料；将浆料转移到喷雾干燥设备中进行喷雾干燥造粒，设定干燥温度为250℃，干燥4小时，得到颗粒；在氮气(90％v/v)+氢气(10％v/v)保护气氛中，将颗粒在700℃下烧结10小时，得到正极活性材料1，碳包覆的Li 0.994Mo 0.001Mn 0.65Fe 0.35P 0.999Si 0.001O 3.999F 0.001。正极活性材料可用电感耦合等离子体发射光谱(ICP)进行元素含量的检测。
制备例2
除了将高纯Li 2CO 3的量改变为0.4885mol，将Mo(SO 4) 3换成等摩尔的MgSO 4，将FeSO 4﹒H 2O的量改变为0.68mol，在制备掺杂的草酸锰时还加入0.02mol的Ti(SO 4) 2，并将H 4SiO 4换成等摩尔的HNO 3之外，其他与制备例1相同。
制备例3
除了在将高纯Li 2CO 3的量改变为0.496mol，将Mo(SO 4) 3换成等摩尔的W(SO 4) 3，将H 4SiO 4换成等摩尔的H 2SO 4之外，其他与制备例1相同。
制备例4
除了将高纯Li 2CO 3的量改变为0.4985mol，将0.001mol的Mo(SO 4) 3换成0.0005mol的Al 2(SO 4) 3和NH 4HF 2换成等摩尔的NH 4HCl 2之外，其他与制备例1相同。
制备例5
除了将0.7mol的FeSO 4﹒H 2O改为0.69mol，在制备掺杂的草酸 锰时还加入0.01molVCl 2，将Li 2CO 3的量改变为0.4965mol，将0.001mol的Mo(SO 4) 3换成0.0005mol的Nb 2(SO 4) 5和H 4SiO 4换成等摩尔的H 2SO 4之外，其他与制备例1相同。
制备例6
除了将FeSO 4﹒H 2O的量改为0.68mol，在制备掺杂的草酸锰时还加入0.01mol的VCl 2和0.01mol的MgSO 4，将Li 2CO 3的量改变为0.4965mol，将0.001mol的Mo(SO 4) 3换成0.0005mol的Nb 2(SO 4) 5和H 4SiO 4换成等摩尔的H 2SO 4之外，其他与制备例1相同。
制备例7
除了将MgSO 4换成等摩尔的CoSO 4之外，其他与制备例6相同。
制备例8
除了将MgSO 4换成等摩尔的NiSO 4之外，其他与制备例6相同。
制备例9
除了将FeSO 4﹒H 2O的量改为0.698mol，在制备掺杂的草酸锰时还加入0.002mol的Ti(SO 4) 2，将Li 2CO 3的量改变为0.4955mol，将0.001mol的Mo(SO 4) 3换成0.0005mol的Nb 2(SO 4) 5，H 4SiO 4换成等摩尔的H 2SO 4，NH 4HF 2换成等摩尔的NH 4HCl 2之外，其他与制备例1相同。
制备例10
除了将FeSO 4﹒H 2O的量改为0.68mol，在制备掺杂的草酸锰时还加入0.01mol的VCl 2和0.01mol的MgSO 4，将Li 2CO 3的量改变为0.4975mol，将0.001mol的Mo(SO 4) 3换成0.0005mol的Nb 2(SO 4) 5和NH 4HF 2换成等摩尔的NH 4HBr 2之外，其他与制备例1相同。
制备例11
除了将FeSO 4﹒H 2O的量改为0.69mol，在制备掺杂的草酸锰时还加入0.01mol的VCl 2，将Li 2CO 3的量改变为0.499mol，将Mo(SO 4) 3换成等摩尔的MgSO 4和NH 4HF 2换成等摩尔的NH 4HBr 2之外，其他与制备例1相同。
制备例12
除了将MnSO 4﹒H 2O的量改为1.36mol，将FeSO 4﹒H 2O的量改为0.6mol，在制备掺杂的草酸锰时还加入0.04mol的VCl 2，将Li 2CO 3的量改变为0.4985mol，将Mo(SO 4) 3换成等摩尔的MgSO 4和H 4SiO 4换成等摩尔的HNO 3之外，其他与制备例1相同。
制备例13
除了将MnSO 4﹒H 2O的量改为1.16mol，FeSO 4﹒H 2O的量改为0.8mol之外，其他与制备例12相同。
制备例14
除了将MnSO 4﹒H 2O的量改为1.3mol，VCl 2的量改为0.1mol之外，其他与制备例12相同。
制备例15
除了将MnSO 4﹒H 2O的量改为1.2mol，在制备掺杂的草酸锰时还加入0.1mol的VCl 2，将Li 2CO 3的量改变为0.494mol，将0.001mol的Mo(SO 4) 3换成0.005mol的MgSO 4和H 4SiO 4换成等摩尔的H 2SO 4之外，其他与制备例1相同。
制备例16
除了将MnSO 4﹒H 2O的量改为1.2mol，在制备掺杂的草酸锰时还加入0.1mol的VCl 2，将Li 2CO 3的量改变为0.467mol，将0.001mol的Mo(SO 4) 3换成0.005mol的MgSO 4，0.001mol的H 4SiO 4换成0.005mol的H 2SO 4和1.175mol浓度为85％的磷酸换成1.171mol浓度 为85％的磷酸之外，其他与制备例1相同。
制备例17
除了将MnSO 4﹒H 2O的量改为1.2mol，在制备掺杂的草酸锰时还加入0.1mol的VCl 2，将Li 2CO 3的量改变为0.492mol，将0.001mol的Mo(SO 4) 3换成0.005mol的MgSO 4，H 4SiO 4换成等摩尔的H 2SO 4和0.0005mol的NH 4HF 2改成0.0025mol之外，其他与制备例1相同。
制备例18
除了将FeSO 4﹒H 2O的量改为0.5mol，在制备掺杂的草酸锰时还加入0.1mol的VCl 2和0.1mol的CoSO 4，将Li 2CO 3的量改变为0.492mol，将0.001mol的Mo(SO 4) 3换成0.005mol的MgSO 4，H 4SiO 4换成等摩尔的H 2SO 4和0.0005mol的NH 4HF 2改成0.0025mol之外，其他与制备例1相同。
制备例19
除了将FeSO 4﹒H 2O的量改为0.4mol，将0.1mol的CoSO 4改为0.2mol之外，其他与制备例18相同。
制备例20
除了将MnSO 4﹒H 2O的量改为1.5mol，FeSO 4﹒H 2O的量改为0.1mol，CoSO 4的量改为0.3mol之外，其他与制备例18相同。
制备例21
除了将0.1mol的CoSO 4换成0.1mol的NiSO 4之外，其他与制备例18相同。
制备例22
除了将MnSO 4﹒H 2O的量改为1.5mol，FeSO 4﹒H 2O的量改为0.2mol，将0.1mol的CoSO 4换成0.2mol的NiSO 4之外，其他与制备 例18相同。
制备例23
除了将MnSO 4﹒H 2O的量改为1.4mol，FeSO 4﹒H 2O的量改为0.3mol，CoSO 4的量改为0.2mol之外，其他与制备例18相同。
制备例24
除了将1.3mol的MnSO 4﹒H 2O改为1.2mol，0.7mol的FeSO 4﹒H 2O改为0.5mol，在制备掺杂的草酸锰时还加入0.1mol的VCl 2和0.2mol的CoSO 4，将Li 2CO 3的量改变为0.497mol，将0.001mol的Mo(SO 4) 3换成0.005mol的MgSO 4，H 4SiO 4换成等摩尔的H 2SO 4和0.0005mol的NH 4HF 2改成0.0025mol之外，其他与制备例1相同。
制备例25
除了将MnSO 4﹒H 2O的量改为1.0mol，FeSO 4﹒H 2O的量改为0.7mol，CoSO 4的量改为0.2mol之外，其他与制备例18相同。
制备例26
除了将MnSO 4﹒H 2O的量改为1.4mol，FeSO 4﹒H 2O的量改为0.3mol，在制备掺杂的草酸锰时还加入0.1mol的VCl 2和0.2mol的CoSO 4，将Li 2CO 3的量改变为0.4825mol，将0.001mol的Mo(SO 4) 3换成0.005mol的MgSO 4，H 4SiO 4的量改成0.1mol，磷酸的量改成0.9mol和NH 4HF 2的量改成0.04mol之外，其他与制备例1相同。
制备例27
除了将MnSO 4﹒H 2O的量改为1.4mol，FeSO 4﹒H 2O的量改为0.3mol，在制备掺杂的草酸锰时还加入0.1mol的VCl 2和0.2mol的CoSO 4，将Li 2CO 3的量改变为0.485mol，将0.001mol的Mo(SO 4) 3换成0.005mol的MgSO 4，H 4SiO 4的量改成0.08mol，磷酸的量改成0.92mol和NH 4HF 2的量改成0.05mol之外，其他与制备例1相同。
制备例28-41
按照与制备例1相同的方式制备正极活性材料，但改变制备掺杂的草酸锰时的搅拌转速、温度、在砂磨机中研磨搅拌的时间、烧结温度和烧结时间，具体如下表1所示。
表1制备例28-41中制备掺杂的草酸锰时的搅拌转速、温度、在砂磨机中研磨搅拌的时间、烧结温度和烧结时间
Figure PCTCN2022079295-appb-000001
制备例42-54
按照与制备例1相同的方式制备正极活性材料，但改变锂源、锰源、磷源和掺杂元素A、B、C、D的源，具体如下表2所示。制得的正极活性材料组成与实施例1相同，即，均为Li 0.994Mo 0.001Mn 0.65Fe 0.35P 0.999Si 0.001O 3.999F 0.001。
表2制备例42-54中锂源、锰源、磷源和掺杂元素A、B、C、D的源
Figure PCTCN2022079295-appb-000002
制备例55
镍钴锰酸锂LiNi 0.5Co 0.2Mn 0.3O 2作为正极活性材料。
制备例56
将制备例1和制备例55的正极活性材料按照质量比1:1混合作为正极活性材料。
制备例57
镍钴锰酸锂LiNi 0.33Co 0.33Mn 0.34O 2作为正极活性材料。
制备例58
镍钴锰酸锂LiNi 0.8Co 0.1Mn 0.1O 2作为正极活性材料。
制备例59
镍钴铝酸锂LiNi 0.33Co 0.33Al 0.34O 2作为正极活性材料。
制备例60
镍钴铝酸锂LiNi 0.5Co 0.2Al 0.3O 2作为正极活性材料。
制备例61
镍钴铝酸锂LiNi 0.8Co 0.1Al 0.1O 2作为正极活性材料。
制备例62
钴酸锂LiCoO 2作为正极活性材料。
制备例63
将制备例1和制备例57的正极活性材料按照质量比1:1混合作为正极活性材料。
制备例64
将制备例1和制备例58的正极活性材料按照质量比1:1混合作为正极活性材料。
制备例65
将制备例1和制备例59的正极活性材料按照质量比1:1混合作为正极活性材料。
制备例66
将制备例1和制备例60的正极活性材料按照质量比1:1混合作为正极活性材料。
制备例67
将制备例1和制备例61的正极活性材料按照质量比1:1混合作为正极活性材料。
制备例68
将制备例1和制备例62的正极活性材料按照质量比1:1混合作为正极活性材料。
对比例1
制备草酸锰：将1mol的MnSO 4﹒H 2O加至反应釜中，并加入10L去离子水和1mol二水合草酸(以草酸计)。将反应釜加热至80℃，以600rpm的转速搅拌6小时,反应终止(无气泡产生)，得到草酸锰悬浮液。然后过滤悬浮液，将滤饼在120℃下烘干，之后进行研磨，得到中值粒径Dv 50为50-200nm的草酸锰颗粒。
制备磷酸锰锂：取1mol上述草酸锰颗粒、0.5mol碳酸锂、含有1mol磷酸的浓度为85％的磷酸水溶液和0.005mol蔗糖加入到20L去离子水中。将混合物转入砂磨机中充分研磨搅拌10小时，得到浆料。将浆料转移到喷雾干燥设备中进行喷雾干燥造粒，设定干燥温度为250℃，干燥4小时，得到颗粒。在氮气(90体积％)+氢气(10体积％)保护气氛中，将上述粉料在700℃下烧结10小时，得到碳包覆的LiMnPO 4。
对比例2
除了在对比例1中，将1mol的MnSO 4﹒H 2O换成0.85mol的MnSO 4﹒H 2O和0.15mol的FeSO 4﹒H 2O，并加入到混料机中充分混合6小时之后再加入反应釜之外，其它与对比例1相同。
对比例3
除了将MnSO 4﹒H 2O的量改为1.9mol，0.7mol的FeSO 4﹒H 2O 换成0.1mol的ZnSO 4，将Li 2CO 3的量改变为0.495mol，将0.001mol的Mo(SO 4) 3换成0.005mol的MgSO 4，将磷酸的量改成1mol，不加入H 4SiO 4和NH 4HF 2之外，其他与制备例1相同。
对比例4
除了将MnSO 4﹒H 2O的量改为1.2mol，FeSO 4﹒H 2O的量改为0.8mol，将Li 2CO 3的量改变为0.45mol，将0.001mol的Mo(SO 4) 3换成0.005mol的Nb 2(SO 4) 5，将0.999mol的磷酸改成1mol，0.0005mol的NH 4HF 2改成0.025mol，不加入H 4SiO 4之外，其他与制备例1相同。
对比例5
除了将MnSO 4﹒H 2O的量改为1.4mol，FeSO 4﹒H 2O的量改为0.6mol，将Li 2CO 3的量改变为0.38mol，将0.001mol的Mo(SO 4) 3换成0.12mol的MgSO 4之外，其他与制备例1相同。
对比例6
除了将MnSO 4﹒H 2O的量改为0.8mol，0.7mol的FeSO 4﹒H 2O换成1.2mol的ZnSO 4，将Li 2CO 3的量改变为0.499mol，将0.001mol的Mo(SO 4) 3换成0.001mol的MgSO 4之外，其他与制备例1相同。
对比例7
除了将MnSO 4﹒H 2O的量改为1.4mol，FeSO 4﹒H 2O的量改为0.6mol，将Li 2CO 3的量改变为0.534mol，将0.001mol的Mo(SO 4) 3换成0.001mol的MgSO 4，将磷酸的量改成0.88mol，H 4SiO 4的量改成0.12mol，NH 4HF 2的量改成0.025mol之外，其他与制备例1相同。
对比例8
除了将MnSO 4﹒H 2O的量改为1.2mol，FeSO 4﹒H 2O的量改为0.8mol，将Li 2CO 3的量改变为0.474mol，将0.001mol的Mo(SO 4) 3换成0.001mol的MgSO 4，将磷酸的量改成0.93mol，H 4SiO 4的量改成 0.07mol，NH 4HF 2的量改成0.06mol之外，其他与制备例1相同。
将正极活性材料、粘结剂PVDF和导电剂超导炭黑(Super-P)按照97％:1.5％:1.5％的质量比混合，然后分散于N-甲基吡咯烷酮溶剂中，得到固含量为60％w/w的正极活性材料的浆料。
正极极片的制备
实施例1
将制备例1正极活性材料的浆料以0.019g/cm 2的涂布量均匀涂在集流体铝箔的两面，在100～120℃的高温下真空干燥14h，辊压机压实，得到正极极片P1。
实施例2
将制备例55正极活性材料的浆料以0.019g/cm 2的涂布量均匀涂在集流体铝箔的两面，在100～120℃的高温下真空干燥14h，辊压机压实，得到正极极片P2。
实施例3
将制备例1正极活性材料的浆料以0.019g/cm 2的涂布量均匀涂布在铝箔的一面上，将制备例55正极活性材料的浆料以0.019g/cm 2的涂布量均匀涂布在铝箔的另一面上，在100～120℃的高温下真空干燥14h，辊压机压实，得到正极极片P3。
实施例4
将制备例56正极活性材料的浆料以0.019g/cm 2的涂布量均匀涂在集流体铝箔的两面，其他与实施例3相同，得到正极极片P4。
实施例5
将制备例1正极活性材料的浆料以0.019g/cm 2的涂布量均匀涂布在铝箔的一面上，将制备例56正极活性材料的浆料以0.019g/cm 2的 涂布量均匀涂布在铝箔的另一面上，其他与实施例3相同，得到正极极片P5。
实施例6
将制备例55正极活性材料的浆料以0.019g/cm 2的涂布量均匀涂布在铝箔的一面上，将制备例56正极活性材料以0.019g/cm 2的涂布量的浆料均匀涂布在铝箔的另一面上，其他与实施例3相同，得到正极极片P6。
实施例7
在铝箔的两面均依次涂布制备例1正极活性材料的浆料和制备例55正极活性材料的浆料，每层浆料的涂布量均为0.010g/cm 2，然后，在100～120℃高温真空干燥14h，辊压机压实，得到正极极片P7。
实施例8
在铝箔的两面均依次涂布制备例55正极活性材料的浆料和制备例1正极活性材料的浆料，每层浆料的涂布量均为0.010g/cm 2，其他与实施例7相同，得到正极极片P8。
实施例9
在铝箔的两面均依次涂布制备例1正极活性材料的浆料和制备例56正极活性材料的浆料，每层浆料的涂布量均为0.010g/cm 2，其他与实施例7相同，得到正极极片P9。
实施例10
在铝箔的两面均依次涂布制备例56正极活性材料的浆料和制备例1正极活性材料的浆料，每层浆料的涂布量均为0.010g/cm 2，其他与实施例7相同，得到正极极片P10。
实施例11
在铝箔的两面均依次涂布制备例55正极活性材料的浆料和制备例56正极活性材料的浆料，每层浆料的涂布量均为0.010g/cm 2，其他与实施例7相同，得到正极极片P11。
实施例12
在铝箔的两面均依次涂布制备例56正极活性材料的浆料和制备例55正极活性材料的浆料，每层浆料的涂布量均为0.010g/cm 2，其他与实施例7相同，得到正极极片P12。
实施例13
在铝箔的A面均依次涂布制备例1正极活性材料的浆料和制备例55正极活性材料的浆料，每层浆料的涂布量均为0.010g/cm 2，在铝箔的B面均匀涂布制备例1正极活性材料的浆料，浆料的涂布量为0.020g/cm 2，然后，在100～120℃高温真空干燥14h，辊压机压实，得到正极极片P13。
实施例14
在铝箔的A面均依次涂布制备例1正极活性材料的浆料和制备例55正极活性材料的浆料，每层浆料的涂布量均为0.010g/cm 2，在铝箔的B面均匀涂布制备例55正极活性材料的浆料，浆料的涂布量为0.020g/cm 2，其他与实施例13相同，得到正极极片P14。
实施例15
在铝箔的A面均依次涂布制备例1正极活性材料的浆料和制备例55正极活性材料的浆料，每层浆料的涂布量均为0.010g/cm 2，在铝箔的B面均匀涂布制备例56正极活性材料的浆料，浆料的涂布量为0.020g/cm 2，其他与实施例13相同，得到正极极片P15。
实施例16
在铝箔的A面均依次涂布制备例55正极活性材料的浆料和制备例1正极活性材料的浆料，每层浆料的涂布量均为0.010g/cm 2，在铝箔的B面均匀涂布制备例1正极活性材料的浆料，浆料的涂布量为0.020g/cm 2，其他与实施例13相同，得到正极极片P16。
实施例17
在铝箔的A面均依次涂布制备例55正极活性材料的浆料和制备例1正极活性材料的浆料，每层浆料的涂布量均为0.010g/cm 2，在铝箔的B面均匀涂布制备例55正极活性材料的浆料，浆料的涂布量为0.020g/cm 2，其他与实施例13相同，得到正极极片P17。
实施例18
在铝箔的A面均依次涂布制备例55正极活性材料的浆料和制备例1正极活性材料的浆料，每层浆料的涂布量均为0.010g/cm 2，在铝箔的B面均匀涂布制备例56正极活性材料的浆料，浆料的涂布量为0.020g/cm 2，其他与实施例13相同，得到正极极片P18。
实施例19
在铝箔的A面均依次涂布制备例1正极活性材料的浆料和制备例56正极活性材料的浆料，每层浆料的涂布量均为0.010g/cm 2，在铝箔的B面均匀涂布制备例1正极活性材料的浆料，浆料的涂布量为0.020g/cm 2，其他与实施例13相同，得到正极极片P19。
实施例20
在铝箔的A面均依次涂布制备例1正极活性材料的浆料和制备例56正极活性材料的浆料，每层浆料的涂布量均为0.010g/cm 2，在铝箔的B面均匀涂布制备例55正极活性材料的浆料，浆料的涂布量为0.020g/cm 2，其他与实施例13相同，得到正极极片P20。
实施例21
在铝箔的A面均依次涂布制备例1正极活性材料的浆料和制备例56正极活性材料的浆料，每层浆料的涂布量均为0.010g/cm 2，在铝箔的B面均匀涂布制备例56正极活性材料的浆料，浆料的涂布量为0.020g/cm 2，其他与实施例13相同，得到正极极片P21。
实施例22
在铝箔的A面均依次涂布制备例56正极活性材料的浆料和制备例1正极活性材料的浆料，每层浆料的涂布量均为0.010g/cm 2，在铝箔的B面均匀涂布制备例1正极活性材料的浆料，浆料的涂布量为0.020g/cm 2，其他与实施例13相同，得到正极极片P22。
实施例23
在铝箔的A面均依次涂布制备例56正极活性材料的浆料和制备例1正极活性材料的浆料，每层浆料的涂布量均为0.010g/cm 2，在铝箔的B面均匀涂布制备例55正极活性材料的浆料，浆料的涂布量为0.020g/cm 2，其他与实施例13相同，得到正极极片P23。
实施例24
在铝箔的A面均依次涂布制备例56正极活性材料的浆料和制备例1正极活性材料的浆料，每层浆料的涂布量均为0.010g/cm 2，在铝箔的B面均匀涂布制备例56正极活性材料的浆料，浆料的涂布量为0.020g/cm 2，其他与实施例13相同，得到正极极片P24。
实施例25
在铝箔的A面均依次涂布制备例55正极活性材料的浆料和制备例56正极活性材料的浆料，每层浆料的涂布量均为0.010g/cm 2，在铝箔的B面均匀涂布制备例1正极活性材料的浆料，浆料的涂布量为0.020g/cm 2，其他与实施例13相同，得到正极极片P25。
实施例26
在铝箔的A面均依次涂布制备例55正极活性材料的浆料和制备例56正极活性材料的浆料，每层浆料的涂布量均为0.010g/cm 2，在铝箔的B面均匀涂布制备例55正极活性材料的浆料，浆料的涂布量为0.020g/cm 2，其他与实施例13相同，得到正极极片P26。
实施例27
在铝箔的A面均依次涂布制备例55正极活性材料的浆料和制备例56正极活性材料的浆料，每层浆料的涂布量均为0.010g/cm 2，在铝箔的B面均匀涂布制备例56正极活性材料的浆料，浆料的涂布量为0.020g/cm 2，其他与实施例13相同，得到正极极片P27。
实施例28
在铝箔的A面均依次涂布制备例56正极活性材料的浆料和制备例55正极活性材料的浆料，每层浆料的涂布量均为0.010g/cm 2，在铝箔的B面均匀涂布制备例1正极活性材料的浆料，浆料的涂布量为0.020g/cm 2，其他与实施例13相同，得到正极极片P28。
实施例29
在铝箔的A面均依次涂布制备例56正极活性材料的浆料和制备例55正极活性材料的浆料，每层浆料的涂布量均为0.010g/cm 2，在铝箔的B面均匀涂布制备例55正极活性材料的浆料，浆料的涂布量为0.020g/cm 2，其他与实施例13相同，得到正极极片P29。
实施例30
在铝箔的A面均依次涂布制备例56正极活性材料的浆料和制备例55正极活性材料的浆料，每层浆料的涂布量均为0.010g/cm 2，在铝箔的B面均匀涂布制备例56正极活性材料的浆料，浆料的涂布量为0.020g/cm 2，其他与实施例13相同，得到正极极片P30。
实施例31
将制备例57正极活性材料的浆料以0.019g/cm 2的涂布量均匀涂在集流体铝箔的两面，在100～120℃的高温下真空干燥14h，辊压机压实，得到正极极片P31。
实施例32
将制备例58正极活性材料的浆料以0.019g/cm 2的涂布量均匀涂在集流体铝箔的两面，在100～120℃的高温下真空干燥14h，辊压机压实，得到正极极片P32。
实施例33
将制备例59正极活性材料的浆料以0.019g/cm 2的涂布量均匀涂在集流体铝箔的两面，在100～120℃的高温下真空干燥14h，辊压机压实，得到正极极片P33。
实施例34
将制备例60正极活性材料的浆料以0.019g/cm 2的涂布量均匀涂在集流体铝箔的两面，在100～120℃的高温下真空干燥14h，辊压机压实，得到正极极片P34。
实施例35
将制备例61正极活性材料的浆料以0.019g/cm 2的涂布量均匀涂在集流体铝箔的两面，在100～120℃的高温下真空干燥14h，辊压机压实，得到正极极片P35。
实施例36
将制备例62正极活性材料的浆料以0.019g/cm 2的涂布量均匀涂在集流体铝箔的两面，在100～120℃的高温下真空干燥14h，辊压机压实，得到正极极片P36。
实施例37
将制备例63正极活性材料的浆料以0.019g/cm 2的涂布量均匀涂在集流体铝箔的两面，在100～120℃的高温下真空干燥14h，辊压机压实，得到正极极片P37。
实施例38
将制备例64正极活性材料的浆料以0.019g/cm 2的涂布量均匀涂在集流体铝箔的两面，其他与实施例37相同，得到正极极片P38。
实施例39
将制备例65正极活性材料的浆料以0.019g/cm 2的涂布量均匀涂在集流体铝箔的两面，其他与实施例37相同，得到正极极片P39。
实施例40
将制备例66正极活性材料的浆料以0.019g/cm 2的涂布量均匀涂在集流体铝箔的两面，其他与实施例37相同，得到正极极片P40。
实施例41
将制备例67正极活性材料的浆料以0.019g/cm 2的涂布量均匀涂在集流体铝箔的两面，其他与实施例37相同，得到正极极片P41。
实施例42
将制备例68正极活性材料的浆料以0.019g/cm 2的涂布量均匀涂在集流体铝箔的两面，其他与实施例37相同，得到正极极片P42。
以上各正极极片的参数见表3。
表3正极极片参数
Figure PCTCN2022079295-appb-000003
Figure PCTCN2022079295-appb-000004
Figure PCTCN2022079295-appb-000005
Figure PCTCN2022079295-appb-000006
Figure PCTCN2022079295-appb-000007
“*”：第1层指与铝箔表面接触的一层，第2层指设置在第1层上的一层。
“#”：第一正极活性材料指制备例1制得的正极活性材料，第二正极活性材料指制备例55、制备例57、制备例58、制备例59、制备例60、制备例61或制备例62的正极活性材料。
负极极片的制备
将负极活性材料人造石墨、导电剂超导炭黑(Super-P)、粘结剂丁苯橡胶(SBR)、增稠剂羧甲基纤维素钠(CMC-Na)按照质量比为95％：1.5％：1.8％：1.7％溶于去离子水中，充分搅拌混合均匀后，得到粘度3000mPa.s、固含52％的负极浆料；将负极浆料涂覆在6μm的负极集流体铜箔上，之后在100℃烘烤4小时以烘干，辊压，得到压实密度为1.75g/cm3的负极极片。
隔离膜
采用聚丙烯膜。
电解液的制备
将碳酸乙烯酯、碳酸二甲酯和1,2-丙二醇碳酸酯按体积比1:1:1混合，然后将LiPF 6均匀溶解在上述溶液中，得到电解液。该电解液中，LiPF 6的浓度为1mol/L。
全电池的制备
采用上述的正极极片，按照负极极片、隔膜、正极极片的顺序，采用卷绕法形成裸电芯，分别冲切出铝极耳和铜极耳，得到裸电芯；通过转接片将两个裸电芯铜与铜极耳，铝与铝极耳一起焊接到电池顶盖上，对裸电芯进行包裹绝缘后，将裸电芯装入铝壳中，将顶盖与铝壳焊接形成干电芯，对干电芯进行烘烤除水后注入电解液，对电池进行化成和老化，相应地得到全电池。其中，正极极片P1、P2、P3、P8、P10、P11、P12、P17、P18、P23、P24、P26、P27所制的电池 结构如图7-19所示。
扣式电池的制备
将上述的正极极片与负极、电解液一起在扣电箱中组装成扣式电池(下文也称“扣电”)。
Ⅰ.正极活性材料的性质测试
1.正极活性材料化学式的测定
采用球差电镜仪(ACSTEM)对正极活性材料内部微观结构和表面结构进行高空间分辨率表征，结合三维重构技术得到正极活性材料的化学式。
2.晶格变化率测量方法
在25℃恒温环境下，将正极活性材料样品置于XRD(型号为Bruker D8 Discover)中，采用1°/min对样品进行测试，并对测试数据进行整理分析，参照标准PDF卡片，计算出此时的晶格常数a0、b0、c0和v0(a0,b0和c0表示晶胞各个方面上的长度大小，v0表示晶胞体积，可通过XRD精修结果直接获取)。
将正极活性材料样品按照制备正极极片P1的方法制成正极极片，然后按照上述“扣式电池的制备”制备成扣电，并对上述扣电以0.05C小倍率进行充电，直至电流减小至0.01C。然后将扣电中的正极极片取出，并置于DMC中浸泡8小时。然后烘干，刮粉，并筛选出其中粒径小于500nm的颗粒。取样并按照与上述测试新鲜样品同样的方式计算出其晶格常数v1，将(v0-v1)/v0×100％作为其完全脱嵌锂前后的晶格变化率示于表中。
3.Li/Mn反位缺陷浓度测量方法
将“晶格变化率测量方法”中测试的XRD结果与标准晶体的PDF(Powder Diffraction File)卡片对比，得出Li/Mn反位缺陷浓度。具体而言，将“晶格变化率测量方法”中测试的XRD结果导入通用结构 分析系统(GSAS)软件中，自动获得精修结果，其中包含了不同原子的占位情况，通过读取精修结果获得Li/Mn反位缺陷浓度。
4.表面氧价态测量方法
取5g正极活性材料样品按照上述制备正极极片P1的方法制成正极极片，然后按照上述“扣式电池的制备”制备成扣电。对扣电采用0.05C小倍率进行充电，直至电流减小至0.01C。然后将扣电中的正极极片取出，并置于DMC中浸泡8小时。然后烘干，刮粉，并筛选出其中粒径小于500nm的颗粒。将所得颗粒用电子能量损失谱(EELS，所用仪器型号为Talos F200S)进行测量，获取能量损失近边结构(ELNES)，其反映元素的态密度和能级分布情况。根据态密度和能级分布，通过对价带态密度数据进行积分，算出占据的电子数，从而推算出充电后的表面氧的价态。
5.压实密度测量方法
取5g正极活性材料的粉末放于压实专用模具(美国CARVER模具，型号13mm)中，然后将模具放在压实密度仪器上。施加3T的压力，在设备上读出压力下粉末的厚度(卸压后的厚度)，通过ρ＝m/v，计算出压实密度。
6.循环后Mn(以及Mn位掺杂的Fe)溶出量测量方法
将正极活性材料样品按照上述制备正极极片P1的方法制成正极极片，然后按照上述“全电池的制备”制备成全电池。
采用将45℃下循环至容量衰减至80％后的全电池采用0.1C倍率进行放电至截止电压2.0V。然后将电池拆开，取出负极极片，在负极极片上随机取30个单位面积(1540.25mm 2)的圆片，用Agilent ICP-OES730测试电感耦合等离子体发射光谱(ICP)。根据ICP结果计算其中Fe(如果正极活性材料的Mn位掺杂有Fe的话)和Mn的量，从而计算循环后Mn(以及Mn位掺杂的Fe)的溶出量。测试标准依据EPA-6010D-2014。
7.扣式电池初始克容量测量方法
在2.5～4.3V下，将扣式电池按照0.1C充电至4.3V，然后在4.3V下恒压充电至电流小于等于0.05mA，静置5min，然后按照0.1C放电至2.0V，此时的放电容量为初始克容量，记为D0。
8. 3C充电恒流比测量方法
在25℃恒温环境下，将新鲜全电池静置5min，按照1/3C放电至2.5V。静置5min，按照1/3C充电至4.3V，然后在4.3V下恒压充电至电流小于等于0.05mA。静置5min，记录此时的充电容量为C0。按照1/3C放电至2.5V，静置5min，再按照3C充电至4.3V，静置5min，记录此时的充电容量为C1。3C充电恒流比即为C1/C0×100％。
3C充电恒流比越高，说明电池的倍率性能越好。
9.全电池45℃循环性能测试
在45℃的恒温环境下，在2.5～4.3V下，将全电池按照1C充电至4.3V，然后在4.3V下恒压充电至电流小于等于0.05mA。静置5min，然后按照1C放电至2.5V，记录此时的放电容量为D0。重复前述充放电循环，直至放电容量降低到D0的80％。记录此时电池经过的循环圈数。
10.全电池60℃胀气测试
在60℃下，存储100％充电状态(SOC)的全电池。在存储前后及过程中测量电芯的开路电压(OCV)和交流内阻(IMP)以监控SOC，并测量电芯的体积。其中在每存储48h后取出全电池，静置1h后测试开路电压(OCV)、内阻(IMP)，并在冷却至室温后用排水法测量电芯体积。排水法即先用表盘数据自动进行单位转换的天平单独测量电芯的重力F 1，然后将电芯完全置于去离子水(密度已知为1g/cm 3)中，测量此时的电芯的重力F 2，电芯受到的浮力F 浮即为F 1-F 2，然后根据阿基米德原理F 浮＝ρ×g×V 排，计算得到电芯体积V＝(F 1-F 2) /(ρ×g)。
由OCV、IMP测试结果来看，本实验过程中直至存储结束，实施例的电池始终保持99％以上的SOC。
存储30天后，测量电芯体积，并计算相对于存储前的电芯体积，存储后的电芯体积增加的百分比。
另外，测量电芯残余容量。在2.5～4.3V下，将全电池按照1C充电至4.3V，然后在4.3V下恒压充电至电流小于等于0.05mA。静置5min，记录此时的充电容量为电芯残余容量。
表4中示出制备例1-11和对比例1-8的正极活性材料组成。表5中示出制备例1-11和对比例1-8的正极活性材料或扣电或全电按照上述性能测试方法测得的性能数据。表6示出制备例12-27的正极活性材料组成。表7中示出制备例12-27的正极活性材料或扣电或全电按照上述性能测试方法测得的性能数据。表8中示出制备例28-41的正极活性材料或扣电或全电按照上述性能测试方法测得的性能数据。表9中示出制备例42-54的正极活性材料或扣电或全电按照上述性能测试方法测得性能数据。
表4制备例1-11及对比例1-8正极活性材料的化学式
  化学式
制备例1 Li 0.994Mo 0.001Mn 0.65Fe 0.35P 0.999Si 0.001O 3.999F 0.001
制备例2 Li 0.977Mg 0.001Mn 0.65Fe 0.34Ti 0.01P 0.999N 0.001O 3.999F 0.001
制备例3 Li 0.992W 0.001Mn 0.65Fe 0.35P 0.999S 0.001O 3.999F 0.001
制备例4 Li 0.997Al 0.001Mn 0.65Fe 0.35P 0.999Si 0.001O 3.999Cl 0.001
制备例5 Li 0.993Nb 0.001Mn 0.65Fe 0.345V 0.005P 0.999S 0.001O 3.999F 0.001
制备例6 Li 0.993Nb 0.001Mn 0.65Fe 0.34V 0.005Mg 0.005P 0.999S 0.001O 3.999F 0.001
制备例7 Li 0.993Nb 0.001Mn 0.65Fe 0.34V 0.005Co 0.005P 0.999S 0.001O 3.999F 0.001
制备例8 Li 0.993Nb 0.001Mn 0.65Fe 0.34V 0.005Ni 0.005P 0.999S 0.001O 3.999F 0.001
制备例9 Li 0.991Nb 0.001Mn 0.65Fe 0.349Ti 0.001P 0.999S 0.001O 3.999Cl 0.001
制备例10 Li 0.995Nb 0.001Mn 0.65Fe 0.34V 0.005Mg 0.005P 0.999Si 0.001O 3.999Br 0.001
制备例11 Li 0.998Mg 0.001Mn 0.65Fe 0.345V 0.005P 0.999Si 0.001O 3.999Br 0.001
对比例1 LiMnPO 4
对比例2 LiMn 0.85Fe 0.15PO 4
对比例3 Li 0.990Mg 0.005Mn 0.95Zn 0.05PO 4
对比例4 Li 0.90Nb 0.01Mn 0.6Fe 0.4PO 3.95F 0.05
对比例5 Li 0.76Mg 0.12Mn 0.7Fe 0.3P 0.999Si 0.001O 3.999F 0.001
对比例6 Li 0.998Mg 0.001Mn 0.4Zn 0.6P 0.999Si 0.001O 3.999F 0.001
对比例7 Li 1.068Mg 0.001Mn 0.7Fe 0.3P 0.88Si 0.12O 3.95F 0.05
对比例8 Li 0.948Mg 0.001Mn 0.6Fe 0.4P 0.93Si 0.07O 3.88F 0.12
表5制备例1-11和对比例1-8的正极活性材料或扣电或全电按照上述性能测试方法测得的性能数据
Figure PCTCN2022079295-appb-000008
Figure PCTCN2022079295-appb-000009
表6制备例12-27正极活性材料的化学式及元素比
  化学式 (1-y):y a：x
制备例12 Li 0.997Mg 0.001Mn 0.68Fe 0.3V 0.02P 0.999N 0.001O 3.999F 0.001 2.26 997
制备例13 Li 0.997Mg 0.001Mn 0.58Fe 0.4V 0.02P 0.999N 0.001O 3.999F 0.001 1.45 997
制备例14 Li 0.997Mg 0.001Mn 0.65Fe 0.3V 0.05P 0.999N 0.001O 3.999F 0.001 2.17 997
制备例15 Li 0.988Mg 0.005Mn 0.6Fe 0.35V 0.05P 0.999S 0.001O 3.999F 0.001 1.71 197.6
制备例16 Li 0.984Mg 0.005Mn 0.6Fe 0.35V 0.05P 0.995S 0.005O 3.999F 0.001 1.71 196.8
制备例17 Li 0.984Mg 0.005Mn 0.6Fe 0.35V 0.05P 0.999S 0.001O 3.995F 0.005 1.71 196.8
制备例18 Li 0.984Mg 0.005Mn 0.65Fe 0.25V 0.05Co 0.05P 0.999S 0.001O 3.995F 0.005 2.60 196.8
制备例19 Li 0.984Mg 0.005Mn 0.65Fe 0.20V 0.05Co 0.10P 0.999S 0.001O 3.995F 0.005 3.25 196.8
制备例20 Li 0.984Mg 0.005Mn 0.75Fe 0.05V 0.05Co 0.15P 0.999S 0.001O 3.995F 0.005 15.0 196.8
制备例21 Li 0.984Mg 0.005Mn 0.65Fe 0.25V 0.05Ni 0.05P 0.999S 0.001O 3.995F 0.005 2.60 196.8
制备例22 Li 0.984Mg 0.005Mn 0.75Fe 0.10V 0.05Ni 0.10P 0.999S 0.001O 3.995F 0.005 7.50 196.8
制备例23 Li 0.984Mg 0.005Mn 0.7Fe 0.15V 0.05Co 0.10P 0.999S 0.001O 3.995F 0.005 4.67 196.8
制备例24 Li 0.984Mg 0.005Mn 0.6Fe 0.25V 0.05Co 0.10P 0.999S 0.001O 3.995F 0.005 2.40 196.8
制备例25 Li 0.984Mg 0.005Mn 0.5Fe 0.35V 0.05Co 0.10P 0.999S 0.001O 3.995F 0.005 1.43 196.8
制备例26 Li 1.01Mg 0.005Mn 0.7Fe 0.15V 0.05Co 0.10P 0.9Si 0.1O 3.92F 0.08 4.67 202
制备例27 Li 0.97Mg 0.005Mn 0.7Fe 0.15V 0.05Co 0.10P 0.92Si 0.08O 3.9F 0.1 4.67 194
表7制备例12-27的正极活性材料或扣电或全电按照上述性能测试方法测得的性能数据
Figure PCTCN2022079295-appb-000010
Figure PCTCN2022079295-appb-000011
表8制备例28-41的正极活性材料或扣电或全电按照上述性能测试方法测得的性能数据
Figure PCTCN2022079295-appb-000012
Figure PCTCN2022079295-appb-000013
表9制备例42-54的正极活性材料或扣电或全电按照上述性能测试方法测得的性能数据
Figure PCTCN2022079295-appb-000014
Figure PCTCN2022079295-appb-000015
由上述表5、7、8、9可见，本申请制备例的各正极活性材料均在循环性能、高温稳定性、克容量和压实密度中的一个甚至全部方面实现了比对比例更优的效果。
由制备例18-20、23-25之间相比，可以看出，在其他元素相同的情况下，(1-y):y在1至4范围内，能够进一步提升二次电池的能量密度和循环性能。
Ⅱ.电池测试
采用正极极片P1-P42制备的二次电池进行如下测试：
(1)按照国标GB 38031-2020“电动汽车用动力蓄电池安全要求”中的方法测定二次电池的能量密度和炉温实验结果；
(2)针刺测试：将二次电池充满至100％SOC，用Φ8mm钢针以25mm/2的速度刺穿电芯，观察1h，如未发生起火，则通过测试；
(3)按照国标GBT31486-2015“电动汽车用动力蓄电池电性能要求及试验方法”测定二次电池的室温1C充电容量保持率以及低温放电容量保持率，以获取电池的动力学数据；
(4)按照国标GBT31484-2015“电动汽车用动力蓄电池循环寿命要求及试验方法”测定二次电池的循环寿命数据；
上述结果见表10
Figure PCTCN2022079295-appb-000016
Figure PCTCN2022079295-appb-000017
Figure PCTCN2022079295-appb-000018
Figure PCTCN2022079295-appb-000019
Figure PCTCN2022079295-appb-000020

Claims (17)

  1. 一种正极极片，包括正极集流体和设置在所述正极集流体的至少一个表面上的正极膜层；所述正极膜层为单层结构或多层结构；当所述正极膜层为单层结构时，至少一个所述正极膜层同时包含化学式为Li aA xMn 1-yR yP 1-zC zO 4-nD n的第一正极活性材料和第二正极活性材料；和/或，当所述正极膜层为多层结构时，至少一个所述正极膜层的至少一层中同时包含化学式为Li aA xMn 1-yR yP 1-zC zO 4-nD n的第一正极活性材料和第二正极活性材料；
    其中，
    所述A包括选自Zn、Al、Na、K、Mg、Nb、Mo和W中的一种或多种元素；
    所述R包括选自Ti、V、Zr、Fe、Ni、Mg、Co、Ga、Sn、Sb、Nb和Ge中的一种或多种元素；
    所述C包括选自B、S、Si和N中的一种或多种元素；
    所述D包括选自S、F、Cl和Br中的一种或多种元素；
    所述a选自0.9至1.1的范围，所述x选自0.001至0.1的范围，所述y选自0.001至0.5的范围，所述z选自0.001至0.1的范围，所述n选自0.001至0.1的范围；
    所述第二正极活性材料选自LiNi bCo cMn (1-b-c)O 2、LiNi bCo cAl (1-b-c)O 2和LiCoO 2中的一种或多种；其中，b独立地选自0.3-0.9(可选为0.33-0.8)，b与c之和独立地选自0.3-0.9(可选为0.66-0.9)。
  2. 一种正极极片，包括正极集流体和设置在所述正极集流体的至少一个表面上的正极膜层；至少一个所述正极膜层为多层结构，任一具有多层结构的正极膜层在不同层中分别包含化学式为Li aA xMn 1-yR yP 1-zC zO 4-nD n的第一正极活性材料和第二正极活性材料；
    其中，
    所述A包括选自Zn、Al、Na、K、Mg、Nb、Mo和W中的一种或多种元素，
    所述R包括选自Ti、V、Zr、Fe、Ni、Mg、Co、Ga、Sn、Sb、Nb和Ge中的一种或多种元素，
    所述C包括选自B、S、Si和N中的一种或多种元素，
    所述D包括选自S、F、Cl和Br中的一种或多种元素，
    所述a选自0.9至1.1的范围，所述x选自0.001至0.1的范围，所述y选自0.001至0.5的范围，所述z选自0.001至0.1的范围，所述n选自0.001至0.1的范围；
    所述第二正极活性材料选自LiNi bCo cMn (1-b-c)O 2、LiNi bCo cAl (1-b-c)O 2和LiCoO 2中的一种或多种；其中，b独立地选自0.3-0.9(可选为0.33-0.8)，b与c之和独立地选自0.3-0.9(可选为0.66-0.9)；
    可选地，任一具有多层结构的所述正极膜层在相邻层中分别包含所述第一正极活性材料和所述第二正极活性材料。
  3. 一种正极极片，包括正极集流体和分别设置在所述正极集流体的两个表面上的正极膜层A和正极膜层B；所述正极膜层A和所述正极膜层B独立地为单层结构或多层结构；所述正极膜层A的至少一层中包含化学式为Li aA xMn 1-yR yP 1-zC zO 4-nD n的第一正极活性材料，同时，所述正极膜层B的至少一层中包含第二正极活性材料；
    其中，
    所述A包括选自Zn、Al、Na、K、Mg、Nb、Mo和W中的一种或多种元素，
    所述R包括选自Ti、V、Zr、Fe、Ni、Mg、Co、Ga、Sn、Sb、Nb和Ge中的一种或多种元素，
    所述C包括选自B、S、Si和N中的一种或多种元素，
    所述D包括选自S、F、Cl和Br中的一种或多种元素，
    所述a选自0.9至1.1的范围，所述x选自0.001至0.1的范围，所述y选自0.001至0.5的范围，所述z选自0.001至0.1的范围，所 述n选自0.001至0.1的范围；
    所述第二正极活性材料选自LiNi bCo cMn (1-b-c)O 2、LiNi bCo cAl (1-b-c)O 2和LiCoO 2中的一种或多种；其中，b独立地选自0.3-0.9(可选为0.33-0.8)，b与c之和独立地选自0.3-0.9(可选为0.66-0.9)。
  4. 根据权利要求1至3中任一项所述的正极极片，其中，所述第一活性材料与所述第二活性材料的质量比为1:7-7:1，可选为1:4-4:1。
  5. 根据权利要求1至4中任一项所述的正极极片，其中，所述第一正极活性材料中，
    R选自Ti、V、Zr、Fe、Ni、Mg、Co、Ga、Sn、Sb、Nb和Ge中的至少两种元素；
    可选地，
    所述A为选自Mg和Nb中的任一种元素，和/或，
    所述R为选自Fe、Ti、V、Co和Mg中的至少两种元素，可选地为Fe与选自Ti、V、Co和Mg中的一种以上元素，和/或，
    所述C为S，和/或，
    所述D为F。
  6. 根据权利要求1至5中任一项所述的正极极片，其中，所述第一正极活性材料中，所述x选自0.001-0.005的范围；和/或，所述y选自0.01至0.5的范围，可选地选自0.25至0.5的范围；和/或，所述z选自0.001至0.005的范围；和/或，所述n选自0.001至0.005的范围；和/或，(1-y)与y的比值选自1-4，可选为选自1.5-3；和/或，a与x的比值选自9-1100，可选为选自190-998。
  7. 根据权利要求1至6中任一项所述的正极极片，其中，所述第一正极活性材料的晶格变化率为8％以下，可选地为4％以下。
  8. 根据权利要求1至7中任一项所述的正极极片，其中，所述第一正极活性材料的Li/Mn反位缺陷浓度为2％以下，可选地为0.5％以下。
  9. 根据权利要求1至8中任一项所述的正极极片，其中，所述第一正极活性材料的表面氧价态为-1.82以下，可选地为-1.89～-1.98。
  10. 根据权利要求1至9中任一项所述的正极极片，其中，所述第一正极活性材料在3T下的压实密度为2.0g/cm 3以上，可选地为2.2g/cm 3以上。
  11. 根据权利要求1至10中任一项所述的正极极片，其中，所述第一正极活性材料的表面还包覆有碳。
  12. 根据权利要求1至11中任一项所述的正极极片，其中，所述第一正极活性材料中，
    LiNi bCo cMn (1-b-c)O 2中的b、(1-b-c)和c的比值为5:2:3或3:1:1或8:1:1；和/或，
    LiNi bCo cAl (1-b-c)O 2中的b、c和(1-b-c)的比值为5:2:3或3:1:1或8:1:1。
  13. 根据权利要求1至12中任一项所述的正极极片，其中，所述第一正极活性材料和所述第二正极活性材料的质量之和占所述正极极片的质量的88％-98.7％。
  14. 一种二次电池，包括权利要求1至13中任一项所述的正极极片。
  15. 一种电池模块，包括权利要求14所述的二次电池。
  16. 一种电池包，包括权利要求15所述的电池模块。
  17. 一种用电装置，包括选自权利要求14所述的二次电池、权利要求15所述的电池模块和权利要求16所述的电池包中的至少一种。
PCT/CN2022/079295 2022-03-04 2022-03-04 正极极片、二次电池、电池模块、电池包和用电装置 Ceased WO2023164931A1 (zh)