WO2023276527A1 - 非水電解質二次電池 - Google Patents

非水電解質二次電池 Download PDF

Info

Publication number
WO2023276527A1
WO2023276527A1 PCT/JP2022/022083 JP2022022083W WO2023276527A1 WO 2023276527 A1 WO2023276527 A1 WO 2023276527A1 JP 2022022083 W JP2022022083 W JP 2022022083W WO 2023276527 A1 WO2023276527 A1 WO 2023276527A1
Authority
WO
WIPO (PCT)
Prior art keywords
aqueous electrolyte
lithium
composite oxide
secondary battery
positive electrode
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2022/022083
Other languages
English (en)
French (fr)
Inventor
淵龍 仲
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Panasonic Intellectual Property Management Co Ltd
Original Assignee
Panasonic Intellectual Property Management Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Panasonic Intellectual Property Management Co Ltd filed Critical Panasonic Intellectual Property Management Co Ltd
Priority to US18/564,871 priority Critical patent/US20240291033A1/en
Priority to JP2023531723A priority patent/JP7814002B2/ja
Priority to EP22832685.6A priority patent/EP4366015A4/en
Priority to CN202280045885.XA priority patent/CN117581406A/zh
Publication of WO2023276527A1 publication Critical patent/WO2023276527A1/ja
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

非水電解質二次電池は、正極と、負極と、非水電解質と、を備える。正極は、正極活物質を含み、正極活物質は、Ｎｉと、Ｍｎと、Ａｌと、を含むリチウム遷移金属複合酸化物を含む。リチウム遷移金属複合酸化物に含まれるＬｉ以外の金属元素に占めるＮｉ、ＭｎおよびＡｌの割合が、それぞれ、Ｎｉ：５０原子％以上、Ｍｎ：１０原子％以下、およびＡｌ：１０原子％以下である。リチウム遷移金属複合酸化物がＣｏを含む場合、Ｌｉ以外の金属元素に占めるＣｏの割合が１．５原子％以下である。非水電解質は、オキサレート化合物を含み、オキサレート化合物は、リチウムカチオンと、オキサレート錯体のアニオンと、を含む。

Description

非水電解質二次電池
　本開示は、非水電解質二次電池に関する。
　リチウムイオン二次電池に代表される非水電解質二次電池は、正極と、負極と、非水電解質とを備える。非水電解質二次電池の優れた特性を確保するために、電池の構成要素の改良が試みられている。
　特許文献１は、イソシアヌル酸の窒素原子上に置換基を有していても良い炭素数１～２０の有機基を有する化合物（Ａ）と、ニトリル化合物、イソシアネート化合物、ジフルオロリン酸化合物、またはフルオロスルホン酸塩などとを含有する非水電解液を提案している。
　特許文献２は、式１：ＬｉｘＮｉ１－ｙ－ｚ－ｖ－ｗＣｏｙＡｌｚＭ１ｖＭ２ｗＯ２で表されるリチウム含有複合酸化物からなり、式１中の元素Ｍ１は、Ｍｎ、Ｔｉ、Ｙ、Ｎｂ、ＭｏおよびＷよりなる群から選ばれた少なくとも１種であり、元素Ｍ２は、Ｍｇ、Ｃａ、ＳｒおよびＢａよりなる群から選ばれた少なくとも２種であり、かつ、元素Ｍ２は、少なくともＭｇとＣａとを含み、式１は、０．９７≦ｘ≦１．１、０．０５≦ｙ≦０．３５、０．００５≦ｚ≦０．１、０．０００１≦ｖ≦０．０５、および０．０００１≦ｗ≦０．０５を満たし、複合酸化物は、一次粒子が集合して二次粒子を形成しており、複合酸化物の一次粒子の平均粒径は、０．１μｍ以上、３μｍ以下であり、複合酸化物の二次粒子の平均粒径は、８μｍ以上、２０μｍ以下である、非水電解液二次電池用の正極活物質を提案している。
特開２０１４－１９４９３０号公報 特開２００６－３１０１８１号公報
　リチウム遷移金属複合酸化物中のＣｏは近年価格が高騰している。リチウム遷移金属複合酸化物中のＣｏ含有量を低減すると、コスト的に有利であるが、非水電解質二次電池のサイクル特性が低下する。これは、リチウム遷移金属複合酸化物の格子構造が不安定になり、副反応によって劣化が促進されるためと考えられる。
　本開示の一側面は、正極と、負極と、非水電解質と、を備え、前記正極は、正極活物質を含み、前記正極活物質は、Ｎｉと、Ｍｎと、Ａｌと、を含むリチウム遷移金属複合酸化物を含み、前記リチウム遷移金属複合酸化物に含まれるＬｉ以外の金属元素に占めるＮｉ、ＭｎおよびＡｌの割合が、それぞれＮｉ：５０原子％以上、Ｍｎ：１０原子％以下、およびＡｌ：１０原子％以下であり、前記リチウム遷移金属複合酸化物がＣｏを含む場合、Ｌｉ以外の金属元素に占めるＣｏの割合が１．５原子％以下であり、前記非水電解質は、オキサレート化合物を含み、前記オキサレート化合物は、リチウムカチオンと、オキサレート錯体のアニオンと、を含む、非水電解質二次電池に関する。
　本開示によれば、Ｃｏを含まないリチウム遷移金属複合酸化物またはＣｏ含有量が少ないリチウム遷移金属複合酸化物を用いる場合でも、サイクル特性に優れる非水電解質二次電池を提供することができる。
　本発明の新規な特徴を添付の請求の範囲に記述するが、本発明は、構成および内容の両方に関し、本発明の他の目的および特徴と併せ、図面を照合した以下の詳細な説明によりさらによく理解されるであろう。
本開示の一実施形態に係る非水電解質二次電池の一部を切欠いた概略斜視図である。
　以下では、本開示に係る非水電解質二次電池の実施形態について例を挙げて説明するが、本開示は以下で説明する例に限定されない。以下の説明では、具体的な数値や材料を例示する場合があるが、本開示の効果が得られる限り、他の数値や材料を適用してもよい。この明細書において、「数値Ａ～数値Ｂ」という記載は、数値Ａおよび数値Ｂを含み、「数値Ａ以上で数値Ｂ以下」と読み替えることが可能である。以下の説明において、特定の物性や条件などに関する数値の下限と上限とを例示した場合、下限が上限以上とならない限り、例示した下限のいずれかと例示した上限のいずれかを任意に組み合わせることができる。複数の材料が例示される場合、その中から１種を選択して単独で用いてもよく、２種以上を組み合わせて用いてもよい。
　また、本開示は、添付の特許請求の範囲に記載の複数の請求項から任意に選択される２つ以上の請求項に記載の事項の組み合わせを包含する。つまり、技術的な矛盾が生じない限り、添付の特許請求の範囲に記載の複数の請求項から任意に選択される２つ以上の請求項に記載の事項を組み合わせることができる。
　非水電解質二次電池には、少なくともリチウムイオン電池、リチウム金属二次電池などが含まれる。
　本開示に係る非水電解質二次電池は、正極と負極と非水電解質とを備える。正極は、正極活物質を含む。正極活物質は、ＮｉとＭｎとＡｌとを含むリチウム遷移金属複合酸化物を含む。
　リチウム遷移金属複合酸化物のＣｏ含有量を低減して、Ｎｉ含有量を多くすることができれば、コスト的に有利であるとともに、高容量を確保することができる。そこで、本開示に係る非水電解質二次電池では、リチウム遷移金属複合酸化物のＮｉ含有量を高くする。一方、本開示に係る非水電解質二次電池において、リチウム遷移金属複合酸化物は、Ｃｏを含まないか、Ｌｉ以外の金属元素に占めるＣｏの割合が１．５原子％以下に制限されている。以下、本開示に係る非水電解質二次電池におけるリチウム遷移金属複合酸化物を「複合酸化物ＮＭＡ」とも称する。
　複合酸化物ＮＭＡに含まれるＬｉ以外の金属元素に占めるＮｉ、ＭｎおよびＡｌの割合は、それぞれＮｉ：５０原子％以上、Ｍｎ：１０原子％以下、および、Ａｌ：１０原子％以下であり、かつ複合酸化物ＮＭＡは、Ｃｏを含まないか、Ｌｉ以外の金属元素に占めるＣｏの割合が１．５原子％以下である。
　ＭｎおよびＡｌは、Ｃｏ含有量が低減された複合酸化物ＮＭＡの結晶構造の安定化に寄与する。しかし、複合酸化物ＮＭＡは、Ｃｏ含有量が１．５原子％以下にまで制限されており、かつＮｉ含有量が多いため、結晶構造が不安定になりやすく、複合酸化物ＮＭＡからＡｌ、Ｎｉ等の金属が溶出し得る。金属が溶出すると、正極容量が低下し、サイクル特性（もしくは容量維持率）が低下する。特に、Ｎｉ含有量が多い複合酸化物ＮＭＡでは、溶出したＮｉが複合酸化物ＮＭＡの粒子表面にＬｉイオンの吸蔵および放出を妨げる構造の酸化被膜を形成し、内部抵抗の上昇を招く場合がある。また、溶出した金属が負極で析出し、二次電池としての耐久性に影響を及ぼす場合もある。
　上記に鑑み、本開示に係る非水電解質二次電池では、複合酸化物ＮＭＡを用いるとともに、オキサレート化合物を含む非水電解質を用いる。オキサレート化合物は、リチウムカチオンと、オキサレート錯体のアニオンと、を含む。オキサレート化合物が生成するオキサレート錯体のアニオンは、解離度が高く、非水電解質全体のイオン伝導度を高めるとともに、複合酸化物ＮＭＡの粒子表面で被膜を形成し、金属の溶出を抑制する効果を有するものと考えられる。そのため、優れたサイクル特性を確保できるとともに、オキサレート化合物に由来する被膜は、イオン伝導性に優れるため、電極反応を阻害する影響は軽微であると推測される。
　非水電解質は、更に、後述する一般式（２）で表される有機ケイ素化合物を含んでもよい。有機ケイ素化合物は、複合酸化物ＮＭＡの粒子表面に副反応を抑制する強固な被膜を形成する。これにより、より優れたサイクル特性を確保できるとともに、内部抵抗の増加が更に抑制される。仮に有機ケイ素化合物を単独で使用する場合、被膜が過度に厚く形成される傾向があり、イオン伝導に対する抵抗が大きくなることがある。これに対し、オキサレート化合物と有機ケイ素化合物との組み合わせに由来する被膜は、イオン伝導性に優れている。すなわち、オキサレート化合物は、有機ケイ素化合物に由来する被膜のイオン伝導性を向上させる作用も有する。
　ところで、オキサレート化合物を複合酸化物ＮＭＡよりもＣｏ含有量が多いリチウム遷移金属複合酸化物と組み合わせても、サイクル特性を向上させる効果や内部抵抗の増加を抑制する効果を顕著に得ることができない。オキサレート化合物は複合酸化物ＮＭＡと組み合わせることで上記効果が顕著に得られる。複合酸化物ＮＭＡにおいて効果が顕著となるのは、複合酸化物ＮＭＡは、Ｃｏ含有量がより多いリチウム遷移金属複合酸化物に比べて、複合酸化物自体の抵抗が大きく、かつ粒子が比較的脆いためと考えられる。複合酸化物ＮＭＡの粒子は、クラックが発生しやすく、金属の溶出も顕著になりやすく、充放電に伴う抵抗の上昇が顕在化しやすい。よって、複合酸化物ＮＭＡでは、オキサレート化合物に由来する被膜による特性の向上幅が大きくなる。一方、Ｃｏ含有量が多いリチウム遷移金属複合酸化物は、そのような観点ではより優れているため、オキサレート化合物を用いる必要性が低いといえる。
　以下に、本実施形態の非水電解質二次電池について構成要素ごとにより具体的に説明する。
［正極］
　正極は、正極活物質を含む。正極は、通常、正極集電体と、正極集電体に保持された層状の正極合剤（以下、正極合剤層と称する）を備えている。正極合剤層は、正極合剤の構成成分を分散媒に分散させた正極スラリを、正極集電体の表面に塗布し、乾燥させることにより形成できる。乾燥後の塗膜を、必要により圧延してもよい。
　正極合剤は、必須成分として、正極活物質を含み、任意成分として、結着剤、増粘剤、導電剤等を含むことができる。
　（正極活物質）
　正極活物質は、複合酸化物ＮＭＡを含む。複合酸化物ＮＭＡは、ＮｉとＭｎとＡｌとを含み、微量のＣｏを含んでもよく、Ｃｏを含まなくてもよい。製造コスト削減の観点からは、Ｃｏ含有量は少ないほど望ましく、Ｌｉ以外の金属元素に占めるＣｏの割合は１．５原子％以下であり、１．０原子％以下が望ましく、０．５原子％以下がより望ましく、Ｃｏを含まないことが最も望ましい。一方、高容量化の観点から、複合酸化物ＮＭＡにおいて、Ｌｉ以外の金属元素に占めるＮｉ、ＭｎおよびＡｌの割合は、それぞれＮｉ：５０原子％以上、Ｍｎ：１０原子％以下、およびＡｌ：１０原子％以下である。Ｌｉ以外の金属元素に占めるＮｉ含有量は８０原子％以上が望ましく、９０原子％以上がより望ましく、９２原子％以上でもよい。Ｍｎ含有量は、７原子％以下でもよく、５原子％以下でもよく、３原子％以下でもよい。Ａｌ含有量は、９原子％以下でもよく、７原子％以下でもよく、５原子％以下でもよい。複合酸化物ＮＭＡは、例えば、層状の結晶構造（例えば、岩塩型結晶構造）を有する。
　複合酸化物ＮＭＡは、例えば、式：ＬｉαＮｉ（１－ｘ１－ｘ２－ｙ－ｚ）Ｃｏｘ１Ｍｎｘ２ＡｌｙＭｅｚＯ２＋βで表される。元素Ｍｅは、Ｌｉ、Ｎｉ、Ｍｎ、Ａｌ、Ｃｏおよび酸素以外の元素である。
　上記式において、リチウムの原子比を示すαは、例えば、０．９５≦α≦１．０５である。αは、充放電により増減する。酸素の原子比を示す（２＋β）において、βは、－０．０５≦β≦０．０５を満たす。
　Ｎｉの原子比を示す１－ｘ１－ｘ２－ｙ－ｚ（＝ｖ）は、例えば、０．６８５以上であり、０．８以上であってもよく、０．９０以上であってもよく、０．９２以上であってもよい。また、Ｎｉの原子比を示すｖは、０．９５以下であってもよい。ｖは０．６８５以上、０．９５以下（０．６８５≦ｖ≦０．９５）であってもよく、０．８０以上、０．９５以下であってもよく、０．９０以上、０．９５以下であってもよく、０．９２以上、０．９５以下であってもよい。
　Ｎｉの原子比ｖが高いほど、充電時に複合酸化物ＮＭＡから多くのリチウムイオンを引き抜くことができ、容量を高めることができる。しかしながら、このように容量を高めた複合酸化物ＮＭＡ中のＮｉはその価数が高くなる傾向にある。また、Ｎｉの原子比が高くなると、相対的に他の元素の原子比が小さくなる。この場合、特に満充電状態において結晶構造が不安定になり易く、充放電の繰り返しによってリチウムイオンの可逆的な吸蔵および放出が困難な結晶構造に変化することで不活性化しやすくなる。その結果、サイクル特性が低下しやすい。本実施形態に係る非水電解質二次電池では、このようにＮｉ含有量が高い複合酸化物ＮＭＡを用いるにもかかわらず、オキサレート化合物を含む非水電解質を用いることで優れたサイクル特性を確保することができる。
　Ｃｏの原子比を示すｘ１は、例えば、０．０１５以下（０≦ｘ１≦０．０１５）であり、０．０１以下であってもよく、０．００５以下であってもよい。ｘ１が０の場合には、Ｃｏが検出限界以下である場合が包含される。
　Ｍｎの原子比を示すｘ２は、例えば、０．１以下（０＜ｘ２≦０．１）であり、０．０７以下であってもよく、０．０５以下であってもよく、０．０３以下であってもよい。ｘ２は、０．０１以上であってもよく、０．０２以上であってもよい。Ｍｎは複合酸化物ＮＭＡの結晶構造の安定化に寄与するとともに、複合酸化物ＮＭＡが安価なＭｎを含むことでコスト削減に有利となる。
　Ａｌの原子比を示すｙは、例えば、０．１以下（０＜ｙ≦０．１）であり、０．０９以下であってもよく、０．０７以下であってもよく、０．０５以下であってもよい。ｙは、０．０１以上であってもよく、０．０２以上であってもよい。Ａｌは複合酸化物ＮＭＡの結晶構造の安定化に寄与する。また、０．０５≦ｘ２＋ｙ≦０．１を満たすことが好ましい。この場合、オキサレート化合物の効果や、充放電を繰り返した後の内部抵抗の増加を抑制する効果が更に顕在化する。
　元素Ｍｅの原子比を示すｚは、例えば、０≦ｚ≦０．１０であり、０＜ｚ≦０．０５であってもよく、０．００１≦ｚ≦０．００５であってもよい。
　元素Ｍｅは、Ｔｉ、Ｚｒ、Ｎｂ、Ｍｏ、Ｗ、Ｆｅ、Ｚｎ、Ｂ、Ｓｉ、Ｍｇ、Ｃａ、Ｓｒ、ＳｃおよびＹからなる群より選択された少なくとも１種であってもよい。中でも、Ｎｂ、ＳｒおよびＣａからなる群より選択された少なくとも１種が複合酸化物ＭＮＡに含まれている場合、複合酸化物ＮＭＡの表面構造が安定化し、抵抗が低減し、金属の溶出が更に抑えられと考えられる。元素Ｍｅは、複合酸化物ＮＭＡの粒子表面の近傍に偏在しているとより効果的である。
　複合酸化物ＮＭＡを構成する元素の含有量は、誘導結合プラズマ発光分光分析装置（Ｉｎｄｕｃｔｉｖｅｌｙ　ｃｏｕｐｌｅｄ　ｐｌａｓｍａ　ａｔｏｍｉｃ　ｅｍｉｓｓｉｏｎ　ｓｐｅｃｔｒｏｓｃｏｐｙ：ＩＣＰ－ＡＥＳ）、電子線マイクロアナライザー（Ｅｌｅｃｔｒｏｎ　Ｐｒｏｂｅ　Ｍｉｃｒｏ　Ａｎａｌｙｚｅｒ：ＥＰＭＡ）、あるいはエネルギー分散型Ｘ線分析装置（Ｅｎｅｒｇｙ　ｄｉｓｐｅｒｓｉｖｅ　Ｘ－ｒａｙ　ｓｐｅｃｔｒｏｓｃｏｐｙ：ＥＤＸ）等により測定することができる。
　複合酸化物ＮＭＡは、例えば、複数の一次粒子が凝集した二次粒子である。一次粒子の粒径は、一般的に０．０５μｍ以上、１μｍ以下である。複合酸化物の二次粒子の平均粒径は、例えば３μｍ以上、３０μｍ以下であり、５μｍ以上、２５μｍ以下であってもよい。
　なお、本明細書中、二次粒子の平均粒径とは、レーザー回折散乱法で測定される粒度分布において、体積積算値が５０％となる粒径（体積平均粒径）を意味する。このような粒径を、Ｄ５０と称することがある。測定装置には、例えば、株式会社堀場製作所（ＨＯＲＩＢＡ）製「ＬＡ－７５０」を用いることができる。
　複合酸化物ＮＭＡは、例えば、次のような手順で得ることができる。まず、複合酸化物ＮＭＡを構成する金属元素を含む塩の溶液に、攪拌下で、水酸化ナトリウムなどのアルカリを含む溶液を滴下し、ｐＨをアルカリ側（例えば、８．５～１２．５）に調整することにより、金属元素（Ｎｉ、Ｍｎ、Ａｌ、必要に応じてＣｏ、必要に応じて元素Ｍ）を含む複合水酸化物を析出させる。続いて、複合水酸化物を焼成することにより、金属元素を含む複合酸化物（以下、「原料複合酸化物」とも称する。）を得る。このときの焼成温度は、特に制限されないが、例えば、３００℃～６００℃である。
　次いで、原料複合酸化物と、リチウム化合物と、必要に応じて元素Ｍを含む化合物とを混合し、混合物を、酸素気流下、焼成することにより、複合酸化物ＮＭＡを得ることができる。このときの焼成温度は、特に制限されないが、例えば、４５０℃以上８００℃以下である。各焼成は、一段階で行ってもよく、多段階で行ってもよく、昇温しながら行ってもよい。
　原料複合酸化物とリチウム化合物とを混合する際に、元素Ｍを含む化合物を混合することで、元素Ｍを複合酸化物ＮＭＡの粒子表面の近傍に偏在させることができる。
　リチウム化合物としては、酸化リチウム、水酸化リチウム、炭酸リチウム、リチウムハロゲン化物などを用いてもよい。
　正極活物質は、複合酸化物ＮＭＡ以外のリチウム遷移金属複合酸化物を含むことができるが、複合酸化物ＮＭＡの比率が多いことが好ましい。正極活物質に占める複合酸化物ＮＭＡの比率は、例えば、９０質量％以上であり、９５質量％以上であってもよい。正極活物質に占める複合酸化物の比率は、１００質量％以下である。
　（その他）
　結着剤としては、例えば、樹脂材料が用いられる。結着剤としては、例えば、フッ素樹脂、ポリオレフィン樹脂、ポリアミド樹脂、ポリイミド樹脂、アクリル樹脂、ビニル樹脂、ゴム状材料（例えばスチレンブタジエン共重合体（ＳＢＲ））等が挙げられる。結着剤は、１種を単独で用いてもよく、２種以上を組み合わせて用いてもよい。
　増粘剤としては、例えば、セルロースエーテルなどのセルロース誘導体が挙げられる。セルロース誘導体としては、カルボキシメチルセルロース（ＣＭＣ）およびその変性体、メチルセルロースなどが挙げられる。増粘剤は、１種を単独で用いてもよく、２種以上を組み合わせて用いてもよい。
　導電剤としては、例えば、導電性繊維、導電性粒子が挙げられる。導電性繊維としては、炭素繊維、カーボンナノチューブ、金属繊維などが挙げられる。導電性粒子としては、導電性炭素（カーボンブラック、黒鉛など）、金属粉末などが挙げられる。導電剤は、１種を単独で用いてもよく、２種以上を組み合わせて用いてもよい。
　正極スラリに用いる分散媒としては、特に制限されないが、例えば、水、アルコール、Ｎ－メチル－２－ピロリドン（ＮＭＰ）、これらの混合溶媒などが挙げられる。
　正極集電体としては、例えば、金属箔を用い得る。正極集電体は多孔質であってもよい。多孔質の集電体としては、例えば、ネット、パンチングシート、エキスパンドメタルなどが挙げられる。正極集電体の材質としては、例えば、ステンレス鋼、アルミニウム、アルミニウム合金、チタンなどが例示できる。正極集電体の厚さは、特に限定されないが、例えば、１～５０μｍであり、５～３０μｍであってもよい。
［負極］
　負極は、少なくとも負極集電体を含み、負極活物質を含んでもよい。負極は、通常、負極集電体と、負極集電体に保持された層状の負極合剤（以下、負極合剤層と称する）を備えている。負極合剤層は、負極合剤の構成成分を分散媒に分散させた負極スラリを、負極集電体の表面に塗布し、乾燥させることにより形成できる。乾燥後の塗膜を、必要により圧延してもよい。
　負極合剤は、必須成分として、負極活物質を含み、任意成分として、結着剤、増粘剤、導電剤等を含むことができる。
　（負極活物質）
　負極活物質としては、金属リチウム、リチウム合金などを用いてもよいが、電気化学的にリチウムイオンを吸蔵および放出可能な材料が好適に用いられる。このような材料としては、炭素質材料、Ｓｉ含有材料などが挙げられる。負極は、負極活物質を１種含んでいてもよく、２種以上組み合わせて含んでもよい。
　炭素質材料としては、例えば、黒鉛、易黒鉛化炭素（ソフトカーボン）、難黒鉛化炭素（ハードカーボン）が挙げられる。炭素質材料は、１種を単独で用いてもよく、２種以上を組み合わせて用いてもよい。
　充放電の安定性に優れ、不可逆容量も少ないことから、中でも、炭素質材料としては黒鉛が好ましい。黒鉛としては、例えば、天然黒鉛、人造黒鉛、黒鉛化メソフェーズカーボン粒子が挙げられる。
　Ｓｉ含有材料としては、Ｓｉ単体、ケイ素合金、およびケイ素化合物（ケイ素酸化物など）、リチウムイオン伝導相（マトリックス）内にシリコン相が分散している複合材料などが挙げられる。ケイ素酸化物としては、ＳｉＯｘ粒子が挙げられる。ｘは、例えば０．５≦ｘ＜２であり、０．８≦ｘ≦１．６であってもよい。リチウムイオン伝導相としては、ＳｉＯ２相、シリケート相および炭素相からなる群より選択される少なくとも１種を用い得る。
　（その他）
　結着剤、増粘剤および導電剤ならびに負極スラリに用いる分散媒としては、例えば、正極で例示した材料を用い得る。
　負極集電体としては、例えば、金属箔を用い得る。負極集電体は多孔質であってもよい。負極集電体の材質としては、例えば、ステンレス鋼、ニッケル、ニッケル合金、銅、銅合金などが例示できる。負極集電体の厚さは、特に限定されないが、例えば、１～５０μｍであり、５～３０μｍであってもよい。
［非水電解質］
　非水電解質は、通常、非水溶媒とリチウム塩（オキサレート化合物以外のリチウム塩）と添加剤とを含む。
　（オキサレート化合物）
　非水電解質は、添加剤としてオキサレート化合物を含む。オキサレート化合物は、リチウムカチオンと、オキサレート錯体のアニオンとを含む。オキサレート化合物は、非水電解質中でオキサレート錯体のアニオンを生成し得る。よって、オキサレート錯体のアニオンは、オキサレート化合物としてカウントされる。
　オキサレート化合物は、下記の一般式（１）で表される化合物を含むことが好ましい。
Figure JPOXMLDOC01-appb-C000003
　一般式（１）中、Ｍは、ＰまたはＢである。ＭがＰである場合、ｎは１～３の整数であり、ｍ＝６－２ｎを満たす。ＭがＢである場合、ｎは１または２であり、ｍ＝４－２ｎを満たす。
　オキサレート化合物は、リチウムジフルオロビスオキサレートホスフェート：ＬｉＰＦ２（Ｃ２Ｏ４）２、リチウムテトラフルオロオキサレートホスフェート：ＬｉＰＦ４（Ｃ２Ｏ４）、リチウムトリスオキサレートホスフェート：ＬｉＰ（Ｃ２Ｏ４）３、リチウムビスオキサレートボレート：ＬｉＢ（Ｃ２Ｏ４）２、およびリチウムジフルオロオキサレートボレート：ＬｉＢＦ２（Ｃ２Ｏ４）からなる群より選択された少なくとも１種を含むことが好ましい。中でも、リチウムジフルオロビスオキサレートホスフェートがより好ましい。
　非水電解質中のオキサレート化合物の含有量は、３質量％以下であってもよく、１．５質量％以下でもよく、１質量％以下でもよく、０．５質量％以下でもよい。オキサレート化合物の含有量がこのような範囲である場合、正極表面における過度な被膜形成が抑制され、充放電を繰り返した場合の内部抵抗の増加を抑制する効果を高めることができる。非水電解質二次電池では、保存または充放電の間、非水電解質中のオキサレート化合物の含有量が変化する。そのため、非水電解質二次電池から採取される非水電解質中にオキサレート化合物が検出限界以上の濃度で残存していればよい。非水電解質中のオキサレート化合物の含有量は、０．０１質量％以上であってもよい。
　非水電解質二次電池の製造に用いられる非水電解質中のオキサレート化合物の含有量は、０．０１質量％以上であってもよく、０．１質量％以上または０．３質量％以上であってもよい。非水電解質二次電池の製造に用いられる非水電解質中のオキサレート化合物の含有量は、例えば、１．５質量％以下であり、１質量％以下または０．５質量％以下であってもよい。これらの下限値と上限値とは任意に組み合わせることができる。
　（有機ケイ素化合物）
　非水電解質は、添加剤として、更に、下記の一般式（２）で表される有機ケイ素化合物を含んでもよい。
Figure JPOXMLDOC01-appb-C000004
　一般式（２）中、Ｒ１～Ｒ４は、それぞれ独立して、アルキル基、アルケニル基、アルキニル基、またはアルコキシ基であり、かつ、Ｒ１～Ｒ４の少なくとも１つは、アルケニル基またはアルキニル基である。
　アルキル基、アルケニル基、アルキニル基、またはアルコキシ基のアルキル基は、直鎖状あってもよく、分岐鎖状であってもよい。アルキル基、アルケニル基、アルキニル基、またはアルコキシ基の炭素数は、例えば、１～１０であってもよく、１～６または１～４であってもよい。
　アルキル基としては、メチル基、エチル基、ｎ－プロピル基、イソプロピル基、ｎ－ブチル基、ｓｅｃ－ブチル基、ｔｅｒｔ－ブチル基、ヘキシル基、２－エチルヘキシル基、デシル基、テトラデシル基、ステアリル基等が挙げられる。中でも、メチル基、エチル基が好ましい。アルケニル基としては、ビニル基、アリル基、プロパ－２－エン－１－イル基、４－ヘキセニル基、５－ヘキセニル基等が挙げられる。中でも、ビニル基、アリル基が好ましい。アルキニル基としては、エチニル基、プロパルギル基等が挙げられる。アルコキシ基としては、メトキシ基、エトキシ基、ｎ－プロポキシ基、イソプロポキシ基等が挙げられる。アルキル基、アルケニル基、アルキニル基、またはアルコキシ基の水素原子の少なくとも１つはハロゲン原子等に置換されていてもよい。
　有機ケイ素化合物は、テトラビニルシラン、テトラアリルシラン、およびジメチルジビニルシランからなる群より選択された少なくとも１種を含むことが好ましい。中でも、テトラビニルシランがより好ましい。
　Ｒ１～Ｒ４の少なくとも１つが、アルケニル基またはアルキニル基である場合、有機ケイ素化合物は重合性不飽和結合を有し得、当該化合物由来のオリゴマーもしくはポリマーの成分を含む強固な被膜を正極活物質の表面に形成し得る。当該被膜は優れた保護機能を有し、正極活物質からの金属の溶出抑制の効果が更に高められる。
　非水電解質中の有機ケイ素化合物の含有量は、１．５質量％以下が好ましく、１質量％以下または０．５質量％以下であってもよい。有機ケイ素化合物の含有量がこのような範囲である場合、正極表面における過度な被膜形成が抑制され、充放電を繰り返した場合の内部抵抗の増加を抑制する効果を高めることができる。非水電解質二次電池では、保存または充放電の間、非水電解質中の有機ケイ素化合物の含有量は変化する。そのため、非水電解質二次電池から採取される非水電解質中に、有機ケイ素化合物が検出限界以上の濃度で残存していればよい。非水電解質中の有機ケイ素化合物の含有量は、０．０１質量％以上であってもよい。
　非水電解質二次電池の製造に用いられる非水電解質中の有機ケイ素化合物の含有量は、０．０１質量％以上であってもよく、０．１質量％以上または０．３質量％以上であってもよい。非水電解質二次電池の製造に用いられる非水電解質中の有機ケイ素化合物の含有量は、例えば、１．５質量％以下であり、１質量％以下または０．５質量％以下であってもよい。これらの下限値と上限値とは任意に組み合わせることができる。
　非水電解質中のオキサレート化合物および有機ケイ素化合物の含有量は、例えば、ガスクロマトグラフィーを用いて、下記の条件で求められる。
　使用機器：（株）島津製作所製、ＧＣ－２０１０　Ｐｌｕｓ
　カラム：Ｊ＆Ｗ社製、ＨＰ－１（膜厚１μｍ、内径０．３２ｍｍ、長さ６０ｍ）
　カラム温度：５０℃から昇温速度５℃／ｍｉｎで９０℃に昇温し、９０℃で１５分維持し、次いで、９０℃から２５０℃に昇温速度１０℃／ｍｉｎで昇温し、２５０℃で１５分維持
　スプリット比：１／５０
　線速度：３０．０ｃｍ／ｓｅｃ
　注入口温度：２７０℃
　注入量：１μＬ
　検出器：ＦＩＤ　２９０℃（ｓｅｎｓ．１０１）
　非水電解質において、有機ケイ素化合物のオキサレート化合物に対する質量割合（＝有機ケイ素化合物／オキサレート化合物）は、例えば、０．５～１．５であってもよく、０．８～１．２であってもよい。両成分の質量割合がこのような範囲である場合、複合酸化物ＮＭＡの粒子表面に形成される被膜組成のバランスが良くなる。すなわち、イオン伝導性に優れ、かつ金属の溶出を抑制する効果や、充放電を繰り返した場合の内部抵抗の増加を抑制する効果が大きい被膜が形成される。
　（非水溶媒）
　非水溶媒としては、例えば、環状炭酸エステル、鎖状炭酸エステル、環状カルボン酸エステル、鎖状カルボン酸エステルが挙げられる。環状炭酸エステルとしては、プロピレンカーボネート（ＰＣ）、エチレンカーボネート（ＥＣ）等が挙げられる。鎖状炭酸エステルとしては、ジエチルカーボネート（ＤＥＣ）、エチルメチルカーボネート（ＥＭＣ）、ジメチルカーボネート（ＤＭＣ）等が挙げられる。環状カルボン酸エステルとしては、γ－ブチロラクトン（ＧＢＬ）、γ－バレロラクトン（ＧＶＬ）等が挙げられる。鎖状カルボン酸エステルとしては、ギ酸メチル、ギ酸エチル、ギ酸プロピル、酢酸メチル（ＭＡ）、酢酸エチル、酢酸プロピル、プロピオン酸メチル、プロピオン酸エチル、プロピオン酸プロピル等が挙げられる。非水電解質は、非水溶媒を１種含んでもよく、２種以上組み合わせて含んでもよい。
　（リチウム塩）
　リチウム塩としては、例えば、ＬｉＣｌＯ４、ＬｉＢＦ４、ＬｉＰＦ６、ＬｉＡｌＣｌ４、ＬｉＳｂＦ６、ＬｉＳＣＮ、ＬｉＣＦ３ＳＯ３、ＬｉＣＦ３ＣＯ２、ＬｉＡｓＦ６、ＬｉＢ１０Ｃｌ１０、低級脂肪族カルボン酸リチウム、ＬｉＣｌ、ＬｉＢｒ、ＬｉＩ、ホウ酸塩、イミド塩が挙げられる。ホウ酸塩としては、ビス（１，２－ベンゼンジオレート（２－）－Ｏ，Ｏ’）ホウ酸リチウム、ビス（２，３－ナフタレンジオレート（２－）－Ｏ，Ｏ’）ホウ酸リチウム、ビス（２，２’－ビフェニルジオレート（２－）－Ｏ，Ｏ’）ホウ酸リチウム、ビス（５－フルオロ－２－オレート－１－ベンゼンスルホン酸－Ｏ，Ｏ’）ホウ酸リチウム等が挙げられる。イミド塩としては、ビスフルオロスルホニルイミドリチウム（ＬｉＮ（ＦＳＯ２）２）、ビストリフルオロメタンスルホン酸イミドリチウム（ＬｉＮ（ＣＦ３ＳＯ２）２）、トリフルオロメタンスルホン酸ノナフルオロブタンスルホン酸イミドリチウム（ＬｉＮ（ＣＦ３ＳＯ２）（Ｃ４Ｆ９ＳＯ２））、ビスペンタフルオロエタンスルホン酸イミドリチウム（ＬｉＮ（Ｃ２Ｆ５ＳＯ２）２）等が挙げられる。非水電解質は、リチウム塩を、１種含んでもよく、２種以上組み合わせて含んでもよい。
　非水電解質中のリチウム塩（オキサレート化合物以外のリチウム塩）の濃度は、例えば、０．５ｍｏｌ／Ｌ以上、２ｍｏｌ／Ｌ以下である。
　非水電解質は、更に、他の添加剤を含んでもよい。他の添加剤としては、例えば、ビニレンカーボネート、フルオロエチレンカーボネート、およびビニルエチレンカーボネートからなる群より選択される少なくとも１種が挙げられる。
［セパレータ］
　正極と負極との間には、セパレータを介在させることが望ましい。セパレータは、イオン透過度が高く、適度な機械的強度および絶縁性を備えている。セパレータとしては、微多孔薄膜、織布、不織布等を用いることができる。セパレータの材質としては、ポリプロピレン、ポリエチレン等のポリオレフィンが好ましい。
　非水電解質二次電池の構造の一例としては、正極および負極がセパレータを介して巻回されてなる電極群が非水電解質と共に外装体に収容された構造が挙げられる。ただし、これに限られず、他の形態の電極群が適用されてもよい。例えば、正極と負極とがセパレータを介して積層された積層型の電極群でもよい。非水電解質二次電池の形態も限定されず、例えば、円筒型、角型、コイン型、ボタン型、ラミネート型などであればよい。
　以下、本開示に係る非水電解質二次電池の一例として角形の非水電解質二次電池の構造を、図１を参照しながら説明する。
　電池は、有底角形の電池ケース４と、電池ケース４内に収容された電極群１および非水電解質（図示せず）とを備えている。電極群１は、長尺帯状の負極と、長尺帯状の正極と、これらの間に介在するセパレータとを有する。負極の負極集電体は、負極リード３を介して、封口板５に設けられた負極端子６に電気的に接続されている。負極端子６は、樹脂製ガスケット７により封口板５から絶縁されている。正極の正極集電体は、正極リード２を介して、封口板５の裏面に電気的に接続されている。すなわち、正極は、正極端子を兼ねる電池ケース４に電気的に接続されている。封口板５の周縁は、電池ケース４の開口端部に嵌合し、嵌合部はレーザー溶接されている。封口板５には非水電解質の注入孔があり、注液後に封栓８により塞がれる。
　以下、本開示を実施例および比較例に基づいて具体的に説明するが、本開示は以下の実施例に限定されるものではない。
［実施例］
《実施例１～７および比較例１～６》
　下記の手順で、非水電解質二次電池を作製し、評価を行った。
（１）正極の作製
　正極活物質粒子９５質量部に、アセチレンブラック２．５質量部と、ポリフッ化ビニリデン２．５質量部と、適量のＮＭＰとを加え、混合し、正極スラリを得た。次に、アルミニウム箔の表面に正極スラリを塗布し、塗膜を乾燥させた後、圧延して、アルミニウム箔の両面に正極合剤層（厚み９５μｍ、密度３．６ｇ／ｃｍ３）を形成し、正極を得た。
　正極活物質粒子は、次のような手順で作製した。
　硫酸ニッケル、硫酸アルミニウム、および、必要に応じて、硫酸コバルトまたは硫酸マンガンを溶解させた水溶液を調製した。水溶液中の硫酸ニッケルの濃度を１ｍｏｌ／Ｌとし、他の硫酸塩の濃度については、Ｎｉと各金属元素との比率の関係が表１に示す値となるように調節した。
　５０℃にて、水溶液を攪拌しながら、水酸化ナトリウムを３０質量％濃度で含む水溶液を混合物のｐＨが１２になるまで滴下し、水酸化物を析出させた。水酸化物を濾過により回収して、水洗し、乾燥させた。乾燥物を、窒素雰囲気下、５００℃で８時間焼成することにより複合酸化物を得た。
　得られた複合酸化物と、水酸化リチウムとを、Ｌｉと、Ｎｉ、Ｃｏ、ＭｎおよびＡｌの合計とが、１：１の原子比になるように混合した。混合物を、電気炉を用いて、酸素雰囲気中、昇温速度２．０℃／ｍｉｎで、室温から６５０℃まで加熱することにより焼成した。その後、昇温速度０．５℃／ｍｉｎで、６５０℃から７５０℃まで加熱して焼成した。得られた焼成物を水洗し、乾燥することにより複合酸化物ＮＭＡ（正極活物質粒子）を得た。
（２）負極の作製
　ケイ素複合材料と黒鉛とを５：９５の質量比で混合し、負極活物質として用いた。負極活物質と、ＣＭＣのナトリウム塩（ＣＭＣ－Ｎａ）と、ＳＢＲと、水とを所定の質量比で混合し、負極スラリを調製した。次に、負極集電体である銅箔の表面に負極スラリを塗布し、塗膜を乾燥させた後、圧延して、銅箔の両面に負極合剤層を形成した。
（３）非水電解質の調製
　ＥＣおよびＥＭＣとの混合溶媒（ＥＣ：ＥＭＣ＝３：７（体積比））に、ＬｉＰＦ6お
よび必要に応じて表１に示すオキサレート化合物（第１成分）および有機ケイ素化合物（第２成分）を溶解させることにより、非水電解質（電解液）を調製した。電解液におけるＬｉＰＦ6の濃度は１．０ｍｏｌ／Ｌとした。調製した非水電解質中の第１成分および第２成分の濃度（初期濃度）は、表１中に示す値（質量％）とした。
（４）非水電解質二次電池の作製
　上記で得られた正極にＡｌ製の正極リードを取り付け、上記で得られた負極にＮｉ製の負極リードを取り付けた。不活性ガス雰囲気中で、正極と負極とをポリエチレン薄膜（セパレータ）を介して渦巻状に捲回し、捲回型の電極群を作製した。電極群を、Ａｌ層を備えるラミネートシートで形成される袋状の外装体に収容し、上記非水電解質を注入した後、外装体を封止して非水電解質二次電池を作製した。なお、電極群を外装体に収容する際、正極リードおよび負極リードの一部は、それぞれ、外装体より外部に露出させた。
（５）評価
　実施例および比較例で得られた非水電解質二次電池について、下記の評価を行った。
（ａ）初期の直流抵抗値（ＤＣＩＲ）
　２５℃の温度環境において、電池を０．３Ｉｔの電流で電圧が４．２Ｖになるまで定電流充電し、その後、４．２Ｖの定電圧で電流が０．０５Ｉｔになるまで定電圧充電した。次いで、０．３Ｉｔの定電流で１００分間放電し、充電状態（Ｓｔａｔｅ　ｏｆ　ｃｈａｒｇｅ：ＳＯＣ）を５０％にした。
　ＳＯＣ５０％の電池に対して、０Ａ、０．１Ａ、０．５Ａおよび１．０Ａのそれぞれの電流値で１０秒間放電したときの電圧値を測定した。放電の電流値と１０秒後の電圧値との関係を最小二乗法で直線に近似したときの傾きの絶対値からＤＣＩＲ（初期のＤＣＩＲ）を算出した。
（ｂ）充放電サイクル試験
　４５℃の環境温度において、電池を０．５Ｉｔの定電流で電圧が４．２Ｖになるまで定電流充電し、その後、４．２Ｖの定電圧で電流が０．０２Ｉｔになるまで定電圧充電した。次いで、０．５Ｉｔの定電流で電圧が３．０Ｖになるまで定電流放電を行った。この充電および放電を１サイクルとして、２００サイクル繰り返した。
（ｃ）ＤＣＩＲ上昇率（ΔＤＣＩＲ）
　上記（ｂ）の充放電サイクル試験で充放電を２００サイクル繰り返した後の電池を用いる以外は、上記（ａ）の場合と同様にして、ＤＣＩＲ（２００サイクル目のＤＣＩＲ）を算出した。初期のＤＣＩＲに対する２００サイクル後のＤＣＩＲの比率をＤＣＩＲ上昇率として、以下の式により算出した。
　ＤＣＩＲ上昇率（％）＝｛（２００サイクル目のＤＣＩＲ－初期のＤＣＩＲ）／初期のＤＣＩＲ}×１００
（ｄ）容量維持率（ＭＲ）
　上記（ｂ）の充放電サイクル試験において、１サイクル目の放電容量と２００サイクル目の放電容量とを測定し、以下の式により容量維持率を求め、サイクル特性の指標とした。
　容量維持率（％）＝（２００サイクル目の放電容量／１サイクル目の放電容量）×１００
　評価結果を表１に示す。表１中、Ｅ１～Ｅ７は、実施例１～７であり、Ｃ１～Ｃ６は、比較例１～６である。表１中の第１成分（オキサレート化合物）について、Ａ１は、リチウムジフルオロビスオキサレートホスフェートであり、Ａ２は、リチウムテトラフルオロオキサレートホスフェートであり、Ａ３は、リチウムビスオキサレートボレートである。表１中の第２成分（有機ケイ素化合物）について、Ｂ１は、テトラビニルシランであり、Ｂ２は、テトラアリルシランであり、Ｂ３は、ジメチルジビニルシラン、Ｂ４は、テトラメチルシランであり、Ｂ５は、テトラエチルシランである。なお、Ｂ４およびＢ５は、一般式（２）で表される化合物ではない。
Figure JPOXMLDOC01-appb-T000005
  
　Ｃｏを含まない複合酸化物ＮＭＡを用いる場合（Ｃ４）、Ｃｏを相対的に多く含む複合酸化物を用いる場合（Ｃ１）に比べて、ＭＲが２．０％低下し（８６．５％→８４．５％）、ΔＤＣＩＲが１．８％増大した（２２．４％→２４．２％）。
　Ｅ１およびＣ４では、それぞれ、Ｃｏを含まない複合酸化物ＮＭＡを正極活物質に用い、Ｅ１では非水電解質にＡ１を添加し、Ｃ４では非水電解質にＡ１を添加しなかった。Ｅ１では、Ｃ４に対して、ＭＲが３．８％と大幅に上昇し（８４．５％→８８．３％）、ΔＤＣＩＲが５．０％と大幅に低減された（１９．２％→２４．２％）。
　一方、Ｃ１およびＣ２では、それぞれ、Ｃｏを相対的に多く含む複合酸化物を正極活物質に用い、Ｃ２では非水電解質にＡ１を添加し、Ｃ１では非水電解質にＡ１を添加しなかった。Ｃ２では、Ｃ１に対して、ＭＲが０．８％しか上昇せず（８６．５％→８７．３％）、ΔＤＣＩＲも２．２％しか低減されなかった（２２．４％→２０．２％）。
　Ｃｏを含まない複合酸化物ＮＭＡを用いたＥ１では、Ｃｏを相対的に多く含む複合酸化物を用いたＣ２に比べて、非水電解質へのＡ１の添加による効果が顕著に得られた。
　Ｅ１およびＥ２では、それぞれ、Ｃｏを含まない複合酸化物ＮＭＡを正極活物質に用い、Ｅ１では非水電解質にＡ１を添加し、Ｅ２では非水電解質にＡ１およびＢ１を添加した。Ｅ２では、Ｅ１よりも、ＭＲが更に１．５％と大幅に上昇し（８８．３％→８９．８％）、ΔＤＣＩＲが更に低減された（１９．２％→１７．２％）。
　一方、Ｃ４およびＣ５では、それぞれ、Ｃｏを含まない複合酸化物ＮＭＡを正極活物質に用い、Ｃ４では非水電解質にＡ１およびＢ１のいずれも添加せず、Ｃ５では非水電解質にＢ１を添加し、Ａ１を添加しなかった。Ｃ５では、Ｃ４に対して、ＭＲが０．４％しか上昇しなかった（８４．５％→８４．９％）。
　Ｃｏを含まない複合酸化物ＮＭＡを正極活物質に用いる場合、Ａ１とともにＢ１を非水電解質に添加することで、サイクル特性の低下抑制の効果がより顕著に得られた。
　非水電解質にＡ１およびＢ２を添加したＥ３においても、Ｅ１よりも、ＭＲが更に上昇し（８８．３％→８９．１％）、ΔＤＣＩＲが更に低減された（１９．２％→１８．５％）。
　非水電解質にＢ４を添加したＣ３では、非水電解質にＢ４を添加しなかったＣ１に比べて、ＭＲが低下し、ΔＤＣＩＲが増大した。非水電解質にＢ５を添加したＣ６では、非水電解質にＢ５を添加しなかったＣ４に比べて、ＭＲが低下し、ΔＤＣＩＲが増大した。
　また、Ｅ４およびＥ６では、それぞれ、Ｃｏを含まない複合酸化物ＮＭＡを正極活物質に用い、Ｅ４では非水電解質にＡ２を添加し、Ｅ６では非水電解質にＡ３を添加した。Ｅ４およびＥ６においても、Ｅ１の場合と同様に、ＭＲが大幅に上昇し、ΔＤＣＩＲが大幅に低減された。
　非水電解質にＡ２およびＢ１を添加したＥ５では、Ｅ４と比べて、ＭＲが更に上昇し、ΔＤＣＩＲが更に低減された。非水電解質にＡ３およびＢ３を添加したＥ７では、Ｅ６と比べて、ＭＲが更に上昇し、ΔＤＣＩＲが更に低減された。
　本開示に係る非水電解質二次電池は、移動体通信機器、携帯電子機器等の主電源に有用である。また、非水電解質二次電池は、高容量でありながらも、サイクル特性に優れることで、車載用途にも適している。しかし、非水電解質二次電池の用途は、これらに限定されるものではない。
　本発明を現時点での好ましい実施態様に関して説明したが、そのような開示を限定的に解釈してはならない。種々の変形および改変は、上記開示を読むことによって本発明に属する技術分野における当業者には間違いなく明らかになるであろう。したがって、添付の請求の範囲は、本発明の真の精神および範囲から逸脱することなく、すべての変形および改変を包含する、と解釈されるべきものである。
　１：電極群、２：正極リード、３：負極リード、４：電池ケース、５：封口板、６：負極端子、７：ガスケット、８：封栓

Claims (9)

  1. 　正極と、負極と、非水電解質と、を備え、
    　前記正極は、正極活物質を含み、
    　前記正極活物質は、Ｎｉと、Ｍｎと、Ａｌと、を含むリチウム遷移金属複合酸化物を含み、
    　前記リチウム遷移金属複合酸化物に含まれるＬｉ以外の金属元素に占めるＮｉ、ＭｎおよびＡｌの割合が、それぞれ
    　Ｎｉ：５０原子％以上、
    　Ｍｎ：１０原子％以下、および
    　Ａｌ：１０原子％以下
    であり、
    　前記リチウム遷移金属複合酸化物がＣｏを含む場合、Ｌｉ以外の金属元素に占めるＣｏの割合が１．５原子％以下であり、
    　前記非水電解質は、オキサレート化合物を含み、
    　前記オキサレート化合物は、リチウムカチオンと、オキサレート錯体のアニオンと、を含む、非水電解質二次電池。
  2. 　前記リチウム遷移金属複合酸化物は、下記式：
    　ＬｉαＮｉ（１－ｘ１－ｘ２－ｙ－ｚ）Ｃｏｘ１Ｍｎｘ２ＡｌｙＭｅｚＯ２＋β
    で表され、式中、
    　０．９５≦α≦１．０５、
    　０．６８５≦１－ｘ１－ｘ２－ｙ－ｚ≦０．９５、
    　０≦ｘ１≦０．０１５、
    　０＜ｘ２≦０．１、
    　０＜ｙ≦０．１、
    　０≦ｚ≦０．１、および
    　－０．０５≦β≦０．０５
    を満たし、
    　Ｍｅは、Ｌｉ、Ｎｉ、Ｍｎ、Ａｌ、Ｃｏ、および酸素以外の元素である、請求項１に記載の非水電解質二次電池。
  3. 　前記元素Ｍｅが、Ｔｉ、Ｚｒ、Ｎｂ、Ｍｏ、Ｗ、Ｆｅ、Ｚｎ、Ｂ、Ｓｉ、Ｍｇ、Ｃａ、Ｓｒ、Ｓｃ、およびＹからなる群より選択された少なくとも１種である、請求項２に記載の非水電解質二次電池。
  4. 　前記オキサレート化合物は、一般式（１）：
    Figure JPOXMLDOC01-appb-C000001
     で表される化合物を含み、一般式（１）中、
    　Ｍは、ＰまたはＢであり、
    　ＭがＰである場合、ｎは１～３の整数であり、ｍ＝６－２ｎを満たし、
    　ＭがＢである場合、ｎは１または２であり、ｍ＝４－２ｎを満たす、
    請求項１～３のいずれか１項に記載の非水電解質二次電池。
  5. 　前記オキサレート化合物は、リチウムジフルオロビスオキサレートホスフェート、リチウムテトラフルオロオキサレートホスフェート、リチウムトリスオキサレートホスフェート、リチウムビスオキサレートボレート、およびリチウムジフルオロオキサレートボレートからなる群より選択された少なくとも１種を含む、請求項４に記載の非水電解質二次電池。
  6. 　前記非水電解質中の前記オキサレート化合物の含有量は、３質量％以下である、請求項１～５のいずれか１項に記載の非水電解質二次電池。
  7. 　前記非水電解質は、更に、一般式（２）：
    Figure JPOXMLDOC01-appb-C000002
     で表される有機ケイ素化合物を含み、一般式（２）中、
    　Ｒ１～Ｒ４は、それぞれ独立して、アルキル基、アルケニル基、アルキニル基、またはアルコキシ基であり、かつ、
    　Ｒ１～Ｒ４の少なくとも１つは、アルケニル基またはアルキニル基である、
    請求項１～６のいずれか１項に記載の非水電解質二次電池。
  8. 　前記有機ケイ素化合物は、テトラビニルシラン、テトラアリルシラン、およびジメチルジビニルシランからなる群より選択された少なくとも１種を含む、請求項７に記載の非水電解質二次電池。
  9. 　前記非水電解質中の前記有機ケイ素化合物の含有量は、１．５質量％以下である、請求項７または８に記載の非水電解質二次電池。
PCT/JP2022/022083 2021-06-30 2022-05-31 非水電解質二次電池 Ceased WO2023276527A1 (ja)