AT524697A1 - THERMOPLASTIC ELASTOMER COMPOSITION - Google Patents
THERMOPLASTIC ELASTOMER COMPOSITION Download PDFInfo
- Publication number
- AT524697A1 AT524697A1 ATA50012/2021A AT500122021A AT524697A1 AT 524697 A1 AT524697 A1 AT 524697A1 AT 500122021 A AT500122021 A AT 500122021A AT 524697 A1 AT524697 A1 AT 524697A1
- Authority
- AT
- Austria
- Prior art keywords
- thermoplastic elastomer
- polymer
- elastomer composition
- amorphous
- process oil
- Prior art date
Abstract
Die Erfindung betrifft eine thermoplastische Elastomerzusammensetzung, enthaltend trans-Polynorbornen (PNR), zumindest ein Prozessöl und/oder Harz und zumindest ein amorphes und/oder teilkristallines Polymer, sowie deren Herstellung und Verwendung.The invention relates to a thermoplastic elastomer composition containing trans-polynorbornene (PNR), at least one process oil and/or resin and at least one amorphous and/or partially crystalline polymer, and the production and use thereof.
Description
Die Erfindung betrifft eine thermoplastische Elastomerzusammensetzung, ein Verfahren zu deren Herstellung sowie deren Verwendung zur Herstellung von The invention relates to a thermoplastic elastomer composition, a process for its production and its use for the production of
Dämpfungselementen. damping elements.
Dämpfungselemente werden in vielen Sparten der Technik benötigt. So kommen sie beispielsweise bei der Lagerung von verschiedensten mechanischen Teilen zum Einsatz, ebenso wie zur Dämpfung von Vibrationen, zum Schutz vor äußerer Damping elements are required in many branches of technology. For example, they are used to store a wide variety of mechanical parts, as well as to dampen vibrations and protect against external influences
Krafteinwirkung oder auch zur Reduktion von schallbedingten Vibrationen. force or to reduce noise-induced vibrations.
Diese Dämpfungselemente sind üblicherweise aus einem vulkanisierten Elastomer hergestellt, das mithilfe von Vernetzungsmitteln beispielsweise in einer Presse geformt und vernetzt wird. Diese Herstellung ist aufgrund des notwendigen Baus von zumeist beheizbaren Pressformen kostenintensiv, zudem sind keine These damping elements are usually made of a vulcanized elastomer, which is shaped and crosslinked using crosslinking agents, for example in a press. This production is cost-intensive due to the necessary construction of mostly heatable press molds, and there are none
kontinuierliche Fertigung und damit hohe Durchsätze möglich. continuous production and thus high throughput possible.
Daher werden für eine kostengünstige Fertigung von Dämpfungselementen thermoplastische Elastomere (TPE) eingesetzt, bei welchen als Polymerbasis üblicherweise Styrol-Butadien-Kautschuke (E-SBR, S-SBR), Acrylnitrilkautschuk, Naturkautschuk, Butadienkautschuk oder auch Sonderkautschuke eingesetzt werden. Diese Materialien weisen jedoch üblicherweise nur in einem geringen Temperaturbereich tatsächlich auch die gewünschten absorbierenden Dämpfungseigenschaften auf und verlieren diese insbesondere bei Raumtemperatur und höheren Gebrauchstemperaturen. For this reason, thermoplastic elastomers (TPE) are used for cost-effective production of damping elements, in which styrene-butadiene rubber (E-SBR, S-SBR), acrylonitrile rubber, natural rubber, butadiene rubber or special rubbers are usually used as the polymer basis. However, these materials usually only actually have the desired absorbing damping properties in a small temperature range and lose these properties in particular at room temperature and higher usage temperatures.
In der EP 3 042 929 B1 des Anmelders ist eine Gummimischungszusammensetzung aus trans-Polynorbornen und Silikonkautschuk für den Einsatz als AntiVibrationsbauelement beschrieben, das peroxidisch vernetzt wird. Dieses Material mit hervorragenden Dämpfungseigenschaften über einen weiten Temperaturbereich The applicant's EP 3 042 929 B1 describes a rubber mixture composition of trans-polynorbornene and silicone rubber for use as an anti-vibration component, which is crosslinked peroxide. This material with excellent damping properties over a wide temperature range
ist jedoch für eine thermoplastische Verarbeitung ungeeignet. however, is unsuitable for thermoplastic processing.
In der US 4,203,884 A ist eine thermoplastische Zusammensetzung basierend auf Polynorbornen beschrieben, das mit kristallinen Polyolefinen, insbesondere Polyethylen oder Polypropylen zur Senkung der Glasübergangstemperatur versetzt und anschließend vulkanisiert wird. Die in diesem Stand der Technik beschriebenen US Pat. No. 4,203,884 A describes a thermoplastic composition based on polynorbornene to which crystalline polyolefins, in particular polyethylene or polypropylene, are added to lower the glass transition temperature and then vulcanized. Those described in this prior art
thermoplastischen Zusammensetzungen haben den Nachteil, dass sie nur über thermoplastic compositions have the disadvantage that they only over
einen geringen Verlustfaktor tan ö und damit nur über mäßige Dämpfungseigenschaften verfügen. Der Verlustfaktor tan 6 stellt einen wesentlichen Parameter in der dynamisch-mechanischen Analyse (DMA) von Kunststoffen dar. Je höher der Verlustfaktor ist, desto besser sind die Dämpfungseigenschaften des getesteten Materials. have a low loss factor tan ö and therefore only moderate damping properties. The dissipation factor tan 6 represents an essential parameter in the dynamic mechanical analysis (DMA) of plastics. The higher the dissipation factor, the better the damping properties of the tested material.
Es ist daher Aufgabe der Erfindung, eine thermoplastische Elastomerzusammensetzung zur Verfügung zu stellen, die über herausragende Dämpfungseigenschaften verfügt und eine kostengünstige Verarbeitung mittels Spritzgussverfahren bzw. vergleichbarer Technologien erlaubt. It is therefore the object of the invention to provide a thermoplastic elastomer composition which has outstanding damping properties and allows cost-effective processing by means of injection molding processes or comparable technologies.
Diese Aufgabe wird erfindungsgemäß durch eine thermoplastische Elastomerzusammensetzung, enthaltend trans-Polynorbornen (PNR), zumindest ein Prozessöl und/oder Harz und zumindest ein amorphes und/oder teilamorphes Polymer gelöst. Bei dieser Elastomerzusammensetzung handelt es sich um einen sogenannten Polymerblend, also eine Mischung (Compound) von zwei oder mehr Polymeren, wobei keine chemischen Bindungen zwischen den Polymeren vorhanden sind. Lediglich die physikalisch wirkenden Dipol-Bindungskräfte von transPolynorbornen unterstützen die erzielbare Festigkeit des erfindungsgemäßen Polymerblends. According to the invention, this object is achieved by a thermoplastic elastomer composition containing trans-polynorbornene (PNR), at least one process oil and/or resin and at least one amorphous and/or partially amorphous polymer. This elastomer composition is what is known as a polymer blend, i.e. a mixture (compound) of two or more polymers, with no chemical bonds between the polymers. Only the physically acting dipole binding forces of transpolynorbornene support the achievable strength of the polymer blend according to the invention.
Ein wesentlicher Vorteil der erfindungsgemäßen Zusammensetzung besteht darin, dass durch geeignete Auswahl der Ausgangsstoffe, insbesondere der Wahl des amorphen und/oder teilkristallinen Polymers, der verschiedenen Materialkomponenten mit unterschiedlichen Glasübergangstemperaturen in Kombination mit trans-Polynorbornen eine Verarbeitung mittels Spritzguss bzw. vergleichbarer Fertigungstechnologien ermöglicht wird. Es werden hierbei thermoplastische und elastische Materialien erhalten, die aufgrund der Verwendung von amorphen oder teilkristallinen Polymeren eine verbesserte Absorption von Stoß- und Vibrationsenergie gegenüber herkömmlichen Thermoplasten aufweisen. Diese verbesserten Eigenschaften bleiben über einen weiten Temperaturbereich, An essential advantage of the composition according to the invention is that a suitable selection of the starting materials, in particular the selection of the amorphous and/or semi-crystalline polymer, of the various material components with different glass transition temperatures in combination with trans-polynorbornene enables processing by means of injection molding or comparable production technologies. In this way, thermoplastic and elastic materials are obtained which, due to the use of amorphous or partially crystalline polymers, have improved absorption of impact and vibration energy compared to conventional thermoplastics. These improved properties remain over a wide temperature range,
insbesondere auch bei Kälte erhalten. especially preserved in the cold.
Unter amorphen Polymeren werden im allgemeinen Polymere verstanden, die über keine kristallinen Strukturen verfügen, vielmehr liegen die Polymerketten als knäuelartige Struktur vor. Diese gemäß der Erfindung in der trans-Polynorbornen-Amorphous polymers are generally understood to mean polymers that do not have any crystalline structures; rather, the polymer chains are present as a tangle-like structure. This according to the invention in the trans-polynorbornene
Matrix vorliegenden Polymerknäuel haben einen wesentlichen Einfluss auf die Matrix present polymer balls have a significant impact on the
verbesserten Dämpfungseigenschaften der erfindungsgemäßen thermoplastischen improved damping properties of the thermoplastic according to the invention
Elastomerzusammensetzung. elastomer composition.
So wird bei der jeweiligen Gebrauchstemperatur ein hoher Verlustfaktor tan ö >0,3, vorzugsweise >1 erhalten, woraus sich eine hohe Stoßenergieabsorption bzw. hohe Vibrationsdämpfung ergibt. Die Einstellung des Gebrauchstemperaturbereichs erfolgt durch geeignete Auswahl der Polymermischung, nämlich der Wahl des zumindest einen Prozessöls und/oder Harzes sowie des zumindest einen amorphen bzw. teilkristallinen Polymers. Ebenso lassen sich dadurch auch mechanische Eigenschaften, insbesondere die Festigkeit und Steifigkeit des Materials sowie die A high loss factor tan δ >0.3, preferably >1, is thus obtained at the respective service temperature, resulting in high impact energy absorption and high vibration damping. The service temperature range is set by suitable selection of the polymer mixture, namely the selection of the at least one process oil and/or resin and the at least one amorphous or partially crystalline polymer. This also allows mechanical properties, in particular the strength and stiffness of the material and the
Härte in einem Bereich von 10 bis 95 Shore A einstellen. Set the hardness in a range from 10 to 95 Shore A.
Besonders gute Dämpfungseigenschaften des Materials werden erzielt, wenn die erfindungsgemäße thermoplastische Elastomerzusammensetzung zumindest ein Prozessöl enthält, das je nach gewünschter Gebrauchstemperatur aromatisch, paraffinisch oder naphthenisch ist. Particularly good damping properties of the material are achieved if the thermoplastic elastomer composition according to the invention contains at least one process oil which is aromatic, paraffinic or naphthenic, depending on the desired service temperature.
So hat sich insbesondere der Polymerblend NSX 100 RAE, einem transPolynorbornen in Kombination mit dem Prozessöl RAE (refinded aromatic extract) (ein Produkt der ASTRON Development & Production sro) als besonders geeignetes Ausgangsmaterial für die Herstellung eines Dämpfungselements mithilfe eines klassischen Spritzgussverfahrens erwiesen, wenn er mit zumindest einem amorphen und/oder teilkristallinen Polymer compoundiert wird, das vorzugsweise Ethylen-Vinylacetat-Copolymer (EVAC), Polyvinylchlorid (PVC), Acrylnitril-ButadienKautschuk (NBR), und/oder besonders bevorzugt ein Cycloolefin-Polymer (COP) und/oder ein Cycloolefin-Copolymer (COC) enthält. In particular, the polymer blend NSX 100 RAE, a transpolynorbornene in combination with the process oil RAE (refinded aromatic extract) (a product of ASTRON Development & Production sro) has proven to be a particularly suitable starting material for the production of a damping element using a classic injection molding process if it is compounded with at least one amorphous and/or partially crystalline polymer, which is preferably ethylene-vinyl acetate copolymer (EVAC), polyvinyl chloride (PVC), acrylonitrile-butadiene rubber (NBR), and/or particularly preferably a cycloolefin polymer (COP) and/or contains a cycloolefin copolymer (COC).
In einer alternativen Ausführung der Erfindung ist zumindest teilweise das amorphe und/oder teilkristalline Polymer durch einen Styrol-Butadien-Kautschuk (SBR) ersetzt. Damit wird eine erfindungsgemäße thermoplastische Elastomerzusammensetzung erhalten, die annähernd die gleichen dämpfenden und mechanischen Eigenschaften wie ohne den Zusatz von SBR aufweist, jedoch In an alternative embodiment of the invention, the amorphous and/or partially crystalline polymer is at least partially replaced by a styrene-butadiene rubber (SBR). A thermoplastic elastomer composition according to the invention is thus obtained which has approximately the same damping and mechanical properties as without the addition of SBR, however
kostengünstiger herzustellen ist. is cheaper to produce.
In weiteren Ausführungen der Erfindung enthält die erfindungsgemäße thermoplastische Elastomerzusammensetzung weitere Zusatzstoffe, die die mechanischen und/oder chemischen Eigenschaften der Zusammensetzung, In further embodiments of the invention, the thermoplastic elastomer composition according to the invention contains further additives which improve the mechanical and/or chemical properties of the composition,
insbesondere auch deren Beständigkeit gegen Umwelteinflüsse, weiter verbessern. Hierbei kommen insbesondere Lichtstabilisatoren, UV-Stabilisatoren, Weichmacher, Antioxidantien und Füllstoffe, insbesondere silanisierte Kieselsäure oder Ruß zum in particular their resistance to environmental influences. Light stabilizers, UV stabilizers, plasticizers, antioxidants and fillers, in particular silanized silica or carbon black, come into play here
Einsatz. Mission.
Die Aufgabe wird des Weiteren durch ein Verfahren zur Herstellung eines thermoplastischen Elastomers auf Basis von trans-Polynorbornen in Form eines Polymerblends gelöst, wobei trans-Polynorbornen mit zumindest einem Prozessöl und/oder Harz sowie mit zumindest einem amorphen oder teilkristallinen Polymer compoundiert wird. Dieser Polymerblend kann nachfolgend granuliert oder als Endloshalbzeug anschließend auf einer konventionellen Spritzgussanlage oder The object is also achieved by a method for producing a thermoplastic elastomer based on trans-polynorbornene in the form of a polymer blend, wherein trans-polynorbornene is compounded with at least one process oil and/or resin and with at least one amorphous or partially crystalline polymer. This polymer blend can then be granulated or as a continuous semi-finished product on a conventional injection molding system or
mittels vergleichbarer Fertigungstechnologie verarbeitet werden. be processed using comparable manufacturing technology.
Eine besonders bevorzugte thermoplastische Elastomerzusammensetzung gemäß der Erfindung wird erhalten, wenn das Massenverhältnis von trans-Polynorbornen mit zumindest einem Prozessöl und/oder Harz zum zumindest ein amorphes oder teilkristallinen Polymer 1:10 bis 10:1 beträgt. Die aus derart erhaltenen Zusammensetzungen hergestellten Dämpfungselemente weisen ein A particularly preferred thermoplastic elastomer composition according to the invention is obtained when the mass ratio of trans-polynorbornene with at least one process oil and/or resin to at least one amorphous or partially crystalline polymer is 1:10 to 10:1. The damping elements produced from compositions obtained in this way have a
ausgezeichnetes Dämpfungsverhalten auf. excellent damping behavior.
Um die Beständigkeit und/oder Verarbeitbarkeit der erfindungsgemäßen thermoplastischen Elastomerzusammensetzung zu verbessern, ist vorzugsweise vorgesehen, dass dem Polymerblend zusätzlich zumindest ein Additiv, das aus einer Gruppe ausgewählt ist, die Lichtstabilisatoren, UV-Stabilisatoren, Weichmacher, Antioxidantien und Füllstoffe, insbesondere silanisierte Kieselsäure oder Ruß enthält, zugesetzt wird. In order to improve the stability and / or processability of the thermoplastic elastomer composition according to the invention, it is preferably provided that the polymer blend also has at least one additive selected from a group consisting of light stabilizers, UV stabilizers, plasticizers, antioxidants and fillers, in particular silanized silica or contains carbon black is added.
Eine verbesserte Homogenität der thermoplastischen Elastomerzusammensetzung wird erhalten, wenn die Herstellung des Polymerblends zweistufig erfolgt, wobei in einem ersten Compoundierungsschritt trans-Polynorbornen mit zumindest einem Prozessöl und/oder Harz vermischt wird, um einen ersten Polymerblend zu erhalten, und der erste Polymerblend aus dem ersten Verblendungsschritt mit zumindest einem amorphen oder teilkristallinen Polymer in einem zweiten Compoundierungsschritt vermischt wird, um einen zweiten Polymerblend zu erhalten. Hierbei können gegebenenfalls zusätzliche Additive während des ersten und/oder zweiten Compoundierungsschritt zugefügt werden. Improved homogeneity of the thermoplastic elastomer composition is obtained when the polymer blend is produced in two stages, with trans-polynorbornene being mixed with at least one process oil and/or resin in a first compounding step to obtain a first polymer blend, and the first polymer blend from the first Blending step is mixed with at least one amorphous or semi-crystalline polymer in a second compounding step to obtain a second polymer blend. If necessary, additional additives can be added here during the first and/or second compounding step.
Der erfindungsgemäße Polymerblend hat sich insbesondere zur Herstellung von Dämpfungselementen im Spritzgussverfahren bewährt. Diese Dämpfungselemente sind in weiten Bereichen einsetzbar, beispielsweise für die Herstellung von Protektoren für den Sportbereich, Vibrationsdämpfer für Präzisionsmaschinen, geräuschdämmende Elemente beispielsweise in der Automobilindustrie, The polymer blend according to the invention has proven itself in particular for the production of damping elements in the injection molding process. These damping elements can be used in a wide range of areas, for example for the production of protectors for the sports sector, vibration dampers for precision machines, noise-damping elements for example in the automotive industry,
Dämpfungselemente in der Tontechnik, speziell für Kopfhörer, und vieles mehr. Dampening elements in audio engineering, especially for headphones, and much more.
Im Folgenden wird anhand von nicht-einschränkenden Ausführungsbeispielen die The following is based on non-limiting embodiments
Erfindung näher erläutert. Invention explained in more detail.
In der nachfolgenden Tabelle 1 sind fünf unterschiedliche Polymerblends auf Basis von trans-Polynorbornen dargestellt, während in Tabelle 2 deren Table 1 below shows five different polymer blends based on trans-polynorbornene, while Table 2 shows them
Materialeigenschaften angeführt sind. Material properties are listed.
Als Ausgangsmaterial wurde jeweils NSX RAE 100, ein kommerziell erhältliches Produkt der ASTRON Development & Production sro verwendet. Hierbei handelt es sich um einen Polymerblend aus trans-Polynorbornen mit einem aromatischen Prozessöl (RAE, refinded aromatic extract) im Verhältnis 1:100. Dieser erste Polymerblend wird anschließend auf an sich bekannte Weise mit einem der In each case, NSX RAE 100, a commercially available product from ASTRON Development & Production sro, was used as the starting material. This is a polymer blend of trans-polynorbornene with an aromatic process oil (RAE, refinded aromatic extract) in a ratio of 1:100. This first polymer blend is then in a conventional manner with one of
nachfolgenden amorphen bzw. teilkristallinen Polymere compoundiert. subsequent amorphous or semi-crystalline polymers compounded.
TABELLE 1 Batch 1 2 3 4 Ausgangsmaterial [in phr] NSX RAE 100 50 50 50 50 TABLE 1 Batch 1 2 3 4 Feedstock [in phr] NSX RAE 100 50 50 50 50
(ASTRON DEVELOPMENT & PRODUCTION SRO) (ASTRON DEVELOPMENT & PRODUCTION SRO)
Polymer 2 [in phr] Polymer 2 [phr]
COC E140 50 (TOPAS ADVANCED POLYMERS GMBH) COC E140 50 (TOPAS ADVANCED POLYMERS GMBH)
Levaprene 800 HV [EVAC] 50 (ARLANXEO PERFORMANCE ELASTOMERS) Levaprene 800 HV [EVAC] 50 (ARLANXEO PERFORMANCE ELASTOMERS)
PVC 50 (SOLVIN GMBH & CO. KG) PVC 50 (SOLVIN GMBH & CO. KG)
Kumho KNB40M [NBR] 50 (KUMHO Südkorea) Kumho KNB40M [NBR] 50 (KUMHO South Korea)
Additive in [phr] Additives in [phr]
Antilux 3 3 3 3 Antilux 3 3 3 3
Antioxidant 2 2 2 2 Antioxidant 2 2 2 2
Eisenoxid blk 2 2 2 2 TABELLE 2 Iron oxide blk 2 2 2 2 TABLE 2
Batch 1 2 3 4 Batch 1 2 3 4
Härte Shore A 55 35 25 27 Hardness Shore A 55 35 25 27
Elastizität bei 7 8 17 15 Elasticity at 7 8 17 15
Raumtemperatur [%] Room temperature [%]
Kalkulatorischer Tg 54 14 52 2 Imputed Tg 54 14 52 2
Hierbei korrelieren die kalkulatorischen Glasübergangstemperaturen Tg mit den Untersuchungsergebnissen mittels dynamisch-mechanischer Analyse (DMA). The calculated glass transition temperatures Tg correlate with the test results using dynamic mechanical analysis (DMA).
Untersuchungen des Anmelders haben ergeben, dass eine thermoplastische Elastomerzusammensetzung basierend auf trans-Polynorbornen und Nitrilkautschuk sowie hydriertem Nitrilkautschuk eine besonders hohe Beständigkeit gegen Säuren und Basen aufweist, während ein Polymerblend mit EVAC, oder auch mit PVC, Investigations by the applicant have shown that a thermoplastic elastomer composition based on trans-polynorbornene and nitrile rubber as well as hydrogenated nitrile rubber has a particularly high resistance to acids and bases, while a polymer blend with EVAC, or with PVC,
gemäß der Erfindung ein thermoplastisches Elastomer liefert, das über eine according to the invention provides a thermoplastic elastomer which has a
verbesserte Beständigkeit gegen UV-Bestrahlung und Ozon verfügt. improved resistance to UV radiation and ozone.
Insbesondere Polymerblends mit COP oder COC gemäß der Erfindung stellen thermoplastisch verarbeitbare Elastomere zur Verfügung, die über ausgezeichnete stoß- und vibrationshemmende Eigenschaften verfügen. So weisen derartige Materialien beispielsweise durch entsprechende Materialkombinationen zwei Dämpfungspeaks bei unterschiedlichen Temperaturen auf, sodass sie über einen weiten Temperaturbereich über gute bis ausgezeichnete Dämpfungseigenschaften In particular, polymer blends with COP or COC according to the invention provide thermoplastically processable elastomers which have excellent impact and vibration-inhibiting properties. Such materials, for example, have two damping peaks at different temperatures due to appropriate material combinations, so that they have good to excellent damping properties over a wide temperature range
verfügen. feature.
In der nachfolgenden Tabelle 3 wurden die Materialeigenschaften einer herkömmlichen vulkanisierten Gummimischung A basierend von Polynorbornen mit der Bezeichnung A-XOC® der Firma D-NOV GmbH (HG3 Sarl) mit einer erfindungsgemäßen thermoplastischen Elastomerzusammensetzung B verglichen. Die Elastomerzusammensetzung B ist ein Polymerblend mit folgenden Table 3 below compares the material properties of a conventional vulcanized rubber mixture A based on polynorbornene with the designation A-XOC® from D-NOV GmbH (HG3 Sarl) with a thermoplastic elastomer composition B according to the invention. Elastomer Composition B is a polymer blend having the following
Bestandteilen: components:
trans-Polynorbornen: 70 Prozessöl RAE: 70 COC: 100 Kieselsäure: 30 Silane: 3 Ozon-Alterungsschutz: 4 UV-Schutz: 3 Gesamt: 280 trans-polynorbornene: 70 process oil RAE: 70 COC: 100 silica: 30 silanes: 3 ozone anti-aging: 4 UV protection: 3 total: 280
Es wurden aus beiden Polymerblends A und B Dämpfungselemente für Gelenksprotektoren gefertigt und ihre Materialeigenschaften analysiert. Eine Prüfung nach EN 1621-1 ergibt eine 10-15% verbesserte Schutzleistung für jene Gelenksprotektoren, die aus dem erfindungsgemäßen thermoplastisch Damping elements for joint protectors were made from both polymer blends A and B and their material properties were analyzed. A test according to EN 1621-1 shows a 10-15% improved protective performance for those joint protectors made from the thermoplastic according to the invention
verarbeitbaren Elastomer gefertigt wurden. processable elastomer were manufactured.
TABELLE 3 Mischung A Mischung B Härte in Shore A 35 40 Dichte 1,04 1,02 [g/mm3] Transmitted Force 16 14 [kN; gemäß EN 1621-1] Heiz-Kühlzeit/Produkt 12,5 0,8 TABLE 3 Mixture A Mixture B Hardness in Shore A 35 40 Density 1.04 1.02 [g/mm3] Transmitted Force 16 14 [kN; according to EN 1621-1] heating-cooling time/product 12.5 0.8
[min] [minutes]
Ein signifikanter Unterschied dieser beiden Mischungen besteht jedoch auch in deren Verarbeitungszeit: Vulkanisierte Mischungen wie die Gummimischung A auf Basis von Polynorbornen, benötigen eine lange Vulkanisationszeit (12 min) mit anschließender Kühlzeit (2,5 min), somit eine Gesamtzykluszeit von 12,5 min, der eine geringe Kühlzeit des Polymerblends B (0,8 min) für das gleiche Produkt gegenübersteht. Durch die Verwendung einer marktüblichen, vollautomatisierten Kunststoffspritzmaschine beträgt der Output an Produkten bis zum 15-fachen einer Vulkanisationspresse bzw. das 3-fache im Vergleich zu einer GummiInjektionsmaschine. Zudem sind die Anschaffungskosten für Maschinen und Formen, bedingt durch die erforderlichen Temperaturen und Drücke beim A significant difference between these two compounds is their processing time: Vulcanized compounds such as rubber compound A based on polynorbornene require a long vulcanization time (12 minutes) followed by a cooling time (2.5 minutes), resulting in a total cycle time of 12.5 minutes , which contrasts with the short cooling time of polymer blend B (0.8 min) for the same product. By using a commercially available, fully automated plastic injection molding machine, the product output is up to 15 times that of a vulcanization press or 3 times that of a rubber injection machine. In addition, the acquisition costs for machines and molds are due to the temperatures and pressures required
vernetzenden Gummispritzverfahren (Mischung A) wesentlich höher. cross-linked rubber spraying process (mixture A) is significantly higher.
Ähnliche Materialwerte in einer kostengünstigen thermoplastischen Elastomerzusammensetzung werden erhalten, wenn das COC (z.B. COC E140)bis zu 70% seines Gewichts durch SBR 1712 ersetzt wird. Similar material values in a low cost thermoplastic elastomer composition are obtained if the COC (e.g. COC E140) is replaced by SBR 1712 up to 70% of its weight.
Damit erlaubt die erfindungsgemäße thermoplastische Elastomerzusammensetzung The thermoplastic elastomer composition according to the invention thus allows
eine kostengünstige Herstellung von Dämpfungselementen, die über ausgezeichnete Dämpfungseigenschaften verfügen. a cost-effective production of damping elements that have excellent damping properties.
Claims (1)