AT64186B

AT64186B - Hammerable aluminum and lead containing zinc alloys.

Info

Publication number: AT64186B
Authority: AT
Inventors: Thomas Abraham Bayliss; Byron George Clark
Original assignee: Thomas Abraham Bayliss; Byron George Clark
Priority date: 1911-05-23
Filing date: 1912-05-18
Publication date: 1914-03-26

Description

  

   <Desc/Clms Page number 1> 
 



  Hämmerbare aluminium-und bleihaltige Zinklegierungen. 



   Den Gegenstand der vorliegenden Erfindung bilden aluminium- und bleihaltige Zinklegierungen, welche hämmerbar sind. Der Erfindung gemäss enthalten diese Legierungen in fertigem Zustande die Bestandteile innerhalb der nachstehenden Grenzwerte : 
 EMI1.1 
 
<tb> 
<tb> Zink <SEP> .... <SEP> 99-100 <SEP> bis <SEP> 99.9%
<tb> Aluminium <SEP> 0.001 <SEP> ,, <SEP> 0.9%,
<tb> Blei <SEP> 0-010", <SEP> 0-9%.
<tb> 
 
 EMI1.2 
 wie folgt dar :

   Technisch reines (raffiniertes) Zink und Blei werden in einem Tiegel oder Ofen geschmolzen, und zwar, um eine Oxydation zu verhindern, unter   Luftabschluss.   Die Temperatur wird auf   3Ö0   bis 4500 C gebracht und auf   dieser Höhe   gehalten,   um   das Zink und Blei zu schmelzen, worauf das Aluminium in festem oder geschmolzenem Zustande (entweder rein oder in legierter Form) der gewünschten Zusammensetzung gemäss   hinzugefügt   wird. Wenn das Aluminium sich in der Masse gleichmässig verteilt hat, die einzelnen Bestandteile geschmolzen, innig miteinander   vermischt   und sohin zum (lu6 bereit 
 EMI1.3 
   ! 50   bis   200"C) erreicht   ist, dem ersten   Walzprozess   unterworfen.

   Hiebei werden Bleche von entsprechender   Grosse   hergestellt,   wekhe   man alsdann in einem geeignet eingerichteten   und geheizten Ofen bei einer Temperatur von 200 bis 250 C ausglüht. Dieses Ausgluhen,   das erforderlichen Falles   wiederholt wtrd, gtbt   die notlgt'Hitze für das nachfolgende Aus- 
 EMI1.4 
 operation unter ahnlichen Bedingungen. 



   Das in dieser   Weise erhaltene Metall   ist ausserordentitch zah und fest,   hammerbar   
 EMI1.5 
 Langen bis zu 30 bis   HO M,   je nach dem   praktischen Bedarf, ausgewalzt werden. the   Legierung kann   dm   einzelnen Bestandteile in allen Verhältnissen innerhalb der eingangs 
 EMI1.6 
 
 EMI1.7 
 
<tb> 
<tb> Zink <SEP> 99 <SEP> 85%.
<tb> 



  Aluminium. <SEP> 0-100/.
<tb> 



  Blet <SEP> ... <SEP> 0.05%.
<tb> 
 
 EMI1.8 
 bis 0.9% und Blei 0.01 bis 0.9% enthalten. 

**WARNUNG** Ende DESC Feld kannt Anfang CLMS uberlappen**.



   <Desc / Clms Page number 1>
 



  Hammerable aluminum and lead containing zinc alloys.



   The present invention relates to zinc alloys containing aluminum and lead, which can be hammered. According to the invention, these alloys contain the components within the following limit values in the finished state:
 EMI1.1
 
<tb>
<tb> zinc <SEP> .... <SEP> 99-100 <SEP> to <SEP> 99.9%
<tb> aluminum <SEP> 0.001 <SEP> ,, <SEP> 0.9%,
<tb> lead <SEP> 0-010 ", <SEP> 0-9%.
<tb>
 
 EMI1.2
 as follows:

   Technically pure (refined) zinc and lead are melted in a crucible or furnace, in order to prevent oxidation, in the absence of air. The temperature is brought to 30 ° to 4500 ° C. and maintained at this level to melt the zinc and lead, after which the aluminum is added in solid or molten state (either pure or in alloyed form) according to the desired composition. When the aluminum has been evenly distributed in the mass, the individual components are melted, intimately mixed with one another and so ready for (lu6
 EMI1.3
   ! 50 to 200 "C) is reached, subjected to the first rolling process.

   Here, sheets of the appropriate size are produced, which are then annealed in a suitably equipped and heated furnace at a temperature of 200 to 250 C. This annealing, which is repeated if necessary, provides the necessary heat for the subsequent
 EMI1.4
 operation under similar conditions.



   The metal obtained in this way is extraordinarily tough and strong, hammerable
 EMI1.5
 Lengths of up to 30 to HO M, depending on practical needs, can be rolled out. The alloy can dm the individual components in all proportions within the input
 EMI1.6
 
 EMI1.7
 
<tb>
<tb> zinc <SEP> 99 <SEP> 85%.
<tb>



  Aluminum. <SEP> 0-100 /.
<tb>



  Blet <SEP> ... <SEP> 0.05%.
<tb>
 
 EMI1.8
 up to 0.9% and lead 0.01 to 0.9%.

** WARNING ** End of DESC field may overlap beginning of CLMS **.

Claims

2. 1, alloy according to claim 1, containing 99.85% zinc, 0.1% aluminum and 0.05% lead. ** WARNING ** End of CLMS field may overlap beginning of DESC **.