ATE194857T1 - Chromatfreie oxidüberzüge auf aluminiumgegenständen - Google Patents

Chromatfreie oxidüberzüge auf aluminiumgegenständen

Info

Publication number
ATE194857T1
ATE194857T1 AT91103498T AT91103498T ATE194857T1 AT E194857 T1 ATE194857 T1 AT E194857T1 AT 91103498 T AT91103498 T AT 91103498T AT 91103498 T AT91103498 T AT 91103498T AT E194857 T1 ATE194857 T1 AT E194857T1
Authority
AT
Austria
Prior art keywords
cobalt
solution
conversion coating
hexavalent complex
iii hexavalent
Prior art date
Application number
AT91103498T
Other languages
English (en)
Inventor
Mathias P Schriever
Original Assignee
Boeing Co
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Boeing Co filed Critical Boeing Co
Application granted granted Critical
Publication of ATE194857T1 publication Critical patent/ATE194857T1/de

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01G—COMPOUNDS CONTAINING METALS NOT COVERED BY SUBCLASSES C01D OR C01F
    • C01G51/00—Compounds of cobalt
    • C01G51/20—Complexes with ammonia
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C22/00—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals
    • C23C22/05—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals using aqueous solutions
    • C23C22/06—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals using aqueous solutions using aqueous acidic solutions with pH less than 6
    • C23C22/48—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals using aqueous solutions using aqueous acidic solutions with pH less than 6 not containing phosphates, hexavalent chromium compounds, fluorides or complex fluorides, molybdates, tungstates, vanadates or oxalates
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C22/00—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals
    • C23C22/05—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals using aqueous solutions
    • C23C22/06—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals using aqueous solutions using aqueous acidic solutions with pH less than 6
    • C23C22/48—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals using aqueous solutions using aqueous acidic solutions with pH less than 6 not containing phosphates, hexavalent chromium compounds, fluorides or complex fluorides, molybdates, tungstates, vanadates or oxalates
    • C23C22/56—Treatment of aluminium or alloys based thereon
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C22/00—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals
    • C23C22/05—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals using aqueous solutions
    • C23C22/60—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals using aqueous solutions using alkaline aqueous solutions with pH greater than 8
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C22/00—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals
    • C23C22/05—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals using aqueous solutions
    • C23C22/60—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals using aqueous solutions using alkaline aqueous solutions with pH greater than 8
    • C23C22/66—Treatment of aluminium or alloys based thereon
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C22/00—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals
    • C23C22/05—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals using aqueous solutions
    • C23C22/68—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals using aqueous solutions using aqueous solutions with pH between 6 and 8
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C22/00—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals
    • C23C22/82—After-treatment
    • C23C22/83—Chemical after-treatment
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/26—Web or sheet containing structurally defined element or component, the element or component having a specified physical dimension
    • Y10T428/263—Coating layer not in excess of 5 mils thick or equivalent
    • Y10T428/264—Up to 3 mils
    • Y10T428/265—1 mil or less

Landscapes

  • Chemical & Material Sciences (AREA)
  • Organic Chemistry (AREA)
  • General Chemical & Material Sciences (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Engineering & Computer Science (AREA)
  • Materials Engineering (AREA)
  • Mechanical Engineering (AREA)
  • Metallurgy (AREA)
  • Inorganic Chemistry (AREA)
  • Chemical Treatment Of Metals (AREA)
AT91103498T 1990-05-17 1991-03-07 Chromatfreie oxidüberzüge auf aluminiumgegenständen ATE194857T1 (de)

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
US07/525,800 US5298092A (en) 1990-05-17 1990-05-17 Non-chromated oxide coating for aluminum substrates

Publications (1)

Publication Number Publication Date
ATE194857T1 true ATE194857T1 (de) 2000-08-15

Family

ID=24094649

Family Applications (1)

Application Number Title Priority Date Filing Date
AT91103498T ATE194857T1 (de) 1990-05-17 1991-03-07 Chromatfreie oxidüberzüge auf aluminiumgegenständen

Country Status (8)

Country Link
US (3) US5298092A (de)
EP (1) EP0458020B1 (de)
JP (1) JP3194593B2 (de)
AT (1) ATE194857T1 (de)
DE (1) DE69132326T2 (de)
DK (1) DK0458020T3 (de)
ES (1) ES2148141T3 (de)
GR (1) GR3034635T3 (de)

Families Citing this family (41)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5551994A (en) * 1990-05-17 1996-09-03 The Boeing Company Non-chromated oxide coating for aluminum substrates
CA2087473C (en) * 1990-05-17 2001-10-16 Matthias P. Schriever Non-chromated oxide coating for aluminum substrates
US5411606A (en) * 1990-05-17 1995-05-02 The Boeing Company Non-chromated oxide coating for aluminum substrates
US5298092A (en) * 1990-05-17 1994-03-29 The Boeing Company Non-chromated oxide coating for aluminum substrates
US5468307A (en) * 1990-05-17 1995-11-21 Schriever; Matthias P. Non-chromated oxide coating for aluminum substrates
US5472524A (en) * 1990-05-17 1995-12-05 The Boeing Company Non-chromated cobalt conversion coating method and coated articles
DE69126507T2 (de) * 1990-11-30 1997-09-25 Boeing Co Chromatfreier Kobalt-Konversionsüberzug
ES2125231T3 (es) * 1991-07-19 1999-03-01 Boeing Co Revestimientos de oxido no cromado para sustratos de aluminio.
MY111371A (en) * 1992-06-25 1999-12-31 Boeing Co Non-chromated oxide coating for aluminum substrates.
CN1138873C (zh) * 1992-06-25 2004-02-18 波音公司 在金属基体上形成钴转化膜层的方法，钴转化镀膜液及其用途
RU2130977C1 (ru) * 1993-01-19 1999-05-27 Дзе Боинг Компани Способ формирования оксидного кобальтового конверсионного покрытия и водный химический раствор для получения оксидного кобальтового конверсионного покрытия
WO1996021753A1 (en) * 1995-01-13 1996-07-18 Henkel Corporation Composition and process for forming a solid adherent protective coating on metal surfaces
US5948178A (en) * 1995-01-13 1999-09-07 Henkel Corporation Composition and process for forming a solid adherent protective coating on metal surfaces
AR001268A1 (es) * 1995-03-22 1997-10-08 Henkel Corp Procedimiento para formar un recubrimiento protector adherente solido sobre superficies metalicas.
US6059867A (en) * 1995-10-10 2000-05-09 Prc-Desoto International, Inc. Non-chromate corrosion inhibitors for aluminum alloys
EP0859872B1 (de) * 1995-10-10 2002-06-19 Prc-Desoto International, Inc. Nichtchromatische korrosionsinhibitoren für aluminiumlegierungen
US5866652A (en) * 1996-02-27 1999-02-02 The Boeing Company Chromate-free protective coatings
US5940729A (en) * 1996-04-17 1999-08-17 International Business Machines Corp. Method of planarizing a curved substrate and resulting structure
FR2752851B1 (fr) * 1996-09-02 1998-11-13 Cfpi Ind Bain et procede de phosphatation de substrats metalliques, concentre pour la preparation de ce bain et substrats metalliques traites a l'aide de ces bain et procede
US5873953A (en) * 1996-12-26 1999-02-23 The Boeing Company Non-chromated oxide coating for aluminum substrates
US6315823B1 (en) 1998-05-15 2001-11-13 Henkel Corporation Lithium and vanadium containing sealing composition and process therewith
DE19834394A1 (de) * 1998-07-30 2000-02-03 Rheinmetall W & M Gmbh Waffenrohr mit einer verschleißmindernden Hartchromschicht
US6432225B1 (en) 1999-11-02 2002-08-13 The Boeing Company Non-chromated oxide coating for aluminum substrates
AU2002361689A1 (en) * 2002-01-04 2003-07-30 University Of Dayton Non-toxic corrosion protection pigments based on cobalt
US7235142B2 (en) * 2002-01-04 2007-06-26 University Of Dayton Non-toxic corrosion-protection rinses and seals based on cobalt
US7294211B2 (en) 2002-01-04 2007-11-13 University Of Dayton Non-toxic corrosion-protection conversion coats based on cobalt
US6946078B2 (en) * 2002-02-27 2005-09-20 Lynntech, Inc. Electrochemical method and apparatus for producing and separating ferrate (VI) compounds
US7045051B2 (en) * 2002-02-27 2006-05-16 Lynntech, Inc. Electrochemical method for producing ferrate(VI) compounds
US20030221590A1 (en) * 2003-01-13 2003-12-04 Sturgill Jeffrey A. Non-toxic corrosion-protection pigments based on permanganates and manganates
US20040011252A1 (en) * 2003-01-13 2004-01-22 Sturgill Jeffrey A. Non-toxic corrosion-protection pigments based on manganese
US7090112B2 (en) * 2003-08-29 2006-08-15 The Boeing Company Method and sealant for joints
US6905060B2 (en) * 2003-10-24 2005-06-14 The Boeing Company Method and sealant for weld joints
US20050282003A1 (en) * 2004-06-18 2005-12-22 Alexander Mayzel Coated article and process for coating article with anticorrosive finish
US7732033B2 (en) * 2005-08-26 2010-06-08 The Curators Of The University Of Missouri Sealants for structural member joints and methods of using same
CN101384751B (zh) * 2006-02-14 2013-01-02 汉高股份及两合公司 在金属表面上使用的原地干燥的三价铬抗腐蚀涂料的组合物与方法
EP2044239B1 (de) * 2006-05-10 2014-09-03 Henkel AG & Co. KGaA Verfahren zur herstellung einer korrosionsbeständigen metalloberflächenbeschichtung unter verwendung einer verbesserten dreiwertigen chromhaltigen zusammensetzung
US20110005287A1 (en) * 2008-09-30 2011-01-13 Bibber Sr John Method for improving light gauge building materials
US11072712B2 (en) 2011-06-08 2021-07-27 Henkel Ag & Co. Kgaa Corrosion resistant sol-gel coating and composition and process for making the same
CA2808981A1 (en) * 2013-03-05 2014-09-05 Sherritt International Corporation Method of recovering metals while mitigating corrosion
US10156016B2 (en) 2013-03-15 2018-12-18 Henkel Ag & Co. Kgaa Trivalent chromium-containing composition for aluminum and aluminum alloys
CN111218172B (zh) 2020-01-23 2022-07-19 广东省建筑科学研究院集团股份有限公司 一种从源头消除重金属铬和VOCs污染的复合涂层及制备方法

Family Cites Families (50)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US1551613A (en) * 1923-03-07 1925-09-01 Aluminum Co Of America Coated aluminum articles and process and means for producing same
US1607676A (en) * 1924-10-29 1926-11-23 Firm Dr Otto Sprenger Patentve Process for obtaining metal coatings on articles of aluminum and aluminum alloys
DE745704C (de) * 1941-04-18 1944-12-06 Verfahren zur Herstellung glasklarer und farbloser Oxydschichten auf Aluminium und seinen Legierungen
US2906009A (en) * 1954-04-30 1959-09-29 Siemens Ag High temperature-resisting insulating coatings of increased durability and methods of producing same
US2796370A (en) * 1955-03-04 1957-06-18 Charles W Ostrander Composition and method for producing corrosion resistant protective coating on aluminum and aluminum alloys
US2796371A (en) * 1955-03-16 1957-06-18 Allied Res Products Inc Corrosion resistant protective coating on aluminum and aluminum alloys
NL283192A (de) * 1961-09-14
US3138479A (en) * 1961-12-20 1964-06-23 Burroughs Corp Method for the electroless deposition of high coercive magnetic film
US3403035A (en) * 1964-06-24 1968-09-24 Process Res Company Process for stabilizing autocatalytic metal plating solutions
US3423214A (en) * 1965-06-30 1969-01-21 Ibm Magnetic cobalt and cobalt alloy plating bath and process
US3438798A (en) * 1965-08-23 1969-04-15 Arp Inc Electroless plating process
US3592747A (en) * 1966-08-17 1971-07-13 Samuel L Cohn & Charles C Cohn Method of forming a decorative and protective coating on a surface
US3444007A (en) * 1967-03-13 1969-05-13 Hooker Chemical Corp Process of forming paint-base coatings on zinc and zinc alloy surfaces
US3615740A (en) * 1970-02-02 1971-10-26 Pennwalt Corp Chromate conversion coating compositions containing prusside accelerator
US3790453A (en) * 1971-03-22 1974-02-05 Lockheed Aircraft Corp Corrosion protected anodized aluminum surfaces
US3870607A (en) * 1971-04-21 1975-03-11 Avco Corp Bearing Manufacture
US3819424A (en) * 1971-06-17 1974-06-25 Oxy Metal Finishing Corp Method and composition for treating metal surfaces
US3954510A (en) * 1972-10-18 1976-05-04 Diamond Shamrock Corporation Metal treating compositions of controlled pH
US3928237A (en) * 1972-11-17 1975-12-23 Robert E Davis Method of catalyst preparation for use in suppressing hydrocarbon and carbon monoxide emission from internal combustion engines
GB1345868A (en) * 1973-02-14 1974-02-06 Rca Corp Electroless cobalt plating bath
US3877981A (en) * 1973-04-30 1975-04-15 Rca Corp Method of electroless plating
US3905838A (en) * 1974-04-10 1975-09-16 Hikaru Ito Bath for treating aluminum and aluminum alloys to form oxide film nonelectrolytically thereon and method for the treatment
US3993510A (en) * 1975-05-21 1976-11-23 The United States Of America As Represented By The Secretary Of The Navy Thixotropic chemical conversion material for corrosion protection of aluminum and aluminum alloys
CA1057108A (en) * 1975-08-06 1979-06-26 Vernon L. Bissonette Process of bleaching silver images to form dye images
JPS53104301A (en) * 1977-02-22 1978-09-11 Ricoh Kk Treating solution for lithographic printing
US4150172A (en) * 1977-05-26 1979-04-17 Kolk Jr Anthony J Method for producing a square loop magnetic media for very high density recording
US4218240A (en) * 1979-05-14 1980-08-19 Gte Products Corporation Method for producing cobaltic hexammine compounds and cobalt metal powder
US4233063A (en) * 1979-05-14 1980-11-11 Gte Products Corporation Process for producing cobalt powder
AU526731B2 (en) * 1979-12-28 1983-01-27 Matsushita Electric Industrial Co., Ltd. Method for making a selective absorption film for solar energy
US4278477A (en) * 1980-03-19 1981-07-14 Amchem Products, Inc. Metal treatment
US4278463A (en) * 1980-03-28 1981-07-14 Gte Products Corporation Process for recovering cobalt
US4261766A (en) * 1980-06-13 1981-04-14 Early California Industries, Inc. Method for inhibiting fatigue of aluminum
US4392920A (en) * 1981-06-10 1983-07-12 The United States Of America As Represented By The Administrator Of The National Aeronautics And Space Administration Method of forming oxide coatings
JPS581076A (ja) * 1981-06-26 1983-01-06 Nisshin Steel Co Ltd Ｌｎｇ又はｌｐｇタンク用高ニッケル―鉄合金鋼板の表面処理方法
US4348224A (en) * 1981-09-10 1982-09-07 Gte Products Corporation Method for producing cobalt metal powder
US4381203A (en) * 1981-11-27 1983-04-26 Amchem Products, Inc. Coating solutions for zinc surfaces
US4637374A (en) * 1982-09-08 1987-01-20 Sharp Kabushiki Kaisha Selective absorption film of a solar heat collector
US4659605A (en) * 1984-05-16 1987-04-21 Richardson Chemical Company Electroless deposition magnetic recording media process and products produced thereby
US4631093A (en) * 1984-07-27 1986-12-23 Tre Corporation Chromate free method of treating metal substrates to impart corrosion resistance and color to the substrate surface
US4647347A (en) * 1984-08-16 1987-03-03 Amchen Products, Inc. Process and sealant compositions for sealing anodized aluminum
JPS61238979A (ja) * 1985-04-15 1986-10-24 Kobe Steel Ltd 着色亜鉛合金めつき鋼板の製造方法
US4897129A (en) * 1986-05-12 1990-01-30 The Lea Manufacturing Company Corrosion resistant coating
US4804407A (en) * 1988-05-13 1989-02-14 Gte Products Corporation Method for recovering cobalt from hexammine cobaltic (111) solutions
JPH0730458B2 (ja) * 1988-08-08 1995-04-05 日本パーカライジング株式会社 亜鉛又は亜鉛系めっき材料の黒色化処理方法
BR8903960A (pt) * 1988-08-08 1990-03-20 Nihon Parkerizing Processo para tratamento de uma superficie de zinco
JPH0331484A (ja) * 1989-06-27 1991-02-12 Nippon Parkerizing Co Ltd 亜鉛または亜鉛系メッキ材料の黒色化処理法
JPH03226584A (ja) * 1990-01-30 1991-10-07 Nippon Parkerizing Co Ltd 亜鉛系めっき鋼板用表面処理液及び表面処理方法
US5298092A (en) * 1990-05-17 1994-03-29 The Boeing Company Non-chromated oxide coating for aluminum substrates
DE69126507T2 (de) * 1990-11-30 1997-09-25 Boeing Co Chromatfreier Kobalt-Konversionsüberzug
ES2125231T3 (es) * 1991-07-19 1999-03-01 Boeing Co Revestimientos de oxido no cromado para sustratos de aluminio.

Also Published As

Publication number Publication date
JPH04231478A (ja) 1992-08-20
DE69132326D1 (de) 2000-08-24
US5298092A (en) 1994-03-29
EP0458020A1 (de) 1991-11-27
GR3034635T3 (en) 2001-01-31
ES2148141T3 (es) 2000-10-16
DE69132326T2 (de) 2001-05-03
DK0458020T3 (da) 2000-10-30
JP3194593B2 (ja) 2001-07-30
EP0458020B1 (de) 2000-07-19
US5415687A (en) 1995-05-16
US5487949A (en) 1996-01-30

Similar Documents

Publication Publication Date Title
ATE194857T1 (de) Chromatfreie oxidüberzüge auf aluminiumgegenständen
ES2104655T3 (es) Revestimiento de conversion de cobalto exento de cromato.
NO945026L (no) Fremgangsmåte ved fremstilling av et koboltbasert belegg på et aluminiumsubstrat
US4263059A (en) Coating solutions of trivalent chromium for coating zinc and cadmium surfaces
DE69130502D1 (de) Nicht-chromatierte Oxidüberzüge für Aluminiumsubstrate
CA2087473A1 (en) Non-chromated oxide coating for aluminum substrates
US4278477A (en) Metal treatment
US5294266A (en) Process for a passivating postrinsing of conversion layers
JP2003166074A (ja) 亜鉛及び亜鉛合金めっき上に六価クロムフリー防錆皮膜を形成するための処理溶液、六価クロムフリー防錆皮膜及びその形成方法。
US4670066A (en) Process for the treatment by chemical conversion of substrates of zinc or of one of its alloys, concentrate and bath used for performing this process
CA2019810A1 (en) Surface blackening treatment for zinciferous surfaces
GB1461244A (en) Treatment of metal surfaces with trivalent chromium solutions
CA2018631C (en) Process for a passivating postrinsing of phosphate layers
MY110203A (en) Non-chromated oxide coating for aluminium substrates
Schriever Non-chromated oxide coating for aluminum substrates
Schriever Non-chromated cobalt conversion coating
RU93004412A (ru) Нехромированное окисное покрытие для алюминиевых подложек

Legal Events

Date Code Title Description
UEP Publication of translation of european patent specification
EELA Cancelled due to lapse of time