ATE413930T1 - Materialien mit niedriger dielektrizitätskonstante und herstellungsverfahren dafür - Google Patents

Materialien mit niedriger dielektrizitätskonstante und herstellungsverfahren dafür

Info

Publication number
ATE413930T1
ATE413930T1 AT07012503T AT07012503T ATE413930T1 AT E413930 T1 ATE413930 T1 AT E413930T1 AT 07012503 T AT07012503 T AT 07012503T AT 07012503 T AT07012503 T AT 07012503T AT E413930 T1 ATE413930 T1 AT E413930T1
Authority
AT
Austria
Prior art keywords
low
porogen
materials
dielectricity
silica
Prior art date
Application number
AT07012503T
Other languages
English (en)
Inventor
Martha Collins
Lisa Deis
John Kirner
James Macdougall
Brian Peterson
Scott Weigel
Original Assignee
Air Prod & Chem
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Air Prod & Chem filed Critical Air Prod & Chem
Application granted granted Critical
Publication of ATE413930T1 publication Critical patent/ATE413930T1/de

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C18/00—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating
    • C23C18/02—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating by thermal decomposition
    • C23C18/12—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating by thermal decomposition characterised by the deposition of inorganic material other than metallic material
    • C23C18/1204—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating by thermal decomposition characterised by the deposition of inorganic material other than metallic material inorganic material, e.g. non-oxide and non-metallic such as sulfides, nitrides based compounds
    • C23C18/1208—Oxides, e.g. ceramics
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C18/00—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating
    • C23C18/02—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating by thermal decomposition
    • C23C18/12—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating by thermal decomposition characterised by the deposition of inorganic material other than metallic material
    • C23C18/125—Process of deposition of the inorganic material
    • C23C18/1262—Process of deposition of the inorganic material involving particles, e.g. carbon nanotubes [CNT], flakes
    • C23C18/127—Preformed particles
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C18/00—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating
    • C23C18/14—Decomposition by irradiation, e.g. photolysis, particle radiation or by mixed irradiation sources
    • C23C18/143—Radiation by light, e.g. photolysis or pyrolysis
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C18/00—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating
    • C23C18/14—Decomposition by irradiation, e.g. photolysis, particle radiation or by mixed irradiation sources
    • C23C18/145—Radiation by charged particles, e.g. electron beams or ion irradiation
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01B—CABLES; CONDUCTORS; INSULATORS; SELECTION OF MATERIALS FOR THEIR CONDUCTIVE, INSULATING OR DIELECTRIC PROPERTIES
    • H01B3/00—Insulators or insulating bodies characterised by the insulating materials; Selection of materials for their insulating or dielectric properties
    • H01B3/18—Insulators or insulating bodies characterised by the insulating materials; Selection of materials for their insulating or dielectric properties mainly consisting of organic substances
    • H01B3/30—Insulators or insulating bodies characterised by the insulating materials; Selection of materials for their insulating or dielectric properties mainly consisting of organic substances plastics; resins; waxes
    • H01B3/46—Insulators or insulating bodies characterised by the insulating materials; Selection of materials for their insulating or dielectric properties mainly consisting of organic substances plastics; resins; waxes silicones
    • H—ELECTRICITY
    • H10—SEMICONDUCTOR DEVICES; ELECTRIC SOLID-STATE DEVICES NOT OTHERWISE PROVIDED FOR
    • H10P—GENERIC PROCESSES OR APPARATUS FOR THE MANUFACTURE OR TREATMENT OF DEVICES COVERED BY CLASS H10
    • H10P14/00—Formation of materials, e.g. in the shape of layers or pillars
    • H10P14/60—Formation of materials, e.g. in the shape of layers or pillars of insulating materials
    • H10P14/65—Formation of materials, e.g. in the shape of layers or pillars of insulating materials characterised by treatments performed before or after the formation of the materials
    • H10P14/6516—Formation of materials, e.g. in the shape of layers or pillars of insulating materials characterised by treatments performed before or after the formation of the materials of treatments performed after formation of the materials
    • H10P14/6536—Formation of materials, e.g. in the shape of layers or pillars of insulating materials characterised by treatments performed before or after the formation of the materials of treatments performed after formation of the materials by exposure to radiation, e.g. visible light
    • H10P14/6539—Formation of materials, e.g. in the shape of layers or pillars of insulating materials characterised by treatments performed before or after the formation of the materials of treatments performed after formation of the materials by exposure to radiation, e.g. visible light by exposure to corpuscular radiation, e.g. exposure to electrons, alpha-particles, protons or ions
    • H—ELECTRICITY
    • H10—SEMICONDUCTOR DEVICES; ELECTRIC SOLID-STATE DEVICES NOT OTHERWISE PROVIDED FOR
    • H10P—GENERIC PROCESSES OR APPARATUS FOR THE MANUFACTURE OR TREATMENT OF DEVICES COVERED BY CLASS H10
    • H10P14/00—Formation of materials, e.g. in the shape of layers or pillars
    • H10P14/60—Formation of materials, e.g. in the shape of layers or pillars of insulating materials
    • H10P14/63—Formation of materials, e.g. in the shape of layers or pillars of insulating materials characterised by the formation processes
    • H10P14/6326—Deposition processes
    • H10P14/6328—Deposition from the gas or vapour phase
    • H10P14/6334—Deposition from the gas or vapour phase using decomposition or reaction of gaseous or vapour phase compounds, i.e. chemical vapour deposition
    • H10P14/6336—Deposition from the gas or vapour phase using decomposition or reaction of gaseous or vapour phase compounds, i.e. chemical vapour deposition in the presence of a plasma [PECVD]
    • H—ELECTRICITY
    • H10—SEMICONDUCTOR DEVICES; ELECTRIC SOLID-STATE DEVICES NOT OTHERWISE PROVIDED FOR
    • H10P—GENERIC PROCESSES OR APPARATUS FOR THE MANUFACTURE OR TREATMENT OF DEVICES COVERED BY CLASS H10
    • H10P14/00—Formation of materials, e.g. in the shape of layers or pillars
    • H10P14/60—Formation of materials, e.g. in the shape of layers or pillars of insulating materials
    • H10P14/63—Formation of materials, e.g. in the shape of layers or pillars of insulating materials characterised by the formation processes
    • H10P14/6326—Deposition processes
    • H10P14/6342—Liquid deposition, e.g. spin-coating, sol-gel techniques or spray coating
    • H—ELECTRICITY
    • H10—SEMICONDUCTOR DEVICES; ELECTRIC SOLID-STATE DEVICES NOT OTHERWISE PROVIDED FOR
    • H10P—GENERIC PROCESSES OR APPARATUS FOR THE MANUFACTURE OR TREATMENT OF DEVICES COVERED BY CLASS H10
    • H10P14/00—Formation of materials, e.g. in the shape of layers or pillars
    • H10P14/60—Formation of materials, e.g. in the shape of layers or pillars of insulating materials
    • H10P14/66—Formation of materials, e.g. in the shape of layers or pillars of insulating materials characterised by the type of materials
    • H10P14/665—Porous materials
    • H—ELECTRICITY
    • H10—SEMICONDUCTOR DEVICES; ELECTRIC SOLID-STATE DEVICES NOT OTHERWISE PROVIDED FOR
    • H10P—GENERIC PROCESSES OR APPARATUS FOR THE MANUFACTURE OR TREATMENT OF DEVICES COVERED BY CLASS H10
    • H10P14/00—Formation of materials, e.g. in the shape of layers or pillars
    • H10P14/60—Formation of materials, e.g. in the shape of layers or pillars of insulating materials
    • H10P14/66—Formation of materials, e.g. in the shape of layers or pillars of insulating materials characterised by the type of materials
    • H10P14/668—Formation of materials, e.g. in the shape of layers or pillars of insulating materials characterised by the type of materials the materials being characterised by the deposition precursor materials
    • H10P14/6681—Formation of materials, e.g. in the shape of layers or pillars of insulating materials characterised by the type of materials the materials being characterised by the deposition precursor materials the precursor containing a compound comprising Si
    • H10P14/6684—Formation of materials, e.g. in the shape of layers or pillars of insulating materials characterised by the type of materials the materials being characterised by the deposition precursor materials the precursor containing a compound comprising Si the compound comprising silicon and oxygen
    • H10P14/6686—Formation of materials, e.g. in the shape of layers or pillars of insulating materials characterised by the type of materials the materials being characterised by the deposition precursor materials the precursor containing a compound comprising Si the compound comprising silicon and oxygen the compound being a molecule comprising at least one silicon-oxygen bond and the compound having hydrogen or an organic group attached to the silicon or oxygen, e.g. a siloxane
    • H—ELECTRICITY
    • H10—SEMICONDUCTOR DEVICES; ELECTRIC SOLID-STATE DEVICES NOT OTHERWISE PROVIDED FOR
    • H10P—GENERIC PROCESSES OR APPARATUS FOR THE MANUFACTURE OR TREATMENT OF DEVICES COVERED BY CLASS H10
    • H10P14/00—Formation of materials, e.g. in the shape of layers or pillars
    • H10P14/60—Formation of materials, e.g. in the shape of layers or pillars of insulating materials
    • H10P14/69—Inorganic materials
    • H10P14/692—Inorganic materials composed of oxides, glassy oxides or oxide-based glasses
    • H10P14/6921—Inorganic materials composed of oxides, glassy oxides or oxide-based glasses containing silicon
    • H10P14/6922—Inorganic materials composed of oxides, glassy oxides or oxide-based glasses containing silicon the material containing Si, O and at least one of H, N, C, F or other non-metal elements, e.g. SiOC, SiOC:H or SiONC
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/31504—Composite [nonstructural laminate]
    • Y10T428/31652—Of asbestos
    • Y10T428/31663—As siloxane, silicone or silane

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Materials Engineering (AREA)
  • Organic Chemistry (AREA)
  • Metallurgy (AREA)
  • Mechanical Engineering (AREA)
  • General Chemical & Material Sciences (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Physics & Mathematics (AREA)
  • Thermal Sciences (AREA)
  • Inorganic Chemistry (AREA)
  • Health & Medical Sciences (AREA)
  • Toxicology (AREA)
  • Ceramic Engineering (AREA)
  • Spectroscopy & Molecular Physics (AREA)
  • Nanotechnology (AREA)
  • Formation Of Insulating Films (AREA)
  • Internal Circuitry In Semiconductor Integrated Circuit Devices (AREA)
  • Inorganic Insulating Materials (AREA)
AT07012503T 2003-04-01 2004-03-26 Materialien mit niedriger dielektrizitätskonstante und herstellungsverfahren dafür ATE413930T1 (de)

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
US10/404,195 US20050260420A1 (en) 2003-04-01 2003-04-01 Low dielectric materials and methods for making same

Publications (1)

Publication Number Publication Date
ATE413930T1 true ATE413930T1 (de) 2008-11-15

Family

ID=32850585

Family Applications (1)

Application Number Title Priority Date Filing Date
AT07012503T ATE413930T1 (de) 2003-04-01 2004-03-26 Materialien mit niedriger dielektrizitätskonstante und herstellungsverfahren dafür

Country Status (7)

Country Link
US (1) US20050260420A1 (de)
EP (3) EP1837086A3 (de)
JP (1) JP4028512B2 (de)
AT (1) ATE413930T1 (de)
DE (1) DE602004017794D1 (de)
SG (1) SG113504A1 (de)
TW (2) TWI299321B (de)

Families Citing this family (51)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US7208389B1 (en) 2003-03-31 2007-04-24 Novellus Systems, Inc. Method of porogen removal from porous low-k films using UV radiation
JP2004307692A (ja) * 2003-04-09 2004-11-04 Shin Etsu Chem Co Ltd 多孔質膜形成用組成物、多孔質膜の製造方法、多孔質膜、層間絶縁膜及び半導体装置
JP2004307693A (ja) * 2003-04-09 2004-11-04 Shin Etsu Chem Co Ltd 多孔質膜形成用組成物、多孔質膜の製造方法、多孔質膜、層間絶縁膜、及び半導体装置
US7253125B1 (en) 2004-04-16 2007-08-07 Novellus Systems, Inc. Method to improve mechanical strength of low-k dielectric film using modulated UV exposure
US9659769B1 (en) 2004-10-22 2017-05-23 Novellus Systems, Inc. Tensile dielectric films using UV curing
JP2006196624A (ja) * 2005-01-12 2006-07-27 Tri Chemical Laboratory Inc 膜形成材料および膜形成方法
US7510982B1 (en) 2005-01-31 2009-03-31 Novellus Systems, Inc. Creation of porosity in low-k films by photo-disassociation of imbedded nanoparticles
US7166531B1 (en) 2005-01-31 2007-01-23 Novellus Systems, Inc. VLSI fabrication processes for introducing pores into dielectric materials
US8889233B1 (en) 2005-04-26 2014-11-18 Novellus Systems, Inc. Method for reducing stress in porous dielectric films
US8454750B1 (en) 2005-04-26 2013-06-04 Novellus Systems, Inc. Multi-station sequential curing of dielectric films
US8980769B1 (en) 2005-04-26 2015-03-17 Novellus Systems, Inc. Multi-station sequential curing of dielectric films
US8282768B1 (en) 2005-04-26 2012-10-09 Novellus Systems, Inc. Purging of porogen from UV cure chamber
US8137465B1 (en) 2005-04-26 2012-03-20 Novellus Systems, Inc. Single-chamber sequential curing of semiconductor wafers
JP4657859B2 (ja) * 2005-09-09 2011-03-23 ローム株式会社 多孔質薄膜の製造方法、多孔質薄膜およびこれを用いた半導体装置
WO2007043205A1 (ja) * 2005-10-14 2007-04-19 Yatabe Massao 照射装置、照射方法及び半導体デバイス
CN101296999A (zh) * 2005-10-28 2008-10-29 东丽株式会社 硅氧烷树脂组合物及其制造方法
JP4949692B2 (ja) * 2006-02-07 2012-06-13 東京応化工業株式会社 低屈折率シリカ系被膜形成用組成物
JP2007251080A (ja) * 2006-03-20 2007-09-27 Fujifilm Corp プラスチック基板の固定方法、回路基板およびその製造方法
US20070232046A1 (en) * 2006-03-31 2007-10-04 Koji Miyata Damascene interconnection having porous low K layer with improved mechanical properties
JP4847231B2 (ja) * 2006-06-29 2011-12-28 ルネサスエレクトロニクス株式会社 電界に起因する剥離物による汚染を防止する装置
JP5380797B2 (ja) * 2006-08-21 2014-01-08 富士通株式会社 半導体デバイスの製造方法
US7851232B2 (en) * 2006-10-30 2010-12-14 Novellus Systems, Inc. UV treatment for carbon-containing low-k dielectric repair in semiconductor processing
US10037905B2 (en) 2009-11-12 2018-07-31 Novellus Systems, Inc. UV and reducing treatment for K recovery and surface clean in semiconductor processing
US8465991B2 (en) 2006-10-30 2013-06-18 Novellus Systems, Inc. Carbon containing low-k dielectric constant recovery using UV treatment
US7906174B1 (en) * 2006-12-07 2011-03-15 Novellus Systems, Inc. PECVD methods for producing ultra low-k dielectric films using UV treatment
WO2008111393A1 (ja) * 2007-03-13 2008-09-18 Kaneka Corporation 中空シリコーン系微粒子と有機高分子とからなる樹脂組成物および層間絶縁膜
US8242028B1 (en) 2007-04-03 2012-08-14 Novellus Systems, Inc. UV treatment of etch stop and hard mask films for selectivity and hermeticity enhancement
US20080254619A1 (en) * 2007-04-14 2008-10-16 Tsang-Jung Lin Method of fabricating a semiconductor device
US8211510B1 (en) 2007-08-31 2012-07-03 Novellus Systems, Inc. Cascaded cure approach to fabricate highly tensile silicon nitride films
US20090093135A1 (en) * 2007-10-04 2009-04-09 Asm Japan K.K. Semiconductor manufacturing apparatus and method for curing material with uv light
US8298965B2 (en) * 2008-09-03 2012-10-30 American Air Liquide, Inc. Volatile precursors for deposition of C-linked SiCOH dielectrics
US9050623B1 (en) 2008-09-12 2015-06-09 Novellus Systems, Inc. Progressive UV cure
US8323521B2 (en) * 2009-08-12 2012-12-04 Tokyo Electron Limited Plasma generation controlled by gravity-induced gas-diffusion separation (GIGDS) techniques
WO2011099768A2 (ko) * 2010-02-09 2011-08-18 서강대학교산학협력단 고온 오존처리를 포함하는 나노기공 초저유전 박막의 제조 방법 및 이에 의해 제조된 나노기공 초저유전 박막
US8932674B2 (en) 2010-02-17 2015-01-13 American Air Liquide, Inc. Vapor deposition methods of SiCOH low-k films
US8491962B2 (en) * 2010-04-02 2013-07-23 National Taiwan University Method for manufacturing a low-k layer
US20120325228A1 (en) * 2011-06-23 2012-12-27 Williams Jonnie R Alkaloid composition for e-cigarette
US20130167461A1 (en) * 2011-12-28 2013-07-04 E. I. Du Pont De Nemours And Company Method for producing metalized fibrous composite sheet with olefin coating
US8741393B2 (en) 2011-12-28 2014-06-03 E I Du Pont De Nemours And Company Method for producing metalized fibrous composite sheet with olefin coating
WO2013142580A1 (en) * 2012-03-20 2013-09-26 Applied Nanotech Holdings, Inc. Application of dielectric layer and circuit traces on heat sink
DE102013107240A1 (de) * 2013-07-09 2015-01-15 Institut Für Verbundwerkstoffe Gmbh Gemisch zur Herstellung von Nanopartikeln aus Siliziumdioxid, Verwendung eines solchen Gemisches, Verfahren zur Herstellung von Nanopartikeln aus Siliziumdioxid, Verwendung von nach dem Verfahren hergestellten Nanopartikeln aus Siliziumdioxid sowie nach dem Verfahren hergestellte Nanopartikel aus Siliziumdioxid
CN104269355A (zh) * 2014-09-05 2015-01-07 京东方科技集团股份有限公司 处理氧化硅的方法,薄膜晶体管的制造方法及薄膜晶体管
US10471052B2 (en) 2015-02-19 2019-11-12 Mymd Pharmaceuticals, Inc. Method of treating addictions to opioids
US9847221B1 (en) 2016-09-29 2017-12-19 Lam Research Corporation Low temperature formation of high quality silicon oxide films in semiconductor device manufacturing
EP3306354B1 (de) * 2016-10-07 2021-12-22 Corporation de L'Ecole Polytechnique de Montreal Artikel mit einer nanolaminatbeschichtung
US11164739B2 (en) * 2018-02-08 2021-11-02 Versum Materials Us, Llc Use of silicon structure former with organic substituted hardening additive compounds for dense OSG films
ES2912801T3 (es) * 2018-04-26 2022-05-27 Kurita Water Ind Ltd Estabilización de composiciones que comprenden hidróxido de trialquilalcanolamina cuaternaria
US11404267B2 (en) * 2019-12-30 2022-08-02 Micron Technology, Inc. Semiconductor structure formation
TWI797640B (zh) 2020-06-18 2023-04-01 法商液態空氣喬治斯克勞帝方法研究開發股份有限公司 基於矽之自組裝單層組成物及使用該組成物之表面製備
US20230386825A1 (en) * 2020-10-20 2023-11-30 Versum Materials Us, Llc Alkoxydisiloxanes and dense organosilica films made therefrom
US20240071817A1 (en) * 2022-08-26 2024-02-29 Applied Materials, Inc. Adhesion improvement between low-k materials and cap layers

Family Cites Families (53)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US104225A (en) * 1870-06-14 John f
US18129A (en) * 1857-09-08 Tube fob steam-pressure gages
US5003178A (en) * 1988-11-14 1991-03-26 Electron Vision Corporation Large-area uniform electron source
US4999397A (en) * 1989-07-28 1991-03-12 Dow Corning Corporation Metastable silane hydrolyzates and process for their preparation
US5010159A (en) * 1989-09-01 1991-04-23 Dow Corning Corporation Process for the synthesis of soluble, condensed hydridosilicon resins containing low levels of silanol
MY113904A (en) * 1995-05-08 2002-06-29 Electron Vision Corp Method for curing spin-on-glass film utilizing electron beam radiation
US6652922B1 (en) * 1995-06-15 2003-11-25 Alliedsignal Inc. Electron-beam processed films for microelectronics structures
US6080526A (en) * 1997-03-24 2000-06-27 Alliedsignal Inc. Integration of low-k polymers into interlevel dielectrics using controlled electron-beam radiation
US6042994A (en) * 1998-01-20 2000-03-28 Alliedsignal Inc. Nanoporous silica dielectric films modified by electron beam exposure and having low dielectric constant and low water content
US6235353B1 (en) * 1998-02-24 2001-05-22 Alliedsignal Inc. Low dielectric constant films with high glass transition temperatures made by electron beam curing
US6054206A (en) * 1998-06-22 2000-04-25 Novellus Systems, Inc. Chemical vapor deposition of low density silicon dioxide films
US6177143B1 (en) * 1999-01-06 2001-01-23 Allied Signal Inc Electron beam treatment of siloxane resins
US6361837B2 (en) * 1999-01-15 2002-03-26 Advanced Micro Devices, Inc. Method and system for modifying and densifying a porous film
US6150232A (en) * 1999-02-05 2000-11-21 Chartered Semiconductor Manufacturing Ltd. Formation of low k dielectric
KR100308213B1 (ko) * 1999-02-12 2001-09-26 윤종용 반도체 장치를 위한 저유전 층간 절연막의 제조 방법
US6207555B1 (en) * 1999-03-17 2001-03-27 Electron Vision Corporation Electron beam process during dual damascene processing
US6204201B1 (en) * 1999-06-11 2001-03-20 Electron Vision Corporation Method of processing films prior to chemical vapor deposition using electron beam processing
US6589889B2 (en) * 1999-09-09 2003-07-08 Alliedsignal Inc. Contact planarization using nanoporous silica materials
US6271146B1 (en) * 1999-09-30 2001-08-07 Electron Vision Corporation Electron beam treatment of fluorinated silicate glass
US6420441B1 (en) * 1999-10-01 2002-07-16 Shipley Company, L.L.C. Porous materials
US6440550B1 (en) * 1999-10-18 2002-08-27 Honeywell International Inc. Deposition of fluorosilsesquioxane films
US6592980B1 (en) * 1999-12-07 2003-07-15 Air Products And Chemicals, Inc. Mesoporous films having reduced dielectric constants
KR100677782B1 (ko) * 2000-01-17 2007-02-05 제이에스알 가부시끼가이샤 절연막 형성용 재료의 제조 방법
US6576300B1 (en) * 2000-03-20 2003-06-10 Dow Corning Corporation High modulus, low dielectric constant coatings
US6558755B2 (en) * 2000-03-20 2003-05-06 Dow Corning Corporation Plasma curing process for porous silica thin film
US6759098B2 (en) * 2000-03-20 2004-07-06 Axcelis Technologies, Inc. Plasma curing of MSQ-based porous low-k film materials
US6913796B2 (en) * 2000-03-20 2005-07-05 Axcelis Technologies, Inc. Plasma curing process for porous low-k materials
US6576568B2 (en) * 2000-04-04 2003-06-10 Applied Materials, Inc. Ionic additives for extreme low dielectric constant chemical formulations
US6495479B1 (en) * 2000-05-05 2002-12-17 Honeywell International, Inc. Simplified method to produce nanoporous silicon-based films
US6271273B1 (en) * 2000-07-14 2001-08-07 Shipley Company, L.L.C. Porous materials
AU2001288954A1 (en) * 2000-09-13 2002-03-26 Shipley Company, L.L.C. Electronic device manufacture
WO2002045145A2 (en) * 2000-11-30 2002-06-06 Shipley Company, L.L.C. Uv-free curing of organic dielectrica
US6583048B2 (en) * 2001-01-17 2003-06-24 Air Products And Chemicals, Inc. Organosilicon precursors for interlayer dielectric films with low dielectric constants
US6355563B1 (en) * 2001-03-05 2002-03-12 Chartered Semiconductor Manufacturing Ltd. Versatile copper-wiring layout design with low-k dielectric integration
DE10112561C2 (de) * 2001-03-15 2003-12-18 Infineon Technologies Ag Verfahren zur Erzeugung von auf einem Substrat haftenden porösen organischen Schichten
US7074489B2 (en) * 2001-05-23 2006-07-11 Air Products And Chemicals, Inc. Low dielectric constant material and method of processing by CVD
US6716770B2 (en) * 2001-05-23 2004-04-06 Air Products And Chemicals, Inc. Low dielectric constant material and method of processing by CVD
US20030211244A1 (en) * 2002-04-11 2003-11-13 Applied Materials, Inc. Reacting an organosilicon compound with an oxidizing gas to form an ultra low k dielectric
US6846515B2 (en) * 2002-04-17 2005-01-25 Air Products And Chemicals, Inc. Methods for using porogens and/or porogenated precursors to provide porous organosilica glass films with low dielectric constants
EP1504138A2 (de) * 2002-05-08 2005-02-09 Applied Materials, Inc. Verfahren zur härtung von filmen niedriger dielektrizitätskonstante mit einem elektronenstrahl
US7060330B2 (en) * 2002-05-08 2006-06-13 Applied Materials, Inc. Method for forming ultra low k films using electron beam
US20040101632A1 (en) * 2002-11-22 2004-05-27 Applied Materials, Inc. Method for curing low dielectric constant film by electron beam
US6936551B2 (en) * 2002-05-08 2005-08-30 Applied Materials Inc. Methods and apparatus for E-beam treatment used to fabricate integrated circuit devices
US7122880B2 (en) * 2002-05-30 2006-10-17 Air Products And Chemicals, Inc. Compositions for preparing low dielectric materials
US7307343B2 (en) * 2002-05-30 2007-12-11 Air Products And Chemicals, Inc. Low dielectric materials and methods for making same
AU2003282988A1 (en) * 2002-10-21 2004-05-13 Massachusetts Institute Of Technology Pecvd of organosilicate thin films
US20040096586A1 (en) * 2002-11-15 2004-05-20 Schulberg Michelle T. System for deposition of mesoporous materials
US7294934B2 (en) * 2002-11-21 2007-11-13 Intel Corporation Low-K dielectric structure and method
US6960327B2 (en) * 2003-01-30 2005-11-01 The Regents Of The University Of California Methods for removing organic compounds from nano-composite materials
US7098149B2 (en) * 2003-03-04 2006-08-29 Air Products And Chemicals, Inc. Mechanical enhancement of dense and porous organosilicate materials by UV exposure
TWI240959B (en) * 2003-03-04 2005-10-01 Air Prod & Chem Mechanical enhancement of dense and porous organosilicate materials by UV exposure
US7030468B2 (en) * 2004-01-16 2006-04-18 International Business Machines Corporation Low k and ultra low k SiCOH dielectric films and methods to form the same
US7060638B2 (en) * 2004-03-23 2006-06-13 Applied Materials Method of forming low dielectric constant porous films

Also Published As

Publication number Publication date
EP1837086A2 (de) 2007-09-26
EP1837086A3 (de) 2007-12-05
DE602004017794D1 (de) 2008-12-24
EP1832351A3 (de) 2007-12-05
SG113504A1 (en) 2005-08-29
TWI299321B (en) 2008-08-01
TW200420493A (en) 2004-10-16
EP1464410A1 (de) 2004-10-06
EP1832351B1 (de) 2008-11-12
TW200640785A (en) 2006-12-01
US20050260420A1 (en) 2005-11-24
JP4028512B2 (ja) 2007-12-26
JP2004312004A (ja) 2004-11-04
EP1832351A2 (de) 2007-09-12

Similar Documents

Publication Publication Date Title
ATE413930T1 (de) Materialien mit niedriger dielektrizitätskonstante und herstellungsverfahren dafür
WO2007017843A3 (en) Hollow silica particles, compositions comprising them, and methods for making same
IL188790A0 (en) Processes for preparing low dielectric films
WO2009093209A3 (ru) 2-AЛKИЛAMИHO-3-APИЛCУЛЬФOHИЛ-ЦИKЛOAЛKAHO [e ИЛИ d] ПИPAЗOЛO [1,5-a] ПИPИMИДИHЫ - АНТАГОНИСТЫ СЕРОТОНИНОВЫХ 5-HT6 РЕЦЕПТОРОВ, СПОСОБЫ ИХ ПОЛУЧЕНИЯ И ПРИМЕНЕНИЯ
MY139520A (en) Porous low dielectric constant compositions and methods for making and using same
EP1122770A3 (de) Isolierender Film auf Basis von SiO2 und seine Herstellung
AU2001233764A1 (en) Stabilizer mixtures for polyolefins
WO2007021508A3 (en) Hollow silica particles and methods for making same
ATE305145T1 (de) Polycyclische derivate zur veränderung der optischen eigenschaften und ätzbeständigkeitseignenschaften
TW200504466A (en) Resist composition and patterning process
TW200640937A (en) Cyclic siloxane compound, material for si-containing film forming, and the use thereof
TW200602301A (en) Fluorine-containing cyclic compound, fluorine-containing polymer compound, resist material using same and method for forming pattern
TW200600971A (en) Calixresorcinarene compounds, photoresist base materials, and compositions thereof
PL2041147T3 (pl) Kompozycja do hydrofobowej obróbki i oszklenia
TW200600962A (en) Top anti-refelctive coating polymer, its preparation method and top anti-reflective coating composition comprising the same
TW200609288A (en) Material and method for forming low-dielectric-constant film
TW200518184A (en) Photoresist composition for EUV and method for forming photoresist pattern using the same
WO2005004221A3 (en) Low-k-dielectric material
TW200504164A (en) Composition for forming porous film and method for forming the same, porous film and method for forming the same, interlevel insulator film, and semiconductor device
CN110952074B (zh) 硅化合物和使用硅化合物沉积膜的方法
DE602005010305D1 (de) Thermoplastische halogenierte polymerzusammensetzung
TW200722927A (en) Fluorinated cyclic structure-bearing silicon compounds and silicon resins, resist compositions using the same, and patterning process
TW200611334A (en) Porous ceramic materials as low-k films in semiconductor devices
TW200725185A (en) Hardmask compositions for resist underlayer films
MXPA03006360A (es) Piperazinilcarbonilquinolinas e-isoquinolinas.

Legal Events

Date Code Title Description
RER Ceased as to paragraph 5 lit. 3 law introducing patent treaties