ATE426686T1 - Hochfestes und kaltgewaltzes stahlblech mit hervorragender verformbarkeit und plattiertes stahlblech - Google Patents

Hochfestes und kaltgewaltzes stahlblech mit hervorragender verformbarkeit und plattiertes stahlblech

Info

Publication number
ATE426686T1
ATE426686T1 AT05008773T AT05008773T ATE426686T1 AT E426686 T1 ATE426686 T1 AT E426686T1 AT 05008773 T AT05008773 T AT 05008773T AT 05008773 T AT05008773 T AT 05008773T AT E426686 T1 ATE426686 T1 AT E426686T1
Authority
AT
Austria
Prior art keywords
steel sheet
cold rolled
less
rolled steel
controlled
Prior art date
Application number
AT05008773T
Other languages
English (en)
Inventor
Shushi Ikeda
Yoichi Mukai
Hiroshi Akamizu
Koichi Makii
Koichi Sugimoto
Shunichi Hashimoto
Kenji Saito
Original Assignee
Kobe Steel Ltd
Shinshu Tlo Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Kobe Steel Ltd, Shinshu Tlo Co Ltd filed Critical Kobe Steel Ltd
Application granted granted Critical
Publication of ATE426686T1 publication Critical patent/ATE426686T1/de

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/02—Ferrous alloys, e.g. steel alloys containing silicon
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/04—Ferrous alloys, e.g. steel alloys containing manganese
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/12—Ferrous alloys, e.g. steel alloys containing tungsten, tantalum, molybdenum, vanadium, or niobium

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Materials Engineering (AREA)
  • Mechanical Engineering (AREA)
  • Metallurgy (AREA)
  • Organic Chemistry (AREA)
  • Heat Treatment Of Sheet Steel (AREA)
  • Coating With Molten Metal (AREA)
AT05008773T 2004-04-22 2005-04-21 Hochfestes und kaltgewaltzes stahlblech mit hervorragender verformbarkeit und plattiertes stahlblech ATE426686T1 (de)

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
JP2004126916 2004-04-22

Publications (1)

Publication Number Publication Date
ATE426686T1 true ATE426686T1 (de) 2009-04-15

Family

ID=34935538

Family Applications (1)

Application Number Title Priority Date Filing Date
AT05008773T ATE426686T1 (de) 2004-04-22 2005-04-21 Hochfestes und kaltgewaltzes stahlblech mit hervorragender verformbarkeit und plattiertes stahlblech

Country Status (4)

Country Link
US (2) US20050247378A1 (de)
EP (1) EP1589126B1 (de)
AT (1) ATE426686T1 (de)
DE (1) DE602005013442D1 (de)

Families Citing this family (26)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP3764411B2 (ja) * 2002-08-20 2006-04-05 株式会社神戸製鋼所 焼付硬化性に優れた複合組織鋼板
US7314532B2 (en) * 2003-03-26 2008-01-01 Kabushiki Kaisha Kobe Seiko Sho (Kobe Steel, Ltd.) High-strength forged parts having high reduction of area and method for producing same
JP4288364B2 (ja) * 2004-12-21 2009-07-01 株式会社神戸製鋼所 伸びおよび伸びフランジ性に優れる複合組織冷延鋼板
CA2531615A1 (en) * 2004-12-28 2006-06-28 Kabushiki Kaisha Kobe Seiko Sho (Kobe Steel, Ltd.) High strength thin steel sheet having high hydrogen embrittlement resisting property
JP4716359B2 (ja) * 2005-03-30 2011-07-06 株式会社神戸製鋼所 均一伸びに優れた高強度冷延鋼板およびその製造方法
JP4716358B2 (ja) * 2005-03-30 2011-07-06 株式会社神戸製鋼所 強度と加工性のバランスに優れた高強度冷延鋼板およびめっき鋼板
EP2679699A3 (de) * 2005-03-31 2014-08-20 Kabushiki Kaisha Kobe Seiko Sho Hochfestes kaltgewalztes Stahlblech und Fahrzeugkomponenten aus Stahl mit ausgezeichneten Eigenschaften der Beschichtungsfilmhaftung, Bearbeitbarkeit und Wasserstoffversprödungswiderstandsfähigkeit
EP1749895A1 (de) * 2005-08-04 2007-02-07 ARCELOR France Herstellungsprozess von Stahlblechen mit hoher Festigkeit und exzellenter Dehnung und hergestellte Produkte
EP1978113B1 (de) 2005-12-06 2018-08-01 Kabushiki Kaisha Kobe Seiko Sho Nach dem verzinken wärmebehandelte stahlbleche mit hoher festigkeit und hervorragender pulverisiserungsbeständigkeit und herstellungsverfahren dafür
GB2439069B (en) * 2006-03-29 2011-11-30 Kobe Steel Ltd High Strength cold-rolled steel sheet exhibiting excellent strength-workability balance and plated steel sheet
CN100510143C (zh) 2006-05-29 2009-07-08 株式会社神户制钢所 延伸凸缘性优异的高强度钢板
JP4974341B2 (ja) * 2006-06-05 2012-07-11 株式会社神戸製鋼所 成形性、スポット溶接性、および耐遅れ破壊性に優れた高強度複合組織鋼板
JP5030200B2 (ja) * 2006-06-05 2012-09-19 株式会社神戸製鋼所 伸び、伸びフランジ性および溶接性に優れた高強度鋼板
JP4164537B2 (ja) * 2006-12-11 2008-10-15 株式会社神戸製鋼所 高強度薄鋼板
EP1990431A1 (de) 2007-05-11 2008-11-12 ArcelorMittal France Verfahren zur Herstellung von kalt gewalzten und geglühten Stahlblechen mit sehr hoher Festigkeit und so hergestellte Bleche
JP5671359B2 (ja) 2010-03-24 2015-02-18 株式会社神戸製鋼所 温間加工性に優れた高強度鋼板
EP2439290B1 (de) 2010-10-05 2013-11-27 ThyssenKrupp Steel Europe AG Mehrphasenstahl, aus einem solchen Mehrphasenstahl hergestelltes kaltgewalztes Flachprodukt und Verfahren zu dessen Herstellung
EP2439291B1 (de) 2010-10-05 2013-11-27 ThyssenKrupp Steel Europe AG Mehrphasenstahl, aus einem solchen Mehrphasenstahl hergestelltes kaltgewalztes Flachprodukt und Verfahren zu dessen Herstellung
JP5662902B2 (ja) 2010-11-18 2015-02-04 株式会社神戸製鋼所 成形性に優れた高強度鋼板、温間加工方法、および温間加工された自動車部品
JP5667472B2 (ja) 2011-03-02 2015-02-12 株式会社神戸製鋼所 室温および温間での深絞り性に優れた高強度鋼板およびその温間加工方法
US9745639B2 (en) 2011-06-13 2017-08-29 Kobe Steel, Ltd. High-strength steel sheet excellent in workability and cold brittleness resistance, and manufacturing method thereof
JP5636347B2 (ja) 2011-08-17 2014-12-03 株式会社神戸製鋼所 室温および温間での成形性に優れた高強度鋼板およびその温間成形方法
JP5860308B2 (ja) 2012-02-29 2016-02-16 株式会社神戸製鋼所 温間成形性に優れた高強度鋼板およびその製造方法
JP5860354B2 (ja) 2012-07-12 2016-02-16 株式会社神戸製鋼所 降伏強度と成形性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
CN104513927B (zh) * 2014-12-19 2017-04-05 宝山钢铁股份有限公司 一种抗拉强度800MPa级高强度高韧性钢板及其制造方法
CN107429369B (zh) 2015-02-24 2019-04-05 新日铁住金株式会社 冷轧钢板及其制造方法

Family Cites Families (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5328528A (en) * 1993-03-16 1994-07-12 China Steel Corporation Process for manufacturing cold-rolled steel sheets with high-strength, and high-ductility and its named article
JP2000313936A (ja) * 1999-04-27 2000-11-14 Kobe Steel Ltd 延性に優れた合金化溶融亜鉛めっき鋼板およびその製造方法
JP3750789B2 (ja) * 1999-11-19 2006-03-01 株式会社神戸製鋼所 延性に優れる溶融亜鉛めっき鋼板およびその製造方法
US7090731B2 (en) * 2001-01-31 2006-08-15 Kabushiki Kaisha Kobe Seiko Sho (Kobe Steel, Ltd.) High strength steel sheet having excellent formability and method for production thereof
FR2830260B1 (fr) * 2001-10-03 2007-02-23 Kobe Steel Ltd Tole d'acier a double phase a excellente formabilite de bords par etirage et procede de fabrication de celle-ci
JP3840436B2 (ja) 2002-07-12 2006-11-01 株式会社神戸製鋼所 加工性に優れた高強度鋼板
JP3828466B2 (ja) * 2002-07-29 2006-10-04 株式会社神戸製鋼所 曲げ特性に優れた鋼板
JP3764411B2 (ja) * 2002-08-20 2006-04-05 株式会社神戸製鋼所 焼付硬化性に優れた複合組織鋼板
CN100591789C (zh) * 2002-12-24 2010-02-24 新日本制铁株式会社 焊接热影响区的耐软化性优良且扩孔弯边性好的高强度钢板及其制造方法
US7314532B2 (en) * 2003-03-26 2008-01-01 Kabushiki Kaisha Kobe Seiko Sho (Kobe Steel, Ltd.) High-strength forged parts having high reduction of area and method for producing same

Also Published As

Publication number Publication date
EP1589126A1 (de) 2005-10-26
EP1589126B1 (de) 2009-03-25
US20050247378A1 (en) 2005-11-10
DE602005013442D1 (de) 2009-05-07
US8597439B2 (en) 2013-12-03
US20100092332A1 (en) 2010-04-15

Similar Documents

Publication Publication Date Title
ATE426686T1 (de) Hochfestes und kaltgewaltzes stahlblech mit hervorragender verformbarkeit und plattiertes stahlblech
WO2009066734A1 (ja) 高強度冷延鋼板
ES2568649T3 (es) Chapa de acero de alta resistencia galvanizada en caliente con excelente adherencia del baño y capacidad de expansión de agujeros y método de producción de la misma
ES2526974T3 (es) Hojas de acero de alta resistencia que presentan un balance excelente entre capacidad de expansión de agujeros y ductilidad y también una resistencia a fatiga excelente, hojas de acero revestidas de zinc y procedimientos para producir las hojas de acero
MX2010008622A (es) Lamina de acero galvanizada por inmersion en caliente, de alta tenacidad, con excelente procesabilidad y procedimiento para la produccion de la misma.
TW200615387A (en) A high-strength thin steel sheet excellent in elongation and hole-expandability, and a method for producing the same
MX2010003835A (es) Acero estructurado metalografico complejo y metodo para manufacturarlo.
UA92039C2 (ru) Композиция высокопрочной пластичной стали, лист стали и его применение, способ получения горячекатанного и холоднокатанного листа из стали
PL381033A1 (pl) Blacha walcowana na zimno mająca wytrzymałość na rozciąganie 780MPa lub więcej, doskonałą miejscową odkształcalność i zmniejszony wzrost twardości zgrzeiny
MX349893B (es) Lamina de acero laminada en caliente de alta proporcion de rendimiento, que tiene excelente absorcion de energia de impacto a baja temperatura y resistencia al reblandecimiento de la haz y metodo de produccion de la misma.
MX373588B (es) LÁMINA DE ACERO GALVANIZADA POR INMERSIÓN EN CALIENTE, DE ALTA RESISTENCIA, Y LÁMINA DE ACERO GALVANIZADA POR INMERSIÓN EN CALIENTE, ALEADA, DE ALTA RESISTENCIA, QUE TIENE EXCELENTE ADHESIÓN DE ENCHAPADO, FORMABILIDAD, Y CAPACIDAD DE EXPANSIÓN DE AGUJERO CON RESISTENCIA A LA TRACCIÓN DE 980 MPa O MÁS Y MÉTODO DE FABRICACIÓN DE LAS MISMAS.
MX2009010538A (es) Lamina de acero de alta resistentcia enchapada en caliente por inmersion para uso en estampacion, superior en tenacidad a baja temperatura y metodo de produccion de la misma.
MX2013012116A (es) Placa de acero laminada en frio de alta resistencia que tiene excelente alargamiento por tension uniforme y capacidad de expansion de agujeros y metodo de fabricacion de la misma.
DE60116477D1 (de) Warm-, kaltgewalzte und schmelz-galvanisierte stahlplatte mit exzellentem reckalterungsverhalten
CA2387322A1 (en) High-ductility steel sheet excellent in press formability and strain age hardenability, and method for manufacturing the same
TW200940717A (en) High strength steel sheet having superior ductility and method for manufacturing the same
MX350016B (es) Lámina de acero con altas propiedades de resistencia mecánica, ductilidad y de formación, método de producción de la misma y uso de dichas láminas.
IN2014DN11262A (de)
MX366776B (es) Lamina de acero, laminada en caliente, recocida y galvanizada por inmersion en caliente, y proceso para producir la misma.
WO2002044434A1 (en) Composite structure type high tensile strength steel plate, plated plate of composite structure type high tensile strength steel and method for their production
EP1512760A3 (de) Hohes Stahlblech der Dehnfestigkeit ausgezeichnet für die Verarbeitung und Proze für die Produktion desselben
WO2008108363A1 (ja) 冷間圧延鋼板および合金化溶融亜鉛めっき鋼板ならびにそれらの製造方法
IN2014DN00269A (de)
MX2024002348A (es) Lamina de acero de alta resistencia y metodo de fabricacion de la misma.
IN2014KN01170A (de)

Legal Events

Date Code Title Description
UEP Publication of translation of european patent specification

Ref document number: 1589126

Country of ref document: EP

EEIH Change in the person of patent owner