ATE440918T1 - Palladium komplexe für den druck von leiterkarten - Google Patents

Palladium komplexe für den druck von leiterkarten

Info

Publication number
ATE440918T1
ATE440918T1 AT04756142T AT04756142T ATE440918T1 AT E440918 T1 ATE440918 T1 AT E440918T1 AT 04756142 T AT04756142 T AT 04756142T AT 04756142 T AT04756142 T AT 04756142T AT E440918 T1 ATE440918 T1 AT E440918T1
Authority
AT
Austria
Prior art keywords
palladium
composition
ink
aliphatic amine
jettable
Prior art date
Application number
AT04756142T
Other languages
English (en)
Inventor
Herbert Etheridge
Original Assignee
Hewlett Packard Development Co
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hewlett Packard Development Co filed Critical Hewlett Packard Development Co
Application granted granted Critical
Publication of ATE440918T1 publication Critical patent/ATE440918T1/de

Links

Classifications

    • H—ELECTRICITY
    • H05—ELECTRIC TECHNIQUES NOT OTHERWISE PROVIDED FOR
    • H05K—PRINTED CIRCUITS; CASINGS OR CONSTRUCTIONAL DETAILS OF ELECTRIC APPARATUS; MANUFACTURE OF ASSEMBLAGES OF ELECTRICAL COMPONENTS
    • H05K3/00—Apparatus or processes for manufacturing printed circuits
    • H05K3/10—Apparatus or processes for manufacturing printed circuits in which conductive material is applied to the insulating support in such a manner as to form the desired conductive pattern
    • H05K3/18—Apparatus or processes for manufacturing printed circuits in which conductive material is applied to the insulating support in such a manner as to form the desired conductive pattern using precipitation techniques to apply the conductive material
    • H05K3/181—Apparatus or processes for manufacturing printed circuits in which conductive material is applied to the insulating support in such a manner as to form the desired conductive pattern using precipitation techniques to apply the conductive material by electroless plating
    • H05K3/182—Apparatus or processes for manufacturing printed circuits in which conductive material is applied to the insulating support in such a manner as to form the desired conductive pattern using precipitation techniques to apply the conductive material by electroless plating characterised by the patterning method
    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
    • C09D11/00—Inks
    • C09D11/30—Inkjet printing inks
    • C09D11/38—Inkjet printing inks characterised by non-macromolecular additives other than solvents, pigments or dyes
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C18/00—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating
    • C23C18/16—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating by reduction or substitution, e.g. electroless plating
    • C23C18/1601—Process or apparatus
    • C23C18/1603—Process or apparatus coating on selected surface areas
    • C23C18/1607—Process or apparatus coating on selected surface areas by direct patterning
    • C23C18/1608—Process or apparatus coating on selected surface areas by direct patterning from pretreatment step, i.e. selective pre-treatment
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C18/00—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating
    • C23C18/16—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating by reduction or substitution, e.g. electroless plating
    • C23C18/1601—Process or apparatus
    • C23C18/1603—Process or apparatus coating on selected surface areas
    • C23C18/1607—Process or apparatus coating on selected surface areas by direct patterning
    • C23C18/161—Process or apparatus coating on selected surface areas by direct patterning from plating step, e.g. inkjet
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C18/00—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating
    • C23C18/16—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating by reduction or substitution, e.g. electroless plating
    • C23C18/1601—Process or apparatus
    • C23C18/1619—Apparatus for electroless plating
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C18/00—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating
    • C23C18/16—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating by reduction or substitution, e.g. electroless plating
    • C23C18/1601—Process or apparatus
    • C23C18/1633—Process of electroless plating
    • C23C18/1646—Characteristics of the product obtained
    • C23C18/165—Multilayered product
    • C23C18/1651—Two or more layers only obtained by electroless plating
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C18/00—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating
    • C23C18/16—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating by reduction or substitution, e.g. electroless plating
    • C23C18/1601—Process or apparatus
    • C23C18/1633—Process of electroless plating
    • C23C18/1655—Process features
    • C23C18/1658—Process features with two steps starting with metal deposition followed by addition of reducing agent
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C18/00—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating
    • C23C18/16—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating by reduction or substitution, e.g. electroless plating
    • C23C18/1601—Process or apparatus
    • C23C18/1633—Process of electroless plating
    • C23C18/1689—After-treatment
    • C23C18/1692—Heat-treatment
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C18/00—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating
    • C23C18/16—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating by reduction or substitution, e.g. electroless plating
    • C23C18/18—Pretreatment of the material to be coated
    • C23C18/1851—Pretreatment of the material to be coated of surfaces of non-metallic or semiconducting in organic material
    • C23C18/1872—Pretreatment of the material to be coated of surfaces of non-metallic or semiconducting in organic material by chemical pretreatment
    • C23C18/1886—Multistep pretreatment
    • C23C18/1889—Multistep pretreatment with use of metal first
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C18/00—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating
    • C23C18/16—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating by reduction or substitution, e.g. electroless plating
    • C23C18/18—Pretreatment of the material to be coated
    • C23C18/20—Pretreatment of the material to be coated of organic surfaces, e.g. resins
    • C23C18/2006—Pretreatment of the material to be coated of organic surfaces, e.g. resins by other methods than those of C23C18/22 - C23C18/30
    • C23C18/2046—Pretreatment of the material to be coated of organic surfaces, e.g. resins by other methods than those of C23C18/22 - C23C18/30 by chemical pretreatment
    • C23C18/2073—Multistep pretreatment
    • C23C18/208—Multistep pretreatment with use of metal first
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C18/00—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating
    • C23C18/16—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating by reduction or substitution, e.g. electroless plating
    • C23C18/18—Pretreatment of the material to be coated
    • C23C18/20—Pretreatment of the material to be coated of organic surfaces, e.g. resins
    • C23C18/28—Sensitising or activating
    • C23C18/30—Activating or accelerating or sensitising with palladium or other noble metal
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C18/00—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating
    • C23C18/16—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating by reduction or substitution, e.g. electroless plating
    • C23C18/31—Coating with metals
    • C23C18/42—Coating with noble metals
    • C23C18/44—Coating with noble metals using reducing agents
    • H—ELECTRICITY
    • H05—ELECTRIC TECHNIQUES NOT OTHERWISE PROVIDED FOR
    • H05K—PRINTED CIRCUITS; CASINGS OR CONSTRUCTIONAL DETAILS OF ELECTRIC APPARATUS; MANUFACTURE OF ASSEMBLAGES OF ELECTRICAL COMPONENTS
    • H05K2203/00—Indexing scheme relating to apparatus or processes for manufacturing printed circuits covered by H05K3/00
    • H05K2203/01—Tools for processing; Objects used during processing
    • H05K2203/0104—Tools for processing; Objects used during processing for patterning or coating
    • H05K2203/013—Inkjet printing, e.g. for printing insulating material or resist
    • H—ELECTRICITY
    • H05—ELECTRIC TECHNIQUES NOT OTHERWISE PROVIDED FOR
    • H05K—PRINTED CIRCUITS; CASINGS OR CONSTRUCTIONAL DETAILS OF ELECTRIC APPARATUS; MANUFACTURE OF ASSEMBLAGES OF ELECTRICAL COMPONENTS
    • H05K3/00—Apparatus or processes for manufacturing printed circuits
    • H05K3/10—Apparatus or processes for manufacturing printed circuits in which conductive material is applied to the insulating support in such a manner as to form the desired conductive pattern
    • H05K3/12—Apparatus or processes for manufacturing printed circuits in which conductive material is applied to the insulating support in such a manner as to form the desired conductive pattern using thick film techniques, e.g. printing techniques to apply the conductive material or similar techniques for applying conductive paste or ink patterns
    • H05K3/1241—Apparatus or processes for manufacturing printed circuits in which conductive material is applied to the insulating support in such a manner as to form the desired conductive pattern using thick film techniques, e.g. printing techniques to apply the conductive material or similar techniques for applying conductive paste or ink patterns by ink-jet printing or drawing by dispensing
    • H05K3/125—Apparatus or processes for manufacturing printed circuits in which conductive material is applied to the insulating support in such a manner as to form the desired conductive pattern using thick film techniques, e.g. printing techniques to apply the conductive material or similar techniques for applying conductive paste or ink patterns by ink-jet printing or drawing by dispensing by ink-jet printing

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Materials Engineering (AREA)
  • Organic Chemistry (AREA)
  • General Chemical & Material Sciences (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Mechanical Engineering (AREA)
  • Metallurgy (AREA)
  • Manufacturing & Machinery (AREA)
  • Microelectronics & Electronic Packaging (AREA)
  • Life Sciences & Earth Sciences (AREA)
  • Wood Science & Technology (AREA)
  • Inks, Pencil-Leads, Or Crayons (AREA)
  • Manufacturing Of Printed Wiring (AREA)
  • Ink Jet Recording Methods And Recording Media Thereof (AREA)
  • Ink Jet (AREA)
AT04756142T 2003-07-11 2004-06-25 Palladium komplexe für den druck von leiterkarten ATE440918T1 (de)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US10/618,522 US7537799B2 (en) 2003-07-11 2003-07-11 Methods of forming electrically conductive pathways using palladium aliphatic amine complexes
PCT/US2004/020497 WO2005010108A1 (en) 2003-07-11 2004-06-25 Palladium complexes for printing circuits

Publications (1)

Publication Number Publication Date
ATE440918T1 true ATE440918T1 (de) 2009-09-15

Family

ID=33565148

Family Applications (1)

Application Number Title Priority Date Filing Date
AT04756142T ATE440918T1 (de) 2003-07-11 2004-06-25 Palladium komplexe für den druck von leiterkarten

Country Status (7)

Country Link
US (3) US7537799B2 (de)
EP (2) EP1644453B1 (de)
CN (1) CN100528984C (de)
AT (1) ATE440918T1 (de)
DE (1) DE602004022816D1 (de)
TW (1) TWI352723B (de)
WO (1) WO2005010108A1 (de)

Families Citing this family (22)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR100678419B1 (ko) * 2005-04-01 2007-02-02 삼성전기주식회사 기판의 표면처리방법, 배선형성방법 및 배선기판
US20060268290A1 (en) * 2005-05-25 2006-11-30 Thieme Gmbh & Co. Kg Printing table for flatbed printers
US20070080775A1 (en) * 2005-10-07 2007-04-12 Hideki Akimoto Trimming resistor and method of manufacture thereof
US7981508B1 (en) 2006-09-12 2011-07-19 Sri International Flexible circuits
GB0619539D0 (en) 2006-10-04 2006-11-15 Hexcel Composites Ltd Curable resin films
CN101591488B (zh) * 2008-05-26 2011-12-21 富葵精密组件(深圳)有限公司 油墨及利用该油墨制作导电线路的方法
US8747599B2 (en) * 2008-05-29 2014-06-10 Chidella Krishna Sastry Process for making self-patterning substrates and the product thereof
CN101600301A (zh) * 2008-06-04 2009-12-09 富葵精密组件(深圳)有限公司 电路板及其制作方法
GB0902398D0 (en) 2009-02-13 2009-04-01 Conductive Inkjet Tech Ltd Diffractive optical elements
KR101803956B1 (ko) * 2010-05-06 2017-12-01 주식회사 동진쎄미켐 대기압에서 소성 가능한 구리 나노입자의 제조방법
KR101765731B1 (ko) * 2011-03-09 2017-08-08 삼성디스플레이 주식회사 금속 패턴의 형성 방법 및 이를 포함한 표시 기판의 제조 방법
US8574665B2 (en) * 2011-06-06 2013-11-05 Xerox Corporation Palladium precursor composition
US8568824B2 (en) * 2011-06-06 2013-10-29 Xerox Corporation Palladium precursor composition
US8986819B2 (en) 2011-06-06 2015-03-24 Xerox Corporation Palladium precursor composition
US8741036B2 (en) * 2012-02-02 2014-06-03 Xerox Corporation Composition of palladium unsaturated organoamine complex and palladium nanoparticles
US8613796B1 (en) * 2012-09-17 2013-12-24 Xerox Corporation Palladium precursor composition having a fluorinated component
US20140161972A1 (en) * 2012-12-09 2014-06-12 National Sun Yat-Sen University Method for forming conductive film at room temperature
US9217093B1 (en) 2014-05-30 2015-12-22 Xerox Corporation Palladium ink compositions
US9822271B2 (en) 2014-07-16 2017-11-21 Electronics For Imaging, Inc. Ceramic inkjet ink for red decoration
TWI856948B (zh) 2017-08-03 2024-10-01 美商電子墨水股份有限公司 包含鈀之導電墨水組成物及用於製造其之方法
CN110952081B (zh) * 2018-09-27 2022-04-29 Imec 非营利协会 用于形成互连部的方法和溶液
EP3912439B1 (de) 2019-02-14 2024-04-03 Orbotech Ltd. Verfahren und vorrichtung zur herstellung eines pcb-produkts mit sehr dichten leitern

Family Cites Families (37)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3222218A (en) * 1962-01-02 1965-12-07 Exxon Research Engineering Co Metal coating process
US3846138A (en) * 1973-08-02 1974-11-05 Webline Corp Electroless copper plating
US3896252A (en) * 1974-02-04 1975-07-22 Dow Chemical Co Process of metal plating on plastics
DE2920940A1 (de) * 1979-05-21 1980-12-04 Schering Ag Verfahren zur herstellung von gedruckten schaltungen
US4368281A (en) * 1980-09-15 1983-01-11 Amp Incorporated Printed circuits
US4486274A (en) * 1981-02-27 1984-12-04 At&T Bell Laboratories Palladium plating prodedure
US4406755A (en) * 1982-03-08 1983-09-27 Technic Inc. Bright palladium electrodeposition
US4377450A (en) * 1982-04-15 1983-03-22 Bell Telephone Laboratories, Incorporated Palladium electroplating procedure
US4454010A (en) * 1982-08-30 1984-06-12 At & T Bell Laboratories Palladium plating procedure
US4584316A (en) * 1983-03-25 1986-04-22 Research Corporation Palladium anti-cancer complexes
US4469714A (en) * 1983-09-02 1984-09-04 Okuno Chemical Industry Co., Ltd. Composition for bonding electroconductive metal coating to electrically nonconductive material
JPS60252129A (ja) * 1984-05-29 1985-12-12 Honda Motor Co Ltd スロツトル弁を備える内燃エンジンの作動制御装置
US4668533A (en) * 1985-05-10 1987-05-26 E. I. Du Pont De Nemours And Company Ink jet printing of printed circuit boards
US5024733A (en) * 1989-08-29 1991-06-18 At&T Bell Laboratories Palladium alloy electroplating process
US5227223A (en) * 1989-12-21 1993-07-13 Monsanto Company Fabricating metal articles from printed images
US5120578A (en) * 1990-05-31 1992-06-09 Shipley Company Inc. Coating composition
US5184604A (en) * 1991-10-29 1993-02-09 Brillante Jose C Animal mouth retractor
US5882736A (en) * 1993-05-13 1999-03-16 Atotech Deutschland Gmbh palladium layers deposition process
EP0693579B1 (de) * 1994-07-21 1997-08-27 W.C. Heraeus GmbH Bad zum galvanischen Abscheiden von Palladium-Silber-Legierungen
US6123876A (en) * 1995-04-04 2000-09-26 Canon Kabushiki Kaisha Metal-containing composition for forming electron-emitting device
JP3241613B2 (ja) 1995-10-12 2001-12-25 キヤノン株式会社 電子放出素子、電子源および画像形成装置の製造方法
JP3229223B2 (ja) * 1995-10-13 2001-11-19 キヤノン株式会社 電子放出素子、電子源及び画像形成装置の製造法並びに電子放出素子製造用金属組成物
US5650265A (en) * 1995-12-22 1997-07-22 Eastman Kodak Company Silver halide light-sensitive element
US5889083A (en) * 1996-09-06 1999-03-30 Videojet Systems International, Inc. Aqueous jet ink compositions
US6063174A (en) * 1997-09-22 2000-05-16 Canon Kabushiki Kaisha Ink for use in ink-jet recording, color filter, liquid crystal panel, computer and method for producing color filter
WO1999018255A1 (en) * 1997-10-03 1999-04-15 Massachusetts Institute Of Technology Selective substrate metallization
WO1999038176A1 (en) * 1998-01-22 1999-07-29 Matsushita Electric Industrial Co., Ltd. Ink for electronic component, method for producing electronic component by using the ink for electronic component, and ink-jet device
KR20010072835A (ko) * 1998-08-21 2001-07-31 추후제출 전기 회로 및 구성요소의 프린팅
JP2000232269A (ja) * 1999-02-10 2000-08-22 Nec Toyama Ltd プリント配線板およびプリント配線板の製造方法
US6346222B1 (en) * 1999-06-01 2002-02-12 Agere Systems Guardian Corp. Process for synthesizing a palladium replenisher for electroplating baths
EP1198852B1 (de) * 1999-07-21 2009-12-02 E Ink Corporation Bevorzugte methode, elektrische leiterbahnen für die kontrolle eines elektronischen displays herzustellen
US6257732B1 (en) * 1999-09-29 2001-07-10 American Spray Coating Method for forming a metallic mirror surface and solutions for the same
JP3812730B2 (ja) * 2001-02-01 2006-08-23 富士写真フイルム株式会社 遷移金属錯体及び発光素子
EP1282175A3 (de) * 2001-08-03 2007-03-14 FUJIFILM Corporation Muster aus leitendem Material und Verfahren zur dessen Herstellung
US6951666B2 (en) * 2001-10-05 2005-10-04 Cabot Corporation Precursor compositions for the deposition of electrically conductive features
US20050006339A1 (en) * 2003-07-11 2005-01-13 Peter Mardilovich Electroless deposition methods and systems
US20050199587A1 (en) * 2004-03-12 2005-09-15 Jon Bengston Non-chrome plating on plastic

Also Published As

Publication number Publication date
EP2103661A1 (de) 2009-09-23
US7896483B2 (en) 2011-03-01
TW200502330A (en) 2005-01-16
DE602004022816D1 (de) 2009-10-08
EP1644453A1 (de) 2006-04-12
US20090201333A1 (en) 2009-08-13
US20050005820A1 (en) 2005-01-13
WO2005010108A1 (en) 2005-02-03
US7537799B2 (en) 2009-05-26
EP1644453B1 (de) 2009-08-26
EP2103661A3 (de) 2009-11-25
CN100528984C (zh) 2009-08-19
CN1823145A (zh) 2006-08-23
US20090249976A1 (en) 2009-10-08
TWI352723B (en) 2011-11-21

Similar Documents

Publication Publication Date Title
DE602004022816D1 (de) Palladium komplexe für den druck von leiterkarten
CA2393399A1 (en) Soldering flux
DE60226871D1 (de) Tintenstrahltinte enthaltend fluorchemische tenside
EP1835512A4 (de) Leitfähiger farbstoff
WO2001087535A3 (en) Soldering flux with cationic surfactant
DE69529705T2 (de) Verfahren und Lösung zur Reinigung eines Substrats von einer Metallkontamination
TW200505308A (en) Electronic substrate, electronic circuit, and method and device for manufacture of the same
ATE463845T1 (de) Dünnfilmtranistor-bauelement und diesbezügliches verfahren
MY158861A (en) Deposition and patterning process
ATE508756T1 (de) Verfahren zur deaktivierung von nukleinsäuren
TW200621912A (en) Ink-jet printing of coupling agents for trace or circuit deposition templating
DE60135467D1 (de) Verfahren, vorrichtung und verwendung des auftragens eines viskosen mediums auf ein substrat
ATE482303T1 (de) Zusammensetzung und verfahren zur haftfähigkeitsverbesserung der polymerischen materialien auf kupfer- oder kupferlegierungsoberflächen
KR920022941A (ko) 프레플럭스의 사용방법 및 프린트 배선판과 그 제조방법
CA2248497A1 (en) Composition and method for stripping solder and tin from printed circuit boards
ATE199735T1 (de) Bedruckter artikel und verfahren
DE69838420D1 (de) Verfahren zur modifizierung von oberflächen
GB2452174A (en) A method and composition for selectively stripping nickel from a substrate
KR20090009734A (ko) 표면처리제
US5062902A (en) Fluxing agents comprising β-diketone and β-ketoimine ligands and a process for using the same
JPH0353120B2 (de)
TW200609381A (en) Composition for formining a chemical layer on surfaces of copper and copper alloys
EP4090914A1 (de) Tintenstrahlgedruckte leiterplatten
Heisler et al. Novel approach to mixed-technology processing
DE59901562D1 (de) Leiterplatte mit einem heatsink und verfahren zum anbringen eines heatsink

Legal Events

Date Code Title Description
RER Ceased as to paragraph 5 lit. 3 law introducing patent treaties