  "COMPS:TION DE PAVEMENT, ETC.- 
SLA PRÉSENTE INVENTION A POUR OBJET UNE NOUVELLE COMPOSITION CONVENANT POUR LES PAVEMENTS ET LE TRAITEMENT SUPERFICIEL DES ROUTES,   ET*.,   CETTE COMPOSITION CONTENANT UN MÉLANGE DE CAOUTCHOUC ET DE BITUME. ELLE A ÉGALEMENT POUR OBJET UN PROCEDE DE PRÉPARATION DE CETTE COMPOSITION, EN UTILISANT UNE DISPERSION DE CAOUTCHOUC DANS UN ALCOOL POLYHYORIQUE.   L'INVENTION   A ÉGALEMENT POUR OBJET LA DISPERSION DE CAOUTCHOUC DANS UN ALCOOL   POLVHYDRtQUE,   DE   MÊME   QUE LA PREPARATION DE CETTE DIS-   PERSION.   



   Depuis PLUSIEURS ANNÉES, ON A UTILISÉ, DANS LES PAVEMENTS, DES MÉLANGES DE CAOUTCHOUC ET DE BITUME. BIEN QUE L'ON CONNAISSE CERTAINS AVANTAGES RÉSULTANT DE   1.'UTILISATION   DU CAOUTCHOUC SOUS FORME DE LATEX, IL Y A CEPENDANT PLUSIEURS 

 <Desc/Clms Page number 2> 

 INCONVÉNIENTS, PROBABLEMENT DUS AU FAIT qu'une PETITE QUANTITÉ SEULEMENT D'EAU DANS LE BITUME, MÊME AUSSI FAIBLE QU'UNE FRACTION DE   POUR CENT,   FAIT BOUILLIR LE 
 EMI2.1 
 BITUME ET LE TRANSFORME EN MOUSSE, LORSQU'IL EST CHAUFFÉ AU-DELA DU POINT D'BULLI- TION DE L'EAU. 



   SUIVANT LA PRÉSENTE INVENTION, ON REMPLACE L'EAU DU LATEX PAR UN ALCOOL POLYHYDRIQUE ET L'ON MÉLANGE CETTE DISPERSION AVEC LE   BITUME.   ON PEUT FORMER LA DISPERSION EN ÉVAPORANT L'EAU DU LATEX SOUS VIDE ET EN LA REMPLAÇANT PAR   L'ALCOOL.   
 EMI2.2 
 Deze, LORSQUE LE CAOUTCHOUC EST UN POLYMÈRE SYNTHÉTIQUE, ON PEUT OBTENIR DIREC- TEMENT CETTE DISPERSION DU POLYMÈRE DANS L'ALCOOL EN EFFECTUANT LA POLYMERISATION 
 EMI2.3 
 DANS L'ALCOOL AU LIEU DE L'EAU. QPoUR CERTAINS LATEX, IL FAUT AUGMENTER LA QUANTI-   @é   DE STABILISANT PAR RAPPORT1 CELLE REQUISE POUR UN LATEX AQUEUX, AFIN   D'EMPECHER   LA COAGULATION AU COURS DU TRAITEMENT. 



   L'ALCOOL NE DISSOUT PAS LE CAOUTCHOUC, MAIS IL SE DISPERSE DANS LES HUI- 
 EMI2.4 
 LES ET LES AUTUS CONSTITUANTS DU BITUME ET LE CAOUTCHOUC EST AU MOINS PARTIELLEMENT   SOLUBLC   DANS LA DISPERSION OBTENUE. 



   LES   caoutchoucs pouvant   ÊTRE UTILiSÉS ONT, DE   PRÉFÉRENCE,   UNE VALEUR 
 EMI2.5 
 MOONEY (ML/4/MO"0') DE 5O OU PLUS. LE CAOUTCHOUC PEUT ÊTRE UN CAOUTCHOUC NATUREL, UN CHLOROPRINE, UN COPOLBAIR± Osl80BUTYL±NÌ80PRÉNE (CAOUTCHOUC BUTYLE), UN COPOLYMÈRE DE BUTADIINE-AORTLONITRILE, UN HOMOPOLYMÈRE DtUN DIÈNE OU UN COPOtb4kRE DE DJINES, OU L'UN OU L'AUTRE CAOUTCHOUC RÉGÉNÉRÉ, MAIS IL EST, DE PREFERENCE, UN COPOLYMRE DE (1) UN.dDtÈNE, COMME PAR EXEMPLE LE BUTADIÈNE, L'ISOPRÈNE, LE 2 D'MÉTHYL-SUTADtÈNE, LE PIPÉRYLÈNE, LE 2-CHLORO-BUTADIINE, LE 2, 3-DICHLOROBUTADIÈNE, LE 2-FLUDRO-BUTADIINE, ETC, ET (2) D'UN COMPOSÉ VINYLIQUE AROMATIQUE, COMME PAR EXEMPLE LE STYRÈNE, LE TOLUENE VINYLIQUE, LE NAPHTALENE VINYLIQUE, UN STYRENE NUCLÉAIRE SUBSTITUÉ, COMME PAR EXEMPLE UN HALO-STYRENE, UN ALCOYL-STYRINE. 



  ETC.   CES CAOUTCHOUCS   SE   DISSOLVENT   DANS UNE CERTAINE MESURE DANS UNE   dispersion   CAOUTCHOUTEUSE DE BITUME ET   D'ALCOOL.   IL EST PRÉFÉRABLE D'EMPLOYER UN COPOLYMERE DE   BUTADIÈNE   ET DE STYRENE. 



   LE BITUME   utilisé   SUIVANT LA PRESENTE INVENTION PEUT   ETRE   DE L'ASPHALTE OU DU GOUDRON ET IL COMPREND LES bitumes NATURELS ET   SYNTHETIQUES,   COMME PAR EXEMPLE LES   RESIDUS   DE LA DISTILLATION DU   PETROLE,   LES GOUDRONS DE HOUILLE, ETC, DE MÊME QUE D'AUTRES   MATIERES   BITUMINEUSES DE PAVEMENT, COMME PAR EXEMPLE LES GOUDRONS DE GAZ MÉNAGER, LES GOUDRONS DE FOURSA   COKE,   LES GOUDRONS DE GAZ A L'EAU, LES 
 EMI2.6 
 P#IX, LES HUILES DE ROUTE, LES BITUMES PYROGENES, LES BITUMES DE FRACTION DE RETOUR, ETC. 

 <Desc/Clms Page number 3> 

 
 EMI3.1 
 LE BITUME A, DE PREFERENCE, UNE pénétration, A ?3 C, D'AU MOINS 40 ET LA PÉNÉTRATION PEUT ÊTRE DE 100 OU PLUS (ESSAI DE PÉNÉTRATION : A.S.T.M.

   O LE LATEX EST UTILISÉ EN UNE QUANTITÉ TELLE qu'il Y ait ENVIRON I À 15 % (POIDS SEC) DE CAOUTCHOUC POUR 99-85 % CE   BITUME.   EN RÈGLE GENERALE, ON   UTILISE   
 EMI3.2 
 A À 100 % D'ALCOOL POLYHYDRJQUE, CALCULAS SUR LE POIDS DE CAOUTCHOUC. 



  L?ALCOOL PEUT ÊTRE N'IMPORTE QUEL ALCOOL POLYHYDRIQUE AYANT UN POINT D'EBULLITION SUPÉRIEUR À CELUI DE L'EAU, PAR EXEMPLE LA GLYCÉRINE OU UN GLYCOL. 



  ON UTILISE, DE préférence, UOLYÉTHYLÈNE-GLYCOL, BIEN QUE L'ON PUISSE ÉGALEMENT EMPLOYER UPOLYPROPYLINE-GLYCOL, ETC. LA COMPOSITION DU LATEX PEUT VARIER ENTRE ENVIRON 20 ET 80 % (EN POIDS) DE CAOUTCHOUC ET   80   A   20 %   D'ALCOOL. EN   RÈGLE   GENERALE, LA QUANTITÉ   D'ALCOOL   EST   REDUITE,   CAR IL AGIT COMME PLANIFIANT, BIEN QUE L'ON 
 EMI3.3 
 PUISSE CEPENDANT EMPLOYER lU6QU'À 80 % DE GLYCÉRINE: SI L'ON désire UNE GRANDE FLUIDITÉ DANS LE PRODUIT. S'IL Y A PLUS DE 80 % DE CAOUTCHOUC DANS LE MELAME, LA DISPERSION EST   PATEUSE   ET DURE A TRAITER. 



   LA DISPERSION DU CAOUTCHOUC DANS L'ALCOOL EST OBTENUE EN CHAUFFANT LE 
 EMI3.4 
 LATEX 1 UNE TEMPÉRATURE DE, PAR EXEMPLE, 200 1 300  F ($3 X 1490 C) SOUS UN VIDE DE g)0ÀX26853Mti±:s ET EN AJOUTANT L'ALCOOL AVANT LE chauffage OU PROGRESSIVEMENT PENDANT CE DERNIER OU ENCORE EN AJOUTANT UN PEU D'ALCOOL AUX DEUX   ETAPES,   ON PEUT AJOUTER, AU LATEX,  1 L'ALCOOL   OU AU MÉLANGE ALCOOL-LATEX, N'IMPORTE QUEL   STABILI-   
 EMI3.5 
 SANT NÉCESSAIRE POUlAAINTEN1R LES MOLDCULUS DE CAOUTCHOUC EN SUSPENSION DANS L'ALCOOL. 



   ON DONNERA, À TITRE   d'illustration,   L'EXEMPLE   SUIVANT   
 EMI3.6 
 ON CHAUFFE UNPOLYMERE ÉLASTOMÈRE DE BUTADIÈNE ET DE STYRENE (RAPPORT DE 75:25) DANS UN LXTEX, AYANT UNE TENEUR DE 60   %   DE   SOLIDES,   À 116  C, SOUS UN VIDE DE 22 POUCES DE MERCURE, TOUT EN AJOUTANT SUFFISAMMENT DE GLYCÉRINE POUR OBTENIR 
 EMI3.7 
 UNE DISPERSION AYANT UNE TENEUR DE ,55 o DE CAOUTCHOUC. ON MAINTIENT LE VIDE, JUSQU' CE QUE PRATIQUEMENT TOUTE L'EAU SOIT ÉLIMINÉE DU LATEX.

   ON MÉLANGE LE PRODUIT OBTENU AVEC DE L'ASPHALTE DE RÉSIDUS DE PÉTROLE, AVANT UNE PENETRAI ON DE 83-!00 (METHODE DE PÉNÉTRATION : A.S.T.M. 0-5), TOUT EN agitant DANS LE RÉSERVOIR D'UN DISTRIBUTEUR DE BITUME SOUS PRESSION OU AUTRE RÉSERVOIR D'ASPHALTE, POUR OBTENIR UN MÉLANGE DE 94, 6 % D'ASPHALTE,   3 %   DE CAOUTCHOUC ET   2,4 %   DE GLYCÉRINE, DE MÉLANGE ÉTANT ESSENTIELLEMENT EXEMPT D'EAU. EN   POURSUIVANT   LE   MÉLANGE,   LE CAOUTCHOUC SE DISSOUT DANS LES HUILES PROVENANT DE L'ASPHALTE ET IL GONFLE, AVEC UN MÉLANGE DE L'ASPHALTE ST DU CAOUTCHOUC AUX INTERFACES ENTRE LES PARTICULES DE 
 EMI3.8 
 CATUTCHOUC ET L'ASPHALTE. 

 <Desc/Clms Page number 4> 

 
 EMI4.1 
 LA FAIBLE TENEUR EN GLYCÉRINE EST DISPERSÉE DANS L'ASPHALTE ET DERT 1 PLASTIFIER LE MELANGE. 



   LES MÉLANGES DE BITUME-CAOUTCHOUC SONT HABITUELLEMENT   APPLIQUES   A CHAUD. 



  ON PEUT PRÉPARER CE MÉLANGE A PARTIR D'UN LATEX AQUEUX OU D'UN PRODUIT   CAOUTCHOU-   TEUX EN POUDRE,   MAIS  CETTE PRÉPARATION EST LENTE ET EXIGE UN APPAREILLAGE COÛTEUX. 



    DÈS LORS, LES MÉLANGES PRÉPARÉS A PARTIR D'UN LATEX DE CAOUTCHOUC AQUEUX OU DE   
 EMI4.2 
 PRODUITS CAOUTCHOUTEUX EN POUDRE, DOIVENT ÊTRE FABRIQUÉS DANS UNE tNSTALLAT'ON ET TRANSPORTES 1 CHAUD 8U LIEU DE L'UTILISATION, CE QUI PEUT NÉOE88fTER UN STOCKAGE DANS UN CAMION CITERNE PENDANT PLUSIEURS JOURS DE ROUTE. Si LES CONDITIONS   ATMOS-   
 EMI4.3 
 PHeRtQUES NE SONT PAS FAVORABLES LORSQUE LE CAMION DOIT ÊTRE DÉCHARGÉ PRES DU LIEU D'UTILISATION, LE MELANGE EST CONSERVÉ 1 CHAUD JUSQUTÀ CE QUE LE TEMPS S'AMELIORE. 



  CE STOCKAGE PROLONGÉ   DÉTERRIORE   LES   PROPRIETES   AVANTAGEUSES DU MÉLANGE. 



   ON A FAIT UN   emploi     très   LARGE DU BITUME SEUL, MAIS IL DEVIENT CASSANT A FROID ET SE   RAMOLLIT À  LA CHALEUR EN ÉTÉ. UN MÉLANGE AVEC DU CAOUTCHOUC DONNE 
 EMI4.4 
 UN PRODUIT AYANT DE MEILLEURES PROPRIÉTÉS PHYSIQUES DANS TOUTES LEWOOND.TI0NS ATM18PHLtZZjQUEB. LtA8G00L PLASTIFIE LE MELANGE, MAIS LA QUANTITÉ PRÉSENTE EST TRES FAIBLE. LES   ETHYLENE-GLYCOLS   A POINT D'ÉBULLITION INFÉRIEUR ONT TENDANCE A   82±VA-     POR@@   A LA TEMPERATURE LAQUELLE CERTAINS BITUMES SONT CHAUFFÉS POUR LA   LIVRA.SON   ET L'APPLICATION DE SORTE QUE LA GLYCÉRINE EST   GENERALEMENT   PRÉFÉRÉE. ON PEUT EMPLOYER UN   MÉLANGE   DE GLYCÉRINE ET D'UN GLYCOL. 



   LE   MÉLANGE   EST UYILISÉ POUR LES PAVEMENTS, LES TRAITEMENTS DES SURFACES 
 EMI4.5 
 OU LtÉTANCHÉIFtCATION DES VOIES ROUTIÈRES, LES CHAMPS D'AVIATION6 ETC., OU ENOORE COMME ADHéSIF OU AGENT DtÉTANCHÉfFjCATiON POUR LES APPLICATIONS INDUSTRIELLES. ON PEUT AJOUTER UNAGRÉGAT JAU MÉLANGE, LE TYPE ET LA QUANTITÉ DE CET AGRÉGAT VARIANT SUIVANT LES CONDITIONS REQUISES POUR UN CERTAIN TYPE D'APPLICATION. LE MÉLANGE PEUT ÊTRE VERSÉ OU PULVÉRISÉ SUR   L'AGREGAT   OU ENCORE ÊTRE MÉLANGÉ AVEC CE DERNIER. 
 EMI4.6 
 HABITUELLEMENT, LA SURFACE À TRAITER EST RECOUVERTE PAR 1.1 MELANGE ET L't^GIRIfQAT (PIERRES OU AUTRES) Y EST DISPERSE, ALORS QUE LE MÉLANGE EST ENCORE CHAUD. 



  HABITUELLEMENT, POUR CHAQUE LAPtHCATION, L'ÉPAISSEUR DE L'AQREGËT NE DEPASSERA PAS UNE COUCHE ET L'ÉPAISSEUR DU MELANGE REPRÉSENTERA   ENVIRON   UN TIERS DE LA HAUTEUR MOYENNE DE PIERRES. 



   LA   PRESENTE INVENTION   EST   ILLUSTREE     D'UNE     MANIERE   PLUS   DETAILLEE   DANS LES . 



    DESSINS   EN ANNEXE, DANS   LESQUELS :  
LA FG1. 1 EST UNE REPRODUCTION PHOTOGRAPHIQUE   D'UN     MELANGE,   AGRANDIE TROIS CENTS FOIS ET   @   

 <Desc/Clms Page number 5> 

 
 EMI5.1 
 LA Fic. 2 EST UNE,VATION LATÉRALE D'UNE SURFACE TRAITÉE. LA   FIG.  1 REPRÉSENTE UN MÉLANGE DE 3% EN POIDS DE CAOUTCHOUC DE LATEX 
 EMI5.2 
 GR-S 2105 (COPOLYMÈRE ÉLASTONÈ8E DE BUTADIÈNE ET DE STYRENE), DE 2,4 % DE GLYCÉRINE, ESSENTIELLEMENT EXEMPTE D'EAU ET DE   94,6 %   DE   RÉSIDU   D'ASPHALTE DE LA DISTILLATION DU PÉTROLE. LE CERCLE BLANO A ÉTÉ FORMÉ PAR USE BULLE D'AIR. LES ZONES PLUS CLAI- RES MONTRENT LE CAOUTCHOUC QUI A DISSOUS L'HUILE DE L'ASPHALTE.

   LORSQUE LES PARTI- CULES DE CAOUTCHOUC GONFLENT, ELLES   @ONT   TENDANCE   1 et   RÉUNIR. LES MATIÈRES      CAOUTCHOUTEUSES   PARTICULIEREMENT   SOUHAITABLES SONT CELLES QUI SONT PARTIELLEMENT; SOLUBLES DANS L'ASPHALTE. LES ZONES PLUS NOIRES   REPRESENTENT   L'ASPHALTE. DANS LE: PRODUIT FINAL, IL Y A UNE PHASE CONTINUE D'ASPHALTE ET LE CAOUTCHOUC A TENDANCE 
 EMI5.3 
 X FORMER UNE PHASE CONTINUE. LE CAOUTCHOUC NE SE 01 880UT PAS DANS L'ALCOOL,MAIS L'ALCOOL EST DANS LE MÉLANGE FINAL. 



   LA FIG. 2 REPRÉSENTE UNE COUCHE DE MÉLANGE   5   DE CAOUTCHOUC-ASPHALTE SUR LA ROUTE ASPHALTÉE, EN BÉTON OU AUTRE 6, DES MORCEAUX DE PIERRE 7 ÉTANT   DISPERSÉS   SUR CE MÉLANGE. LES PIERRES SONT AJOUTÉES TANDIS QUE LE MÉLANGE EST ENCORE VISQUEUX ET FLUIDE   ET/*   MÉLANGE FORME UNE FERME   LIAISON   AVEC LES PIERRES. 



   LE MÉLANGE EST AVANTAGEUSEMENT PRÉPARÉ SUR LE LIEU D'UTILISATION. 



  LE MÉLANGE PEUT ÊTRE ÉVENTUELLEMENT PRÉPARÉ A UN AUTRE ENDROIT, POUR ÊTRE AMENÉ ENSUITE AU LIEU D'UTILISATION. 



   PAR LE TERME "LATEX", UTILISÉ DANS LA PRÉSENTE DESCRIPTION, ON ENTEND   @   DES DISPERSIONS (PARFOIS APPELÉES LATEX) DE MEME QUE LES LATEX NATURELS ET   SYNTHÉ-   TIQUES. 



    REVENDICATIONS .    
 EMI5.4 
 



  1, DispERatoN DE 20 À SO PARTIES EN POIDS DE CAOUTCHOUC DANS 80 1 20 PARTIES D'UN ALCOOL POLYHYDRIQUE AYANT UN POINT DÎÉBULLITION SUPÉRIEUR 1 CELUI DE   LEAU,   LE CAOUTCHOUC ÉTANT CHOISI PARMI LA CLASSE COMPRENANT LE CAOUTCHOUC NATUREL, ' 
 EMI5.5 
 LES CHLOROPRINES, LES HOMOPOLYUkRra ET LES-COPOLYMERE8 DE DIÈNES, LES OOPOLYNÈRES DtACRYLONITRILE ET DE BUTADIÈNE, LES COPOLYMERES D'ISOBUTYLINE ET D'ISOPRÈNE, LES OOPOLYMÈRBS D'UN DIÈNE ET D'UN COMPOSÉ VINYLIQUE AROMATIQUE, DE MÊME QUE LES CAOUTCHOUCS RÉGÉNÉRÉS. 
 EMI5.6 
 



  2. MÉLANGE DE DISPERSION DE H , PARTIES DE aiTumE AVEC UNE PÉNÉTRATION D'AU MOINS 40, DE 15 X f PARTIE DE CAOUTCHOUC, DE MÊME QU'UN ALCOOL POY8YDRJQUE AYANT UN POINT Dlé%ULLITION SUPÉRIEUR X CELUI DE L'EAU ET PRÉSENT EN UNE 

**ATTENTION** fin du champ DESC peut contenir debut de CLMS **.

Claims (1)

1. <Desc/Clms Page number 6> QUANTITÉ ÉGALE A 20-80 PARTIES EN POIDS PAR 80-20 PARTIES DU CAOUTCHOUC PRESENT, LE EMI6.1 camu-rchouc ÉTANT DE LA CLASSE COMPRENANT LE CAOUTCHOUC NATUREL, LES CHLOROPRINES, LES HOMOPOLYMIRES ET OOPOaYMÉRE6 DE DIÈNES, LES COPOLYMERES OTACRYLONITRILE ET DE BUTADIÈNE, LES COPOLYMERES D?/608UTYLÉNE ET D'ISOPRÈNE, LES COPOLYMERES D'UN DIÈNE ET D'UN MONOMERE VINYLIQUE AROMATIQUE, DE MÊME QUE LES CAOUTCHOUCS RÉGÉNÉRÉS.

   MÉLANGE DE DISPERSION SUIVANT LA REVENDICATION 2, CARACTÉRISÉ EN CE QUE LE BITUMEA UNE PÉNÉTRATION DE 40 A 300.

   4. DISPERSION SUIVANT L'UNE OU L'AUTRE DES REVENDICATIONS PRÉCÉDENTES, CARACTÉRISÉE EN CE QUE LE CAOUTCHOUC EST UN OOPOLYMERE DE BUTADIÈNE ET DE STYRÈNE ET EN CE QUE L'ALCOOL POLYHYDRIQUE EST DE LA GLYCÉRINE.

   3. PROCÉDÉ DE PRÉPARATION D'UNE DISPERSION CAOUTCHOUTEUSE DE 20 A 80 PAR- EMI6.2 TIES 8N POIDS DE CAOUTCHOUC DANS 80 1 20 PARTIES EN POIDS D'UN ALCOOL POLYHYDRIQUE AYANT UN POINT DÉBU1;LITION SUPERIEUR CELUI DE L'EAU, CARACTÉRISÉ EN CE QU'ON AJOUTE L'ALCOOL UN LATEX CAOUTCHOUTEUX ET EN CE QU'ON EN VOLATILISE L'EAU SOUS LA CHALEUR ET SOUS VIDE, LE CAOUTCHOUC APPARTENANT A LA CLASSE COMPRENANT LE CAOUTCHOUC NATUREL, LES CHLOROPRENES, LES HOMO POLYMÈRES ET COPOLYMERES DE DIÈNES, LES EMI6.3 COPOLYMÈRES D'ACRYLOITRILE ET DE BUTADIÈNE, LES COPOITMIRES OT160BUTYLÉNE ET Dt160PRÉNELE6 COPOLYMIRES D'UN DIÈNE ET D'UN COMPOSÉ AROMATIQUE, DE MÊME QUE LES CAOUTCHOUCS RÉGÉNÉRÉS.

   6. PROCÉDÉ DE PRÉPARATION D'UN MÉLANGE DE CAOUTCHOUC-BITUME, CARACTÉRISÉ EMI6.4 EN CE QU'ON MELAN1E 83 A 99 PARTIES EN POIDS DE BITUME AYANT UNE PÉNÉTRATION D'AU MOINS 40, AVEC UNE DISPERSION SUIVANT LA REVENDICATION i.

   7. DISPERSION DE CAOUTCHOUC-ALCOOL POLYHYDRIQUE, ENTSUBSTANCE COMME DÉCRIT et-DESSUS EMI6.5 8.. mélanqe CAOUTCHOUC-BITUME, EN SUBSTANCE COMME DÉCRIT ci-DESSUS.

   9. CoMPOSITIONS DE PAVEMENTS ET DE TRAITEMENT DES SURFACES CARACTÉRISÉES EN CE QU'ELLES COMPRENNENT UN AGRÉGAT ET UN MÉLANGE DE CAOUTCHOUC-BITUME SUIVANT L'UNE OU L'AUTRE DES REVENDICATIONS 2 A 4 ET 8.