BR0200003A - Aço para formas de material plástico e processo para o tratamento térmico das mesmas - Google Patents

Aço para formas de material plástico e processo para o tratamento térmico das mesmas

Info

Publication number
BR0200003A
BR0200003A BR0200003A BR0200003A BR0200003A BR 0200003 A BR0200003 A BR 0200003A BR 0200003 A BR0200003 A BR 0200003A BR 0200003 A BR0200003 A BR 0200003A BR 0200003 A BR0200003 A BR 0200003A
Authority
BR
Brazil
Prior art keywords
steel
heat treatment
maximum
thermal
treatment
Prior art date
Application number
BR0200003A
Other languages
English (en)
Other versions
BR0200003B1 (pt
Inventor
Klaus Sammt
Original Assignee
Boehler Edelstahl
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Boehler Edelstahl filed Critical Boehler Edelstahl
Publication of BR0200003A publication Critical patent/BR0200003A/pt
Publication of BR0200003B1 publication Critical patent/BR0200003B1/pt

Abstract

"AçO PARA FORMAS DE MATERIAL PLáSTICO E PROCESSO PARA O TRATAMENTO TéRMICO DAS MESMAS". A invenção refere-se a um aço endurecível com martensita com capacidade de levantamento de aparas aperfeiçoada, boa capacidade de solda e alta resistência à corrosão, um processo para o tratamento térmico de um tal aço, bem como seu emprego. De acordo com a invenção, este aço contém (em %, em peso) 0,02 - 0,075 % de carbono 0,1 - 0,6 % de silício 0,5 - 0,9 % de manganês 0,08 - 0,25 % de enxofre no máximo 0,04 % de fósforo 12.4 - 15,2 % de cromo 0,05 - 1,0 % de molibdênio 0,2 - 1,8 % de níquel no máximo 0,15 % de vanádio 0,1 - 0,45 % de cobre no máximo 0,03 % de alumínio 0,02 - 0,08 % de nitrogênio, bem como eventualmente um ou vários outros elementos de liga até o máximo de 2,0 %, restante ferro e impurezas condicionadas pela preparação e possui uma quota de ferrita na estrutura de menos do que 28 %, em volume. Um processo para o tratamento térmico de um aço endurecível com martensita com capacidade de levantamento de aparas aperfeiçoada, cujo processo prepara um objeto temperado também em grande corte transversal, constitui-se essencialmente no fato, de que um bloco de aço com a composição acima é submetido em uma primeira etapa a um tratamento de calcinação para a formação e ajuste de uma quota de ferrita na estrutura e em uma segunda etapa é efetuada uma deformação térmica do mesmo, depois do que em uma terceira etapa é efetuada uma calcinação macia e, em seguida, um melhoramento térmico.
BR0200003A 2001-02-14 2002-01-03 aço martensìtico e processo para o tratamento térmico de um aço martensìtico passìvel de endurecimento com boa usinabilidade. BR0200003B1 (pt)

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
AT2302001A AT409636B9 (de) 2001-02-14 2001-02-14 Stahl für kunststoffformen und verfahren zur wärmebehandlung desselben

Publications (2)

Publication Number Publication Date
BR0200003A true BR0200003A (pt) 2002-10-29
BR0200003B1 BR0200003B1 (pt) 2010-11-16

Family

ID=3669928

Family Applications (1)

Application Number Title Priority Date Filing Date
BR0200003A BR0200003B1 (pt) 2001-02-14 2002-01-03 aço martensìtico e processo para o tratamento térmico de um aço martensìtico passìvel de endurecimento com boa usinabilidade.

Country Status (11)

Country Link
US (1) US6893608B2 (pt)
EP (1) EP1233080B1 (pt)
KR (1) KR100500263B1 (pt)
CN (2) CN100558926C (pt)
AT (1) AT409636B9 (pt)
BR (1) BR0200003B1 (pt)
CA (1) CA2371333C (pt)
DE (1) DE50107038D1 (pt)
DK (1) DK1233080T3 (pt)
ES (1) ES2247052T3 (pt)
TW (1) TW528811B (pt)

Families Citing this family (18)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20040007527A1 (en) * 1998-11-23 2004-01-15 Zenon Environmental Inc. Membrane filtration device and process
US20050079087A1 (en) * 2003-10-09 2005-04-14 Henn Eric D. Steel alloy for injection molds
FR2872825B1 (fr) * 2004-07-12 2007-04-27 Industeel Creusot Acier inoxydable martensitique pour moules et carcasses de moules d'injection
US20080073006A1 (en) * 2006-09-27 2008-03-27 Henn Eric D Low alloy steel plastic injection mold base plate, method of manufacture and use thereof
JP5412851B2 (ja) * 2009-01-29 2014-02-12 大同特殊鋼株式会社 プラスチック成形金型用鋼およびプラスチック成形金型
US8557059B2 (en) * 2009-06-05 2013-10-15 Edro Specialty Steels, Inc. Plastic injection mold of low carbon martensitic stainless steel
BRPI0904608A2 (pt) 2009-11-17 2013-07-02 Villares Metals Sa aÇo inoxidÁvel para moldes com menor quantidade de ferrita delta
KR101268764B1 (ko) * 2009-12-22 2013-05-29 주식회사 포스코 내식성을 향상시킨 사출성형 몰드용 마르텐사이트 스테인리스강
CN103540871B (zh) * 2013-11-07 2017-04-12 首钢总公司 一种低碳高Cr高N强耐腐蚀性用钢及其生产方法
AT515157B1 (de) * 2013-11-21 2016-12-15 Böhler Edelstahl GmbH & Co KG Verfahren zur Herstellung von Kunststoffformen aus martensitischem Chromstahl und Kunststoffform
CN103741048B (zh) * 2013-12-28 2016-05-04 扬州立德粉末冶金股份有限公司 一种汽油机活塞胀圈及其制备方法
CN106978564A (zh) * 2017-03-30 2017-07-25 钢铁研究总院 一种析出硬化型塑料模具钢及其制备方法
CN110184547B (zh) * 2019-07-03 2020-09-29 攀钢集团攀枝花钢铁研究院有限公司 含氮塑料模具宽厚扁钢及其制备方法
US20230357906A1 (en) * 2021-01-13 2023-11-09 Nippon Steel Stainless Steel Corporation Martensite-based stainless steel material and method for producing same
CN114855061A (zh) * 2022-07-05 2022-08-05 中特泰来模具技术有限公司 一种镜面塑料模具钢及其制备方法
CN116219317A (zh) * 2022-12-20 2023-06-06 攀钢集团攀枝花钢铁研究院有限公司 一种低成本耐蚀模具扁钢及其生产方法
CN118389947A (zh) * 2024-04-19 2024-07-26 邯郸新兴特种管材有限公司 高韧性95s钢级油井管用不锈钢、高韧性95s钢级油井管及其制备方法
CN120555904B (zh) * 2025-06-11 2025-11-04 中航上大高温合金材料股份有限公司 一种注塑模具用模具钢及其制备方法

Family Cites Families (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3401035A (en) * 1967-12-07 1968-09-10 Crucible Steel Co America Free-machining stainless steels
US3767390A (en) * 1972-02-01 1973-10-23 Allegheny Ludlum Ind Inc Martensitic stainless steel for high temperature applications
FR2567151B1 (fr) * 1984-07-04 1986-11-21 Ugine Aciers Procede de fabrication de barres ou de fil machine en acier inoxydable martensitique et produits correspondants
DE3672280D1 (de) * 1985-02-19 1990-08-02 Kawasaki Steel Co Sehr weicher rostfreier stahl.
EP0508574A1 (en) * 1991-04-11 1992-10-14 Crucible Materials Corporation Martensitic stainless steel article and method for producing the same
US6045633A (en) 1997-05-16 2000-04-04 Edro Engineering, Inc. Steel holder block for plastic molding
JP2002509195A (ja) 1998-01-16 2002-03-26 シーアールエス ホールディングス，インコーポレイテッド 快削用マルテンサイト系ステンレス鋼
JP3327853B2 (ja) * 1998-11-27 2002-09-24 日本高周波鋼業株式会社 耐発錆性に優れた快削ステンレス系金型用鋼

Also Published As

Publication number Publication date
US20020162614A1 (en) 2002-11-07
EP1233080A1 (de) 2002-08-21
DK1233080T3 (da) 2005-12-19
TW528811B (en) 2003-04-21
CN1370851A (zh) 2002-09-25
ATA2302001A (de) 2002-02-15
AT409636B9 (de) 2002-12-27
CN101041885A (zh) 2007-09-26
HK1107123A1 (zh) 2008-03-28
CN100558926C (zh) 2009-11-11
KR100500263B1 (ko) 2005-07-11
BR0200003B1 (pt) 2010-11-16
CA2371333A1 (en) 2002-08-14
AT409636B (de) 2002-09-25
KR20020066990A (ko) 2002-08-21
ES2247052T3 (es) 2006-03-01
DE50107038D1 (de) 2005-09-15
EP1233080B1 (de) 2005-08-10
US6893608B2 (en) 2005-05-17
CA2371333C (en) 2007-04-24

Similar Documents

Publication Publication Date Title
BR9602054A (pt) Aço e processo para fabricação de uma peça de alta resistência à abrasão; tal peça e utilização da mesma
BR0300280A (pt) Aço inoxidável dúplex para usinas de produção de uréia
BR0208629A (pt) Aço e tubulação em aço para uso à elevada temperatura
BR112015011302A2 (pt) chapa de aço laminada a quente com alta resistência que tem excelente endurecibilidade por cozimento e tenacidade de baixa temperatura com resistência à tração máxima de 980 mpa ou mais
BRPI0412746A (pt) aço inoxidável martensìtico
BRPI0614391B8 (pt) composição para a produção de aço, chapa de aço, processos para produção de uma chapa laminada à quente e à frio e uso de uma chapa de aço.
US3251682A (en) Low-alloy tough steel
KR970704901A (ko) 우수한 열간 가공성 및 황화물 응력 균열 저항을 가지는 마르텐사이트계 스테인리스 스틸(martensitic stainless steel having excellent hot workability and sulfide stress cracking resistance)
SE8403861L (sv) Martensitiskt utskiljningsherdbart stal
CA2412525A1 (en) Steel alloy, plastic moulding tool and tough-hardened blank for plastic moulding tools
CA2371333A1 (en) Steel for plastic molds and process for the heat treatment thereof
US2858206A (en) Nickel-free, low-alloy, high-strength steel
BR0315696A (pt) Peça de aço de construção soldável, processo para a fabricação de uma peça de aço soldável e processo para a fabricação de uma chapa de aço soldável
JPH10110248A (ja) 耐孔食性の優れた高硬度マルテンサイト系ステンレス鋼
BR0315695A (pt) Peça de aço de construção soldável, processo para a fabricação de uma peça de aço soldável e processo para a fabricação de uma chapa de aço soldável
ES2188103T3 (es) Utilizacion de acero debilmente aleado en aplicaciones que implican p ropiedades anti-coquizacion.
ATE267887T1 (de) Stahlmaterial, dessen verwendung und herstellung
DE69917444D1 (de) Wärmebehandlungsfähiger Werkzeugstahl mit hervorragender Bearbeitbarkeit und Kaltumformbarkeit; Matrizen aus diesem Stahl
JPS61147834A (ja) 耐食性高強度Ｎｉ基合金
JPS61279656A (ja) 熱間鍛造用非調質鋼
BRPI0710268A2 (pt) aço para trabalho a quente
JPH036352A (ja) 耐遅れ破壊性及び冷間鍛造性を備えた高強度ボルト用鋼
BR112022004010A2 (pt) Aço para facas, aço para facas de martensita, faca, e método de produção de aço para facas de martensita
JPS552743A (en) Steel excellent in damping performance and manufacture thereof
BR102015025517A2 (pt) aço para molas de alta força que tem excelentes propriedades de laminação de fio-máquina

Legal Events

Date Code Title Description
B06A Patent application procedure suspended [chapter 6.1 patent gazette]
B06A Patent application procedure suspended [chapter 6.1 patent gazette]
B09A Decision: intention to grant [chapter 9.1 patent gazette]
B16A Patent or certificate of addition of invention granted [chapter 16.1 patent gazette]

Free format text: PRAZO DE VALIDADE: 20 (VINTE) ANOS CONTADOS A PARTIR DE 03/01/2002, OBSERVADAS AS CONDICOES LEGAIS.

B21F Lapse acc. art. 78, item iv - on non-payment of the annual fees in time

Free format text: REFERENTE A 20A ANUIDADE.

B24J Lapse because of non-payment of annual fees (definitively: art 78 iv lpi, resolution 113/2013 art. 12)

Free format text: EM VIRTUDE DA EXTINCAO PUBLICADA NA RPI 2651 DE 26-10-2021 E CONSIDERANDO AUSENCIA DE MANIFESTACAO DENTRO DOS PRAZOS LEGAIS, INFORMO QUE CABE SER MANTIDA A EXTINCAO DA PATENTE E SEUS CERTIFICADOS, CONFORME O DISPOSTO NO ARTIGO 12, DA RESOLUCAO 113/2013.