Description

  

  Procédé de préparation d'alliages contenant du carbure de niobium.    La présente invention est relative à un  procédé de préparation d'alliages contenant  du carbure de niobium en partant de ma  tières contenant du niobium à l'état oxydé,  telles que minerais, sous-produits métallur  giques ou analogues.  



  Suivant la présente invention, la     matière     première est soumise à un chauffage avec  fusion de la masse en présence de carbone  et de fer, de manière à former des ferro  alliages dans lesquels le niobium se trouve  au moins pour sa plus grande partie sous  forme de carbure.  



  L'opération de réduction peut être effec  tuée dans tout four approprié, par exemple  dans     un    four électrique à arc.  



  Le ferro-alliage obtenu peut être soumis  à une épuration chimique. On le soumet no  tamment après l'avoir éventuellement, par  broyage ou granulation, amené au degré de  finesse voulu, à une attaque par un acide  approprié, tel l'acide sulfurique. Après éli-         mination    des éléments solubilisés dans cette  dernière opération, le résidu, dans lequel le       Nb    se retrouve à l'état de carbure, est     soumis     à une préparation     mécanique    appropriée, de  façon à en séparer les particules les plus  lourdes, constituées par les carbures de     Nb.     



  L'opération de réduction peut se faire  dans un four électrique, par exemple à arc,  dont le creuset ou la cuve, ou seulement une  partie de ces éléments, sont constitués par  des briques de carbone ou un pisé de car  bone, de manière à obtenir par     l'opération     de réduction un ferro-alliage dans lequel le  niobium est au moins pour sa plus grande  partie sous forme de carbure.



  Process for the preparation of alloys containing niobium carbide. The present invention relates to a process for preparing alloys containing niobium carbide, starting from materials containing niobium in the oxidized state, such as ores, metallurgical by-products or the like.



  According to the present invention, the raw material is subjected to heating with melting of the mass in the presence of carbon and iron, so as to form ferroalloys in which the niobium is at least for the most part in the form of carbide. .



  The reduction operation can be carried out in any suitable furnace, for example in an electric arc furnace.



  The ferroalloy obtained can be subjected to chemical purification. It is subjected in particular after having optionally, by grinding or granulation, brought to the desired degree of fineness, to attack by an appropriate acid, such as sulfuric acid. After removal of the elements solubilized in this last operation, the residue, in which the Nb is found in the carbide state, is subjected to an appropriate mechanical preparation, so as to separate the heaviest particles therefrom, consisting of carbides of Nb.



  The reduction operation can be carried out in an electric furnace, for example an arc furnace, of which the crucible or the vessel, or only part of these elements, are constituted by carbon bricks or a carbon rammed earth, so as to obtain by the operation of reduction a ferroalloy in which the niobium is at least for the greater part in the form of carbide.

Claims

CLAIM Process for the preparation of alloys containing niobium carbide, starting from materials containing niobium in the oxidized state, characterized in that the raw material is subjected to -a heating with melting of the mass in the presence of carbon and iron, so as to form ferro-alloys in which niobium is found at least for the most part in the form of earbure. SUBCLAIM A method according to claim. in which the. raw material is reduced in the presence of iron in a t, electric furnace of which at least part of the container for the mass being processed is;

internally coated with carbon.