CH295440A - Watch component. - Google Patents

Watch component.

Info

Publication number
CH295440A
CH295440A CH295440DA CH295440A CH 295440 A CH295440 A CH 295440A CH 295440D A CH295440D A CH 295440DA CH 295440 A CH295440 A CH 295440A
Authority
CH
Switzerland
Prior art keywords
sep
impurities
rest
alloy
gong
Prior art date
Application number
Other languages
German (de)
Inventor
Reinhard Dr Straumann
Original Assignee
Reinhard Dr Straumann
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Reinhard Dr Straumann filed Critical Reinhard Dr Straumann
Publication of CH295440A publication Critical patent/CH295440A/en

Description

  

      Uhrenbestandteil.       Die vorliegende Erfindung bezieht sich  auf einen     Uhrenbestandteil,    welcher aus einer       aushärtbaren    Legierung gefertigt ist. Als       Uhrenbestandteile        kommen    zum Beispiel  Anker, Triebfedern, Räder, Unruhen und der  gleichen, in Frage.  



  Als nichtmagnetische Bestandteile für  Uhren sind bis heute     Bestandteile    verwendet  worden, die aus     Berylliumbronze    bestehen  und in der Hauptsache Kupfer neben klei  neren Mengen     Beryllium    enthalten. Aus  dieser Legierung erzeugte Bestandteile haben  jedoch den     Nachteil,    dass sie leicht oxydieren  und deshalb durch galvanische     Überzüge     geschützt werden müssen. Diese     Überzüge     haften erfahrungsgemäss nicht sehr gut und  haben sich beispielsweise bei     Ankern        für     Uhren als     nachteilig    erwiesen, weil sie den  guten Gang stören.  



  Ferner werden im Patent     Nr.292475          Uhrenbestandteile    beschrieben, welche aus  einer Legierung bestehen, die neben den  üblichen     Verunreinigungen        mindestens    65%  Kupfer, höchstens 30% Nickel und höch  stens 30% Mangan enthält, und,     ähnlich     den     Beryllium-Kupfer-Legierungen,        aushärt-          bar    ist, die aber zum Beispiel für Bestandteile  des     Ankerganges    für Uhren nicht genügend  hart und     nicht    genügend     korrosionsbeständig     ist.  



  Überdies sind     Uhrenbestandteile,        wie     Anker, Unruhen, Räder usw., bekannt, welche  aus einer     Kupfer-Nickel-Mangan-Legierung       bestehen, die einen Nickel- und     Mangangehalt     von insgesamt mindestens 50% aufweist,       während    der Rest der Legierung aus Kupfer  nebst üblichen     Verunreinigungen    besteht.  Solche     Uhrenbestandteile        weisen.    eine ge  steigerte Härte und eine gute Korrosions  festigkeit auf, neigen aber nach längerem An  lassen zu Brüchigkeit, was sich in gewissen  Fällen     nachteilig    auswirkt.  



  Die     vorliegende        Erfindung    bezweckt,  diesen Nachteil zu beheben, und dies     wird    er  reicht durch Zugabe von Kobalt in     einer     Menge von 1 bis 200/,.  



  Der     Uhrenbestandteil    der     vorliegenden          Erfindung    ist dadurch     gekennzeichnet,    dass er  aus einer     Legierung    besteht, die     einen    Nickel  und     Mangangehalt    von insgesamt     mindestens     50% und einen     Kobaltgehalt    von 1 bis 20%  aufweist, während der Rest der Legierung in  -der Hauptsache aus Kupfer besteht.  



  Dank des     Kobaltzusatzes        wird    die Deh  nungsfähigkeit solcher     Uhrenbestandteile    und  demzufolge deren Bruchfestigkeit erheblich  verbessert.  



  Im folgenden seien einige Beispiele von  Legierungen, die sich     insbesondere        für    die  Herstellung von     Ankern,    jedoch auch für     Un-          ruhen    und Räder     eignen,    aufgezählt.     Selbst-          verständlich        können    Legierungen der nach  stehend     wiedergegebenen    Zusammensetzun  gen auch für andere Bestandteile für Uhren  Verwendung     finden.       
EMI0002.0001     
  
    <I>Beispiel <SEP> 1: <SEP> Beispiel <SEP> 2: <SEP> Beispiel <SEP> 3: <SEP> Beispiel <SEP> 4: <SEP> Beispiel <SEP> s:

   <SEP> Beispiel <SEP> 6:</I>
<tb>  Cu <SEP> 43 /a <SEP> Cu <SEP> 360/Q <SEP> Cu <SEP> 340/Q <SEP> Cu <SEP> 400/Q <SEP> Cu <SEP> 340/Q <SEP> Cu <SEP> 290/Q
<tb>  Co <SEP> 50/Q <SEP> Co <SEP> 50/Q <SEP> Co <SEP> 80/Q <SEP> Co <SEP> 20/Q <SEP> Co <SEP> 50/Q <SEP> Co <SEP> 10 /Q
<tb>  Ni <SEP> 250/Q <SEP> Ni <SEP> 280/Q <SEP> Ni <SEP> 220/Q <SEP> Ni <SEP> 340/Q <SEP> Ni <SEP> 300/Q <SEP> Ni <SEP> 310/Q
<tb>  Mn.25 /Q <SEP> Mn30 /Q <SEP> Mn <SEP> 35 /Q <SEP> Mn <SEP> 23 /Q <SEP> Mn <SEP> 30a/Q <SEP> Mn <SEP> 29%
<tb>  Rest <SEP> Rest <SEP> Rest <SEP> Rest <SEP> Rest <SEP> Rest
<tb>  Verunreini- <SEP> Verunreini- <SEP> Verunreini- <SEP> Verunreini- <SEP> Verunreini- <SEP> Verunreini  gungen <SEP> gongen <SEP> gongen <SEP> gongen <SEP> gongen <SEP> gongen
<tb>  <I>Beispiel <SEP> 7: <SEP> Beispiel <SEP> 8: <SEP> Beispiel <SEP> 9: <SEP> Beispiel <SEP> 10: <SEP> Beispiel <SEP> 11:

   <SEP> Beispiel <SEP> 12:</I>
<tb>  Cu <SEP> 20,5% <SEP> Cu <SEP> 330/Q <SEP> Cu <SEP> 260/Q <SEP> Cu <SEP> 280/Q <SEP> Cu <SEP> 430/Q <SEP> Cu <SEP> 37,5%
<tb>  Co <SEP> 20% <SEP> . <SEP> Co <SEP> 50/Q <SEP> Co <SEP> 40/Q <SEP> Co <SEP> 80/Q <SEP> Co <SEP> 50/Q <SEP> Co <SEP> 1%
<tb>  Ni <SEP> 100/Q <SEP> Ni <SEP> 150/Q <SEP> Ni <SEP> 210/Q <SEP> Ni <SEP> 280/Q <SEP> Ni <SEP> 25,5% <SEP> Ni <SEP> 16 /Q
<tb>  Mn, <SEP> 480/Q <SEP> Mn450/Q <SEP> Mn <SEP> 48 <SEP> 0/Q <SEP> Mn <SEP> 350/Q <SEP> Mn <SEP> 25, <SEP> 80/Q <SEP> Mn <SEP> 45 <SEP> 0/Q
<tb>  Rest <SEP> Rest <SEP> Rest <SEP> Rest <SEP> Rest <SEP> Rest
<tb>  Verunreini- <SEP> Verunreini- <SEP> Verunreini- <SEP> Verunreini- <SEP> Verunreini- <SEP> Verunreini  gungen <SEP> gongen <SEP> gongen <SEP> gongen <SEP> gongen <SEP> gongen



      Watch component. The present invention relates to a watch component made from a hardenable alloy. For example, anchors, mainsprings, wheels, balance wheels and the like come into question as watch components.



  As non-magnetic components for clocks, components have been used to this day that consist of beryllium bronze and mainly contain copper in addition to smaller amounts of beryllium. Components produced from this alloy, however, have the disadvantage that they are easily oxidized and therefore have to be protected by galvanic coatings. Experience has shown that these coatings do not adhere very well and have proven to be disadvantageous in the case of anchors for watches, for example, because they interfere with good running.



  Furthermore, watch components are described in patent no. 292475, which consist of an alloy which, in addition to the usual impurities, contains at least 65% copper, at most 30% nickel and at most 30% manganese, and, similar to beryllium-copper alloys, hardens. is bar, but is not sufficiently hard and not sufficiently corrosion-resistant for components of the anchor passage for watches, for example.



  In addition, watch components such as anchors, balance wheels, wheels, etc. are known which consist of a copper-nickel-manganese alloy with a total nickel and manganese content of at least 50%, while the remainder of the alloy is made of copper and the usual impurities consists. Such watch components have. increased hardness and good corrosion resistance, but tend to become brittle after prolonged tempering, which in certain cases has a disadvantageous effect.



  The present invention aims to remedy this drawback, and it will do so by adding cobalt in an amount of 1 to 200 /.



  The watch component of the present invention is characterized in that it consists of an alloy having a nickel and manganese content of at least 50% in total and a cobalt content of 1 to 20%, while the remainder of the alloy consists mainly of copper.



  Thanks to the addition of cobalt, the elasticity of such watch components and consequently their breaking strength is considerably improved.



  Some examples of alloys which are particularly suitable for the manufacture of armatures, but also for balance wheels and wheels, are listed below. It goes without saying that alloys of the compositions shown below can also be used for other components for watches.
EMI0002.0001
  
    <I> Example <SEP> 1: <SEP> Example <SEP> 2: <SEP> Example <SEP> 3: <SEP> Example <SEP> 4: <SEP> Example <SEP> s:

   <SEP> Example <SEP> 6: </I>
<tb> Cu <SEP> 43 / a <SEP> Cu <SEP> 360 / Q <SEP> Cu <SEP> 340 / Q <SEP> Cu <SEP> 400 / Q <SEP> Cu <SEP> 340 / Q <SEP> Cu <SEP> 290 / Q
<tb> Co <SEP> 50 / Q <SEP> Co <SEP> 50 / Q <SEP> Co <SEP> 80 / Q <SEP> Co <SEP> 20 / Q <SEP> Co <SEP> 50 / Q <SEP> Co <SEP> 10 / Q
<tb> Ni <SEP> 250 / Q <SEP> Ni <SEP> 280 / Q <SEP> Ni <SEP> 220 / Q <SEP> Ni <SEP> 340 / Q <SEP> Ni <SEP> 300 / Q <SEP> Ni <SEP> 310 / Q
<tb> Mn.25 / Q <SEP> Mn30 / Q <SEP> Mn <SEP> 35 / Q <SEP> Mn <SEP> 23 / Q <SEP> Mn <SEP> 30a / Q <SEP> Mn <SEP > 29%
<tb> rest <SEP> rest <SEP> rest <SEP> rest <SEP> rest <SEP> rest
<tb> Impurities- <SEP> Impurities- <SEP> Impurities- <SEP> Impurities- <SEP> Impurities- <SEP> Impurities <SEP> gong <SEP> gong <SEP> gong <SEP> gong <SEP> gong
<tb> <I> example <SEP> 7: <SEP> example <SEP> 8: <SEP> example <SEP> 9: <SEP> example <SEP> 10: <SEP> example <SEP> 11:

   <SEP> Example <SEP> 12: </I>
<tb> Cu <SEP> 20.5% <SEP> Cu <SEP> 330 / Q <SEP> Cu <SEP> 260 / Q <SEP> Cu <SEP> 280 / Q <SEP> Cu <SEP> 430 / Q <SEP> Cu <SEP> 37.5%
<tb> Co <SEP> 20% <SEP>. <SEP> Co <SEP> 50 / Q <SEP> Co <SEP> 40 / Q <SEP> Co <SEP> 80 / Q <SEP> Co <SEP> 50 / Q <SEP> Co <SEP> 1%
<tb> Ni <SEP> 100 / Q <SEP> Ni <SEP> 150 / Q <SEP> Ni <SEP> 210 / Q <SEP> Ni <SEP> 280 / Q <SEP> Ni <SEP> 25.5 % <SEP> Ni <SEP> 16 / Q
<tb> Mn, <SEP> 480 / Q <SEP> Mn450 / Q <SEP> Mn <SEP> 48 <SEP> 0 / Q <SEP> Mn <SEP> 350 / Q <SEP> Mn <SEP> 25, <SEP> 80 / Q <SEP> Mn <SEP> 45 <SEP> 0 / Q
<tb> rest <SEP> rest <SEP> rest <SEP> rest <SEP> rest <SEP> rest
<tb> Impurities- <SEP> Impurities- <SEP> Impurities- <SEP> Impurities- <SEP> Impurities- <SEP> Impurities <SEP> gongen <SEP> gong <SEP> gong <SEP> gong <SEP> gong

 

Claims (1)

PATENTANSPRUCI3 : Uhrenbestandteil, dadurch gekennzeich net, dass er aus einer Legierung besteht, die einen Nickel- und Mangangehalt von insge- samt mindestens 500/Q und einen Kobaltgehalt von 1 bis 200/Q aufweist, während der Rest der Legierung in der Hauptsache aus Kupfer besteht. PATENT CLAIM3: Watch component, characterized in that it consists of an alloy with a total nickel and manganese content of at least 500 / Q and a cobalt content of 1 to 200 / Q, while the rest of the alloy is mainly made of copper consists.
CH295440D 1951-08-07 1951-08-07 Watch component. CH295440A (en)