CH370248A - Matière frittée pour organes de frottement autolubrifiants - Google Patents

Matière frittée pour organes de frottement autolubrifiants

Info

Publication number
CH370248A
CH370248A CH340761A CH340761A CH370248A CH 370248 A CH370248 A CH 370248A CH 340761 A CH340761 A CH 340761A CH 340761 A CH340761 A CH 340761A CH 370248 A CH370248 A CH 370248A
Authority
CH
Switzerland
Prior art keywords
sep
material according
contains approximately
sintered material
self
Prior art date
Application number
CH340761A
Other languages
English (en)
Inventor
Grounauer Louis-Etienne
Gehrig Marcel
Original Assignee
Micropaliers S A
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Micropaliers S A filed Critical Micropaliers S A
Priority to CH340761A priority Critical patent/CH370248A/fr
Publication of CH370248A publication Critical patent/CH370248A/fr

Description


  Matière     frittée    pour organes de frottement     autolubrifiants            L'objet,    de l'invention est une matière frittée  destinée plus particulièrement à la fabrication de  paliers, de petite mécanique autolubrifiants à sec.  



  On sait que les matières frittées sont obtenues  par compression d'un mélange     intime    de poudres  fines. La matière frittée selon l'invention est obtenue  par compression à froid du mélange très poussé de  ses constituants, par chauffage pendant une ving  taine de minutes du produit comprimé, puis par une  seconde compression à chaud. Il est important que  le mélange de poudres soit au départ dans un état  d'humidité déterminé.  



  Ladite matière frittée est caractérisée par le fait  qu'elle comprend au moins deux métaux ne formant  pas un alliage et un     sulfure    métallique.  



  La partie métallique de la matière frittée     peut-          être    composée de cuivre et de zinc, de cuivre, zinc  et aluminium ou d'aluminium et d'étain.  



  Le     sulfure    métallique constitue l'agent lubrifiant  à sec ; il se trouve dans la matière frittée en propor  tion de 12 % par exemple, soit sous forme de sul  fure de fer     (FeS)    soit sous celle de     sulfure    de mo  lybdène     (MoS.).     



  On peut incorporer au mélange de départ en  viron 8 % d'un fondant tel que     B407Na2.        10H20,          B407Naz,        5H20,        B100lENa2.        10H20,        B(OH)3,        B203     et/ou une faible quantité de kaolin (environ<B>3%).</B>  



  Les matières frittées conformes à l'invention  conviennent particulièrement bien à la fabrication  des paliers de petite mécanique en raison de leur  très faible coefficient de frottement, de leur dureté       voisine    de celle des pivots et de leurs autres carac  téristiques physiques favorables.

    
EMI0001.0021     
  
    <I>Exemples <SEP> de <SEP> compositions <SEP> frittées <SEP> selon <SEP> l'invention</I>
<tb>  Métaux <SEP> Sulfure
<tb>  métallique <SEP> Fondant <SEP> Kaolin
<tb>  0/a <SEP>  /o <SEP> ,/o <SEP>  /o
<tb>  Cu <SEP> 60. <SEP> Zn <SEP> 20 <SEP> . <SEP> . <SEP> . <SEP> 12 <SEP> 8
<tb>  Cu <SEP> 39. <SEP> Zn <SEP> 15. <SEP> A126 <SEP> . <SEP> 12 <SEP> 8
<tb>  Cu <SEP> 61. <SEP> Zn <SEP> 27 <SEP> . <SEP> . <SEP> . <SEP> 12
<tb>  Cu <SEP> 42. <SEP> Zn <SEP> 18. <SEP> A128 <SEP> . <SEP> 12
<tb>  A128 <SEP> . <SEP> Sn <SEP> 60 <SEP> . <SEP> . <SEP> . <SEP> . <SEP> 12 <SEP> 3
<tb>  Cu <SEP> 40. <SEP> Zn <SEP> 17. <SEP> A128 <SEP> . <SEP> 12 <SEP> 3

Claims (1)

  1. REVENDICATION Matière frittée pour organes de frottement auto- lubrifiants, caractérisée par le fait qu'elle comprend au moins deux métaux ne formant pas un alliage et un sulfure métallique. SOUS-REVENDICATIONS 1. Matière selon la revendication, caractérisée par le fait qu'elle contient environ 12;% de sulfure métallique. 2. Matière selon la revendication, caractérisée par le fait que le sulfure métallique est le sulfure de fer (FeS). 3.
    Matière selon la revendication, caractérisée par le fait que le sulfure métallique est le sulfure de molybdène (MoS2). 4. Matière selon la revendication, caractérisée par le fait qu'elle contient environ<B>60%</B> de cuivre et 20 % de zinc. 5. Matière selon la revendication, caractérisée par le fait qu'elle contient environ 39 % de cuivre, 15 % de zinc et 26 % d'aluminium. 6. Matière selon la revendication et les sous- revendications 4 et 5, caractérisée par le fait qu'elle contient environ 8 % de fondant. 7.
    Matière selon la revendication et la sous- revendication 6, caractérisée par le fait que le fon dant est un composé du bore. 8. Matière selon la revendication, caractérisée par le fait qu'elle contient environ 61 % de cuivre et 27 % de zinc. 9. Matière selon la revendication, caractérisée par le fait qu'elle contient environ 42 % de cuivre, 18 % de zinc et 28 % d'aluminium. 10. Matière selon la revendication, caractérisée par le fait qu'elle contient environ 28 % d'alumi nium et 60 % d'étain. 11. Matière selon la revendication, caractérisée par le fait qu'elle contient environ 40 % de cuivre, 17 % de zinc et 28 % d'aluminium. 12.
    Matière selon la revendication et les sous revendications 10 et 11, caractérisée par le fait qu'elle contient environ 3 % de kaolin.
CH340761A 1961-03-22 1961-03-22 Matière frittée pour organes de frottement autolubrifiants CH370248A (fr)