CN101037822A - Method for producing spinning elasticized fabric by blending of two ingredient elastic polyester dacron and wool - Google Patents
Method for producing spinning elasticized fabric by blending of two ingredient elastic polyester dacron and wool Download PDFInfo
- Publication number
- CN101037822A CN101037822A CN200710020952.XA CN200710020952A CN101037822A CN 101037822 A CN101037822 A CN 101037822A CN 200710020952 A CN200710020952 A CN 200710020952A CN 101037822 A CN101037822 A CN 101037822A
- Authority
- CN
- China
- Prior art keywords
- wool
- elastic polyester
- fabric
- heat setting
- dyeing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a manufacturing method of worsted elastic fabrics by blending two components: elastic polyester terylene and wool. Said method comprises the following steps: cutting two-component elastic polyester terylene tow-beams into short fibres with a barbe length of 5 mm more or less than 85 mm, then manufacturing them into wool tops which are then dyed; mixing, drafting and blending 50-80% of wools and 20-50% of two-component elastic polyester terylene short-fibre wool tops; heat setting and pot-laying steaming the product mentioned above, with a heat setting temperature of 160-165 DEG C, wherein a small tensile force of 50-100 N is applied after the heat setting course; treating the product mentioned above firstly with a freshening agent of a 0.5-2% non-ionic and colorless liquid shaped modified cyclodextrin 711 (ROTTA-FRESH 711) and then with a crosslinking agent of 0.5-2% modified dihydroxymethyl dihydroxy ethyleneurea (ROTTA-FRESH 289), wherein the freshening agent of non-ionic and colorless liquid shaped modified cyclodextrin is crosslinked into the fabric permanently. During the weaving and finishing courses, said method exhibits easy processablity, excellent elasticity and size stability of finished product fabrics.
Description
Technical field
The present invention relates to the method for a kind of two ingredient elastic polyester dacron and wool blended production spinning elasticized fabric.Belong to textile technology field.
Background technology
The traditional elastic wool fabric generally adopts elastic filaments such as Lycra to improve the elasticity of fabric.This kind fabric is difficult for processing in weaving, afterwards putting in order, be prone to phenomenons such as fabric edge curl, folding line, elastic instability and the core that shows money or valuables one carries unintentionally, finished product fabric elasticity retentivity is poor, and relaxation easily takes place, fabric is difficult to reach better elastic and DIMENSIONAL STABILITY, and the colored type of fabric is subjected to certain limitation.
Summary of the invention
The objective of the invention is to overcome above-mentioned deficiency, a kind of two ingredient elastic polyester dacron that easily processing, finished product fabric elasticity and DIMENSIONAL STABILITY are good in weaving, afterwards putting in order and the method for wool blended production spinning elasticized fabric are provided.
The object of the present invention is achieved like this: the method for a kind of two ingredient elastic polyester dacron and wool blended production spinning elasticized fabric, it is characterized in that it comprise system bar, dyeing, with wool blend and fabric knitting, back arrangement and special finishing technology, each processing step is as follows:
A, system bar
The two ingredient elastic polyester dacron tow of 2～5 DENIER is cut into the staple fibre that fiber clings to cloth length 85 ± 5mm, make two ingredient elastic polyester dacron staple fibre wool top.
B, dyeing
The two ingredient elastic polyester dacron staple fibre wool top pinecone is placed in the top dyeing machine dyes, Winding Tension Controlling is 10～30CN, dyeing temperature 120 ℃ ± 2, it is to have the powerful high temperature resistant dressing agent MDL (non-ionic surface active agent MDL) 1%～5% that disperses the level dyeing effect that the inside and outside cycle frequency of dye liquor 2～5 times/minute, dyeing are selected auxiliary agent for use.
C and wool blend
Wool with 50%～80% and 20%～50% two ingredient elastic polyester dacron staple fibre wool top blending, add in the blending process with castor-oil plant be Main Ingredients and Appearance with crude oil 0.1～1% (percentage by weight) and polyoxyethylene deriv antistatic additive 1,166 0.1～2% (percentage by weight), needle plate needle gage 4～7cm, drafting tension 50～150CN.
D, fabric manufacturing
Same common process.
E, back arrangement
Being different from conventional operation part is: HEAT SETTING is put after jar steaming, 160～165 ℃ of heat setting temperatures (fabric shrink 5～15%), and each operation is taked small tension receiving coil 50～100N after the HEAT SETTING.
F, special finishing
Handle with 0.5～2% nonionic, colourless liquid shape modified cyclodextrin 711 (ROTTA-FRESH711) freshener earlier, use hydroxymethyl-2 dihydroxy-ethylene urea (ROTTA-FINISH289) crosslinking agent of 0.5～2% modification crosslinked then, permanent crosslinked in fabric nonionic, colourless liquid shape modified cyclodextrin freshener.
Compare with existing Lycra spinning elasticized fabric, the present invention has following advantage:
1, two ingredient elastic polyester dacron bar and the wool tops silver mixing that adopts the process of chopping to make, fiber is injury-free, and mixes.
2, dyeing make dye the colourless flower of two ingredient elastic polyester dacron staple fibre, do not have inside and outside aberration, soaping fastness, crabbing fastness all reach more than 4 grades.
3, postfinishing process makes lining have elasticity, soft and smooth property, drapability preferably.
4, fabric has bad smell functions such as absorption stink with perspiration, smoke, oil flavor after HEAT SETTING is handled, and washing back absorption peculiar smell function can activate again.
Through the improvement of above-mentioned technology, the performance that the present invention is superior shows the following aspects:
1, adopts two ingredient elastic polyester dacron staple fibre and wool blended, the easily processing in weaving, afterwards putting in order of this kind fabric, phenomenons such as fabric edge curl, folding line, elastic instability and the core that shows money or valuables one carries unintentionally can not appear, finished product fabric elasticity retentivity is good, relaxation can not take place, fabric can reach better elastic and DIMENSIONAL STABILITY, and the colored type of fabric can not be restricted.
2, fabric is frivolous, and feel is soft and smooth, and wrinkle resistance, drapability is good, face is smooth bright and clean.
3, fabric has bad smell functions such as absorption stink with perspiration, smoke, oil flavor, and washing back absorption peculiar smell function can activate again.
4, production cost has reduced by 10～45 yuan/meter (pressing assortment) than the similar Lycra fabric that contains.
The specific embodiment
Embodiment 1:
A, system bar
The two ingredient elastic polyester dacron tow of 2 DENIER adopt that patterning method makes that fiber is straight, 1/gram of card nailing neps quantity, fiber crust cloth length 85mm, disperse (%) 18, discrete length (%) 20, monofilament strength (CN) 8, percentage elongation (%) 60, crispation number of fineness is (individual/cm) 20 fiber.
B, dyeing
The two ingredient elastic polyester dacron fiber wool top pinecone is placed in the top dyeing machine dyes, Winding Tension Controlling is 10CN, 120 ℃ of dyeing temperatures, it is to have the powerful high temperature resistant dressing agent MDL (non-ionic surface active agent) 1% that disperses the level dyeing effect that the inside and outside cycle frequency of dye liquor 2 times/minute, dyeing are selected auxiliary agent for use.
C and wool blend
The mixed drawing-off blending of wool with 50% and 50% two ingredient elastic polyester dacron staple fibre, in the blending process in addition castor-oil plant be Main Ingredients and Appearance with crude oil 1% percentage by weight, with polyoxyethylene deriv antistatic additive 1,166 0.1% percentage by weights, needle plate needle gage 7cm, drafting tension 50CN.All the other same common process.
D, fabric manufacturing
Same common process
E, back arrangement
Being different from conventional operation part is: HEAT SETTING is put after jar steaming, 165 ℃ of heat setting temperatures, and each operation is taked small tension receiving coil 80CN after (fabric shrink 8%) HEAT SETTING.
F, special finishing
Handle with 2% nonionic, colourless liquid shape modified cyclodextrin (ROTTA-FRESH711) freshener earlier, use hydroxymethyl-2 dihydroxy-ethylene urea (ROTTA-FINISH289) crosslinking agent of 2% modification crosslinked then, permanent crosslinked in fabric nonionic, colourless liquid shape modified cyclodextrin (ROTTA-FRESH711) freshener.
Embodiment 2:
A, system bar
The two ingredient elastic polyester dacron tow of 3 DENIER adopt that patterning method makes that fiber is straight, 1/gram of card nailing neps quantity, fiber crust cloth length 85mm, disperse (%) 20, discrete length (%) 25, monofilament strength (CN) 10, percentage elongation (%) 60, crispation number of fineness is (individual/CM) 20 fiber.
B, dyeing
The two ingredient elastic polyester dacron fiber wool top pinecone is placed in the top dyeing machine dyes, Winding Tension Controlling is 10CN, 120 ℃ of dyeing temperatures, the inside and outside cycle frequency of dye liquor 2 times/minute, and it is to have the powerful high temperature resistant dressing agent MDL (non-ionic surface active agent) 2% that disperses the level dyeing effect that auxiliary agent is selected in dyeing for use.
C and wool blend
The mixed drawing-off blending of wool with 60% and 40% two ingredient elastic polyester dacron staple fibre, in the blending process in addition castor-oil plant be Main Ingredients and Appearance with crude oil 1.5% percentage by weight, with polyoxyethylene deriv antistatic additive 1,166 0.5% percentage by weights, needle plate needle gage 7cm, drafting tension 50CN.All the other same common process.
D, fabric manufacturing
Same common process
E, back arrangement
Being different from conventional operation part is: HEAT SETTING is put after jar steaming, 165 ℃ of heat setting temperatures, and each operation is taked small tension receiving coil 50N after (fabric shrink 10%) HEAT SETTING.
F, special finishing
Handle with 2% nonionic, colourless liquid shape modified cyclodextrin (ROTTA-FRESH711) freshener earlier, use hydroxymethyl-2 dihydroxy-ethylene urea (ROTTA-FINISH289) crosslinking agent of 2% modification crosslinked then, permanent crosslinked in fabric nonionic, colourless liquid shape modified cyclodextrin (ROTTA-FRESH711) freshener.
Embodiment 3:
A, system bar
The two ingredient elastic polyester dacron tow of 2.5 DENIER adopt that patterning method makes that fiber is straight, 1.5/gram of card nailing neps quantity, fiber crust cloth length 85mm, disperse (%) 18, discrete length (%) 20, monofilament strength (CN) 8, percentage elongation (%) 60, crispation number of fineness is (individual/CM) 20 fiber.
B, dyeing
The two ingredient elastic polyester dacron fiber wool top pinecone is placed in the top dyeing machine dyes, Winding Tension Controlling is 10CN, 120 ℃ of dyeing temperatures, the inside and outside cycle frequency of dye liquor 2 times/minute, and it is to have the powerful high temperature resistant dressing agent MDL (non-ionic surface active agent) 1% that disperses the level dyeing effect that auxiliary agent is selected in dyeing for use.
C and wool blend
The mixed drawing-off blending of wool with 65% and 35% two ingredient elastic polyester dacron staple fibre, in the blending process in addition castor-oil plant be Main Ingredients and Appearance with crude oil 1% percentage by weight, with polyoxyethylene deriv antistatic additive 1,166 0.1% percentage by weights, needle plate needle gage 7cm, drafting tension 50CN.All the other same common process.
D, fabric manufacturing
Same common process
E, back arrangement
Being different from conventional operation part is: HEAT SETTING is put after jar steaming, 160 ℃ of heat setting temperatures, and each operation is taked small tension receiving coil 50N after (fabric shrink 15%) HEAT SETTING.
F, special finishing
Handle with 2% nonionic, colourless liquid shape modified cyclodextrin (ROTTA-FRESH711) freshener earlier, use hydroxymethyl-2 dihydroxy-ethylene urea (ROTTA-FINISH289) crosslinking agent of 2% modification crosslinked then, permanent crosslinked in fabric nonionic, colourless liquid shape modified cyclodextrin (ROTTA-FRESH711) freshener.
Embodiment 4:
A, system bar
The two ingredient elastic polyester dacron tow of 2.5 DENIER adopt that patterning method makes that fiber is straight, 1.5/gram of card nailing neps quantity, fiber crust cloth length 85mm, disperse (%) 18, discrete length (%) 20, monofilament strength (CN) 8, percentage elongation (%) 60, crispation number of fineness is (individual/CM) 20 fiber.
B, dyeing
The two ingredient elastic polyester dacron fiber wool top pinecone is placed in the top dyeing machine dyes, Winding Tension Controlling is 12CN, 120 ℃ of dyeing temperatures, the inside and outside cycle frequency of dye liquor 2 times/minute, and it is to have the powerful high temperature resistant dressing agent MDL (non-ionic surface active agent) 1% that disperses the level dyeing effect that auxiliary agent is selected in dyeing for use.
C and wool blend
The mixed drawing-off blending of wool with 70% and 30% two ingredient elastic polyester dacron staple fibre, in the blending process in addition castor-oil plant be Main Ingredients and Appearance with crude oil 1% percentage by weight, with polyoxyethylene deriv antistatic additive 1,166 0.1% percentage by weights, needle plate needle gage 7cm, drafting tension 50CN.All the other same common process.
D, fabric manufacturing
Same common process
E, back arrangement
Being different from conventional operation part is: HEAT SETTING is put after jar steaming, 165 ℃ of heat setting temperatures, and each operation is taked small tension receiving coil 50N after (fabric shrink 15%) HEAT SETTING.
F, special finishing
Handle with 2% nonionic, colourless liquid shape modified cyclodextrin (ROTTA-FRESH711) freshener earlier, use hydroxymethyl-2 dihydroxy-ethylene urea (ROTTA-FINISH289) crosslinking agent of 2% modification crosslinked then, permanent crosslinked in fabric nonionic, colourless liquid shape modified cyclodextrin (ROTTA-FRESH711) freshener.
Embodiment 5:
A, system bar
The two ingredient elastic polyester dacron tow of 2 DENIER adopt that patterning method makes that fiber is straight, 1/gram of card nailing neps quantity, fiber crust cloth length 85mm, disperse (%) 18, discrete length (%) 20, monofilament strength (CN) 8, percentage elongation (%) 60, crispation number of fineness is (individual/CM) 20 fiber.
B, dyeing
The two ingredient elastic polyester dacron fiber wool top pinecone is placed in the top dyeing machine dyes, Winding Tension Controlling is 10CN, 120 ℃ of dyeing temperatures, the inside and outside cycle frequency of dye liquor 2 times/minute, and it is to have the powerful high temperature resistant dressing agent MDL (non-ionic surface active agent) 1% that disperses the level dyeing effect that auxiliary agent is selected in dyeing for use.
C and wool blend
The mixed drawing-off blending of wool with 80% and 20% two ingredient elastic polyester dacron staple fibre, in the blending process in addition castor-oil plant be Main Ingredients and Appearance with crude oil 1% percentage by weight, with polyoxyethylene deriv antistatic additive 1,166 0.1% percentage by weights, needle plate needle gage 7cm, drafting tension 50CN.All the other same common process.
D, fabric manufacturing
Same common process
E, back arrangement
Being different from conventional operation part is: HEAT SETTING is put after jar steaming, 160 ℃ of heat setting temperatures, and each operation is taked small tension receiving coil 100N after (fabric shrink 15%) HEAT SETTING.
F, special finishing
Handle with 2% nonionic, colourless liquid shape modified cyclodextrin (ROTTA-FRESH711) freshener earlier, use hydroxymethyl-2 dihydroxy-ethylene urea (ROTTA-FINISH289) crosslinking agent of 2% modification crosslinked then, permanent crosslinked in fabric nonionic, colourless liquid shape modified cyclodextrin (ROTTA-FRESH711) freshener.
Claims (1)
1, the method for a kind of two ingredient elastic polyester dacron and wool blended production spinning elasticized fabric, it is characterized in that it comprise system bar, dyeing, with wool blend and fabric knitting, back arrangement and special finishing technology, each processing step is as follows:
A, system bar
The two ingredient elastic polyester dacron tow of 2～5 DENIER is cut into the staple fibre that fiber clings to cloth length 85 ± 5mm, make two ingredient elastic polyester dacron staple fibre wool top;
B, dyeing
The two ingredient elastic polyester dacron staple fibre wool top pinecone is placed in the top dyeing machine dyes, Winding Tension Controlling is 10～30CN, dyeing temperature 120 ℃ ± 2, the inside and outside cycle frequency of dye liquor 2～5 times/minute, non-ionic surface active agent MDL 1%～5% is selected in dyeing for use;
C and wool blend
The mixed drawing-off blending of wool with 50%～80% and 20%～50% two ingredient elastic polyester dacron staple fibre wool top, add in the blending process with castor-oil plant be Main Ingredients and Appearance with crude oil 0.1～1% percentage by weight and polyoxyethylene deriv antistatic additive 1,166 0.1～2% percentage by weights, needle plate needle gage 4～7cm, drafting tension 50～150CN;
D, fabric manufacturing
E, back arrangement
HEAT SETTING is put after jar steaming, 160～165 ℃ of heat setting temperatures, and each operation is taked small tension receiving coil 50～100N after the HEAT SETTING;
F, special finishing
Handle with 0.5～2% nonionic, colourless liquid shape modified cyclodextrin 711 (ROTTA-FRESH711) freshener earlier, use hydroxymethyl-2 dihydroxy-ethylene urea (ROTTA-FIMSH289) crosslinking agent of 0.5～2% modification crosslinked then, permanent crosslinked in fabric nonionic, colourless liquid shape modified cyclodextrin freshener.