CN101288507A - Manufacturing technique of crease-shedding uniforms lining - Google Patents
Manufacturing technique of crease-shedding uniforms lining Download PDFInfo
- Publication number
- CN101288507A CN101288507A CNA2008100608789A CN200810060878A CN101288507A CN 101288507 A CN101288507 A CN 101288507A CN A2008100608789 A CNA2008100608789 A CN A2008100608789A CN 200810060878 A CN200810060878 A CN 200810060878A CN 101288507 A CN101288507 A CN 101288507A
- Authority
- CN
- China
- Prior art keywords
- temperature
- resin liquid
- lining
- crease
- uniforms
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a technique for manufacturing anti-wrinkle liner of suits. The technique comprises the processes of weaving base fabric, overflow and loose pre-treatment, immersing in resin liquid and rolling, drying, gluing, baking, coiling and so on. The technique adopts environment-friendly resin liquid with high quality for twice-immersing and twice-rolling treatment which causes the resin liquid to sufficiently permeate into fibers and to become uniformly cross-linking, leads the treated fabric to obtain good anti-wrinkle recoverability and solid hand feeling. Nylon polyamine hotmelt adhesive is used for double-dot coating, which is characterized by strong adhesion fastness, having good drapability after being bonded with the fabric and excellent anti-wrinkle property when in use. The lining cloth has soft hand feeling and good anti-wrinkle property. Suits made from the lining cloth have the advantages of fullness and being docile. The anti-wrinkle property and sizing property after washing are better than any other ordinary adhesive lining cloth. The lining cloth is mainly used for wash-and-wear suits and career wears.
Description
[technical field]
The present invention relates to a kind of textile technology, more particularly, is a kind of production technology of crease-shedding uniforms lining.
[background technology]
Present western-style clothes lining product all is that to select polyster fibre for use be that raw material carries out base cloth and weaves, base cloth through overflow pre-treatment and the arrangement of typing back after, adopt polyamide hot to carry out the two point coating again and form.
This western-style clothes lining with have non-ironing require lining bonding after, after fabric had been subjected to crimping or washing, the lining after bonding can produce folding line or wrinkle, influences the attractive in appearance and clean and tidy of clothes, must can not reach non-ironing requirement along replying smooth or well-pressed outward appearance through flatiron.
[summary of the invention]
Purpose of the present invention solves the problems of the prior art exactly, proposes a kind of production technology of crease-shedding uniforms lining, can make the western-style clothes lining cloth soft, and has good wrinkle resistance.
For achieving the above object, the present invention proposes a kind of production technology of crease-shedding uniforms lining, in turn include the following steps:
Base cloth is weaved: warp thread adopts the R40S spun rayon yarn, and weft yarn adopts the T75D polyester low stretch yarn, weaves through full-automatic jet plane;
The pre-treatment of overflow pine formula: the base cloth after weaving carries out expanded, the loose pre-setting of preshrunk through overflow machine to be handled;
Pad resin liquid: normal temperature adopts resin liquid that base cloth is padded processing down, and pick-up rate is 70%, and the proportioning of resin liquid is: resin finishing agent: 80 grams per liters; Softening agent: 20 grams per liters; Bleeding agent: 2 grams per liters; Mgcl
2: 12 grams per liters;
Oven dry: first low temperature preliminary drying, middle again temperature oven dry, high temperature bakes then, cools off cropping again;
Point glue: adopt the nylon polyamide hot to carry out the two point coating;
Bake and batch: after baking under 190-205 ℃ the temperature, batch.
As preferably, described pad to pad in the resin liquid step to handle adopt two to soak two and roll.
As preferably, described baking step is to adopt 50 ℃-60 ℃ temperature preliminary drying 3-5 minute earlier, adopt again 90 ℃-100 ℃ temperature with fabric drying to moisture content 10%, adopt 150 ℃-160 ℃ temperature to bake 60-90 second then, cool off cropping again.
As preferably, cylinder order number: CP40 in the described some glue step, the speed of a motor vehicle: 40m/min, drying room temperature: 170-180 ℃, workshop condition temperature: 20-30 ℃.
Beneficial effect of the present invention: the present invention adopts the resin liquid choose high-quality environmental protection to carry out two to soak two and roll processing, make the abundant infiltrated fiber of resin liquid inside, and make it crosslinked evenly, make the fabric after the arrangement obtain good crease recovery, plentiful feel.Adopt the nylon polyamide hot to carry out the two point coating, bonding intensity is strong, drapability is preferably arranged with lining after bonding, can play excellent wrinkle resistance when dress is used.Fabric is after handling through resin liquid, resin finishing agent just and the molecule of amorphous region generate covalent cross-linking between strong, stretched out the strand that two strong " big hands " hold on to the amorphous region just as the finishing agent unimolecule, produce the effect that pins down and fix at the fiber molecule interchain, make it can not produce relative displacement, so just reduce the deformation of not replying immediately, thereby improved the deformation recovery ability of fiber.The lining cloth of producing is soft in sense, has good wrinkle resistance, and the western-style clothes of selecting for use this lining cloth to make is plentiful, docile, and its wrinkle resistance, to wash the back constancy be that common adhesive lining is incomparable, and product is mainly used in the western-style clothes of various non-ironing requirements and business wear with lining.
Feature of the present invention and advantage will be elaborated in conjunction with the accompanying drawings by embodiment.
[description of drawings]
Fig. 1 is the process chart of the production technology of a kind of crease-shedding uniforms lining of the present invention.
[specific embodiment]
Consult Fig. 1, a kind of production technology of crease-resistant two clothes linings in turn includes the following steps:
Base cloth weaves 1: warp thread adopts the R40S spun rayon yarn, and weft yarn adopts the T75D polyester low stretch yarn, weaves through full-automatic jet plane.Warp thread and weft yarn form through " 3+1 " twill weave.
Overflow pine formula pre-treatment 2: the base cloth after weaving carries out expanded, the loose pre-setting of preshrunk through overflow machine to be handled.
Pad resin liquid 3: normal temperature adopts resin liquid that base cloth is padded processing down, and pick-up rate is about 70%, and the proportioning of resin liquid is: resin finishing agent ECO:80 grams per liter; Softening agent NTL-1:20 grams per liter; Penetrating agent JFC: 2 grams per liters; Mgcl
2: 12 grams per liters.Pad and handle to adopt two to soak two and roll, so-called two soak two roll be exactly base cloth in padding liquid through secondary " dipping → roll compacting " process, padding liquid is clamp-oned organizing in the space of base cloth, and, padding liquid is evenly distributed on the fabric except that unnecessary padding liquid.Its crease-resistant mechanism is to have improved the crease recovery ability of fabric greatly through behind the anti-crease finishing, has promptly improved the elasticity of fabric.Fabric is after handling through finishing agent, finishing agent just and the molecule of amorphous region generate covalent cross-linking between strong, stretched out the strand that two strong " big hands " hold on to the amorphous region just as the finishing agent unimolecule, produce the effect that pins down and fix at the fiber molecule interchain, make it can not produce relative displacement, so just reduce the deformation of not replying immediately, thereby improved the deformation recovery ability of fiber.
Oven dry 4: first low temperature preliminary drying, middle again temperature oven dry, high temperature bakes then, cools off cropping again.Be introduced into temperature preliminary drying 3-5 minute that pre-baking oven adopts 50 ℃-60 ℃, enter again drying baker adopt 90 ℃-100 ℃ temperature with fabric drying to moisture content about 10%, the oven dry back is for stablizing the shrinkage of base cloth, need bake, adopt 150 ℃-160 ℃ temperature to bake 60-90 second, cool off cropping at last again.
Point glue 5: adopt the nylon polyamide hot to carry out the two point coating.The gluing process parameter is: cylinder order number: CP40, the speed of a motor vehicle: 40m/min, drying room temperature: 170-180 ℃, workshop condition temperature: 20-30 ℃.
Bake and batch 6: after baking under 190-205 ℃ the temperature, batch.
The foregoing description is to explanation of the present invention, is not limitation of the invention, and any scheme after simple transformation on the basis of the present invention all belongs to protection scope of the present invention.
Claims (4)
1. the production technology of a crease-shedding uniforms lining is characterized in that: in turn include the following steps:
Base cloth is weaved (1): warp thread adopts the R40S spun rayon yarn, and weft yarn adopts the T75D polyester low stretch yarn, weaves through full-automatic jet plane;
The formula pre-treatment (2) of overflow pine: the base cloth after weaving carries out expanded, the loose pre-setting of preshrunk through overflow machine to be handled;
Pad resin liquid (3): normal temperature adopts resin liquid that base cloth is padded processing down, and pick-up rate is 70%, and the proportioning of resin liquid is: resin finishing agent: 80 grams per liters; Softening agent: 20 grams per liters; Bleeding agent: 2 grams per liters; Mgcl
2: 12 grams per liters;
Oven dry (4): first low temperature preliminary drying, middle again temperature oven dry, high temperature bakes then, cools off cropping again;
Point glue (5): adopt the nylon polyamide hot to carry out the two point coating;
Bake and batch (6): after baking under 190-205 ℃ the temperature, batch.
2. the production technology of a kind of crease-shedding uniforms lining as claimed in claim 1 is characterized in that: described pad to pad in resin liquid (3) step to handle adopt two to soak two and roll.
3. the production technology of a kind of crease-shedding uniforms lining as claimed in claim 1, it is characterized in that: described oven dry (4) step is to adopt earlier 50 ℃-60 ℃ temperature preliminary drying 3-5 minute, adopt again 90 ℃-100 ℃ temperature with fabric drying to moisture content 10%, adopt 150 ℃-160 ℃ temperature to bake 60-90 second then, cool off cropping again.
4. as the production technology of claim 1 or 2 or 3 described a kind of crease-shedding uniforms linings, it is characterized in that: cylinder order number: CP40 in described glue (5) step, the speed of a motor vehicle: 40m/min, drying room temperature: 170-180 ℃, workshop condition temperature: 20-30 ℃.