CN101597457A - Nanometer photocatalyst aqueous polyester coating for woodenware - Google Patents
Nanometer photocatalyst aqueous polyester coating for woodenware Download PDFInfo
- Publication number
- CN101597457A CN101597457A CNA2008100165672A CN200810016567A CN101597457A CN 101597457 A CN101597457 A CN 101597457A CN A2008100165672 A CNA2008100165672 A CN A2008100165672A CN 200810016567 A CN200810016567 A CN 200810016567A CN 101597457 A CN101597457 A CN 101597457A
- Authority
- CN
- China
- Prior art keywords
- woodenware
- nanometer
- nano
- polyester coating
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a kind of nanometer photocatalyst aqueous polyester coating for woodenware with disinfection and clean flavor aldehydes removal function, its element comprises following composition: nano aqueous organosilicon crylic acid latex 10-30, nano aqueous polyaminoester emulsion 70-90, deionized water 10, nano photo-catalytic 5, nanometer formaldehyde-trapping agent 2, and dispersion agent, defoamer, film coalescence aid, wetting agent, wax liquid and levelling thickening material etc.Mainly be to have added nano photo-catalytic auxiliary agent and nanometer formaldehyde-trapping agent among the preparation method, adopt polyaminoester emulsion and organosilicon-modified acrylic emulsion, this nanometer photocatalyst aqueous polyester coating for woodenware has increased the hardness of paint film, can effectively decompose, toxic and harmfuls such as benzene, formaldehyde in the decontamination chamber, play the effect that purifies air, have germ-resistant effect, better to the perviousness of sheet material.
Description
Technical field
The present invention relates to the chemistry painting industry technical field, particularly have the nanometer photocatalyst aqueous polyester coating for woodenware and the preparation method of disinfection and clean flavor aldehydes removal function.
Background technology
Along with the enhancing of people to the finishing environmental consciousness, aqueous woodware paint seldom, does not fire the welcome that advantages such as not quick-fried high security, xanthochromia, brushing area be not big more and more are subjected to market with its asepsis environment-protecting, odorlessness, volatilizable thing.The insider claims that the development of water-miscible paint will be trend of the times, and with the full substitution oil-base paint.
Aqueous woodware paint in the market has a variety of, but is mainly pure third, benzene emulsion system.Their main drawback is a difference of hardness, and the paint film fullness ratio is poor, and does not have the function of disinfection and the aldehydes removal of clean flavor.
Summary of the invention
The purpose of this invention is to provide a kind of nanometer photocatalyst aqueous polyester coating for woodenware with disinfection and clean flavor aldehydes removal function, this nanometer photocatalyst aqueous polyester coating for woodenware toxic and harmful such as formaldehyde in the air of degrading effectively, can effectively kill various bacteria, also possess functions such as deodorizing, anti-soil simultaneously.
Another object of the present invention provides a kind of above-mentioned method with nanometer photocatalyst aqueous polyester coating for woodenware of disinfection and clean flavor aldehydes removal function for preparing.
The objective of the invention is to be achieved through the following technical solutions: a kind of nanometer photocatalyst aqueous polyester coating for woodenware with disinfection and clean flavor aldehydes removal function, its element comprises following composition:
(1), the nano aqueous organosilicon crylic acid latex 10
(2), the nano aqueous polyaminoester emulsion 90
(3), deionized water 10
(4), dispersion agent 0.3-0.5
(5), defoamer 0.3-0.5
(6), film coalescence aid 5-10
(7), antimildew disinfectant 0.05-0.1
(8), wetting agent 0.1-0.2
(9), wax liquid 2-5
(10), essence 0.1
(11), nano photo-catalytic 5
(12), the nanometer formaldehyde-trapping agent 2
(13), levelling thickening material 0.5-1.2
Another object of the present invention is achieved through the following technical solutions:
A, (1) in the mentioned component is put in the high speed dispersor that rotating speed is 1500-2000rpm, jitter time is 10 minutes;
B, will put stirrer into, under the stirring velocity of 200-400rpm, stir 20 minutes, mix through product and (2) that steps A obtains;
C, (3) added in the stirrer stirred 10 minutes, mix;
D, (4) (5) are added in the stirrer, stirs after 15 minutes, slowly add (6), (7), (8), (9), (10), (11), (12), (13) stirring more successively;
E, will not have shrinkage cavity through the product inspection that step D obtains after, both filter and package finished product.
In technique scheme, nano photo-catalytic auxiliary agent and nanometer formaldehyde-trapping agent have been added;
In technique scheme, adopt polyaminoester emulsion and organosilicon-modified acrylic emulsion.
The present invention compared with prior art, its advantage is: 1, adopted polyaminoester emulsion and organosilicon-modified acrylic emulsion to increase the hardness of paint film, can reach 2-3H, not only can be used for house decoration, can also use with varnish as furniture; 2, add formaldehyde-trapping agent, can effectively decompose, toxic and harmful such as phenyl aldehyde in the decontamination chamber, played the effect that purifies air, reached pregnant woman and baby's health demand standard; 3, add the nano photo-catalytic auxiliary agent, have germ-resistant effect; 4, emulsion adopts the nano level product, and is better to the perviousness of sheet material.
Embodiment
The invention will be further described below in conjunction with embodiment.
Embodiment one:
Following steps are 500kg priming paint production tables:
Nano aqueous organosilicon crylic acid latex: 10kg
Nano aqueous polyaminoester emulsion: 90kg
Deionized water: 50kg
Dispersion agent: 2kg
Defoamer: 1.5kg
Film coalescence aid: 25kg
Antimildew disinfectant: 0.5kg
Wetting agent: 0.2kg
Wax liquid: 2kg
Essence: 0.1kg
Nano photo-catalytic: 5kg
Nanometer formaldehyde-trapping agent: 2kg
Levelling thickening material: 0.5kg
The preparation technology of the foregoing description is:
1, the nano aqueous organosilicon crylic acid latex is put in the high speed dispersor that rotating speed is 1500-2000rpm, jitter time is 10 minutes;
2, will put stirrer into through product and nano aqueous polyaminoester emulsion that steps A obtains, under the stirring velocity of 200-400rpm, stir 20 minutes, mix;
3, deionized water is added in the stirrer and to stir 10 minutes, mix;
4, dispersion agent, defoamer are added in the stirrer, stir after 15 minutes, slowly add film coalescence aid, antimildew disinfectant, wetting agent stirring, wax liquid, essence, thickening material, nano photo-catalytic, nanometer formaldehyde-trapping agent more successively;
5, will not have shrinkage cavity through the product inspection that above-mentioned steps obtains after, both filter and package finished product.Embodiment two:
Following steps are 500kg finish paint production tables:
Nano aqueous organosilicon crylic acid latex: 10kg
Nano aqueous polyaminoester emulsion: 90kg
Deionized water: 50kg
Dispersion agent: 1.5kg
Defoamer: 0.5kg
Film coalescence aid: 10kg
Antimildew disinfectant: 0.25kg
Wetting agent: 0.1kg
Wax liquid: 1kg
Essence: 0.1kg
Flatting silica: 1kg
Levelling thickening material: 2.5kg
Nano photo-catalytic: 5kg
Nanometer formaldehyde-trapping agent: 2kg
The preparation technology of the foregoing description is:
1, the nano aqueous organosilicon crylic acid latex is put in the high speed dispersor that rotating speed is 1500-2000rpm, jitter time is 10 minutes;
2, will put stirrer into through product and nano aqueous polyaminoester emulsion that steps A obtains, under the stirring velocity of 200-400rpm, stir 20 minutes, mix;
3, deionized water is added in the stirrer and to stir 10 minutes, mix;
4, dispersion agent, defoamer are added in the stirrer, stir after 15 minutes, slowly add film coalescence aid, antimildew disinfectant, wetting agent stirring, wax liquid, essence, flatting silica, thickening material, nano photo-catalytic, nanometer formaldehyde-trapping agent more successively;
5, will not have shrinkage cavity through the product inspection that above-mentioned steps obtains after, both filter and package finished product.
Claims (5)
1, a kind of have disinfection and the nanometer photocatalyst aqueous polyester coating for woodenware of the aldehydes removal function of distinguishing the flavor of only, and its element comprises following composition:
(1), nano aqueous organosilicon crylic acid latex 10-30
(2), nano aqueous polyaminoester emulsion 70-90
(3), deionized water 10
(4), dispersion agent 0.3-0.5
(5), defoamer 0.3-0.5
(6), film coalescence aid 5-10
(7), antimildew disinfectant 0.05-0.1
(8), wetting agent 0.1-0.2
(9), wax liquid 2-5
(10), essence 0.1
(11), nano photo-catalytic 5
(12), the nanometer formaldehyde-trapping agent 2
(13), levelling type thickening material 0.5-1.2
2, a kind ofly prepare that claim 1 is described to have disinfection and the method for the nanometer photocatalyst aqueous polyester coating for woodenware of the aldehydes removal function of distinguishing the flavor of only, it is characterized in that may further comprise the steps:
A, (1) in the mentioned component is put in the high speed dispersor that rotating speed is 1500-2000rpm, jitter time is 10 minutes;
B, will put stirrer into, under the stirring velocity of 200-400rpm, stir 20 minutes, mix through product and (2) that steps A obtains;
C, (3) added in the stirrer stirred 10 minutes, mix;
D, (4) (5) are added in the stirrer, stirs after 15 minutes, slowly add (6), (7), (8), (9), (10), (11), (12), (13) stirring more successively;
E, will not have shrinkage cavity through the product inspection that step D obtains after, both filter and package finished product.
3, according to claim 1 have disinfection and the nanometer photocatalyst aqueous polyester coating for woodenware of the aldehydes removal function of distinguishing the flavor of only, it is characterized in that having added nano photo-catalytic auxiliary agent and nanometer formaldehyde-trapping agent.
4, according to claim 1 have disinfection and the nanometer photocatalyst aqueous polyester coating for woodenware of the aldehydes removal function of distinguishing the flavor of only, it is characterized in that adopting polyaminoester emulsion and organosilicon-modified acrylic emulsion.
5, according to claim 1 have disinfection and the nanometer photocatalyst aqueous polyester coating for woodenware of the aldehydes removal function of distinguishing the flavor of only, it is characterized in that emulsion adopts the nano level product.