CN101993595A - No-toxicity anti-bacterium negative ion material - Google Patents
No-toxicity anti-bacterium negative ion material Download PDFInfo
- Publication number
- CN101993595A CN101993595A CN2009100176563A CN200910017656A CN101993595A CN 101993595 A CN101993595 A CN 101993595A CN 2009100176563 A CN2009100176563 A CN 2009100176563A CN 200910017656 A CN200910017656 A CN 200910017656A CN 101993595 A CN101993595 A CN 101993595A
- Authority
- CN
- China
- Prior art keywords
- negative ion
- powder
- toxicity
- bacterium
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a no-toxicity anti-bacterium negative ion material. No-toxicity and tasteless glutin is used as a carrier to be directly sprayed onto a wall surface, and the no-toxicity and tasteless glutin can be also used as an addictive to be added with a dope, a paint and the like, and also can be smeared on the surface of a fabric and the like. The no-toxicity anti-bacterium negative ion material provided by the invention is characterized by comprising the following components in percentage by weight: 25-50 of negative ion powder, 0.5-5 of nanometer titanium dioxide, 10-20 of tomalin powder, 2-15 of zinc oxide powder, 0.01-1.0 of silver antibacterial agent and the balance of glutin aqueous solution. In the invention, the no-toxicity anti-bacterium negative ion material has the advantages of simple preparation process and low cost, can release the negative ions and has extremely remarkable effect on sterilization.
Description
Technical field
The invention belongs to the technical field of functional type material, particularly relate to a kind of nontoxic antibacterial anionic material.
Background technology
As everyone knows, bacterium is the seed of trouble of harm humans health, and bacterium can cause all kinds of epiphytotics generations.Conventional at present sterilization generally adopts the spraying disinfection method to kill the bacterium of indoor and outdoor, but environment is polluted, and sterilization effect is not lasting, and bacterium easily develops immunity to drugs, but also needs carry out every day.In environmental evaluation, negative ion concentration is listed in an important parameter weighing Air quality in the air, and the negative ion of proper concn offsets the obnoxious flavour in the deacration in the air, suppresses bacterium and purifies air, to people's good health and a long life and ecotope, all has important effect of crisis.Therefore how to begin one's study environment purification and create an environment that is rich in negative ion of increasing people promotes health.
Chinese patent ZL03129256.9 provides a kind of antibacterial anionic coating; Chinese patent ZL03153116.4 then provides a kind of negative ion paint additive, and they all are the coating of research, and preparation technology is more loaded down with trivial details.
Summary of the invention
The invention provides a kind of nontoxic antibacterial anionic material, utilize nonpoisonous and tasteless gelatin to make carrier, can directly spray metope, also can do additive, add coating, paint etc. to.Can also spread upon fabric face etc.
Technical scheme of the present invention is as follows:
A kind of nontoxic antibacterial anionic material is characterized in that: contain following ingredients:
Composition weight %
Negative ion powder 25-50
Nano titanium oxide 0.5-5
Tourmaline powder 10-20
Oxide powder and zinc 2-15
Silver-series antibacterial agent 0.01-1.0
The aqueous gelatin solution surplus
Nontoxic antibacterial anionic material provided by the invention, described aqueous gelatin solution is that gelatin is dissolved in the water, its weight concentration is 25-50%.
Antibacterial anionic material provided by the invention, described silver-series antibacterial agent are a kind of or two kinds of mixtures in Silver Nitrate, the Sulfuric acid disilver salt.
Making processes of the present invention is: gets gelatin and adds in the water, and heating, stirring and dissolving under less than 500 rev/mins stirring at low speed, adds negative ion powder, nano titanium oxide, Tourmaline powder, oxide powder and zinc, Silver Nitrate respectively then.Strengthen rotating speed then gradually, make abundant dispersion, dissolving, become uniform solution.
Gelatin is a kind of tasteless, colourless (slightly light yellow), translucent, hard non-crystalline state thing, it is insoluble to organic solvent, its water-absorbent is strong, viscosity is high, be widely used in weaving, printing, printing and dyeing, plastics, electronics, national defence, aviation, coated abrasive, match, China ink, loading material of rubber, artwork stickup, wood furniture, leather glazing, dyeing and weaving starching, metallurgical plating bath, bill be coated with matter, cosmetic hair jelly, etc. in industry and the department.The present invention adopts nonpoisonous and tasteless gelatin to do carrier, the nontoxic antibacterial anionic material scope of application that provides is extensive, and preparation technology is simple, cost is low, sterilization effect is obvious especially, detect through national Disease Control and Prevention Center,, can reach 100% sterilization effect as intestinal bacteria, streptococcus aureus etc. to can morbific bacterium.
Embodiment
Embodiment 1:
Negative ion powder 500
Nano titanium oxide 50
Tourmaline powder 100
Oxide powder and zinc 20
Silver Nitrate 2
Aqueous gelatin solution 328
Making processes of the present invention is: get 82 parts of gelatin and add in 246 parts of water, heating, stirring and dissolving under less than 500 rev/mins stirring at low speed, adds 500 parts of negative ion powders, 50 parts of nano titanium oxides, 100 parts of Tourmaline powder, 20 parts of oxide powder and zincs, 2 parts of Silver Nitrates respectively then.Strengthen rotating speed then gradually, make abundant dispersion, dissolving, become uniform solution.
Embodiment 2:
Negative ion powder 250
Nano titanium oxide 5
Tourmaline powder 200
Oxide powder and zinc 150
Sulfuric acid disilver salt 10
Aqueous gelatin solution 385
Making processes of the present invention is: get 190 parts of gelatin and add in 195 parts of water, heating, stirring and dissolving under less than 500 rev/mins stirring at low speed, adds 250 parts of negative ion powders, 5 parts of nano titanium oxides, 200 parts of Tourmaline powder, 150 parts of oxide powder and zincs, 10 parts of Sulfuric acid disilver salts respectively then.Strengthen rotating speed then gradually, make abundant dispersion, dissolving, become uniform solution.
Embodiment 3:
Negative ion powder 500
Nano titanium oxide 50
Tourmaline powder 100
Oxide powder and zinc 20
Silver Nitrate 2
Sulfuric acid disilver salt 5
Aqueous gelatin solution 323
Making processes of the present invention is: get 80 parts of gelatin and add in 250 parts of water, heating, stirring and dissolving, under less than 500 rev/mins stirring at low speed, add 500 parts of negative ion powders, 50 parts of nano titanium oxides, 100 parts of Tourmaline powder, 20 parts of oxide powder and zincs, 2 parts of Silver Nitrates, 5 parts of Sulfuric acid disilver salts respectively then.Strengthen rotating speed then gradually, make abundant dispersion, dissolving, become uniform solution.
Claims (3)
1. nontoxic antibacterial anionic material is characterized in that: contain following ingredients:
Composition weight %
Negative ion powder 25-50
Titanium valve 0.5-5
Tourmaline powder 10-20
Oxide powder and zinc 2-15
Silver-series antibacterial agent 0.01-1.0
The aqueous gelatin solution surplus
2. antibacterial anionic material according to claim 1 is characterized in that: described aqueous gelatin solution is that gelatin is dissolved in the water, and its weight concentration is 25-50%.
3. antibacterial anionic material according to claim 1 and 2 is characterized in that: described silver-series antibacterial agent is a kind of or two kinds of mixtures in Silver Nitrate, the Sulfuric acid disilver salt.