CN102732111A - Wear-resistant antiskid paint - Google Patents

Abstract

The invention relates to a paint and aims to provide a wear-resistant antiskid paint which is fast to dry and easy to construct and has excellent physical properties and chemical properties. The paint comprises the following raw materials of: by weight, 50-60 parts of acrylic resin, 5-8 parts of titanium dioxide, 0.2-0.3 part of carbon black, 1-5 parts of a thickening agent, 3-6 parts of an anti-settling agent, 30-40 parts of emery, and 0.1-0.2 part of a flexibilizer. Combining physical antiskid performance with chemical anticorrosion performance, the product is fast to dry and easy for construction and is a wear-resistant antiskid paint with excellent physical properties and chemical properties. The product has high wear resistance and a good antiskid effect, can be widely applied for skid resistance and anticorrosion of a storage tank, a ladder, roof slop and a passageway, and has protection and safe production effects.

Description

Wear-resistant anti-slip coating

technical field

The invention relates to a paint, in particular to a wear-resistant and anti-slip acrylic one-component paint.

Background technique

At present, most of the existing similar products in domestic fishing use polyurethane, epoxy resin, etc. as adhesives, and use quartz sand, corundum or rubber particles to make a surface-like anti-skid coating similar to sandpaper. These products have better initial anti-skid effect, but after being trampled for a period of time, the anti-skid effect will obviously decrease after the dust is bonded, and the due anti-skid effect cannot be achieved. Therefore, a wear-resistant anti-skid coating is provided.

Contents of the invention

The purpose of the present invention is to provide a wear-resistant anti-skid coating which is fast drying, easy to apply, and has excellent physical and chemical properties.

Task of the present invention is accomplished by the following technical solutions:

A wear-resistant anti-slip coating, comprising the following raw materials in parts by weight: acrylic resin: 50-60 parts; titanium dioxide: 5-8 parts; carbon black: 0.2-0.3 parts; thickener: 1-5 parts; Agent: 3-6 parts; emery: 30-40 parts; toughening agent: 0.1-0.2 parts.

The beneficial effect of the wear-resistant anti-skid coating of the present invention is: the product combines physical anti-skid and chemical anti-corrosion, and is fast drying, easy to construct, and has excellent physical properties and chemical properties. The product has high wear-resistant and anti-skid effects It is excellent and can be widely used in anti-slip and anti-corrosion of storage tanks, ladders, irrigation slopes, and aisles, and plays a role in protection and safe production.

Detailed ways

The wear-resistant and anti-skid coating of the present invention will be further described below.

Example 1

Wear-resistant antiskid coating in the embodiment of the present invention comprises the raw material of following weight:

Acrylic resin: 50kg;

Titanium dioxide: 5kg;

Carbon black: 0.2kg;

Thickener: 1kg;

Anti-sedimentation agent: 3kg;

Corundum: 30kg;

Toughener: 0.1kg.

Example 2

Wear-resistant antiskid coating in the embodiment of the present invention comprises the raw material of following weight:

Acrylic resin: 55kg;

Titanium dioxide: 6kg;

Carbon black: 0.25kg;

Thickener: 3kg;

Anti-sedimentation agent: 4kg;

Corundum: 35kg;

Toughener: 0.15kg.

Example 3

Wear-resistant antiskid coating in the embodiment of the present invention comprises the raw material of following weight:

Acrylic resin: 60kg;

Titanium dioxide: 8kg;

Carbon black: 0.3kg;

Thickener: 5kg;

Anti-sedimentation agent: 6kg;

Corundum: 40kg;

Toughener: 0.2kg.

After the paint is applied, the anti-slip paint film is 2-3mm, and it is hard to dry for 24 hours, and the painted facilities are put into use for 7 days.

This product combines physical anti-skid and chemical anti-corrosion, and is fast drying, easy to apply, and has excellent physical and chemical properties. This product has high wear resistance and excellent anti-skid effect, and can be widely used in storage tanks and ladders. , The anti-slip and anti-corrosion of the topping slope and the aisle play a role in protection and safe production.

The above embodiment is only a description of the preferred implementation of the present invention, and is not intended to limit the scope of the present invention. On the premise of not departing from the design spirit of the present invention, ordinary engineers and technicians in the field can make various modifications to the technical solution of the present invention. and improvements, all should fall within the scope of protection determined by the claims of the present invention.

Claims (1)

1. a wear-resisting skid-resistant coating is characterized in that: the raw material that comprises following parts by weight: vinyl resin: 50-60 part; White titanium pigment: 5-8 part; Carbon black: 0.2-0.3 part; Thickening material: 1-5 part; Anti-settling agent: 3-6 part; Silicon carbide: 30-40 part; Toughner: 0.1-0.2 part.