CN102807813A - 水性聚氨酯地坪漆 - Google Patents
水性聚氨酯地坪漆 Download PDFInfo
- Publication number
- CN102807813A CN102807813A CN2012102911857A CN201210291185A CN102807813A CN 102807813 A CN102807813 A CN 102807813A CN 2012102911857 A CN2012102911857 A CN 2012102911857A CN 201210291185 A CN201210291185 A CN 201210291185A CN 102807813 A CN102807813 A CN 102807813A
- Authority
- CN
- China
- Prior art keywords
- water
- paint
- lacquer
- parts
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开一种水性聚氨酯地坪漆，尤其是一种双组份水性聚氨酯地坪漆，所述地坪漆由主漆和固化剂组合而成，所述主漆中含有水溶性羟基树脂，所述固化剂为可水溶性含异氰酸根的聚合物。本发明找到一种溶于水的含羟基的树脂用于制漆，使用时和一种溶于水的含异氰酸根的聚合物配合，通过化学反应交联成具有立体网状结构的漆膜，从而得到物化性能优异的双组份水性聚氨酯地坪漆。所述双组份水性聚氨酯地坪漆，通过两个组份中的活泼基团发生缩合反应，交联成膜，从而提高了漆膜的交联密度，使得漆膜的硬度高，耐磨性等物化性能显著提高。
Description
技术领域
本发明涉及一种水性聚氨酯地坪漆，尤其是一种双组份水性聚氨酯地坪漆。
背景技术
目前，水性聚氨酯地坪产品的技术方案大多是先合成聚氨酯树脂，然后乳化分散于水中，属于单组分技术。由于现有技术是将水性聚氨酯树脂合成大分子，然后乳化溶于水制得的，使用时，随着水分挥发交联成膜，交联密度不高，用这种树脂做的地坪物化性能不好，漆膜的硬度一般不高，耐溶剂性、耐磨性不强。
发明内容
本发明的目的在于克服现有技术中的不足之处而提供一种漆膜硬度高，耐磨性和耐候性等物化性能优异的水性聚氨酯地坪漆。
为实现上述目的，本发明采取的技术方案为：一种水性聚氨酯地坪漆，由主漆和固化剂组合而成，所述主漆中含有水溶性羟基树脂，所述固化剂为可水溶性含异氰酸根的聚合物。
现有单组份水性聚氨酯由于其硬度、耐磨性等物化性能不足，因此不适合来做高品质地坪漆。本发明的出发点在于找到一种水性含羟基的树脂和一种水溶性含异氰酸根的聚合物，用它们配合制漆，从而得到性能优异的双组份水性聚氨酯地坪漆，有效提高产品的硬度、耐磨性和耐候性等物化性能。
本发明所述水性聚氨酯地坪漆，找到一种溶于水的含羟基的树脂用于制漆，使用时和一种溶于水的含异氰酸根的聚合物配合，通过化学反应交联成具有立体网状结构的漆膜，从而得到物化性能优异的双组份水性聚氨酯地坪漆。所述双组份水性聚氨酯地坪漆，通过两个组份中的活泼基团发生缩合反应，交联成膜，从而提高了漆膜的交联密度，使得漆膜的硬度高，耐磨性等物化性能显著提高。
作为本发明所述水性聚氨酯地坪漆的优选实施方式，所述主漆含有以下重量份的组分：
作为本发明所述水性聚氨酯地坪漆的优选实施方式，所述润湿剂为烷基酚聚氧乙烯醚、聚氧乙烯改性剂中的至少一种；所述分散剂为聚丙烯酸钾盐、聚丙烯酸钠盐中的至少一种；所述消泡剂为矿物油、有机二氧化硅改性剂、硅酮类消泡剂中的至少一种；所述颜料为钛白粉、钛黄、酞青蓝中的至少一种；所述填料为矿物石粉、滑石粉。重钙、石英粉、玻璃粉中的至少一种；所述防腐剂为卡松、尼泊金酯类中的至少一种；所述流变改性剂为聚氨酯流变剂、缔合型丙烯酸聚合物中的至少一种；所述表面改性剂为含氟的改性聚乙烯蜡、改性的二甲基硅氧烷中的至少一种。
作为本发明所述水性聚氨酯地坪漆的更优选实施方式，所述消泡剂为硅酮类消泡剂；所述填料为石英粉、玻璃粉中的至少一种。在主漆中加入强效消泡剂硅酮类消泡剂，可将固化剂的异氰酸根和水反应产生的二氧化碳迅速排出破泡。在主漆中加入耐磨性更好的石英粉、玻璃粉作为填料，可进一步提高产品的耐磨性。
本发明的水性聚氨酯地坪漆，是通过两个组份的反应基团经过进一步的化学反应交联成膜，交联密度高，使得漆膜的硬度高，耐磨性等物化性能优异。成膜过程中的反应如下：
反应一是主反应，它是主漆树脂和固化剂树脂之间的反应。主漆中主体树脂必须是带羟基的树脂，而且具有亲水性，通过乳化分散，做成水性树脂。固化剂树脂是异氰酸酯单体通过聚合反应而成，再接入一些亲水相。由于固化剂的反应基团是立体分布，而主漆树脂的反应基团也不止一个，所以反应后会形成化学链条纵横交错的立体网络结构，使得漆膜性能得到提高。
反应二是固化剂的异氰酸根和水反应，生产胺基树脂和二氧化碳，这个二氧化碳如果不及时排出会影响漆膜外观和性能。在主漆中加入强效的消泡剂酮类消泡剂，使得反应产生的二氧化碳迅速排出破泡。胺基树脂又与异氰酸根进行反应生成脲树脂。
作为本发明所述水性聚氨酯地坪漆的优选实施方式，所述水溶性羟基树脂为阴离子型聚丙烯酸分散体、聚酯聚氨酯分散体中的至少一种。
作为本发明所述水性聚氨酯地坪漆的优选实施方式，所述固化剂为氨基磺酸盐改性的HDI三聚体、氨基磺酸盐改性的IPDI三聚体中的至少一种。
作为本发明所述水性聚氨酯地坪漆的优选实施方式，使用时，所述主漆与固化剂的重量比为5:1。
水溶性树脂中不存在容易被紫外线分解的基团，而且水溶性固化剂用耐候性优异的单体来合成，使得固化后的漆膜具有优秀的耐候性。
本发明的双组份水性聚氨酯地坪漆，优选了水性树脂和固化剂，从而保证了优异的物化性能；采用耐候性优异的异氰酸酯单体合成的固化剂，在主漆用的水性含羟基树脂中避免引入耐候性差的基团，进一步提高了产品的耐候性。本发明所述水性聚氨酯地坪漆与现有产品相比，具有更好的硬度、耐磨性、耐候性等物化性能。
具体实施方式
为更好的说明本发明的目的、技术方案和优点，下面将结合具体实施例对本发明作进一步说明。
实施例1
本发明水性聚氨酯地坪漆的一种实施例，所述地坪漆含有以下重量份的组分：
主漆：水溶性羟基树脂：阴离子型聚丙烯酸酯分散体40份
润湿剂：烷基酚聚氧乙烯醚0.3份
分散剂：聚丙烯酸钾盐0.4份
消泡剂：矿物油0.3份
颜料：钛白粉15份
填料：矿物石粉25份
防腐剂：卡松0.2份
流变改性剂：聚氨酯流变剂0.3份
表面改性剂：含氟的改性聚乙烯蜡0.5份。
固化剂：氨基磺酸盐改性的HDI三聚体16.4份。
使用时，将主漆与固化剂混合均匀即可。
本实施例中，使用时，主漆与固化剂的重量比为5:1。
实施例2
本发明水性聚氨酯地坪漆的一种实施例，所述地坪漆含有以下重量份的组分：
主漆：水溶性羟基树脂：聚酯聚氨酯分散体50份
润湿剂：聚氧乙烯改性剂0.6份
分散剂：聚丙烯酸钠盐0.3份
消泡剂：有机二氧化硅改性剂0.6份
颜料：钛黄10份
填料：滑石粉30份
防腐剂：尼泊金酯类0.1份
流变改性剂：缔合型丙烯酸聚合物0.6份
表面改性剂：改性的二甲基硅氧烷0.3份。
固化剂：氨基磺酸盐改性的IPDI三聚体18.5份。
使用时，将主漆与固化剂混合均匀即可。
本实施例中，使用时，主漆与固化剂的重量比为5:1。
实施例3
本发明水性聚氨酯地坪漆的一种实施例，所述地坪漆含有以下重量份的组分：
主漆：水溶性羟基树脂：阴离子型聚丙烯酸酯分散体45份
润湿剂：聚氧乙烯改性剂0.5份
分散剂：聚丙烯酸钠盐0.6份
消泡剂：有机二氧化硅改性剂0.5份
颜料：酞青蓝20份
填料：重钙20份
防腐剂：卡松0.1份
流变改性剂：缔合型丙烯酸聚合物0.6份
表面改性剂：含氟的改性聚乙烯蜡0.2份。
固化剂：氨基磺酸盐改性的HDI三聚体17.5份。
使用时，将主漆与固化剂混合均匀即可。
本实施例中，使用时，主漆与固化剂的重量比为5:1。
实施例4
本发明水性聚氨酯地坪漆的一种实施例，所述地坪漆含有以下重量份的组分：
主漆：水溶性羟基树脂：阴离子型聚丙烯酸酯分散体20份、聚酯聚氨酯分散体42份
润湿剂：烷基酚聚氧乙烯醚0.4份
分散剂：聚丙烯酸钾盐0.6份
消泡剂：硅酮类消泡剂0.6份
颜料：钛白粉10份、酞青蓝8份
填料：石英粉20份、玻璃粉6份
防腐剂：尼泊金酯类0.1份
流变改性剂：聚氨酯流变剂0.4份
表面改性剂：改性的二甲基硅氧烷0.5份。
固化剂：氨基磺酸盐改性的IPDI三聚体17.7份。
使用时，将主漆与固化剂混合均匀即可。
本实施例中，使用时，主漆与固化剂的重量比为5:1。
实施例5
采用实施例1-4所述水性聚氨酯地坪漆作为发明组，采用如下所述的现有产品作为对照组。
现有产品中的一种聚氨酯地坪漆，包含以下重量份的组分：
水 3.9份
防冻剂：PG 1.5份
助分散剂：AMP 950 0.18份
润湿剂：BYK 154 0.39份
分散剂：BYK 181 0.39份
消泡剂：BYK 024 0.3份
流变剂：RHEOLATE 288 0.2份
颜料：R-706 21.94份
成膜物：PUD聚氨酯树脂 64.1份
填料：COASOL 2.5份
基材润湿剂：TEGO KL 245 0.2份
消泡剂：BYK 025 0.1份
流变剂：RHEOLATE 288 0.2份
防霉剂：BIOX AA 148 1份
防腐剂：BIOX VFB1 0.2份
水 2.9份。
分别采用发明组和对照组的地坪漆制板，并用同样的方法检测其性能，结果如表1。
表1
由表1可看出，发明组的水性聚氨酯地坪漆与对照组相比，具有更好的硬度、耐磨性、耐酸碱性和耐候性等物化性能。
最后所应当说明的是，以上实施例仅用以说明本发明的技术方案而非对本发明保护范围的限制，尽管参照较佳实施例对本发明作了详细说明，本领域的普通技术人员应当理解，可以对本发明的技术方案进行修改或者等同替换，而不脱离本发明技术方案的实质和范围。
Claims (7)
1.一种水性聚氨酯地坪漆，其特征在于，由主漆和固化剂组合而成，所述主漆中含有水溶性羟基树脂，所述固化剂为可水溶性含异氰酸根的聚合物。
2.如权利要求1所述的水性聚氨酯地坪漆，其特征在于，所述主漆含有以下重量份的组分：
3.如权利要求2所述的水性聚氨酯地坪漆，其特征在于，所述润湿剂为烷基酚聚氧乙烯醚、聚氧乙烯改性剂中的至少一种；所述分散剂为聚丙烯酸钾盐、聚丙烯酸钠盐中的至少一种；所述消泡剂为矿物油、有机二氧化硅改性剂、硅酮类消泡剂中的至少一种；所述颜料为钛白粉、钛黄、酞青蓝中的至少一种；所述填料为矿物石粉、滑石粉。重钙、石英粉、玻璃粉中的至少一种；所述防腐剂为卡松、尼泊金酯类中的至少一种；所述流变改性剂为聚氨酯流变剂、缔合型丙烯酸聚合物中的至少一种；所述表面改性剂为含氟的改性聚乙烯蜡、改性的二甲基硅氧烷中的至少一种。
4.如权利要求3所述的水性聚氨酯地坪漆，其特征在于，所述消泡剂为硅酮类消泡剂；所述填料为石英粉、玻璃粉中的至少一种。
5.如权利要求1或2所述的水性聚氨酯地坪漆，其特征在于，所述水溶性羟基树脂为阴离子型聚丙烯酸酯分散体、聚酯聚氨酯分散体中的至少一种。
6.如权利要求1或2所述的水性聚氨酯地坪漆，其特征在于，所述固化剂为氨基磺酸盐改性的HDI三聚体、氨基磺酸盐改性的IPDI三聚体中的至少一种。
7.如权利要求1或2所述的水性聚氨酯地坪漆，其特征在于，使用时，所述主漆与固化剂的重量比为5:1。