CN102995010B - 以TiO2、二甲胺、炭黑、乙炔和氮气为组元的激光诱导金属表层复合TiCN强化方法 - Google Patents

以TiO2、二甲胺、炭黑、乙炔和氮气为组元的激光诱导金属表层复合TiCN强化方法 Download PDF

Info

Publication number
CN102995010B
CN102995010B CN201210565231.8A CN201210565231A CN102995010B CN 102995010 B CN102995010 B CN 102995010B CN 201210565231 A CN201210565231 A CN 201210565231A CN 102995010 B CN102995010 B CN 102995010B
Authority
CN
China
Prior art keywords
acetylene
nitrogen
dimethylamine
carbon black
laser
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201210565231.8A
Other languages
English (en)
Other versions
CN102995010A (zh
Inventor
王辉
童涵
左健民
肖圣亮
张荣荣
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Haian Huacheng New Material Co ltd
Original Assignee
Changzhou University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Changzhou University filed Critical Changzhou University
Priority to CN201210565231.8A priority Critical patent/CN102995010B/zh
Publication of CN102995010A publication Critical patent/CN102995010A/zh
Application granted granted Critical
Publication of CN102995010B publication Critical patent/CN102995010B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

以TiO2、二甲胺、炭黑、乙炔和氮气为组元的激光诱导金属表层复合TiCN强化方法，本发明涉及金属材料的表面强化技术领域。在金属表面涂敷TiO2和二甲胺、炭黑的混合物，在乙炔和氮气共存的条件下，用激光束在涂敷所述混合物的金属表面进行扫描。通过以上工艺，可以在金属表层原位复合生成TiCN，实现对碳素结构钢表面的强化与提高耐磨性。

Description

以TiO2、二甲胺、炭黑、乙炔和氮气为组元的激光诱导金属表层复合TiCN强化方法
技术领域
本发明涉及金属材料的表面强化技术领域。
背景技术
氮碳化钛（TiCN)是一种性能优良、用途广泛的非氧化物材料, 也是一种性能优异的涂层材料，是碳化钛和氮化钛的无限固溶体，兼具有碳化钛和氮化钛的优点, 具有高硬度、耐磨、耐腐蚀、抗氧化等特性, 并具有良好的导热性、导电性和化学稳定性, 被广泛用于切削刀具、粉末冶金以及金属陶瓷制品，是目前研究和应用最为广泛的薄膜材料之一。
TiCN涂层的制备技术目前主要是化学气相沉积(CVD) 和物理气相沉积（PVD）。CVD法沉积温度高，超过了绝大多数钢材的热处理温度，并且CVD 以氯化物为原料，需要一套提供制备含Ti 卤化物气体的设备，工艺复杂，成本较高，与目前提倡的绿色工业相抵触。PVD 法形成温度较低、涂层较薄，与基体的结合强度低，涂层易于从基底剥落，且绕镀性较差。
不论是CVD法还是PVD法，所获得的TiCN涂层都较薄，厚度只有几个微米（μm），并且涂层与基体是机械结合，结合面强度低，使用中涂层易发生剥落。
发明内容
本发明的目的旨在提供一种以TiO2、二甲胺、炭黑、乙炔和氮气为组元的激光诱导金属表层复合TiCN强化方法，可以使金属表面层原位复合生成TiCN，从而对金属表面进行强化与提高耐磨性。
本发明是通过以下技术方案实现的：
在金属表面涂敷TiO2和二甲胺、炭黑的混合物，在乙炔和氮气共存的条件下，用激光束在涂敷所述混合物的金属表面进行扫描。
通过以上工艺，可以在金属表层原位复合生成TiCN，实现对碳素结构钢表面的强化与提高耐磨性。
本发明具有以下优点：
1、TiCN是在金属表层原位复合生成，而不是在表面沉积，因此不存在涂层与基体的结合力问题；
2、原位复合有TiCN的金属表层厚度可达500至600微米，显微硬度可达HV2600至HV2700以上，因此即使表面在使用过程中有微磨损，仍然具有很好的硬度和耐磨性。
进一步地，本发明所述TiO2为工业纯TiO2，所述工业纯TiO2和二甲胺、炭黑的合物质量比为7:4:3。
涂敷所述混合物的厚度为1.5～2。
所述乙炔的流量为5～6L/min，所述氮气的流量为7～8L/min。
所述激光束的扫描速度为400～600mm/min，功率为700～900W，波长为1.06μm或10.6μm，光斑直径为2～3毫米。
具体实施方式
    一、对Q235A、20钢、40钢、45钢、20G、20Mn、40Mn和60Mn碳素结构钢分别进行表面处理：
1、在碳素结构钢表面敷以工业纯TiO2和二甲胺、炭黑混合物，其质量比为7:4:3，厚度为1.5毫米；
2、随激光光斑移动，通以乙炔和氮气混合气体，乙炔、氮气流量分别为5L/min和7L/min;
3、激光光束以500mm/min速度进行扫描，激光功率为900W，激光波长为1.06μm，光斑直径为2毫米。
4、经检测，经过处理的碳素结构钢表层复合有可达500微米的TiCN，显微硬度可达HV2600以上。
二、对20MnV、40Cr、35CrMoV和20CrMnSi合金结构钢分别进行表面处理：
1、在合金结构钢表面敷以工业纯TiO2和二甲胺、炭黑混合物，其质量比为7:4:3，厚度为1.5毫米；
2、随激光光斑移动，通以乙炔和氮气混合气体，乙炔、氮气流量分别为5L/min和7L/min;
3、激光光束以400mm/min速度进行扫描，激光功率为700W，激光波长为1.06μm，光斑直径为2毫米。
4、经检测，经过处理的合金结构钢表层复合有可达500微米的TiCN，显微硬度可达HV2650以上。
三、对65Mn、60Si2Mn和50CrVA弹簧钢分别进行表面处理：
1、在弹簧钢表面敷以工业纯TiO2和二甲胺、炭黑混合物，其质量比为7:4:3，厚度为2毫米；
2、随激光光斑移动，通以乙炔和氮气混合气体，乙炔、氮气流量分别为6L/min和8L/min;
3、激光光束以600mm/min速度进行扫描，激光功率为800W，激光波长为1.06μm，光斑直径为3毫米。
4、经检测，经过处理的弹簧钢表层复合有可达500微米的TiCN，显微硬度可达HV2700以上。
四、对T8A、T9A 、T10A、T11A、9SiCr、Cr12MoV和3Cr2Mo工具钢分别进行表面处理：
1、在工具钢表面敷以工业纯TiO2和二甲胺、炭黑混合物，其质量比为7:4:3，厚度为1.5毫米；
2、随激光光斑移动，通以乙炔和氮气混合气体，乙炔、氮气流量分别为5L/min和7L/min;
3、激光光束以400mm/min速度进行扫描，激光功率为1000W，激光波长为10. 6μm，光斑直径为3毫米。
4、经检测，经过处理的工具钢表层复合有可达500微米的TiCN，显微硬度可达HV2700以上。
五、对W18Cr4V、W6Mo5Cr4V2和W6Mo5Cr4V2Al高速钢分别进行表面处理：
1、在高速钢表面敷以工业纯TiO2和二甲胺、炭黑混合物，其质量比为7:4:3，厚度为1.5毫米；
2、随激光光斑移动，通以乙炔和氮气混合气体，乙炔、氮气流量分别为6L/min和8L/min;
3、激光光束以500mm/min速度进行扫描，激光功率为1100W，激光波长为10. 6μm，光斑直径为2毫米。
4、经检测，经过处理的高速钢表层复合有可达600微米的TiCN，显微硬度可达HV2700以上。
六、对YG3X、YG6X、YK15、YG20、YT15、YS25、YW1、YW2和YL10硬质合金分别进行表面处理：
1、在硬质合金表面敷以工业纯TiO2和二甲胺、炭黑混合物，其质量比为7:4:3，厚度为2毫米；
2、随激光光斑移动，通以乙炔和氮气混合气体，乙炔、氮气流量分别为6L/min和8L/min;
3、激光光束以600mm/min速度进行扫描，激光功率为1200W，激光波长为10. 6μm，光斑直径为3毫米。
4、经检测，经过处理的硬质合金表层复合有可达550微米的TiCN，显微硬度可达HV2700以上。

Claims (2)

1.以TiO2、二甲胺、炭黑、乙炔和氮气为组元的激光诱导金属表层复合TiCN强化方法，其特征在于在金属表面涂敷TiO2和二甲胺、炭黑的混合物，在乙炔和氮气共存的条件下，用激光束在涂敷所述混合物的金属表面进行扫描；所述TiO2为工业纯TiO2，所述工业纯TiO2和二甲胺、炭黑的合物质量比为7:4:3；涂敷所述混合物的厚度为1.5～2毫米；所述激光束的扫描速度为400～600mm/min，功率为700～900W，波长为1.06μm或10.6μm，光斑直径为2～3毫米。
2.根据权利要求1所述以TiO2、二甲胺、炭黑、乙炔和氮气为组元的激光诱导金属表层复合TiCN强化方法，其特征在于所述乙炔的流量为5～6L/min，所述氮气的流量为7～8L/min。
CN201210565231.8A 2012-12-24 2012-12-24 以TiO2、二甲胺、炭黑、乙炔和氮气为组元的激光诱导金属表层复合TiCN强化方法 Expired - Fee Related CN102995010B (zh)