CN103072425A - Making method of lacquer painting and lacquer painting made by method - Google Patents
Making method of lacquer painting and lacquer painting made by method Download PDFInfo
- Publication number
- CN103072425A CN103072425A CN2013100314771A CN201310031477A CN103072425A CN 103072425 A CN103072425 A CN 103072425A CN 2013100314771 A CN2013100314771 A CN 2013100314771A CN 201310031477 A CN201310031477 A CN 201310031477A CN 103072425 A CN103072425 A CN 103072425A
- Authority
- CN
- China
- Prior art keywords
- lacquer painting
- base material
- colored paint
- lacquer
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the technical field of craft making, particularly relates to a making method of a lacquer painting and the lacquer painting made by the method, and provides a making method of the lacquer painting having richer lacquer painting patterns and carriers, and capable of simultaneously displaying surface visual characteristics of colored lacquer and various hard materials. The making method of the lacquer painting adopts the technical scheme that the method comprises the following steps: A, a base material is selected, and the base material is a hard material; B, at least one surface of the base material is coated with the colored lacquer, and a base material A is obtained; C, the base material A is dried, and a base material B is obtained; and D, patterns are engraved on the surface of the base material B coated with the colored lacquer. The lacquer painting and the making method have the benefits that the colored lacquer is organically combined with the hard materials, the function of the colored lacquer in the traditional lacquer painting is inherited, the carriers and patterns of the lacquer painting are richer, and the surface visual characteristics of various hard materials can be displayed.
Description
Technical field
The present invention relates to the ornameutal handiwork technical field, be specifically related to a kind of preparation method and usefulness of lacquer painting
The lacquer painting that described method is made.
Background technology
Lacquer painting is a kind of important handicraft, and traditional preparation method is: conceive first the pattern of lacquer painting, and right
Rear according to pattern one or more layers colored paint of base material coating at hard material, colored paint itself is pie graph then
The main body of case.The significant deficiency of this preparation method is: the pattern of lacquer painting is only by the colored paint structure that adds
Become, carrier is single, pattern is dull, and appreciation effect is not good enough; And the colored paint of pie graph main case body part will
Base material wraps fully, can't show the surface properties of various base materials at all, does not also namely take full advantage of base
The distinctive character of material self, such as: when base material was aluminium sheet, aluminium sheet itself had graceful silvery white coloured light
The pool has artistic value, yet the pattern of lacquer painting only is made of colored paint, and carrier is single, the pattern list
Transfer, the natural silvery white gloss of aluminium sheet is wrapped by the colored paint of traditional lacquer painting, has wasted the distinctive surface of aluminium
Character.
Summary of the invention
Problem to be solved by this invention provide a kind of lacquer painting pattern and carrier thereof more abundant and can with
The preparation method of a kind of lacquer painting of the surperficial visual characteristic of Shi Zhanxian colored paint and various hard materials.
In order to address the above problem, technical scheme provided by the present invention is:
A kind of preparation method of lacquer painting said method comprising the steps of:
A, choose base material, described base material is hard material;
B, apply colored paint at least one surface of base material, obtain base material A;
C, dry substrate A obtain base material B;
D, apply the surface engraving pattern of colored paint at base material B.
Optionally, described method is further comprising the steps of:
A, before engraving, the drawing of design pattern;
B, drawing is fixed on the surface that base material B applies colored paint.
Optionally, described base material is metallic plate.
Optionally, described metallic plate is aluminium sheet.
Optionally, the thickness of described aluminium sheet〉3mm.
Optionally, the color of described colored paint is black.
Optionally, the thickness of described colored paint is 0.01mm-0.2mm.
The present invention also provides a kind of lacquer painting, and described lacquer painting is according to any one lacquer provided by the present invention
The preparation method of drawing is made.
Beneficial effect of the present invention is:
After adopting technical scheme of the present invention, thoroughly solved in the prior art lacquer painting pattern only by the colored paint structure
The drawback that carrier is single, pattern is dull that becomes and bring, the surface that has also solved various hard materials simultaneously
Applied the drawback cause to represent self surface characteristics by colored paint.In the present invention, colored paint and hard material
The surface of material all is the organic component of lacquer painting pattern, mutually sets off, and indispensable, this lacquer painting is not
Only inherited the function of colored paint in traditional lacquer painting, also so that the carrier of lacquer painting and pattern are abundanter, can also
The surperficial visual characteristic that enough represents various hard materials, the organic assembling of this lacquer painting and hard material forms
A kind of brand-new lacquer painting product and preparation method.
Such as, when hard material was aluminium sheet, in the prior art, the main body pattern of lacquer painting was only by colored paint
Consist of, and aluminium sheet itself is wrapped by colored paint, this is not only so that the undue dullness of lacquer painting pattern, carrier are single,
The silvery white metallic luster that also can't represent aluminum material self simultaneously; By contrast, in the technology of the present invention
In the scheme, the main body pattern of lacquer painting is made of jointly aluminium sheet and colored paint, and specifically: these consist of main body
The colored paint that the surface of aluminum plate of pattern applies is all removed by quarter, and these carve aluminium sheet part and its limit except colored paint
The colored paint that the edge is divided has then consisted of the brand-new lacquer painting of a width of cloth, and this lacquer painting has not only been inherited look in traditional lacquer painting
The function of lacquer also so that the carrier of lacquer painting and pattern are abundanter, can also represent the silvery white of aluminium sheet self
Non-ferrous metal gloss has thoroughly solved the drawback of prior art.
Further, in the technical solution of the present invention, before engraving, the drawing of design pattern, then
Drawing is fixed on the surface of base material B coating colored paint.This has overcome needs in the prior art in advance at look
The shortcoming of lacquer surface tracing reduces operation, is simple and easy to greatly improve with, make efficiency.
Further, in the technical solution of the present invention, described base material is metallic plate.On the one hand, metallic plate with
The colored paint collocation, the metallic luster of metallic plate can make the whole structure of lacquer painting have more aesthetic; The opposing party
Face, because metallic plate is harder, engraving tool is difficult to scratch metallic plate and causes destroying base material.
Further, in the technical solution of the present invention, described base material is aluminium sheet.Aluminium sheet not only itself has excellent
Refined silvery white gloss, and the whole ornamental value that can promote greatly lacquer painting when arranging in pairs or groups with colored paint with
Artistic value.
Further, in the technical solution of the present invention, the thickness of described aluminium sheet〉3mm.Thickness when aluminium sheet〉3mm
The time, engraving tool is difficult to scratch aluminium sheet, has also just effectively protected base material, thereby has improved efficiency of construction
With yield rate.
Further, in the technical solution of the present invention, the color of described colored paint is black.The colored paint of black with
Argenteous aluminium sheet is arranged in pairs or groups, and not only can farthest represent the silvery white metallic luster of aluminium sheet, and
This organic assembling makes the whole appreciation effect of lacquer painting obtain very big lifting.
Further, in the technical solution of the present invention, the thickness of described colored paint is 0.01mm-0.2mm.This both
Poor, the defective that wears no resistance of stereoeffect has also overcome colored paint thickness when having overcome colored paint thickness＜0.01mm
Increase the defective of colored paint cost and engraving difficulty during 0.2mm.
The specific embodiment
The below will be clearly and completely described the technical scheme in the embodiment of the invention, obviously, and institute
The embodiment that describes only is the present invention's part embodiment, rather than whole embodiment.Based on this
Embodiment in bright, those of ordinary skills obtain under the creative work prerequisite not making
Every other embodiment belongs to the scope of protection of the invention.
Embodiment one:
A kind of preparation method of lacquer painting said method comprising the steps of:
A, choose base material, described base material is hard material;
B, apply colored paint at least one surface of base material, obtain base material A;
C, dry substrate A obtain base material B;
D, apply the surface engraving pattern of colored paint at base material B.
At first, described base material is hard material, and both constructabilities is also so that engraving tool is difficult to scratch base
Material and cause destroying base material.
Secondly, apply colored paint at least one surface of base material, obtain base material A.In practice, can basis
Specifically need to apply colored paint by the one or more or all surfaces in all surface of base material, also can
Specific nature according to base material is selected suitable coating colored paint, such as: when base material is aluminium sheet, can make
Be that primary raw material adds diluent, modifier, drier etc. simultaneously in order to coal tar asphalt and coal tar
The colored paint that organic solvent forms.
Again, dry substrate A obtains base material B.The effect of dry substrate A is so that substrate surface is coated with
The colored paint that covers can solidified forming, possesses good sculpture and visual effect.
At last, apply the surface engraving pattern of colored paint at base material B.In the manufacturing process of lacquer painting, at base
Material B applies on the surface of colored paint, according to required pattern the colored paint of pattern corresponding position is carved and is removed, and exposes base
The hard material part of material, and the colored paint of this part hard material and its marginal portion consists of lacquer painting jointly
The main body pattern, solved thoroughly that lacquer painting pattern in the prior art only is made of colored paint and the carrier that brings is single,
The drawback of pattern dullness, the surface that has also solved various hard materials is simultaneously applied by colored paint and causes and can't open up
The drawback of existing self surface characteristics.Furtherly, this lacquer painting has not only been inherited colored paint in traditional lacquer painting
Function also so that the carrier of lacquer painting and pattern are abundanter, can also represent the surface of various hard materials
Visual characteristic, the organic assembling of this lacquer painting and hard material have formed a kind of brand-new lacquer painting product and system
Make method.
Embodiment two:
On the basis of the preparation method of embodiment one described a kind of lacquer painting, described method also comprises following
Step: A, before engraving, the drawing of design pattern; B, drawing is fixed on base material B applies look
On the surface of lacquer, then carve at colored paint with engraving tool according to drawing.The function of above step exists
In: overcome the shortcoming that needs in the prior art in advance in the tracing of colored paint surface, reduced operation, be simple and easy to
Greatly improve with, make efficiency.
Embodiment three:
On the basis of the preparation method of embodiment one or two described a kind of lacquer paintings, described base material is metal
Plate.On the one hand, the metallic luster of metallic plate itself has aesthetic, and metallic plate and colored paint collocation,
Can make the whole structure of lacquer painting have more aesthetic; On the other hand, because metallic plate is harder, the carver
Tool is difficult to scratch metallic plate, has also just effectively protected base material, thereby has improved efficiency of construction and yield rate.
Embodiment four:
On the basis of the preparation method of the described a kind of lacquer painting of aforementioned one to three any one embodiment, institute
Stating base material is aluminium sheet.Aluminium sheet not only itself has graceful silvery white gloss, and can when arranging in pairs or groups with colored paint
Whole ornamental value and artistic value with great lifting lacquer painting.
Embodiment five:
On the basis of the preparation method of the described a kind of lacquer painting of aforementioned one to four any one embodiment, institute
The thickness of stating aluminium sheet is 3.1mm, 4mm, 5mm, 1cm, 10cm, 50cm, 1m.Thickness＜3mm when aluminium sheet
The time, engraving tool easily scratches aluminium sheet and causes destroying base material, when the thickness of aluminium sheet be 3.1mm, 4mm,
5mm, 1cm, 10cm, 50cm, 1m etc. all during the thickness of 3mm, engraving tool be difficult to scratch aluminium sheet and
Cause destroying base material.
So the thickness of described aluminium sheet can be 3.1mm, 4mm, 5mm, 1cm, 10cm, 50cm, 1m etc.
All meet the thickness of above-mentioned beneficial effect.
Embodiment six:
On the basis of the preparation method of the described a kind of lacquer painting of aforementioned one to five any one embodiment, institute
The color of stating colored paint is black.The colored paint effect of black is, after argenteous aluminium sheet collocation, not only
The silvery white metallic luster that can farthest represent aluminium sheet, and this organic assembling makes the whole of lacquer painting
The body appreciation effect has obtained very big lifting.So, in practice, can also select dark reddish brown, brown, dark
The blue grade and the obvious color of silvery white contrast effect is to satisfy above-mentioned beneficial effect.
Embodiment seven:
On the basis of the preparation method of the described a kind of lacquer painting of aforementioned one to six any one embodiment, institute
The thickness of stating colored paint is 0.01mm-0.2mm.
When the thickness of described colored paint＜0.01mm, the stereoeffect of described colored paint is poor, and wears no resistance;
Thickness when described colored paint〉during 0.2mm, thicker colored paint has then increased colored paint cost and engraving difficulty.
The present invention also provides a kind of lacquer painting, and described lacquer painting is according to any one lacquer provided by the present invention
The preparation method of drawing is made.
To sum up, the preparation method of above a kind of lacquer painting that the embodiment of the invention is provided and with described method system
The lacquer painting of doing is described in detail, and has used specific case herein to principle of the present invention and enforcement side
Formula is set forth, and the explanation of above embodiment just is used for helping to understand method of the present invention and core thereof
Thought; Simultaneously, for one of ordinary skill in the art, according to thought of the present invention, at implementation
All will change on mode and the range of application, in summary, this description should not be construed as right
Restriction of the present invention.
Claims (7)
1. the preparation method of a lacquer painting is characterized in that, said method comprising the steps of:
A, choose base material, described base material is hard material;
B, apply colored paint at least one surface of base material, obtain base material A;
C, dry substrate A obtain base material B;
D, apply the surface engraving pattern of colored paint at base material B.
2. the preparation method of described a kind of lacquer painting according to claim 1 is characterized in that, described method is also wrapped
Draw together following steps:
A, before engraving, the drawing of design pattern;
B, drawing is fixed on the surface that base material B applies colored paint.
3. according to claim 1 or the preparation method of 2 described a kind of lacquer paintings, it is characterized in that described base material
Be metallic plate.
4. the preparation method of described a kind of lacquer painting according to claim 3 is characterized in that, described metallic plate is
Aluminium sheet.
5. the preparation method of described a kind of lacquer painting according to claim 4 is characterized in that, described aluminium sheet thick
Degree〉3mm.
6. the preparation method of described a kind of lacquer painting according to claim 5 is characterized in that the face of described colored paint
Look is black.
7. the preparation method of described a kind of lacquer painting according to claim 6 is characterized in that, described colored paint thick
Degree is 0.01mm-0.2mm.
8, a kind of lacquer painting is characterized in that, described lacquer painting be according to claim 1-7 in any one described
Method is made.