CN103421416B - A kind of anticorrosive coating and preparation method thereof - Google Patents
A kind of anticorrosive coating and preparation method thereof Download PDFInfo
- Publication number
- CN103421416B CN103421416B CN201310372050.8A CN201310372050A CN103421416B CN 103421416 B CN103421416 B CN 103421416B CN 201310372050 A CN201310372050 A CN 201310372050A CN 103421416 B CN103421416 B CN 103421416B
- Authority
- CN
- China
- Prior art keywords
- anticorrosive coating
- tetrafluoroethylene
- polyvinyl alcohol
- acrylic resin
- hydroxyethyl acrylate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention provides a kind of anticorrosive coating, be made up of each component of following mass fraction: epoxy acrylic resin 40-45 part, phenylformic acid dibutylester 3-6 part, Hydroxyethyl acrylate 5-8 part, tetrafluoroethylene 2-3 part, polyvinyl alcohol 12-15 part, p methoxy phenol 2-3 part.Anticorrosive coating of the present invention has good sticking power (1 grade) and excellent corrosion resistance nature, can in 24 hours complete drying, after being applied to metallic surface, can effectively prevent metal to be corroded.
Description
Technical field
The invention belongs to technical field of coatings, be specifically related to a kind of anticorrosive coating and preparation method thereof.
Background technology
Every year domestic all by a large amount of metals because metallic corrosion metal is damaged, lose the result of its original performance.Cause a large amount of metals to scrap, financial loss is very large.People work out the corrosion that many kinds of measures prevents and suppresses metal, and wherein coating is antirust is a kind of effective means.Therefore, this invention exploits a kind of outer metallic surface anticorrosive coating with good sticking power and excellent corrosion resistance nature.
Summary of the invention
The invention provides a kind of outer metallic surface anticorrosive coating with good sticking power and excellent corrosion resistance nature, for this reason, the present invention also provides the preparation method of this anticorrosive coating.
A kind of anticorrosive coating provided by the invention, is made up of each component of following mass fraction: epoxy acrylic resin 40-45 part, phenylformic acid dibutylester 3-6 part, Hydroxyethyl acrylate 5-8 part, tetrafluoroethylene 2-3 part, polyvinyl alcohol 12-15 part, p methoxy phenol 2-3 part.
Further, described anticorrosive coating is made up of each component of following mass fraction: epoxy acrylic resin 42 parts, phenylformic acid dibutylester 5 parts, Hydroxyethyl acrylate 6 parts, tetrafluoroethylene 3 parts, polyvinyl alcohol 13 parts, p methoxy phenol 2 parts.
Further, described anticorrosive coating also comprises the acetone of 3-5 weight part.
Preferably, described anticorrosive coating also comprises the acetone of 4 weight parts.
Second object of the present invention is to provide the preparation method of above-mentioned anticorrosive coating, is each component to be mixed, and is warming up to 60-70 DEG C, stirs 2 hours, be down to room temperature, obtain anticorrosive coating under 500-600r/min rotating speed.
Anticorrosive coating of the present invention has good sticking power (1 grade) and excellent corrosion resistance nature, can in 24 hours complete drying, after being applied to metallic surface, can effectively prevent metal to be corroded.
Embodiment
embodiment 1
The formula of anticorrosive coating of the present invention is as follows:
Epoxy acrylic resin 42kg, phenylformic acid dibutylester 5kg, Hydroxyethyl acrylate 6kg, tetrafluoroethylene 3kg, polyvinyl alcohol 13kg, p methoxy phenol 2kg.
The preparation method of anticorrosive coating of the present invention is: 42kg epoxy acrylic resin, 5kg phenylformic acid dibutylester, 6kg Hydroxyethyl acrylate, 3kg tetrafluoroethylene, 13kg polyvinyl alcohol, 2kg p methoxy phenol are added successively in reaction vessel, be warming up to 65 DEG C, stir 2 hours under 550r/min rotating speed, be down to room temperature, obtain anticorrosive coating.
embodiment 2
The formula of anticorrosive coating of the present invention is as follows:
Epoxy acrylic resin 40kg, phenylformic acid dibutylester 6kg, Hydroxyethyl acrylate 5kg, tetrafluoroethylene 2kg, polyvinyl alcohol 12kg, p methoxy phenol 3kg.
The preparation method of anticorrosive coating of the present invention is: 40kg epoxy acrylic resin, 6kg phenylformic acid dibutylester, 5kg Hydroxyethyl acrylate, 2kg tetrafluoroethylene, 12kg polyvinyl alcohol, 3kg p methoxy phenol are added successively in reaction vessel, be warming up to 60 DEG C, stir 2 hours under 500r/min rotating speed, be down to room temperature, obtain anticorrosive coating.
embodiment 3
The formula of anticorrosive coating of the present invention is as follows:
Epoxy acrylic resin 45kg, phenylformic acid dibutylester 3kg, Hydroxyethyl acrylate 8kg, tetrafluoroethylene 2.5kg, polyvinyl alcohol 15kg, p methoxy phenol 2.5kg.
The preparation method of anticorrosive coating of the present invention is: 45kg epoxy acrylic resin, 3kg phenylformic acid dibutylester, 8kg Hydroxyethyl acrylate, 2.5kg tetrafluoroethylene, 15kg polyvinyl alcohol, 2.5kg p methoxy phenol are added successively in reaction vessel, be warming up to 65 DEG C, stir 2 hours under 600r/min rotating speed, be down to room temperature, obtain anticorrosive coating.
embodiment 4
The formula of anticorrosive coating of the present invention is as follows:
Epoxy acrylic resin 42kg, phenylformic acid dibutylester 5kg, Hydroxyethyl acrylate 6kg, tetrafluoroethylene 3kg, polyvinyl alcohol 13kg, p methoxy phenol 2kg, acetone 4kg.
The preparation method of anticorrosive coating of the present invention is: 42kg epoxy acrylic resin, 5kg phenylformic acid dibutylester, 6kg Hydroxyethyl acrylate, 3kg tetrafluoroethylene, 13kg polyvinyl alcohol, 2kg p methoxy phenol, 4kg acetone are added successively in reaction vessel, be warming up to 65 DEG C, stir 2 hours under 550r/min rotating speed, be down to room temperature, obtain anticorrosive coating.
embodiment 5
The formula of anticorrosive coating of the present invention is as follows:
Epoxy acrylic resin 43kg, phenylformic acid dibutylester 6kg, Hydroxyethyl acrylate 5kg, tetrafluoroethylene 2kg, polyvinyl alcohol 14kg, p methoxy phenol 3kg, acetone 5kg.
The preparation method of anticorrosive coating of the present invention is: 43kg epoxy acrylic resin, 6kg phenylformic acid dibutylester, 5kg Hydroxyethyl acrylate, 2kg tetrafluoroethylene, 14kg polyvinyl alcohol, 3kg p methoxy phenol, 5kg acetone are added successively in reaction vessel, be warming up to 60 DEG C, stir 2 hours under 500r/min rotating speed, be down to room temperature, obtain anticorrosive coating.
embodiment 6
The formula of anticorrosive coating of the present invention is as follows:
Epoxy acrylic resin 45kg, phenylformic acid dibutylester 5kg, Hydroxyethyl acrylate 7kg, tetrafluoroethylene 2.5kg, polyvinyl alcohol 15kg, p methoxy phenol 2.5kg, acetone 3kg.
The preparation method of anticorrosive coating of the present invention is: 45kg epoxy acrylic resin, 5kg phenylformic acid dibutylester, 7kg Hydroxyethyl acrylate, 2.5kg tetrafluoroethylene, 15kg polyvinyl alcohol, 2.5kg p methoxy phenol, 3kg acetone are added successively in reaction vessel, be warming up to 65 DEG C, stir 2 hours under 600r/min rotating speed, be down to room temperature, obtain anticorrosive coating.
During use, it is evenly applied to metallic surface, dries.
Last it is noted that the foregoing is only the preferred embodiments of the present invention, be not limited to the present invention, although with reference to previous embodiment to invention has been detailed description, for a person skilled in the art, it still can be modified to the technical scheme described in foregoing embodiments, or carries out equivalent replacement to wherein portion of techniques feature.Within the spirit and principles in the present invention all, any amendment done, equivalent replacement, improvement etc., all should be included within protection scope of the present invention.
Claims (3)
1. an anticorrosive coating, is characterized in that: described anticorrosive coating is made up of each component of following mass fraction: epoxy acrylic resin 40-45 part, phenylformic acid dibutylester 3-6 part, Hydroxyethyl acrylate 5-8 part, tetrafluoroethylene 2-3 part, polyvinyl alcohol 12-15 part, p methoxy phenol 2-3 part, acetone 3-5 part.
2. anticorrosive coating according to claim 1, is characterized in that: described acetone is 4 parts.
3. the preparation method of the anticorrosive coating described in claim 1 or 2, is each component mixed, is warming up to 60-70 DEG C, stirs 2 hours, be down to room temperature, obtain anticorrosive coating under 500-600r/min rotating speed.