CN103704911A - Method for manufacturing apparel fabric of sportswear - Google Patents
Method for manufacturing apparel fabric of sportswear Download PDFInfo
- Publication number
- CN103704911A CN103704911A CN201310746563.0A CN201310746563A CN103704911A CN 103704911 A CN103704911 A CN 103704911A CN 201310746563 A CN201310746563 A CN 201310746563A CN 103704911 A CN103704911 A CN 103704911A
- Authority
- CN
- China
- Prior art keywords
- parts
- moisture absorption
- high moisture
- add
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及一种运动型服装面料的制造方法，它采用如下步骤：A）取丝胶溶液、环糊精、加入谷氨酰胺转氨酶溶液搅拌均匀，然后进行冷冻干燥，均匀粉碎。B）取步骤A）得到的产物、丙烯酸、甲基丙烯酸钠、羧甲基纤维素钠、过硫酸钾和水，搅拌反应；C）在步骤B)的产物中加入乙二醇二缩水甘油基乙醚水溶液，搅拌反应；D）将产物烘干，均匀粉碎，研磨后得高吸放湿材料；E）将步骤D）得到的高吸放湿材料加入到聚酯熔体中，搅拌均匀后，进行纺丝，获得改性聚酯纤维；F）以丙纶丝为经线，以改性聚酯纤维作纬线进行织造加工，获得运动型服装面料。本发明的有益效果是：1）制备方法简单；2）通过改变聚酯纤维大分子的化学组分，使聚酯纤维具备高吸水性和快速排湿性；3）该服装面料既有良好的舒适性，又不会粘贴皮肤而产生冷湿感。The invention relates to a manufacturing method of sports clothing fabric, which adopts the following steps: A) taking sericin solution, cyclodextrin, adding glutamine transaminase solution and stirring evenly, then freeze-drying and uniformly pulverizing. B) Take the product obtained in step A), acrylic acid, sodium methacrylate, sodium carboxymethylcellulose, potassium persulfate and water, and stir to react; C) Add ethylene glycol diglycidyl to the product in step B) Ethyl ether solution, stirring and reacting; D) Dry the product, pulverize it evenly, and grind it to obtain a high moisture absorption and desorption material; E) Add the high moisture absorption and desorption material obtained in step D) into the polyester melt, stir evenly, Spinning to obtain modified polyester fibers; F) Weaving with polypropylene yarns as warp threads and modified polyester fibers as weft threads to obtain sportswear fabrics. The beneficial effects of the invention are: 1) The preparation method is simple; 2) By changing the chemical composition of the polyester fiber macromolecules, the polyester fiber has high water absorption and fast moisture drainage; 3) The clothing fabric has good comfort Non-toxic, and will not stick to the skin and produce a cold and wet feeling.
Description
技术领域technical field
本发明涉及一种运动型服装面料的制造方法，属于纺织服装技术领域。The invention relates to a method for manufacturing sports clothing fabrics, belonging to the technical field of textiles and clothing.
背景技术Background technique
近年来，人们对服装面料的舒适性、健康性、安全性和环保性等要求越来越高，随着人们在户外活动时间的增加，休闲服与运动服相互渗透和融为一体的趋势也日益受广大消费者的青睐，这类服装的面料，既要求有良好的舒适性，又要求在尽情活动时，一旦出现汗流浃背情况，服装不会粘贴皮肤而产生冷湿感。In recent years, people have higher and higher requirements for the comfort, health, safety and environmental protection of clothing fabrics. With the increase of people's outdoor activities, the trend of mutual penetration and integration of casual wear and sportswear is also Increasingly favored by consumers, the fabrics of this type of clothing not only require good comfort, but also require that the clothing will not stick to the skin and produce a cold and damp feeling when sweating profusely occurs during activities.
聚酯纤维的强力、耐磨性、回弹性和尺寸稳定性均能较好满足各种最终用途的需要，但聚酯纤维是一种典型的疏水性纤维，吸湿率只有0.4％，作为贴身服用材料，它的穿着舒适性很差，尤其当人体出汗时它排汗困难，给人闷热不适的感觉。聚酯纤维是合成纤维中产量最大、用途最广的纤维品种，通过改性，利用聚酯纤维开发服装面料具有积极的意义。The strength, abrasion resistance, resilience and dimensional stability of polyester fiber can better meet the needs of various end uses, but polyester fiber is a typical hydrophobic fiber with a moisture absorption rate of only 0.4%. Material, its wearing comfort is very poor, especially when the human body sweats, it has difficulty perspiring, giving people a hot and uncomfortable feeling. Polyester fiber is the largest and most versatile fiber variety among synthetic fibers. It is of positive significance to use polyester fiber to develop clothing fabrics through modification.
发明内容Contents of the invention
本发明的目的在于克服现有技术存在的不足，而提供一种运动型服装面料的制造方法。显著影响人体舒适性的是服装面料的综合散热、散湿性能，服装面料的关键是水分要能够快速吸收、释放。本专利通过改变聚酯纤维大分子的化学组分，使聚酯纤维具备高吸水性和快速排湿的这两种性能，同时以丙纶丝为经线，以高吸放湿改性聚酯纤维作纬线进行织造加工，获得服装面料，从而使服装面料既有良好的舒适性，又可以在尽情活动时，一旦出现汗流浃背情况，服装不会粘贴皮肤而产生冷湿感。The object of the present invention is to overcome the deficiencies in the prior art and provide a method for manufacturing sportswear fabrics. What significantly affects the comfort of the human body is the comprehensive heat dissipation and moisture dissipation performance of clothing fabrics. The key to clothing fabrics is that moisture can be quickly absorbed and released. In this patent, by changing the chemical composition of polyester fiber macromolecules, the polyester fiber has the properties of high water absorption and fast moisture release. The weft thread is weaved to obtain clothing fabrics, so that the clothing fabrics have good comfort, and when you are active, once sweating occurs, the clothing will not stick to the skin and produce a cold and wet feeling.
为了达到上述目的，本发明采用的技术方案是：一种运动型服装面料的制造方法，它采用如下步骤：In order to achieve the above object, the technical solution adopted in the present invention is: a kind of manufacture method of sports clothing fabric, and it adopts following steps:
A）按质量份数取重量百分比浓度为5～10%的丝胶溶液100份、β－环糊精1～3份、加入重量百分比浓度为10%的谷氨酰胺转氨酶溶液0.1～2份，搅拌均匀，在20～30℃条件下放置1～3个小时，然后在零下50℃条件下进行冷冻干燥，均匀粉碎；A) Take 100 parts of sericin solution with a concentration of 5 to 10% by weight, 1 to 3 parts of β-cyclodextrin, and add 0.1 to 2 parts of a transglutaminase solution with a concentration of 10% by weight in parts by mass, Stir evenly, place at 20-30°C for 1-3 hours, then freeze-dry at minus 50°C, and pulverize evenly;
B）按质量份数取步骤A）得到的产物0.2～1份、丙烯酸5～10份、甲基丙烯酸钠1～2份、羧甲基纤维素钠2～5份、过硫酸钾0.05～0.15份，水10～15份，在40～50℃下，搅拌反应0.5小时；B) Take 0.2-1 part of the product obtained in step A) in parts by mass, 5-10 parts of acrylic acid, 1-2 parts of sodium methacrylate, 2-5 parts of sodium carboxymethylcellulose, and 0.05-0.15 parts of potassium persulfate 10-15 parts of water, stirred and reacted for 0.5 hours at 40-50°C;
C）按质量份数在步骤B)的产物中加入重量百分比浓度为5%的乙二醇二缩水甘油基乙醚水溶液1～5份，在温度为55～75℃下，搅拌反应1小时；C) Add 1 to 5 parts of an aqueous solution of ethylene glycol diglycidyl ether with a concentration of 5% by weight to the product of step B) in parts by mass, and stir and react for 1 hour at a temperature of 55 to 75°C;
D）将步骤C)所得的产物烘干，均匀粉碎，研磨后得粒径不大于1μｍ的高吸放湿材料；D) drying the product obtained in step C), uniformly crushing, and grinding to obtain a high moisture absorption and desorption material with a particle size not greater than 1 μm;
E）将步骤D）得到的高吸放湿材料加入到聚酯熔体中，搅拌均匀后，进行纺丝，获得改性聚酯纤维；其中步骤D）制得的高吸放湿材料的加入量为聚酯熔体的重量的5%～10%；E) Add the high moisture absorption and release material obtained in step D) into the polyester melt, stir evenly, and then spin to obtain modified polyester fibers; where the high moisture absorption and release material obtained in step D) is added The amount is 5% to 10% of the weight of the polyester melt;
F）以丙纶丝为经线，以步骤E）的高吸放湿改性聚酯纤维作纬线进行织造加工，获得运动型服装面料。F) Weaving and processing the polypropylene yarn as the warp and the high moisture absorption and release modified polyester fiber in step E) as the weft to obtain the sportswear fabric.
本发明与现有方法相比，具有如下突出的优点：1）制备方法简单；2）本发明通过改变聚酯纤维大分子的化学组分，使聚酯纤维具备高吸水性和快速排湿的这两种性能；3）以丙纶丝为经线，以高吸放湿改性聚酯纤维作纬线进行织造加工，使服装面料既有良好的舒适性，又可以在尽情活动时，一旦出现汗流浃背情况，服装不会粘贴皮肤而产生冷湿感。Compared with the existing method, the present invention has the following outstanding advantages: 1) The preparation method is simple; 2) The present invention makes the polyester fiber have high water absorption and fast moisture-discharging properties by changing the chemical composition of the polyester fiber macromolecule These two properties; 3) Polypropylene yarn is used as the warp thread, and high moisture absorption and release modified polyester fiber is used as the weft thread for weaving processing, so that the clothing fabric has good comfort and can be sweated when you are active. , Clothing will not stick to the skin and produce a cold and wet feeling.
具体实施方式Detailed ways
下面将结合具体实施例对本发明做详细的介绍：本发明所述一种运动型服装面料的制造方法，它采用如下步骤：The present invention will be described in detail below in conjunction with specific embodiment: the manufacture method of a kind of sports clothing lining of the present invention, it adopts the following steps:
A）按质量份数取重量百分比浓度为5～10%的丝胶溶液100份、β－环糊精1～3份、加入重量百分比浓度为10%的谷氨酰胺转氨酶溶液0.1～2份，搅拌均匀，在20～30℃条件下放置1～3个小时，然后在零下50℃条件下进行冷冻干燥，均匀粉碎；A) Take 100 parts of sericin solution with a concentration of 5 to 10% by weight, 1 to 3 parts of β-cyclodextrin, and add 0.1 to 2 parts of a transglutaminase solution with a concentration of 10% by weight in parts by mass, Stir evenly, place at 20-30°C for 1-3 hours, then freeze-dry at minus 50°C, and pulverize evenly;
B）按质量份数取步骤A）得到的产物0.2～1份、丙烯酸5～10份、甲基丙烯酸钠1～2份、羧甲基纤维素钠2～5份、过硫酸钾0.05～0.15份，水10～15份，在40～50℃下，搅拌反应0.5小时；B) Take 0.2-1 part of the product obtained in step A) in parts by mass, 5-10 parts of acrylic acid, 1-2 parts of sodium methacrylate, 2-5 parts of sodium carboxymethylcellulose, and 0.05-0.15 parts of potassium persulfate 10-15 parts of water, stirred and reacted for 0.5 hours at 40-50°C;
C）按质量份数在步骤B)的产物中加入重量百分比浓度为5%的乙二醇二缩水甘油基乙醚水溶液1～5份，在温度为55～75℃下，搅拌反应1小时；C) Add 1 to 5 parts of an aqueous solution of ethylene glycol diglycidyl ether with a concentration of 5% by weight to the product of step B) in parts by mass, and stir and react for 1 hour at a temperature of 55 to 75°C;
D）将步骤C)所得的产物烘干，均匀粉碎，研磨后得粒径不大于1μｍ的高吸放湿材料；D) drying the product obtained in step C), uniformly crushing, and grinding to obtain a high moisture absorption and desorption material with a particle size not greater than 1 μm;
E）将步骤D）得到的高吸放湿材料加入到聚酯熔体中，搅拌均匀后，进行纺丝，获得改性聚酯纤维；其中步骤D）制得的高吸放湿材料的加入量为聚酯熔体的重量的5%～10%；E) Add the high moisture absorption and release material obtained in step D) into the polyester melt, stir evenly, and then spin to obtain modified polyester fibers; where the high moisture absorption and release material obtained in step D) is added The amount is 5% to 10% of the weight of the polyester melt;
F）以丙纶丝为经线，以步骤E）的高吸放湿改性聚酯纤维作纬线进行织造加工，获得运动型服装面料。F) Weaving and processing the polypropylene yarn as the warp and the high moisture absorption and release modified polyester fiber in step E) as the weft to obtain the sportswear fabric.
本发明所述的实施例可以在上述技术方案的基础上，通过具体数值的不同替换，可以得到无数个实施例，因此，以下所述的三个实施例，仅仅只是无数个实施例中的个例，任何在上述技术方案所做的技术数值替换，均属于本发明的保护范围。The embodiments of the present invention can be based on the above technical solutions, through the different replacement of specific values, can obtain countless embodiments, therefore, the three embodiments described below are just one of the countless embodiments For example, any replacement of technical values in the above technical solutions falls within the protection scope of the present invention.
实施例1：本发明所述运动型服装面料的制造方法，它采用如下步骤：Embodiment 1: the manufacture method of sportswear fabric of the present invention, it adopts following steps:
A）按质量份数取重量百分比浓度为5%的丝胶溶液100份、β－环糊精1份、加入重量百分比浓度为10%的谷氨酰胺转氨酶溶液0.1份，搅拌均匀，在20～30℃条件下放置1个小时，然后在零下50℃条件下进行冷冻干燥，均匀粉碎；A) According to the number of parts by mass, take 100 parts of sericin solution with a concentration of 5% by weight, 1 part of β-cyclodextrin, and add 0.1 part of a transglutaminase solution with a concentration of 10% by weight, and stir evenly. Place at 30°C for 1 hour, then freeze-dry at minus 50°C, and pulverize evenly;
B）按质量份数取步骤A）得到的产物0.2份、丙烯酸5份、甲基丙烯酸钠1份、羧甲基纤维素钠2份、过硫酸钾0.05份，水10份，在40～50℃下，搅拌反应0.5小时；B) Take 0.2 parts of the product obtained in step A) in parts by mass, 5 parts of acrylic acid, 1 part of sodium methacrylate, 2 parts of sodium carboxymethylcellulose, 0.05 parts of potassium persulfate, and 10 parts of water. At ℃, stir the reaction for 0.5 hours;
C）按质量份数在步骤B)的产物中加入重量百分比浓度为5%的乙二醇二缩水甘油基乙醚水溶液1份，在温度为55℃下，搅拌反应1小时；C) Add 1 part of an aqueous solution of ethylene glycol diglycidyl ether with a concentration of 5% by weight to the product of step B) in parts by mass, and stir and react for 1 hour at a temperature of 55°C;
D）将步骤C)所得的产物烘干，均匀粉碎，研磨后得粒径不大于1μｍ的高吸放湿材料；D) drying the product obtained in step C), uniformly crushing, and grinding to obtain a high moisture absorption and desorption material with a particle size not greater than 1 μm;
E）将步骤D）得到的高吸放湿材料加入到聚酯熔体中，搅拌均匀后，进行纺丝，获得改性聚酯纤维；其中步骤D）制得的高吸放湿材料的加入量为聚酯熔体的重量的5%；E) Add the high moisture absorption and release material obtained in step D) into the polyester melt, stir evenly, and then spin to obtain modified polyester fibers; where the high moisture absorption and release material obtained in step D) is added The amount is 5% of the weight of polyester melt;
F）以丙纶丝为经线，以步骤E）的高吸放湿改性聚酯纤维作纬线进行织造加工，获得运动型服装面料。F) Weaving and processing the polypropylene yarn as the warp and the high moisture absorption and release modified polyester fiber in step E) as the weft to obtain the sportswear fabric.
实施例2：本发明所述运动型服装面料的制造方法，它采用如下步骤：Embodiment 2: the manufacture method of sportswear fabric of the present invention, it adopts the following steps:
A）按质量份数取重量百分比浓度为8%的丝胶溶液100份、β－环糊精2份、加入重量百分比浓度为10%的谷氨酰胺转氨酶溶液1份，搅拌均匀，在20℃条件下放置2个小时，然后在零下50℃条件下进行冷冻干燥，均匀粉碎；A) According to the number of parts by mass, take 100 parts of sericin solution with a concentration of 8% by weight, 2 parts of β-cyclodextrin, and add 1 part of a transglutaminase solution with a concentration of 10% by weight, stir evenly, and heat at 20°C Place under low temperature conditions for 2 hours, then freeze-dry at minus 50°C, and evenly pulverize;
B）按质量份数取步骤A）得到的产物0.6份、丙烯酸8份、甲基丙烯酸钠1份、羧甲基纤维素钠3份、过硫酸钾0.1份，水10份，在40℃下，搅拌反应0.5小时；B) Take 0.6 parts of the product obtained in step A) in parts by mass, 8 parts of acrylic acid, 1 part of sodium methacrylate, 3 parts of sodium carboxymethylcellulose, 0.1 parts of potassium persulfate, and 10 parts of water, at 40 °C , stirred and reacted for 0.5 hours;
C）按质量份数在步骤B)的产物中加入重量百分比浓度为5%的乙二醇二缩水甘油基乙醚水溶液3份，在温度为65℃下，搅拌反应1小时；C) Add 3 parts of an aqueous solution of ethylene glycol diglycidyl ether with a concentration of 5% by weight to the product of step B) in parts by mass, and stir and react for 1 hour at a temperature of 65°C;
D）将步骤C)所得的产物烘干，均匀粉碎，研磨后得粒径不大于1μｍ的高吸放湿材料；D) drying the product obtained in step C), uniformly crushing, and grinding to obtain a high moisture absorption and desorption material with a particle size not greater than 1 μm;
E）将步骤D）得到的高吸放湿材料加入到聚酯熔体中，搅拌均匀后，进行纺丝，获得改性聚酯纤维；其中步骤D）制得的高吸放湿材料的加入量为聚酯熔体的重量的8%；E) Add the high moisture absorption and release material obtained in step D) into the polyester melt, stir evenly, and then spin to obtain modified polyester fibers; where the high moisture absorption and release material obtained in step D) is added The amount is 8% of the weight of polyester melt;
F）以丙纶丝为经线，以步骤E）的高吸放湿改性聚酯纤维作纬线进行织造加工，获得运动型服装面料。F) Weaving and processing the polypropylene yarn as the warp and the high moisture absorption and release modified polyester fiber in step E) as the weft to obtain the sportswear fabric.
实施例3：本发明所述运动型服装面料的制造方法，它采用如下步骤：Embodiment 3: the manufacture method of sportswear fabric of the present invention, it adopts the following steps:
A）按质量份数取重量百分比浓度为10%的丝胶溶液100份、β－环糊精3份、加入重量百分比浓度为10%的谷氨酰胺转氨酶溶液2份，搅拌均匀，在30℃条件下放置3个小时，然后在零下50℃条件下进行冷冻干燥，均匀粉碎；A) According to the number of parts by mass, take 100 parts of sericin solution with a concentration of 10% by weight, 3 parts of β-cyclodextrin, and add 2 parts of a transglutaminase solution with a concentration of 10% by weight, stir well, and heat at 30°C Place it under the same conditions for 3 hours, then freeze-dry it at minus 50°C, and pulverize it evenly;
B）按质量份数取步骤A）得到的产物1份、丙烯酸10份、甲基丙烯酸钠2份、羧甲基纤维素钠5份、过硫酸钾0.15份，水15份，在50℃下，搅拌反应0.5小时；B) Take 1 part of the product obtained in step A) in parts by mass, 10 parts of acrylic acid, 2 parts of sodium methacrylate, 5 parts of sodium carboxymethylcellulose, 0.15 parts of potassium persulfate, and 15 parts of water, at 50 °C , stirred and reacted for 0.5 hours;
C）按质量份数在步骤B)的产物中加入重量百分比浓度为5%的乙二醇二缩水甘油基乙醚水溶液5份，在温度为75℃下，搅拌反应1小时；C) Add 5 parts of ethylene glycol diglycidyl ethyl ether aqueous solution with a concentration of 5% by weight to the product of step B) in parts by mass, and stir and react for 1 hour at a temperature of 75°C;
D）将步骤C)所得的产物烘干，均匀粉碎，研磨后得粒径不大于1μｍ的高吸放湿材料；D) drying the product obtained in step C), uniformly crushing, and grinding to obtain a high moisture absorption and desorption material with a particle size not greater than 1 μm;
E）将步骤D）得到的高吸放湿材料加入到聚酯熔体中，搅拌均匀后，进行纺丝，获得改性聚酯纤维；其中步骤D）制得的高吸放湿材料的加入量为聚酯熔体的重量的10%；E) Add the high moisture absorption and release material obtained in step D) into the polyester melt, stir evenly, and then spin to obtain modified polyester fibers; where the high moisture absorption and release material obtained in step D) is added The amount is 10% of the weight of polyester melt;
F）以丙纶丝为经线，以步骤E）的高吸放湿改性聚酯纤维作纬线进行织造加工，获得运动型服装面料。F) Weaving and processing the polypropylene yarn as the warp and the high moisture absorption and release modified polyester fiber in step E) as the weft to obtain the sportswear fabric.
Claims (1)